WO2016039475A1 - 合わせガラス用中間膜及び合わせガラス - Google Patents

合わせガラス用中間膜及び合わせガラス Download PDF

Info

Publication number
WO2016039475A1
WO2016039475A1 PCT/JP2015/075936 JP2015075936W WO2016039475A1 WO 2016039475 A1 WO2016039475 A1 WO 2016039475A1 JP 2015075936 W JP2015075936 W JP 2015075936W WO 2016039475 A1 WO2016039475 A1 WO 2016039475A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
laminated glass
polyvinyl acetal
acetal resin
less
Prior art date
Application number
PCT/JP2015/075936
Other languages
English (en)
French (fr)
Inventor
達矢 岩本
奈美 水口
祐磨 武田
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=55459214&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2016039475(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority to EP15839712.5A priority Critical patent/EP3192779B1/en
Priority to JP2015547188A priority patent/JP6613141B2/ja
Priority to KR1020167034251A priority patent/KR102309449B1/ko
Priority to BR112017004162A priority patent/BR112017004162A2/pt
Priority to CN201580048937.9A priority patent/CN107001134B/zh
Priority to MX2017002850A priority patent/MX2017002850A/es
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to TW105108143A priority patent/TWI780024B/zh
Publication of WO2016039475A1 publication Critical patent/WO2016039475A1/ja
Priority to US15/455,293 priority patent/US11141958B2/en
Priority to US15/455,323 priority patent/US10967611B2/en
Priority to US15/455,444 priority patent/US11135811B2/en
Priority to US15/455,457 priority patent/US20170246842A1/en
Priority to US15/455,379 priority patent/US20170197395A1/en
Priority to US15/455,461 priority patent/US10525677B2/en
Priority to US15/455,355 priority patent/US10967612B2/en
Priority to US16/690,655 priority patent/US11407205B2/en
Priority to US16/935,522 priority patent/US11235559B2/en

Abstract

　各層間の接着力を高めることができる合わせガラス用中間膜を提供する。　本発明に係る合わせガラス用中間膜は、ポリビニルアセタール樹脂と可塑剤とを含む第１の層と、ポリビニルアセタール樹脂と可塑剤とを含む第２の層とを備え、前記第２の層が、前記第１の層の第１の表面に積層されており、前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率と、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率とが異なり、前記第１の層がフィラーを含むか、前記第２の層がフィラーを含むか、又は、中間膜が前記第１の層と前記第２の層との界面に部分的にフィラーを含む。

Description

合わせガラス用中間膜及び合わせガラス
　本発明は、合わせガラスを得るために用いられる合わせガラス用中間膜に関する。また、本発明は、上記合わせガラス用中間膜を用いた合わせガラスに関する。
　合わせガラスは、外部衝撃を受けて破損してもガラスの破片の飛散量が少なく、安全性に優れている。このため、上記合わせガラスは、自動車、鉄道車両、航空機、船舶及び建築物等に広く使用されている。上記合わせガラスは、２つのガラス板の間に合わせガラス用中間膜を挟み込むことにより、製造されている。
　上記合わせガラス用中間膜としては、１層の構造を有する単層の中間膜と、２層以上の構造を有する多層の中間膜とがある。
　上記合わせガラス用中間膜の一例として、下記の特許文献１には、アセタール化度が６０～８５モル％のポリビニルアセタール樹脂１００重量部と、アルカリ金属塩及びアルカリ土類金属塩の内の少なくとも一種の金属塩０．００１～１．０重量部と、３０重量部を超える可塑剤とを含む遮音層が開示されている。この遮音層は、単層で中間膜として用いられ得る。
　さらに、下記の特許文献１には、上記遮音層と他の層とが積層された多層の中間膜も記載されている。遮音層に積層される他の層は、アセタール化度が６０～８５モル％のポリビニルアセタール樹脂１００重量部と、アルカリ金属塩及びアルカリ土類金属塩の内の少なくとも一種の金属塩０．００１～１．０重量部と、３０重量部以下である可塑剤とを含む。
　下記の特許文献２には、３３℃以上のガラス転移温度を有するポリマー層である中間膜が開示されている。特許文献２では、上記ポリマー層が、厚みが４．０ｍｍ以下であるガラス板の間に配置されることが記載されている。
　下記の特許文献３には、ポリビニルアセタール（Ａ）、少なくとも１種の可塑剤（Ｂ）、フュームドシリカ（Ｃ）及び少なくとも１種の塩基性化合物（Ｄ）を含む中間膜が開示されている。この中間膜では、フュームドシリカ（Ｃ）と可塑化ポリビニルアセタール（Ａ＋Ｂ）との屈折率の差が０．０１５以下であり、重量比Ｃ／（Ａ＋Ｂ）が２．７／１００～６０／１００である。
特開２００７－０７０２００号公報 ＵＳ２０１３／０２３６７１１Ａ１ ＷＯ２００８／１２２６０８Ａ１
　特許文献１～３に記載のような従来の多層の中間膜において、各層間の接着力が低いことがある。特に、隣接する２つの層にそれぞれ含まれるポリビニルアセタール樹脂の水酸基の含有率が異なると、各層間の接着力が低くなりやすい。
　本発明の目的は、各層間の接着力を高めることができる合わせガラス用中間膜を提供することである。また、本発明は、上記合わせガラス用中間膜を用いた合わせガラスを提供することも目的とする。
　本発明の広い局面によれば、ポリビニルアセタール樹脂と可塑剤とを含む第１の層と、ポリビニルアセタール樹脂と可塑剤とを含む第２の層とを備え、前記第２の層が、前記第１の層の第１の表面に積層されており、前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率と、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率とが異なり、前記第１の層がフィラーを含むか、前記第２の層がフィラーを含むか、又は、中間膜が前記第１の層と前記第２の層との界面に部分的にフィラーを含む、合わせガラス用中間膜が提供される。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記第１の層がフィラーを含むか、又は、前記第２の層がフィラーを含む。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記第１の層がフィラーを含み、前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率は、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率よりも低い。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率と、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率との差の絶対値は５モル％以上である。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記第１の層中の前記ポリビニルアセタール樹脂１００重量部に対する前記第１の層中の前記可塑剤の含有量は、前記第２の層中の前記ポリビニルアセタール樹脂１００重量部に対する前記第２の層中の前記可塑剤の含有量よりも多い。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記フィラーは表面に水酸基を有する。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記フィラーがシリカ粒子である。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記第１の層中の前記ポリビニルアセタール樹脂１００重量部に対して、前記第１の層中の前記可塑剤の含有量が５０重量部以上である。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記第１の層が前記フィラーを含む場合に、前記第１の層中の前記ポリビニルアセタール樹脂１００重量部に対して、前記第１の層中の前記フィラーの含有量が５重量部以上、６４重量部以下である。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記中間膜は、ポリビニルアセタール樹脂と可塑剤とを含む第３の層を備え、前記第３の層は、前記第１の層の前記第１の表面とは反対の第２の表面側に積層されている。
