WO2017209210A1 - Composition de résine époxy, feuille de stade b, composition de résine époxy durcie, feuille de résine, feuille de métal avec résine, et substrat métallique - Google Patents

Composition de résine époxy, feuille de stade b, composition de résine époxy durcie, feuille de résine, feuille de métal avec résine, et substrat métallique Download PDF

Info

Publication number
WO2017209210A1
WO2017209210A1 PCT/JP2017/020343 JP2017020343W WO2017209210A1 WO 2017209210 A1 WO2017209210 A1 WO 2017209210A1 JP 2017020343 W JP2017020343 W JP 2017020343W WO 2017209210 A1 WO2017209210 A1 WO 2017209210A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
epoxy resin
epoxy
general formula
mass
Prior art date
Application number
PCT/JP2017/020343
Other languages
English (en)
Japanese (ja)
Inventor
一也 木口
慎吾 田中
智雄 西山
竹澤　由高
Original Assignee
日立化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日立化成株式会社 filed Critical 日立化成株式会社
Publication of WO2017209210A1 publication Critical patent/WO2017209210A1/fr

Abstract

L'invention concerne une composition de résine époxy qui comprend deux sortes de composé époxy ou plus possédant un squelette mésogène, un agent de durcissement, et une charge inorganique. Les deux sortes de composé époxy ou plus possédant un squelette mésogène sont mutuellement compatibles, et permettent de former une structure smectique par réaction avec ledit agent de durcissement.
PCT/JP2017/020343 2016-06-02 2017-05-31 Composition de résine époxy, feuille de stade b, composition de résine époxy durcie, feuille de résine, feuille de métal avec résine, et substrat métallique WO2017209210A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016111371 2016-06-02
JP2016-111371 2016-06-02

Publications (1)

Publication Number Publication Date
WO2017209210A1 true WO2017209210A1 (fr) 2017-12-07

Family

ID=60478811

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/020343 WO2017209210A1 (fr) 2016-06-02 2017-05-31 Composition de résine époxy, feuille de stade b, composition de résine époxy durcie, feuille de résine, feuille de métal avec résine, et substrat métallique

Country Status (2)

Country Link
TW (1) TW201815865A (fr)
WO (1) WO2017209210A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018168556A1 (fr) * 2017-03-15 2018-09-20 日立化成株式会社 Résine époxyde, composition de résine époxyde, produit durci de résine époxyde et matériau composite
WO2020045560A1 (fr) * 2018-08-31 2020-03-05 Jnc株式会社 Composition, produit durci, corps stratifié et dispositif électronique
CN113993947A (zh) * 2019-06-21 2022-01-28 住友电木株式会社 热固性树脂组合物、树脂片及金属基基板

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008239679A (ja) * 2007-03-26 2008-10-09 Sumitomo Chemical Co Ltd エポキシ樹脂組成物
JP2008266594A (ja) * 2007-03-26 2008-11-06 Sumitomo Chemical Co Ltd エポキシ樹脂組成物
JP2009215390A (ja) * 2008-03-10 2009-09-24 Shin Kobe Electric Mach Co Ltd 積層板の製造法
JP2012149191A (ja) * 2011-01-20 2012-08-09 Hitachi Chemical Co Ltd 熱硬化性樹脂組成物、並びにその半硬化物及び硬化物
JP2013227451A (ja) * 2012-04-26 2013-11-07 Hitachi Chemical Co Ltd エポキシ樹脂組成物、半硬化エポキシ樹脂組成物、硬化エポキシ樹脂組成物、樹脂シート、プリプレグ、積層板、金属基板、及びプリント配線板
WO2015141797A1 (fr) * 2014-03-20 2015-09-24 日立化成株式会社 Composition de résine, feuille de résine, produit durci constitué d'une feuille de résine, stratifié à base de feuilles de résine, produit durci constitué d'un stratifié à base de feuilles de résine et leur procédé de production, dispositif semi-conducteur et dispositif à del.
WO2016093248A1 (fr) * 2014-12-08 2016-06-16 日立化成株式会社 Composition de résine époxy, feuille de résine, pré-imprégné, feuille métallique dotée de résine, substrat métallique et dispositif semi-conducteur pour alimentation électrique
WO2016104788A1 (fr) * 2014-12-26 2016-06-30 日立化成株式会社 Matériau de moulage à base de résine époxy, article moulé, article moulé durci et procédé de fabrication d'un article moulé

