AR089851A1 - Metodo y sistema para elaborar un material resistente al desgaste, articulo producido y miembro de desgaste - Google Patents

Metodo y sistema para elaborar un material resistente al desgaste, articulo producido y miembro de desgaste

Info

Publication number
AR089851A1
AR089851A1 ARP130100279A AR089851A1 AR 089851 A1 AR089851 A1 AR 089851A1 AR P130100279 A ARP130100279 A AR P130100279A AR 089851 A1 AR089851 A1 AR 089851A1
Authority
AR
Argentina
Prior art keywords
wear
preparing
resistant material
resistant composite
composite material
Prior art date
Application number
Other languages
English (en)
Original Assignee
Esco Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Esco Corp filed Critical Esco Corp
Publication of AR089851A1 publication Critical patent/AR089851A1/es

Abstract

Un sistema y método de formación de un material compuesto resistente al desgaste incluye colocar un material de relleno poroso resistente al desgaste en una cavidad de molde e infiltrar el material de relleno con un material de matriz por calentamiento hasta una temperatura suficiente para fundir el material de la matriz, luego enfriar el conjunto para formar un material compuesto a resistente al desgaste. El sistema y el método se pueden usar para formar el material compuesto resistente al desgaste sobre la superficie de un sustrato, como una parte para equipamiento de excavación u otra parte mecánica. Un material de matriz apropiado puede ser cualquiera de una variedad de aleaciones de hierro dúctiles.
ARP130100279 2012-01-31 2013-01-30 Metodo y sistema para elaborar un material resistente al desgaste, articulo producido y miembro de desgaste AR089851A1 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US201261593091P 2012-01-31 2012-01-31

Publications (1)

Publication Number Publication Date
AR089851A1 true AR089851A1 (es) 2014-09-24

Family

ID=48870491

Family Applications (1)

Application Number Title Priority Date Filing Date
ARP130100279 AR089851A1 (es) 2012-01-31 2013-01-30 Metodo y sistema para elaborar un material resistente al desgaste, articulo producido y miembro de desgaste

Country Status (28)

Country Link
US (2) US10543528B2 (es)
EP (1) EP2809466B8 (es)
JP (1) JP6445868B2 (es)
KR (1) KR102037764B1 (es)
CN (3) CN110153396A (es)
AP (1) AP2014007838A0 (es)
AR (1) AR089851A1 (es)
AU (1) AU2013202962C1 (es)
BR (1) BR112014018839B1 (es)
CA (1) CA2860627A1 (es)
CL (1) CL2014001962A1 (es)
CO (1) CO7030955A2 (es)
EA (1) EA032732B1 (es)
ES (1) ES2693770T3 (es)
HK (1) HK1198149A1 (es)
HR (1) HRP20182085T1 (es)
JO (1) JO3717B1 (es)
MX (2) MX370222B (es)
MY (1) MY167939A (es)
NZ (2) NZ626215A (es)
PE (1) PE20142428A1 (es)
PH (1) PH12014501414B1 (es)
PL (1) PL2809466T3 (es)
SG (1) SG11201403315YA (es)
TR (1) TR201816566T4 (es)
TW (1) TWI567270B (es)
UA (1) UA114099C2 (es)
WO (1) WO2013116183A1 (es)