　本発明に係る合わせガラス用中間膜のある特定の局面では、合わせガラス用中間膜の厚みをＴとしたときに、前記第１の層の厚みが、０．４Ｔ以下である。
　本発明に係る合わせガラス用中間膜のある特定の局面では、ＪＩＳ　Ｒ３２０８に準拠した、厚み２ｍｍの２枚のグリーンガラスの間に合わせガラス用中間膜を挟み込むことにより合わせガラスを得たときに、得られる合わせガラスの可視光線透過率が７０％以上である。
　本発明に係る合わせガラス用中間膜のある特定の局面では、前記中間膜は、厚みが１ｍｍ以下である第１のガラス板を用いて、前記第１のガラス板と第２のガラス板との間に配置されて、合わせガラスを得るために用いられる。
　本発明の広い局面によれば、第１の合わせガラス部材と、第２の合わせガラス部材と、上述した合わせガラス用中間膜とを備え、前記第１の合わせガラス部材と前記第２の合わせガラス部材との間に、前記合わせガラス用中間膜が配置されている、合わせガラスが提供される。
　本発明に係る合わせガラスのある特定の局面では、前記第１の合わせガラス部材が第１のガラス板であり、前記第１のガラス板の厚みが１ｍｍ以下である。
　本発明に係る合わせガラス用中間膜は、ポリビニルアセタール樹脂と可塑剤とを含む第１の層と、ポリビニルアセタール樹脂と可塑剤とを含む第２の層とを備え、上記第２の層が、上記第１の層の第１の表面に積層されており、上記第１の層中の上記ポリビニルアセタール樹脂の水酸基の含有率と、上記第２の層中の上記ポリビニルアセタール樹脂の水酸基の含有率とが異なり、上記第１の層がフィラーを含むか、上記第２の層がフィラーを含むか、又は、中間膜が上記第１の層と上記第２の層との界面に部分的にフィラーを含むので、各層間の接着力を高めることができる。
図１は、本発明の第１の実施形態に係る合わせガラス用中間膜を模式的に示す断面図である。 図２は、図１に示す合わせガラス用中間膜を用いた合わせガラスの一例を模式的に示す断面図である。
　以下、本発明を詳細に説明する。
　本発明に係る合わせガラス用中間膜（本明細書において、「中間膜」と略記することがある）は、２層以上の構造を有する。本発明に係る中間膜は、２層の構造を有していてもよく、３層以上の構造を有していてもよい。本発明に係る中間膜は、ポリビニルアセタール樹脂と可塑剤とを含む第１の層を備える。本発明に係る中間膜は、ポリビニルアセタール樹脂と可塑剤とを含む第２の層を備える。本発明に係る中間膜では、上記第２の層が、上記第１の層の第１の表面側に積層されている。
　本発明に係る中間膜では、上記第１の層中の上記ポリビニルアセタール樹脂の水酸基の含有率と、上記第２の層中の上記ポリビニルアセタール樹脂の水酸基の含有率とが異なる。
　本発明に係る中間膜では、上記第１の層がフィラーを含むか、上記第２の層がフィラーを含むか、又は、中間膜が上記第１の層と上記第２の層との界面に部分的にフィラーを含む。上記第１の層がフィラーを含んでいてもよく、上記第２の層がフィラーを含んでいてもよく、中間膜が上記第１の層と上記第２の層との界面に部分的にフィラーを含んでいてもよい。
　本発明に係る中間膜では、上記の構成が備えられているので、各層間の接着力を高めることができる。さらに、各層間の剥離を抑えることができる。
　各層間の接着力を均一にかつ効果的に高める観点からは、上記第１の層がフィラーを含むか、又は上記第２の層がフィラーを含むことが好ましい。中間膜が上記第１の層と上記第２の層との界面に部分的にフィラーを含む場合に、上記第１の層と上記第２の層とが上記フィラーにより接触していない部分と、上記第１の層と上記第２の層とが直接接触している部分とが存在する。
　上記第１の層がフィラーを含み、上記第１の層中の上記ポリビニルアセタール樹脂の水酸基の含有率が、上記第２の層中の上記ポリビニルアセタール樹脂の水酸基の含有率よりも低い場合には、中間膜を用いた合わせガラスの曲げ剛性を高めることができる。また、合わせガラスを得るために、中間膜は、第１のガラス板と第２のガラス板との間に配置されることが多い。第１のガラス板の厚みが薄くても、本発明に係る中間膜の使用により、合わせガラスの曲げ剛性を充分に高くすることができる。また、第１のガラス板と第２のガラス板との双方の厚みが薄くても、本発明に係る中間膜の使用により、合わせガラスの曲げ剛性を充分に高くすることができる。なお、第１のガラス板と第２のガラス板との双方の厚みが厚いと、合わせガラスの曲げ剛性はより一層高くなる。
　さらに、上記第１の層がフィラーを含み、上記第１の層中の上記ポリビニルアセタール樹脂の水酸基の含有率が、上記第２の層中の上記ポリビニルアセタール樹脂の水酸基の含有率よりも低い場合には、中間膜を用いた合わせガラスの遮音性も高めることができる。
　上記中間膜は、３層以上の構造を有していてもよく、第１の層及び第２の層に加えて第３の層を備えていてもよい。上記中間膜は、ポリビニルアセタール樹脂と可塑剤とを含む第３の層をさらに備えることが好ましい。上記中間膜が上記第２の層及び上記第３の層を備える場合に、上記第１の層の上記第１の表面とは反対の第２の表面側に、上記第３の層が配置される。上記第３の層がフィラーを含んでいてもよく、中間膜が上記第１の層と上記第３の層との界面にフィラーを含んでいてもよい。
　上記第２の層の上記第１の層側とは反対の表面は、合わせガラス部材又はガラス板が積層される表面であることが好ましい。上記第２の層に積層されるガラス板の厚みは１ｍｍ以下であることが好ましい。上記第１の層の第１の表面（上記第２の層側の表面）とは反対の第２の表面は、合わせガラス部材又はガラス板が積層される表面であってもよい。上記第１の層に積層されるガラス板の厚みは１ｍｍ以下であることが好ましい。上記第３の層の上記第１の層側とは反対の表面は、合わせガラス部材又はガラス板が積層される表面であることが好ましい。上記第３の層に積層されるガラス板の厚みは１ｍｍ以下であることが好ましい。
　中間膜に起因して曲げ剛性を充分に高くすることができるので、上記中間膜は、厚みが１ｍｍ以下である第１のガラス板を用いて、該第１のガラス板と第２のガラス板との間に配置されて、合わせガラスを得るために好適に用いられる。中間膜に起因して曲げ剛性を充分に高くすることができるので、上記中間膜は、厚みが１ｍｍ以下である第１のガラス板と厚みが１ｍｍ以下である第２のガラス板とを用いて、上記第１のガラス板と上記第２のガラス板との間に配置されて、合わせガラスを得るためにより好適に用いられる。
　以下、図面を参照しつつ、本発明の具体的な実施形態を説明する。
　図１に、本発明の第１の実施形態に係る合わせガラス用中間膜を模式的に断面図で示す。
　図１に示す中間膜１１は、２層以上の構造を有する多層の中間膜である。中間膜１１は、合わせガラスを得るために用いられる。中間膜１１は、合わせガラス用中間膜である。中間膜１１は、第１の層１と、第２の層２と、第３の層３とを備える。第１の層１の第１の表面１ａに、第２の層２が配置されており、積層されている。第１の層１の第１の表面１ａとは反対の第２の表面１ｂに、第３の層３が配置されており、積層されている。第１の層１は中間層である。第２の層２及び第３の層３はそれぞれ、保護層であり、本実施形態では表面層である。第１の層１は、第２の層２と第３の層３との間に配置されており、挟み込まれている。従って、中間膜１１は、第２の層２と第１の層１と第３の層３とがこの順で積層された多層構造（第２の層２／第１の層１／第３の層３）を有する。
　なお、第１の層１と第３の層３との間には、他の層が配置されていてもよい。第１の層１と第３の層３とはそれぞれ、直接積層されていることが好ましい。他の層として、ポリエチレンテレフタレート等を含む層が挙げられる。
　第１の層１は、ポリビニルアセタール樹脂と可塑剤とを含む。第２の層２は、ポリビニルアセタール樹脂と可塑剤とを含む。第３の層３は、ポリビニルアセタール樹脂を含むことが好ましく、可塑剤を含むことが好ましい。
　中間膜は、中間膜における中間層又は中間膜における表面層ではない層として、第１の層を備えていてもよい。中間膜は、中間膜における表面層として、第２の層を備えることが好ましい。中間膜は、中間膜における表面層として、第３の層を備えることが好ましい。
　以下、本発明に係る中間膜を構成する上記第１の層、上記第２の層及び上記第３の層の詳細、並びに上記第１の層、上記第２の層及び上記第３の層に含まれる各成分の詳細を説明する。
　（ポリビニルアセタール樹脂又は熱可塑性樹脂）
　上記第１の層は、ポリビニルアセタール樹脂（以下、ポリビニルアセタール樹脂（１）と記載することがある）を含む。上記第２の層は、ポリビニルアセタール樹脂（以下、ポリビニルアセタール樹脂（２）と記載することがある）を含む。上記第３の層は、熱可塑性樹脂（以下、熱可塑性樹脂（３）と記載することがある）を含むことが好ましく、熱可塑性樹脂（３）として、ポリビニルアセタール樹脂（以下、ポリビニルアセタール樹脂（３）と記載することがある）を含むことが好ましい。上記ポリビニルアセタール樹脂（１）と上記ポリビニルアセタール樹脂（２）と上記ポリビニルアセタール樹脂（３）とは、同一であってもよく、異なっていてもよいが、遮音性がより一層高くなることから、上記ポリビニルアセタール樹脂（１）は、上記ポリビニルアセタール樹脂（２）及び上記ポリビニルアセタール樹脂（３）と異なっていることが好ましい。上記ポリビニルアセタール樹脂（１）、上記ポリビニルアセタール樹脂（２）及び上記ポリビニルアセタール樹脂（３）はそれぞれ、１種のみが用いられてもよく、２種以上が併用されてもよい。上記熱可塑性樹脂（３）は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記熱可塑性樹脂としては、ポリビニルアセタール樹脂、エチレン－酢酸ビニル共重合体樹脂、エチレン－アクリル酸共重合体樹脂、ポリウレタン樹脂及びポリビニルアルコール樹脂等が挙げられる。これら以外の熱可塑性樹脂を用いてもよい。
