CN103725168A - 一种缩醛漆包线漆及其制备方法 - Google Patents

一种缩醛漆包线漆及其制备方法 Download PDF

Info

Publication number
CN103725168A
CN103725168A CN201310598809.4A CN201310598809A CN103725168A CN 103725168 A CN103725168 A CN 103725168A CN 201310598809 A CN201310598809 A CN 201310598809A CN 103725168 A CN103725168 A CN 103725168A
Authority
CN
China
Prior art keywords
parts
wire enamel
acetal
add
nylon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310598809.4A
Other languages
English (en)
Inventor
张勇进
方小辉
章小虎
刘琛
胡强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING TIANHE SPECIAL INSULATED WIRE Co Ltd
Original Assignee
TONGLING TIANHE SPECIAL INSULATED WIRE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING TIANHE SPECIAL INSULATED WIRE Co Ltd filed Critical TONGLING TIANHE SPECIAL INSULATED WIRE Co Ltd
Priority to CN201310598809.4A priority Critical patent/CN103725168A/zh
Publication of CN103725168A publication Critical patent/CN103725168A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种缩醛漆包线漆，其特征在于，由下列重量份（公斤）的原料制成：聚乙烯醇缩甲醛树脂12-15、三聚磷酸钠3-4、烟片胶2-3、聚酯树脂15-20、尼龙12 12-15、E-44环氧树脂5-10、纳米二氧化硅3-4、聚己二酸9-11，4-丁二醇酯二醇10-12、氧化镁3-5、莱茵蜡3-5、单丁基氧化锡2-3、环烷酸钴2-3、二甲基甲酰胺3-4、助剂7-9、间对甲酚80-90、二甲苯100-120；本发明缩醛漆包线漆能够满足155℃的热级，高于普通的缩醛漆包线漆，而且比普通的缩醛漆包线漆具有更好的耐磨性。

Description

一种缩醛漆包线漆及其制备方法
技术领域
本发明涉及一种漆包线漆，尤其是一种缩醛漆包线漆及其制备方法。
背景技术
漆包线是一种电工材料，它是在一根圆形的铜线表面加工一层薄薄的高强度绝缘层，起到与外界绝缘的作用。按规格可加工成比发丝还细的毛丝线，像拇指般粗的纱包线。漆包线具有很好的绝缘效果和防水能力。在电器方面应用很广泛，如电动机，发电机，水泵，电磁铁，电焊机，家用电器，无线通讯，扬声器，电报机，变压器等。漆包线漆是生产漆包线的必要绝缘材料，漆包线漆要求具有良好的附着性、机械强度、绝缘性能、耐热性能、耐磨性能、耐盐雾及耐恶劣环境性能等，但是普通的漆包线漆存在耐热性、耐磨性差、强度不够、耐热级低于120℃等问题，难以满足不同环境的要求。需要对漆包线漆的配方与生产工艺进行改进，进一步提高漆包漆的性能，降低其生产成本。
发明内容
本发明的目的就是提供一种缩醛漆包线漆及其制备方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种缩醛漆包线漆，其特征在于，由下列重量份（公斤）的原料制成：聚乙烯醇缩甲醛树脂12-15、三聚磷酸钠3-4、烟片胶2-3、聚酯树脂15-20、尼龙12  12-15、E-44环氧树脂5-10、纳米二氧化硅3-4、聚己二酸9-11，4-丁二醇酯二醇10-12、氧化镁3-5、莱茵蜡3-5、单丁基氧化锡2-3、环烷酸钴2-3、二甲基甲酰胺3-4、助剂7-9、间对甲酚80-90、二甲苯100-120；
所述的助剂由下列重量份原料制成：纳米云母粉0.2-0.3、硅烷偶联剂KH550 1-2、对苯二酚1-2、二季戊四醇六丙烯酸酯5-7、交联剂TAC2-3、聚异丁烯2-3、甲基丙烯酸二甲氨基乙酯10-12、乙酯丁酯4-6、没食子酸丙酯2-3、薏仁油1-2；其制备方法是将各物料混合，加热至60-70℃，搅拌反应30-40分钟，即得。
所述的缩醛漆包线漆的制备方法，其特征在于包括以下步骤：
（1）、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀，加热到45-55℃，加入尼龙12，搅拌并加热到160-180℃，至尼龙12完全溶解后，再加入聚己二酸、4-丁二醇酯二醇、二甲基甲酰胺、环烷酸钴，保温反应5-6小时；
（2）、将步骤（1）反应物料降温至65-85℃，加入单丁基氧化锡、莱茵蜡、烟片胶、助剂，保持温度，搅拌反应2-3小时；
（3）、再加入剩余物料，升温至95-100℃，继续搅拌反应2-3小时；
（4）、冷却物料至50-60℃，研磨至20-40μm浆料，过滤即得。
本发明缩醛漆包线漆有以下有益效果：本发明缩醛漆包线漆能够满足155℃的热级，高于普通的缩醛漆包线漆，而且比普通的缩醛漆包线漆具有更好的耐磨性。
具体实施方式
所述的缩醛漆包线漆是由下列重量份（公斤）的原料制成：聚乙烯醇缩甲醛树脂12、三聚磷酸钠4、烟片胶2、聚酯树脂15、尼龙12  15、E-44环氧树脂5、纳米二氧化硅4、聚己二酸9，4-丁二醇酯二醇10、氧化镁5、莱茵蜡3、单丁基氧化锡3、环烷酸钴2、二甲基甲酰胺4、助剂7、间对甲酚80、二甲苯100；
所述的助剂由下列重量份（公斤）原料制成：纳米云母粉0.2、硅烷偶联剂KH550 1、对苯二酚2、二季戊四醇六丙烯酸酯7、交联剂TAC2、聚异丁烯2、甲基丙烯酸二甲氨基乙酯10、乙酯丁酯6、没食子酸丙酯3、薏仁油1；其制备方法是将各物料混合，加热至60-70℃，搅拌反应30-40分钟，即得。
制备方法包括以下步骤：
（1）、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀，加热到45-55℃，加入尼龙12，搅拌并加热到160-180℃，至尼龙12完全溶解后，再加入聚己二酸、4-丁二醇酯二醇、二甲基甲酰胺、环烷酸钴，保温反应5-6小时；
（2）、将步骤（1）反应物料降温至65-85℃，加入单丁基氧化锡、莱茵蜡、烟片胶、助剂，保持温度，搅拌反应2-3小时；
（3）、再加入剩余物料，升温至95-100℃，继续搅拌反应2-3小时；
（4）、冷却物料至50-60℃，研磨至20-40μm浆料，过滤即得。
使用本发明漆制线材主要性能指标如下：
1、附着性好；
2、耐热等级≥ 155℃，热冲击达到185℃漆膜不开裂；
3、粘结强度15N/mm2；
4、耐变压器油1200小时/105℃，漆膜无损坏。

