WO2023038148A1 - ポリプロピレン系包装材料 - Google Patents
ポリプロピレン系包装材料 Download PDFInfo
- Publication number
- WO2023038148A1 WO2023038148A1 PCT/JP2022/034180 JP2022034180W WO2023038148A1 WO 2023038148 A1 WO2023038148 A1 WO 2023038148A1 JP 2022034180 W JP2022034180 W JP 2022034180W WO 2023038148 A1 WO2023038148 A1 WO 2023038148A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polypropylene
- layer
- packaging material
- ethylene
- mass
- Prior art date
Abstract
本発明は、ポリプロピレンを主成分とする樹脂がマトリックスであり、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有するエチレン-プロピレンブロック共重合体から成るポリプロピレン系包装材料に関するものであり、低温下における耐落下衝撃性、耐ブロッキング性、滑り性、フレーバー性の全てを備えた包装材料を提供できる。
Description
本発明は、ポリプロピレン系包装材料に関するものであり、より詳細には、耐落下衝撃性、耐ブロッキング性、滑り性、及びフレーバー性を備え、食品包装に好適に使用可能なポリプロピレン系包装材料及びこの包装材料から成る表層を有する積層体に関する。
プロピレン系重合体から成る包装材料は、ヒートシール性を発現可能であると共に、耐熱性や、衛生性、さらにはフレーバー性にも優れていることから、各種食品を収容する包装材料として広く利用されている。近年、軽量化や経済性の観点から、包装容器の薄肉化が進んでいることや、或いは寒冷地等での使用にも対応し得るために低温下での耐落下衝撃性(耐衝撃性)も必要とされ、より高い耐落下衝撃性が求められている。このような高い耐落下衝撃性を有するポリプロピレンとして、インパクトポリプロピレンとも呼ばれるプロピレンブロック共重合体を包装材料に使用することも行われている。
また包装材料に要求される他の性能として、耐ブロッキング性がある。すなわち、フィルム同士が重ね合わされたときにブロッキングが生じにくいことが必要であるが、上記プロピレンブロック共重合体から成るフィルムは、軟質なゴム成分が配合されていることから耐ブロッキング性に乏しく、更に改質されることが望まれている。
このような耐落下衝撃性及び耐ブロッキング性等の特性を改善するため、例えば下記特許文献1には、プロピレンブロック共重合体にエチレン・α-オレフィン共重合体を配合して成るプロピレン系樹脂組成物が提案されている。
このような耐落下衝撃性及び耐ブロッキング性等の特性を改善するため、例えば下記特許文献1には、プロピレンブロック共重合体にエチレン・α-オレフィン共重合体を配合して成るプロピレン系樹脂組成物が提案されている。
また下記特許文献2には、ポリプロピレンブロック共重合体を使用し、略球状のエラストマー粒子が分散して成る表層を有する多層フィルムが提案されている。
トレイやカップ等の容器においては、容器成形、内容物の充填・密封、梱包等が、搬送ラインで搬送されながら連続的に行われるため、ライン上で容器詰まりを生じない搬送性、すなわち滑り性を有することも要求されており、ポリプロピレン系包装材料においても優れた滑り性を有することも必要である。また食品用途においては特に、内容物のフレーバーを損なわないことも重要である。
しかしながら、上記特許文献1及び2に記載されたプロピレンブロック共重合体を用いた包装材料においては、低温条件下における耐落下衝撃性、耐ブロッキング性及び滑り性の全てを充分満足し得ることは困難であった。またこれらの性能と共に、外観特性やフレーバー性をも兼ね備えた包装材料を提供することは困難であった。
しかしながら、上記特許文献1及び2に記載されたプロピレンブロック共重合体を用いた包装材料においては、低温条件下における耐落下衝撃性、耐ブロッキング性及び滑り性の全てを充分満足し得ることは困難であった。またこれらの性能と共に、外観特性やフレーバー性をも兼ね備えた包装材料を提供することは困難であった。
従って本発明の目的は、低温条件下における耐落下衝撃性、耐ブロッキング性、滑り性、フレーバー性の全てを兼ね備えたポリプロピレン系包装材料及びこの包装材料を表層として備える積層体を提供することである。
本発明によれば、ポリプロピレンを主成分とする樹脂がマトリックスであり、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有するエチレン-プロピレンブロック共重合体であることを特徴とするポリプロピレン系包装材料が提供される。
本発明の包装材料においては、
[1]前記ドメインのアスペクト比が、1.2~9.0の範囲であること、
[2]前記ドメインの短径が0.2~4.0μm、長径が0.5~5.0μmの範囲にあること、
[3]前記ポリプロピレンを主成分とする樹脂100質量部に対して、前記ポリプロピレン系エラストマーを1~30質量部含有すること、
[4]前記ポリプロピレン系エラストマーの重量平均分子量(Mw)が50万~100万であり、数平均分子量(Mn)が1万~30万であること、
[5]前記ポリプロピレンを主成分とする樹脂の重量平均分子量(Mw)が30万~80万であり、数平均分子量(Mn)が1万~30万であること、
[6]前記エチレン-プロピレンブロック共重合体100質量部に対して、ホモポリプロピレンを1~30質量部含有すること、
[7]面粗さ(Sa)が、0.15~1.0μmであること、
[8]シート、フィルム、トレイ、カップの何れかの形状を有すること、
が好適である。
[1]前記ドメインのアスペクト比が、1.2~9.0の範囲であること、
[2]前記ドメインの短径が0.2~4.0μm、長径が0.5~5.0μmの範囲にあること、
[3]前記ポリプロピレンを主成分とする樹脂100質量部に対して、前記ポリプロピレン系エラストマーを1~30質量部含有すること、
[4]前記ポリプロピレン系エラストマーの重量平均分子量(Mw)が50万~100万であり、数平均分子量(Mn)が1万~30万であること、
[5]前記ポリプロピレンを主成分とする樹脂の重量平均分子量(Mw)が30万~80万であり、数平均分子量(Mn)が1万~30万であること、
[6]前記エチレン-プロピレンブロック共重合体100質量部に対して、ホモポリプロピレンを1~30質量部含有すること、
[7]面粗さ(Sa)が、0.15~1.0μmであること、
[8]シート、フィルム、トレイ、カップの何れかの形状を有すること、
が好適である。
本発明によればまた、上記ポリプロピレン系包装材料であるエチレン-プロピレンブロック共重合体から成るポリプロピレン層を表層として備える積層体であって、前記ポリプロピレン層の面粗さ(Sa)が、0.15~1.0μmであることを特徴とする積層体が提供される。
本発明の積層体においては、
[1]前記ポリプロピレン層を内外層、酸素吸収性層及びガスバリア性層を中間層として少なくとも備えること、
[2]トレイ又はカップの形状を有すること、
が好適である。
[1]前記ポリプロピレン層を内外層、酸素吸収性層及びガスバリア性層を中間層として少なくとも備えること、
[2]トレイ又はカップの形状を有すること、
が好適である。
本発明によればまた、エチレン-プロピレンブロック共重合体からなるポリプロピレン層を表層として備える積層体の製造方法において、前記エチレン-プロピレンブロック共重合体に、粘度調整剤としてホモポリプロピレンを配合して溶融混練することにより、MFR(230℃、2.16kg荷重)を0.1~10g/10分の範囲に粘度調整し、該粘度調整された溶融樹脂を押出すことにより、面粗さが0.15μm~1.0μmである表層を形成することを特徴とする積層体の製造方法が提供される。
本発明の積層体の製造方法においては、
[1]前記エチレン-プロピレンブロック共重合体100質量部に対して、前記ホモポリプロピレンを1~30質量部配合すること、
[2]前記エチレン-プロピレンブロック共重合体100質量部に対して、前記ポリプロピレン系エラストマーを1~30質量部含有すること、
[3]前記ポリプロピレン系エラストマーの重量平均分子量(Mw)が50万~100万であり、数平均分子量(Mn)が1万~30万であること、
[4]前記ポリプロピレンを主成分とする樹脂の重量平均分子量(Mw)が30万~80万であり、数平均分子量(Mn)が1万~30万であること、
が好適である。
[1]前記エチレン-プロピレンブロック共重合体100質量部に対して、前記ホモポリプロピレンを1~30質量部配合すること、
[2]前記エチレン-プロピレンブロック共重合体100質量部に対して、前記ポリプロピレン系エラストマーを1~30質量部含有すること、
[3]前記ポリプロピレン系エラストマーの重量平均分子量(Mw)が50万~100万であり、数平均分子量(Mn)が1万~30万であること、
[4]前記ポリプロピレンを主成分とする樹脂の重量平均分子量(Mw)が30万~80万であり、数平均分子量(Mn)が1万~30万であること、
が好適である。
本発明の包装材料は、ポリプロピレンを主成分とする樹脂をマトリックスとし、紡錘形状のポリプロピレン系エラストマーがドメインとなる分散構造を有し、且つこの紡錘形状のドメインの形状及び大きさが制御されていることにより、優れた耐落下衝撃性と滑り性及び耐ブロッキング性の両立が可能になる。
また特定のポリプロピレン系エラストマーを用いることにより、優れたフレーバー性を発現可能である。