　上記ポリビニルアセタール樹脂は、例えば、ポリビニルアルコールをアルデヒドによりアセタール化することにより製造できる。上記ポリビニルアセタール樹脂は、ポリビニルアルコールのアセタール化物であることが好ましい。上記ポリビニルアルコールは、例えば、ポリ酢酸ビニルをけん化することにより得られる。上記ポリビニルアルコールのけん化度は、一般に７０～９９．９モル％である。
　上記ポリビニルアルコール（ＰＶＡ）の平均重合度は、好ましくは２００以上、より好ましくは５００以上、より一層好ましくは１５００以上、更に好ましくは１６００以上、特に好ましくは２６００以上、最も好ましくは２７００以上、好ましくは５０００以下、より好ましくは４０００以下、更に好ましくは３５００以下である。上記平均重合度が上記下限以上であると、合わせガラスの耐貫通性がより一層高くなる。上記平均重合度が上記上限以下であると、中間膜の成形が容易になる。
　上記ポリビニルアルコールの平均重合度は、ＪＩＳ　Ｋ６７２６「ポリビニルアルコール試験方法」に準拠した方法により求められる。
　上記ポリビニルアセタール樹脂におけるアセタール基の炭素数は３～５であることが好ましく、４又は５であることが好ましい。
　上記アルデヒドとして、一般には、炭素数が１～１０のアルデヒドが好適に用いられる。上記炭素数が１～１０のアルデヒドとしては、例えば、ホルムアルデヒド、アセトアルデヒド、プロピオンアルデヒド、ｎ－ブチルアルデヒド、イソブチルアルデヒド、ｎ－バレルアルデヒド、２－エチルブチルアルデヒド、ｎ－ヘキシルアルデヒド、ｎ－オクチルアルデヒド、ｎ－ノニルアルデヒド、ｎ－デシルアルデヒド、及びベンズアルデヒド等が挙げられる。なかでも、アセトアルデヒド、プロピオンアルデヒド、ｎ－ブチルアルデヒド、イソブチルアルデヒド、ｎ－ヘキシルアルデヒド又はｎ－バレルアルデヒドが好ましく、アセトアルデヒド、プロピオンアルデヒド、ｎ－ブチルアルデヒド、イソブチルアルデヒド又はｎ－バレルアルデヒドがより好ましく、ｎ－ブチルアルデヒド又はｎ－バレルアルデヒドが更に好ましい。上記アルデヒドは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記ポリビニルアセタール樹脂（１）の水酸基の含有率（水酸基量）は、好ましくは１７モル％以上、より好ましくは２０モル％以上、更に好ましくは２２モル％以上、好ましくは３０モル％以下、より好ましくは２７モル％未満、更に好ましくは２５モル％以下、特に好ましくは２４モル％以下である。上記水酸基の含有率が上記下限以上であると、中間膜の接着力がより一層高くなる。特に、上記ポリビニルアセタール樹脂（１）の水酸基の含有率が２０モル％以上であると反応効率が高く生産性に優れ、また２７モル％未満であると、合わせガラスの遮音性がより一層高くなる。また、上記水酸基の含有率が上記上限以下であると、中間膜の柔軟性が高くなり、中間膜の取扱いが容易になる。
　上記ポリビニルアセタール樹脂（１）の水酸基の含有率（水酸基量）は、好ましくは１７モル％以上、より好ましくは２０モル％以上、更に好ましくは２２モル％以上、好ましくは２８モル％以下、より好ましくは２７モル％以下、更に好ましくは２５モル％以下、特に好ましくは２４モル％以下である。上記水酸基の含有率が上記下限以上であると、中間膜の機械強度がより一層高くなる。特に、上記ポリビニルアセタール樹脂（１）の水酸基の含有率が２０モル％以上であると反応効率が高く生産性に優れ、また２８モル％以下であると、合わせガラスの遮音性がより一層高くなる。また、上記水酸基の含有率が上記上限以下であると、中間膜の柔軟性が高くなり、中間膜の取扱いが容易になる。特に、上記ポリビニルアセタール樹脂（１）の水酸基の含有率が２８モル％以下である中間膜を用いた合わせガラスは曲げ剛性が低くなる傾向にあるが、フィラーの使用により、曲げ剛性を顕著に改善できる。
　上記ポリビニルアセタール樹脂（２）及び上記ポリビニルアセタール樹脂（３）の水酸基の各含有率は、好ましくは２５モル％以上、より好ましくは２８モル％以上、より好ましくは３０モル％以上、より一層好ましくは３１．５モル％以上、更に好ましくは３２モル％以上、特に好ましくは３３モル％以上、好ましくは３８モル％以下、より好ましくは３７モル％以下、更に好ましくは３６．５モル％以下、特に好ましくは３６モル％以下である。上記水酸基の含有率が上記下限以上であると、曲げ剛性がより一層高くなり、中間膜の接着力がより一層高くなる。また、上記水酸基の含有率が上記上限以下であると、中間膜の柔軟性が高くなり、中間膜の取扱いが容易になる。
　遮音性をより一層高める観点からは、上記ポリビニルアセタール樹脂（１）の水酸基の含有率は、上記ポリビニルアセタール樹脂（２）の水酸基の含有率よりも低いことが好ましい。遮音性をより一層高める観点からは、上記ポリビニルアセタール樹脂（１）の水酸基の含有率は、上記ポリビニルアセタール樹脂（３）の水酸基の含有率よりも低いことが好ましい。遮音性を更に一層高める観点からは、上記ポリビニルアセタール樹脂（１）の水酸基の含有率と、上記ポリビニルアセタール樹脂（２）の水酸基の含有率との差の絶対値は、及び上記ポリビニルアセタール樹脂（１）の水酸基の含有率と、上記ポリビニルアセタール樹脂（３）の水酸基の含有率との差の絶対値は、好ましくは１モル％以上、より好ましくは５モル％以上、更に好ましくは９モル％以上、特に好ましくは１０モル％以上、最も好ましくは１２モル％以上である。上記ポリビニルアセタール樹脂（１）の水酸基の含有率と、上記ポリビニルアセタール樹脂（２）の水酸基の含有率との差の絶対値は、及び上記ポリビニルアセタール樹脂（１）の水酸基の含有率と、上記ポリビニルアセタール樹脂（３）の水酸基の含有率との差の絶対値は、好ましくは２０モル％以下である。シリカ粒子などのフィラーを用いると、シリカ粒子などのフィラーを用いていない場合と比べて、フィラーの影響で遮音性が低くなる傾向があるが、このような水酸基の含有率の関係を満足することで、遮音性を効果的に高めることができる。
　上記ポリビニルアセタール樹脂の水酸基の含有率は、水酸基が結合しているエチレン基量を、主鎖の全エチレン基量で除算して求めたモル分率を百分率で示した値である。上記水酸基が結合しているエチレン基量は、例えば、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠して測定できる。
　上記ポリビニルアセタール樹脂（１）のアセチル化度（アセチル基量）は、好ましくは０．０１モル％以上、より好ましくは０．１モル％以上、より一層好ましくは７モル％以上、更に好ましくは９モル％以上、好ましくは３０モル％以下、より好ましくは２５モル％以下、更に好ましくは２４モル％以下、特に好ましくは２０モル％以下である。上記アセチル化度が上記下限以上であると、ポリビニルアセタール樹脂と可塑剤との相溶性が高くなる。上記アセチル化度が上記上限以下であると、中間膜及び合わせガラスの耐湿性が高くなる。特に、上記ポリビニルアセタール樹脂（１）のアセチル化度が０．１モル％以上、２５モル％以下であると、耐貫通性に優れる。
　上記ポリビニルアセタール樹脂（２）及び上記ポリビニルアセタール樹脂（３）の各アセチル化度は、好ましくは０．０１モル％以上、より好ましくは０．５モル％以上、好ましくは１０モル％以下、より好ましくは２モル％以下である。上記アセチル化度が上記下限以上であると、ポリビニルアセタール樹脂と可塑剤との相溶性が高くなる。上記アセチル化度が上記上限以下であると、中間膜及び合わせガラスの耐湿性が高くなる。
　上記アセチル化度は、アセチル基が結合しているエチレン基量を、主鎖の全エチレン基量で除算して求めたモル分率を百分率で示した値である。上記アセチル基が結合しているエチレン基量は、例えば、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠して測定できる。
　上記ポリビニルアセタール樹脂（１）のアセタール化度（ポリビニルブチラール樹脂の場合にはブチラール化度）は、好ましくは４７モル％以上、より好ましくは６０モル％以上、好ましくは８５モル％以下、より好ましくは８０モル％以下、更に好ましくは７５モル％以下である。上記アセタール化度が上記下限以上であると、ポリビニルアセタール樹脂と可塑剤との相溶性が高くなる。上記アセタール化度が上記上限以下であると、ポリビニルアセタール樹脂を製造するために必要な反応時間が短くなる。
　上記ポリビニルアセタール樹脂（２）及び上記ポリビニルアセタール樹脂（３）の各アセタール化度（ポリビニルブチラール樹脂の場合にはブチラール化度）は、好ましくは５５モル％以上、より好ましくは６０モル％以上、好ましくは７５モル％以下、より好ましくは７１モル％以下である。上記アセタール化度が上記下限以上であると、ポリビニルアセタール樹脂と可塑剤との相溶性が高くなる。上記アセタール化度が上記上限以下であると、ポリビニルアセタール樹脂を製造するために必要な反応時間が短くなる。
　上記アセタール化度は、主鎖の全エチレン基量から、水酸基が結合しているエチレン基量と、アセチル基が結合しているエチレン基量とを差し引いた値を、主鎖の全エチレン基量で除算して求めたモル分率を百分率で示した値である。
　なお、上記水酸基の含有率（水酸基量）、アセタール化度（ブチラール化度）及びアセチル化度は、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法により測定された結果から算出することが好ましい。但し、ＡＳＴＭ　Ｄ１３９６－９２による測定を用いてもよい。ポリビニルアセタール樹脂がポリビニルブチラール樹脂である場合は、上記水酸基の含有率（水酸基量）、上記アセタール化度（ブチラール化度）及び上記アセチル化度は、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法により測定された結果から算出され得る。
