WO2020110993A1 - 無機固体電解質二次電池用電極、および無機固体電解質二次電池 - Google Patents

無機固体電解質二次電池用電極、および無機固体電解質二次電池 Download PDF

Info

Publication number
WO2020110993A1
WO2020110993A1 PCT/JP2019/045952 JP2019045952W WO2020110993A1 WO 2020110993 A1 WO2020110993 A1 WO 2020110993A1 JP 2019045952 W JP2019045952 W JP 2019045952W WO 2020110993 A1 WO2020110993 A1 WO 2020110993A1
Authority
WO
WIPO (PCT)
Prior art keywords
solid electrolyte
electrode
secondary battery
electrolyte secondary
inorganic solid
Prior art date
Application number
PCT/JP2019/045952
Other languages
English (en)
French (fr)
Inventor
克人 三浦
琢寛 幸
託也 三輪
瑞絵 鰐渕
雅人 田渕
Original Assignee
株式会社大阪ソーダ
技術研究組合リチウムイオン電池材料評価研究センター
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社大阪ソーダ, 技術研究組合リチウムイオン電池材料評価研究センター filed Critical 株式会社大阪ソーダ
Priority to CN201980076987.6A priority Critical patent/CN113439354A/zh
Priority to JP2020557702A priority patent/JP7400729B2/ja
Priority to KR1020217015367A priority patent/KR20210093907A/ko
Publication of WO2020110993A1 publication Critical patent/WO2020110993A1/ja

Abstract

固体電解質二次電池に優れた充放電特性を発揮させる新規な固体電解質二次電池用電極を提供する。　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料と、活物質とを含有する電極材料層を備える、固体電解質二次電池用電極。

Description

無機固体電解質二次電池用電極、および無機固体電解質二次電池
　本発明は、無機固体電解質二次電池用電極、その製造方法、及び無機固体電解質二次電池に関する。
　従来、リチウムイオン電池に代表される非水電解質二次電池は、電解質にイオン伝導性の点から溶液またはペースト状のものが用いられている。しかし、液漏れによる機器の損傷の恐れがあることから、種々の安全対策が必要であり、大型電池開発の障壁になっている。
　これに対し高分子固体電解質、無機固体電解質などの電解質が固体化された固体電解質が提案されている。高分子固体電解質は、一般に柔軟性、曲げ加工性、および成形性に優れ、応用されるデバイスの設計の自由度が高くなるなどの利点があるが、負荷特性や低温特性が悪いために、高温作動の電池用途に限られるという欠点がある。一方、無機固体電解質は、高分子固体電解質と比べて、イオン伝導性が高いものの、電解質が結晶質あるいは非晶質からなり、充放電時の正負極活物質による体積変化の緩和が難しく、更に、電極と電解質の界面抵抗が高いため、充放電特性が不十分という問題がある。
　無機固体電解質と電極の界面の抵抗を下げる方法として、例えば、特許文献１においては、リチウムイオン伝導性バインダーを含む溶媒中に活物質を分散させ、硫化物系固体電解質を添加し、加熱乾燥後、活物質シートを形成させている。しかしながら、活物質とリチウムイオン伝導性バインダーを分散させて、電極を作製すると、電極内に空隙ができる。電解液系では、電極内の空隙は、有機電解液で満たされており、電極内のイオン伝導性に寄与されるが、硫化物系固体電解質を含む電極には、空隙が存在するので、特に、体積エネルギー密度に不利な要素となる。また、硫化物系固体電解質の添加量は活物質１００質量部に対して、２５～１００質量部が必要であり、電極の活物質量が少なく、高エネルギー密度の電池には不向きである。
　また、例えば特許文献２においては、高分子化合物と電解質塩と電極活物質を希釈剤に入れ、加熱攪拌後、被覆された電極活物質を得ている。この方法では、活物質同士の結着性に対して効果があるが、特許文献１と同様、電極内に空隙ができる。
　さらに、電極内に高分子固体電解質を含浸する方法として、例えば特許文献３の実施例には、モノマー状にあるポリエチレンオキシドとＬｉＢＦ4を含浸させて重合の記載があるが、ポリエチレンオキシドを更に重合できる方法は知られていない。また、ポリエチレンオキシドは過酸化物などの重合開始剤を用いても、架橋することはできない。ポリエチレンオキシドは、結晶性が高く、融点（６０℃）以下になると、結晶化に伴い、柔軟性がなくなり、結着性が弱くなる。また、融点以上になると、ポリエチレンオキシドが溶融するため形状維持ができなくなり、結着性が弱くなるという問題がある。ポリエチレンオキシドでは無機固体電解質の界面の抵抗を下げることは困難である。
特開２０１０－３３９１８号公報 特開２０１６－１９７５９０号公報 特開２０００－１３８０７３号公報
　本発明は、無機固体電解質二次電池に優れた充放電特性を発揮させる新規な無機固体電解質二次電池用電極を提供することを主な目的とする。さらに、本発明は、当該無機固体電解質二次電池用電極の製造方法、及び当該無機固体電解質二次電池用電極を利用した無機固体電解質二次電池を提供することも目的とする。
　本発明者は、上記の課題を解決すべく鋭意検討を行った。その結果、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料と、活物質とを含有する電極材料層を備える固体電解質二次電池用電極は、固体電解質二次電池に優れた充放電特性を発揮させることを見出した。本発明は、このような知見に基づいて、さらに検討を重ねることにより完成したものである。