また特定のポリプロピレン系エラストマーを用いることにより、優れたフレーバー性を発現可能である。
さらに本発明の積層体においては、上記ポリプロピレン系包装材料を表層として備え、該表層の面粗さ(Sa)が0.15~1.0μmであることにより、優れた耐落下衝撃性と滑り性及び耐ブロッキング性の両立が可能である。また本発明の積層体においては上記範囲の分子量を有するプロピレン系重合体が使用されていることにより、フレーバー性にも優れている。
また本発明の積層体の製造方法においては、ホモポリプロピレンを配合することにより、エチレン-プロピレンブロック共重合体の粘度を成形に適した粘度に調整することが可能となり、積層体の耐落下衝撃性を損なうことなく成形性(作業性)を改良することができる。
また本発明の積層体の製造方法においては、ホモポリプロピレンを配合することにより、エチレン-プロピレンブロック共重合体の粘度を成形に適した粘度に調整することが可能となり、積層体の耐落下衝撃性を損なうことなく成形性(作業性)を改良することができる。
(ポリプロピレン系包装材料)
本発明の包装材料は、上述した通り、ポリプロピレンを主成分とする樹脂をマトリックスとし、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有することが重要な特徴である。
本発明においては、ポリプロピレン系エラストマーから成る紡錘形状のドメインがポリプロピレンを主成分とする樹脂から成るマトリックス中に分散していることにより、耐落下衝撃性が更に向上されていると共に、このゴム成分から成るドメインの分散粒径が制御されていることにより、耐落下衝撃性のみならず、滑り性及び耐ブロッキング性の両立を図ることが可能となる。
すなわち、プロピレンブロック共重合体を用いた包装材料において、低温下でも優れた耐落下衝撃性を発現させるためには、ゴム成分(ポリプロピレン系エラストマー)の含有量が多く、且つこのゴム成分から成るドメイン(分散粒子)は耐落下衝撃性のみならず外観特性の点からも微分散していることが好適である。その一方、耐ブロッキング性や滑り性を向上させるためには、ゴム成分の含有量は少なく、且つこのゴム成分から成る分散粒子は表面に凹凸を形成できるように大きいことが好適である。
本発明においてはこのような観点から、ポリプロピレンを主成分とする樹脂から成るマトリックス中にポリプロピレン系エラストマーから成る紡錘形状のドメインが形成された分散構造を有することによって、優れた耐落下衝撃性と耐ブロッキング性及び滑り性を両立できることを見出した。
本発明の包装材料は、上述した通り、ポリプロピレンを主成分とする樹脂をマトリックスとし、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有することが重要な特徴である。
本発明においては、ポリプロピレン系エラストマーから成る紡錘形状のドメインがポリプロピレンを主成分とする樹脂から成るマトリックス中に分散していることにより、耐落下衝撃性が更に向上されていると共に、このゴム成分から成るドメインの分散粒径が制御されていることにより、耐落下衝撃性のみならず、滑り性及び耐ブロッキング性の両立を図ることが可能となる。
すなわち、プロピレンブロック共重合体を用いた包装材料において、低温下でも優れた耐落下衝撃性を発現させるためには、ゴム成分(ポリプロピレン系エラストマー)の含有量が多く、且つこのゴム成分から成るドメイン(分散粒子)は耐落下衝撃性のみならず外観特性の点からも微分散していることが好適である。その一方、耐ブロッキング性や滑り性を向上させるためには、ゴム成分の含有量は少なく、且つこのゴム成分から成る分散粒子は表面に凹凸を形成できるように大きいことが好適である。
本発明においてはこのような観点から、ポリプロピレンを主成分とする樹脂から成るマトリックス中にポリプロピレン系エラストマーから成る紡錘形状のドメインが形成された分散構造を有することによって、優れた耐落下衝撃性と耐ブロッキング性及び滑り性を両立できることを見出した。
本発明においては、ポリプロピレン系エラストマーから成るドメインによる優れた耐落下衝撃性を発現するために、上記紡錘形状のドメインのアスペクト比が1.2~9.0、1.2~8.0、1.9~8.0、特に1.9~5.0の範囲にある紡錘形状であることが好ましい。アスペクト比が大きいと耐落下衝撃性は良いが滑り性に劣る傾向がある。またかかるドメインは、短径が0.2~4.0μm、特に0.2~2.0μm、長径が0.5~5.0μm、特に0.5~3.0μmの範囲にあることが好適である。尚、ドメインの短径及び長径の測定方法については後述する。
また、円相当のドメインサイズは、0.5μm~5.0μm、特に0.5μm~1.0μmの範囲にあることが好ましい。ドメインサイズは小さすぎると表面の凹凸が形成されず滑り性に劣り、大きすぎると凹凸が形成され滑り性は良いが耐落下衝撃性に劣る傾向がある。
また、円相当のドメインサイズは、0.5μm~5.0μm、特に0.5μm~1.0μmの範囲にあることが好ましい。ドメインサイズは小さすぎると表面の凹凸が形成されず滑り性に劣り、大きすぎると凹凸が形成され滑り性は良いが耐落下衝撃性に劣る傾向がある。
前述したドメイン形状及びサイズの制御は、マトリックスであるポリプロピレンを主成分とする樹脂及びポリプロピレン系エラストマーの分子量や組成、混練等の樹脂製造方法により決定される。
本発明の包装材料において、ポリプロピレン系エラストマーは、ポリプロピレンを主成分とする樹脂100質量部に対して、1~30質量部、特に5.0~25質量部の量で含有されていることが好ましい。上記範囲よりもポリプロピレン系エラストマーの量が少ないと、上記範囲にある場合に比して耐落下衝撃性を充分に向上することができないおそれがあり、その一方上記範囲よりもポリプロピレン系エラストマーの量が多いと、上記範囲にある場合に比して、耐ブロッキング性及び滑り性が低下するだけでなく、フレーバー性が低下すると共に、表面凹凸も大きくなり外観特性に劣るようになる。
本発明の包装材料において、ポリプロピレン系エラストマーは、ポリプロピレンを主成分とする樹脂100質量部に対して、1~30質量部、特に5.0~25質量部の量で含有されていることが好ましい。上記範囲よりもポリプロピレン系エラストマーの量が少ないと、上記範囲にある場合に比して耐落下衝撃性を充分に向上することができないおそれがあり、その一方上記範囲よりもポリプロピレン系エラストマーの量が多いと、上記範囲にある場合に比して、耐ブロッキング性及び滑り性が低下するだけでなく、フレーバー性が低下すると共に、表面凹凸も大きくなり外観特性に劣るようになる。
[ポリプロピレンを主成分とする樹脂]
本発明の包装材料において、マトリックスとなるポリプロピレンを主成分とする樹脂は、プロピレンを主体とする単量体が重合されてなるホモ或いはランダムポリプロピレンである。
ポリプロピレンを主成分とする樹脂は、重量平均分子量(Mw)が30万~80万、特に30万~60万の範囲にあり、数平均分子量(Mn)が1万~30万、特に5万~20万の範囲にあることが好適である。ポリプロピレンを主成分とする樹脂の分子量が上記範囲よりも小さい場合には、上記範囲にある場合に比して耐落下衝撃性の低下や衛生性が損なわれるおそれがあり、一方上記範囲よりも大きい場合には、上記範囲にある場合に比して樹脂圧異常により成形性が低下するおそれがある。
またポリプロピレンを主成分とする樹脂は、耐熱性や成形性の観点から、立体規則性の指標であるメソペンタッド分率([mmmm])が95~99の範囲にあることが好適である。
本発明の包装材料において、マトリックスとなるポリプロピレンを主成分とする樹脂は、プロピレンを主体とする単量体が重合されてなるホモ或いはランダムポリプロピレンである。
ポリプロピレンを主成分とする樹脂は、重量平均分子量(Mw)が30万~80万、特に30万~60万の範囲にあり、数平均分子量(Mn)が1万~30万、特に5万~20万の範囲にあることが好適である。ポリプロピレンを主成分とする樹脂の分子量が上記範囲よりも小さい場合には、上記範囲にある場合に比して耐落下衝撃性の低下や衛生性が損なわれるおそれがあり、一方上記範囲よりも大きい場合には、上記範囲にある場合に比して樹脂圧異常により成形性が低下するおそれがある。
またポリプロピレンを主成分とする樹脂は、耐熱性や成形性の観点から、立体規則性の指標であるメソペンタッド分率([mmmm])が95~99の範囲にあることが好適である。
[ポリプロピレン系エラストマー]
本発明の包装材料において、紡錘形状のドメインを構成するポリプロピレン系エラストマーとしては、例えばプロピレン-エチレン系エラストマーが挙げられる。プロピレン-エチレン系エラストマーとしては、プロピレンとエチレンとのランダム共重合体であって、エチレン単位とプロピレン単位の質量比が、15:85~50:50の範囲にある共重合体が好ましい。また、必要に応じて、相溶性や耐落下衝撃性向上のためα-オレフィン等を共重合したエラストマーを使用してもよい。
ポリプロピレン系エラストマーは、重量平均分子量(Mw)が50万~100万、好適には65万~100万、より好適には70万~100万、特に好適には70万~90万の範囲にあり、数平均分子量(Mn)が1万~30万、好適には2万~20万、特に好適には10万~20万の範囲にあることが望ましい。上記範囲よりも分子量が小さい場合には、上記範囲にある場合に比してドメイン形状が筋状となり粒径が小さく微分散となり容器の表面凹凸が平滑となり耐ブロッキング性や滑り性を満足出来ないおそれがあり、一方上記範囲よりも分子量が大きい場合には、ドメイン形状が略球状となり粒径が大きく疎分散となるため耐落下衝撃性に劣るおそれがある。さらには、フレーバー性が低下する傾向がある。