　合わせガラスの耐貫通性をより一層良好にする観点からは、上記ポリビニルアセタール樹脂（１）は、アセチル化度（ａ）が８モル％未満であり、かつアセタール化度（ａ）が６５モル％以上であるポリビニルアセタール樹脂（Ａ）であるか、又はアセチル化度（ｂ）が８モル％以上であるポリビニルアセタール樹脂（Ｂ）であることが好ましい。上記ポリビニルアセタール樹脂（２）及び上記ポリビニルアセタール樹脂（３）は、上記ポリビニルアセタール樹脂（Ａ）であってもよく、上記ポリビニルアセタール樹脂（Ｂ）であってもよい。
　上記ポリビニルアセタール樹脂（Ａ）のアセチル化度（ａ）は８モル％未満、好ましくは７．９モル％以下、より好ましくは７．８モル％以下、更に好ましくは６．５モル％以下、特に好ましくは６モル％以下、好ましくは０．１モル％以上、より好ましくは０．５モル％以上、更に好ましくは２モル％以上、特に好ましくは５モル％以上、最も好ましくは５．５モル％以上である。上記アセチル化度（ａ）が０．１モル％以上、８モル％未満であると、可塑剤の移行を容易に制御でき、合わせガラスの遮音性がより一層高くなる。
　上記ポリビニルアセタール樹脂（Ａ）のアセタール化度（ａ）は６５モル％以上、好ましくは６６モル％以上、より好ましくは６７モル％以上、更に好ましくは６７．５モル％以上、特に好ましくは７５モル％以上、好ましくは８５モル％以下、より好ましくは８４モル％以下、更に好ましくは８３モル％以下、特に好ましくは８２モル％以下である。上記アセタール化度（ａ）が上記下限以上であると、合わせガラスの遮音性がより一層高くなる。上記アセタール化度（ａ）が上記上限以下であると、ポリビニルアセタール樹脂（Ａ）を製造するために必要な反応時間を短縮できる。
　上記ポリビニルアセタール樹脂（Ａ）の水酸基の含有率（ａ）は好ましくは１８モル％以上、より好ましくは１９モル％以上、更に好ましくは２０モル％以上、特に好ましくは２１モル％以上、最も好ましくは２３モル％以上、好ましくは３１モル％以下、より好ましくは３０モル％以下、更に好ましくは２９モル％以下、特に好ましくは２８モル％以下である。上記水酸基の含有率（ａ）が上記下限以上であると、上記第２の層の接着力がより一層高くなる。上記水酸基の含有率（ａ）が上記上限以下であると、合わせガラスの遮音性がより一層高くなる。
　上記ポリビニルアセタール樹脂（Ｂ）のアセチル化度（ｂ）は、８モル％以上、好ましくは９モル％以上、より好ましくは９．５モル％以上、更に好ましくは１０モル％以上、特に好ましくは１０．５モル％以上、好ましくは３０モル％以下、より好ましくは２８モル％以下、更に好ましくは２６モル％以下、特に好ましくは２４モル％以下である。上記アセチル化度（ｂ）が上記下限以上であると、合わせガラスの遮音性がより一層高くなる。上記アセチル化度（ｂ）が上記上限以下であると、ポリビニルアセタール樹脂（Ｂ）を製造するために必要な反応時間を短縮できる。
　上記ポリビニルアセタール樹脂（Ｂ）のアセタール化度（ｂ）は好ましくは５０モル％以上、より好ましくは５３モル％以上、更に好ましくは５５モル％以上、特に好ましくは６０モル％以上、好ましくは７８モル％以下、より好ましくは７５モル％以下、更に好ましくは７２モル％以下、特に好ましくは７０モル％以下である。上記アセタール化度（ｂ）が上記下限以上であると、合わせガラスの遮音性がより一層高くなる。上記アセタール化度（ｂ）が上記上限以下であると、ポリビニルアセタール樹脂（Ｂ）を製造するために必要な反応時間を短縮できる。
　上記ポリビニルアセタール樹脂（Ｂ）の水酸基の含有率（ｂ）は好ましくは１８モル％以上、より好ましくは１９モル％以上、更に好ましくは２０モル％以上、特に好ましくは２１モル％以上、最も好ましくは２３モル％以上、好ましくは３１モル％以下、より好ましくは３０モル％以下、更に好ましくは２９モル％以下、特に好ましくは２８モル％以下である。上記水酸基の含有率（ｂ）が上記下限以上であると、上記第２の層の接着力がより一層高くなる。上記水酸基の含有率（ｂ）が上記上限以下であると、合わせガラスの遮音性がより一層高くなる。
　上記ポリビニルアセタール樹脂（Ａ）及び上記ポリビニルアセタール樹脂（Ｂ）はそれぞれ、ポリビニルブチラール樹脂であることが好ましい。
　（可塑剤）
　上記第１の層（単層の中間膜を含む）は、可塑剤（以下、可塑剤（１）と記載することがある）を含む。上記第２の層は、可塑剤（以下、可塑剤（２）と記載することがある）を含む。上記第３の層は、可塑剤（以下、可塑剤（３）と記載することがある）を含むことが好ましい。ポリビニルアセタール樹脂と可塑剤との併用により、ポリビニルアセタール樹脂と可塑剤とを含む層の合わせガラス部材又は他の層に対する接着力が適度に高くなる。上記可塑剤は特に限定されない。上記可塑剤（１）と上記可塑剤（２）と上記可塑剤（３）とは同一であってもよく、異なっていてもよい。上記可塑剤（１）、上記可塑剤（２）及び上記可塑剤（３）はそれぞれ、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記可塑剤としては、一塩基性有機酸エステル及び多塩基性有機酸エステル等の有機エステル可塑剤、並びに有機リン酸可塑剤及び有機亜リン酸可塑剤などの有機リン酸可塑剤等が挙げられる。なかでも、有機エステル可塑剤が好ましい。上記可塑剤は液状可塑剤であることが好ましい。
　上記一塩基性有機酸エステルとしては、グリコールと一塩基性有機酸との反応によって得られたグリコールエステル等が挙げられる。上記グリコールとしては、トリエチレングリコール、テトラエチレングリコール及びトリプロピレングリコール等が挙げられる。上記一塩基性有機酸としては、酪酸、イソ酪酸、カプロン酸、２－エチル酪酸、ヘプチル酸、ｎ－オクチル酸、２－エチルヘキシル酸、ｎ－ノニル酸及びデシル酸等が挙げられる。
　上記多塩基性有機酸エステルとしては、多塩基性有機酸と、炭素数４～８の直鎖又は分岐構造を有するアルコールとのエステル化合物等が挙げられる。上記多塩基性有機酸としては、アジピン酸、セバシン酸及びアゼライン酸等が挙げられる。
　上記有機エステル可塑剤としては、トリエチレングリコールジ－２－エチルプロパノエート、トリエチレングリコールジ－２－エチルブチレート、トリエチレングリコールジ－２－エチルヘキサノエート、トリエチレングリコールジカプリレート、トリエチレングリコールジ－ｎ－オクタノエート、トリエチレングリコールジ－ｎ－ヘプタノエート、テトラエチレングリコールジ－ｎ－ヘプタノエート、ジブチルセバケート、ジオクチルアゼレート、ジブチルカルビトールアジペート、エチレングリコールジ－２－エチルブチレート、１，３－プロピレングリコールジ－２－エチルブチレート、１，４－ブチレングリコールジ－２－エチルブチレート、ジエチレングリコールジ－２－エチルブチレート、ジエチレングリコールジ－２－エチルヘキサノエート、ジプロピレングリコールジ－２－エチルブチレート、トリエチレングリコールジ－２－エチルペンタノエート、テトラエチレングリコールジ－２－エチルブチレート、ジエチレングリコールジカプリレート、アジピン酸ジヘキシル、アジピン酸ジオクチル、アジピン酸ヘキシルシクロヘキシル、アジピン酸ヘプチルとアジピン酸ノニルとの混合物、アジピン酸ジイソノニル、アジピン酸ジイソデシル、アジピン酸ヘプチルノニル、セバシン酸ジブチル、油変性セバシン酸アルキド、及びリン酸エステルとアジピン酸エステルとの混合物等が挙げられる。これら以外の有機エステル可塑剤を用いてもよい。上述のアジピン酸エステル以外の他のアジピン酸エステルを用いてもよい。
　上記有機リン酸可塑剤としては、トリブトキシエチルホスフェート、イソデシルフェニルホスフェート及びトリイソプロピルホスフェート等が挙げられる。
　上記可塑剤は、下記式（１）で表されるジエステル可塑剤であることが好ましい。
Figure JPOXMLDOC01-appb-C000001
　上記式（１）中、Ｒ１及びＲ２はそれぞれ、炭素数２～１０の有機基を表し、Ｒ３は、エチレン基、イソプロピレン基又はｎ－プロピレン基を表し、ｐは３～１０の整数を表す。上記式（１）中のＲ１及びＲ２はそれぞれ、炭素数５～１０の有機基であることが好ましく、炭素数６～１０の有機基であることがより好ましい。
　上記可塑剤は、ジ－（２－ブトキシエチル）－アジペート（ＤＢＥＡ）、トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）、トリエチレングリコールジ－２－エチルブチレート（３ＧＨ）又はトリエチレングリコールジ－２－エチルプロパノエートを含むことが好ましく、トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）、トリエチレングリコールジ－２－エチルブチレート（３ＧＨ）又はトリエチレングリコールジ－２－エチルプロパノエートを含むことがより好ましく、トリエチレングリコールジ－２－エチルヘキサノエート又はトリエチレングリコールジ－２－エチルブチレートを含むことが更に好ましく、トリエチレングリコールジ－２－エチルヘキサノエートを含むことが特に好ましい。
　上記ポリビニルアセタール樹脂（２）１００重量部に対する上記可塑剤（２）の含有量（以下、含有量（２）と記載することがある）、並びに上記熱可塑性樹脂（３）１００重量部に対する上記可塑剤（３）の含有量（以下、含有量（３）と記載することがある）はそれぞれ、好ましくは１０重量部以上、より好ましくは１５重量部以上、更に好ましくは２０重量部以上、特に好ましくは２４重量部以上、好ましくは４０重量部以下、より好ましくは３５重量部以下、更に好ましくは３２重量部以下、特に好ましくは３０重量部以下である。上記含有量（２）及び上記含有量（３）が上記下限以上であると、中間膜の柔軟性が高くなり、中間膜の取扱いが容易になる。上記含有量（２）及び上記含有量（３）が上記上限以下であると、曲げ剛性がより一層高くなる。
　上記ポリビニルアセタール樹脂（１）１００重量部に対する上記可塑剤（１）の含有量（以下、含有量（１）と記載することがある）は、好ましくは５０重量部以上、より好ましくは５５重量部以上、更に好ましくは６０重量部以上好ましくは１００重量部以下、より好ましくは９０重量部以下、更に好ましくは８５重量部以下、特に好ましくは８０重量部以下である。上記含有量（１）が上記下限以上であると、中間膜の柔軟性が高くなり、中間膜の取扱いが容易になる。上記含有量（１）が上記上限以下であると、合わせガラスの耐貫通性がより一層高くなる。