　即ち、本発明は、下記に掲げる態様の発明を提供する。
項１．　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料と、活物質とを含有する電極材料層を備える、無機固体電解質二次電池用電極。
項２．　前記活物質が、ＬｉＭＯ2、ＬｉＭ2Ｏ4、Ｌｉ2ＭＯ3、ＬｉＭＥＯ4（式中のＭは、遷移金属からなり、Ｃｏ、Ｍｎ、Ｎｉ、Ｃｒ、Ｆｅ、Ｔｉの少なくとも一種を含んでいる。ＥはＰ、Ｓｉの少なくとも１種を含んでいる。）からなる群より選択される少なくとも１種である、項１に記載の無機固体電解質二次電池用電極。
項３．　前記活物質が、炭素材料、シリコン系化合物、及びスズ系化合物からなる群より選択される少なくとも１種である、項１に記載の無機固体電解質二次電池用電極。
項４．　前記イオン伝導性ポリマーは、側鎖にエチレンオキシド単位を有するポリエーテルである、項１～３のいずれか１項に記載の無機固体電解質二次電池用電極。
項５．　無機固体電解質と共に、固体電解質二次電池に用いられる、項１～４のいずれか１項に記載の無機固体電解質二次電池用電極。
項６．　前記無機固体電解質は、酸化物系固体電解質又は硫化物系固体電解質である、項５に記載の無機固体電解質二次電池用電極。
項７．　活物質を含む層に、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料を含浸させる工程を含む、無機固体電解質二次電池用電極の製造方法。
項８．　前記イオン伝導性ポリマー材料を含浸させた層を、加熱又は活性エネルギー線照射によって架橋させる工程を含む、項７に記載の無機固体電解質二次電池用電極の製造方法。
項９．　項１～６のいずれかに記載の無機固体電解質二次電池用電極を含む、無機固体電解質二次電池。
　本発明によれば、無機固体電解質二次電池に優れた充放電特性を発揮させる新規な無機固体電解質二次電池用電極を提供することができる。さらに、本発明によれば、当該無機固体電解質二次電池用電極の製造方法、及び当該無機固体電解質二次電池用電極を利用した無機固体電解質二次電池を提供することもできる。
　本発明の無機固体電解質二次電池用電極は、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料と、活物質とを含有する電極材料層を備えることを特徴としている。本発明の無機固体電解質二次電池用電極は、このような構成を備えていることにより、無機固体電解質二次電池に優れた充放電特性を発揮させることができる。
　より具体的には、本発明の無機固体電解質二次電池用電極（以下、「本発明の電極」と表記することがある）においては、活物質に加えて、さらに、前記のイオン伝導性ポリマー材料が、電極材料層に含まれていることにより、電極材料層に含まれる活物質などの電極材料（具体的には、活物質粒子、バインダー、導電助剤、増粘剤、無機固体電解質など）の空隙がイオン伝導性ポリマー材料によって埋められ、電極材料層の内部の界面抵抗が効果的に低下し、結果として、優れた充放電特性が発揮されるものと考えられる。また、無機固体電解質二次電池は、高温環境（例えば１００℃以上の高温環境）で使用されることもあるが、本発明の電極を用いることにより、高温環境において優れた充放電特性が発揮される。以下、本発明の無機固体電解質二次電池用電極、その製造方法、及び本発明の無機固体電解質二次電池用電極を利用した無機固体電解質二次電池について詳述する。
　なお、本明細書において、「～」で結ばれた数値は、「～」の前後の数値を下限値及び上限値として含む数値範囲を意味する。複数の下限値と複数の上限値が別個に記載されている場合、任意の下限値と上限値を選択し、「～」で結ぶことができるものとする。
　本発明の電極は、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料と、活物質とを含有する電極材料層を備える。より具体的には、本発明の電極は、当該電極材料層に加えて、集電体を備えており、電極材料層は集電体の上に形成されている。イオン伝導性ポリマー材料の詳細については後述する。
　本発明の電極は、無機固体電解質二次電池において、正極及び負極のいずれとすることもできる。正極においては、集電体に正極材料層を形成し、負極においては、集電体に負極材料層を形成する。本発明の電極が正極である場合には、正極材料層が前記のイオン伝導性ポリマー材料と正極活物質とを含有する。また、本発明の電極が負極である場合には、負極材料層が前記のイオン伝導性ポリマー材料と負極活物質とを含有する。
　正極、負極には、公知の集電体を用いることができる。具体的には、正極には、集電体として、アルミニウム、ニッケル、ステンレス、金、白金、チタン等の金属が使用される。負極には、集電体として、銅、ニッケル、ステンレス、金、白金、チタン等の金属が使用される。
　また、正極材料層、負極材料層は、それぞれ、前記のイオン伝導性ポリマー材料に加えて、少なくとも正極活物質、負極活物質を含有し、更に導電助剤、バインダー、増粘剤を含有していてもよく、必要に応じて、後述の無機固体電解質を含有させてもよい。
　本発明で使用される正極活物質は、ＬｉＭＯ2、ＬｉＭ2Ｏ4、Ｌｉ2ＭＯ3、ＬｉＭＥＯ4のいずれかの組成からなるリチウム金属含有複合酸化物粉末である。ここで式中のＭは主として遷移金属からなり、Ｃｏ、Ｍｎ、Ｎｉ、Ｃｒ、Ｆｅ、Ｔｉの少なくとも一種を含んでいる。Ｍは遷移金属からなるが、遷移金属以外にもＡｌ、Ｇａ、Ｇｅ、Ｓｎ、Ｐｂ、Ｓｂ、Ｂｉ、Ｓｉ、Ｐ、Ｂなどが添加されていてもよい。ＥはＰ、Ｓｉの少なくとも１種を含んでいる。正極活物質の粒子径には５０μｍ以下が好ましく、更に好ましくは２０μｍ以下のものを用いる。これらの活物質は、３Ｖ（ｖｓ．Ｌｉ／Ｌｉ＋）以上の起電力を有するものである。
　正極活物質の具体例としては、コバルト酸リチウム、ニッケル酸リチウム、ニッケル／コバルト／マンガン酸リチウム（３元系）、スピネル型マンガン酸リチウム、リン酸鉄リチウムなどが挙げられる。
　本発明で使用される負極活物質は、リチウムイオンなどのアルカリ金属イオンを吸蔵・放出可能な構造（層間化合物）を有する炭素材料（天然黒鉛、人造黒鉛、非晶質炭素等）か、リチウムイオンなどのアルカリ金属イオンを吸蔵・放出可能なリチウム、アルミニウム系化合物、スズ系化合物、シリコン系化合物、チタン系化合物等の金属である。粉末の場合、粒子径は１０ｎｍ以上１００μｍ以下が好ましく、更に好ましくは２０ｎｍ以上２０μｍ以下である。また、金属と炭素材料との混合活物質として用いてもよい。
