CN101016669B - 一种具有形状物理记忆性功能面料的制备工艺 - Google Patents
一种具有形状物理记忆性功能面料的制备工艺 Download PDFInfo
- Publication number
- CN101016669B CN101016669B CN2007100197626A CN200710019762A CN101016669B CN 101016669 B CN101016669 B CN 101016669B CN 2007100197626 A CN2007100197626 A CN 2007100197626A CN 200710019762 A CN200710019762 A CN 200710019762A CN 101016669 B CN101016669 B CN 101016669B
- Authority
- CN
- China
- Prior art keywords
- fabric
- shape
- preparation technology
- shaping
- described step
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种具有形状物理记忆性功能面料的制备工艺，包括：(一)经、纬纱线原料的选择及纤维原料的预处理；(二)织物组织的设计、织造，以及织物坯布的预处理；(三)织物的染色与整理；(四)成品织物的烘干和定型等。本发明制得的各种组织的具有形状物理记忆性功能面料，不仅柔软而厚实，透气而保暖，且起绉效果好，具有极佳的褶裥保形效果。织物具有良好形状、结构稳定性、立体感强外，易于抚平，织物达到免烫效果，具有良好的形状物理记忆性能。
Description
技术领域
本发明涉及一种纺织面料，特别是具有形状物理记忆性功能面料的制备工艺。
背景技术
随着社会经济的快速发展，人们的生活水平不断的提高，多功能、舒适性的服装越来越受到消费者的青睐，消费者对面料的功能性要求也越来越高。近年来国内外市场呈现出对各种形状物理性记忆功能面料的追求。形状记忆织物主要有聚合物织物和记忆合金织物，织物的构成方式有机织物、针织物和非织造织物等。
CN 1159498介绍了一种织物和成衣形状记忆处理剂，处理后的织物或成衣洗可穿级别大于3.5级，褶裥防皱大于4级。CN 1519416A介绍了一种织物物理抗皱保形的加工方法，通过对热熔复合纤维织物或成衣进行热压烫后，皮层共聚酯部分受热熔融，与其接触的纤维发生粘结，从而赋予织物持久的抗皱保形和褶裥保持性。目前形状记忆面料的研究和发展仍处于起步阶段，更多的还是通过后整理或借助合金织物来达到织物的记忆效果。
聚对苯二甲酸丙二醇酯(PTT)作为一种新型的聚酯产品，具有优良的理化性能。在化纤应用领域中，PTT纤维综合了锦纶的柔性和色牢度、腈纶的蓬松性、涤纶的抗污性，加上PTT纤维本身固有的弹性，将各种纤维的优良服用性能集于一体。本发明专利的创新之处在于通过采用特殊加工方法制得的具有形状记忆特性的PTT纤维，制得的面料经过特殊的染整后处理，体现出面料良好的形状物理性记忆效果。这主要因PTT纤维本身由大分子结构所赋予的独特柔性或者PTT纤维所特有的低模量的趋向，加上合适的纤维集合方式(这里主要是指织物组织结构)，获得一种具有特殊形状记忆风格的织物面料，面料除了保持PTT一些特有的优良特性外，更是在首创了PTT纤维在形状物理记忆性面料上的开发与应用。
发明内容
