WO2022065220A1 - Poutre de cadre en acier, structure de jonction colonne-poutre, et structure les comprenant - Google Patents

Poutre de cadre en acier, structure de jonction colonne-poutre, et structure les comprenant Download PDF

Info

Publication number
WO2022065220A1
WO2022065220A1 PCT/JP2021/034260 JP2021034260W WO2022065220A1 WO 2022065220 A1 WO2022065220 A1 WO 2022065220A1 JP 2021034260 W JP2021034260 W JP 2021034260W WO 2022065220 A1 WO2022065220 A1 WO 2022065220A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel
steel beam
column
axial direction
lower flange
Prior art date
Application number
PCT/JP2021/034260
Other languages
English (en)
Japanese (ja)
Inventor
隆行 難波
椋太 荒木田
Original Assignee
Ｊｆｅスチール株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｊｆｅスチール株式会社 filed Critical Ｊｆｅスチール株式会社
Priority to JP2021568881A priority Critical patent/JP7226590B2/ja
Publication of WO2022065220A1 publication Critical patent/WO2022065220A1/fr

Abstract

L'invention concerne une poutre de cadre en acier, une structure de jonction colonne-poutre, et une structure les comprenant, qui, même lorsqu'elles sont utilisées dans un environnement à basse température, peuvent empêcher une partie soudée au niveau d'une extrémité dans une direction axiale de matériau de subir une rupture fragile pendant une action de charge à court terme telle qu'une force sismique, et qui peuvent présenter une résistance à la fatigue et une capacité de déformation plastique élevées.　La poutre de cadre en acier présente une bride supérieure, une bride inférieure et une âme reliant la bride supérieure et la bride inférieure, la bride supérieure, la bride inférieure et l'âme étant formées à partir d'un matériau d'acier présentant une valeur d'impact Charpy d'au moins 27 J à -40 °C ; et la poutre de cadre en acier présente une forme telle que, lorsqu'un moment de flexion symétrique inverse augmentant progressivement est exercé sur les deux extrémités dans la direction axiale du matériau de la poutre de cadre en acier, et que la bride supérieure et/ou la bride inférieure cèdent, la position au niveau de laquelle ladite bride supérieure et/ou ladite bride inférieure cèdent initialement soit une position autre que l'extrémité distale dans la direction axiale du matériau.
PCT/JP2021/034260 2020-09-23 2021-09-17 Poutre de cadre en acier, structure de jonction colonne-poutre, et structure les comprenant WO2022065220A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021568881A JP7226590B2 (ja) 2020-09-23 2021-09-17 鉄骨梁、柱梁接合構造およびこれを有する構造物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-158258 2020-09-23
JP2020158258 2020-09-23

Publications (1)

Publication Number Publication Date
WO2022065220A1 true WO2022065220A1 (fr) 2022-03-31

Family

ID=80845367

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/034260 WO2022065220A1 (fr) 2020-09-23 2021-09-17 Poutre de cadre en acier, structure de jonction colonne-poutre, et structure les comprenant

Country Status (2)

Country Link
JP (1) JP7226590B2 (fr)
WO (1) WO2022065220A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002276028A (ja) * 2001-03-13 2002-09-25 Nippon Steel Corp 耐震性に優れた柱梁仕口部およびその施工方法
JP2016011439A (ja) * 2014-06-27 2016-01-21 新日鐵住金株式会社 冷間プレス成形角形鋼管用厚鋼板、冷間プレス成形角形鋼管、及び溶接継手

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002276028A (ja) * 2001-03-13 2002-09-25 Nippon Steel Corp 耐震性に優れた柱梁仕口部およびその施工方法
JP2016011439A (ja) * 2014-06-27 2016-01-21 新日鐵住金株式会社 冷間プレス成形角形鋼管用厚鋼板、冷間プレス成形角形鋼管、及び溶接継手

Also Published As

Publication number Publication date
JP7226590B2 (ja) 2023-02-21
JPWO2022065220A1 (fr) 2022-03-31

Similar Documents

Publication Publication Date Title
JP5741356B2 (ja) ラーメン骨組の柱梁接合部
JP2011001792A (ja) ラーメン骨組の柱梁接合部構造および圧延ｈ形鋼
JP5577676B2 (ja) 柱と梁の溶接接合構造
JP4691210B2 (ja) 耐震鉄骨構造およびその設計方法
WO2022065220A1 (fr) Poutre de cadre en acier, structure de jonction colonne-poutre, et structure les comprenant
JP2010216153A (ja) 仕口補強構造
JP6481665B2 (ja) 鉄骨柱とｈ形梁又はｉ形梁の接合構造及びその接合方法
JP2015224517A (ja) 梁端部の接合構造
JP7138460B2 (ja) 鉄骨梁の補強方法および鉄骨梁
WO2018012495A1 (fr) Structure de liaison poutre-poteau
JP7351271B2 (ja) 鉄骨梁、柱梁接合構造およびこれを有する構造物
JP7262518B2 (ja) 間柱型鋼材ダンパー
JP6362131B2 (ja) 建物の水平力補強構造
JP3402312B2 (ja) 柱梁接合部、柱用圧延ｈ形鋼およびその製造方法
KR102307939B1 (ko) 기둥과 보의 접합구조
JP3389910B2 (ja) 柱梁接合部
KR102426247B1 (ko) 기둥과 보의 접합구조
JP2023146182A (ja) 溶接組立箱形断面部材およびその設計方法
JP7368849B2 (ja) 制振ダンパー
JP7098363B2 (ja) 梯子型耐力壁架構
KR102329508B1 (ko) 기둥과 보의 접합구조
JP6823980B2 (ja) 鋼製耐震壁、耐震壁付建物及び耐震壁付建物の施工方法
WO2010103812A1 (fr) Structure d'acier résistant aux séismes
JP2003105856A (ja) スプリットティ接合金物及び柱と梁の接合構造
JP2023142944A (ja) 溶接継手

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2021568881

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21872349

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21872349

Country of ref document: EP

Kind code of ref document: A1