　導電助剤を用いる場合には、公知の導電助剤を用いることができ、黒鉛、ファーネスブラック、アセチレンブラック、ケッチェンブラックなどの導電性カーボンブラック、カーボンナノチューブなどの炭素繊維、または金属粉末等が挙げられる。これら導電助剤は１種または２種以上用いてもよい。
　バインダーとしては、例えばＰＶｄＦ等のフッ素樹脂、フッ素ゴムやアクリルゴム、変性アクリルゴム、スチレン－ブタジエンゴム、アクリル系重合体、ビニル系重合体、前記記載のイオン伝導性ポリマーから選ばれる１種以上の化合物を用いることができる。これらバインダーは活物質を１００質量部として、好ましくは５質量部以下、より好ましくは３質量部以下、例えば０．０１～２質量部添加する。
　増粘剤の具体例としては、カルボキシメチルセルロース、メチルセルロース、ヒドロキシメチルセルロース、エチルセルロースおよびこれらの塩（ナトリウム塩等のアルカリ金属塩、アンモニウム塩）、ポリビニルアルコール、ポリアクリル酸塩、ポリエチレンオキサイド等が挙げられるこれら増粘剤は１種または２種以上用いてもよい。これら増粘剤は活物質を１００質量部として、好ましくは５質量部以下、より好ましくは３質量部以下、例えば０．０１～２質量部添加する。また、塗工液の粘度が低い場合には増粘剤を併用することができる。
　集電体と電極材料層を備える電極の作製方法は特に限定されず一般的な方法を利用することができる。例えば、正極活物質あるいは負極活物質、導電助剤、バインダー、水またはＮ-メチル-２-ピロリドン（ＮＭＰ）等の溶媒、必要に応じて増粘剤などからなる電極材料のペースト（塗工液）をドクターブレード法やシルクスクリーン法などにより集電体表面上に適切な厚さに均一に塗布することより行われる。
　例えばドクターブレード法では、負極活物質粉末や正極活物質粉末、導電助剤、バインダー等を水に分散してスラリー状にし、金属電極基板に塗布した後、所定のスリット幅を有するブレードにより適切な厚さに均一化する。電極は活物質塗布後、余分な有機溶剤を除去するため、例えば、１００℃の熱風や８０℃減圧状態で乾燥する。乾燥後の電極はプレス装置によってプレス成型することで、集電体の上に電極材料層を積層した電極前駆体を形成する。
　本発明の電極においては、このように形成された電極前駆体の電極材料層に、イオン伝導性ポリマー材料を含浸させることにより、イオン伝導性ポリマー材料と活物質とを含む電極を好適に製造することができる。すなわち、前述した従来の電極材料層の製造方法を利用して、電極材料層を形成すると、電極材料層を構成している電極材料間には活物質粒子などの空隙が形成される。本発明の電極においては、電極材料の空隙をイオン伝導性ポリマー材料が埋めるため、電極材料層の内部の界面抵抗を効率的に低下させることができる。
　イオン伝導性ポリマー材料は、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含む。具体的には、本発明のイオン伝導性ポリマー材料は、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーと、リチウム塩化合物との混合物である。
　本発明の電極において、電極材料層に含まれるイオン伝導性ポリマー材料の含有量としては、特に制限されないが、充放電特性を好適に向上させる観点から、活物質１００質量部に対して、好ましくは５～５０質量部、より好ましくは１５～３０質量部である。
　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーとしては、例えば、側鎖にエチレンオキシド単位を有するポリエーテル、側鎖にエチレンオキシド単位を有するホウ酸エステル、側鎖にエチレンオキシド単位を有するポリオレフィン等があり、好ましくは側鎖にエチレンオキシド単位を有するポリエーテルである。
　側鎖にエチレンオキシド単位を有するポリエーテルは、側鎖にエチレンオキシド単位を有するエポキシ化合物から形成された構成単位を含むことが好ましい。すなわち、イオン伝導性ポリマーは、側鎖にエチレンオキシド単位を有するエポキシ化合物を少なくとも単量体としたポリマーであることが好ましい。
　側鎖にエチレンオキシド単位を有するエポキシ化合物としては、例えば、下記式（２）で表される単量体が挙げられ、下記式（２）、必要により下記式（１）、下記式（３）で表される単量体を用いた分岐型ポリエーテルは、側鎖にエチレンオキシド単位を有するポリエーテル（ｉ）となる。式（１）～（３）で表される単量体は、１種類のみを用いてもよいし、２種類以上を混合して用いてもよい。
Figure JPOXMLDOC01-appb-C000001
Figure JPOXMLDOC01-appb-C000002
［式（２）中、Ｒは－ＣＨ2Ｏ（ＣＨ2ＣＨ2Ｏ）nＲ4であり、Ｒ4は炭素数１～６のアルキル基であり、ｎは０～１２の数である。］
Figure JPOXMLDOC01-appb-C000003
［式（３）中、Ｒ5は、エチレン性不飽和基を含有する基を表す。］
　式（３）の単量体としては、アリルグリシジルエーテル、４－ビニルシクロヘキシルグリシジルエーテル、α－テルピニルグリシジルエーテル、シクロヘキセニルメチルグリシジルエーテル、ｐ－ビニルベンジルグリシジルエーテル、アリルフェニルグリシジルエーテル、ビニルグリシジルエーテル、３，４－エポキシ－１－ブテン、３，４－エポキシ－１－ペンテン、４，５－エポキシ－２－ペンテン、１，２－エポキシ－５，９－シクロドデカンジエン、３，４－エポキシ－１－ビニルシクロヘキセン、１，２－エポキシ－５－シクロオクテン、アクリル酸グリシジル、メタクリル酸グリシジル、ソルビン酸グリシジル、ケイ皮酸グリシジル、クロトン酸グリシジル、グリシジル－４－ヘキセノエートが用いられる。好ましくは、アリルグリシジルエーテル、アクリル酸グリシジル、メタクリル酸グリシジルである。
　側鎖にエチレンオキシド単位を有するポリエーテル（ｉ）の合成は、例えば、次のようにして行うことができる。開環重合触媒として有機アルミニウムを主体とする触媒系、有機亜鉛を主体とする触媒系、有機錫－リン酸エステル縮合物触媒系などの配位アニオン開始剤、または対イオンにＫ+を含むカリウムアルコキシド、ジフェニルメチルカリウム、水酸化カリウムなどのアニオン開始剤を用いて、各単量体を溶媒の存在下又は不存在下、反応温度１０～１２０℃、撹拌下で反応させることによってポリエーテル（ｉ）が得られる。重合度、あるいは得られる共重合体の性質などの点から、配位アニオン開始剤が好ましく、なかでも有機錫－リン酸エステル縮合物触媒系が取り扱い易く特に好ましい。