よって、ポリプロピレン系エラストマーのエチレン単位とプロピレン単位の質量比や分子量、ポリプロピレンを主成分とする樹脂の分子量を制御することにより、ポリプロピレン系エラストマーのドメインを上述したアスペクト比を有する紡錘形状に伸長することができると共に、両者の相溶性が向上し、上述した大きさに微分散することが可能となり、耐落下衝撃性と、耐ブロッキング性及び滑り性の両立が可能となる。
本発明の包装材料において、紡錘形状のドメインを構成するポリプロピレン系エラストマーとしては、例えばプロピレン-エチレン系エラストマーが挙げられる。プロピレン-エチレン系エラストマーとしては、プロピレンとエチレンとのランダム共重合体であって、エチレン単位とプロピレン単位の質量比が、15:85~50:50の範囲にある共重合体が好ましい。また、必要に応じて、相溶性や耐落下衝撃性向上のためα-オレフィン等を共重合したエラストマーを使用してもよい。
ポリプロピレン系エラストマーは、重量平均分子量(Mw)が50万~100万、好適には65万~100万、より好適には70万~100万、特に好適には70万~90万の範囲にあり、数平均分子量(Mn)が1万~30万、好適には2万~20万、特に好適には10万~20万の範囲にあることが望ましい。上記範囲よりも分子量が小さい場合には、上記範囲にある場合に比してドメイン形状が筋状となり粒径が小さく微分散となり容器の表面凹凸が平滑となり耐ブロッキング性や滑り性を満足出来ないおそれがあり、一方上記範囲よりも分子量が大きい場合には、ドメイン形状が略球状となり粒径が大きく疎分散となるため耐落下衝撃性に劣るおそれがある。さらには、フレーバー性が低下する傾向がある。
よって、ポリプロピレン系エラストマーのエチレン単位とプロピレン単位の質量比や分子量、ポリプロピレンを主成分とする樹脂の分子量を制御することにより、ポリプロピレン系エラストマーのドメインを上述したアスペクト比を有する紡錘形状に伸長することができると共に、両者の相溶性が向上し、上述した大きさに微分散することが可能となり、耐落下衝撃性と、耐ブロッキング性及び滑り性の両立が可能となる。
本発明のポリプロピレン系エラストマーが紡錘形状になる点について、以下のとおり推察する。製膜したフィルムやシートまたはカップやトレイ等の二次加工した容器においては、押出(成形)する方向に樹脂が引き延ばされる。そのため、樹脂中のドメイン形状も追従し、押出方向の先端が先細りになり図1に示すような紡錘形状となる。しかし、マトリックスとドメインの分子量の違いやドメイン自体の分子量、マトリックスとドメインの相溶性によりドメイン形状が異なることが考えられる。例えば、ドメインの分子量が低くマトリックスと相溶性が高い場合には筋状となり、面粗さが低く平滑であるため滑り性が悪いと推測する。一方、ドメインの分子量が高くマトリックスとの相溶性が低い場合は略球状となり、耐落下衝撃性に劣ると推測する。なお、相溶性はポリプロピレン系エラストマーの組成やエチレン-αオレフィン共重合体等の添加により影響する。
[エチレン-プロピレンブロック共重合体]
ポリプロピレンを主成分とする樹脂がマトリックスであり、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有するエチレン-プロピレンブロック共重合体のMFR(230℃、2.16kg荷重)は、0.1~10g/10分、特に0.2~5g/10分の範囲にあることが成形面で好適である。
また、ポリプロピレンを主成分とする樹脂やポリプロピレン系エラストマーの原料もしくは原料の一部が石油由来のみならず廃棄プラスチックからガス化や油化等のモノマー化技術よりケミカルリサイクルされた材料もしくは植物由来等のバイオマス材料から製造されたエチレン-プロピレンブロック共重合体であってもよい。バイオマス度は放射性炭素濃度測定等により測定できる。 さらに、ポリプロピレンを主成分とする樹脂やポリプロピレン系エラストマーを製造する際、原料からの重合段階において、環境負荷低減の観点からフタル酸エステル化合物等のSVHC物質(欧州のRegistration,Evaluation,Authorization and Restriction of Chemicals(REACH)規制におけるSubstance of Very High Concern)を使用しない触媒系で製造することが望ましい。
ポリプロピレンを主成分とする樹脂がマトリックスであり、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有するエチレン-プロピレンブロック共重合体のMFR(230℃、2.16kg荷重)は、0.1~10g/10分、特に0.2~5g/10分の範囲にあることが成形面で好適である。
また、ポリプロピレンを主成分とする樹脂やポリプロピレン系エラストマーの原料もしくは原料の一部が石油由来のみならず廃棄プラスチックからガス化や油化等のモノマー化技術よりケミカルリサイクルされた材料もしくは植物由来等のバイオマス材料から製造されたエチレン-プロピレンブロック共重合体であってもよい。バイオマス度は放射性炭素濃度測定等により測定できる。 さらに、ポリプロピレンを主成分とする樹脂やポリプロピレン系エラストマーを製造する際、原料からの重合段階において、環境負荷低減の観点からフタル酸エステル化合物等のSVHC物質(欧州のRegistration,Evaluation,Authorization and Restriction of Chemicals(REACH)規制におけるSubstance of Very High Concern)を使用しない触媒系で製造することが望ましい。
[他の成分]
本発明の包装材料においては、上述したエチレン-プロピレンブロック共重合体以外に、粘度調整剤としてホモポリプロピレンを配合することが好適である。
すなわち、ポリプロピレンを主成分とする樹脂及びポリプロピレン系エラストマーから成る樹脂組成物は、耐落下衝撃性と滑り性を両立するためポリプロピレン系エラストマーの分子量が高い傾向であり粘度が高く、成形性に劣る場合があることから、ホモポリプロピレンを配合することにより粘度を調整し、溶融樹脂の押出性を改良することができ、包装材料の耐落下衝撃性を損なうことなく成形性(作業性)を改良することができる。
ホモポリプロピレンのMFR(230℃、2.16kg荷重)は、粘度調整という観点から、0.5~20g/10分の範囲にあることが好ましい。
ホモポリプロピレンは、エチレン-プロピレンブロック共重合体100質量部に対して、1~40質量部、特に1~30質量部の量で添加することが好適である。
本発明の包装材料においては、上述したエチレン-プロピレンブロック共重合体以外に、粘度調整剤としてホモポリプロピレンを配合することが好適である。
すなわち、ポリプロピレンを主成分とする樹脂及びポリプロピレン系エラストマーから成る樹脂組成物は、耐落下衝撃性と滑り性を両立するためポリプロピレン系エラストマーの分子量が高い傾向であり粘度が高く、成形性に劣る場合があることから、ホモポリプロピレンを配合することにより粘度を調整し、溶融樹脂の押出性を改良することができ、包装材料の耐落下衝撃性を損なうことなく成形性(作業性)を改良することができる。
ホモポリプロピレンのMFR(230℃、2.16kg荷重)は、粘度調整という観点から、0.5~20g/10分の範囲にあることが好ましい。
ホモポリプロピレンは、エチレン-プロピレンブロック共重合体100質量部に対して、1~40質量部、特に1~30質量部の量で添加することが好適である。
また本発明の包装材料においては、更なる耐落下衝撃性向上のため高密度ポリエチレン、中密度ポリエチレン、低密度ポリエチレン、線状低密度ポリエチレン等のエチレン-α-オレフィン共重合体、エラストマーやプラストマー等のゴム成分を添加してもよい。さらに、滑り性向上のためステアリン酸カルシウム等の滑剤やシリカ粒子等のアンチブロッキング剤の添加、上述したゴム成分との併用も可能である。公知の添加剤、例えば、酸化防止剤などを少量配合することも必要に応じてできる。
近年の環境問題の高まりより脱プラの一環として、廃棄プラスチックからガス化や油化等のモノマー化技術よりケミカルリサイクルされた材料もしくは植物由来等のバイオマス材料を配合することも重要である。
近年の環境問題の高まりより脱プラの一環として、廃棄プラスチックからガス化や油化等のモノマー化技術よりケミカルリサイクルされた材料もしくは植物由来等のバイオマス材料を配合することも重要である。
(ポリプロピレン系包装材料の調製)
本発明の包装材料は、溶融押出する方法や、或いはこれらのペレットを混練機で溶融混練する方法等、公知の方法により調製することができる。
本発明において、ポリプロピレン系エラストマーのドメインが前述した大きさ及びアスペクト比の紡錘形状である分散状態となるように、溶融混練することが必要であり、用いる樹脂の粘度等に応じて適宜混練条件を調整することが必要である。
溶融混練における温度条件は特に制限はないが、170~270℃の範囲で行うことが好ましい。上記範囲よりも低い温度では、効率よく混練することができないおそれがあり、上記範囲よりも高い温度では樹脂の劣化を招くおそれがある。
本発明の包装材料は、溶融押出する方法や、或いはこれらのペレットを混練機で溶融混練する方法等、公知の方法により調製することができる。
本発明において、ポリプロピレン系エラストマーのドメインが前述した大きさ及びアスペクト比の紡錘形状である分散状態となるように、溶融混練することが必要であり、用いる樹脂の粘度等に応じて適宜混練条件を調整することが必要である。
溶融混練における温度条件は特に制限はないが、170~270℃の範囲で行うことが好ましい。上記範囲よりも低い温度では、効率よく混練することができないおそれがあり、上記範囲よりも高い温度では樹脂の劣化を招くおそれがある。
