WO2015115627A1 - 合わせガラス及び合わせガラスの取り付け方法 - Google Patents

合わせガラス及び合わせガラスの取り付け方法 Download PDF

Info

Publication number
WO2015115627A1
WO2015115627A1 PCT/JP2015/052774 JP2015052774W WO2015115627A1 WO 2015115627 A1 WO2015115627 A1 WO 2015115627A1 JP 2015052774 W JP2015052774 W JP 2015052774W WO 2015115627 A1 WO2015115627 A1 WO 2015115627A1
Authority
WO
WIPO (PCT)
Prior art keywords
laminated glass
resin layer
wavelength
resin
infrared
Prior art date
Application number
PCT/JP2015/052774
Other languages
English (en)
French (fr)
Inventor
山口　宏平
聖樹 山本
中島　大輔
松本　泉
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to MX2016009650A priority Critical patent/MX2016009650A/es
Priority to KR1020167018238A priority patent/KR102335700B1/ko
Priority to EP15743027.3A priority patent/EP3100989B1/en
Priority to CA2936172A priority patent/CA2936172A1/en
Priority to JP2015510559A priority patent/JP6955840B2/ja
Priority to RU2016135244A priority patent/RU2687997C2/ru
Priority to CN201580003549.9A priority patent/CN105873877B/zh
Priority to US15/111,396 priority patent/US11524487B2/en
Priority to BR112016016934-4A priority patent/BR112016016934B1/pt
Publication of WO2015115627A1 publication Critical patent/WO2015115627A1/ja

Abstract

　遮熱性が高い合わせガラスを提供する。　本発明に係る合わせガラスは、第１の合わせガラス部材と、第２の合わせガラス部材と、第１，第２の合わせガラス部材の間に配置された中間膜とを備え、中間膜は、赤外線を反射する赤外線反射層と、赤外線反射層の第１の表面側に配置されており、かつ熱可塑性樹脂を含む第１の樹脂層と、赤外線反射層の第２の表面側に配置されており、かつ熱可塑性樹脂を含む第２の樹脂層とを備え、第１の合わせガラス部材と第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率は、第２の合わせガラス部材と第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも１５％以上高い。

Description

合わせガラス及び合わせガラスの取り付け方法
　本発明は、自動車及び建築物などの合わせガラスに用いられる合わせガラスに関する。また、本発明は、上記合わせガラスの取り付け方法に関する。
　合わせガラスは、外部衝撃を受けて破損してもガラスの破片の飛散量が少なく、安全性に優れている。このため、上記合わせガラスは、自動車、鉄道車両、航空機、船舶及び建築物等に広く使用されている。上記合わせガラスは、一対のガラス板の間に合わせガラス用中間膜を挟み込むことにより、製造されている。このような車両及び建築物の開口部に用いられる合わせガラスには、高い遮熱性が求められる。
　可視光よりも長い波長７８０ｎｍ以上の赤外線は、紫外線と比較して、エネルギー量が小さい。しかしながら、赤外線は熱的作用が大きく、赤外線が物質に吸収されると熱として放出される。このため、赤外線は一般に熱線と呼ばれている。従って、合わせガラスの遮熱性を高めるためには、赤外線を十分に遮断する必要がある。
　上記赤外線（熱線）を効果的に遮断するための遮熱粒子を含む中間膜として、下記の特許文献１には、錫ドープ酸化インジウム粒子（ＩＴＯ粒子）又はアンチモンドープ酸化錫粒子（ＡＴＯ粒子）を含む中間膜が開示されている。下記の特許文献２には、酸化タングステン粒子を含む中間膜が開示されている。
ＷＯ２００１／０２５１６２Ａ１ ＷＯ２００５／０８７６８０Ａ１
　近年、中間膜を用いた合わせガラスでは、高い遮熱性と高い可視光線透過率（Ｖｉｓｉｂｌｅ　Ｔｒａｎｓｍｉｔｔａｎｃｅ）とを両立することが求められる。すなわち、合わせガラスでは、上記可視光線透過率を高く維持したままで、遮熱性を高くする必要がある。
　しかし、特許文献１，２に記載のような従来の合わせガラスでは、高い遮熱性と高い可視光線透過率とを両立できないことがある。
　本発明の目的は、遮熱性が高い合わせガラスを提供すること、並びに該合わせガラスの取り付け方法を提供することである。
　本発明の限定的な目的は、遮熱性が高く、かつ可視光線透過率が高い合わせガラスを提供すること、並びに該合わせガラスの取り付け方法を提供することである。
　本発明の広い局面によれば、第１の合わせガラス部材と、第２の合わせガラス部材と、前記第１の合わせガラス部材と前記第２の合わせガラス部材との間に配置された中間膜とを備え、前記中間膜が、赤外線を反射する赤外線反射層と、前記赤外線反射層の第１の表面側に配置されており、かつ熱可塑性樹脂を含む第１の樹脂層と、前記赤外線反射層の前記第１の表面とは反対の第２の表面側に配置されており、かつ熱可塑性樹脂を含む第２の樹脂層とを備え、前記中間膜における前記第１の樹脂層の外側に、前記第１の合わせガラス部材が配置されており、前記中間膜における前記第２の樹脂層の外側に、前記第２の合わせガラス部材が配置されており、前記第１の合わせガラス部材と前記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材と前記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも１５％以上高い、合わせガラスが提供される。
　前記第１の合わせガラス部材と前記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材と前記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも、好ましくは２０％以上高く、より好ましくは３０％以上高い。
　本発明に係る合わせガラスのある特定の局面では、前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いか、又は、前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い。
　本発明に係る合わせガラスの他の特定の局面では、前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い。
　本発明に係る合わせガラスのさらに他の特定の局面では、前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い。