　側鎖にエチレンオキシド単位を有するポリエーテル（ｉ）において、式（１）の単量体に由来する繰り返し単位（Ａ）と、式（２）の単量体に由来する繰り返し単位（Ｂ）と、式（３）の単量体に由来する繰り返し単位（Ｃ）とのモル比は、（Ａ）９５～５モル％、（Ｂ）５～９５モル％、および（Ｃ）０～２０モル％が適当であり、好ましくは（Ａ）９２～９モル％、（Ｂ）７～９０モル％、および（Ｃ）１～１５モル％、更に好ましくは（Ａ）８８～１８モル％、（Ｂ）１０～８０モル％、および（Ｃ）２～１５モル％である。繰り返し単位（Ａ）が９５モル％以下であるとガラス転移温度の上昇とオキシエチレン鎖の結晶化を招かず、結果的にイオン伝導性の点で好ましい。
　側鎖にエチレンオキシド単位を有するポリエーテル（ｉ）の具体例としては、エチレンオキシド／ジエチレングリコールメチルグリシジルエーテル／アリルグリシジルエーテル三元共重合体、エチレンオキシド／ジエチレングリコールメチルグリシジルエーテル／メタクリル酸グリシジル三元共重合体、エチレンオキシド／ジエチレングリコールメチルグリシジルエーテル／アクリル酸グリシジル三元共重合体等が挙げられる。
　側鎖にエチレンオキシド単位を有するポリエーテル（ｉ）の重量平均分子量は特に限定されないが、１万～３００万であってよく、５万～２５０万であることがより好ましく、１０万～２００万であることが特に好ましい。重量平均分子量はゲルパーミエーションクロマトグラフィー（ＧＰＣ）で、溶媒としてジメチルホルムアミド（ＤＭＦ）を使用して、標準ポリスチレン換算により算出する。
　イオン伝導性ポリマー材料に含まれるイオン伝導性ポリマーの含有量としては、導電性ポリマー材料全体を１００質量部として、好ましくは５～９５質量部、より好ましくは１０～９０質量部である。
　イオン伝導性ポリマーは、架橋体を含んでいてもよい。
　リチウム塩化合物としては、リチウムイオン電池に一般的に利用されているような、広い電位窓を有するリチウム塩化合物が好適である。リチウム塩化合物としては、例えば、ＬｉＢＦ4、ＬｉＰＦ6、ＬｉＣｌＯ4、ＬｉＣＦ3ＳＯ3、ＬｉＮ（ＣＦ3ＳＯ2）2（ＬｉＴＦＳＩ），ＬｉＮ（ＳＦＯ2）2（ＬｉＦＳＩ）、ＬｉＮ（Ｃ2Ｆ5ＳＯ2）2、ＬｉＮ［ＣＦ3ＳＣ（Ｃ2Ｆ5ＳＯ2）3］2などを挙げられるが、これらに限定されない。これらは、単独で用いても、２種類以上を混合して用いても良い。
　イオン伝導性ポリマー材料に含まれるリチウム塩化物の含有量としては、リチウム塩化合物のモル数／イオン伝導性ポリマーのエーテル酸素原子の総モル数の値が０．０００１～５が好ましく、更に好ましくは０．００１～０．５の範囲がよい。
　また、イオン伝導性ポリマー材料には、常温溶融塩が含まれていてもよい。常温溶融塩は、常温において少なくとも一部が液状を呈する塩をいい、常温とは電源が通常作動すると想定される温度範囲をいう。電源が通常作動すると想定される温度範囲とは、上限が１２０℃程度、場合によっては６０℃程度であり、下限は－４０℃程度、場合によっては－２０℃程度である。
　常温溶融塩はイオン液体とも呼ばれており、ピリジン系、脂肪族アミン系、脂環族アミン系の４級アンモニウム有機物カチオンが知られている。４級アンモニウム有機物カチオンとしては、ジアルキルイミダゾリウム、トリアルキルイミダゾリウム、などのイミダゾリウムイオン、テトラアルキルアンモニウムイオン、アルキルピリジニウムイオン、ピラゾリウムイオン、ピロリジニウムイオン、ピペリジニウムイオンなどが挙げられる。特に、イミダゾリウムカチオンが好ましい。
　なお、テトラアルキルアンモニウムイオンとしては、トリメチルエチルアンモニウムイオン、トリメチルエチルアンモニウムイオン、トリメチルプロピルアンモニウムイオン、トリメチルヘキシルアンモニウムイオン、テトラペンチルアンモニウムイオン、トリエチルメチルアンモニウムイオンなどが挙げられるが、これらに限定されるものではない。
　また、アルキルピリジウムイオンとしては、Ｎ－メチルピリジウムイオン、Ｎ－エチルピリジニウムイオン、Ｎ－プロピルピリジニウムイオン、Ｎ－ブチルピリジニウムイオン、１－エチル－２メチルピリジニウムイオン、１－ブチル－４－メチルピリジニウムイオン、１－ブチル－２，４ジメチルピリジニウムイオンなどが挙げられるが、これらに限定されるものではない。
　イミダゾリウムカチオンとしては、１，３－ジメチルイミダゾリウムイオン、１－エチル－３－メチルイミダゾリウムイオン、１－メチル－３－エチルイミダゾリウムイオン、１－メチル－３－ブチルイミダゾリウムイオン、１－ブチル－３－メチルイミダゾリウムイオン、１，２，３－トリメチルイミダゾリウムイオン、１，２－ジメチル－３－エチルイミダゾリウムイオン、１，２－ジメチル－３－プロピルイミダゾリウムイオン、１－ブチル－２，３－ジメチルイミダゾリウムイオンなどが挙げられるが、これらに限定されるものではない。
　なお、これらのカチオンを有する常温溶融塩は、単独で用いてもよく、または２種以上を混合して用いても良い。
　イオン伝導性ポリマー材料に常温溶融塩が含まれる場合、その含有量としては、イオン伝導性ポリマー１００質量部に対して、好ましくは１０～１０００質量部、より好ましくは２０～５００質量部である。
　イオン伝導性ポリマー材料は、可塑剤などを含んでいてもよい。可塑剤としては、特に限定されないが、ジシアノ化合物、分岐型エーテル化合物が好ましい。可塑剤を添加する場合は、イオン伝導性ポリマーを架橋することが好ましい。この架橋は、化学架橋であり、イオン伝導性ポリマー材料からの可塑剤の流出を抑制できる。
　ジシアノ化合物としてはスクシノニトリル、グルタロニトリル、アジポニトリル、１，５－ジシアノペンタン、１，６－ジシアノヘキサン、１，７－ジシアノヘプタン、１，８－ジシアノオクタン等が挙げられる。分岐型エーテル化合物の例として、下記の多分岐型エーテル化合物などが挙げられる。
Figure JPOXMLDOC01-appb-C000004
Figure JPOXMLDOC01-appb-C000005
