CN103013642A - 一种含纳米TiO2的水基热轧轧制液及其制备方法 - Google Patents

一种含纳米TiO2的水基热轧轧制液及其制备方法 Download PDF

Info

Publication number
CN103013642A
CN103013642A CN2013100023009A CN201310002300A CN103013642A CN 103013642 A CN103013642 A CN 103013642A CN 2013100023009 A CN2013100023009 A CN 2013100023009A CN 201310002300 A CN201310002300 A CN 201310002300A CN 103013642 A CN103013642 A CN 103013642A
Authority
CN
China
Prior art keywords
water
nano
hot rolling
tio
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100023009A
Other languages
English (en)
Other versions
CN103013642B (zh
Inventor
孙建林
朱作鑫
牛泰龙
刘娜娜
李岩
朱泽郎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Science and Technology Beijing USTB
Original Assignee
University of Science and Technology Beijing USTB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Science and Technology Beijing USTB filed Critical University of Science and Technology Beijing USTB
Priority to CN201310002300.9A priority Critical patent/CN103013642B/zh
Publication of CN103013642A publication Critical patent/CN103013642A/zh
Application granted granted Critical
Publication of CN103013642B publication Critical patent/CN103013642B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于润滑剂技术领域，涉及一种含纳米TiO2的水基热轧轧制液及其制备方法，用于板带钢热轧过程中的润滑。本发明选择具有缓蚀防锈性能优良的纳米TiO2作为极压剂，选用六偏磷酸钠和十二烷基苯磺酸钠作为分散剂，将去离子水、六偏磷酸钠、十二烷基苯磺酸钠、三乙醇胺、异噻唑啉酮、丙三醇和苯并三氮唑依次加入，放入放在转速为80-120转/分钟反应釜中进行加热搅拌，当温度达到60°C时，加入纳米二氧化钛，保温并持续搅拌30分钟，随后停止加热继续搅拌至室温，得到白色悬浊状液体，即配成所需水基轧制液。使用该轧水基轧制液降低了传统热轧油带来的污染，能显著提高钢材轧后缓释防锈性能，表面质量好，防腐蚀周期长。

Description

一种含纳米TiO2的水基热轧轧制液及其制备方法
 
技术领域
本发明涉及润滑剂技术领域，用于板带钢热轧过程中的润滑，其具体的是一种含纳米TiO2的水基热轧轧制液及其制备方法。
 
背景技术
近年来，热轧工艺润滑技术已经得到了广泛的应用，热轧润滑效果也得到了认可，然而目前热轧润滑剂大多使用热轧油，传统的热轧油在轧制过程中油耗高、生产环境恶劣、污染冷却水、钢材缓蚀防锈性能差等。随着纳米技术在各行各业的应用，纳米水基轧制液使以水代油变成了现实，润滑冷却性能好，满足热轧轧制要求、缓蚀防锈性能优良、污染少的水性轧制液完全可以取代热轧油，为钢材热轧节能减排、环保生产提供参考依据。
 
发明内容
本发明的目的是提供一种稳定性、润滑性、缓蚀防锈性能优良的水基纳米热轧轧制液。
一种含纳米TiO2的水基热轧轧制液，其主要组分及所占重量百分比如下。
序号 组分名称 重量百分比（100%）
1 纳米二氧化钛 0.2-1.0
2 六偏磷酸钠 0.5-2.0
3 十二烷基苯磺酸钠 1.0-3.0
4 三乙醇胺 1.0-3.0
5 异噻唑啉酮 0.5-1.0
6 丙三醇 10-15.0
7 苯并三氮唑 0.5-1.0
8 去离子水 80-86
     本发明选择具有缓蚀防锈性能优良的纳米TiO2作为极压剂，选用六偏磷酸钠和十二烷基苯磺酸钠作为分散剂，将纳米TiO2均匀稳定的分散到水中，配制成具有缓蚀防锈性能的水基纳米热轧轧制液。
该轧制油的制作方法：将去离子水、六偏磷酸钠、十二烷基苯磺酸钠、三乙醇胺、异噻唑啉酮、丙三醇和苯并三氮唑依次加入，放入放在转速为80-120转/分钟反应釜中进行加热搅拌，当温度达到50～70°C时，加入纳米二氧化钛，保温并持续搅拌30-45分钟，随后停止加热继续搅拌至室温，得到白色悬浊状液体，即配成所需水基轧制液。
本发明水基轧制液可以直接用于钢铁的热轧加工过程。使用该轧水基轧制液降低了传统热轧油带来的污染，能显著提高钢材轧后缓释防锈性能，表面质量好，防腐蚀周期长。
 