　本発明に係る合わせガラスのさらに他の特定の局面では、前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高く、かつ、前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い。
　本発明に係る合わせガラスのさらに他の特定の局面では、前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも１０％以上高く、かつ、前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも１０％以上高い。
　本発明に係る合わせガラスの別の特定の局面では、前記赤外線反射層が、金属箔付き樹脂フィルム、樹脂層上に金属層及び誘電層が形成された多層積層フィルム、多層樹脂フィルム又は液晶フィルムである。
　前記第１の樹脂層と前記第２の樹脂層との内の少なくとも一方が、接着力調整剤を含むことが好ましい。前記第１の樹脂層と前記第２の樹脂層との双方が、前記接着力調整剤を含むことがより好ましい。
　本発明に係る合わせガラスの他の特定の局面では、前記第２の樹脂層が金属酸化物粒子を含む。
　本発明に係る合わせガラスのさらに他の特定の局面では、前記金属酸化物粒子が、錫ドープ酸化インジウム粒子又は酸化タングステン粒子である。
　本発明に係る合わせガラスの別の特定の局面では、前記第２の樹脂層が、フタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物の内の少なくとも１種を含む。
　本発明に係る合わせガラスの別の特定の局面では、前記第１の樹脂層中の前記熱可塑性樹脂がポリビニルアセタール樹脂であり、前記第２の樹脂層中の前記熱可塑性樹脂がポリビニルアセタール樹脂である。
　本発明に係る合わせガラスのさらに別の特定の局面では、前記第１の樹脂層が可塑剤を含み、前記第２の樹脂層が可塑剤を含む。
　本発明に係る合わせガラスの他の特定の局面では、前記第１の樹脂層が紫外線遮蔽剤を含む。
　本発明に係る合わせガラスのさらに他の特定の局面では、前記第２の樹脂層が紫外線遮蔽剤を含む。
　本発明の広い局面によれば、上述した合わせガラスを、建築物又は車両において、外部空間と前記外部空間から熱線が入射される内部空間との間の開口部に取り付ける方法であって、前記第１の合わせガラス部材が、前記外部空間側に位置するように、かつ前記第２の合わせガラス部材が前記内部空間側に位置するように、前記合わせガラスを前記開口部に取り付ける、合わせガラスの取り付け方法が提供される。
　本発明に係る合わせガラスは、上記第１の合わせガラス部材と上記第１の樹脂層と上記赤外線反射層と上記第２の樹脂層と上記第２の合わせガラス部材とがこの順で並んで配置されており、上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の合わせガラス部材と上記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも１５％以上高いので、遮熱性を高くすることができる。
図１は、本発明の一実施形態に係る合わせガラスを示す部分切欠断面図である。 図２は、本発明の一実施形態に係る合わせガラスに用いられる合わせガラス用中間膜を示す部分切欠断面図である。
　以下、図面を参照しつつ、本発明の具体的な実施形態及び実施例を説明することにより本発明を明らかにする。
　図２に、本発明の一実施形態に係る合わせガラスに用いられる合わせガラス用中間膜を模式的に部分切欠断面図で示す。
　図２に示す中間膜１は、多層中間膜である。中間膜１は、合わせガラスを得るために用いられる。中間膜１は、合わせガラス用中間膜である。中間膜１は、赤外線反射層２と、赤外線反射層２の第１の表面２ａ側に配置された第１の樹脂層３と、赤外線反射層２の第１の表面２ａとは反対の第２の表面２ｂ側に配置された第２の樹脂層４とを備える。第１の樹脂層３は、赤外線反射層２の第１の表面２ａに積層されている。第２の樹脂層４は、赤外線反射層２の第２の表面２ｂに積層されている。赤外線反射層２は、中間層であり、熱線を反射する性能を有する。第１，第２の樹脂層３，４は、本実施形態では表面層である。赤外線反射層２は、第１，第２の樹脂層３，４の間に配置されている。赤外線反射層２は、第１，第２の樹脂層３，４の間に挟み込まれている。従って、中間膜１は、第１の樹脂層３と、赤外線反射層２と、第２の樹脂層４とがこの順で積層された多層構造を有する。
　なお、赤外線反射層２と第１の樹脂層３との間、及び、赤外線反射層２と第２の樹脂層４との間にはそれぞれ、他の層が配置されていてもよい。赤外線反射層２と第１の樹脂層３、及び、赤外線反射層２と第２の樹脂層４とはそれぞれ、直接積層されていることが好ましい。他の層として、ポリビニルアセタール樹脂等の熱可塑性樹脂を含む層、ポリエチレンテレフタレートやポリエチレンナフタレート等を含む層、並びに金属箔等の無機化合物により形成された層が挙げられる。これらの他の層が含まれる場合、１種の層のみが含まれていてもよく、２種以上の異なる層が含まれていてもよい。
　上記赤外線反射層は赤外線を反射する。上記赤外線反射層は、赤外線を反射する性能を有していれば特に限定されない。赤外線を反射する性能に優れることから、上記赤外線反射層が、８００～２０００ｎｍの範囲内の少なくとも１つの波長において、赤外線透過率が４０％以下である性質を有することが好ましい。なお、後述する実施例で用いた赤外線反射層の赤外線透過率は、上記の好ましい条件を満足する。８００～２０００ｎｍの範囲内の少なくとも１つの波長において、赤外線透過率はより好ましくは３０％以下、更に好ましくは２０％以下である。
　上記赤外線反射層としては、金属箔付き樹脂フィルム、樹脂層上に金属層及び誘電層が形成された多層積層フィルム、グラファイトを含むフィルム、多層樹脂フィルム及び液晶フィルム等が挙げられる。これらのフィルムは、赤外線を反射する性能を有する。
　上記赤外線反射層は、金属箔付き樹脂フィルム、樹脂層上に金属層及び誘電層が形成された多層積層フィルム、多層樹脂フィルム又は液晶フィルムであることが特に好ましい。これらのフィルムは、赤外線の反射性能にかなり優れている。従って、これらのフィルムの使用により、遮熱性がより一層高く、高い可視光線透過率をより一層長期間に渡り維持できる合わせガラスが得られる。上記赤外線反射層は、金属箔付き樹脂フィルム、多層樹脂フィルム又は液晶フィルムであってもよい。
　上記金属箔付き樹脂フィルムは、樹脂フィルムと、該樹脂フィルムの外表面に積層された金属箔とを備える。上記樹脂フィルムの材料としては、ポリエチレンテレフタレート樹脂、ポリエチレンナフタレート樹脂、ポリビニルアセタール樹脂、エチレン－酢酸ビニル共重合体樹脂、エチレン－アクリル共重合体樹脂、ポリウレタン樹脂、ポリビニルアルコール樹脂、ポリオレフィン樹脂、ポリ塩化ビニル樹脂及びポリイミド樹脂等が挙げられる。上記金属箔の材料としては、アルミニウム、銅、銀、金、パラジウム、及びこれらを含む合金等が挙げられる。
　上記樹脂層上に金属層及び誘電層が形成された多層積層フィルムは、樹脂層（樹脂フィルム）に、金属層及び誘電層が交互に任意の層数で積層された多層積層フィルムである。
　上記多層積層フィルムにおける上記樹脂層（樹脂フィルム）の材料としては、上記金属箔付き樹脂フィルムにおける樹脂フィルムの材料と同様の材料が挙げられる。上記多層積層フィルムにおける上記樹脂層（樹脂フィルム）の材料としては、ポリエチレン、ポリプロピレン、ポリ乳酸、ポリ（４－メチルペンテン－１）、ポリフッ化ビニリデン、環状ポリオレフィン、ポリメチルメタクリレート、ポリ塩化ビニル、ポリビニルアルコール、ナイロン６，１１，１２，６６などのポリアミド、ポリスチレン、ポリカーボネート、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエステル、ポリフェニレンサルファイド及びポリエーテルイミド等が挙げられる。上記多層積層フィルムにおける上記金属層の材料としては、上記金属箔付き樹脂フィルムにおける上記金属箔の材料と同様の材料が挙げられる。上記金属層の両面もしくは片面に、金属もしくは混合酸化物のコート層を付与することができる。上記コート層の材料としては、ＺｎＯ、Ａｌ２Ｏ３、Ｇａ２Ｏ３、ＩｎＯ３、ＭｇＯ、Ｔｉ、ＮｉＣｒ及びＣｕ等が挙げられる。