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2725904T3 (es) * 2013-10-02 2019-09-30 Oerlikon Metco Us Inc Barra de soldadura fuerte para formar un recubrimiento resistente al desgaste y un recubrimiento resistente al desgaste
WO2015103670A1 (en) * 2014-01-09 2015-07-16 Bradken Uk Limited Wear member incorporating wear resistant particles and method of making same
GB2523583C (en) * 2014-02-28 2019-12-25 Castings Tech International Limited Forming a composite component
CN104525716B (zh) * 2014-11-18 2016-10-05 西安理工大学 冷冲模具及其制备方法
AU2016317860B2 (en) 2015-09-04 2021-09-30 Scoperta, Inc. Chromium free and low-chromium wear resistant alloys
CN105925929B (zh) * 2016-06-27 2018-08-21 福建省诺希科技园发展有限公司 一种ZrC-SiC/NiCrMoV热作模具钢涂层制备方法
JP6761596B2 (ja) * 2016-07-29 2020-09-30 三菱マテリアル株式会社 複合材料からなる切削工具
CN106048404A (zh) * 2016-08-18 2016-10-26 江阴联华铸造有限公司 一种汽车曲轴用抗疲劳耐磨球墨铸铁件及其制备方法
CN108251803B (zh) * 2016-12-29 2020-06-02 深圳先进技术研究院 TiB2自润滑涂层及其制备方法和耐磨构件
JP6322300B1 (ja) * 2017-01-06 2018-05-09 株式会社エーアイ 白金加工品の製造方法
CN107400886A (zh) * 2017-07-19 2017-11-28 武汉理工大学 一种基于激光熔融沉积的汽车离合器面片及其制备方法
WO2019018605A1 (en) * 2017-07-20 2019-01-24 Esco Group Llc HARD SURFACE PRODUCTS FOR ABRASIVE APPLICATIONS AND METHODS OF MAKING THE SAME
WO2020086971A1 (en) 2018-10-26 2020-04-30 Oerlikon Metco (Us) Inc. Corrosion and wear resistant nickel based alloys
CN111136242B (zh) * 2018-11-06 2022-04-08 有研金属复材技术有限公司 一种非均质多功能金属基复合材料铸件的制备方法
CN109438997A (zh) * 2018-11-27 2019-03-08 徐州市恩矿新材料有限公司 一种用于耐磨材料的组合物的配方
RU2765870C2 (ru) * 2019-08-05 2022-02-04 Акционерное общество "НАУЧНО-ИССЛЕДОВАТЕЛЬСКИЙ ИНСТИТУТ МАШИНОСТРОЕНИЯ" (АО "НИИМаш") Способ соединения деталей и устройство для его осуществления
EP4121232A1 (en) * 2020-03-18 2023-01-25 CONV Australia Holding Pty Ltd. Wear resistant composite
US11882777B2 (en) 2020-07-21 2024-01-30 Osmundson Mfg. Co. Agricultural sweep with wear resistant coating
RU2753362C1 (ru) * 2020-11-11 2021-08-13 Акционерное общество "Пермский завод "Машиностроитель" Способ наплавки медных сплавов на сталь
CN112626456A (zh) * 2021-01-05 2021-04-09 天津职业技术师范大学(中国职业培训指导教师进修中心) 一种兼具高硬度和高韧性的ZrB2-Ni涂层及其制备工艺
JP2022146047A (ja) * 2021-03-22 2022-10-05 キオクシア株式会社 セレクタ装置及び半導体記憶装置
CN113388777B (zh) * 2021-04-22 2022-07-08 宁国市开源电力耐磨材料有限公司 一种耐磨铸钢件及其制备工艺
CN117381942B (zh) * 2023-10-10 2024-05-03 广州市恒宏生态建材有限公司 一种环保耐磨的无机生态石的制备工艺