Claims (3)

1.一种缩醛漆包线漆，其特征在于，由下列重量份（公斤）的原料制成：聚乙烯醇缩甲醛树脂12-15、三聚磷酸钠3-4、烟片胶2-3、聚酯树脂15-20、尼龙12  12-15、E-44环氧树脂5-10、纳米二氧化硅3-4、聚己二酸9-11，4-丁二醇酯二醇10-12、氧化镁3-5、莱茵蜡3-5、单丁基氧化锡2-3、环烷酸钴2-3、二甲基甲酰胺3-4、助剂7-9、间对甲酚80-90、二甲苯100-120。
2.根据权利要求1所述的助剂由下列重量份原料制成：纳米云母粉0.2-0.3、硅烷偶联剂KH550 1-2、对苯二酚1-2、二季戊四醇六丙烯酸酯5-7、交联剂TAC2-3、聚异丁烯2-3、甲基丙烯酸二甲氨基乙酯10-12、乙酯丁酯4-6、没食子酸丙酯2-3、薏仁油1-2；其制备方法是将各物料混合，加热至60-70℃，搅拌反应30-40分钟，即得。
3.根据权利要求1所述的缩醛漆包线漆的制备方法，其特征在于包括以下步骤：
（1）、称取二甲苯、间对甲酚投入带有搅拌器的反应釜中搅拌混合均匀，加热到45-55℃，加入尼龙12，搅拌并加热到160-180℃，至尼龙12完全溶解后，再加入聚己二酸、4-丁二醇酯二醇、二甲基甲酰胺、环烷酸钴，保温反应5-6小时；
（2）、将步骤（1）反应物料降温至65-85℃，加入单丁基氧化锡、莱茵蜡、烟片胶、助剂，保持温度，搅拌反应2-3小时；
（3）、再加入剩余物料，升温至95-100℃，继续搅拌反应2-3小时；
（4）、冷却物料至50-60℃，研磨至20-40μm浆料，过滤即得。
CN201310598809.4A 2013-11-25 2013-11-25 一种缩醛漆包线漆及其制备方法 Pending CN103725168A (zh)