CN102604238A - 汽车散热管路耐高温橡胶材料的制备方法 - Google Patents

汽车散热管路耐高温橡胶材料的制备方法 Download PDF

Info

Publication number
CN102604238A
CN102604238A CN201210060251XA CN201210060251A CN102604238A CN 102604238 A CN102604238 A CN 102604238A CN 201210060251X A CN201210060251X A CN 201210060251XA CN 201210060251 A CN201210060251 A CN 201210060251A CN 102604238 A CN102604238 A CN 102604238A
Authority
CN
China
Prior art keywords
rubber
agent
prescription
temperature
banbury mixer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201210060251XA
Other languages
English (en)
Other versions
CN102604238B (zh
Inventor
冯一东
尤建义
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO TIP RUBBER TECHNOLOGY Co Ltd
Original Assignee
NINGBO TIP RUBBER TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO TIP RUBBER TECHNOLOGY Co Ltd filed Critical NINGBO TIP RUBBER TECHNOLOGY Co Ltd
Priority to CN201210060251XA priority Critical patent/CN102604238B/zh
Publication of CN102604238A publication Critical patent/CN102604238A/zh
Application granted granted Critical
Publication of CN102604238B publication Critical patent/CN102604238B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种汽车散热管路耐高温橡胶材料的制备方法，包括配方、制备工艺。本发明采用三元乙丙橡胶与氯磺化聚乙烯橡胶并用，在配方中采用过氧化二异丙苯、N，N’-间苯撑双马来酰亚胺的硫化体系，在配方中加入2，2，4-三甲基-1，2-二氢化喹啉聚合体和2-巯基苯并咪唑的防老剂，在配方中加入氧化镁，以提高材料的耐热性能；并配套以相应制备工艺的技术方案，克服了现有技术存在耐高温性能低，难以满足汽车工业对橡胶制品日益增高耐热要求的问题与不足，通过制备出具备耐175℃高温性能的橡胶材料，使所制作的汽车散热管路橡胶制品达到了提高耐热性能，满足汽车工业对橡胶制品日益增高的耐热需求，符合耐高温标准的目的。