本発明の包装材料は、溶融混練された樹脂を押出成形又は射出成形等公知の製造方法により、フィルム、シート、チューブ等所望の形状に成形することができ、或いは得られたシートから熱成形によりカップ、トレイ等の形状に成形することができる。
本発明の包装材料は、面粗さ(Sa)が、0.15~1.0μmの範囲にあることが好適である。これにより、外観特性を損なうことなく、優れた耐ブロッキング性及び滑り性を発現できる。尚、面粗さ(Sa)は、線の算術平均高さ:Raを面に拡張したパラメーターであり、ISO25178で規定されている、表面の平均面に対して、各点の高さの差の絶対値の平均である。
本発明の包装材料は、面粗さ(Sa)が、0.15~1.0μmの範囲にあることが好適である。これにより、外観特性を損なうことなく、優れた耐ブロッキング性及び滑り性を発現できる。尚、面粗さ(Sa)は、線の算術平均高さ:Raを面に拡張したパラメーターであり、ISO25178で規定されている、表面の平均面に対して、各点の高さの差の絶対値の平均である。
(積層体)
本発明においては、上述したエチレン-プロピレンブロック共重合体から成る樹脂組成物の単層構成の成形体であってもよいが、他の層を備えた多層構造を有する積層体とすることもできる。
このような多層構造にする場合には、上述したエチレン-プロピレンブロック共重合体の樹脂組成物から成るポリプロピレン層が、表層(最外層又は最内層)であることが好適であり、特に最外層であることが望ましい。すなわち、積層体の表層が、ポリプロピレン系エラストマーから成る紡錘形状のドメインがポリプロピレンを主成分とする樹脂から成るマトリックス中に分散している分散構造を有していることにより、耐落下衝撃性が更に向上され、低温下においても優れた耐落下衝撃性を発現できると共に、面粗さが上記範囲にあることにより、優れた滑り性及び耐ブロッキング性を発現することが可能となる。
本発明においては、上述したエチレン-プロピレンブロック共重合体から成る樹脂組成物の単層構成の成形体であってもよいが、他の層を備えた多層構造を有する積層体とすることもできる。
このような多層構造にする場合には、上述したエチレン-プロピレンブロック共重合体の樹脂組成物から成るポリプロピレン層が、表層(最外層又は最内層)であることが好適であり、特に最外層であることが望ましい。すなわち、積層体の表層が、ポリプロピレン系エラストマーから成る紡錘形状のドメインがポリプロピレンを主成分とする樹脂から成るマトリックス中に分散している分散構造を有していることにより、耐落下衝撃性が更に向上され、低温下においても優れた耐落下衝撃性を発現できると共に、面粗さが上記範囲にあることにより、優れた滑り性及び耐ブロッキング性を発現することが可能となる。
[多層構造]
本発明の積層体においては、上述したポリプロピレン層は表層(最外層又は最内層)であることが重要であり、少なくとも最外層、好適には最外層及び最内層の両方であることが好ましい。表層がポリプロピレン層から成る限り種々の多層構造を有することができるが、ガスバリア層、酸素吸収性層、接着層、リグラインド層、吸着剤含有層等、従来公知の他の層を中間層として有することが好適である。
本発明の積層体は、これに限定されないが、以下の層構成を例示することができる。
ポリプロピレン層(最外層)/接着層/ガスバリア層/接着層/ポリプロピレン表層(最内層)、ポリプロピレン層(最外層)/接着層/ガスバリア層/接着層/酸素吸収性層/ポリプロピレン層(最内層)、ポリプロピレン層(最外層)/接着層/ガスバリア層/接着層/酸素吸収性層/接着層/ガスバリア層/接着層/ポリプロピレン層(最内層)、ポリプロピレン層(最外層)/リグラインド層/接着層/ガスバリア層/接着層/酸素吸収性層/ポリプロピレン層(最内層)、ポリプロピレン層(最外層)/リグラインド層/接着層/ガスバリア層/接着層/ポリプロピレン表層(最内層)、ポリプロピレン層(最外層)/リグラインド層/接着層/ガスバリア層/ガスバリア性樹脂をマトリックス樹脂とする酸素吸収性層/ガスバリア層/接着層/吸着剤含有層/ポリプロピレン層(最内層)等を例示できる。
尚、最内層は、上記ポリプロピレン層に変えて、或いは上記ポリプロピレン層に加えて、易剥離性樹脂から成る層にすることもできる。
本発明の積層体においては、上述したポリプロピレン層は表層(最外層又は最内層)であることが重要であり、少なくとも最外層、好適には最外層及び最内層の両方であることが好ましい。表層がポリプロピレン層から成る限り種々の多層構造を有することができるが、ガスバリア層、酸素吸収性層、接着層、リグラインド層、吸着剤含有層等、従来公知の他の層を中間層として有することが好適である。
本発明の積層体は、これに限定されないが、以下の層構成を例示することができる。
ポリプロピレン層(最外層)/接着層/ガスバリア層/接着層/ポリプロピレン表層(最内層)、ポリプロピレン層(最外層)/接着層/ガスバリア層/接着層/酸素吸収性層/ポリプロピレン層(最内層)、ポリプロピレン層(最外層)/接着層/ガスバリア層/接着層/酸素吸収性層/接着層/ガスバリア層/接着層/ポリプロピレン層(最内層)、ポリプロピレン層(最外層)/リグラインド層/接着層/ガスバリア層/接着層/酸素吸収性層/ポリプロピレン層(最内層)、ポリプロピレン層(最外層)/リグラインド層/接着層/ガスバリア層/接着層/ポリプロピレン表層(最内層)、ポリプロピレン層(最外層)/リグラインド層/接着層/ガスバリア層/ガスバリア性樹脂をマトリックス樹脂とする酸素吸収性層/ガスバリア層/接着層/吸着剤含有層/ポリプロピレン層(最内層)等を例示できる。
尚、最内層は、上記ポリプロピレン層に変えて、或いは上記ポリプロピレン層に加えて、易剥離性樹脂から成る層にすることもできる。
本発明の積層体においては、各層の層厚みは、積層体の形態や製造方法等によって異なり、一概に規定できないが、フィルム又はシートの場合には、ポリプロピレン表層(最外層)の厚みは、5~800μm、特に5~500μmの範囲にあり、ポリプロピレン表層(最内層)の厚みは、5~800μm、特に5~500μmの範囲にあることが好ましい。また他の層の厚みは、最外層、最内層が上記の厚み範囲にある場合において、ガスバリア層(複数形成する場合は合計厚み)は、5~500μm、特に5~200μmの範囲にあることが好ましく、酸素吸収性層は、5~500μm、特に5~200μmの範囲にあることが好ましい。またリグラインド層を設ける場合には、50~1000μm、特に50~800μmの範囲で形成することが好ましい。更に、吸着剤含有層を設ける場合には、5~500μm、特に5~300μmの範囲で形成することが好ましい。
また本発明の積層体が、圧空成形等の熱成形による多層容器(カップ、トレイ等)の場合には、多層容器の最薄肉部となる胴部において、ポリプロピレン表層(最外層)の厚みは、1~160μm、特に1~100μmの範囲にあり、ポリプロピレン表層(最内層)の厚みは、1~160μm、特に1~100μmの範囲にあることが好ましい。また他の層の厚みは、最外層、最内層が上記の厚み範囲にある場合において、ガスバリア層(複数形成する場合は合計厚み)は、1~100μm、特に1~40μmの範囲にあることが好ましく、酸素吸収性層は、1~100μm、特に1~40μmの範囲にあることが好ましい。またリグラインド層を設ける場合には、10~200μm、特に10~160μmの範囲で形成することが好ましい。更に、吸着剤含有層を設ける場合には、1~100μm、特に1~60μmの範囲で形成することが好ましい。
これにより、耐落下衝撃性や成形性を損なうことなく、ガスバリア性や酸素吸収性或いはフレーバー性等の各層が有する効果を充分に発揮することが可能になる。
これにより、耐落下衝撃性や成形性を損なうことなく、ガスバリア性や酸素吸収性或いはフレーバー性等の各層が有する効果を充分に発揮することが可能になる。
[ガスバリア層]
本発明の積層体においてガスバリア層は、従来公知のバリア性樹脂を使用することができるが、特にエチレン-ビニルアルコール共重合体から成ることが好適である。エチレン-ビニルアルコール共重合体は、例えば、エチレン含有量が20~60mol%、特に25~50mol%のエチレン-酢酸ビニル共重合体を、ケン化度が96%以上、特に99mol%以上となるようにケン化して得られる共重合体ケン化物がガスバリア性の点で好適であるが、本発明においては特に、エチレン含有量が20~35mol%のエチレン-ビニルアルコール共重合体と、エチレン含有量が36~50mol%のエチレン-ビニルアルコール共重合体を、90:10~50:50、特に80:20~60:40の配合比(質量比)でブレンドして使用することが好ましい。これにより、ガスバリア層が優れたガスバリア性を維持しつつ成形性が改良されるため、外観ムラのない積層体を成形することが可能になる。
このエチレン-ビニルアルコール共重合体は、フィルムを形成し得るに足る分子量を有するべきであり、一般に、[フェノール/水]の質量比が85/15の混合溶媒中、30℃で測定して0.01dl/g以上、特に0.05dl/g以上の固有粘度を有することが望ましい。
本発明の積層体においてガスバリア層は、従来公知のバリア性樹脂を使用することができるが、特にエチレン-ビニルアルコール共重合体から成ることが好適である。エチレン-ビニルアルコール共重合体は、例えば、エチレン含有量が20~60mol%、特に25~50mol%のエチレン-酢酸ビニル共重合体を、ケン化度が96%以上、特に99mol%以上となるようにケン化して得られる共重合体ケン化物がガスバリア性の点で好適であるが、本発明においては特に、エチレン含有量が20~35mol%のエチレン-ビニルアルコール共重合体と、エチレン含有量が36~50mol%のエチレン-ビニルアルコール共重合体を、90:10~50:50、特に80:20~60:40の配合比(質量比)でブレンドして使用することが好ましい。これにより、ガスバリア層が優れたガスバリア性を維持しつつ成形性が改良されるため、外観ムラのない積層体を成形することが可能になる。