　合わせガラスの遮音性を高めるために、上記含有量（１）は上記含有量（２）よりも多いことが好ましく、上記含有量（１）は上記含有量（３）よりも多いことが好ましい。特に、上記含有量（１）が５５重量部以上である中間膜を用いた合わせガラスは曲げ剛性が低くなる傾向にあるが、フィラーの使用により、曲げ剛性を顕著に改善できる。
　合わせガラスの遮音性をより一層高める観点からは、上記含有量（２）と上記含有量（１）との差の絶対値、並びに上記含有量（３）と上記含有量（１）との差の絶対値はそれぞれ、好ましくは１０重量部以上、より好ましくは１５重量部以上、更に好ましくは２０重量部以上である。上記含有量（２）と上記含有量（１）との差の絶対値、並びに上記含有量（３）と上記含有量（１）との差の絶対値はそれぞれ、好ましくは８０重量部以下、より好ましくは７５重量部以下、更に好ましくは７０重量部以下である。
　（フィラー）
　中間膜は、フィラーを含む。フィラーは、第１の層中、第２の層中、又は第１の層と第２の層との界面に存在する。フィラーの使用により、各層間の接着力が高くなり、更に遮音性を低下させず、曲げ剛性も高くなる。上記フィラーは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記フィラーとしては、炭酸カルシウム粒子及びシリカ粒子等が挙げられる。
　各層間の接着力をより一層高める観点からは、フィラーは表面に水酸基を有することが好ましい。各層間の接着力をより一層高める観点からは、フィラーはシリカ粒子であることが好ましい。
　上記シリカ粒子のＢＥＴ法による比表面積は好ましくは５０ｍ２／ｇ以上、より好ましくは１００ｍ２／ｇ以上、更に好ましくは２００ｍ２／ｇ以上、特に好ましくは２５０ｍ２／ｇ以上、最も好ましくは３００ｍ２／ｇ以上、好ましくは５００ｍ２／ｇ以下である。上記比表面積は、比表面積／細孔分布測定装置を用いてガス吸着法により測定できる。上記測定装置としては、例えば島津製作所社製「アサップ２４２０」等が挙げられる。
　ポリビニルアセタール樹脂又は熱可塑性樹脂とフィラーとを含む層において、上記ポリビニルアセタール樹脂又は上記熱可塑性樹脂１００重量部に対して、上記フィラーの含有量は、好ましくは１重量部以上、より好ましくは５重量部以上、更に好ましくは１０重量部以上、特に好ましくは１５重量部以上、好ましくは７０重量部以下、より好ましくは６４重量部以下、より一層好ましくは６０重量部以下、更に好ましくは５５重量部以下、特に好ましくは４５重量部以下、最も好ましくは３５重量部以下である。上記ポリビニルアセタール樹脂（１）１００重量部に対して、上記フィラーの含有量は、好ましくは１重量部以上、より好ましくは５重量部以上、更に好ましくは１０重量部以上、特に好ましくは１５重量部以上、好ましくは７０重量部以下、より好ましくは６４重量部以下、より一層好ましくは６０重量部以下、更に好ましくは５５重量部以下、特に好ましくは４５重量部以下、最も好ましくは３５重量部以下である。上記シリカ粒子の含有量が上記下限以上及び上記上限以下であることが好ましい。上記フィラーの含有量が上記下限以上であると、各層間の接着力がより一層高くなり、曲げ剛性がより一層高くなる。上記フィラーの含有量が上記上限以下であると、遮音性がより一層高くなる。
　（遮熱性化合物）
　上記中間膜は、遮熱性化合物を含むことが好ましい。上記第１の層は、遮熱性化合物を含むことが好ましい。上記第２の層は、遮熱性化合物を含むことが好ましい。上記第３の層は、遮熱性化合物を含むことが好ましい。上記遮熱性化合物は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　成分Ｘ：
　上記中間膜は、フタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物の内の少なくとも１種の成分Ｘを含むことが好ましい。上記第１の層は、上記成分Ｘを含むことが好ましい。上記第２の層は、上記成分Ｘを含むことが好ましい。上記第３の層は、上記成分Ｘを含むことが好ましい。上記成分Ｘは遮熱性化合物である。上記成分Ｘは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記成分Ｘは特に限定されない。成分Ｘとして、従来公知のフタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物を用いることができる。
　中間膜及び合わせガラスの遮熱性をより一層高くする観点からは、上記成分Ｘは、フタロシアニン、フタロシアニンの誘導体、ナフタロシアニン及びナフタロシアニンの誘導体からなる群から選択される少なくとも１種であることが好ましく、フタロシアニン及びフタロシアニンの誘導体の内の少なくとも１種であることがより好ましい。
　遮熱性を効果的に高め、かつ長期間にわたり可視光線透過率をより一層高いレベルで維持する観点からは、上記成分Ｘは、バナジウム原子又は銅原子を含有することが好ましい。上記成分Ｘは、バナジウム原子を含有することが好ましく、銅原子を含有することも好ましい。上記成分Ｘは、バナジウム原子又は銅原子を含有するフタロシアニン及びバナジウム原子又は銅原子を含有するフタロシアニンの誘導体の内の少なくとも１種であることがより好ましい。中間膜及び合わせガラスの遮熱性を更に一層高くする観点からは、上記成分Ｘは、バナジウム原子に酸素原子が結合した構造単位を有することが好ましい。
　上記成分Ｘを含む層（第１の層、第２の層又は第３の層）１００重量％中、上記成分Ｘの含有量は、好ましくは０．００１重量％以上、より好ましくは０．００５重量％以上、更に好ましくは０．０１重量％以上、特に好ましくは０．０２重量％以上、好ましくは０．２重量％以下、より好ましくは０．１重量％以下、更に好ましくは０．０５重量％以下、特に好ましくは０．０４重量％以下である。上記成分Ｘの含有量が上記下限以上及び上記上限以下であると、遮熱性が充分に高くなり、かつ可視光線透過率が充分に高くなる。例えば、可視光線透過率を７０％以上にすることが可能である。
　遮熱粒子：
　上記中間膜は、遮熱粒子を含むことが好ましい。上記第１の層は、上記遮熱粒子を含むことが好ましい。上記第２の層は、上記遮熱粒子を含むことが好ましい。上記第３の層は、上記遮熱粒子を含むことが好ましい。上記遮熱粒子は遮熱性化合物である。遮熱粒子の使用により、赤外線（熱線）を効果的に遮断できる。上記遮熱粒子は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　合わせガラスの遮熱性をより一層高める観点からは、上記遮熱粒子は、金属酸化物粒子であることがより好ましい。上記遮熱粒子は、金属の酸化物により形成された粒子（金属酸化物粒子）であることが好ましい。
　可視光よりも長い波長７８０ｎｍ以上の赤外線は、紫外線と比較して、エネルギー量が小さい。しかしながら、赤外線は熱的作用が大きく、赤外線が物質に吸収されると熱として放出される。このため、赤外線は一般に熱線と呼ばれている。上記遮熱粒子の使用により、赤外線（熱線）を効果的に遮断できる。なお、遮熱粒子とは、赤外線を吸収可能な粒子を意味する。
　上記遮熱粒子の具体例としては、アルミニウムドープ酸化錫粒子、インジウムドープ酸化錫粒子、アンチモンドープ酸化錫粒子（ＡＴＯ粒子）、ガリウムドープ酸化亜鉛粒子（ＧＺＯ粒子）、インジウムドープ酸化亜鉛粒子（ＩＺＯ粒子）、アルミニウムドープ酸化亜鉛粒子（ＡＺＯ粒子）、ニオブドープ酸化チタン粒子、ナトリウムドープ酸化タングステン粒子、セシウムドープ酸化タングステン粒子、タリウムドープ酸化タングステン粒子、ルビジウムドープ酸化タングステン粒子、錫ドープ酸化インジウム粒子（ＩＴＯ粒子）、錫ドープ酸化亜鉛粒子、珪素ドープ酸化亜鉛粒子等の金属酸化物粒子や、六ホウ化ランタン（ＬａＢ６）粒子等が挙げられる。これら以外の遮熱粒子を用いてもよい。なかでも、熱線の遮蔽機能が高いため、金属酸化物粒子が好ましく、ＡＴＯ粒子、ＧＺＯ粒子、ＩＺＯ粒子、ＩＴＯ粒子又は酸化タングステン粒子がより好ましく、ＩＴＯ粒子又は酸化タングステン粒子が特に好ましい。特に、熱線の遮蔽機能が高く、かつ入手が容易であるので、錫ドープ酸化インジウム粒子（ＩＴＯ粒子）が好ましく、酸化タングステン粒子も好ましい。
　中間膜及び合わせガラスの遮熱性をより一層高くする観点からは、酸化タングステン粒子は、金属ドープ酸化タングステン粒子であることが好ましい。上記「酸化タングステン粒子」には、金属ドープ酸化タングステン粒子が含まれる。上記金属ドープ酸化タングステン粒子としては、具体的には、ナトリウムドープ酸化タングステン粒子、セシウムドープ酸化タングステン粒子、タリウムドープ酸化タングステン粒子及びルビジウムドープ酸化タングステン粒子等が挙げられる。
　中間膜及び合わせガラスの遮熱性をより一層高くする観点からは、セシウムドープ酸化タングステン粒子が特に好ましい。中間膜及び合わせガラスの遮熱性を更に一層高くする観点からは、該セシウムドープ酸化タングステン粒子は、式：Ｃｓ０．３３ＷＯ３で表される酸化タングステン粒子であることが好ましい。
　上記遮熱粒子の平均粒子径は好ましくは０．０１μｍ以上、より好ましくは０．０２μｍ以上、好ましくは０．１μｍ以下、より好ましくは０．０５μｍ以下である。平均粒子径が上記下限以上であると、熱線の遮蔽性が充分に高くなる。平均粒子径が上記上限以下であると、遮熱粒子の分散性が高くなる。
　上記「平均粒子径」は、体積平均粒子径を示す。平均粒子径は、粒度分布測定装置（日機装社製「ＵＰＡ－ＥＸ１５０」）等を用いて測定できる。
　上記遮熱粒子を含む層（第１の層、第２の層又は第３の層）１００重量％中、上記遮熱粒子の含有量は、好ましくは０．０１重量％以上、より好ましくは０．１重量％以上、更に好ましくは１重量％以上、特に好ましくは１．５重量％以上、好ましくは６重量％以下、より好ましくは５．５重量％以下、更に好ましくは４重量％以下、特に好ましくは３．５重量％以下、最も好ましくは３重量％以下である。上記遮熱粒子の含有量が上記下限以上及び上記上限以下であると、遮熱性が充分に高くなり、かつ可視光線透過率が充分に高くなる。
　（金属塩）
