CN101462876A - 一种氧化锆陶瓷纤维板的制备方法 - Google Patents
一种氧化锆陶瓷纤维板的制备方法 Download PDFInfo
- Publication number
- CN101462876A CN101462876A CNA2009100137821A CN200910013782A CN101462876A CN 101462876 A CN101462876 A CN 101462876A CN A2009100137821 A CNA2009100137821 A CN A2009100137821A CN 200910013782 A CN200910013782 A CN 200910013782A CN 101462876 A CN101462876 A CN 101462876A
- Authority
- CN
- China
- Prior art keywords
- zirconium
- preparation
- zirconia ceramic
- yttrium
- ceramic beaverboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (9)