　イオン伝導性ポリマー材料に可塑剤が含まれる場合、可塑剤の含有量としては、イオン伝導性ポリマー１００質量部に対して、好ましくは１０～１０００質量部、より好ましくは２０～５００質量部である。
　イオン伝導性ポリマー材料の形成には、熱反応開始剤、光反応開始剤、架橋助剤を用いてもよい。
　熱反応開始剤としては、有機過酸化物、アゾ化合物等から選ばれるラジカル開始剤が用いられる。有機過酸化物としては、ケトンパーオキシド、パーオキシケタール、ハイドロパーオキシド、ジアルキルパーオキシド、ジアシルパーオキシド、パーオキシエステル等、通常架橋用途に使用されているものが用いられ、アゾ化合物としてはアゾニトリル化合物、アゾアミド化合物、アゾアミジン化合物等、通常架橋用途に使用されているものが用いられる。ラジカル開始剤の添加量は種類により異なるが、通常、イオン伝導性ポリマーを１００質量部として０．１～１０質量部の範囲内である。
　光反応開始剤としては、アルキルフェノン系、ベンゾフェノン系、アシルフォスフィンオキサイド系、チタノセン類、トリアジン類、ビスイミダゾール類、オキシムエステル類などラジカル開始剤が用いられる。これらのラジカル重合開始剤の添加量は種類により異なるが、通常、イオン伝導性ポリマーを１００質量部として０．０１～５．０質量部の範囲内である。
　架橋助剤としては、エチレングリコールジアクリレート、エチレングリコールジメタクリレート、オリゴエチレングリコールジアクリレート、オリゴエチレングリコールジメタクリレート、トリメチロールプロパントリアクリレート、アリルメタクリレート、アリルアクリレート、ジアリルマレート、トリアリルイソシアヌレート、マレイミド、フェニルマレイミド、無水マレイン酸等を任意に用いることができる。
　イオン伝導性ポリマー材料には、後述する方法のため、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー、リチウム塩化合物を溶解させる溶媒を含有してもよく、アセトニトリル、トルエン、テトラヒドロフラン（ＴＨＦ）、ジオキサン、ジメチルスルホキシド（ＤＭＳＯ）、水等の極性の高い溶媒を用いることができる。
　電極材料間の空隙にイオン伝導性ポリマー材料を含ませる方法としては、前述の通り、特に限定されないが、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーおよびリチウム塩化合物が溶媒によって完全に溶解された溶液（組成物）を、活物質を含む層（より具体的には電極材料層前駆体を構成する電極材料の空隙）に含浸させることにより行うことができる。含浸する条件は、できる限り、低い温度（好ましくは、室温以下）で、溶媒をゆっくり蒸発させながら、空隙にイオン伝導性ポリマーおよびリチウム塩化合物を含有させる。また、電極材料層が厚膜の場合には、減圧下で行うこともできる。
　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーを架橋する場合には、イオン伝導性ポリマー材料を含浸させた層を、加熱又は活性エネルギー線照射（紫外線照射など）によって架橋させることができる。
無機固体電解質二次電池
　本発明の無機固体電解質二次電池は、本発明の無機固体電解質二次電池用電極を含む。より具体的には、正極及び負極（少なくとも一方は、本発明の電極によって構成されている）と、正極と負極の間に配置された無機固体電解質とを備える。なお、正極及び負極のうち、本発明の電極を用いなかった電極には、固体電解質二次電池に用いられる公知の電極を用いることができる。本発明の無機固体電解質二次電池用電極については、前述の通りである。
　本発明の無機固体電解質二次電池に用いられる本発明の電極は、活物質に加えて、さらに、前記のイオン伝導性ポリマー材料が、電極材料層に含まれていることにより、電極材料層に含まれる活物質などの電極材料（具体的には、活物質粒子、バインダー、導電助剤、増粘剤、無機固体電解質など）の空隙がイオン伝導性ポリマー材料によって埋められ、電極材料層の内部の界面抵抗が効果的に低下し、結果として、優れた充放電特性が発揮されるものと考えられる。また、本発明の固体電解質二次電池は、高温環境（例えば１００℃以上の高温環境）で使用されることもあるが、本発明の電極を用いることにより、高温環境において優れた充放電特性が発揮される。
　無機固体電解質としては、酸化物系固体電解質、及び硫化物系固体電解質を例示することができる。無機固体電解質は、一般に、電解質を構成する無機固体粒子の集合体である。
　酸化物系固体電解質は、酸素を含有し、かつ、周期律表第１族または第２族に属する金属のイオン伝導性を有し、かつ、電子絶縁性を有するものであれば特に限定されるものではない。
　酸化物系固体電解質を構成する具体的な化合物としては、ＬｉxＬａyＴｉＯ3〔ｘ＝０．３～０．７、ｙ＝０．３～０．７〕（ＬＬＴ）、ＬｉxＬａyＺｒzＭmＯn（ＭはＡｌ，Ｍｇ，Ｃａ，Ｓｒ，Ｖ，Ｎｂ，Ｔａ，Ｔｉ，Ｇｅ，Ｉｎ，Ｓｎの少なくとも１種以上の元素でありｘは５≦ｘ≦１０を満たし、ｙは１≦ｙ≦４を満たし、ｚは１≦ｚ≦４を満たし、ｍは０≦ｍ≦２を満たし、ｎは５≦ｎ≦２０を満たす。）ＬｉxＢyＭzＯn（式中ＭはＣ，Ｓ，Ａｌ，Ｓｉ，Ｇａ，Ｇｅ，Ｉｎ，Ｓｎの少なくとも１種以上の元素でありｘは０≦ｘ≦５を満たし、ｙは０≦ｙ≦１を満たし、ｚは０≦ｚ≦１を満たし、ｎは０≦ｎ≦６を満たす。）、Ｌｉx（Ａｌ，Ｇａ）y（Ｔｉ，Ｇｅ）zＳｉaＰmＯn（ただし、１≦ｘ≦３、０≦ｙ≦１、０≦ｚ≦２、０≦ａ≦１、１≦ｍ≦７、３≦ｎ≦１３）、Ｌｉ(3-2x)ＭxＤＯ（ｘは０以上０．１以下の数を表し、Ｍは２価の金属原子を表す。Ｄはハロゲン原子または２種以上のハロゲン原子の組み合わせを表す。）、ＬｉxＳｉyＯz（１≦ｘ≦５、０＜ｙ≦３、１≦ｚ≦１０）、ＬｉxＳyＯz（１≦ｘ≦３、０＜ｙ≦２、１≦ｚ≦１０）、Ｌｉ3ＢＯ3－Ｌｉ2ＳＯ4、Ｌｉ2Ｏ－Ｂ2Ｏ3－Ｐ2Ｏ5、Ｌｉ2Ｏ－ＳｉＯ2、Ｌｉ6ＢａＬａ2Ｔａ2Ｏ12、Ｌｉ3ＰＯ(4-3/2w)Ｎw（ｗはｗ＜１）、ＬＩＳＩＣＯＮ（Ｌｉｔｈｉｕｍ　ｓｕｐｅｒ　ｉｏｎｉｃ　ｃｏｎｄｕｃｔｏｒ）型結晶構造を有するＬｉ3.5Ｚｎ0.25ＧｅＯ4、ペロブスカイト型結晶構造を有するＬａ0.55Ｌｉ0.35ＴｉＯ3、ＮＡＳＩＣＯＮ（Ｎａｔｒｉｕｍ　ｓｕｐｅｒ　ｉｏｎｉｃ　ｃｏｎｄｕｃｔｏｒ）型結晶構造を有するＬｉＴｉ2Ｐ3Ｏ12、Ｌｉ(1+x+y)（Ａｌ，Ｇａ）x（Ｔｉ，Ｇｅ）(2-x)ＳｉyＰ(3-y)Ｏ12（ただし、０≦ｘ≦１、０≦ｙ≦１）、ガーネット型結晶構造を有するＬｉ7Ｌａ3Ｚｒ2Ｏ１2等が挙げられる。またＬｉ、Ｐ及びＯを含むリン化合物も望ましい。例えばリン酸リチウム（Ｌｉ3ＰＯ4）、リン酸リチウムの酸素の一部を窒素で置換したＬｉＰＯＮ、ＬｉＰＯＤ（Ｄは、Ｔｉ、Ｖ、Ｃｒ、Ｍｎ、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ｚｒ、Ｎｂ、Ｍｏ、Ｒｕ、Ａｇ、Ｔａ、Ｗ、Ｐｔ、Ａｕ等から選ばれた少なくとも１種）等が挙げられる。また、ＬｉＡＯＮ（Ａは、Ｓｉ、Ｂ、Ｇｅ、Ａｌ、Ｃ、Ｇａ等から選ばれた少なくとも１種）等も好ましく用いることができる。