　上記中間膜は、アルカリ金属塩及びアルカリ土類金属塩の内の少なくとも１種の金属塩（以下、金属塩Ｍと記載することがある）を含むことが好ましい。上記第１の層は、上記金属塩Ｍを含むことが好ましい。上記第２の層は、上記金属塩Ｍを含むことが好ましい。上記第３の層は、上記金属塩Ｍを含むことが好ましい。上記金属塩Ｍの使用により、中間膜と合わせガラス部材との接着性又は中間膜における各層間の接着性を制御することが容易になる。上記金属塩Ｍは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記金属塩Ｍは、Ｌｉ、Ｎａ、Ｋ、Ｒｂ、Ｃｓ、Ｍｇ、Ｃａ、Ｓｒ及びＢａからなる群から選択された少なくとも１種の金属を含むことが好ましい。中間膜中に含まれている金属塩は、Ｋ及びＭｇの内の少なくとも１種の金属を含むことが好ましい。
　また、上記金属塩Ｍは、炭素数２～１６の有機酸のアルカリ金属塩又は炭素数２～１６の有機酸のアルカリ土類金属塩であることがより好ましく、炭素数２～１６のカルボン酸マグネシウム塩又は炭素数２～１６のカルボン酸カリウム塩であることが更に好ましい。
　上記炭素数２～１６のカルボン酸マグネシウム塩及び上記炭素数２～１６のカルボン酸カリウム塩としては特に限定されないが、例えば、酢酸マグネシウム、酢酸カリウム、プロピオン酸マグネシウム、プロピオン酸カリウム、２－エチル酪酸マグネシウム、２－エチルブタン酸カリウム、２－エチルヘキサン酸マグネシウム及び２－エチルヘキサン酸カリウム等が挙げられる。
　上記金属塩Ｍを含む層（第１の層、第２の層又は第３の層）におけるＭｇ及びＫの含有量の合計は、好ましくは５ｐｐｍ以上、より好ましくは１０ｐｐｍ以上、更に好ましくは２０ｐｐｍ以上、好ましくは３００ｐｐｍ以下、より好ましくは２５０ｐｐｍ以下、更に好ましくは２００ｐｐｍ以下である。Ｍｇ及びＫの含有量の合計が上記下限以上及び上記上限以下であると、中間膜と合わせガラス部材との接着性又は中間膜における各層間の接着性をより一層良好に制御できる。
　（紫外線遮蔽剤）
　上記中間膜は、紫外線遮蔽剤を含むことが好ましい。上記第１の層は、紫外線遮蔽剤を含むことが好ましい。上記第２の層は、紫外線遮蔽剤を含むことが好ましい。上記第３の層は、紫外線遮蔽剤を含むことが好ましい。紫外線遮蔽剤の使用により、中間膜及び合わせガラスが長期間使用されても、可視光線透過率がより一層低下し難くなる。上記紫外線遮蔽剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記紫外線遮蔽剤には、紫外線吸収剤が含まれる。上記紫外線遮蔽剤は、紫外線吸収剤であることが好ましい。
　上記紫外線遮蔽剤としては、例えば、金属原子を含む紫外線遮蔽剤、金属酸化物を含む紫外線遮蔽剤、ベンゾトリアゾール構造を有する紫外線遮蔽剤、ベンゾフェノン構造を有する紫外線遮蔽剤、トリアジン構造を有する紫外線遮蔽剤、マロン酸エステル構造を有する紫外線遮蔽剤、シュウ酸アニリド構造を有する紫外線遮蔽剤及びベンゾエート構造を有する紫外線遮蔽剤等が挙げられる。
　上記金属原子を含む紫外線吸収剤としては、例えば、白金粒子、白金粒子の表面をシリカで被覆した粒子、パラジウム粒子及びパラジウム粒子の表面をシリカで被覆した粒子等が挙げられる。紫外線遮蔽剤は、遮熱粒子ではないことが好ましい。
　上記紫外線遮蔽剤は、好ましくはベンゾトリアゾール構造を有する紫外線遮蔽剤、ベンゾフェノン構造を有する紫外線遮蔽剤、トリアジン構造を有する紫外線遮蔽剤又はベンゾエート構造を有する紫外線遮蔽剤であり、より好ましくはベンゾトリアゾール構造を有する紫外線遮蔽剤又はベンゾフェノン構造を有する紫外線遮蔽剤であり、更に好ましくはベンゾトリアゾール構造を有する紫外線吸収剤である。
　上記金属酸化物を含む紫外線吸収剤としては、例えば、酸化亜鉛、酸化チタン及び酸化セリウム等が挙げられる。さらに、上記金属酸化物を含む紫外線吸収剤に関して、表面が被覆されていてもよい。上記金属酸化物を含む紫外線吸収剤の表面の被覆材料としては、絶縁性金属酸化物、加水分解性有機ケイ素化合物及びシリコーン化合物等が挙げられる。
　上記ベンゾトリアゾール構造を有する紫外線吸収剤としては、例えば、２－（２’－ヒドロキシ－５’－メチルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「ＴｉｎｕｖｉｎＰ」）、２－（２’－ヒドロキシ－３’，５’－ジ－ｔ－ブチルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２０」）、２－（２’－ヒドロキシ－３’－ｔ－ブチル－５－メチルフェニル）－５－クロロベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２６」）、及び２－（２’－ヒドロキシ－３’，５’－ジ－アミルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２８」）等のベンゾトリアゾール構造を有する紫外線吸収剤が挙げられる。紫外線を吸収する性能に優れることから、上記紫外線遮蔽剤は、ハロゲン原子を含むベンゾトリアゾール構造を有する紫外線吸収剤であることが好ましく、塩素原子を含むベンゾトリアゾール構造を有する紫外線吸収剤であることがより好ましい。
　上記ベンゾフェノン構造を有する紫外線吸収剤としては、例えば、オクタベンゾン（ＢＡＳＦ社製「Ｃｈｉｍａｓｓｏｒｂ８１」）等が挙げられる。
　上記トリアジン構造を有する紫外線吸収剤としては、例えば、ＡＤＥＫＡ社製「ＬＡ－Ｆ７０」及び２－（４，６－ジフェニル－１，３，５－トリアジン－２－イル）－５－［（ヘキシル）オキシ］－フェノール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ１５７７ＦＦ」）等が挙げられる。
　上記マロン酸エステル構造を有する紫外線遮蔽剤としては、２－（ｐ－メトキシベンジリデン）マロン酸ジメチル、テトラエチル－２，２－（１，４－フェニレンジメチリデン）ビスマロネート、２－（ｐ－メトキシベンジリデン）－ビス（１，２，２，６，６－ペンタメチル４－ピペリジニル）マロネート等が挙げられる。
　上記マロン酸エステル構造を有する紫外線遮蔽剤の市販品としては、Ｈｏｓｔａｖｉｎ　Ｂ－ＣＡＰ、Ｈｏｓｔａｖｉｎ　ＰＲ－２５、Ｈｏｓｔａｖｉｎ　ＰＲ－３１（いずれもクラリアント社製）が挙げられる。
　上記シュウ酸アニリド構造を有する紫外線遮蔽剤としては、Ｎ－（２－エチルフェニル）－Ｎ’－（２－エトキシ－５－ｔ－ブチルフェニル）シュウ酸ジアミド、Ｎ－（２－エチルフェニル）－Ｎ’－（２－エトキシ－フェニル）シュウ酸ジアミド、２－エチル－２’－エトキシ－オキシアニリド（クラリアント社製「ＳａｎｄｕｖｏｒＶＳＵ」）などの窒素原子上に置換されたアリール基などを有するシュウ酸ジアミド類が挙げられる。
　上記ベンゾエート構造を有する紫外線吸収剤としては、例えば、２，４－ジ－ｔｅｒｔ－ブチルフェニル－３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシベンゾエート（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ１２０」）等が挙げられる。
　期間経過後の可視光線透過率の低下をより一層抑制する観点からは、上記紫外線遮蔽剤を含む層（第１の層、第２の層又は第３の層）１００重量％中、上記紫外線遮蔽剤の含有量は、好ましくは０．１重量％以上、より好ましくは０．２重量％以上、更に好ましくは０．３重量％以上、特に好ましくは０．５重量％以上、好ましくは２．５重量％以下、より好ましくは２重量％以下、更に好ましくは１重量％以下、特に好ましくは０．８重量％以下である。特に、上記紫外線遮蔽剤を含む層１００重量％中、上記紫外線遮蔽剤の含有量が０．２重量％以上であることにより、中間膜及び合わせガラスの期間経過後の可視光線透過率の低下を顕著に抑制できる。
　（酸化防止剤）
　上記中間膜は、酸化防止剤を含むことが好ましい。上記第１の層は、酸化防止剤を含むことが好ましい。上記第２の層は、酸化防止剤を含むことが好ましい。上記第３の層は、酸化防止剤を含むことが好ましい。上記酸化防止剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記酸化防止剤としては、フェノール系酸化防止剤、硫黄系酸化防止剤及びリン系酸化防止剤等が挙げられる。上記フェノール系酸化防止剤はフェノール骨格を有する酸化防止剤である。上記硫黄系酸化防止剤は硫黄原子を含有する酸化防止剤である。上記リン系酸化防止剤はリン原子を含有する酸化防止剤である。
　上記酸化防止剤は、フェノール系酸化防止剤又はリン系酸化防止剤であることが好ましい。
　上記フェノール系酸化防止剤としては、２，６－ジ－ｔ－ブチル－ｐ－クレゾール（ＢＨＴ）、ブチル化ヒドロキシアニソール（ＢＨＡ）、２，６－ジ－ｔ－ブチル－４－エチルフェノール、ステアリル－β－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート、２，２’－メチレンビス－（４－メチル－６－ブチルフェノール）、２，２’－メチレンビス－（４－エチル－６－ｔ－ブチルフェノール）、４，４’－ブチリデン－ビス－（３－メチル－６－ｔ－ブチルフェノール）、１，１，３－トリス－（２－メチル－ヒドロキシ－５－ｔ－ブチルフェニル）ブタン、テトラキス［メチレン－３－（３’，５’－ブチル－４－ヒドロキシフェニル）プロピオネート］メタン、１，３，３－トリス－（２－メチル－４－ヒドロキシ－５－ｔ－ブチルフェノール）ブタン、１，３，５－トリメチル－２，４，６－トリス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）ベンゼン、ビス（３，３’－ｔ－ブチルフェノール）ブチリックアッシドグリコールエステル及びビス（３－ｔ－ブチル－４－ヒドロキシ－５－メチルベンゼンプロパン酸）エチレンビス（オキシエチレン）等が挙げられる。これらの酸化防止剤の内の１種又は２種以上が好適に用いられる。