このエチレン-ビニルアルコール共重合体は、フィルムを形成し得るに足る分子量を有するべきであり、一般に、[フェノール/水]の質量比が85/15の混合溶媒中、30℃で測定して0.01dl/g以上、特に0.05dl/g以上の固有粘度を有することが望ましい。
また、エチレン-ビニルアルコール共重合体以外のガスバリア性樹脂の例としては、例えば、ナイロン6、ナイロン6・6、ナイロン6/6・6共重合体、メタキシリレンジアジパミド(MXD6)、ナイロン6・10、ナイロン11、ナイロン12、ナイロン13等のポリアミドを挙げることができる。これらのポリアミドの中でも、炭素数100個当りのアミド基の数が5~50個、特に6~20個の範囲にあるものが好適である。これらのポリアミドもフィルムを形成するに足る分子量を有するべきであり、例えば、濃硫酸(濃度1.0g/dl)中、30℃で測定した相対粘度が1.1以上、特に1.5以上であることが望ましい。
尚、ポリアミドはエチレン-ビニルアルコール共重合体にブレンドしてもよく、エチレン-ビニルアルコール共重合体と、ポリアミドの配合比(質量比)が50:50~99:1が好適である。
また、後述するように酸素吸収性樹脂組成物のマトリックス樹脂として、ポリアミドを使用する場合、末端アミノ基濃度が40eq/106g以上のポリアミド樹脂が、酸素吸収時の酸化劣化がないため望ましい。
尚、ポリアミドはエチレン-ビニルアルコール共重合体にブレンドしてもよく、エチレン-ビニルアルコール共重合体と、ポリアミドの配合比(質量比)が50:50~99:1が好適である。
また、後述するように酸素吸収性樹脂組成物のマトリックス樹脂として、ポリアミドを使用する場合、末端アミノ基濃度が40eq/106g以上のポリアミド樹脂が、酸素吸収時の酸化劣化がないため望ましい。
[酸素吸収性層]
本発明の積層体において酸素吸収性層は、前述したポリプロピレン層を構成するプロピレン系重合体や公知のプロピレン系重合体(以下、これらを合わせて単に「プロピレン系重合体」ということがある)、ガスバリア性樹脂、或いはリグラインド樹脂等をマトリックス樹脂として、無機系酸素吸収剤、或いは、(i)酸化性有機成分及び(ii)遷移金属触媒(酸化触媒)からなる有機系酸素吸収剤を上記マトリックス樹脂に含有させて成る樹脂組成物から成ることができる。
本発明の積層体において酸素吸収性層は、前述したポリプロピレン層を構成するプロピレン系重合体や公知のプロピレン系重合体(以下、これらを合わせて単に「プロピレン系重合体」ということがある)、ガスバリア性樹脂、或いはリグラインド樹脂等をマトリックス樹脂として、無機系酸素吸収剤、或いは、(i)酸化性有機成分及び(ii)遷移金属触媒(酸化触媒)からなる有機系酸素吸収剤を上記マトリックス樹脂に含有させて成る樹脂組成物から成ることができる。
(無機系酸素吸収剤)
無機系酸素吸収剤としては、鉄粉、酸化チタン、酸化セリウム、第一鉄塩、亜二チオン酸塩、亜硫酸塩、ハロゲン化金属、ゼオライト等が挙げられる。特に鉄粉及びハロゲン化金属が望ましい。該鉄粉としては、還元鉄粉、アトマイズ鉄粉、電解鉄粉、カルボニル鉄粉等、公知の鉄粉を使用することができる。これらの中でも、多孔質であり比較的比表面積の大きい還元鉄粉、特にロータリー還元鉄粉を好適に用いることができる。ロータリー還元鉄粉は、純度が高く、比表面積が大きいことから、酸素吸収性能に優れている。これらの鉄粉は一種を用いてもよく、二種以上を併用してもよい。酸素吸収剤中の鉄粉の含有量は、酸素吸収剤100質量部に対し、3~40質量部であることが好ましく、5~30質量部であることがより好ましい。
無機系酸素吸収剤としては、鉄粉、酸化チタン、酸化セリウム、第一鉄塩、亜二チオン酸塩、亜硫酸塩、ハロゲン化金属、ゼオライト等が挙げられる。特に鉄粉及びハロゲン化金属が望ましい。該鉄粉としては、還元鉄粉、アトマイズ鉄粉、電解鉄粉、カルボニル鉄粉等、公知の鉄粉を使用することができる。これらの中でも、多孔質であり比較的比表面積の大きい還元鉄粉、特にロータリー還元鉄粉を好適に用いることができる。ロータリー還元鉄粉は、純度が高く、比表面積が大きいことから、酸素吸収性能に優れている。これらの鉄粉は一種を用いてもよく、二種以上を併用してもよい。酸素吸収剤中の鉄粉の含有量は、酸素吸収剤100質量部に対し、3~40質量部であることが好ましく、5~30質量部であることがより好ましい。
前記ハロゲン化金属としては、アルカリ金属、アルカリ土類金属、銅、亜鉛、鉄等のハロゲン化物が挙げられる。具体的には、塩化ナトリウム、臭化ナトリウム、ヨウ化ナトリウム、塩化カリウム、臭化カリウム、ヨウ化カリウム、塩化カルシウム、塩化マグネシウム、塩化バリウム等が挙げられる。これらの中でも塩化ナトリウムが好ましい。これらのハロゲン化金属は一種を用いてもよく、二種以上を併用してもよい。
前記ハロゲン化金属は、酸素吸収剤の主剤である鉄粉100質量部に対して0.1~10質量部配合することが好ましく、1~5質量部配合することがより好ましい。ハロゲン化金属を鉄粉100質量部に対して0.1質量部以上配合することにより、十分な酸素吸収性能を得ることができる。また、ハロゲン化金属を鉄粉100質量部に対して10質量部以下配合することにより、鉄粉含有量の低下による酸素吸収性能の低下を抑制することができ、またハロゲン化金属の染み出しによる外観不良や内容物への付着を抑制することができる。
本発明に係る酸素吸収剤は、鉄粉及びハロゲン化金属以外に、さらにアルカリ性物質を含んでもよい。アルカリ性物質を含むことにより、鉄と水との反応により生成する水素の発生量を低減することができる。前記アルカリ性物質としては、例えば水酸化マグネシウム、水酸化カルシウム、水酸化ストロンチウム、水酸化バリウム、炭酸マグネシウム、炭酸カルシウム、炭酸ストロンチウム、炭酸バリウム等が挙げられる。これらの中でも、水酸化カルシウム、水酸化カルシウムの脱水物である酸化カルシウムが好ましい。これらのアルカリ性物質は一種を用いてもよく、二種以上を併用してもよい。
(有機系酸素吸収剤)
(i)酸化性有機成分
酸化性有機成分としては、エチレン系不飽和基含有重合体を挙げることができる。この重合体は、炭素-炭素二重結合を有しており、この二重結合部分や特に二重結合部に隣接したαメチレンが酸素により容易に酸化され、これにより酸素の捕捉が行われる。
このようなエチレン系不飽和基含有重合体は、例えば、ポリエンを単量体として誘導されたポリエンの単独重合体、或いは上記ポリエンを2種以上組み合わせ若しくは他の単量体と組み合わせてのランダム共重合体、ブロック共重合体等を酸化性重合体として用いることができる。
ポリエンから誘導される重合体の中でも、ポリブタジエン(BR)、ポリイソプレン(IR)、天然ゴム、ニトリル-ブタジエンゴム(NBR)、スチレン-ブタジエンゴム(SBR)、クロロプレンゴム、エチレン-プロピレン-ジエンゴム(EPDM)等が好適であるが、勿論、これらに限定されない。
(i)酸化性有機成分
酸化性有機成分としては、エチレン系不飽和基含有重合体を挙げることができる。この重合体は、炭素-炭素二重結合を有しており、この二重結合部分や特に二重結合部に隣接したαメチレンが酸素により容易に酸化され、これにより酸素の捕捉が行われる。
このようなエチレン系不飽和基含有重合体は、例えば、ポリエンを単量体として誘導されたポリエンの単独重合体、或いは上記ポリエンを2種以上組み合わせ若しくは他の単量体と組み合わせてのランダム共重合体、ブロック共重合体等を酸化性重合体として用いることができる。
ポリエンから誘導される重合体の中でも、ポリブタジエン(BR)、ポリイソプレン(IR)、天然ゴム、ニトリル-ブタジエンゴム(NBR)、スチレン-ブタジエンゴム(SBR)、クロロプレンゴム、エチレン-プロピレン-ジエンゴム(EPDM)等が好適であるが、勿論、これらに限定されない。
また、上述したエチレン系不飽和基含有重合体以外にも、それ自体酸化されやすい重合体、例えばポリプロピレン、エチレン・プロピレン共重合体、或いは末端アミノ基濃度が40eq/106g未満のポリメタキシリレンジアジパミド等も酸化性有機成分として使用することができる。
尚、成形性等の見地から、上述した酸化性重合体やその共重合体の40℃での粘度は1~200Pa・sの範囲にあることが好適である。
これらのポリエン系重合体は、カルボン酸基、カルボン酸無水物基、水酸基が導入された酸変性ポリエン重合体であることが好ましい。
これらの酸化性重合体、或いはその共重合体からなる酸化性有機成分は、酸素吸収性樹脂中で0.01~10質量%の割合で含有されることが好ましい。
尚、成形性等の見地から、上述した酸化性重合体やその共重合体の40℃での粘度は1~200Pa・sの範囲にあることが好適である。
これらのポリエン系重合体は、カルボン酸基、カルボン酸無水物基、水酸基が導入された酸変性ポリエン重合体であることが好ましい。
これらの酸化性重合体、或いはその共重合体からなる酸化性有機成分は、酸素吸収性樹脂中で0.01~10質量%の割合で含有されることが好ましい。
(ii)遷移金属系触媒
遷移金属系触媒としては、鉄、コバルト、ニッケル等の周期律表第VIII族金属が好適であるが、他に銅、銀等の第I族金属、錫、チタン、ジルコニウム等の第IV族金属、バナジウム等の第V族金属、クロム等の第VI族金属、マンガン等の第VII族金属等であってもよい。
遷移金属触媒は、一般に、上記遷移金属の低価数の無機塩、有機塩或いは錯塩の形で使用される。無機塩としては、塩化物等のハライド、硫酸塩等のイオウのオキシ塩、硝酸塩等の窒素のオキシ酸塩、リン酸塩等のリンオキシ塩、ケイ酸塩等を挙げることができる。有機塩としては、カルボン酸塩、スルホン酸塩、ホスホン酸塩等を挙げることができる。また、遷移金属の錯体としては、β-ジケトンまたはβ-ケト酸エステルとの錯体が挙げられる。