　上記多層積層フィルムにおける上記誘電層の材料としては、例えば酸化インジウム等が挙げられる。
　上記多層樹脂フィルムは、複数の樹脂フィルムが積層された積層フィルムである。上記多層樹脂フィルムの材料としては、上記多層積層フィルムにおける上記樹脂層（樹脂フィルム）の材料と同様の材料が挙げられる。上記多層樹脂フィルムにおける樹脂フィルムの積層数は、２以上であり、３以上であってもよく、５以上であってもよい。上記多層樹脂フィルムにおける樹脂フィルムの積層数は、１０００以下であってもよく、１００以下であってもよく、５０以下であってもよい。
　上記多層樹脂フィルムは、異なる光学的性質（屈折率）を有する２種類以上の熱可塑性樹脂層が交互に又はランダムに任意の層数で積層された多層樹脂フィルムであってもよい。このような多層樹脂フィルムは、所望の赤外線反射性能が得られるように構成される。
　上記液晶フィルムとしては、任意の波長の光を反射するコレステリック液晶層を任意の層数で積層したフィルムが挙げられる。このような液晶フィルムは、所望の赤外線反射性能が得られるように構成される。
　上記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率は、上記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いことが好ましい。この場合には、別の見方をすれば、上記第１の樹脂層の赤外線吸収率は、上記第２の樹脂層の赤外線吸収率よりも低い。
　上記第１の樹脂層の上記赤外線透過率が、上記第２の樹脂層の上記赤外線透過率よりも高い場合には、上記第１の樹脂層は、赤外線を比較的多く透過する。このため、上記第１の樹脂層を透過した多くの赤外線は、上記赤外線反射層に至る。上記赤外線反射層は、赤外線を反射するので、上記赤外線反射層に至った赤外線は、上記赤外線反射層により反射される。また、上記第１の樹脂層の赤外線透過率が高いことから、上記赤外線反射層により反射された赤外線の多くは、上記第１の樹脂層を透過する。この結果、中間膜に赤外線が入射された際の中間膜の温度上昇を抑制できる。このため、上記中間膜の遮熱性が高くなり、更に耐光性に優れているので高い可視光線透過率を長期間に渡り維持できる。また、上記中間膜を用いた合わせガラスを建築物又は車両の開口部に取り付けることで、建築物又は車両の内部空間の温度上昇を効果的に抑制できる。
　一方で、上記第１の樹脂層の上記赤外線透過率が、上記第２の樹脂層の上記赤外線透過率よりも高い場合に、仮に上記第１の樹脂層と上記赤外線反射層とを赤外線の一部が透過すると、透過した赤外線は、上記第２の樹脂層に至る。上記第２の樹脂層の赤外線透過率が低いと、上記第２の樹脂層は、赤外線の透過を効果的に遮断する。このため、中間膜全体を通過する熱線の量を低減できる。このことによっても、上記合わせガラス用中間膜の遮熱性が高くなり、上記合わせガラス用中間膜を用いた合わせガラスを建築物又は車両の開口部に取り付けることで、建築物又は車両の内部空間の温度上昇を効果的に抑制できる。
　上記第１の樹脂層と上記第２の樹脂層とは同一であってもよく、異なっていてもよい。上記第１の樹脂層と上記第２の樹脂層とは異なることが好ましい。上記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い場合には、上記第１の樹脂層と上記第２の樹脂層との組成は異なる。
　上記第１の樹脂層は熱可塑性樹脂を含む。上記第１の樹脂層中の熱可塑性樹脂は、ポリビニルアセタール樹脂であることがより好ましい。上記第１の樹脂層は、可塑剤を含むことが好ましく、ポリビニルアセタール樹脂と可塑剤とを含むことがより好ましい。上記第１の樹脂層は、紫外線遮蔽剤を含むことが好ましく、酸化防止剤を含むことが好ましい。
　上記第２の樹脂層は熱可塑性樹脂を含む。上記第２の樹脂層中の熱可塑性樹脂は、ポリビニルアセタール樹脂であることがより好ましい。上記第２の樹脂層は、可塑剤を含むことが好ましく、ポリビニルアセタール樹脂と可塑剤とを含むことがより好ましい。上記第２の樹脂層は、紫外線遮蔽剤を含むことが好ましく、酸化防止剤を含むことが好ましい。
　上記第２の樹脂層は、遮熱性化合物を含むことが好ましい。上記第２の樹脂層が遮熱性化合物を含むことで、上記第１の樹脂層の上記赤外線透過率が、上記第２の樹脂層の上記赤外線透過率よりも高くなる。この結果、上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の上記赤外線透過率を、上記第２の合わせガラス部材と上記第２の樹脂層との２つの層全体の上記赤外線透過率よりも高くすることが容易である。
　上記第１の樹脂層は、遮熱性化合物を含んでいてもよい。また、上記第１の樹脂層中の上記遮熱性化合物の含有量（重量％）が上記第２の樹脂層中の上記遮熱性化合物の含有量（重量％）よりも少ないと、上記第１の樹脂層の上記赤外線透過率を、上記第２の樹脂層の上記赤外線透過率よりも高くすることが容易である。上記遮熱性化合物としては、金属酸化物粒子などの遮熱粒子や、フタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物の内の少なくとも１種の成分（以下、成分Ｘと記載することがある）等が挙げられる。なお、遮熱性化合物とは、赤外線を吸収可能な化合物を意味する。上記第１の樹脂層又は上記第２の樹脂層が複数の遮熱性化合物を含む場合は、上記第１の樹脂層中の上記遮熱性化合物の合計の含有量（重量％）は上記第２の樹脂層中の上記遮熱性化合物の合計の含有量（重量％）よりも少ないことが好ましく、０．０５重量％以上少ないことがより好ましく、０．１重量％以上少ないことが更に好ましく、０．２重量％以上少ないことが特に好ましく、０．４重量％以上少ないことが最も好ましい。さらに、遮熱性がより一層高くなることから、上記第２の樹脂層中の上記遮熱性化合物の合計の含有量（重量％）と上記第１の樹脂層中の上記遮熱性化合物の合計の含有量（重量％）との差は２重量％以下であることが好ましい。
　第１の合わせガラス部材と第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率をＴ１、第２の合わせガラス部材と第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率をＴ２としたときに、Ｔ１はＴ２よりも１５％以上高い。このため、合わせガラスの遮熱性が高くなる。合わせガラスの遮熱性がより一層高くなることから、Ｔ１はＴ２よりも２０％以上高いことが好ましく、２５％以上高いことがより好ましく、３０％以上高いことがより一層好ましく、３５％以上高いことが更に好ましく、４０％以上高いことが更に一層好ましく、４５％以上高いことが特に好ましく、５０％以上高いことが最も好ましい。（Ｔ１－Ｔ２）の値の上限は特に限定されないが、合わせガラスの透明性がより一層高くなることから、（Ｔ１－Ｔ２）は９０％以下であることが好ましく、８５％以下であることがより好ましく、８０％以下であることが更に好ましい。
