CN100371383C - 氟碳弹性组合物的固化方法和固化的含氟弹性体及其制品 - Google Patents

氟碳弹性组合物的固化方法和固化的含氟弹性体及其制品 Download PDF

Info

Publication number
CN100371383C
CN100371383C CNB988016680A CN98801668A CN100371383C CN 100371383 C CN100371383 C CN 100371383C CN B988016680 A CNB988016680 A CN B988016680A CN 98801668 A CN98801668 A CN 98801668A CN 100371383 C CN100371383 C CN 100371383C
Authority
CN
China
Prior art keywords
polyol
linking agent
cured fluoroelastomer
mixture
vinylidene fluoride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB988016680A
Other languages
English (en)
Chinese (zh)
Other versions
CN1243529A (zh
Inventor
A·T·沃尔姆
M·A·格拉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
Minnesota Mining and Manufacturing Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining and Manufacturing Co filed Critical Minnesota Mining and Manufacturing Co
Publication of CN1243529A publication Critical patent/CN1243529A/zh
Application granted granted Critical
Publication of CN100371383C publication Critical patent/CN100371383C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L27/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers
    • C08L27/02—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment
    • C08L27/12—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a halogen; Compositions of derivatives of such polymers not modified by chemical after-treatment containing fluorine atoms
    • C08L27/16—Homopolymers or copolymers or vinylidene fluoride
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/24—Crosslinking, e.g. vulcanising, of macromolecules
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
    • C08K5/0025—Crosslinking or vulcanising agents; including accelerators

Landscapes

  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Processes Of Treating Macromolecular Substances (AREA)
CNB988016680A 1997-01-06 1998-01-06 氟碳弹性组合物的固化方法和固化的含氟弹性体及其制品 Expired - Fee Related CN100371383C (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US08/779,297 US5891965A (en) 1997-01-06 1997-01-06 Low temperature perfluoroether-containing fluoroelastomers
US08/779,297 1997-01-06
PCT/US1998/000098 WO1998030631A1 (en) 1997-01-06 1998-01-06 Perfluoroether-containing fluoroelastomers with good low temperature characteristics

Related Child Applications (1)

Application Number Title Priority Date Filing Date
CNB031594441A Division CN1215117C (zh) 1997-01-06 1998-01-06 具有良好低温特性的氟碳弹性组合物

Publications (2)

Publication Number Publication Date
CN1243529A CN1243529A (zh) 2000-02-02
CN100371383C true CN100371383C (zh) 2008-02-27

Family

ID=25115949

Family Applications (2)

Application Number Title Priority Date Filing Date
CNB988016680A Expired - Fee Related CN100371383C (zh) 1997-01-06 1998-01-06 氟碳弹性组合物的固化方法和固化的含氟弹性体及其制品
CNB031594441A Expired - Fee Related CN1215117C (zh) 1997-01-06 1998-01-06 具有良好低温特性的氟碳弹性组合物

Family Applications After (1)

Application Number Title Priority Date Filing Date
CNB031594441A Expired - Fee Related CN1215117C (zh) 1997-01-06 1998-01-06 具有良好低温特性的氟碳弹性组合物

Country Status (9)

Country Link
US (1) US5891965A (enExample)
EP (1) EP0950078B1 (enExample)
JP (1) JP4134283B2 (enExample)
KR (1) KR100516575B1 (enExample)
CN (2) CN100371383C (enExample)
AU (1) AU6016298A (enExample)
CA (1) CA2274775C (enExample)
DE (1) DE69801981T2 (enExample)
WO (1) WO1998030631A1 (enExample)