　上記リン系酸化防止剤としては、トリデシルホスファイト、トリス（トリデシル）ホスファイト、トリフェニルホスファイト、トリノニルフェニルホスファイト、ビス（トリデシル）ペンタエリスリトールジホスファイト、ビス（デシル）ペンタエリスリトールジホスファイト、トリス（２，４－ジ－ｔ－ブチルフェニル）ホスファイト、ビス（２，４－ジ－ｔ－ブチル－６－メチルフェニル）エチルエステル亜リン酸、トリス（２，４－ジ－ｔ－ブチルフェニル）ホスファイト、及び２，２’－メチレンビス（４，６－ジ－ｔ－ブチル－１－フェニルオキシ）（２－エチルヘキシルオキシ）ホスホラス等が挙げられる。これらの酸化防止剤の内の１種又は２種以上が好適に用いられる。
　上記酸化防止剤の市販品としては、例えばＢＡＳＦ社製「ＩＲＧＡＮＯＸ　２４５」、ＢＡＳＦ社製「ＩＲＧＡＦＯＳ　１６８」、ＢＡＳＦ社製「ＩＲＧＡＦＯＳ　３８」、住友化学工業社製「スミライザーＢＨＴ」、並びにＢＡＳＦ社製「ＩＲＧＡＮＯＸ　１０１０」等が挙げられる。
　中間膜及び合わせガラスの高い可視光線透過率を長期間に渡り維持するために、上記中間膜１００重量％中又は酸化防止剤を含む層（第１の層、第２の層又は第３の層）１００重量％中、上記酸化防止剤の含有量は０．１重量％以上であることが好ましい。また、酸化防止剤の添加効果が飽和するので、上記中間膜１００重量％中又は上記酸化防止剤を含む層１００重量％中、上記酸化防止剤の含有量は２重量％以下であることが好ましい。
　（他の成分）
　上記第１の層、上記第２の層及び上記第３の層はそれぞれ、必要に応じて、ケイ素、アルミニウム又はチタンを含むカップリング剤、分散剤、界面活性剤、難燃剤、帯電防止剤、顔料、染料、接着力調整剤、耐湿剤、蛍光増白剤及び赤外線吸収剤等の添加剤を含んでいてもよい。これらの添加剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　（合わせガラス用中間膜の他の詳細）
　上記中間膜の厚みは特に限定されない。実用面の観点、並びに合わせガラスの耐貫通性及び曲げ剛性を充分に高める観点からは、中間膜の厚みは、好ましくは０．１ｍｍ以上、より好ましくは０．２５ｍｍ以上、好ましくは３ｍｍ以下、より好ましくは１．５ｍｍ以下である。中間膜の厚みが上記下限以上であると、合わせガラスの耐貫通性及び曲げ剛性が高くなる。中間膜の厚みが上記上限以下であると、中間膜の透明性がより一層良好になる。
　中間膜の厚みをＴとする。上記第１の層の厚みは、好ましくは０．０６２５Ｔ以上、より好ましくは０．１Ｔ以上、好ましくは０．４Ｔ以下、より好ましくは０．３７５Ｔ以下、更に好ましくは０．２５Ｔ以下、更に好ましくは０．１５Ｔ以下である。上記第１の層の厚みが０．４Ｔ以下であると、曲げ剛性がより一層良好になる。
　上記第２の層及び上記第３の層の各厚みは、好ましくは０．３Ｔ以上、より好ましくは０．３１２５Ｔ以上、更に好ましくは０．３７５Ｔ以上、好ましくは０．９３７５Ｔ以下、より好ましくは０．９Ｔ以下である。上記第２の層及び上記第３の層の各厚みは、０．４６８７５Ｔ以下であってもよく、０．４５Ｔ以下であってもよい。また、上記第２の層及び上記第３の層の各厚みが上記下限以上及び上記上限以下であると、合わせガラスの剛性と遮音性がより一層高くなる。
　上記第２の層及び上記第３の層の合計の厚みは、好ましくは０．６２５Ｔ以上、より好ましくは０．７５Ｔ以上、更に好ましくは０．８５Ｔ以上、好ましくは０．９３７５Ｔ以下、より好ましくは０．９Ｔ以下である。また、上記第２の層及び上記第３の層の合計の厚みが上記下限以上及び上記上限以下であると、合わせガラスの剛性と遮音性がより一層高くなる。
　本発明に係る中間膜の製造方法としては特に限定されない。本発明に係る中間膜の製造方法としては、各層を形成するための各樹脂組成物を用いて各層をそれぞれ形成した後に、例えば、得られた各層を積層する方法、並びに各層を形成するための各樹脂組成物を押出機を用いて共押出することにより、各層を積層する方法等が挙げられる。連続的な生産に適しているため、押出成形する製造方法が好ましい。
　中間膜の製造効率が優れることから、上記第２の層と上記第３の層とに、同一のポリビニルアセタール樹脂が含まれていることが好ましく、上記第２の層と上記第３の層とに、同一のポリビニルアセタール樹脂及び同一の可塑剤が含まれていることがより好ましく、上記第２の層と上記第３の層とが同一の樹脂組成物により形成されていることが更に好ましい。
　上記中間膜は、両側の表面の内の少なくとも一方の表面に凹凸形状を有することが好ましい。上記中間膜は、両側の表面に凹凸形状を有することがより好ましい。上記の凹凸形状を形成する方法としては特に限定されず、例えば、リップエンボス法、エンボスロール法、カレンダーロール法、及び異形押出法等が挙げられる。定量的に一定の凹凸模様である多数の凹凸形状のエンボスを形成することができることから、エンボスロール法が好ましい。
　（合わせガラス）
　図２は、図１に示す合わせガラス用中間膜を用いた合わせガラスの一例を模式的に示す断面図である。
　図２に示す合わせガラス３１は、第１の合わせガラス部材２１と、第２の合わせガラス部材２２と、中間膜１１とを備える。中間膜１１は、第１の合わせガラス部材２１と第２の合わせガラス部材２２との間に配置されており、挟み込まれている。
　中間膜１１の第１の表面１１ａに、第１の合わせガラス部材２１が積層されている。中間膜１１の第１の表面１１ａとは反対の第２の表面１１ｂに、第２の合わせガラス部材２２が積層されている。第２の層２の外側の表面２ａに第１の合わせガラス部材２１が積層されている。第３の層３の外側の表面３ａに第２の合わせガラス部材２２が積層されている。
　このように、本発明に係る合わせガラスは、第１の合わせガラス部材と、第２の合わせガラス部材と、中間膜とを備えており、該中間膜が、本発明に係る合わせガラス用中間膜である。本発明に係る合わせガラスでは、上記第１の合わせガラス部材と上記第２の合わせガラス部材との間に、上記中間膜が配置されている。
　上記合わせガラス部材としては、ガラス板及びＰＥＴ（ポリエチレンテレフタレート）フィルム等が挙げられる。合わせガラスには、２枚のガラス板の間に中間膜が挟み込まれている合わせガラスだけでなく、ガラス板とＰＥＴフィルム等との間に中間膜が挟み込まれている合わせガラスも含まれる。上記合わせガラスは、ガラス板を備えた積層体であり、少なくとも１枚のガラス板が用いられていることが好ましい。
　上記ガラス板としては、無機ガラス及び有機ガラスが挙げられる。上記無機ガラスとしては、フロート板ガラス、熱線吸収板ガラス、熱線反射板ガラス、磨き板ガラス、型板ガラス、及び線入り板ガラス等が挙げられる。上記有機ガラスは、無機ガラスに代用される合成樹脂ガラスである。上記有機ガラスとしては、ポリカーボネート板及びポリ（メタ）アクリル樹脂板等が挙げられる。上記ポリ（メタ）アクリル樹脂板としては、ポリメチル（メタ）アクリレート板等が挙げられる。
　上記合わせガラス部材の厚みは、好ましくは１ｍｍ以上、好ましくは５ｍｍ以下、より好ましくは３ｍｍ以下である。また、上記合わせガラス部材がガラス板である場合に、該ガラス板の厚みは、好ましくは０．５ｍｍ以上、より好ましくは０．７ｍｍ以上、好ましくは５ｍｍ以下、より好ましくは３ｍｍ以下である。上記合わせガラス部材がＰＥＴフィルムである場合に、該ＰＥＴフィルムの厚みは、好ましくは０．０３ｍｍ以上、好ましくは０．５ｍｍ以下である。
　本発明に係る中間膜の使用により、合わせガラスの厚みが薄くても、合わせガラスの曲げ剛性を高く維持することができる。合わせガラスを軽量化したり、合わせガラスの材料を少なくして環境負荷を低減したり、合わせガラスの軽量化によって自動車の燃費を向上させて環境負荷を低減したりする観点からは、上記ガラス板の厚みは、好ましくは２ｍｍ以下、より好ましくは１．８ｍｍ以下、より一層好ましくは１．５ｍｍ以下、更に好ましくは１ｍｍ以下、更に一層好ましくは０．８ｍｍ以下、特に好ましくは０．７ｍｍ以下である。
　上記合わせガラスの製造方法は特に限定されない。例えば、上記第１の合わせガラス部材と上記第２の合わせガラス部材との間に、中間膜を挟んで、押圧ロールに通したり、又はゴムバッグに入れて減圧吸引したりして、上記第１の合わせガラス部材と上記第２の合わせガラス部材と中間膜との間に残留する空気を脱気する。その後、約７０～１１０℃で予備接着して積層体を得る。次に、積層体をオートクレーブに入れたり、又はプレスしたりして、約１２０～１５０℃及び１～１．５ＭＰａの圧力で圧着する。このようにして、合わせガラスを得ることができる。上記合わせガラスの製造時に、第１の層と第２の層と第３の層とを積層してもよい。
　上記中間膜及び上記合わせガラスは、自動車、鉄道車両、航空機、船舶及び建築物等に使用できる。上記中間膜及び上記合わせガラスは、これらの用途以外にも使用できる。上記中間膜及び上記合わせガラスは、車両用又は建築用の中間膜及び合わせガラスであることが好ましく、車両用の中間膜及び合わせガラスであることがより好ましい。上記中間膜及び上記合わせガラスは、自動車のフロントガラス、サイドガラス、リアガラス又はルーフガラス等に使用できる。上記中間膜及び上記合わせガラスは、自動車に好適に用いられる。上記中間膜は、自動車の合わせガラスを得るために用いられる。
　透明性により一層優れた合わせガラスを得る観点からは、合わせガラスの上記可視光線透過率は、好ましくは６５％以上、より好ましくは７０％以上である。合わせガラスの可視光線透過率は、ＪＩＳ　Ｒ３２１１（１９９８）に準拠して測定できる。本発明の合わせガラス用中間膜を、ＪＩＳ　Ｒ３２０８に準拠した、厚さ２ｍｍの２枚のグリーンガラス（熱線吸収板ガラス）の間に挟み込むことにより得られた合わせガラスの可視光線透過率は７０％以上であることが好ましい。可視光線透過率は、より好ましくは７５％以上である。
　以下に実施例を掲げて本発明を更に詳しく説明する。本発明はこれら実施例のみに限定されない。
　以下の材料を用意した。
　（ポリビニルアセタール樹脂）
　下記の表１～３に示すポリビニルアセタール樹脂を適宜用いた。用いたポリビニルアセタール樹脂では全て、アセタール化に、炭素数４のｎ－ブチルアルデヒドが用いられている。
　ポリビニルアセタール樹脂に関しては、アセタール化度（ブチラール化度）、アセチル化度及び水酸基の含有率はＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法により測定した。なお、ＡＳＴＭ　Ｄ１３９６－９２により測定した場合も、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法と同様の数値を示した。