　第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率をＴｘ１、第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率をＴｘ２としたときに、Ｔｘ１はＴｘ２よりも高いことが好ましい。合わせガラスの遮熱性がより一層高くなることから、Ｔｘ１はＴｘ２よりも１０％以上高いことが好ましく、２０％以上高いことがより好ましく、２５％以上高いことが更に好ましく、３０％以上高いことが特に好ましい。（Ｔｘ１－Ｔｘ２）の値の上限は特に限定されないが、合わせガラスの透明性がより一層高くなることから、（Ｔｘ１－Ｔｘ２）は７０％以下であることが好ましく、６０％以下であることがより好ましく、５０％以下であることが更に好ましく、４０％以下であることが特に好ましい。合わせガラスの遮熱性及び透明性をより一層高めるために、Ｔｘ１の好ましい下限は６０％、好ましい上限は９０％、より好ましい下限は６５％、より好ましい上限は８５％、更に好ましい下限は７０％、更に好ましい上限は８０％である。また、合わせガラスの遮熱性及び透明性をより一層高めるために、Ｔｘ２の好ましい下限は２０％、好ましい上限は７５％、より好ましい下限は２５％、より好ましい上限は６５％、更に好ましい下限は３０％、更に好ましい上限は５５％、特に好ましい下限は３５％、特に好ましい上限は５０％である。
　第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率をＴｙ１、第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率をＴｙ２としたときに、Ｔｙ１はＴｙ２よりも高いことが好ましい。合わせガラスの遮熱性がより一層高くなることから、Ｔｙ１はＴｙ２よりも１０％以上高いことが好ましく、１５％以上高いことがより好ましく、２０％以上高いことが更に好ましい。（Ｔｙ１－Ｔｙ２）の値の上限は特に限定されないが、合わせガラスの透明性がより一層高くなることから、（Ｔｙ１－Ｔｙ２）は５０％以下であることが好ましく、４０％以下であることがより好ましく、３０％以下であることが更に好ましく、２５％以下であることが特に好ましい。合わせガラスの遮熱性及び透明性をより一層高めるために、Ｔｙ１の好ましい下限は５０％、好ましい上限は９０％、より好ましい下限は５５％、より好ましい上限は８８％、更に好ましい下限は６０％、更に好ましい上限は８６％である。また、合わせガラスの遮熱性及び透明性をより一層高めるために、Ｔｙ２の好ましい下限は４０％、好ましい上限は８８％、より好ましい下限は４５％、より好ましい上限は８６％、更に好ましい下限は５５％、更に好ましい上限は７０％、特に好ましい下限は６０％、特に好ましい上限は６５％である。
　なお、第１の合わせガラス部材と第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率Ｔ１は以下のように測定される。
　第１の合わせガラス部材と第１の樹脂層とクリアガラス（厚み２．５ｍｍ）とがこの順に積層された合わせガラスを作製する。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得る。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得る。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ１を算出する。
　第２の合わせガラス部材と第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率Ｔ２は以下のように測定される。
　第２の合わせガラス部材と第２の樹脂層とクリアガラス（厚み２．５ｍｍ）とがこの順に積層された合わせガラスを作製する。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得る。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得る。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ２を算出する。
　また、第１の樹脂層又は第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率Ｔｘ１，Ｔｘ２は以下のようにして測定される。
　第１の樹脂層又は第２の樹脂層を２枚のクリアガラス（厚み２．５ｍｍ）の間に積層し、合わせガラスを作製する。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得る。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得る。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ１を算出する。
　以下、上記第１，第２の樹脂層を構成する材料の詳細を説明する。
　（熱可塑性樹脂）
　上記第１，第２の樹脂層は熱可塑性樹脂を含む。該熱可塑性樹脂は特に限定されない。熱可塑性樹脂として、従来公知の熱可塑性樹脂を用いることができる。熱可塑性樹脂は１種のみが用いられてもよく、２種以上が併用されてもよい。上記第１の樹脂層中の熱可塑性樹脂と、上記第２の樹脂層中の熱可塑性樹脂とは同一であってもよく、異なっていてもよい。
　上記熱可塑性樹脂としては、ポリビニルアセタール樹脂、エチレン－酢酸ビニル共重合体樹脂、エチレン－アクリル酸共重合体樹脂、ポリウレタン樹脂及びポリビニルアルコール樹脂等が挙げられる。これら以外の熱可塑性樹脂を用いてもよい。
　上記熱可塑性樹脂は、ポリビニルアセタール樹脂であることが好ましい。ポリビニルアセタール樹脂と可塑剤との併用により、合わせガラス部材及び赤外線反射層などの他の層に対する第１，第２の樹脂層の接着力がより一層高くなる。
　上記ポリビニルアセタール樹脂は、例えば、ポリビニルアルコールをアルデヒドによりアセタール化することにより製造できる。上記ポリビニルアルコールは、例えば、ポリ酢酸ビニルをけん化することにより製造できる。上記ポリビニルアルコールのけん化度は、一般に７０～９９．８モル％の範囲内である。
　上記ポリビニルアルコールの平均重合度は、好ましくは２００以上、より好ましくは５００以上、好ましくは５０００以下、より好ましくは４０００以下、更に好ましくは３５００以下、特に好ましくは３０００以下、最も好ましくは２５００以下である。上記平均重合度が上記下限以上であると、合わせガラスの耐貫通性がより一層高くなる。上記平均重合度が上記上限以下であると、中間膜の成形が容易になる。なお、上記ポリビニルアルコールの平均重合度は、ＪＩＳ　Ｋ６７２６「ポリビニルアルコール試験方法」に準拠した方法により求められる。
　上記ポリビニルアセタール樹脂に含まれているアセタール基の炭素数は特に限定されない。上記ポリビニルアセタール樹脂を製造する際に用いるアルデヒドは特に限定されない。上記ポリビニルアセタール樹脂におけるアセタール基の炭素数は３又は４であることが好ましい。上記ポリビニルアセタール樹脂におけるアセタール基の炭素数が３以上であると、中間膜のガラス転移温度が充分に低くなる。
　上記アルデヒドは特に限定されない。上記アルデヒドとして、一般には、炭素数が１～１０のアルデヒドが好適に用いられる。上記炭素数が１～１０のアルデヒドとしては、例えば、プロピオンアルデヒド、ｎ－ブチルアルデヒド、イソブチルアルデヒド、ｎ－バレルアルデヒド、２－エチルブチルアルデヒド、ｎ－ヘキシルアルデヒド、ｎ－オクチルアルデヒド、ｎ－ノニルアルデヒド、ｎ－デシルアルデヒド、ホルムアルデヒド、アセトアルデヒド及びベンズアルデヒド等が挙げられる。なかでも、プロピオンアルデヒド、ｎ－ブチルアルデヒド、イソブチルアルデヒド、ｎ－ヘキシルアルデヒド又はｎ－バレルアルデヒドが好ましく、プロピオンアルデヒド、ｎ－ブチルアルデヒド又はイソブチルアルデヒドがより好ましく、ｎ－ブチルアルデヒドが更に好ましい。上記アルデヒドは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記ポリビニルアセタール樹脂の水酸基の含有率（水酸基量）は、好ましくは１５モル％以上、より好ましくは１８モル％以上、更に好ましくは２０モル％以上、特に好ましくは２８モル％以上、好ましくは４０モル％以下、より好ましくは３５モル％以下、更に好ましくは３２モル％以下である。上記水酸基の含有率が上記下限以上であると、中間膜の接着力がより一層高くなる。また、上記水酸基の含有率が上記上限以下であると、中間膜の柔軟性が高くなり、中間膜の取扱いが容易になる。
