CN101161603A - 一种低热膨胀系数的堇青石质瓷电熨斗底板 - Google Patents
一种低热膨胀系数的堇青石质瓷电熨斗底板 Download PDFInfo
- Publication number
- CN101161603A CN101161603A CNA2006100324129A CN200610032412A CN101161603A CN 101161603 A CN101161603 A CN 101161603A CN A2006100324129 A CNA2006100324129 A CN A2006100324129A CN 200610032412 A CN200610032412 A CN 200610032412A CN 101161603 A CN101161603 A CN 101161603A
- Authority
- CN
- China
- Prior art keywords
- percent
- bottom plate
- steinheilite
- electric iron
- yttrium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种低热膨胀系数堇青石质瓷电熨斗底板，它是以堇青石(2MgO·2Al2O3·SiO2)为主晶相，辅加以工业三氧化二铝、二氧化钛、碳酸锶、氧化钇和二氧化硅，该材料组成的重量百分配比为：堇青石：82－88％；三氧化二铝：3－6％；碳酸锶：2－3％；二氧化钛：3－6％；氧化钇：0－2％；二氧化硅：1－3％；该陶瓷材料制做按上述配方称取原料经干磨混料，然后按热压铸生产工艺进行成型和烧成，最后对陶瓷底板工作面进行研磨抛光即制成电熨斗陶瓷底板，它可有效提高电熨斗底板的硬度和表面光洁度，有利于高档布料的熨烫。
Description
所属技术领域
本发明涉及一种陶瓷新材质。特别是涉及电熨斗底板用低热膨胀系数的陶瓷材料。
背景技术
人们知道，堇青石瓷的主要晶相是2MgO·2Al2O3·5SiO2，其离子排列不紧密，晶格内有巨大空腔，但是正由于它的结构疏松，热膨胀系数非常小，因此热稳定性好。目前人们使用的电熨斗的底板一般都是采用金属材料制成，但一般的金属材料与陶瓷材料相比有一个无法克服的缺点：材料硬度低，一但稍有碰撞或出现划痕，就会影响熨斗的使用，对布料造成损伤，特别是对高档布料而言更加严重，而用一般的结构陶瓷材料制成电熨斗底板，这些陶瓷材料热膨胀系数大，经不起急冷急热的冲击，再有现在使用的电熨斗其实都是采用电加热蒸汽熨烫已非传统上通过底板传热方法来熨衣服的方式了，因此对底板材料的热传导要求已大大降低。由此可见，传统的金属材质电熨斗底板存在硬度低易损伤、表面光洁度低不适宜熨烫高级布料等缺陷，同时抗老化性差。
发明内容
为了克服一般陶瓷材料抗热冲击性能差和金属材料硬度低的缺陷，本发明提供一种低热膨胀系数的堇青石质瓷材料，该陶瓷材料做为电熨斗底板具有抗热冲击性好，硬度高，经研磨抛光后表面光洁度高的特点，能更有利于熨烫高级衣料。
本发明解决其技术问题所采用的技术方案是：以堇青石为主要材料组成，配加工业三氧化二铝、碳酸锶、二氧化钛、氧化钇和二氧化硅等组份。
该低热膨胀系数堇青石质瓷配方重量百分组成是：
堇青石：82-88％；三氧化二铝：3-6％；碳酸锶：2-3％；
二氧化钛：3-6％；氧化钇：0-2％；二氧化硅：1-3％；
配方中堇青石采用下列配方合成：苏州土：74％，海城滑石：10％，菱镁矿：16％。
加入三氧化二铝是工业用三氧化二铝，主要是为了增加该材料的强度，加入二氧化钛是增加堇青石主晶相的晶格疏松度，从而使材料的热膨胀糸数更低。加入碳酸锶、氧化钇、二氧化硅是为了增大材料的烧成温度范围。
本发明的有益效果是，由于在堇青石中添加了二氧化钛和三氧化二铝，降低了该材质的热膨胀系数和强度，从而使该瓷质耐热冲击性更好，硬度更高，研磨抛光后表面光洁度更亮。
具体实施方式
首先按下列原料重要百分组成称取原料，即：堇青石：85％；三氧化二铝：5％；碳酸锶：3％；二氧化钛：4％；氧化钇：2％；二氧化硅：1％；
配料后工艺流程如下：干磨混料，加入石蜡制成蜡饼，存放一定时间后熔化加入热压铸机中进行模压成型，再经排蜡和高温烧结，最后进行工作表面研磨抛光即可。
Claims (1)
1.一种低热膨胀系数堇青石质瓷，它由堇青石、三氧化二铝、二氧化钛、碳酸锶、氧化钇和二氧化硅组成，其特征是：该陶瓷材料组成配比为：
原料 配比(wt％)
堇青石 82-88％
二氧化铝 3-6％
碳酸锶 2-3％
二氧化钛 3-6％
氧化钇 0-2％
二氧化硅 1-3％。