遷移金属系触媒は酸素吸収性樹脂中で、遷移金属原子の濃度(質量濃度基準)として100~3000ppmの範囲であることが好ましい。
遷移金属系触媒としては、鉄、コバルト、ニッケル等の周期律表第VIII族金属が好適であるが、他に銅、銀等の第I族金属、錫、チタン、ジルコニウム等の第IV族金属、バナジウム等の第V族金属、クロム等の第VI族金属、マンガン等の第VII族金属等であってもよい。
遷移金属触媒は、一般に、上記遷移金属の低価数の無機塩、有機塩或いは錯塩の形で使用される。無機塩としては、塩化物等のハライド、硫酸塩等のイオウのオキシ塩、硝酸塩等の窒素のオキシ酸塩、リン酸塩等のリンオキシ塩、ケイ酸塩等を挙げることができる。有機塩としては、カルボン酸塩、スルホン酸塩、ホスホン酸塩等を挙げることができる。また、遷移金属の錯体としては、β-ジケトンまたはβ-ケト酸エステルとの錯体が挙げられる。
遷移金属系触媒は酸素吸収性樹脂中で、遷移金属原子の濃度(質量濃度基準)として100~3000ppmの範囲であることが好ましい。
[接着層]
本発明の積層体においては、各層間に必要により接着層を形成することができ、特にガスバリア層がエチレン-ビニルアルコール共重合体から成る場合には、内外層を形成するポリプロピレン層との接着性に乏しいことから、接着層を介在させることが好ましい。
接着層に用いる接着性樹脂としては、カルボン酸、カルボン酸無水物、カルボン酸塩、カルボン酸アミド、カルボン酸エステル等に基づくカルボニル(-CO-)基を主鎖又は側鎖に、1~700ミリイクイバレント(meq)/100g樹脂、特に10~500(meq)/100g樹脂の濃度で含有する熱可塑性樹脂が挙げられる。
本発明の積層体においては、各層間に必要により接着層を形成することができ、特にガスバリア層がエチレン-ビニルアルコール共重合体から成る場合には、内外層を形成するポリプロピレン層との接着性に乏しいことから、接着層を介在させることが好ましい。
接着層に用いる接着性樹脂としては、カルボン酸、カルボン酸無水物、カルボン酸塩、カルボン酸アミド、カルボン酸エステル等に基づくカルボニル(-CO-)基を主鎖又は側鎖に、1~700ミリイクイバレント(meq)/100g樹脂、特に10~500(meq)/100g樹脂の濃度で含有する熱可塑性樹脂が挙げられる。
接着性樹脂の適当な例は、エチレン-アクリル酸共重合体、イオン架橋オレフィン共重合体、無水マレイン酸グラフトポリエチレン、無水マレイン酸変性ポリプロピレン、無水マレイン酸グラフトポリプロピレン、アクリル酸グラフトポリオレフィン、エチレン-酢酸ビニル共重合体、エチレン-ビニルアルコール共重合体と無水マレイン酸変性オレフィン樹脂とのブレンド物から形成されるもの等を挙げることができ、特に無水マレイン酸変性ポリプロピレンや無水マレイン酸グラフトポリプロピレンを好適に使用できる。接着樹脂は、1種又は2種以上を組み合わせて使用することもできるし、ポリオレフィン系の樹脂に配合しても良い。
[吸着剤含有層]
本発明の積層体において、必要により形成される吸着剤含有層は、酸素吸収性層よりも内層側に位置することが好ましく、これにより酸素吸収反応により発生する副生成物の容器内への移行を抑制し、内容物のフレーバー性を向上することができる。
吸着剤は、前述したプロピレン系重合体やリグラインド樹脂に配合することが好適である。
吸着剤としては、従来公知の吸着剤を使用することができるが、ケイ酸塩を主成分とする多孔性無機物、例えばゼオライトや、モンモリロナイト等のスメクタイト粘土鉱物を酸処理して得られる活性白土の粉末が好適であり、特にNa型のZSM5ゼオライトであるハイシリカゼオライト(シリカ/アルミナ比が100以上)が、プラスチックに特有の臭いを捕捉し且つ上記の酸化分解生成物を捕捉する機能に優れており好適である。
このような吸着剤は、一般に、吸着剤含有層中に0.5~10質量%の量で配合することが好適である。
本発明の積層体において、必要により形成される吸着剤含有層は、酸素吸収性層よりも内層側に位置することが好ましく、これにより酸素吸収反応により発生する副生成物の容器内への移行を抑制し、内容物のフレーバー性を向上することができる。
吸着剤は、前述したプロピレン系重合体やリグラインド樹脂に配合することが好適である。
吸着剤としては、従来公知の吸着剤を使用することができるが、ケイ酸塩を主成分とする多孔性無機物、例えばゼオライトや、モンモリロナイト等のスメクタイト粘土鉱物を酸処理して得られる活性白土の粉末が好適であり、特にNa型のZSM5ゼオライトであるハイシリカゼオライト(シリカ/アルミナ比が100以上)が、プラスチックに特有の臭いを捕捉し且つ上記の酸化分解生成物を捕捉する機能に優れており好適である。
このような吸着剤は、一般に、吸着剤含有層中に0.5~10質量%の量で配合することが好適である。
[易剥離性層]
本発明の積層体において、例えば、本発明の積層体が多層シートを熱成形して得られたフランジ付きのトレイ又はカップである場合においては、積層体の最内層が易剥離性層(易開封性層)であることが好適である。すなわち、このようなトレイ又はカップにおいては、蓋材が接合されるフランジ部上面が易剥離性層であることにより、蓋の開封性が顕著に向上する。
このような易剥離性層としては、例えば、少なくともフランジ部との接合面がプロピレン系重合体又はエチレン系重合体から成る蓋材に対して、プロピレン系重合体とエチレン系重合体のブレンド物から易開封性層を形成することが好適である。
上記プロピレン系重合体としては、ホモポリプロピレンの他、プロピレンとエチレンもしくは他のα-オレフィン、例えば、1-ブテン、1-ペンテン、1-ヘキセン、4-メチル-1-ペンテン、1-オクテン等とのランダム共重合体等を挙げることができる。また上記エチレン系重合体としては、低密度ポリエチレン(LDPE)、線状低密度ポリエチレン(LLDPE)、中・高密度ポリエチレン(MDPE、HDPE)等のエチレンの単独重合体、もしくはエチレンと、例えば1-ブテン、1-ペンテン、1-ヘキセン、4-メチル-1-ペンテン、1-オクテン等の他のα-オレフィンや、(メタ)アクリル酸、(メタ)アクリル酸エチル、(メタ)アクリル酸メチル、酢酸ビニル、スチレン等のビニル系単量体等との共重合体、或いはアイオノマー等を挙げることができる。
本発明の積層体において、例えば、本発明の積層体が多層シートを熱成形して得られたフランジ付きのトレイ又はカップである場合においては、積層体の最内層が易剥離性層(易開封性層)であることが好適である。すなわち、このようなトレイ又はカップにおいては、蓋材が接合されるフランジ部上面が易剥離性層であることにより、蓋の開封性が顕著に向上する。
このような易剥離性層としては、例えば、少なくともフランジ部との接合面がプロピレン系重合体又はエチレン系重合体から成る蓋材に対して、プロピレン系重合体とエチレン系重合体のブレンド物から易開封性層を形成することが好適である。
上記プロピレン系重合体としては、ホモポリプロピレンの他、プロピレンとエチレンもしくは他のα-オレフィン、例えば、1-ブテン、1-ペンテン、1-ヘキセン、4-メチル-1-ペンテン、1-オクテン等とのランダム共重合体等を挙げることができる。また上記エチレン系重合体としては、低密度ポリエチレン(LDPE)、線状低密度ポリエチレン(LLDPE)、中・高密度ポリエチレン(MDPE、HDPE)等のエチレンの単独重合体、もしくはエチレンと、例えば1-ブテン、1-ペンテン、1-ヘキセン、4-メチル-1-ペンテン、1-オクテン等の他のα-オレフィンや、(メタ)アクリル酸、(メタ)アクリル酸エチル、(メタ)アクリル酸メチル、酢酸ビニル、スチレン等のビニル系単量体等との共重合体、或いはアイオノマー等を挙げることができる。
(積層体の製造方法)
本発明の積層体の製造方法においては、前記エチレン-プロピレンブロック共重合体に、粘度調整剤としてホモポリプロピレンを配合して溶融混練することにより、MFR(230℃、2.16kg荷重)を0.2~5g/10分の範囲に粘度調整した溶融樹脂を押出すことにより、表層の面粗さ(Sa)が0.15~1.0μm、特に0.15~0.80μmの範囲にある積層体を形成する。
前述した通り、ホモポリプロピレンは、エチレン-プロピレンブロック共重合体100質量部当たり1~40質量部、特に1~30質量部の量で配合されることにより、耐落下衝撃性、耐ブロッキング性及び滑り性等本発明の積層体が有する優れた性能を損なうことなく、樹脂組成物の粘度を上記範囲に調整することができ、成形性(作業性)を向上することが可能となり、ポリプロピレン層の面粗さ(Sa)を上記範囲に調整することが可能となる。すなわち、樹脂組成物のMFRが上記範囲よりも低い場合には樹脂圧異常で製膜出来ない等で目的の積層体を得られなかったり、不安定流動に起因する波打ちが発生して、面粗さ(Sa)を上記範囲に調整できないおそれがある。また上記範囲よりもMFRが高い場合に表層の平滑性が高くなる傾向があり、面粗さ(Sa)を上記範囲に調整することが困難になる。
本発明の積層体の製造方法においては、前記エチレン-プロピレンブロック共重合体に、粘度調整剤としてホモポリプロピレンを配合して溶融混練することにより、MFR(230℃、2.16kg荷重)を0.2~5g/10分の範囲に粘度調整した溶融樹脂を押出すことにより、表層の面粗さ(Sa)が0.15~1.0μm、特に0.15~0.80μmの範囲にある積層体を形成する。