Family Cites Families (155)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1939991A (en) 1931-12-17 1933-12-19 Hard Metal Alloys Inc Diamond cutting tool or the like and method of making the same
US1978319A (en) 1932-06-16 1934-10-23 Harold W Mowery Method of making abrasive metal castings
US2130684A (en) 1936-10-30 1938-09-20 Heald Machine Co Method of forming a cutting tool
US2260593A (en) 1940-05-27 1941-10-28 Texas Electric Steel Casting C Method of making wear resistant surfaces
US2363272A (en) 1942-07-10 1944-11-21 Taeyaerts Jan Diamond-tipped tool and method of making the same
US2603985A (en) 1949-09-29 1952-07-22 Bennie J Vidmar Method of repointing dipper teeth
US2714245A (en) * 1951-12-07 1955-08-02 Sintercast Corp America Sintered titanium carbide alloy turbine blade
US2731711A (en) 1954-05-13 1956-01-24 Gen Electric Sintered tungsten carbide composition
US2833638A (en) * 1955-03-24 1958-05-06 Servco Mfg Corp Hard facing material and method of making
NL275996A (es) 1961-09-06
NL290912A (es) 1962-11-15
US3149411A (en) 1962-12-21 1964-09-22 Jersey Prod Res Co Composite materials containing cemented carbides
US3168767A (en) 1963-04-01 1965-02-09 Kenneth V Lutz Method of and product for rebuilding tampers on compaction rollers
AT282213B (de) * 1968-06-04 1970-06-25 Metallgesellschaft Ag Verfahren zum Erzeugen scharfer Kanten beim Panzern von Maschinenteilen und Werkstücken
US3608170A (en) * 1969-04-14 1971-09-28 Abex Corp Metal impregnated composite casting method
US3882594A (en) 1972-02-22 1975-05-13 Servco Co Method of forming a hard facing on the body of a tool
US3790353A (en) 1972-02-22 1974-02-05 Servco Co Division Smith Int I Hard-facing article
US3894575A (en) 1972-06-05 1975-07-15 Textron Inc High density carbide stud
US3777517A (en) 1972-06-07 1973-12-11 Warren M Shwayder Saw and impact resistant lock shackle
US3932952A (en) 1973-12-17 1976-01-20 Caterpillar Tractor Co. Multi-material ripper tip
US3889093A (en) 1974-01-23 1975-06-10 Kennametal Inc Hardfaced member and method of attaching hardfacing element thereto
US3977227A (en) 1974-02-25 1976-08-31 Noble Charles H Method of cold extruding ductile cast iron tube
US4017480A (en) 1974-08-20 1977-04-12 Permanence Corporation High density composite structure of hard metallic material in a matrix
JPS599615B2 (ja) 1974-09-25 1984-03-03 株式会社リケン 超塑性を有する強靭球状黒鉛鋳鉄及び熱処理方法
US3972570A (en) 1975-04-17 1976-08-03 Caterpillar Tractor Co. Wear-resistant composite track shoe
US3955855A (en) 1975-04-17 1976-05-11 Caterpillar Tractor Co. Wear-resistant composite track link
US4024902A (en) 1975-05-16 1977-05-24 Baum Charles S Method of forming metal tungsten carbide composites
US4013453A (en) 1975-07-11 1977-03-22 Eutectic Corporation Flame spray powder for wear resistant alloy coating containing tungsten carbide
SE399911C (sv) 1976-02-05 1980-01-31 Sandvik Ab Slitdetalj med hog slitstyrka och god hallfasthet, sammansatt av hardmetall och gjutjern
US4052802A (en) 1976-02-23 1977-10-11 Caterpillar Tractor Co. Ground-engaging tool with wear-resistant insert
US4136230A (en) 1976-07-29 1979-01-23 Eutectic Corporation Wear resistant alloy coating containing tungsten carbide
US6735890B2 (en) 2001-07-06 2004-05-18 Esco Corporation Wear assembly
US4187626A (en) 1978-02-27 1980-02-12 Esco Corporation Excavating tool having hard-facing elements