具体实施方式
一、1、实施例1
实施例1配方见下表：
序号 组分名称 重量（g）
1 纳米二氧化钛 0.2
2 六偏磷酸钠 0.5
3 十二烷基苯磺酸钠 1.0
4 三乙醇胺 1.0
5 异噻唑啉酮 0.5
6 丙三醇 10.0
7 苯并三氮唑 0.5
8 去离子水 85.3
按上表的各组分重量配方，将去离子水、六偏磷酸钠、十二烷基苯磺酸钠、三乙醇胺、异噻唑啉酮、丙三醇和苯并三氮唑依次加入，放入放在转速为80-120转/分钟反应釜中进行加热搅拌，当温度达到60°C时，加入纳米二氧化钛，保温并持续搅拌30分钟，随后停止加热继续搅拌至室温，得到白色悬浊状液体，即配成所需水基轧制液，该配方轧制液室温静置7天左右产生少量沉淀，分散效果较好，使用时稍加搅拌即可。
2、实施例2
实施例2配方见下表：
序号 组分名称 重量（g）
1 纳米二氧化钛 0.5
2 六偏磷酸钠 1.0
3 十二烷基苯磺酸钠 2.0
4 三乙醇胺 2.0
5 异噻唑啉酮 0.8
6 丙三醇 12.0
7 苯并三氮唑 0.6
8 去离子水 81.1
按上表配方将去离子水、六偏磷酸钠、十二烷基苯磺酸钠、三乙醇胺、异噻唑啉酮、丙三醇和苯并三氮唑依次加入，放入放在转速为80-120转/分钟反应釜中进行加热搅拌，当温度达到60°C时，加入纳米二氧化钛，保温并持续搅拌30分钟，随后停止加热继续搅拌至室温，得到白色悬浊状液体，即配成所需水基轧制液，该配方轧制液静置72小时以后出现明显分层，4天以后纳米TiO2完全沉淀，使用时需要搅拌。
3、实施例3
实施例3配方见下表：
序号 组分名称 重量（g）
1 纳米二氧化钛 1.0
2 六偏磷酸钠 2.0
3 十二烷基苯磺酸钠 3.0
4 三乙醇胺 2.0
5 异噻唑啉酮 1.0
6 丙三醇 10.0
7 苯并三氮唑 1.0
8 去离子水 80.0
按上表的各组分重量配方，将去离子水、六偏磷酸钠、十二烷基苯磺酸钠、三乙醇胺、异噻唑啉酮、丙三醇和苯并三氮唑依次加入，放入放在转速为80-120转/分钟反应釜中进行加热搅拌，当温度达到60°C时，加入纳米二氧化钛，保温并持续搅拌30分钟，随后停止加热继续搅拌至室温，得到白色悬浊状液体，但根据配方3所配成所需水基轧制液静置48小时以后出现大量TiO2沉淀，使用时需要搅拌。
二、制得的产品性能指标如下：
Figure 2013100023009100002DEST_PATH_IMAGE002

Claims (2)

1.一种含纳米TiO2的水基热轧轧制液，其特征在于选择具有缓蚀防锈性能优良的纳米TiO2作为极压剂，选用六偏磷酸钠和十二烷基苯磺酸钠作为分散剂，将纳米TiO2均匀稳定的分散到水中，配制成具有缓蚀防锈性能的水基纳米热轧轧制液；主要组分及所占重量百分比如下：
序号 组分名称 重量百分比（100%） 1 纳米二氧化钛 0.2-1.0 2 六偏磷酸钠 0.5-2.0 3 十二烷基苯磺酸钠 1.0-3.0 4 三乙醇胺 1.0-3.0 5 异噻唑啉酮 0.5-1.0 6 丙三醇 10-15.0 7 苯并三氮唑 0.5-1.0 8 去离子水 80～86
。
2.如权利要求1所述一种含纳米TiO2的水基热轧轧制液的制作方法，其特征在于：将去离子水、六偏磷酸钠、十二烷基苯磺酸钠、三乙醇胺、异噻唑啉酮、丙三醇和苯并三氮唑依次加入，放入放在转速为80-120转/分钟反应釜中进行加热搅拌，当温度达到50～70°C时，加入纳米二氧化钛，保温并持续搅拌30-45分钟，随后停止加热继续搅拌至室温，得到白色悬浊状液体，即配成所需水基轧制液。
CN201310002300.9A 2013-01-05 2013-01-05 一种含纳米TiO2的水基热轧轧制液及其制备方法 Active CN103013642B (zh)