　その中でも、ＬｉxＬａyＴｉＯ3〔ｘ＝０．３～０．７、ｙ＝０．３～０．７〕（ＬＬＴ）、ＬｉxＬａyＺｒzＭmＯn（ＭはＡｌ，Ｍｇ，Ｃａ，Ｓｒ，Ｖ，Ｎｂ，Ｔａ，Ｔｉ，Ｇｅ，Ｉｎ，Ｓｎの少なくとも１種以上の元素でありｘは５≦ｘ≦１０を満たし、ｙは１≦ｙ≦４を満たし、ｚは１≦ｚ≦４を満たし、ｍは０≦ｍ≦２を満たし、ｎは５≦ｎ≦２０を満たす。）、Ｌｉ7Ｌａ3Ｚｒ2Ｏ12（ＬＬＺ）、Ｌｉ3ＢＯ3、Ｌｉ3ＢＯ3－Ｌｉ2ＳＯ4、Ｌｉ3ＢＯ3－Ｌｉ2ＣＯ3、Ｌｉx（Ａｌ，Ｇａ）y（Ｔｉ，Ｇｅ）zＳｉaＰmＯn（ただし、１≦ｘ≦３、０≦ｙ≦１、０≦ｚ≦２、０≦ａ≦１、１≦ｍ≦７、３≦ｎ≦１３）が好ましい。これらは単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　硫化物系固体電解質は、硫黄を含有し、かつ、周期律表第１族または第２族に属する金属のイオン伝導性を有し、かつ、電子絶縁性を有するものであれば特に限定されるものではない。例えば下記式で示される組成を満たすリチウムイオン伝導性無機固体電解質が挙げられる。
　ＬｉaＭbＰcＳdＡe
　式中、Ｍは、Ｂ、Ｚｎ、Ｓｎ、Ｓｉ、Ｃｕ、Ｇａ、Ｓｂ、Ａｌ及びＧｅから選択される元素を示す。なかでも、Ｂ、Ｓｎ、Ｓｉ、Ａｌ、Ｇｅが好ましく、Ｓｎ、Ａｌ、Ｇｅがより好ましい。Ａは、Ｉ、Ｂｒ、Ｃｌ、Ｆを示し、Ｉ、Ｂｒが好ましく、Ｉが特に好ましい。ａ～ｅは各元素の組成比を示し、ａ：ｂ：ｃ：ｄ：ｅは１～１２：０～１：１：２～１２：０～５を満たす。ａはさらに、１～９が好ましく、１．５～４がより好ましい。ｂは０～０．５が好ましい。ｄはさらに、３～７が好ましく、３．２５～４．５がより好ましい。ｅはさらに、０～３が好ましく、０～２がより好ましい。
　式において、Ｌｉ、Ｍ、Ｐ、Ｓ及びＡの組成比は、好ましくはｂ、ｅが０であり、より好ましくはｂ＝０、ｅ＝０で且つａ、ｃ及びｄの比（ａ：ｃ：ｄ）がａ：ｃ：ｄ＝１～９：１：３～７であり、さらに好ましくはｂ＝０、ｅ＝０で且つａ：ｃ：ｄ＝１．５～４：１：３．２５～４．５である。
　無機固体電解質が粒子状である場合、その粒子径としては、例えば０．０１～１００μｍ、好ましくは０．１～２０μｍが挙げられる。
　本発明の固体電解質二次電池においては、正極と無機固体電解質との間、及び負極と前記無機固体電解質との間の少なくとも一方に、リチウム塩化合物を含む側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー材料の架橋フィルムを配置してもよい。イオン伝導性ポリマー材料の架橋フィルムは、リチウム塩化合物とイオン伝導性ポリマーを含む組成物の架橋フィルムである。当該架橋フィルムを配置することにより、電極や無機固体電解質の界面抵抗をより一層低下させることができる。
　架橋フィルムは、少なくとも、リチウム塩化合物と、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーとを含む組成物を架橋することにより形成される。すなわち、架橋フィルムは、リチウム塩化合物とイオン伝導性ポリマーを含む組成物の架橋フィルムである。リチウム塩化合物及びイオン伝導性ポリマーについては、前述の通りである。
　架橋フィルムに含まれるイオン伝導性ポリマーの含有量としては、架橋フィルム全体を１００質量部として、好ましくは１０～９０質量部、より好ましくは２０～８０質量部である。
　架橋フィルムに含まれるリチウム塩化物の含有量リチウム塩化合物のモル数／イオン伝導性ポリマーのエーテル酸素原子の総モル数の値が０．０００１～５が好ましく、更に好ましくは０．００１～０．５の範囲がよい。
　また、架橋フィルムには、常温溶融塩が含まれていてもよい。常温溶融塩については、前述の通りである。
　架橋フィルムに常温溶融塩が含まれる場合、その含有量としては、イオン伝導性ポリマー１００質量部に対して、好ましくは１０～１０００質量部、より好ましくは２０～５００質量部である。
　架橋フィルムは、可塑剤などを含んでいてもよい。可塑剤については、前述の通りである。
　架橋フィルムに可塑剤が含まれる場合、可塑剤の含有量としては、イオン伝導性ポリマー１００質量部に対して、好ましくは１０～１０００質量部、より好ましくは２０～５００質量部である。
　リチウム塩化合物とイオン伝導性ポリマーを含む組成物に反応開始剤や架橋助剤を配合して、架橋フィルムを形成してもよい。反応開始剤としては、熱反応開始剤、光反応開始剤が挙げられる。
　熱反応開始剤、光反応開始剤、及び架橋助剤については、前述の通りである。
　リチウム塩化合物とイオン伝導性ポリマーを含む組成物には、有機溶媒を配合してもよく、有機溶媒としては、トルエン、キシレン、ベンゼン、アセトニトリル、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、ＴＨＦ（テトラヒドロフラン）が挙げられる。
　架橋フィルムの作製方法は、例えば、イオン伝導性ポリマー、必要に応じて反応開始剤、及びリチウム塩化合物を有機溶媒に混合して溶解して組成物を形成し、基材（例えばＰＥＴフィルムやテフロン（登録商標）板など）上に組成物をキャスティングし、溶媒を除去後、加熱又は紫外線などの活性エネルギー線照射によって架橋フィルムを作製する方法が挙げられる。また、直接、無機固体電解質の表面に当該組成物をキャスティングして、架橋フィルムを作製することもできる。
　架橋フィルムの膜厚は、好ましくは０．１μｍ～２００μｍ、より好ましくは０．５μｍ～１００μｍの範囲内である。
　本発明の無機固体電解質二次電池の積層構成としては、例えば、以下の構成が挙げられる。
正極、無機固体電解質、及び負極が順に積層された積層構成；
正極、架橋フィルム、無機固体電解質、架橋フィルム、及び負極が順に積層された積層構成；
