WO2015178458A1 - Matériau d'adsorption pour l'adsorption de substance provoquant l'encrassement de membrane, procédé de traitement de l'eau l'utilisant et procédé de régénération de matériau d'adsorption - Google Patents

Matériau d'adsorption pour l'adsorption de substance provoquant l'encrassement de membrane, procédé de traitement de l'eau l'utilisant et procédé de régénération de matériau d'adsorption Download PDF

Info

Publication number
WO2015178458A1
WO2015178458A1 PCT/JP2015/064635 JP2015064635W WO2015178458A1 WO 2015178458 A1 WO2015178458 A1 WO 2015178458A1 JP 2015064635 W JP2015064635 W JP 2015064635W WO 2015178458 A1 WO2015178458 A1 WO 2015178458A1
Authority
WO
WIPO (PCT)
Prior art keywords
adsorbent
water
membrane
polymer
group
Prior art date
Application number
PCT/JP2015/064635
Other languages
English (en)
Japanese (ja)
Inventor
祐貴 立花
圭介 森川
寛 山村
義公 渡辺
Original Assignee
株式会社クラレ
学校法人 中央大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2014106855A external-priority patent/JP2017124341A/ja
Application filed by 株式会社クラレ, 学校法人 中央大学 filed Critical 株式会社クラレ
Publication of WO2015178458A1 publication Critical patent/WO2015178458A1/fr

Abstract

　L'invention concerne : un matériau d'adsorption pour adsorber des substances provoquant l'encrassement de membrane, le matériau d'adsorption adsorbant efficacement des substances provoquant l'encrassement de membrane pour une filtration de membrane, notamment des bio-polymères tels que des polysaccharides et des protéines ; un procédé de traitement de l'eau, dans lequel le matériau d'adsorption est utilisé ; un procédé de régénération du matériau d'adsorption. Le matériau d'adsorption comprend un premier polymère qui contient un groupe cationique, le matériau d'adsorption étant utilisé pour adsorber les substances provoquant l'encrassement de membrane, qui présente une région dans laquelle la densité de groupe cationique est de 10 à 30 mmol/g, et qui possède une capacité adsorbante par rapport aux substances provoquant l'encrassement de membrane. Ce procédé de traitement de l'eau comprend au moins une étape d'adsorption pour amener l'eau à traiter, qui contient une substance provoquant l'encrassement de membrane, en contact avec un matériau d'adsorption, et pour amener la substance provoquant l'encrassement de membrane, contenue dans l'eau à traiter, à être adsorbée par le matériau d'adsorption. Dans le procédé de régénération d'un matériau d'adsorption, un matériau d'adsorption, avec lequel une substance provoquant l'encrassement de membrane est adsorbée, est amené en contact avec un fluide de nettoyage chauffé à au moins 40 °C et régénéré.
PCT/JP2015/064635 2014-05-23 2015-05-21 Matériau d'adsorption pour l'adsorption de substance provoquant l'encrassement de membrane, procédé de traitement de l'eau l'utilisant et procédé de régénération de matériau d'adsorption WO2015178458A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2014106855A JP2017124341A (ja) 2014-05-23 2014-05-23 水処理方法
JP2014-106855 2014-05-23
JP2014204547 2014-10-03
JP2014-204547 2014-10-03

Publications (1)

Publication Number Publication Date
WO2015178458A1 true WO2015178458A1 (fr) 2015-11-26

Family

ID=54554118

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/064635 WO2015178458A1 (fr) 2014-05-23 2015-05-21 Matériau d'adsorption pour l'adsorption de substance provoquant l'encrassement de membrane, procédé de traitement de l'eau l'utilisant et procédé de régénération de matériau d'adsorption

Country Status (1)

Country Link
WO (1) WO2015178458A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106277429A (zh) * 2016-08-10 2017-01-04 云南省轻工业科学研究院 从精制糖离交废液中提取抗氧化剂的方法及装置
CN107792950A (zh) * 2016-08-29 2018-03-13 合肥格美电器有限责任公司 一种一体式全屋净水机
JP2021045724A (ja) * 2019-09-19 2021-03-25 名古屋市 半金属用吸着材及び半金属元素除去方法
CN116143227A (zh) * 2023-04-19 2023-05-23 新乡学院 一种吸附-超滤联用处理低浓度重金属污染废水的方法
WO2023176048A1 (fr) * 2022-03-14 2023-09-21 日東電工株式会社 Membrane d'osmose inverse composite et son procédé de production
WO2023176049A1 (fr) * 2022-03-14 2023-09-21 日東電工株式会社 Membrane composite d'osmose inverse et son procédé de production
CN117482932A (zh) * 2023-09-26 2024-02-02 湖南中寅环保设备制造有限公司 一种废润滑油精制吸附剂的再生方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62216641A (ja) * 1986-03-19 1987-09-24 Nippon Shokubai Kagaku Kogyo Co Ltd 環境浄化用吸着剤
JP2006151705A (ja) * 2004-11-25 2006-06-15 Kanto Natural Gas Development Co Ltd フルボ酸含有物およびフルボ酸含有物の製造方法
JP2008279435A (ja) * 2007-04-09 2008-11-20 Hitachi Ltd 廃水中に含まれる有機物の処理方法、処理装置、及び処理システム、並びにビチュメン回収システム
JP2012067268A (ja) * 2010-09-27 2012-04-05 Kuraray Co Ltd 組成物、金属イオン吸着材、及び金属回収方法
JP2012187507A (ja) * 2011-03-10 2012-10-04 Toshiba Corp 水処理装置及び水処理方法
JP2013056286A (ja) * 2011-09-07 2013-03-28 Hitachi Ltd 海水淡水化システム