US4156374A (en) 1978-03-20 1979-05-29 Shwayder Warren M Pre-formed wear pads for drill stabilizers
US4274769A (en) 1978-04-21 1981-06-23 Acker Drill Company, Inc. Impregnated diamond drill bit construction
GB2041427B (en) 1978-11-01 1982-08-18 Nl Industries Inc Insert for tool wear surfaces and method of manufacture
US4327156A (en) 1980-05-12 1982-04-27 Minnesota Mining And Manufacturing Company Infiltrated powdered metal composite article
JPS5788966A (en) 1980-11-21 1982-06-03 Komatsu Ltd Production of abrasion resistant composite material
US4363661A (en) * 1981-04-08 1982-12-14 Ford Motor Company Method for increasing mechanical properties in ductile iron by alloy additions
JPS57171563A (en) 1981-04-15 1982-10-22 Komatsu Ltd Abrasion resistant material
US4608318A (en) 1981-04-27 1986-08-26 Kennametal Inc. Casting having wear resistant compacts and method of manufacture
US4529042A (en) 1981-05-29 1985-07-16 Adams Hard-Facing Company, Inc. Tillage tool appendage
EP0078525A2 (en) * 1981-10-30 1983-05-11 Aktieselskabet Aalborg Portland-Cement-Fabrik A method of improving characteristic of a body
JPS6017819B2 (ja) * 1982-04-01 1985-05-07 マツダ株式会社 高温耐酸化性、耐熱疲労性に優れた球状黒鉛鋳鉄
US4452325A (en) 1982-09-27 1984-06-05 Conoco Inc. Composite structure for cutting tools
US5178647A (en) * 1983-07-29 1993-01-12 Kabushiki Kaisha Toshiba Wear-resistant member
US4499795A (en) 1983-09-23 1985-02-19 Strata Bit Corporation Method of drill bit manufacture
DE3334815C1 (de) 1983-09-26 1984-10-18 Siku GmbH Metall- und Kunststoffwarenfabrik, Rickenbach Werkzeug
US4605157A (en) 1984-01-31 1986-08-12 Nl Industries, Inc. Drill bit manufacturing method
US4638847A (en) 1984-03-16 1987-01-27 Giw Industries, Inc. Method of forming abrasive resistant white cast iron
US4526220A (en) 1984-03-16 1985-07-02 Scherer John R Method for improving performance of chaplets in metal casting
JPS61190353A (ja) 1985-02-20 1986-08-25 Fuji Xerox Co Ltd 複写機のオゾン排出装置
US4719076A (en) 1985-11-05 1988-01-12 Smith International, Inc. Tungsten carbide chips-matrix bearing
US4933240A (en) 1985-12-27 1990-06-12 Barber Jr William R Wear-resistant carbide surfaces
US4676124A (en) 1986-07-08 1987-06-30 Dresser Industries, Inc. Drag bit with improved cutter mount
US4705123A (en) 1986-07-29 1987-11-10 Strata Bit Corporation Cutting element for a rotary drill bit and method for making same
US4938991A (en) 1987-03-25 1990-07-03 Dresser Industries, Inc. Surface protection method and article formed thereby
US5090491A (en) 1987-10-13 1992-02-25 Eastman Christensen Company Earth boring drill bit with matrix displacing material
GB8725671D0 (en) 1987-11-03 1987-12-09 Reed Tool Co Manufacture of rotary drill bits
US4884477A (en) 1988-03-31 1989-12-05 Eastman Christensen Company Rotary drill bit with abrasion and erosion resistant facing
FR2632353A1 (fr) 1988-06-02 1989-12-08 Combustible Nucleaire Outil pour machine d'abattage minier comportant une piece abrasive diamantee
US4916869A (en) 1988-08-01 1990-04-17 L. R. Oliver & Company, Inc. Bonded abrasive grit structure
US5066546A (en) 1989-03-23 1991-11-19 Kennametal Inc. Wear-resistant steel castings
US5027878A (en) 1989-10-05 1991-07-02 Deere & Company Method of impregnation of iron with a wear resistant material
US5030519A (en) 1990-04-24 1991-07-09 Amorphous Metals Technologies, Inc. Tungsten carbide-containing hard alloy that may be processed by melting