正極、架橋フィルム、無機固体電解質、及び負極が順に積層された積層構成；
正極、無機固体電解質、架橋フィルム、及び負極が順に積層された積層構成。
　本発明の無機固体電解質二次電池においては、無機固体電解質と前述の架橋フィルムとが接触していることが好ましい。無機固体電解質は、一般に、電解質を構成する無機固体粒子の集合体により形成されており、粒子間には空隙が存在している。架橋フィルムは、リチウム塩化合物を含むイオン伝導性ポリマーを含む組成物の架橋体であることから、イオン伝導性を有しており、かつ、無機材料と比較して高い柔軟性を有している。従って、当該架橋フィルムは、無機固体電解質との接触面積が大きくなり、その結果、無機固体電解質の界面抵抗が効果的に低下し、本発明の無機固体電解質二次電池は優れた充放電特性を発揮するものと考えられる。なお、電極材料層に含まれる活物質粒子なども空隙を形成することから、本発明の無機固体電解質二次電池においては、架橋フィルムが電極の電極材料層と接触していることも好ましいし、架橋フィルムが電極材料層と無機固体電解質の両方と接触していることも好ましい。
固体電解質二次電池の製造方法
　本発明の固体電解質二次電池の製造方法は特に限定されず、少なくとも、正極、負極、及び無機固体電解質で構成され、公知の方法にて製造される。例えば、コイン型のリチウムイオン電池の場合、正極、無機固体電解質、負極を配置して、外装缶に挿入する。その後、封口体とタブ溶接などで接合して、封口体を封入し、カシめることで蓄電池が得られる。電池の形状は限定されないが、例としてはコイン型、円筒型、シート型などがあげられ、２個以上の電池を積層した構造でもよい。
　以下の実施例において本発明をより具体的に説明するが、本発明はこれらに限定されない。
　本実施例では、コイン電池を作製し、コイン電池の充放電特性の性能評価を以下の実験にて行った。
［作製した電池の評価］
　作製した電池の評価としては充放電装置を用いて充放電試験を行い、充電容量および放電容量を求めた。
充放電測定
　０．１Ｃ（１０時間率）に相当する電流で４．２ＶまでＣＣＣＶ充電（０．０１Ｃカット）後、０．１Ｃに相当する電流で、２．５ＶまでＣＣＣＶ放電（０．０１Ｃカット）を行った。試験温度は１００℃環境とした。
［正極前駆体の実施作製例］
　正極活物質としてＮＣＭ（ニッケル／コバルト／マンガン酸リチウム＝５／２／３）１００質量部に、導電助剤としてアセチレンブラック３質量部、黒鉛３質量部、バインダーとしてＰＶｄＦ３質量部を加え、さらにスラリーの固形分濃度が３５質量％となるようにＮＭＰ溶液中に加えて、十分に混合して正極用スラリーを得た。得られた正極スラリーを厚さ２０μｍのアルミ集電体上にダイコーターを用いて塗布し、１００℃で１２時間以上乾繰後、ロールプレス機にてプレスを行い、厚さ２０μｍの正極を作製した。正極活物質の目付量６．６ｍｇ／ｃｍ2、正極密度３．１ｇ／ｃｍ3、空隙率２６％。
［負極前駆体の実施作製例］
　負極活物質として人造黒鉛（粒径１０μｍ）　１００質量部に、導電助剤として気相成長炭素繊維（ＶＧＣＦ）２質量部、バインダーとしてＳＢＲ　３質量部、増粘剤としてカルボキシメチルセルロースのナトリウム塩　２質量部を加え、さらにスラリーの固形分濃度が３５質量％となるように水を加えて、十分に混合して負極用スラリーを得た。得られた負極スラリーを厚さ１６．５μｍの銅集電体上にダイコーターを用いて塗布し、１００℃で１２時間以上乾繰後、ロールプレス機にてプレスを行い、厚さ２２μｍの負極を作製した。負極活物質の目付量３．１ｍｇ／ｃｍ2、負極密度１．２ｇ／ｃｍ3、空隙率２３％。
［固体電解質二次電池用正極（正極前駆体にイオン伝導性ポリマー及びリチウム塩化合物を含浸した正極）の実施作製例］
　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーとしてエチレンオキシド／ジエチレングリコールメチルグリシジルエーテル／アリルグリシジルエーテル＝８０／１７／３モル％三元共重合体（重量平均分子量１５０万）１００質量部、リチウム塩化合物としてホウフッ化リチウム１２質量部、架橋助剤として、トリメチロールプロパントリアクリレート　１０質量部、ラジカル開始剤としてベンゾイルパーオキシド（ナイパーＢＭＴ、日油株式会社製）０．３質量部をアセトニトリル　９００質量部に完全に溶解させた電極含浸用塗工溶液を調製した。実施作製例で得られた正極前駆体に、電極含浸用塗工溶液を１４０μｍ厚さとなるように塗工した。その後、２時間静置することにより、溶媒を除去しながら、正極前駆体内の空隙にイオン伝導性ポリマーとリチウム塩化合物を含浸した。１００℃で２時間、減圧下、含浸したイオン伝導性ポリマーの架橋を行い、固体電解質二次電池用正極を作製した。正極の断面をＳＥＭ（走査型電子顕微鏡）分析を行った。ＳＥＭにより、正極内の空隙にイオン伝導性ポリマーが観測された。
［固体電解質二次電池用正極の比較作製例］
　実施作製例の固体電解質二次電池用正極において、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーの代わりに、ポリエチレンオキシド１００質量部（重量平均分子量１１０万）を用いて、同様にして、比較用の固体電解質二次電池用正極を作製した。正極の断面について、ＳＥＭ分析を行った。ＳＥＭにより、正極内の空隙にポリエチレンオキシドが観測された。
［固体電解質二次電池用負極（負極前駆体にイオン伝導性ポリマー及びリチウム塩化合物を含浸した負極）の実施作製例］
　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーとしてエチレンオキシド／ジエチレングリコールメチルグリシジルエーテル／アリルグリシジルエーテル＝８０／１７／３モル％三元共重合体（重量平均分子量１５０万）１００質量部、リチウム塩化合物としてＬｉＴＦＳＩ３８質量部を、架橋助剤として、トリメチロールプロパントリアクリレート１０質量部、ラジカル開始剤としてベンゾイルパーオキシド（ナイパーＢＭＴ、日油株式会社製）０．３質量部をアセトニトリル９００質量部に完全に溶解させた電極含浸用塗工溶液を調製した。負極の実施作製例で得られた負極前駆体に、電極含浸用塗工溶液を１２０μｍ厚さとなるように塗工した。その後、２時間静置することにより、溶媒を除去しながら、負極前駆体内の空隙にイオン伝導性ポリマーとリチウム塩化合物を含浸した。１００℃で２時間、減圧下、含浸した側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーの架橋を行い、固体電解質二次電池用負極を作製した。負極の断面をＳＥＭ－ＥＤＸ（走査型電子顕微鏡／エネルギー分散型Ｘ線分光法）分析を行った。ＳＥＭにより、負極内の空隙にイオン伝導性ポリマーが観測され、また、ＥＤＸにより空隙にＦイオンの分布が観測され、これにより、ＬｉＴＦＳＩが空隙の中に含まれていることが確認できた。