前述した通り、ホモポリプロピレンは、エチレン-プロピレンブロック共重合体100質量部当たり1~40質量部、特に1~30質量部の量で配合されることにより、耐落下衝撃性、耐ブロッキング性及び滑り性等本発明の積層体が有する優れた性能を損なうことなく、樹脂組成物の粘度を上記範囲に調整することができ、成形性(作業性)を向上することが可能となり、ポリプロピレン層の面粗さ(Sa)を上記範囲に調整することが可能となる。すなわち、樹脂組成物のMFRが上記範囲よりも低い場合には樹脂圧異常で製膜出来ない等で目的の積層体を得られなかったり、不安定流動に起因する波打ちが発生して、面粗さ(Sa)を上記範囲に調整できないおそれがある。また上記範囲よりもMFRが高い場合に表層の平滑性が高くなる傾向があり、面粗さ(Sa)を上記範囲に調整することが困難になる。
エチレン-プロピレンブロック共重合体とホモポリプロピレンの溶融混練は、これらのペレットを、ミキサー等でドライブレンドした後、溶融押出する方法や、或いはこれらのペレットを混練機で溶融混練する方法等、公知の方法により行うことができる。
本発明においては、ポリプロピレン系エラストマーのドメインが前述した大きさの紡錘形状である分散状態となるように、溶融混練することが必要であり、用いる樹脂の粘度等に応じて適宜混練条件を調整することが必要である。
溶融混練における温度条件は特に制限はないが、170~270℃の範囲で行うことが好ましい。上記範囲よりも低い温度では、効率よく混練することができないおそれがあり、上記範囲よりも高い温度では樹脂の劣化を招くおそれがある。
本発明においては、ポリプロピレン系エラストマーのドメインが前述した大きさの紡錘形状である分散状態となるように、溶融混練することが必要であり、用いる樹脂の粘度等に応じて適宜混練条件を調整することが必要である。
溶融混練における温度条件は特に制限はないが、170~270℃の範囲で行うことが好ましい。上記範囲よりも低い温度では、効率よく混練することができないおそれがあり、上記範囲よりも高い温度では樹脂の劣化を招くおそれがある。
本発明の積層体は、上記のようにMFRが調整された溶融樹脂(ブレンド物)を用いる以外は、従来公知の方法により製造することができ、これに限定されないが、共押出法又は共射出法や、押出ラミネート法により他の層と積層してもよいし、或いは上記ブレンド物から押出成形により単層フィルム又はシートを予め作成し、ドライラミネート法によって他の層と積層することができ、これにより多層フィルム、多層シート、多層チューブ等の形態に成形することができる。また前記多層シートを熱成形することにより、カップ、トレイ等の形態に成形することができる。
本発明の積層体の製造方法においては、積層体を構成する前述した中間層を構成する各種樹脂又は樹脂組成物として、ポリプロピレン層を構成する樹脂組成物(ブレンド物)と熱収縮率が近似するものを使用することが望ましい。例えば、酸素吸収性樹脂層のマトリックスとしてポリプロピレン層を構成する樹脂組成物(ブレンド物)を用いることにより、成形された積層シートの収縮率の差に起因する巻ずれを抑制することが可能となり、成形不良の発生を抑制することが可能となる。
また本発明の製造方法によれば、面粗さ(Sa)が0.15~1.0μmの範囲にあるポリプロピレン表層を有する積層体を成形することができるため、滑り性が向上されており、成形工程、充填・密封工程、梱包工程等を搬送ラインで連続的に行う場合にも、容器詰まりが生じることがなく、優れた生産性を発現できる。
他の層としては、これに限定されるものではないが、ガスバリア性層、酸素吸収性層、リグラインド層、易剥離性層、接着層等、従来ポリプロピレン系多層包装材料に使用されていた公知の層を例示することができる。
尚、多層構造を有する場合には、他の層を構成する樹脂又は樹脂組成物が、エチレン-プロピレンブロック共重合体と近似する熱収縮率を有することが望ましく、これにより積層シートの収縮率の差に起因する巻ずれを抑制することができ、成形不良の発生を抑制することが可能になる。
また本発明の製造方法によれば、面粗さ(Sa)が0.15~1.0μmの範囲にあるポリプロピレン表層を有する積層体を成形することができるため、滑り性が向上されており、成形工程、充填・密封工程、梱包工程等を搬送ラインで連続的に行う場合にも、容器詰まりが生じることがなく、優れた生産性を発現できる。
他の層としては、これに限定されるものではないが、ガスバリア性層、酸素吸収性層、リグラインド層、易剥離性層、接着層等、従来ポリプロピレン系多層包装材料に使用されていた公知の層を例示することができる。
尚、多層構造を有する場合には、他の層を構成する樹脂又は樹脂組成物が、エチレン-プロピレンブロック共重合体と近似する熱収縮率を有することが望ましく、これにより積層シートの収縮率の差に起因する巻ずれを抑制することができ、成形不良の発生を抑制することが可能になる。
本発明を実験例により更に説明するが、本発明はこれらに制限されるものではない。
(実験例1~5)
6種7層の多層シート成形機を使用し、各樹脂を単軸押出機にて溶融混練し、Tダイ温度230℃でTダイからシート状に押出し、冷却ロールに接触させて固化させて巻き取ることにより、厚み500μmの多層シートを成形した。層構成は、外側より最外PP層/リグラインド層/接着層/バリア層/接着層/酸素スカベンジャー層/内PP層/易剥離性接着層である。
最外PP層、内PP層には、表1に示した組成及び分子量を有するポリプロピレンを主成分とする樹脂及びポリプロピレン系エラストマーから成るエチレン-プロピレンブロック共重合体のペレットと白着色用樹脂を使用した。リグラインド層には、本試験時に発生した多層シートの一部やトリム部、シートスケルトンを破砕したスクラップ100質量部に対して、表1に示したエチレン-プロピレンブロック共重合体を44質量部配合し、相溶化剤及び白着色用樹脂を添加したものを使用した。接着層には無水マレイン酸変性ポリプロピレン、酸素スカベンジャー層には鉄系酸素吸収剤(還元鉄粉100質量部及び塩化ナトリウム2質量部及び水酸化カルシウム1質量部の混合物)29質量部をMFR0.6g/10分のランダムポリプロピレン71質量部で混練した樹脂組成物を使用した。易剥離性接着層にはポリプロピレンやポリエチレンをドライブレンドした樹脂である。
また得られた多層シートを145℃に加熱して、プラグアシストして真空圧空成形することによりフランジ付き多層トレイを成形した。
尚、容器寸法はフランジ外径 長軸:155mm×短軸:120mm、口径 長軸:135mm×短軸:100mm、底部外径 長軸:115mm×短軸:90mm、高さ35mmであった。
(実験例1~5)
6種7層の多層シート成形機を使用し、各樹脂を単軸押出機にて溶融混練し、Tダイ温度230℃でTダイからシート状に押出し、冷却ロールに接触させて固化させて巻き取ることにより、厚み500μmの多層シートを成形した。層構成は、外側より最外PP層/リグラインド層/接着層/バリア層/接着層/酸素スカベンジャー層/内PP層/易剥離性接着層である。
最外PP層、内PP層には、表1に示した組成及び分子量を有するポリプロピレンを主成分とする樹脂及びポリプロピレン系エラストマーから成るエチレン-プロピレンブロック共重合体のペレットと白着色用樹脂を使用した。リグラインド層には、本試験時に発生した多層シートの一部やトリム部、シートスケルトンを破砕したスクラップ100質量部に対して、表1に示したエチレン-プロピレンブロック共重合体を44質量部配合し、相溶化剤及び白着色用樹脂を添加したものを使用した。接着層には無水マレイン酸変性ポリプロピレン、酸素スカベンジャー層には鉄系酸素吸収剤(還元鉄粉100質量部及び塩化ナトリウム2質量部及び水酸化カルシウム1質量部の混合物)29質量部をMFR0.6g/10分のランダムポリプロピレン71質量部で混練した樹脂組成物を使用した。易剥離性接着層にはポリプロピレンやポリエチレンをドライブレンドした樹脂である。
また得られた多層シートを145℃に加熱して、プラグアシストして真空圧空成形することによりフランジ付き多層トレイを成形した。
尚、容器寸法はフランジ外径 長軸:155mm×短軸:120mm、口径 長軸:135mm×短軸:100mm、底部外径 長軸:115mm×短軸:90mm、高さ35mmであった。
(実験例6)
最外PP層、内PP層の樹脂100質量部にMFR2.0g/10分(230℃、2.16kg荷重)のホモポリプロピレンを17.7質量部ドライブレンドした樹脂を使用した以外は、実験例1と同様に多層トレイを成形した。
最外PP層、内PP層の樹脂100質量部にMFR2.0g/10分(230℃、2.16kg荷重)のホモポリプロピレンを17.7質量部ドライブレンドした樹脂を使用した以外は、実験例1と同様に多層トレイを成形した。
各種測定方法は以下のとおりである。
<エチレン-プロピレンブロック共重合体の構造解析>
実験例1~5に使用したエチレン-プロピレンブロック共重合体において、ポリプロピレンを主成分とする樹脂(PP成分)及びポリプロピレン系エラストマー(ゴム成分)の配合比、分子量を13C-NMR測定(日本電子製)、GPC測定(Agilent製)により求めた。測定サンプルの前処理として、樹脂をキシレン還流溶解し放冷後個液分離した。キシレン可溶部をメタノールで再沈殿し、沈殿物を濾過し乾燥後、質量測定しゴム成分量とした。キシレン不溶部は、再溶解及びメタノール再沈殿後、濾過し乾燥した樹脂をPP成分とした。実験例6は、ホモポリプロピレンをドライブレンドしているため計算値とした。
<エチレン-プロピレンブロック共重合体の構造解析>
実験例1~5に使用したエチレン-プロピレンブロック共重合体において、ポリプロピレンを主成分とする樹脂(PP成分)及びポリプロピレン系エラストマー(ゴム成分)の配合比、分子量を13C-NMR測定(日本電子製)、GPC測定(Agilent製)により求めた。測定サンプルの前処理として、樹脂をキシレン還流溶解し放冷後個液分離した。キシレン可溶部をメタノールで再沈殿し、沈殿物を濾過し乾燥後、質量測定しゴム成分量とした。キシレン不溶部は、再溶解及びメタノール再沈殿後、濾過し乾燥した樹脂をPP成分とした。実験例6は、ホモポリプロピレンをドライブレンドしているため計算値とした。