Description

汽车散热管路耐高温橡胶材料的制备方法
技术领域
本发明涉及一种橡胶材料的制备方法，具体是指用于制造的汽车散热管路橡胶制品，具备耐175℃高温性能的一种汽车散热管路耐高温橡胶材料的制备方法。
背景技术
现有技术橡胶材料制作的汽车散热管路等橡胶制品的耐热性能低，无法满足175℃高温标准要求；
现有技术的三元乙丙橡胶材料制作的汽车散热管路橡胶制品的试验数据如下：
标准规范
Figure BSA00000682173800011
结论：结论：第2、耐热空气老化项目中的2.1硬度变化、2.2拉伸强度变化、2.3扯断伸长率变化不合格；
因此，现有技术存在耐高温性能低，难以满足汽车工业对橡胶制品日益增高要求的问题与不足。
发明内容
针对上述现有技术存在的问题与不足，本发明采用三元乙丙橡胶并用氯磺化聚乙烯橡胶，以提高材料的耐热性能；在配方中采用过氧化二异丙苯、N，N’-间苯撑双马来酰亚胺的硫化体系，以提高材料的耐热性能；在配方中加入2，2，4-三甲基-1，2-二氢化喹啉聚合体和2-巯基苯并咪唑的防老剂，以提高材料的耐热性能；在配方中加入氧化镁，以提高材料的耐热性能；并配套以相应制备工艺的技术方案，提供一种汽车散热管路耐高温橡胶材料的制备方法，旨在制备出具备耐175℃高温性能的橡胶材料，使所制作的汽车散热管路橡胶制品达到提高耐热性能，满足汽车工业对橡胶制品日益增高的需求，符合高温标准的目的。
本发明的目的是这样实现的：一种汽车散热管路耐高温橡胶材料的制备方法，包括配方、制备工艺，其中：
所述的配方为，
橡胶原料：三元乙丙橡胶，47.33％；氯磺化聚乙烯橡胶，4.73％；
补强剂：高耐磨炉黑，14.20％；快压出炉黑，9.46％；白炭黑，7.10％；
增塑剂：石蜡油，2.37％；
活性剂：氧化镁，9.47％；硬脂酸，0.47％；
硫化剂：过氧化二异丙苯，3.08％；N，N’-间苯撑双马来酰亚胺，0.14％；
防老剂：2，2，4-三甲基-1，2-二氢化喹啉聚合体，1.18％；2-巯基苯并咪唑，0.47％；
配方单位为重量百分比；
所述的制备工艺为混炼；
步骤一、密炼机通水冷却，控制密炼机工作室温度＜100℃，转速：32转/分钟，将配方中的橡胶原料及补强剂、增塑剂、活性剂、防老剂投入到密炼机中，密炼用时5～6分钟，胶温控制在150℃以下排胶，然后在开放式炼机上出片、冷却至室温，获得母炼胶，待用；
步骤二、将母炼胶投入到密炼机中，均匀加入配方中的硫化剂混炼，混炼用时2分钟，胶温控制在110℃以下排胶，然后在开放式炼胶机上出片、冷却，静置8小时～240小时，获得供制作汽车散热管路等制品使用的耐175℃高温的混炼橡胶材料。
用本发明制备的橡胶材料所制造的汽车散热管路，经各项机械强度及理化指标的检测，均符合GB/T531、GB/T528、GB/T3512试验标准，并满足ELV指令要求。
上述，本发明采用三元乙丙橡胶并用氯磺化聚乙烯橡胶，在配方中采用过氧化二异丙苯、N，N’-间苯撑双马来酰亚胺的硫化体系，在配方中加入2，2，4-三甲基-1，2-二氢化喹啉聚合体和2-巯基苯并咪唑的防老剂，在配方中加入氧化镁，以提高材料的耐热性能；并配套以相应制备工艺的技术方案，克服了现有技术存在耐高温性能低，难以满足汽车工业对橡胶制品日益增高耐热要求的问题与不足，所提供的一种汽车散热管路耐高温橡胶材料的制备方法，通过制备出具备耐175℃高温性能的橡胶材料，使所制作的汽车散热管路橡胶制品达到了提高耐热性能，满足汽车工业对橡胶制品日益增高的耐热需求，符合耐高温标准的目的。
实施例说明
以下通过具体实施例对本发明的汽车散热管路耐高温橡胶材料的制备方法作进一步详细说明，所属领域的技术人员可以参照实施例的配方及制备方法制得耐高温汽车散热管路橡胶材料，但不应理解为对本发明的任何限制。
具体实施方式
实施例
品名：汽车散热管路用耐175℃高温的橡胶材料
配方：配方单位为重量百分比；
橡胶原料：三元乙丙橡胶，47.33％；氯磺化聚乙烯橡胶，4.73％；
补强剂：高耐磨炉黑，14.20％；快压出炉黑，9.46％；白炭黑，7.10％；
增塑剂：石蜡油，2.37％；
活性剂：氧化镁，9.47％；硬脂酸，0.47％；
硫化剂：过氧化二异丙苯，3.08％；N，N’-间苯撑双马来酰亚胺，0.14％；
防老剂：2，2，4-三甲基-1，2-二氢化喹啉聚合体，1.18％；2-巯基苯并咪唑，0.47％；
制备：
制备条件、设备
环境气压：一个大气压；
环境温度：室温；
制备设备：18时开炼机、55L加压式密炼机；
制备工艺：混炼；
步骤一、密炼机通水冷却，控制密炼机工作室温度＜100℃，转速：32转/分钟，将配方中的橡胶原料及补强剂、增塑剂、活性剂、防老剂投入到密炼机中，密炼用时5～6分钟，胶温控制在150℃以下排胶，然后在开放式炼机上出片、冷却至室温，获得母炼胶，待用；
步骤二、将母炼胶投入到密炼机中，均匀加入配方中的硫化剂混炼，混炼用时2分钟，胶温控制在110℃以下排胶，然后在开放式炼胶机上出片、冷却，静置8小时～240小时，获得汽车散热管路用耐175℃高温的橡胶材料。
试验
用本发明制备的橡胶材料所制造的汽车散热管路的试验数据如下：
标准规范
Figure BSA00000682173800041
结论：本发明的制品的实测结果：符合上述标准要求。

Claims (1)

1.一种汽车散热管路耐高温橡胶材料的制备方法，其特征在于：包括配方、制备工艺，其中：所述的配方为，
橡胶原料：三元乙丙橡胶，47.33％；氯磺化聚乙烯橡胶，4.73％；
补强剂：高耐磨炉黑，14.20％；快压出炉黑，9.46％；白炭黑，7.10％；
增塑剂：石蜡油，2.37％；
活性剂：氧化镁，9.47％；硬脂酸，0.47％；
硫化剂：过氧化二异丙苯，3.08％；N，N’-间苯撑双马来酰亚胺，0.14％；
防老剂：2，2，4-三甲基-1，2-二氢化喹啉聚合体，1.18％；2-巯基苯并咪唑，0.47％；
配方单位为重量百分比；
所述的制备工艺为混炼；
步骤一、密炼机通水冷却，控制密炼机工作室温度＜100℃，转速：32转/分钟，将配方中的橡胶原料及补强剂、增塑剂、活性剂、防老剂投入到密炼机中，密炼用时5～6分钟，胶温控制在150℃以下排胶，然后在开放式炼机上出片、冷却至室温，获得母炼胶；
步骤二、将母炼胶投入到密炼机中，均匀加入配方中的硫化剂混炼，混炼用时2分钟，胶温控制在110℃以下排胶，然后在开放式炼胶机上出片、冷却，静置8小时～240小时。
CN201210060251XA 2012-02-29 2012-02-29 汽车散热管路耐高温橡胶材料的制备方法 Expired - Fee Related CN102604238B (zh)