［イオン伝導性ポリマー材料の架橋フィルムの作製例］
　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーとしてエチレンオキシド／ジエチレングリコールメチルグリシジルエーテル／アリルグリシジルエーテル＝８０／１７／３モル％三元共重合体（重量平均分子量１５０万）１００質量部、リチウム塩化合物としてＬｉＴＦＳＩ３８質量部を、架橋助剤として、トリメチロールプロパントリアクリレート　１０質量部、ラジカル開始剤としてベンゾイルパーオキシド（ナイパーＢＭＴ、日油株式会社製）０．３質量部をアセトニトリル　９００質量部に溶解させた溶液を調製した。この溶液をポリテトラフルオロエチレン製モールド上にキャストして、室温で乾燥した後、１００℃、２時間、熱架橋を行い、厚さ２０μｍのイオン伝導性ポリマー材料の架橋フィルムを作製した。
電池の製造例
［固体電解質二次電池の実施製造例１］
　ドライルーム内において、固体電解質二次電池用正極の実施作製例で得た正極、作製例のイオン伝導性ポリマー材料の架橋フィルム、無機固体電解質としてＬｉ7Ｌａ3Ｚｒ2Ｏ12（ＬＬＺ，　豊島製作所製　膜厚５００μｍ）、作製例のイオン伝導性ポリマー材料の架橋フィルム、負極としての金属リチウム箔の順に積層後、カシめ、試験用２０３２型コイン電池を製造した。
＜充放電条件＞
　下限電圧２．５Ｖ－上限電圧４．２Ｖ、１００℃
　ＣＣ（０．１Ｃ）－ＣＶ（０．０１Ｃ）充電
　ＣＣ（０．１Ｃ）－ＣＶ（０．０１Ｃ）放電
＜充放電試験結果＞
　充電容量１６８ｍＡｈ／ｇ、放電容量１６２ｍＡｈ／ｇ
［固体電解質二次電池の実施製造例２］
　ドライルーム内において、固体電解質二次電池用正極の実施作製例で得た正極、作製例のイオン伝導性ポリマー材料の架橋フィルム、無機固体電解質としてＬｉ7Ｌａ3Ｚｒ2Ｏ12（ＬＬＺ，　豊島製作所製　膜厚５００μｍ）、作製例のイオン伝導性ポリマー材料の架橋フィルム、固体電解質二次電池用負極の実施作製例で得た負極の順に積層後、カシめ、試験用２０３２型コイン電池を製造した。
＜充放電条件＞
　下限電圧２．５Ｖ－上限電圧４．２Ｖ、１００℃
　ＣＣ（０．１Ｃ）－ＣＶ（０．０１Ｃ）充電
　ＣＣ（０．１Ｃ）－ＣＶ（０．０１Ｃ）放電
＜充放電試験結果＞
　充電容量１５５ｍＡｈ／ｇ　放電容量１４０ｍＡｈ／ｇ
［固体電解質二次電池の比較製造例１］
　ドライルーム内において、固体電解質二次電池用正極の比較例のポリエチレンオキシドを用いた正極、無機固体電解質としてＬｉ7Ｌａ3Ｚｒ2Ｏ12（ＬＬＺ，　豊島製作所製　膜厚５００μＭ）、作製例のイオン伝導性ポリマー材料の架橋フィルム、負極としての金属リチウム箔の順に積層後、カシめ、試験用２０３２型コイン電池を製造した。
＜充放電条件＞
　下限電圧２．５Ｖ－上限電圧４．２Ｖ、１００℃
　ＣＣ（０．１Ｃ）－ＣＶ（０．０１Ｃ）充電
　ＣＣ（０．１Ｃ）－ＣＶ（０．０１Ｃ）放電
＜充放電試験結果＞
　充電容量１００ｍＡｈ／ｇ　放電容量５０ｍＡｈ／ｇ
　電極材料の空隙がイオン伝導性ポリマー材料によって埋められた電極は、埋められていない電極、ポリエチレンオキシドによって埋められた電極と比較して、明らかに、充電および放電容量を向上させていることがわかる。ポリエチレンオキシドは、結晶性が高く、架橋できないので、１００℃の高温では溶融のため形状維持ができなくなり、結着性が弱くなっていることが原因であると考えられる。側鎖にエチレンオキシド単位を有するイオン伝導性ポリマーは、柔軟性と結着性を有するので、無機固体電解質との界面での抵抗を下げる効果があるといえる。
　本発明の固体電解質二次電池用電極は、固体電解質二次電池の電極として利用されることにより、優れた充放電特性を発揮させることができ、電気自動車やハイブリッド電気自動車などの車載用途や家庭用電力貯蔵用の蓄電池といった大型の電池用途に好適に利用可能である。

Claims (9)

  1. 　側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料と、活物質とを含有する電極材料層を備える、無機固体電解質二次電池用電極。
  2. 　前記活物質が、ＬｉＭＯ2、ＬｉＭ2Ｏ4、Ｌｉ2ＭＯ3、ＬｉＭＥＯ4（式中のＭは、遷移金属からなり、Ｃｏ、Ｍｎ、Ｎｉ、Ｃｒ、Ｆｅ、Ｔｉの少なくとも一種を含んでいる。ＥはＰ、Ｓｉの少なくとも１種を含んでいる。）からなる群より選択される少なくとも１種である、請求項１に記載の無機固体電解質二次電池用電極。
  3. 　前記活物質が、炭素材料、シリコン系化合物、及びスズ系化合物からなる群より選択される少なくとも１種である、請求項１に記載の無機固体電解質二次電池用電極。
  4. 　前記イオン伝導性ポリマーは、側鎖にエチレンオキシド単位を有するポリエーテルである、請求項１～３のいずれか１項に記載の無機固体電解質二次電池用電極。
  5. 　無機固体電解質と共に、固体電解質二次電池に用いられる、請求項１～４のいずれか１項に記載の無機固体電解質二次電池用電極。
  6. 　前記無機固体電解質は、酸化物系固体電解質又は硫化物系固体電解質である、請求項５に記載の無機固体電解質二次電池用電極。
  7. 　活物質を含む層に、側鎖にエチレンオキシド単位を有するイオン伝導性ポリマー及びリチウム塩化合物を含むイオン伝導性ポリマー材料を含浸させる工程を含む、無機固体電解質二次電池用電極の製造方法。
  8. 　前記イオン伝導性ポリマー材料を含浸させた層を、加熱又は活性エネルギー線照射によって架橋させる工程を含む、請求項７に記載の無機固体電解質二次電池用電極の製造方法。
  9. 　請求項１～６のいずれかに記載の無機固体電解質二次電池用電極を含む、無機固体電解質二次電池。
PCT/JP2019/045952 2018-11-26 2019-11-25 無機固体電解質二次電池用電極、および無機固体電解質二次電池 WO2020110993A1 (ja)