　上記ポリビニルアセタール樹脂の水酸基の含有率は、水酸基が結合しているエチレン基量を、主鎖の全エチレン基量で除算して求めたモル分率を百分率で示した値である。上記水酸基が結合しているエチレン基量は、例えば、ＪＩＳ　Ｋ６７２６「ポリビニルアルコール試験方法」に準拠して、測定することにより求めることができる。
　上記ポリビニルアセタール樹脂のアセチル化度（アセチル基量）は、好ましくは０．１モル％以上、より好ましくは０．３モル％以上、更に好ましくは０．５モル％以上、好ましくは３０モル％以下、より好ましくは２５モル％以下、更に好ましくは２０モル％以下、特に好ましくは１５モル％以下、最も好ましくは３モル％以下である。上記アセチル化度が上記下限以上であると、ポリビニルアセタール樹脂と可塑剤との相溶性が高くなる。上記アセチル化度が上記上限以下であると、中間膜及び合わせガラスの耐湿性が高くなる。
　上記アセチル化度は、主鎖の全エチレン基量から、アセタール基が結合しているエチレン基量と、水酸基が結合しているエチレン基量とを差し引いた値を、主鎖の全エチレン基量で除算して求めたモル分率を百分率で示した値である。上記アセタール基が結合しているエチレン基量は、例えば、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠して測定できる。
　上記ポリビニルアセタール樹脂のアセタール化度（ポリビニルブチラール樹脂の場合にはブチラール化度）は、好ましくは６０モル％以上、より好ましくは６３モル％以上、好ましくは８５モル％以下、より好ましくは７５モル％以下、更に好ましくは７０モル％以下である。上記アセタール化度が上記下限以上であると、ポリビニルアセタール樹脂と可塑剤との相溶性が高くなる。上記アセタール化度が上記上限以下であると、ポリビニルアセタール樹脂を製造するために必要な反応時間が短くなる。
　上記アセタール化度は、アセタール基が結合しているエチレン基量を、主鎖の全エチレン基量で除算して求めたモル分率を百分率で示した値である。
　上記アセタール化度は、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法により、算出され得る。
　なお、上記水酸基の含有率（水酸基量）、アセタール化度（ブチラール化度）及びアセチル化度は、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法により測定された結果から算出することが好ましい。ポリビニルアセタール樹脂がポリビニルブチラール樹脂である場合は、上記水酸基の含有率（水酸基量）、上記アセタール化度（ブチラール化度）及び上記アセチル化度は、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠した方法により測定された結果から算出することが好ましい。
　（可塑剤）
　中間膜の接着力をより一層高める観点からは、上記第１の樹脂層は可塑剤を含むことが好ましく、上記第２の樹脂層は可塑剤を含むことが好ましい。上記第１，第２の樹脂層中の熱可塑性樹脂が、ポリビニルアセタール樹脂である場合に、上記第１，第２の樹脂層はそれぞれ、可塑剤を含むことが特に好ましい。
　上記可塑剤は特に限定されない。上記可塑剤として、従来公知の可塑剤を用いることができる。上記可塑剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記可塑剤としては、例えば、一塩基性有機酸エステル及び多塩基性有機酸エステル等の有機エステル可塑剤、並びに有機リン酸可塑剤及び有機亜リン酸可塑剤などのリン酸可塑剤等が挙げられる。なかでも、有機エステル可塑剤が好ましい。上記可塑剤は液状可塑剤であることが好ましい。
　上記一塩基性有機酸エステルとしては、特に限定されず、例えば、グリコールと一塩基性有機酸との反応によって得られたグリコールエステル、並びにトリエチレングリコール又はトリプロピレングリコールと一塩基性有機酸とのエステル等が挙げられる。上記グリコールとしては、トリエチレングリコール、テトラエチレングリコール及びトリプロピレングリコール等が挙げられる。上記一塩基性有機酸としては、酪酸、イソ酪酸、カプロン酸、２－エチル酪酸、ヘプチル酸、ｎ－オクチル酸、２－エチルヘキシル酸、ｎ－ノニル酸及びデシル酸等が挙げられる。
　上記多塩基性有機酸エステルとしては、特に限定されず、例えば、多塩基性有機酸と、炭素数４～８の直鎖又は分岐構造を有するアルコールとのエステル化合物が挙げられる。上記多塩基性有機酸としては、アジピン酸、セバシン酸及びアゼライン酸等が挙げられる。
　上記有機エステル可塑剤としては、特に限定されず、トリエチレングリコールジ－２－エチルブチレート、トリエチレングリコールジ－２－エチルヘキサノエート、トリエチレングリコールジカプリレート、トリエチレングリコールジ－ｎ－オクタノエート、トリエチレングリコールジ－ｎ－ヘプタノエート、テトラエチレングリコールジ－ｎ－ヘプタノエート、ジブチルセバケート、ジオクチルアゼレート、ジブチルカルビトールアジペート、エチレングリコールジ－２－エチルブチレート、１，３－プロピレングリコールジ－２－エチルブチレート、１，４－ブチレングリコールジ－２－エチルブチレート、ジエチレングリコールジ－２－エチルブチレート、ジエチレングリコールジ－２－エチルヘキサノエート、ジプロピレングリコールジ－２－エチルブチレート、トリエチレングリコールジ－２－エチルペンタノエート、テトラエチレングリコールジ－２－エチルブチレート、ジエチレングリコールジカプリレート、アジピン酸ジヘキシル、アジピン酸ジオクチル、アジピン酸ヘキシルシクロヘキシル、アジピン酸ヘプチルとアジピン酸ノニルとの混合物、アジピン酸ジイソノニル、アジピン酸ジイソデシル、アジピン酸ヘプチルノニル、セバシン酸ジブチル、油変性セバシン酸アルキド、及びリン酸エステルとアジピン酸エステルとの混合物等が挙げられる。これら以外の有機エステル可塑剤を用いてもよい。
　上記有機リン酸可塑剤としては、特に限定されず、例えば、トリブトキシエチルホスフェート、イソデシルフェニルホスフェート及びトリイソプロピルホスフェート等が挙げられる。
　上記可塑剤は、下記式（１）で表されるジエステル可塑剤であることが好ましい。
Figure JPOXMLDOC01-appb-C000001
　上記式（１）中、Ｒ１及びＲ２はそれぞれ、炭素数２～１０の有機基を表し、Ｒ３は、エチレン基、イソプロピレン基又はｎ－プロピレン基を表し、ｐは３～１０の整数を表す。上記式（１）中のＲ１及びＲ２はそれぞれ、炭素数５～１０の有機基であることが好ましく、炭素数６～１０の有機基であることがより好ましい。
　上記可塑剤は、トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）及びトリエチレングリコールジ－２－エチルブチレート（３ＧＨ）の内の少なくとも１種を含むことが好ましく、トリエチレングリコールジ－２－エチルヘキサノエートを含むことがより好ましい。
　上記可塑剤の含有量は特に限定されない。上記第１，第２の樹脂層において、上記熱可塑性樹脂１００重量部に対して、上記可塑剤の各含有量は、好ましくは２５重量部以上、より好ましくは３０重量部以上、更に好ましくは３５重量部以上、好ましくは７５重量部以下、より好ましくは６０重量部以下、更に好ましくは５０重量部以下、特に好ましくは４０重量部以下である。上記可塑剤の含有量が上記下限以上であると、合わせガラスの耐貫通性がより一層高くなる。上記可塑剤の含有量が上記上限以下であると、中間膜の透明性がより一層高くなる。