US5190092A (en) 1990-08-08 1993-03-02 Deere & Company Method of impregnation of iron with a wear-resistant material
US5113924A (en) 1990-08-17 1992-05-19 Hitchiner Manufacturing Co., Inc. Method of casting wear-resistant, cast iron machine element
FR2667088B1 (fr) 1990-09-20 1994-10-14 Technogenia Sa Dent pour outil d'excavation.
US5355750A (en) 1991-03-01 1994-10-18 Baker Hughes Incorporated Rolling cone bit with improved wear resistant inserts
US5316851A (en) * 1991-06-12 1994-05-31 General Electric Company Silicon carbide composite with metal boride coated fiber reinforcement
US5111600A (en) 1991-07-30 1992-05-12 Caterpillar Inc. Tooth with hard material applied to selected surfaces
US5299620A (en) 1992-01-21 1994-04-05 Deere & Company Metal casting surface modification by powder impregnation
JP2593935Y2 (ja) * 1992-01-31 1999-04-19 東芝タンガロイ株式会社 リングビット
JPH0639523A (ja) * 1992-07-23 1994-02-15 Toshiba Mach Co Ltd 高強度耐食、耐摩耗性部材の製造方法
JPH0679435A (ja) * 1992-09-01 1994-03-22 Eagle Ind Co Ltd 掘削用ビットの製造方法
US5271547A (en) 1992-09-15 1993-12-21 Tunco Manufacturing, Inc. Method for brazing tungsten carbide particles and diamond crystals to a substrate and products made therefrom
US5373907A (en) 1993-01-26 1994-12-20 Dresser Industries, Inc. Method and apparatus for manufacturing and inspecting the quality of a matrix body drill bit
JPH06240710A (ja) 1993-02-10 1994-08-30 Komatsu Ltd 異種材複合型切刃とその製造方法
JPH0778242B2 (ja) 1993-02-12 1995-08-23 日本ユテク株式会社 耐摩耗性複合金属部材の製造方法
FI935559A (fi) 1993-06-14 1994-12-15 Robit Rocktools Ab Oy Menetelmä kovametallinastojen kiinnittämiseksi porakruunuun ja porakruunu
US5441121A (en) 1993-12-22 1995-08-15 Baker Hughes, Inc. Earth boring drill bit with shell supporting an external drilling surface
US6073518A (en) * 1996-09-24 2000-06-13 Baker Hughes Incorporated Bit manufacturing method
US5765624A (en) 1994-04-07 1998-06-16 Oshkosh Truck Corporation Process for casting a light-weight iron-based material
GB2288351B (en) 1994-04-08 1998-03-18 Cutting & Wear Resistant Dev Method for facing a substrate
US5502905A (en) 1994-04-26 1996-04-02 Caterpillar Inc. Tooth having abrasion resistant material applied thereto
US5445231A (en) * 1994-07-25 1995-08-29 Baker Hughes Incorporated Earth-burning bit having an improved hard-faced tooth structure
US5589268A (en) 1995-02-01 1996-12-31 Kennametal Inc. Matrix for a hard composite
US5737980A (en) 1996-06-04 1998-04-14 Smith International, Inc. Brazing receptacle for improved PCD cutter retention
US5880382A (en) 1996-08-01 1999-03-09 Smith International, Inc. Double cemented carbide composites
US6050208A (en) 1996-11-13 2000-04-18 Fern Investments Limited Composite structural laminate
US6033791A (en) 1997-04-04 2000-03-07 Smith And Stout Research And Development, Inc. Wear resistant, high impact, iron alloy member and method of making the same
US6039641A (en) 1997-04-04 2000-03-21 Sung; Chien-Min Brazed diamond tools by infiltration
US6024804A (en) * 1997-05-02 2000-02-15 Ohio Cast Products, Inc. Method of preparing high nodule malleable iron and its named product
US5837069A (en) 1997-09-16 1998-11-17 Weyburn-Bartel Inc. Cast iron components and method of making
US20040006074A1 (en) * 1998-04-28 2004-01-08 The Government Of The United States Of America Cyclin dependent kinase (CDK)4 inhibitors and their use for treating cancer
US6220117B1 (en) 1998-08-18 2001-04-24 Baker Hughes Incorporated Methods of high temperature infiltration of drill bits and infiltrating binder