(1)分散状態(ドメイン形状及び大きさ)
得られた多層トレイの底部において、シート製造時の引き取り方向に平行に切断した断面を透過型電子顕微鏡:TEM(日立製作所製)により観察した。前処理として、多層トレイより切り取ったサンプルをクライオ支持台へ接着し、クライオシステム(ライカ製)によりダイヤモンドナイフ装着のウルトラミクロトーム(ライカ製)で面出しをし、金属酸化物による蒸気染色を施し、超薄切片を作製した。
得られたTEM写真(20μm×20μm四方)から、画像解析式粒度分布ソフト(マウンテック社製Mac-View)により、多層トレイの最外PP層のポリプロピレン系エラストマーのドメインを全て計測し、各々の短径及び長径の測定及びアスペクト比、円相当のドメインサイズを算出した。全ドメイン数の計測結果より平均値を求めた。
得られた多層トレイの底部において、シート製造時の引き取り方向に平行に切断した断面を透過型電子顕微鏡:TEM(日立製作所製)により観察した。前処理として、多層トレイより切り取ったサンプルをクライオ支持台へ接着し、クライオシステム(ライカ製)によりダイヤモンドナイフ装着のウルトラミクロトーム(ライカ製)で面出しをし、金属酸化物による蒸気染色を施し、超薄切片を作製した。
得られたTEM写真(20μm×20μm四方)から、画像解析式粒度分布ソフト(マウンテック社製Mac-View)により、多層トレイの最外PP層のポリプロピレン系エラストマーのドメインを全て計測し、各々の短径及び長径の測定及びアスペクト比、円相当のドメインサイズを算出した。全ドメイン数の計測結果より平均値を求めた。
(2)面粗さSa(単位μm)
得られた多層トレイの底部から10mm×10mmのサンプル片を切り出した。非接触表面形状測定機(zygo社製)を用いて、容器外表面の形状測定を行った。測定ならびに画像解析には、アプリケーションとして、MetroPro(Ver.9.1.4 64-bit)を用いた。282μm×212μmの範囲を測定し、得られた生データから、ノイズ除去のため波長1.326μm以下をカットし測定データとした。N数=5より平均値を求めた。
得られた多層トレイの底部から10mm×10mmのサンプル片を切り出した。非接触表面形状測定機(zygo社製)を用いて、容器外表面の形状測定を行った。測定ならびに画像解析には、アプリケーションとして、MetroPro(Ver.9.1.4 64-bit)を用いた。282μm×212μmの範囲を測定し、得られた生データから、ノイズ除去のため波長1.326μm以下をカットし測定データとした。N数=5より平均値を求めた。
(3)滑り性(単位N)
得られた多層トレイの滑り性は、摩擦測定機(東洋精機製)を用いて、測定時のロードセルにかかかる荷重を動摩擦力として引き摺り抵抗値を求めた。23℃50%RHの環境下で、SUS板上に多層トレイを乗せ600gの重りを負荷した状態で100mm/minの速度で測定を行った。N数=5より平均値を求めた。評価基準は以下の通りである。
○:2.5N未満
△:2.5N以上3.0N未満
×:3.0N以上
得られた多層トレイの滑り性は、摩擦測定機(東洋精機製)を用いて、測定時のロードセルにかかかる荷重を動摩擦力として引き摺り抵抗値を求めた。23℃50%RHの環境下で、SUS板上に多層トレイを乗せ600gの重りを負荷した状態で100mm/minの速度で測定を行った。N数=5より平均値を求めた。評価基準は以下の通りである。
○:2.5N未満
△:2.5N以上3.0N未満
×:3.0N以上
(4)耐落下衝撃性
得られた多層トレイに蒸留水を200g入れ、蓋材でヒートシールし、95℃30分ボイル殺菌後に5℃で24時間保管した。保管後、5℃環境下で150cmの高さより落下させ、多層トレイの耐落下強度を判断した。N数は20個である。評価規準は以下のとおりである。
〇:割れが3個以下であったもの
△:割れが10個未満であったもの
×:10個以上割れたもの
得られた多層トレイに蒸留水を200g入れ、蓋材でヒートシールし、95℃30分ボイル殺菌後に5℃で24時間保管した。保管後、5℃環境下で150cmの高さより落下させ、多層トレイの耐落下強度を判断した。N数は20個である。評価規準は以下のとおりである。
〇:割れが3個以下であったもの
△:割れが10個未満であったもの
×:10個以上割れたもの
(5)フレーバー性
得られた多層トレイに蒸留水を200g入れ、蓋材でヒートシールし、95℃30分ボイル殺菌後に室温で24時間保管した。保管後、10人のパネラーにより4点法による官能評価を実施し、平均点を求めた。評価基準は以下のとおりである。0が無味、4が非常に味を感じるレベルである。
〇:2.5未満
△:2.5以上3.5未満
×:3.5以上
得られた多層トレイに蒸留水を200g入れ、蓋材でヒートシールし、95℃30分ボイル殺菌後に室温で24時間保管した。保管後、10人のパネラーにより4点法による官能評価を実施し、平均点を求めた。評価基準は以下のとおりである。0が無味、4が非常に味を感じるレベルである。
〇:2.5未満
△:2.5以上3.5未満
×:3.5以上
得られた結果より、実験例1及び6は、ポリプロピレン系エラストマーの形状が紡錘状であり滑り性と耐落下衝撃性を両立でき良好な結果が得られ、特に実験例6は樹脂粘度も低く製膜性に優れていた。実験例2は、耐落下衝撃性がやや低かったが、ポリプロピレン系エラストマーが少ないことが影響していると考えられる。実験例3及び5は、耐落下衝撃性がやや低かったが、ポリプロピレン系エラストマーの形状または粒径が影響していると考えられる。また、フレーバー性は劣る結果であり、ポリプロピレン系エラストマーの分子量が影響していると推測する。実験例4は、耐落下衝撃性は良好だが滑り性が悪い結果であった。これはポリプロピレン系エラストマーの形状が筋状でありアスペクト比が高いため、表面凹凸が平滑となり接触面積が大きいためと考察する。
本発明の包装材料及びこの包装材料から成る層を表層とする積層体は、耐落下衝撃性、耐ブロッキング性及びフレーバー性に優れていると共に、優れた滑り性を備えていることから生産ラインにおける搬送性に優れている。このため、大量生産される食品用の包装材料、特にフレーバー性が重視される米飯等を収納する容器に好適に使用できる。また耐熱性に優れたプロピレン系重合体から成るため、レトルト殺菌等に付されるパウチ等の包装材料としても好適に利用できる。
Claims (17)
- ポリプロピレンを主成分とする樹脂がマトリックスであり、紡錘形状のポリプロピレン系エラストマーがドメインとなる相分散構造を有するエチレン-プロピレンブロック共重合体であることを特徴とするポリプロピレン系包装材料。
- 前記ドメインのアスペクト比が、1.2~9.0の範囲である請求項1記載のポリプロピレン系包装材料。
- 前記ドメインの短径が0.2~4.0μm、長径が0.5~5.0μmの範囲にある請求項1又は2記載のポリプロピレン系包装材料。
- 前記ポリプロピレンを主成分とする樹脂100質量部に対して、前記ポリプロピレン系エラストマーを1~30質量部含有する請求項1~3の何れかに記載のポリプロピレン系包装材料。
- 前記ポリプロピレン系エラストマーの重量平均分子量(Mw)が50万~100万であり、数平均分子量(Mn)が1万~30万である請求項1~4の何れかに記載のポリプロピレン系包装材料。
- 前記ポリプロピレンを主成分とする樹脂の重量平均分子量(Mw)が30万~80万であり、数平均分子量(Mn)が1万~30万である請求項1~5の何れかに記載のポリプロピレン系包装材料。
- 前記エチレン-プロピレンブロック共重合体100質量部に対して、ホモポリプロピレンを1~30質量部含有する請求項1~6の何れかに記載のポリプロピレン系包装材料。
- 面粗さ(Sa)が、0.15~1.0μmである請求項1~7の何れかに記載のポリプロピレン系包装材料。
- シート、フィルム、トレイ、カップの何れかの形態を有する請求項1~7の何れかに記載のポリプロピレン系包装材料。
- 請求項1~7の何れかに記載のポリプロピレン系包装材料であるエチレン-プロピレンブロック共重合体から成るポリプロピレン層を表層として備える積層体であって、前記ポリプロピレン層の面粗さ(Sa)が、0.15~1.0μmであることを特徴とする積層体。
- 前記ポリプロピレン層を内外層、酸素吸収性層及びガスバリア性層を中間層として少なくとも備える請求項10記載の積層体。
- トレイ又はカップの形状を有する請求項10又は11に記載の積層体。
- エチレン-プロピレンブロック共重合体からなるポリプロピレン層を表層として備える積層体の製造方法において、
前記エチレン-プロピレンブロック共重合体に、粘度調整剤としてホモポリプロピレンを配合して溶融混練することにより、MFR(230℃、2.16kg荷重)を0.1~10g/10分の範囲に粘度調整し、該粘度調整された溶融樹脂を押出すことにより、面粗さが0.15μm~1.0μmである表層を形成することを特徴とする積層体の製造方法。 - 前記エチレン-プロピレンブロック共重合体100質量部に対して、前記ホモポリプロピレンを1~30質量部配合する請求項13記載の積層体の製造方法。
- 前記エチレン-プロピレンブロック共重合体100質量部に対して、前記ポリプロピレン系エラストマーを1~30質量部含有する請求項13又は14記載の積層体の製造方法。
- 前記ポリプロピレン系エラストマーの重量平均分子量(Mw)が50万~100万であり、数平均分子量(Mn)が1万~30万である請求項13~15の何れかに記載の積層体の製造方法。
- 前記ポリプロピレンを主成分とする樹脂の重量平均分子量(Mw)が30万~80万であり、数平均分子量(Mn)が1万~30万である請求項13~16の何れかに記載の積層体の製造方法。