　（遮熱性化合物）
　成分Ｘ：
　上記第２の樹脂層は、遮熱性化合物を含むことが好ましい。上記第２の樹脂層は、フタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物の内の少なくとも１種の成分Ｘを含むことが好ましい。上記第２の樹脂層は、フタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物の内の少なくとも１種の成分Ｘを含むか、又は、後述する遮熱粒子を含むことが好ましい。上記第１の樹脂層は、上記成分Ｘを含んでいてもよい。上記成分Ｘは遮熱性化合物である。中間膜全体で少なくとも１層に上記成分Ｘを用いることにより、赤外線（熱線）を効果的に遮断できる。上記第２の樹脂層が上記成分Ｘを含むことにより、赤外線をより一層効果的に遮断できる。
　上記成分Ｘは特に限定されない。成分Ｘとして、従来公知のフタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物を用いることができる。上記成分Ｘは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記成分Ｘとしては、フタロシアニン、フタロシアニンの誘導体、ナフタロシアニン、ナフタロシアニンの誘導体、アントラシアニン及びアントラシアニンの誘導体等が挙げられる。上記フタロシアニン化合物及び上記フタロシアニンの誘導体はそれぞれ、フタロシアニン骨格を有することが好ましい。上記ナフタロシアニン化合物及び上記ナフタロシアニンの誘導体はそれぞれ、ナフタロシアニン骨格を有することが好ましい。上記アントラシアニン化合物及び上記アントラシアニンの誘導体はそれぞれ、アントラシアニン骨格を有することが好ましい。
　中間膜及び合わせガラスの遮熱性をより一層高くする観点からは、上記成分Ｘは、フタロシアニン、フタロシアニンの誘導体、ナフタロシアニン及びナフタロシアニンの誘導体からなる群から選択される少なくとも１種であることが好ましく、フタロシアニン及びフタロシアニンの誘導体の内の少なくとも１種であることがより好ましい。
　遮熱性を効果的に高め、かつ長期間にわたり可視光線透過率をより一層高いレベルで維持する観点からは、上記成分Ｘは、バナジウム原子又は銅原子を含有することが好ましい。上記成分Ｘは、バナジウム原子を含有することが好ましく、銅原子を含有することも好ましい。上記成分Ｘは、バナジウム原子又は銅原子を含有するフタロシアニン及びバナジウム原子又は銅原子を含有するフタロシアニンの誘導体の内の少なくとも１種であることがより好ましい。中間膜及び合わせガラスの遮熱性を更に一層高くする観点からは、上記成分Ｘは、バナジウム原子に酸素原子が結合した構造単位を有することが好ましい。
　上記第１の樹脂層又は上記第２の樹脂層が上記成分Ｘを含む場合に、上記第１，第２の樹脂層１００重量％中、上記成分Ｘの各含有量は、好ましくは０．００１重量％以上、より好ましくは０．００５重量％以上、更に好ましくは０．０１重量％以上、特に好ましくは０．０２重量％以上、好ましくは０．２重量％以下、より好ましくは０．１重量％以下、更に好ましくは０．０５重量％以下、特に好ましくは０．０４重量％以下である。上記第１，第２の樹脂層における上記成分Ｘの含有量が上記下限以上及び上記上限以下であると、遮熱性が充分に高くなり、かつ上記可視光線透過率が充分に高くなる。例えば、可視光線透過率を７０％以上にすることが可能である。
　遮熱粒子：
　上記第２の樹脂層は、遮熱粒子を含むことが好ましい。上記第１の樹脂層は、遮熱粒子を含んでいてもよい。遮熱粒子は遮熱性化合物である。中間膜全体で少なくとも１層に遮熱性化合物を用いることにより、赤外線（熱線）を効果的に遮断できる。上記第２の樹脂層が遮熱粒子を含むことにより、赤外線をより一層効果的に遮断できる。
　合わせガラスの遮熱性をより一層高める観点からは、上記遮熱粒子は、金属酸化物粒子であることがより好ましい。上記遮熱粒子は、金属の酸化物により形成された粒子（金属酸化物粒子）であることが好ましい。遮熱粒子は１種のみが用いられてもよく、２種以上が併用されてもよい。
　可視光よりも長い波長７８０ｎｍ以上の赤外線は、紫外線と比較して、エネルギー量が小さい。しかしながら、赤外線は熱的作用が大きく、赤外線が物質にいったん吸収されると熱として放出される。このため、赤外線は一般に熱線と呼ばれている。上記遮熱粒子の使用により、赤外線（熱線）を効果的に遮断できる。なお、遮熱粒子とは、赤外線を吸収可能な粒子を意味する。
　上記遮熱粒子の具体例としては、アルミニウムドープ酸化錫粒子、インジウムドープ酸化錫粒子、アンチモンドープ酸化錫粒子（ＡＴＯ粒子）、ガリウムドープ酸化亜鉛粒子（ＧＺＯ粒子）、インジウムドープ酸化亜鉛粒子（ＩＺＯ粒子）、アルミニウムドープ酸化亜鉛粒子（ＡＺＯ粒子）、ニオブドープ酸化チタン粒子、ナトリウムドープ酸化タングステン粒子、セシウムドープ酸化タングステン粒子、タリウムドープ酸化タングステン粒子、ルビジウムドープ酸化タングステン粒子、錫ドープ酸化インジウム粒子（ＩＴＯ粒子）、錫ドープ酸化亜鉛粒子、珪素ドープ酸化亜鉛粒子等の金属酸化物粒子や、六ホウ化ランタン（ＬａＢ６）粒子等が挙げられる。これら以外の遮熱粒子を用いてもよい。なかでも、熱線の遮蔽機能が高いため、金属酸化物粒子が好ましく、ＡＴＯ粒子、ＧＺＯ粒子、ＩＺＯ粒子、ＩＴＯ粒子又は酸化タングステン粒子がより好ましく、ＩＴＯ粒子又は酸化タングステン粒子が特に好ましい。特に、熱線の遮蔽機能が高く、かつ入手が容易であるので、錫ドープ酸化インジウム粒子（ＩＴＯ粒子）が好ましく、酸化タングステン粒子も好ましい。
　上記酸化タングステン粒子は、下記式（Ｘ１）又は下記式（Ｘ２）で一般に表される。上記中間膜では、下記式（Ｘ１）又は下記式（Ｘ２）で表される酸化タングステン粒子が好適に用いられる。
　ＷｙＯｚ　　・・・式（Ｘ１）
　上記式（Ｘ１）において、Ｗはタングステン、Ｏは酸素を表し、ｙ及びｚは２．０＜ｚ／ｙ＜３．０を満たす。
　ＭｘＷｙＯｚ　　・・・式（Ｘ２）
　上記式（Ｘ２）において、Ｍは、Ｈ、Ｈｅ、アルカリ金属、アルカリ土類金属、希土類元素、Ｍｇ、Ｚｒ、Ｃｒ、Ｍｎ、Ｆｅ、Ｒｕ、Ｃｏ、Ｒｈ、Ｉｒ、Ｎｉ、Ｐｄ、Ｐｔ、Ｃｕ、Ａｇ、Ａｕ、Ｚｎ、Ｃｄ、Ａｌ、Ｇａ、Ｉｎ、Ｔｌ、Ｓｉ、Ｇｅ、Ｓｎ、Ｐｂ、Ｓｂ、Ｂ、Ｆ、Ｐ、Ｓ、Ｓｅ、Ｂｒ、Ｔｅ、Ｔｉ、Ｎｂ、Ｖ、Ｍｏ、Ｔａ及びＲｅからなる群から選択される少なくとも１種の元素、Ｗはタングステン、Ｏは酸素を表し、ｘ、ｙ及びｚは、０．００１≦ｘ／ｙ≦１、及び２．０＜ｚ／ｙ≦３．０を満たす。
　中間膜及び合わせガラスの遮熱性をより一層高くする観点からは、酸化タングステン粒子は、金属ドープ酸化タングステン粒子であることが好ましい。上記「酸化タングステン粒子」には、金属ドープ酸化タングステン粒子が含まれる。上記金属ドープ酸化タングステン粒子としては、具体的には、ナトリウムドープ酸化タングステン粒子、セシウムドープ酸化タングステン粒子、タリウムドープ酸化タングステン粒子及びルビジウムドープ酸化タングステン粒子等が挙げられる。
　中間膜及び合わせガラスの遮熱性をより一層高くする観点からは、セシウムドープ酸化タングステン粒子が特に好ましい。中間膜及び合わせガラスの遮熱性を更に一層高くする観点からは、該セシウムドープ酸化タングステン粒子は、式：Ｃｓ０．３３ＷＯ３で表される酸化タングステン粒子であることが好ましい。
　上記遮熱粒子の平均粒子径は好ましくは０．０１μｍ以上、より好ましくは０．０２μｍ以上、好ましくは０．１μｍ以下、より好ましくは０．０５μｍ以下である。平均粒子径が上記下限以上であると、熱線の遮蔽性が充分に高くなる。平均粒子径が上記上限以下であると、遮熱粒子の分散性が高くなる。