本发明的目的是：提供了一种具有形状物理记忆性功能面料的制备工艺，采用聚对苯二甲酸丙二醇酯(PTT)形状记忆纤维织成的织物面料更易于护理和保型功能、穿着更舒适、以及具有褶皱的易于保持和恢复功能。
本发明的技术方案是：一种具有形状物理记忆性功能面料的制备工艺，包括纤维选用及预处理、坯布织造及处理、染色整理、烘干定型等工序，其特征是采用的原料为聚对苯二甲酸丙二醇酯制得的具有形状记忆特性的长丝，纤度范围22dtex～222dtex；其中该长丝的预处理的工艺条件为纤维加捻200～1800捻/米，捻丝的定型温度60～150℃，捻丝的定型时间20～150分钟；织物的经纬纱线可以全部或经纱或纬纱至少一种选用聚对苯二甲酸丙二醇酯制得的具有形状物理记忆特性的长丝；坯布在40～80℃条件下进行预处理及适量的碱减量处理；织物使用低温分散染料在80～115℃的条件下进行染色；染色后织物经过洗涤，最终经过120～170℃的烘干定型，进布速度8～16米/分钟，定型时间30～80秒。上述所选用的原料为聚对苯二甲酸丙二醇酯制得的具有形状记忆特性的长丝，应具有良好的伸张及伸张回复性能，具有低模量柔软的手感等；所采用的原料为聚对苯二甲酸丙二醇酯制得的具有形状记忆特性的长丝，更合适的纤度范围44dtex～167dtex；PTT形状记忆纤维的预处理条件，更合适加捻600～1200捻/米，捻丝定型温度更合适为100～130℃，捻丝的定型时间更合适为45～90分钟；更合适的织物组织结构为各种复杂变化组织；在原料的选用上更合适经纬纱均选用具有现状记忆特性的PTT纤维；坯布的染色前处理，更合适的温度条件为60～80℃，控制碱减量在小于5％的范围内：织物更合适的染色温度控制在95～100℃；成品最终定型温度更合适为125～145℃。
纤度为44～167dtex的具有形状记忆特性的PTT纤维，采用美国杜邦专利的Sorona聚合物制成，制得的具有形状物理记忆性功能面料，起皱效果好，且易抚平，立体感强，达到免烫效果。该形状记忆面料由PTT形状记忆特性的长丝纱作为经、纬纱交织而成，故面料不但保留了PTT织物的柔性和色牢度、蓬松性、抗污性，同时具有独特的形状记忆的风格。这种风格为褶皱的易于保持和恢复性能，而普通纤维服用面料或者PTT常规纤维织物在这方面是难以达到的。
本发明的优点是：
1.该工艺选用具有形状记忆特性的聚对苯二甲酸丙二醇酯长丝、生产的具有形状物理记忆性功能的各种组织面料，不仅柔软而厚实，透气而保暖，且起绉效果好，具有极佳的褶裥保形效果。
2.本发明制得的纤维除了具有良好的褶裥保形效果，良好的织物形状、结构稳定性、立体感强外，易于抚平，织物达到免烫效果，具有良好的形状物理记忆性能。
下面结合实施例对本发明作进一步描述：
具体实施方式
实施例一：
一种提花网眼黑色形状物理记忆性功能面料的制备工艺，经纬纱均选用105dtex/74f的具有形状记忆特性的聚对苯二甲酸丙二醇酯全牵伸丝。
纤维的预处理：纤维经过倍捻达到600～800捻/米，捻丝在120℃定型45min；
织造：经纱整经后，采用喷水织机进行织造，经密200根/英寸，纬密110根/英寸，幅宽160厘米，制成坯布。
坯布预处理：在温度70℃，时间30～50分钟，加入氢氧化钠及相关助剂；
染色：在50℃时加入汽巴公司产低温分散染料、染色助剂及匀染剂，用冰醋酸等调节PH值在6～7，按1.0℃/分钟升至98℃，保温40分钟。随后按照1.0℃/分钟降温至50℃。用清水洗涤及还原清洗。
定型：织物最终经过130℃的定型，走布速度30米/分钟，幅宽147厘米，即得本发明的具有形状物理记忆性功能面料。