　（可塑剤）
　トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）
　ジ－（２－ブトキシエチル）－アジペート（ＤＢＥＡ）
　（フィラー）
　フィラー（ａ）（シリカ粒子、日本アエロジル社製「ＡＥＲＯＳＩＬ３８０」、ＢＥＴ法による比表面積３８０±３０ｍ２／ｇ）
　フィラー（ｂ）（シリカ粒子、東ソー・シリカ社製「ＢＺ－４００」、ＢＥＴ法による比表面積４５０ｍ２／ｇ）
　フィラー（ｃ）（シリカ粒子、東ソー・シリカ社製「ＡＺ－２０４」、ＢＥＴ法による比表面積３００ｍ２／ｇ）
　フィラー（ｄ）（シリカ粒子、東ソー・シリカ社製「ＡＺ－２０１」、ＢＥＴ法による比表面積３００ｍ２／ｇ）
　（紫外線遮蔽剤）
　Ｔｉｎｕｖｉｎ３２６（２－（２’－ヒドロキシ－３’－ｔ－ブチル－５－メチルフェニル）－５－クロロベンゾトリアゾール、ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２６」）
　（酸化防止剤）
　ＢＨＴ（２，６－ジ－ｔ－ブチル－ｐ－クレゾール）
　（実施例１）
　第１の層を形成するための組成物の作製：
　下記の表１に示す種類のポリビニルアセタール樹脂１００重量部と、可塑剤（３ＧＯ）７５重量部と、フィラー（ａ）５重量部と、紫外線遮蔽剤（Ｔｉｎｕｖｉｎ３２６）０．２重量部と、酸化防止剤（ＢＨＴ）０．２重量部とを混合し、第１の層を形成するための組成物を得た。
　第２の層及び第３の層を形成するための組成物の作製：
　下記の表１に示す種類のポリビニルアセタール樹脂１００重量部と、可塑剤（３ＧＯ）４０重量部と、紫外線遮蔽剤（Ｔｉｎｕｖｉｎ３２６）０．２重量部と、酸化防止剤（ＢＨＴ）０．２重量部とを混合し、第２の層及び第３の層を形成するための組成物を得た。
　中間膜の作製：
　第１の層を形成するための組成物と、第２の層及び第３の層を形成するための組成物とを、共押出機を用いて共押出しすることにより、第２の層（厚み３４０μｍ）、第１の層（厚み１００μｍ）、第３の層（厚み３４０μｍ）をそれぞれ作製した。
　剥離試験用の積層膜の作製：
　剥離試験のために、第１の層を形成するための組成物と、第２の層及び第３の層を形成するための組成物を用いて、それぞれ、厚み７６０μｍの第１の層、第２の層、及び、第３の層を作製し、一方の端部が第２の層、第１の層、ＰＥＴフィルム、及び、第３の層の順に積層され、他方の端部が第２の層、第１の層、及び、第３の層の順に積層された積層体を、真空ラミネーターにて９０℃で３０分間保持し、真空プレスし、剥離試験用の積層膜を得た。
　合わせガラスの作製（可視光線透過率測定用）：
　得られた中間膜を、縦３０ｃｍ×横３０ｃｍの大きさに切断した。次に、ＪＩＳ　Ｒ３２０８に準拠した２枚のグリーンガラス（縦３０ｃｍ×横３０ｃｍ×厚み２ｍｍ）を用意した。この２枚のグリーンガラスの間に、得られた中間膜を挟み込み、真空ラミネーターにて９０℃で３０分間保持し、真空プレスし、積層体を得た。積層体において、ガラス板からはみ出た中間膜部分を切り落とし、合わせガラスを得た。
　（実施例２～２５及び比較例１）
　第１の層を形成するための組成物と第２の層及び第３の層を形成するための組成物とに用いるポリビニルアセタール樹脂、可塑剤及びフィラーの種類と配合量とを下記の表１～３に示すように設定したこと、並びに第１の層、第２の層及び第３の層の厚みを下記の表１～３に示すように設定したこと以外は実施例１と同様にして、中間膜及び合わせガラスを得た。また、実施例２～２５及び比較例１では、実施例１と同じ種類の紫外線遮蔽剤及び酸化防止剤を、実施例１と同様の配合量（ポリビニルアセタール樹脂１００重量部に対して０．２重量部）で配合した。
　（評価）
　（１）可視光線透過率（Ａ光Ｙ値、初期Ａ－Ｙ（３８０～７８０ｎｍ））
　分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３２１１（１９９８）に準拠して、得られた合わせガラスの波長３８０～７８０ｎｍにおける可視光線透過率（Ｖｉｓｉｂｌｅ　Ｔｒａｎｓｍｉｔｔａｎｃｅ）を測定した。可視光線透過率を下記の基準で判定した。
　［可視光線透過率の判定基準］
　○：可視光線透過率が７０％以上
　×：可視光線透過率が７０％未満
　（２）剥離試験における最大荷重
　得られた積層膜を縦８ｃｍ×横１ｃｍの大きさに切断した。切断された積層膜の一方の端部（縦２ｃｍ×横１ｃｍ）では第２の層、第１の層、ＰＥＴフィルム、及び、第３の層がこの順に積層されており、他方の端部（縦６ｃｍ×横１ｃｍ）では第２の層、第１の層、及び、第３の層がこの順に積層されていた。切断された積層膜から、ＰＥＴフィルムを取り除き、第３の層と、第１、２の層とをそれぞれ、エー・アンド・デイ社製のテンシロンの治具に固定し、２５℃の恒温室で６０ｍｍ／ｍｉｎの速度で剥離することで、伸び－荷重曲線を得た。得られた伸び－荷重曲線から、伸びが４０ｍｍに至るまでに観測される最大荷重を評価した。最大荷重が大きいほど、各層間の接着力が高いことを示す。
　詳細及び結果を下記の表１～３に示す。なお、下記の表１～３では、ポリビニルアセタール樹脂、可塑剤及びフィラー以外の配合成分の記載は省略した。
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
　なお、実施例１～５の中間膜を用いた合わせガラスは、実施例６の中間膜を用いた合わせガラスよりも曲げ剛性及び遮音性に優れていた。
　１…第１の層
　１ａ…第１の表面
　１ｂ…第２の表面
　２…第２の層
　２ａ…外側の表面
　３…第３の層
　３ａ…外側の表面
　１１…中間膜
　１１ａ…第１の表面
　１１ｂ…第２の表面
　２１…第１の合わせガラス部材
　２２…第２の合わせガラス部材
　３１…合わせガラス

Claims (15)

  1. 　ポリビニルアセタール樹脂と可塑剤とを含む第１の層と、
    　ポリビニルアセタール樹脂と可塑剤とを含む第２の層とを備え、
    　前記第２の層が、前記第１の層の第１の表面に積層されており、
    　前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率と、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率とが異なり、
    　前記第１の層がフィラーを含むか、前記第２の層がフィラーを含むか、又は、中間膜が前記第１の層と前記第２の層との界面に部分的にフィラーを含む、合わせガラス用中間膜。
  2. 　前記第１の層がフィラーを含むか、又は、前記第２の層がフィラーを含む、請求項１に記載の合わせガラス用中間膜。
  3. 　前記第１の層がフィラーを含み、
    　前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率は、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率よりも低い、請求項２に記載の合わせガラス用中間膜。
  4. 　前記第１の層中の前記ポリビニルアセタール樹脂の水酸基の含有率と、前記第２の層中の前記ポリビニルアセタール樹脂の水酸基の含有率との差の絶対値は５モル％以上である、請求項３に記載の合わせガラス用中間膜。
  5. 　前記第１の層中の前記ポリビニルアセタール樹脂１００重量部に対する前記第１の層中の前記可塑剤の含有量は、前記第２の層中の前記ポリビニルアセタール樹脂１００重量部に対する前記第２の層中の前記可塑剤の含有量よりも多い、請求項１～４のいずれか１項に記載の合わせガラス用中間膜。
  6. 　前記フィラーは表面に水酸基を有する、請求項１～５のいずれか１項に記載の合わせガラス用中間膜。
  7. 　前記フィラーがシリカ粒子である、請求項１～６のいずれか１項に記載の合わせガラス用中間膜。
  8. 　前記第１の層中の前記ポリビニルアセタール樹脂１００重量部に対して、前記第１の層中の前記可塑剤の含有量が５０重量部以上である、請求項１～７のいずれか１項に記載の合わせガラス用中間膜。
  9. 　前記第１の層が前記フィラーを含む場合に、前記第１の層中の前記ポリビニルアセタール樹脂１００重量部に対して、前記第１の層中の前記フィラーの含有量が５重量部以上、６４重量部以下である、請求項１～８のいずれか１項に記載の合わせガラス用中間膜。
  10. 　ポリビニルアセタール樹脂と可塑剤とを含む第３の層を備え、
    　前記第３の層は、前記第１の層の前記第１の表面とは反対の第２の表面側に積層されている、請求項１～９のいずれか１項に記載の合わせガラス用中間膜。
  11. 　合わせガラス用中間膜の厚みをＴとしたときに、前記第１の層の厚みが、０．４Ｔ以下である、請求項１～１０のいずれか１項に記載の合わせガラス用中間膜。
  12. 　ＪＩＳ　Ｒ３２０８に準拠した、厚み２ｍｍの２枚のグリーンガラスの間に合わせガラス用中間膜を挟み込むことにより合わせガラスを得たときに、得られる合わせガラスの可視光線透過率が７０％以上である、請求項１～１１のいずれか１項に記載の合わせガラス用中間膜。
  13. 　厚みが１ｍｍ以下である第１のガラス板を用いて、前記第１のガラス板と第２のガラス板との間に配置されて、合わせガラスを得るために用いられる、請求項１～１２のいずれか１項に記載の合わせガラス用中間膜。
  14. 　第１の合わせガラス部材と、
    　第２の合わせガラス部材と、
    　請求項１～１２のいずれか１項に記載の合わせガラス用中間膜とを備え、
    　前記第１の合わせガラス部材と前記第２の合わせガラス部材との間に、前記合わせガラス用中間膜が配置されている、合わせガラス。
  15. 　前記第１の合わせガラス部材が第１のガラス板であり、
    　前記第１のガラス板の厚みが１ｍｍ以下である、請求項１４に記載の合わせガラス。
PCT/JP2015/075936 2014-09-12 2015-09-11 合わせガラス用中間膜及び合わせガラス WO2016039475A1 (ja)