US6649682B1 (en) * 1998-12-22 2003-11-18 Conforma Clad, Inc Process for making wear-resistant coatings
DE19924683C2 (de) 1999-05-28 2002-02-28 Betek Bergbau & Hartmetall Verfahren zur Bestückung eines Meißelkopfes eines Schaftmeißels und Meißel
US6258180B1 (en) 1999-05-28 2001-07-10 Waupaca Foundry, Inc. Wear resistant ductile iron
US6571493B2 (en) 1999-12-27 2003-06-03 Komatsu Ltd. Cutting edge
JP2001248127A (ja) 1999-12-27 2001-09-14 Komatsu Ltd カッティングエッジ
US6601789B1 (en) 2000-03-22 2003-08-05 Spokane Industries, Inc. Rock crusher impact shoe
US6347676B1 (en) * 2000-04-12 2002-02-19 Schlumberger Technology Corporation Tooth type drill bit with secondary cutting elements and stress reducing tooth geometry
US6719948B2 (en) 2000-05-22 2004-04-13 Massachusetts Institute Of Technology Techniques for infiltration of a powder metal skeleton by a similar alloy with melting point depressed
AUPQ933400A0 (en) 2000-08-10 2000-08-31 Huggett, Paul A method of manufacturing metallic composites produced thereby
CN1108211C (zh) * 2000-09-14 2003-05-14 四川大学 铁基表面复合材料凸轮轴及其制造方法
ES2336897T3 (es) 2001-07-06 2010-04-19 Esco Corporation Acoplamiento para pieza desgastable de excavadora.
EP1450973B1 (fr) 2001-12-04 2006-04-12 Magotteaux International S.A. Pieces de fonderie avec une resistance accrue a l'usure
US7017677B2 (en) 2002-07-24 2006-03-28 Smith International, Inc. Coarse carbide substrate cutting elements and method of forming the same
US20030213861A1 (en) 2002-05-15 2003-11-20 Condon Gary J. Crusher wear components
US7261752B2 (en) 2002-09-24 2007-08-28 Chien-Min Sung Molten braze-coated superabrasive particles and associated methods
US7250069B2 (en) * 2002-09-27 2007-07-31 Smith International, Inc. High-strength, high-toughness matrix bit bodies
RU2228409C1 (ru) 2002-10-29 2004-05-10 Военно-технический университет при Федеральной службе специального строительства Российской Федерации Способ изготовления зуба землеройной машины
CN1747797B (zh) 2003-02-07 2011-08-17 戴蒙得创新股份有限公司 具有扩大抵抗能力的设备磨损表面及其加工方法
US20040234820A1 (en) 2003-05-23 2004-11-25 Kennametal Inc. Wear-resistant member having a hard composite comprising hard constituents held in an infiltrant matrix
US7395882B2 (en) 2004-02-19 2008-07-08 Baker Hughes Incorporated Casing and liner drilling bits
JP2005273439A (ja) * 2004-02-26 2005-10-06 Kubota Corp 掘削用のビット
AU2005202371B2 (en) 2005-05-31 2010-09-23 Sandvik Intellectual Property Ab Method for manufacturing a cutting pick
CA2511309C (en) 2005-06-29 2010-02-16 Ibex Welding Technologies Inc. Method of hard coating a surface with carbide
US8002052B2 (en) 2005-09-09 2011-08-23 Baker Hughes Incorporated Particle-matrix composite drill bits with hardfacing
US7597159B2 (en) 2005-09-09 2009-10-06 Baker Hughes Incorporated Drill bits and drilling tools including abrasive wear-resistant materials
RU2008118420A (ru) 2005-10-11 2009-11-20 Бейкер Хьюз Инкорпорейтед (Us) Система, способ и устройство для повышения износостойкости буровых долот
WO2007059568A1 (en) 2005-11-22 2007-05-31 Composite Alloy Products Pty Ltd A method of manufacturing metallic composites in an inert atmosphere and composites produced thereby
UA15945U (en) 2006-02-10 2006-07-17 Larysa Hryhorivna Babiieva Heat-supply system
US7510032B2 (en) 2006-03-31 2009-03-31 Kennametal Inc. Hard composite cutting insert and method of making the same