Families Citing this family (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE69914923T2 (de) * 1998-08-21 2004-12-09 Dupont Dow Elastomers L.L.C., Wilmington Fluoroelastomerzusammensetzung mit exzellenter verarbeitbarkeit und gute eigenschaften bei niedrigen temperaturen
US6294627B1 (en) * 1998-08-31 2001-09-25 Dyneon Llc Low temperature fluorocarbon elastomers
US6255535B1 (en) 1999-12-22 2001-07-03 Dyneon Llc Fluorine containing allylethers and higher homologs
US6482979B1 (en) 1999-12-22 2002-11-19 Dyneon Llc Perfluorinated acid fluorides and preparation thereof
US6890995B2 (en) * 2001-01-31 2005-05-10 3M Innovative Properties Company Fluoropolymer compositions
US6794457B2 (en) * 2001-04-30 2004-09-21 3M Innovative Properties Company Fluoropolymer curing system containing a nitrogen cure site monomer
CN100471877C (zh) * 2003-12-30 2009-03-25 3M创新有限公司 含氟聚合物的凝聚方法及组合物
ITMI20041571A1 (it) * 2004-07-30 2004-10-30 Solvay Solexis Spa Perfluoroelastomeri
US7402630B2 (en) * 2004-12-16 2008-07-22 3M Innovative Properties Company Curing compositions for fluoropolymers
GB0427913D0 (en) * 2004-12-21 2005-01-19 3M Innovative Properties Co Fluoropolymer for making a fluoroelastomer
US7294677B2 (en) * 2005-08-25 2007-11-13 3M Innovative Properties Company Catalyst for making fluoroelastomer compositions and methods of using the same
US20070135577A1 (en) * 2005-12-09 2007-06-14 Shefelbine Terri A Intermediate elastomer compositions
US8217126B2 (en) * 2007-11-09 2012-07-10 E I Du Pont De Nemours And Company Fluoroolefin monomers and copolymers thereof
GB2459672A (en) * 2008-04-30 2009-11-04 3M Innovative Properties Co Linear short-chained perfluorinated alkoxy allyl ethers and their preparation
US20090306303A1 (en) * 2008-06-09 2009-12-10 Dupont Peformance Elastomers L.L.C. Curable base-resistant fluoroelastomers
US8906821B2 (en) 2009-06-25 2014-12-09 3M Innovative Properties Company Curing compositions for fluoropolymers
WO2013000735A1 (en) * 2011-06-27 2013-01-03 Solvay Specialty Polymers Italy S.P.A. Novel fluorinated unsaturated compound and polymers obtainable therefrom
EP2776498B1 (en) 2011-11-09 2018-12-26 3M Innovative Properties Company Curing compositions for fluoropolymers
WO2017083688A1 (en) 2015-11-13 2017-05-18 3M Innovative Properties Company Compositions including a bimodal blend of amorphous fluoropolymers and their uses
WO2017127569A1 (en) 2016-01-21 2017-07-27 3M Innovative Properties Company Additive processing of fluoroelastomers
TW201815845A (zh) 2016-05-17 2018-05-01 ３Ｍ新設資產公司 包括二氟亞乙烯與四氟乙烯的共聚物之組成物及其使用方法
EP3559105B1 (en) 2016-12-20 2020-11-18 3M Innovative Properties Company Filament based on a composition including fluoropolymer and inorganic filler and method of making a three-dimensional article
US11292763B2 (en) 2017-05-19 2022-04-05 3M Innovative Properties Company Methods of making a polyfluorinated allyl ether and compounds relating to the methods
US20210070686A1 (en) 2017-12-21 2021-03-11 3M Innovative Properties Company Methods of making polyfunctional polyfluorinated compounds
JP2021524539A (ja) * 2018-07-20 2021-09-13 スリーエム イノベイティブ プロパティズ カンパニー ペルフルオロアリルエーテルを含有するフッ化ビニリデンフルオロポリマー
EP3837309A1 (en) * 2018-08-13 2021-06-23 3M Innovative Properties Company Curable fluoroelastomer composition
RU2018141773A (ru) 2018-11-27 2020-05-27 3М Инновейтив Пропертиз Компани Композиции полимерных процессинговых добавок и изделия, полученные с использованием указанных композиций
TWI918597B (zh) 2018-12-17 2026-03-21 美商3M新設資產公司 包括可固化氟聚合物及固化劑之組成物及製造及使用其之方法
US20220227696A1 (en) 2019-06-04 2022-07-21 3M Innovative Properties Company Multifunctional Fluorinated Compound, Fluorinated Polymers Made from the Compound, and Related Methods
CN113950505B (zh) 2019-06-28 2023-05-30 3M创新有限公司 羟基官能化三嗪化合物、包含此类化合物的可固化含氟聚合物组合物以及由其制得的固化制品
WO2021046266A1 (en) 2019-09-05 2021-03-11 3M Innovative Properties Company Composition and article including fluoropolymer and branched silsesquioxane polymer
US20230026338A1 (en) 2019-12-30 2023-01-26 3M Innovative Properties Company Composition Including Fluoropolymer, Benzoyl Peroxide, and Crosslinker and Related Articles and Methods
WO2021214664A1 (en) 2020-04-21 2021-10-28 3M Innovative Properties Company Particles including polytetrafluoroethylene and process for making a three-dimensional article
WO2022114109A1 (ja) * 2020-11-30 2022-06-02 セントラル硝子株式会社 フルオロエラストマー組成物、フッ素ゴム成形体、フッ素ゴム成形体製造用架橋剤、フッ素ゴム成形体製造用架橋促進剤、混合塩およびオニウム塩
US20240132643A1 (en) 2021-02-26 2024-04-25 3M Innovative Properties Company Process for Making a Fluoropolymer and Fluoropolymer Made Therefrom
WO2022189938A1 (en) 2021-03-10 2022-09-15 3M Innovative Properties Company Branched silsesquioxane polymer and compositions and articles including the same
US20250340684A1 (en) 2022-05-17 2025-11-06 Dupont Specialty Products Usa Llc Method of making halo (alkyl vinyl) ether monomers and fluorinated polymers made with the halo (alkyl vinyl) ether monomer
CN120584153A (zh) 2023-01-27 2025-09-02 杜邦特种产品美国有限责任公司 氟聚合物组合物以及由其制成的制品