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008239679A (ja) * 2007-03-26 2008-10-09 Sumitomo Chemical Co Ltd エポキシ樹脂組成物
JP2008266594A (ja) * 2007-03-26 2008-11-06 Sumitomo Chemical Co Ltd エポキシ樹脂組成物
JP2009215390A (ja) * 2008-03-10 2009-09-24 Shin Kobe Electric Mach Co Ltd 積層板の製造法
JP2012149191A (ja) * 2011-01-20 2012-08-09 Hitachi Chemical Co Ltd 熱硬化性樹脂組成物、並びにその半硬化物及び硬化物
JP2013227451A (ja) * 2012-04-26 2013-11-07 Hitachi Chemical Co Ltd エポキシ樹脂組成物、半硬化エポキシ樹脂組成物、硬化エポキシ樹脂組成物、樹脂シート、プリプレグ、積層板、金属基板、及びプリント配線板
WO2015141797A1 (fr) * 2014-03-20 2015-09-24 日立化成株式会社 Composition de résine, feuille de résine, produit durci constitué d'une feuille de résine, stratifié à base de feuilles de résine, produit durci constitué d'un stratifié à base de feuilles de résine et leur procédé de production, dispositif semi-conducteur et dispositif à del.
WO2016093248A1 (fr) * 2014-12-08 2016-06-16 日立化成株式会社 Composition de résine époxy, feuille de résine, pré-imprégné, feuille métallique dotée de résine, substrat métallique et dispositif semi-conducteur pour alimentation électrique
WO2016104788A1 (fr) * 2014-12-26 2016-06-30 日立化成株式会社 Matériau de moulage à base de résine époxy, article moulé, article moulé durci et procédé de fabrication d'un article moulé

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
SHUNSUKE TAKENAKA ET AL.: "Saikin no Tenbo 2 New Liquid Crystalline Materials (Smectic", OYO BUTSURI, vol. 54, no. 2, 5 February 1985 (1985-02-05), pages 143 - 147 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018168556A1 (fr) * 2017-03-15 2018-09-20 日立化成株式会社 Résine époxyde, composition de résine époxyde, produit durci de résine époxyde et matériau composite
US11466119B2 (en) 2017-03-15 2022-10-11 Showa Denko Materials Co., Ltd. Epoxy resin, epoxy resin composition, epoxy resin cured product, and composite material
WO2020045560A1 (fr) * 2018-08-31 2020-03-05 Jnc株式会社 Composition, produit durci, corps stratifié et dispositif électronique
CN113993947A (zh) * 2019-06-21 2022-01-28 住友电木株式会社 热固性树脂组合物、树脂片及金属基基板

Also Published As

Publication number Publication date
TW201815865A (zh) 2018-05-01

Similar Documents

Publication Publication Date Title
JP7201029B2 (ja) エポキシ樹脂組成物、樹脂シート、プリプレグ、樹脂付金属箔、金属基板、及びパワー半導体装置
JP6102082B2 (ja) エポキシ樹脂組成物、半硬化エポキシ樹脂組成物、硬化エポキシ樹脂組成物、樹脂シート、プリプレグ、積層板、金属基板、及びプリント配線板
TWI462947B (zh) Ｂ階片、附樹脂金屬箔、金屬基板、及ｌｅｄ基板
WO2017209208A1 (fr) Procédé de production pour stratifié
WO2017145413A1 (fr) Composition à base de résine époxy, feuille de résine, feuille de stade b, feuille de stade c, objet durci, feuille métallique contenant de la résine et substrat métallique
US10851200B2 (en) Resin composition and method of producing laminate
WO2017209210A1 (fr) Composition de résine époxy, feuille de stade b, composition de résine époxy durcie, feuille de résine, feuille de métal avec résine, et substrat métallique
JP7115538B2 (ja) エポキシ樹脂、エポキシ樹脂組成物、樹脂シート、ｂステージシート、ｃステージシート、硬化物、樹脂付金属箔、金属基板、及びパワー半導体装置
JPWO2016121758A1 (ja) エポキシ樹脂組成物、半硬化エポキシ樹脂組成物、樹脂シート及びプリプレグ
JP7114940B2 (ja) 樹脂組成物膜の製造方法、樹脂シートの製造方法、ｂステージシートの製造方法、ｃステージシートの製造方法、樹脂付金属箔の製造方法及び金属基板の製造方法
US11535700B2 (en) Epoxy polymer, epoxy resin, epoxy resin composition, resin sheet, b-stage sheet, cured product, c-stage sheet, metal foil with resin, metal substrate and method for manufacturing
JP2018030929A (ja) エポキシ樹脂組成物、樹脂シート、ｂステージシート、硬化物、ｃステージシート、樹脂付金属箔、及び金属基板
WO2019106835A1 (fr) Composition de résine, et procédé de fabrication de stratifié
WO2017209209A1 (fr) Procédé de production pour stratifié
JP2019147932A (ja) 樹脂組成物、樹脂シート、ｂステージシート、ｃステージシート、樹脂付金属箔、金属基板及びパワー半導体装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17806761

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17806761

Country of ref document: EP

Kind code of ref document: A1