CN102219264A - 自蔓延燃烧法制备Ca2Fe2O5超细粉的方法 - Google Patents

自蔓延燃烧法制备Ca2Fe2O5超细粉的方法 Download PDF

Info

Publication number
CN102219264A
CN102219264A CN2011100592049A CN201110059204A CN102219264A CN 102219264 A CN102219264 A CN 102219264A CN 2011100592049 A CN2011100592049 A CN 2011100592049A CN 201110059204 A CN201110059204 A CN 201110059204A CN 102219264 A CN102219264 A CN 102219264A
Authority
CN
China
Prior art keywords
ultrafine powder
ca2fe2o5
solution
self
urea
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100592049A
Other languages
English (en)
Inventor
王芬
赵春
朱建锋
杨海波
林营
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi University of Science and Technology
Original Assignee
Shaanxi University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shaanxi University of Science and Technology filed Critical Shaanxi University of Science and Technology
Priority to CN2011100592049A priority Critical patent/CN102219264A/zh
Publication of CN102219264A publication Critical patent/CN102219264A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种Ca2Fe2O5的超细粉的制备，具体涉及一种自蔓延燃烧制备Ca2Fe2O5的超细粉的方法。以硝酸钙和硝酸铁为原料，将硝酸钙和硝酸铁配成同浓度溶液，按1∶1比例均匀混合，再在混合溶液中加尿素作为助燃剂，尿素加入料量∶Fe＝1∶1。然后将上述溶液在超声30min，取出在马弗炉中加热，直接加热到500-800℃，不要保温。便可得到Ca2Fe2O5的超细粉。本发明通过调整溶液浓度，尿素量，和加热温度来改变得到的Ca2Fe2O5的超细粉结构参数、颗粒尺寸、形貌情况。

Description

自蔓延燃烧法制备Ca2Fe2O5超细粉的方法
技术领域
本发明涉及一种Ca2Fe2O5超细粉的制备方法，具体涉及一种自蔓延燃烧法制备Ca2Fe2O5的超细粉的方法。
背景技术
Ca2Fe2O5是含有氧缺陷的钙钛矿型氧化物，属于P型半导体的一种。开始时，这类材料主要用于工业催化材料，磁性材料，压敏材料和高温超导材料。随着对高转换率环境友好性能源的需求，发展了第四代电池技术-固体燃料电池。研究人员发现这类材料不仅具有离子-电子混合导电性能，同时具有高催化性和高稳定性，因此可以用于制备固体燃料电池阴极材料，以代替钴基阴极材料。这类材料还可以做光生电池等。
粉体是材料制备关键，因为粉体的颗粒尺寸、颗粒分布、表面形貌、晶相种类及结构、还有比表面积、气孔率等都会影响材料后续制备工艺及使用性能。
目前主要用溶胶凝胶法制备Ca2Fe2O5超细粉体，这种方法凝胶时间长，干燥后粉体多个温度处理，操作要求高。原料一般为草酸盐，柠檬酸盐成本高。自蔓延燃烧法与它比起其来，不仅工艺操作简单，而且成本低，能耗小。
发明内容
本发明的目的在于克服现有技术的不足，提供了一种低成本、操作简单的自蔓延燃烧法制备Ca2Fe2O5超细粉的方法。
为达上述目的，本发明采用的技术方案是：
1)将硝酸钙和硝酸铁均配成0.1mol/l的溶液；
2)按1∶1的体积比将硝酸钙溶液和硝酸铁溶液混合均匀，再向混合溶液中按尿素∶Fe＝1-2∶1的质量比加入尿素作为助燃剂得混合溶液；
3)将混合溶液超声搅拌30min，取出后在马弗炉于500-800℃加热得到结构参数不同、颗粒尺寸不同、形貌变化的Ca2Fe2O5的超细粉。
本发明通过调整溶液浓度，尿素量，和加热温度来改变得到的Ca2Fe2O5的超细粉结构参数、颗粒尺寸、形貌情况。
附图说明
图1是按照本发明的制备方法将0.1mol/1溶液加热到800℃合成Ca2Fe2O5XRD图谱。
具体实施方式
实施例1：1)将硝酸钙和硝酸铁均配成0.1mol/l的溶液；
2)按1∶1的体积比将硝酸钙溶液和硝酸铁溶液混合均匀，再向混合溶液中按尿素∶Fe＝1∶1的质量比加入尿素作为助燃剂得混合溶液；
3)将混合溶液超声搅拌30min，取出后在马弗炉于800℃加热得到铁红色的Ca2Fe2O5的超细粉，其XRD图谱见图1。
实施例2：本实施例步骤3)马弗炉加热温度为700℃得到深灰偏红色的Ca2Fe2O5的超细粉，其它步骤同实施例1。
实施例3：本实施例步骤3)马弗炉加热温度为600℃得到灰色的Ca2Fe2O5的超细粉，其它步骤同实施例1。
实施例4：本实施例步骤3)马弗炉加热温度为500℃得到黄土色的Ca2Fe2O5的超细粉，其它步骤同实施例1。
实施例5：1)将硝酸钙和硝酸铁均配成0.1mol/l的溶液；
2)按1∶1的体积比将硝酸钙溶液和硝酸铁溶液混合均匀，再向混合溶液中按尿素∶Fe＝2∶1的质量比加入尿素作为助燃剂得混合溶液；
3)将混合溶液超声搅拌30min，取出后在马弗炉于800℃加热得到铁红色的Ca2Fe2O5的超细粉。
实施例6：本实施例步骤3)马弗炉加热温度为700℃得到深灰偏红色的Ca2Fe2O5的超细粉，其它步骤同实施例5。
实施例7：本实施例步骤3)马弗炉加热温度为600℃得到灰色的Ca2Fe2O5的超细粉，其它步骤同实施例5。
实施例8：本实施例步骤3)马弗炉加热温度为500℃得到灰色的Ca2Fe2O5的超细粉，其它步骤同实施例5。
将实例1-4与实例5-8对比，实例5-8得到的产物颜色较深。

Claims (1)

1.自蔓延燃烧法制备Ca2Fe2O5超细粉，其特征在于：
1)将硝酸钙和硝酸铁均配成0.1mol/l的溶液；
2)按1∶1的体积比将硝酸钙溶液和硝酸铁溶液混合均匀，再向混合溶液中按尿素∶Fe＝1-2∶1的质量比加入尿素作为助燃剂得混合溶液；
3)将混合溶液超声搅拌30min，取出后在马弗炉于500-800℃加热得到结构参数不同、颗粒尺寸不同、形貌变化的Ca2Fe2O5的超细粉。
CN2011100592049A 2011-03-14 2011-03-14 自蔓延燃烧法制备Ca2Fe2O5超细粉的方法 Pending CN102219264A (zh)