　上記「平均粒子径」は、体積平均粒子径を示す。平均粒子径は、粒度分布測定装置（日機装社製「ＵＰＡ－ＥＸ１５０」）等を用いて測定できる。
　上記第１の樹脂層又は上記第２の樹脂層が上記遮熱粒子を含む場合に、上記第１，第２の樹脂層１００重量％中、遮熱粒子の各含有量は、好ましくは０．０１重量％以上、より好ましくは０．１重量％以上、更に好ましくは１重量％以上、特に好ましくは１．５重量％以上、好ましくは６重量％以下、より好ましくは５．５重量％以下、更に好ましくは４重量％以下、特に好ましくは３．５重量％以下、最も好ましくは３．０重量％以下である。上記遮熱粒子の含有量が上記下限以上及び上記上限以下であると、遮熱性が充分に高くなり、かつ上記可視光線透過率が充分に高くなる。
　上記第１の樹脂層又は上記第２の樹脂層が上記遮熱粒子を含む場合に、上記第１，第２の樹脂層は、上記遮熱粒子を０．１～１２ｇ／ｍ２の割合で含有することが好ましい。上記遮熱粒子の割合が上記範囲内である場合には、遮熱性が充分に高くなり、かつ上記可視光線透過率が充分に高くなる。上記遮熱粒子の割合は、好ましくは０．５ｇ／ｍ２以上、より好ましくは０．８ｇ／ｍ２以上、更に好ましくは１．５ｇ／ｍ２以上、特に好ましくは３ｇ／ｍ２以上、好ましくは１１ｇ／ｍ２以下、より好ましくは１０ｇ／ｍ２以下、更に好ましくは９ｇ／ｍ２以下、特に好ましくは７ｇ／ｍ２以下である。上記割合が上記下限以上であると、遮熱性がより一層高くなる。上記割合が上記上限以下であると、上記可視光線透過率がより一層高くなる。
　（紫外線遮蔽剤）
　上記第１の樹脂層は、紫外線遮蔽剤を含むことが好ましい。上記第２の樹脂層は、紫外線遮蔽剤を含むことが好ましい。上記第１の樹脂層と上記第２の樹脂層との双方が、紫外線遮蔽剤を含むことがより好ましい。紫外線遮蔽剤の使用により、中間膜及び合わせガラスが長期間使用されても、可視光線透過率がより一層低下し難くなる。該紫外線遮蔽剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記紫外線遮蔽剤には、紫外線吸収剤が含まれる。紫外線遮蔽剤は、紫外線吸収剤であることが好ましい。
　従来広く知られている一般的な紫外線遮蔽剤としては、例えば、金属系紫外線遮蔽剤、金属酸化物系紫外線遮蔽剤、ベンゾトリアゾール系紫外線遮蔽剤（ベンゾトリアゾール化合物）、ベンゾフェノン系紫外線遮蔽剤（ベンゾフェノン化合物）、トリアジン系紫外線遮蔽剤（トリアジン化合物）、マロン酸エステル系紫外線遮蔽剤（マロン酸エステル化合物）、シュウ酸アニリド系紫外線遮蔽剤（シュウ酸アニリド化合物）及びベンゾエート系紫外線遮蔽剤（ベンゾエート化合物）等が挙げられる。
　上記金属系紫外線遮蔽剤としては、例えば、白金粒子、白金粒子の表面をシリカで被覆した粒子、パラジウム粒子及びパラジウム粒子の表面をシリカで被覆した粒子等が挙げられる。紫外線遮蔽剤は、遮熱粒子ではないことが好ましい。
　上記金属酸化物系紫外線遮蔽剤としては、例えば、酸化亜鉛、酸化チタン及び酸化セリウム等が挙げられる。さらに、上記金属酸化物系紫外線遮蔽剤として、表面が被覆されていてもよい。上記金属酸化物系紫外線遮蔽剤の表面の被覆材料としては、絶縁性金属酸化物、加水分解性有機ケイ素化合物及びシリコーン化合物等が挙げられる。
　上記絶縁性金属酸化物としては、シリカ、アルミナ及びジルコニア等が挙げられる。上記絶縁性金属酸化物は、例えば５．０ｅＶ以上のバンドギャップエネルギーを有する。
　上記ベンゾトリアゾール系紫外線遮蔽剤としては、例えば、２－（２’－ヒドロキシ－５’－メチルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「ＴｉｎｕｖｉｎＰ」）、２－（２’－ヒドロキシ－３’，５’－ジ－ｔ－ブチルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２０」）、２－（２’－ヒドロキシ－３’－ｔ－ブチル－５－メチルフェニル）－５－クロロベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２６」）、及び２－（２’－ヒドロキシ－３’，５’－ジ－アミルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２８」）等のベンゾトリアゾール系紫外線遮蔽剤が挙げられる。紫外線を吸収する性能に優れることから、上記ベンゾトリアゾール系紫外線遮蔽剤はハロゲン原子を含むベンゾトリアゾール系紫外線遮蔽剤であることが好ましく、塩素原子を含むベンゾトリアゾール系紫外線遮蔽剤であることがより好ましい。
　上記ベンゾフェノン系紫外線遮蔽剤としては、例えば、オクタベンゾン（ＢＡＳＦ社製「Ｃｈｉｍａｓｓｏｒｂ８１」）等が挙げられる。
　上記トリアジン系紫外線遮蔽剤としては、例えば、２－（４，６－ジフェニル－１，３，５－トリアジン－２－イル）－５－［（ヘキシル）オキシ］－フェノール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ１５７７ＦＦ」）等が挙げられる。
　上記マロン酸エステル系紫外線遮蔽剤としては、２－（ｐ－メトキシベンジリデン）マロン酸ジメチル、テトラエチル－２，２－（１，４－フェニレンジメチリデン）ビスマロネート、２－（ｐ－メトキシベンジリデン）－ビス（１，２，２，６，６－ペンタメチル４－ピペリジニル）マロネート等が挙げられる。
　上記マロン酸エステル系紫外線遮蔽剤の市販品としては、Ｈｏｓｔａｖｉｎ　Ｂ－ＣＡＰ、Ｈｏｓｔａｖｉｎ　ＰＲ－２５、Ｈｏｓｔａｖｉｎ　ＰＲ－３１（いずれもクラリアント社製）が挙げられる。
　上記シュウ酸アニリド系紫外線遮蔽剤としては、Ｎ－（２－エチルフェニル）－Ｎ’－（２－エトキシ－５－ｔ－ブチルフェニル）シュウ酸ジアミド、Ｎ－（２－エチルフェニル）－Ｎ’－（２－エトキシ－フェニル）シュウ酸ジアミド、２－エチル－２’－エトキシ－オキシアニリド（クラリアント社製「ＳａｎｄｕｖｏｒＶＳＵ」）などの窒素原子上に置換されたアリール基などを有するシュウ酸ジアミド類が挙げられる。
　上記ベンゾエート系紫外線遮蔽剤としては、例えば、２，４－ジ－ｔｅｒｔ－ブチルフェニル－３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシベンゾエート（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ１２０」）等が挙げられる。
　中間膜及び合わせガラスの経時後の可視光線透過率の低下を抑制するために、上記紫外線遮蔽剤は、２－（２’－ヒドロキシ－３’－ｔ－ブチル－５－メチルフェニル）－５－クロロベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２６」）、又は２－（２’－ヒドロキシ－３’，５’－ジ－アミルフェニル）ベンゾトリアゾール（ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２８」）であることが好ましく、２－（２’－ヒドロキシ－３’－ｔ－ブチル－５－メチルフェニル）－５－クロロベンゾトリアゾールであってもよい。
　上記第１，第２の樹脂層が上記紫外線遮蔽剤を含む場合に、上記第１，第２の樹脂層１００重量％中、紫外線遮蔽剤の各含有量は、好ましくは０．１重量％以上、より好ましくは０．２重量％以上、更に好ましくは０．３重量％以上、特に好ましくは０．５重量％以上、好ましくは２．５重量％以下、より好ましくは２重量％以下、更に好ましくは１重量％以下、特に好ましくは０．８重量％以下である。上記紫外線遮蔽剤の含有量が上記下限以上及び上記上限以下であると、経時後の可視光線透過率の低下がより一層抑えられる。特に、上記第１，第２の樹脂層１００重量％中、紫外線遮蔽剤の含有量が０．２重量％以上であることにより、中間膜及び合わせガラスの経時後の可視光線透過率の低下を顕著に抑制できる。