织物厚实有身骨，起绉效果好，且易于抚平，达到了免烫效果。此外，织物纹路清晰、颗粒饱满，立体感强，适于男士休闲夹克、女装套裙等。
实施例二：
一种斜纹咖啡色形状物理记忆性功能面料的制备工艺，经纱选用83dtex/48f的具有形状记忆特性的聚对苯二甲酸丙二醇酯全牵伸丝，纬纱则选用83dtex/48f的具有形状记忆特性的聚对苯二甲酸丙二醇酯牵伸假捻丝。
纤维的预处理：经纬纱线均经过倍捻达到600～800捻/米，捻丝在120℃定型55分钟；
织造：经纱整经后，采用喷水织机进行织造，经密203根/英寸，纬密102根/英寸，幅宽160厘米，制成坯布。
坯布预处理：在温度65℃，时间30～50分钟，加入氢氧化钠及相关助剂；
染色：在50℃时加入汽巴公司产低温分散染料、染色助剂及匀染剂，用冰醋酸等调节PH值在6～7，按1.0℃/分钟升至95℃，保温35分钟。随后按照1.0℃/分钟降温至50℃。用清水洗涤及还原清洗。
定型：织物最终经过135℃定型，走布速度26米/分钟，幅宽151厘米，即得本发明的具有形状物理记忆性功能面料。
织物柔软厚实，斜纹纤侵袭明显。织物具有极好的起绉效果好，且平整恢复性极佳。适合于做外套、休闲服饰及各类童装。
实施例三：
一种平纹天蓝色形状物理记忆性功能面料的制备工艺，经纱选用83dtex/72f的具有形状记忆特性的聚对苯二甲酸丙二醇酯全牵伸丝；纬纱选用83dtex/72f的聚对苯二甲酸低弹高网络丝。
纤维的预处理：经纱经过倍捻达到600～800捻/米，捻丝在115℃定型60分钟；
织造：经纱整经后，采用喷水织机进行织造，经密203根/英寸，纬密102根/英寸，幅宽160厘米，制成坯布。
坯布预处理：在温度80℃，时间30～50分钟，加入氢氧化钠及相关助剂；
染色：在50℃时加入汽巴公司产低温分散染料、染色助剂及匀染剂，用冰醋酸等调节PH值在6～7，按1.0℃/分钟升至95℃，保温35分钟。随后按照1.0℃/分钟降温至50℃。用清水洗涤及还原清洗。
定型：织物最终经过145℃定型，走布速度22米/分钟，幅宽144厘米，即得本发明的具有形状物理记忆性功能面料。
织物布面平坦，身骨挺括，织物坚牢。织物具有良好的形状物理记忆性功能，但效果与实例一和实例二比较略差。适合做男女衬衫、夏季外衣等。
Claims (4)
1.一种具有形状物理记忆性功能面料的制备工艺，包括下列步骤：
(1)纤维的选用及预处理；
(2)坯布织造及预处理；
(3)染色整理；
(4)烘干定型；
其特征在于：所述的步骤(1)中，至少经、纬纱线中的一种选用具有形状记忆特性的聚对苯二甲酸丙二醇酯长丝，纤度范围在22dtex～222dtex；具有形状记忆特性的聚对苯二甲酸丙二醇酯长丝的预处理条件为：加捻200～1800捻/米，捻丝定型温度60～150℃，捻丝的定型时间20～150分钟。
2.根据权利要求1所述的形状物理记忆性面料的制备工艺，其特征在于：所述的步骤(2)中，坯布在40～80℃条件下进行预处理及适量的碱减量处理。
3.根据权利要求1所述的形状物理记忆性面料的制备工艺，其特征在于：所述的步骤(3)中，织物使用低温分散染料在80～115℃的条件下进行染色，染色工艺过程：在45℃时加入低温分散性染料、助剂及匀染剂，按1℃/min的升温速度升至95℃，保温30～60min左右，再按1℃/min降温速率降温至45℃，清水洗涤，还原清洗；用冰醋酸调节PH值在5～7。
4.根据权利要求1所述的形状物理记忆性面料的制备工艺，其特征在于：所述的步骤(4)中，经过染色处理后的织物，最终经过120～170℃的烘干定型，进布速度8～16米/分钟，定型时间30～80秒。