US7568770B2 (en) 2006-06-16 2009-08-04 Hall David R Superhard composite material bonded to a steel body
US7445294B2 (en) 2006-08-11 2008-11-04 Hall David R Attack tool
KR100783100B1 (ko) * 2006-11-17 2007-12-07 주식회사 티엠시 굴착기 바켓용 팁 및 그의 제조 방법
US7824605B2 (en) 2006-12-15 2010-11-02 Dexter Foundry, Inc. As-cast carbidic ductile iron
US7523794B2 (en) 2006-12-18 2009-04-28 Hall David R Wear resistant assembly
GB2459217B (en) 2007-01-08 2011-04-27 Halliburton Energy Serv Inc Drill bits and other downhole tools with hardfacing having tungsten carbide pellets and other hard materials
DE112008000203T5 (de) * 2007-01-18 2009-12-24 Halliburton Energy Services, Inc., Houston Gießen von Wolframcarbidmatrix-Bohrspitzenköpfen und Erhitzen von Bohrspitzenkopfabschnitten mit Mikrowellenstrahlung
JP2008246550A (ja) 2007-03-30 2008-10-16 Iwate Industrial Research Center プリフォームの製造方法，プリフォーム及びプリフォームを使用した鋳ぐるみ品
CA2585688C (en) 2007-04-20 2014-10-14 Igor Tsypine Wear-resistant castings and method of fabrication thereof
CN100509213C (zh) * 2007-04-24 2009-07-08 昆明理工大学 制备颗粒增强金属基表面复合材料的真空实型铸渗方法
US8241761B2 (en) 2007-08-15 2012-08-14 Mikhail Garber Abrasion and impact resistant composite castings for working in condition of wear and high dynamic loads
CN101134237B (zh) * 2007-10-11 2010-06-30 丁家伟 增强相金属梯度复合材料制造工艺及设备
US8252225B2 (en) 2009-03-04 2012-08-28 Baker Hughes Incorporated Methods of forming erosion-resistant composites, methods of using the same, and earth-boring tools utilizing the same in internal passageways
EP2242886A1 (en) 2008-01-04 2010-10-27 Excalibur Steel Company Pty Ltd Wear resistant components
US7846381B2 (en) 2008-01-29 2010-12-07 Aarrowcast, Inc. Ferritic ductile cast iron alloys having high carbon content, high silicon content, low nickel content and formed without annealing
CA2729051A1 (en) 2008-06-27 2009-12-30 Excalibur Steel Company Pty Ltd Manufacture of wear resistant composite components
US8191291B2 (en) 2008-07-09 2012-06-05 Esco Corporation Wear member for excavating equipment
US8025112B2 (en) * 2008-08-22 2011-09-27 Tdy Industries, Inc. Earth-boring bits and other parts including cemented carbide
CN101412098B (zh) * 2008-12-03 2011-05-04 西安建筑科技大学 一种原生柱状硬质相复合耐磨块的制备方法
CA2747878A1 (en) * 2008-12-23 2010-07-01 Excalibur Steel Company Pty Ltd Method of manufacturing components
US20100181116A1 (en) 2009-01-16 2010-07-22 Baker Hughes Incororated Impregnated drill bit with diamond pins
US7897204B2 (en) 2009-01-29 2011-03-01 Nanotech Industries, Inc. Method of strengthening tool material by penetration of reinforcing particles
US8201648B2 (en) 2009-01-29 2012-06-19 Baker Hughes Incorporated Earth-boring particle-matrix rotary drill bit and method of making the same
US8839887B2 (en) 2009-03-13 2014-09-23 Smith International, Inc. Composite sintered carbides
US8136571B2 (en) 2009-05-19 2012-03-20 Debruin Mark Carbidic outer edge ductile iron product, and as cast surface alloying process
JP2010274323A (ja) * 2009-06-01 2010-12-09 Sapporo Kokyu Imono Co Ltd セラミックス金属鋳ぐるみ複合材料及びその製造方法
CN201944152U (zh) * 2010-08-06 2011-08-24 昆明理工大学 表面强化的球墨铸铁刹车盘
JOP20200150A1 (ar) * 2011-04-06 2017-06-16 Esco Group Llc قطع غيار بأوجه مقواه باستخدام عملية التقسية المصلدة والطريقة والتجميع المرافق للتصنيع
CN102274946A (zh) 2011-08-29 2011-12-14 镇江汇通金属成型有限公司 一种复合压铸冲头
US8800848B2 (en) 2011-08-31 2014-08-12 Kennametal Inc. Methods of forming wear resistant layers on metallic surfaces