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62216641A (ja) * 1986-03-19 1987-09-24 Nippon Shokubai Kagaku Kogyo Co Ltd 環境浄化用吸着剤
JP2006151705A (ja) * 2004-11-25 2006-06-15 Kanto Natural Gas Development Co Ltd フルボ酸含有物およびフルボ酸含有物の製造方法
JP2008279435A (ja) * 2007-04-09 2008-11-20 Hitachi Ltd 廃水中に含まれる有機物の処理方法、処理装置、及び処理システム、並びにビチュメン回収システム
JP2012067268A (ja) * 2010-09-27 2012-04-05 Kuraray Co Ltd 組成物、金属イオン吸着材、及び金属回収方法
JP2012187507A (ja) * 2011-03-10 2012-10-04 Toshiba Corp 水処理装置及び水処理方法
JP2013056286A (ja) * 2011-09-07 2013-03-28 Hitachi Ltd 海水淡水化システム

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106277429A (zh) * 2016-08-10 2017-01-04 云南省轻工业科学研究院 从精制糖离交废液中提取抗氧化剂的方法及装置
CN107792950A (zh) * 2016-08-29 2018-03-13 合肥格美电器有限责任公司 一种一体式全屋净水机
JP2021045724A (ja) * 2019-09-19 2021-03-25 名古屋市 半金属用吸着材及び半金属元素除去方法
JP7352055B2 (ja) 2019-09-19 2023-09-28 名古屋市 半金属用吸着材及び半金属元素除去方法
WO2023176048A1 (fr) * 2022-03-14 2023-09-21 日東電工株式会社 Membrane d'osmose inverse composite et son procédé de production
WO2023176049A1 (fr) * 2022-03-14 2023-09-21 日東電工株式会社 Membrane composite d'osmose inverse et son procédé de production
CN116143227A (zh) * 2023-04-19 2023-05-23 新乡学院 一种吸附-超滤联用处理低浓度重金属污染废水的方法
CN117482932A (zh) * 2023-09-26 2024-02-02 湖南中寅环保设备制造有限公司 一种废润滑油精制吸附剂的再生方法
CN117482932B (zh) * 2023-09-26 2024-04-16 湖南中寅环保设备制造有限公司 一种废润滑油精制吸附剂的再生方法

Similar Documents

Publication Publication Date Title
WO2015178458A1 (fr) Matériau d'adsorption pour l'adsorption de substance provoquant l'encrassement de membrane, procédé de traitement de l'eau l'utilisant et procédé de régénération de matériau d'adsorption
Gao et al. Ultrasonic control of UF membrane fouling by natural waters: Effects of calcium, pH, and fractionated natural organic matter
Zhang et al. Thin film interfacial cross-linking approach to fabricate a chitosan rejecting layer over poly (ether sulfone) support for heavy metal removal
WO2015076371A1 (fr) Adsorbant polymère hydrophile et procédé de traitement de l'eau utilisant celui-ci
CN108465377B (zh) 一种再生纤维素/壳聚糖复合抗菌纳滤膜的制备方法
KR102702779B1 (ko) 여과를 통해 식수에서 박테리아 제거
JP2017018843A (ja) 水処理方法、水処理用高分子吸着材、およびその再生方法
JP7275034B2 (ja) 超純水を製造するための方法
JP2017094259A (ja) 膜ファウリング抑制材
JP2004066153A (ja) ホウ素選択吸着能を有する有機多孔質体、これを用いたホウ素除去モジュールおよび超純水製造装置
K Goyal et al. Nanotechnology for water treatment
JP2016215147A (ja) 膜ファウリング原因物質吸着材
Dutta et al. Interpenetrating polymer networks for desalination and water remediation: A comprehensive review of research trends and prospects
JP2016215156A (ja) 水処理用安全フィルター
Elshaarawy et al. Dual ionic liquid-based crosslinked chitosan for fine-tuning of antifouling, water throughput, and denitrification performance of polysulfone membrane
JP2016040031A (ja) 冷却塔の循環水処理システム
WO2015076370A1 (fr) Composition adsorbant les biopolymères et procédé de traitement de l'eau l'utilisant
JP2017018842A (ja) 親水性高分子吸着材およびそれを用いた水処理方法
JP2016040030A (ja) 水処理システム
Nazir et al. Polymeric membranes nanocomposites as effective strategy for dye removal
Chooaksorn et al. Enhancement of Cr (VI) ion removal using nanochitosan coated on bituminous activated carbon
JP2016215144A (ja) 水処理システム
JP2016040029A (ja) 海水淡水化システム
JP2017124341A (ja) 水処理方法
JP2007090243A (ja) 水処理用金属イオン吸着剤およびその製造方法、ならびにそれを用いた水処理方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15795481

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15795481

Country of ref document: EP