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0154460A2 (en) * 1984-02-27 1985-09-11 Minnesota Mining And Manufacturing Company Fluoroelastomer compositions containing fluoroaliphatic sulfonamides as curing agents
EP0466340A2 (en) * 1990-07-13 1992-01-15 Minnesota Mining And Manufacturing Company Curing fluorocarbon elastomers

Family Cites Families (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3029227A (en) * 1956-08-20 1962-04-10 Minnesota Mining & Mfg Cross-linking and cross-linking agents
US2975163A (en) * 1956-10-29 1961-03-14 Minnesota Mining & Mfg Fluorine containing organic compounds and preparation thereof
US3250807A (en) * 1963-08-23 1966-05-10 Du Pont Dicarboxylic acids of fluorocarbon ethers and fluorides, esters, amides and salts thereof
NL148300B (nl) * 1964-01-02 1976-01-15 Edison Soc Werkwijze ter bereiding van polyoxyperfluormethylenen.
US3442942A (en) * 1964-04-09 1969-05-06 Montedison Spa Fluorinated oxygen containing acyl fluorides
NL6709067A (enExample) * 1964-04-09 1968-01-08
GB1193122A (en) * 1966-03-24 1970-05-28 Allied Chem Novel Fluoroperhaloisopropyl Methyl Ethers
DE1745169B2 (de) * 1967-02-09 1977-04-21 Montecatini Edison S.P.A., Mailand (Italien) Fluorierte lineare polyaether und verfahren zu ihrer herstellung
US3504411A (en) * 1967-10-11 1970-04-07 Westinghouse Electric Corp Process for producing an electrode tip
US3876654A (en) * 1970-12-23 1975-04-08 Du Pont Fluoroelastomer composition
US3849594A (en) * 1973-05-25 1974-11-19 Westinghouse Electric Corp Multi-picture tv system with audio and doding channels
US4287320A (en) * 1974-08-01 1981-09-01 Minnesota Mining And Manufacturing Company Composition of fluoroelastomer and diorganosulfuroxide
NL189567C (nl) * 1977-12-14 1993-05-17 Montedison Spa Vulcaniseerbare mengsels op basis van elastomere copolymeren van vinylideenfluoride, werkwijze om deze te vulcaniseren en voorwerpen geheel of gedeeltelijk bestaande uit de zo verkregen gevulcaniseerde mengsels.
US4206138A (en) * 1978-08-08 1980-06-03 E. I. Du Pont De Nemours And Company Perfluoroallyl fluorosulfate and its sultone and polymers
US4233421A (en) * 1979-02-26 1980-11-11 Minnesota Mining And Manufacturing Company Fluoroelastomer composition containing sulfonium curing agents
US4273728A (en) * 1979-03-14 1981-06-16 E. I. Du Pont De Nemours And Company Polyfluoroallyloxy compounds, their preparation and copolymers therefrom
US4275225A (en) * 1979-03-14 1981-06-23 E. I. Du Pont De Nemours And Company Polyfluoroallyloxy compounds, their preparation and copolymers therefrom
US4273729A (en) * 1979-03-14 1981-06-16 E. I. Du Pont De Nemours And Company Polyfluoroallyloxy compounds, their preparation and copolymers therefrom
US4292449A (en) * 1979-03-14 1981-09-29 E. I. Du Pont De Nemours And Company Polyfluoroallyloxy compounds, their preparation and copolymers therefrom
US4358559A (en) * 1981-11-19 1982-11-09 Minnesota Mining And Manufacturing Company Tacky fluoroelastomer compositions
US4446270A (en) * 1982-11-22 1984-05-01 Minnesota Mining And Manufacturing Company Vulcanizing fluorocarbon elastomers with one or a mixture of aromatic compounds having hydroxyl and oxyallyl groups
US5086123A (en) * 1984-02-27 1992-02-04 Minnesota Mining And Manufacturing Company Fluoroelastomer compositions containing fluoroaliphatic sulfonamides as curing agents
US4910276A (en) * 1987-08-14 1990-03-20 Asahi Glass Company, Ltd. Cyclic polymerization
US4912171A (en) * 1988-04-01 1990-03-27 Minnesota Mining And Manufacturing Company Fluoroelastomer curing process with phosphonium compound
US5266650A (en) * 1990-10-11 1993-11-30 Minnesota Mining And Manufacturing Company Curing fluorocarbon elastomers
US5384374A (en) * 1991-01-11 1995-01-24 Minnesota Mining And Manufacturing Company Curing fluorocarbon elastomers
US5214106A (en) * 1991-05-22 1993-05-25 E. I. Du Pont De Nemours And Company Cured fluoroelastomer compositions
US5274159A (en) * 1993-02-18 1993-12-28 Minnesota Mining And Manufacturing Company Destructable fluorinated alkoxysilane surfactants and repellent coatings derived therefrom
US5488142A (en) * 1993-10-04 1996-01-30 Minnesota Mining And Manufacturing Company Fluorination in tubular reactor system
US5591804A (en) * 1995-12-21 1997-01-07 Minnesota Mining And Manufacturing Company Fluorinated onium salts, curable compositions containing same, and method of curing using same