Also Published As

Publication number Publication date
MX2014008869A (es) 2014-09-01
US20130196169A1 (en) 2013-08-01
CN104093510A (zh) 2014-10-08
CN105414532A (zh) 2016-03-23
CN110153396A (zh) 2019-08-23
TR201816566T4 (tr) 2018-11-21
ES2693770T3 (es) 2018-12-13
CL2014001962A1 (es) 2014-10-10
CN104093510B (zh) 2017-07-07
US10543528B2 (en) 2020-01-28
MY167939A (en) 2018-10-04
EA201400851A1 (ru) 2014-11-28
US20200139431A1 (en) 2020-05-07
CA2860627A1 (en) 2013-08-08
KR102037764B1 (ko) 2019-10-29
AU2013202962B2 (en) 2015-10-08
NZ710921A (en) 2017-02-24
BR112014018839A2 (es) 2017-06-20
PE20142428A1 (es) 2015-01-22
NZ626215A (en) 2016-03-31
HK1198149A1 (en) 2015-03-13
EP2809466B1 (en) 2018-09-12
WO2013116183A1 (en) 2013-08-08
CO7030955A2 (es) 2014-08-21
EP2809466B8 (en) 2018-11-14
AU2013202962A1 (en) 2013-08-15
PH12014501414A1 (en) 2014-09-22
BR112014018839A8 (pt) 2017-07-11
PH12014501414B1 (en) 2014-09-22
SG11201403315YA (en) 2014-09-26
AP2014007838A0 (en) 2014-07-31
JP2015512785A (ja) 2015-04-30
EA032732B1 (ru) 2019-07-31
AU2013202962C1 (en) 2016-04-07
UA114099C2 (xx) 2017-04-25
EP2809466A4 (en) 2015-07-22
HRP20182085T1 (hr) 2019-02-08
MX2019014693A (es) 2020-02-07
JP6445868B2 (ja) 2018-12-26
PL2809466T3 (pl) 2019-02-28
MX370222B (es) 2019-12-05
TW201337071A (zh) 2013-09-16
KR20140119061A (ko) 2014-10-08
BR112014018839B1 (pt) 2019-03-26
JO3717B1 (ar) 2021-01-31
EP2809466A1 (en) 2014-12-10
TWI567270B (zh) 2017-01-21

Similar Documents

Publication Publication Date Title
AR089851A1 (es) Metodo y sistema para elaborar un material resistente al desgaste, articulo producido y miembro de desgaste
GB201020233D0 (en) Forming objects by infiltrating a printed matrix
WO2014149135A3 (en) Variable-density composite articles, preforms and methods
GB201020232D0 (en) 3D-printed bodies for molding downhole equipment
GB2460774B8 (en) Composite article with magnetocalorically active material and method for its production
PH12014502589A1 (en) Method for operating a high productivity injection molding machine
IL209786A (en) METHOD AND METHOD FOR MAKING PARTS OF COMPOSITE MATERIALS STRENGTHENED WITH MICROWAVES
JO3718B1 (ar) قطع غيار بأوجه مقواه بإستخدام عملية التقسية المصلدة والطريقة والتجميع المرافق للتصنيع
BR112015002192A2 (pt) aparelho de moldagem por injeção e método que compreende uma superfície de cavidade de molde que compreende uma matriz termicamente controlável
BR112016002868A2 (pt) método para produzir moldes não metálicos autoaquecíveis
WO2013155131A3 (en) Thermal isolation for casting articles
IN2014DN09328A (es)
MX2015000920A (es) Metodo para la fabricacion de un preforma, especialmente para uso en la fabricacion de recipientes.
GB2501033A (en) Method for connecting to a pipe
WO2013022490A3 (en) Ballistic applications of composite materials
MX367467B (es) Maquina para producir moldes de arena.
TH145010A (th) วัสดุต้านทานการสึก และระบบและวิธีการของการสร้างวัสดุต้านทานการสึก
FR2992888A1 (fr) Piece en materiau composite munie d'une protection thermique a base de resine et son procede de fabrication
UA81545U (ru) Сборка для крупного слитка
WO2014147230A3 (de) Verfahren und herstellungssystem zur herstellung eines faserverstärkten strukturbauteils
GB201200845D0 (en) Method of sealing cooling holes
MX2012012783A (es) Metodo para la elaboración de cavidades en moldes metálicos por prototipado rápido para la industria de rotomoldeo.
UA81716U (ru) Устройство для получения полых слитков
MX2013013773A (es) Procedimiento y dispositivo para producir piezas de plastico a partir de un material de plastico pulverulento.
UA82866U (ru) Способ получения крупной заготовки на машине непрерывного литья заготовок

Legal Events

Date Code Title Description
FG Grant, registration