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0154460A2 (en) * 1984-02-27 1985-09-11 Minnesota Mining And Manufacturing Company Fluoroelastomer compositions containing fluoroaliphatic sulfonamides as curing agents
EP0466340A2 (en) * 1990-07-13 1992-01-15 Minnesota Mining And Manufacturing Company Curing fluorocarbon elastomers

Also Published As

Publication number Publication date
JP2001508105A (ja) 2001-06-19
CN1215117C (zh) 2005-08-17
KR100516575B1 (ko) 2005-09-22
JP4134283B2 (ja) 2008-08-20
CA2274775C (en) 2007-08-14
CN1243529A (zh) 2000-02-02
WO1998030631A1 (en) 1998-07-16
US5891965A (en) 1999-04-06
CA2274775A1 (en) 1998-07-16
DE69801981T2 (de) 2002-05-29
AU6016298A (en) 1998-08-03
DE69801981D1 (de) 2001-11-15
EP0950078A1 (en) 1999-10-20
KR20000069872A (ko) 2000-11-25
CN1495228A (zh) 2004-05-12
EP0950078B1 (en) 2001-10-10

Similar Documents

Publication Publication Date Title
CN1215117C (zh) 具有良好低温特性的氟碳弹性组合物
JP6987740B2 (ja) フッ素化ブロックコポリマー
JP4570780B2 (ja) 低温フルオロカーボンエラストマ
JP4778663B2 (ja) フルオロポリマー含有組成物
JP5860049B2 (ja) 改質剤及びヨウ素又は臭素末端基を含有する過酸化物硬化性フルオロエラストマー
JP5465175B2 (ja) （パー）フルオロエラストマー組成物
JP2020504226A (ja) フッ素化ブロックコポリマー
KR20090035507A (ko) (퍼)플루오로엘라스토머 조성물
EP0902806B1 (en) Fluoroelastomer compositions
CN102770468B (zh) 用于生产氟弹性体的方法
EP0842980B1 (en) Fluorocarbon elastomer composition
JP2020504225A (ja) ニトリル硬化部位モノマーから誘導されるフッ素化ブロックコポリマー
CN1984947A (zh) 低温性能得到改善的含氟弹性体及其制备方法
JP6333554B2 (ja) 低粘度フルオロエラストマー
KR20000015784A (ko) 유기 오늄 화합물을 함유하는 플루오로엘라스토머 조성물
JP2004527596A (ja) 低いガラス転移温度を有するペルフルオロエラストマーおよびそれらの製造方法
TW201936759A (zh) 可固化氟彈性體組成物
TW201936758A (zh) 用於氟彈性體之交聯劑摻合物
JP7262464B2 (ja) 硬化性フッ素化ポリマー組成物
JP2021535261A (ja) 内部フッ素化可塑剤を含む過酸化物硬化性高フッ素化ポリマー及びそれからの物品
CN1649917A (zh) 可硫化的耐碱含氟弹性体

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
ASS Succession or assignment of patent right

Owner name: 3M INNOVATIVE PROPERTIES COMPANY

Free format text: FORMER OWNER: DYNIAURN CO., LTD.

Effective date: 20101223

C41 Transfer of patent application or patent right or utility model
TR01 Transfer of patent right

Effective date of registration: 20101223

Address after: American Minnesota

Patentee after: 3M Innovative Properties Company

Address before: American Minnesota

Patentee before: Dyniaurn Co., Ltd.

CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20080227

Termination date: 20130106

CF01 Termination of patent right due to non-payment of annual fee