　（酸化防止剤）
　上記第１の樹脂層は、酸化防止剤を含むことが好ましい。上記第２の樹脂層は、酸化防止剤を含むことが好ましい。上記第１の樹脂層と上記第２の樹脂層との双方が酸化防止剤を含むことが好ましい。該酸化防止剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記酸化防止剤としては、フェノール系酸化防止剤、硫黄系酸化防止剤及びリン系酸化防止剤等が挙げられる。上記フェノール系酸化防止剤はフェノール骨格を有する酸化防止剤である。上記硫黄系酸化防止剤は硫黄原子を含有する酸化防止剤である。上記リン系酸化防止剤はリン原子を含有する酸化防止剤である。
　上記酸化防止剤は、フェノール系酸化防止剤又はリン系酸化防止剤であることが好ましい。
　上記フェノール系酸化防止剤としては、２，６－ジ－ｔ－ブチル－ｐ－クレゾール（ＢＨＴ）、ブチル化ヒドロキシアニソール（ＢＨＡ）、２，６－ジ－ｔ－ブチル－４－エチルフェノール、ステアリル－β－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオネート、２，２’－メチレンビス－（４－メチル－６－ブチルフェノール）、２，２’－メチレンビス－（４－エチル－６－ｔ－ブチルフェノール）、４，４’－ブチリデン－ビス－（３－メチル－６－ｔ－ブチルフェノール）、１，１，３－トリス－（２－メチル－ヒドロキシ－５－ｔ－ブチルフェニル）ブタン、テトラキス［メチレン－３－（３’，５’－ブチル－４－ヒドロキシフェニル）プロピオネート］メタン、１，３，３－トリス－（２－メチル－４－ヒドロキシ－５－ｔ－ブチルフェノール）ブタン、１，３，５－トリメチル－２，４，６－トリス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）ベンゼン、ビス（３，３’－ｔ－ブチルフェノール）ブチリックアッシドグリコールエステル及びビス（３－ｔ－ブチル－４－ヒドロキシ－５－メチルベンゼンプロパン酸）エチレンビス（オキシエチレン）等が挙げられる。これらの酸化防止剤の内の１種又は２種以上が好適に用いられる。
　上記リン系酸化防止剤としては、トリデシルホスファイト、トリス（トリデシル）ホスファイト、トリフェニルホスファイト、トリノニルフェニルホスファイト、ビス（トリデシル）ペンタエリスリトールジホスファイト、ビス（デシル）ペンタエリスリトールジホスファイト、トリス（２，４－ジ－ｔ－ブチルフェニル）ホスファイト、ビス（２，４－ジ－ｔ－ブチル－６－メチルフェニル）エチルエステル亜リン酸、トリス（２，４－ジ－ｔ－ブチルフェニル）ホスファイト、及び２，２’－メチレンビス（４，６－ジ－ｔ－ブチル－１－フェニルオキシ）（２－エチルヘキシルオキシ）ホスホラス等が挙げられる。これらの酸化防止剤の内の１種又は２種以上が好適に用いられる。
　上記酸化防止剤の市販品としては、例えばＢＡＳＦ社製「ＩＲＧＡＮＯＸ　２４５」、ＢＡＳＦ社製「ＩＲＧＡＦＯＳ　１６８」、ＢＡＳＦ社製「ＩＲＧＡＦＯＳ　３８」、住友化学工業社製「スミライザーＢＨＴ」、並びにチバガイギー社製「イルガノックス１０１０」等が挙げられる。
　上記第１，第２の樹脂層が上記酸化防止剤を含む場合に、上記第１，第２の樹脂層１００重量％中、酸化防止剤の各含有量は、好ましくは０．１重量％以上、好ましくは２重量％以下、より好ましくは１．８重量％以下である。上記酸化防止剤の含有量が上記下限以上であると、中間膜及び合わせガラスの高い可視光線透過率がより一層長期間に渡り維持される。上記酸化防止剤の含有量が上記上限以下であると、添加効果を得るために過剰な酸化防止剤が生じ難くなる。
　（接着力調整剤）
　上記第１の樹脂層と上記第２の樹脂層との内の少なくとも一方が、接着力調整剤を含むことが好ましい。上記第１の樹脂層は、接着力調整剤を含むことが好ましい。上記第２の樹脂層は、接着力調整剤を含むことが好ましい。上記第１の樹脂層と上記第２の樹脂層との双方が、接着力調整剤を含むことがより好ましい。接着力調整剤の使用により、中間膜とガラスの接着性が制御され、耐貫通性に優れた合わせガラスが得られる。さらに、耐貫通性の試験として、落球試験を行った場合に、上記第１の樹脂層及び上記第２の樹脂層が接着力調整剤を含むことにより、合わせガラスのガラスの破片を小さくすることができるという効果が得られる。特に、接着力調整剤が金属塩であると、合わせガラスのガラスの破片がより一層小さくなる。上記接着力調整剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記接着力調整剤は特に限定されず、金属塩であることが好ましく、アルカリ金属塩、アルカリ土類金属塩及びＭｇ塩からなる群から選択された少なくとも１種の金属塩であることが好ましい。上記金属塩は、Ｋ及びＭｇの内の少なくとも１種の金属を含むことが好ましい。上記金属塩は、炭素数２～１６の有機酸のアルカリ金属塩又は炭素数２～１６の有機酸のアルカリ土類金属塩であることがより好ましく、炭素数２～１６のカルボン酸マグネシウム塩又は炭素数２～１６のカルボン酸カリウム塩であることが更に好ましい。上記炭素数２～１６のカルボン酸マグネシウム塩及び上記炭素数２～１６のカルボン酸カリウム塩としては特に限定されないが、例えば、酢酸マグネシウム、酢酸カリウム、プロピオン酸マグネシウム、プロピオン酸カリウム１９、２－エチルブタン酸マグネシウム、２－エチルブタン酸カリウム、２－エチルヘキサン酸マグネシウム及び２－エチルヘキサン酸カリウム等が挙げられる。
　上記接着力調整剤の含有量は特に限定されない。上記第１の樹脂層及び上記第２の樹脂層において、上記熱可塑性樹脂１００重量部に対して、上記接着力調整剤の各含有量は、好ましい下限が０．０００５重量部、好ましい上限が０．０５重量部である。上記接着力調整剤の含有量が０．０００５重量部以上であると、合わせガラスの耐貫通性が高くなる。上記接着力調整剤の含有量が０．０５重量部以下であると、合わせガラス用中間膜の透明性がより一層高くなる。上記接着力調整剤の含有量のより好ましい下限は０．００２重量部、より好ましい上限は０．０２重量部である。また、第１，第２の樹脂層が２層以上の積層構造を有する場合に、合わせガラス部材に接する表面層において、並びに第１，第２の樹脂層が単層構造を有する場合に、第１，第２の樹脂層において、上記熱可塑性樹脂１００重量部に対して、上記接着力調整剤の含有量は、好ましい下限が０．０００５重量部、好ましい上限が０．０５重量部である。
　第１の樹脂層の耐湿性が高くなることから、第１，２の樹脂層中のアルカリ金属、アルカリ土類金属及びＭｇの各含有量の合計は３００ｐｐｍ以下であることが好ましい。例えば、上記アルカリ金属、アルカリ土類金属及びＭｇは、上記接着力調整剤に由来する金属として含んでもよく、ポリビニルアセタール樹脂を合成する際に用いる中和剤に由来する金属として含んでもよい。第１，２の樹脂層中のアルカリ金属、アルカリ土類金属及びＭｇの含有量の合計は２００ｐｐｍ以下であることがより好ましく、１５０ｐｐｍ以下であることが更に好ましく、１００ｐｐｍ以下であることが特に好ましい。また、第１，第２の樹脂層が２層以上の積層構造を有する場合に、合わせガラス部材に接する表面層において、並びに第１，第２の樹脂層が単層構造を有する場合に、第１，第２の樹脂層において、アルカリ金属、アルカリ土類金属及びＭｇの含有量の合計は、３００ｐｐｍ以下であることが好ましく、２００ｐｐｍ以下であることがより好ましく、１５０ｐｐｍ以下であることが更に好ましく、１００ｐｐｍ以下であることが特に好ましい。
　（他の成分）
　上記合わせガラス用中間膜は、必要に応じて、光安定剤、難燃剤、帯電防止剤、顔料、染料、耐湿剤及び蛍光増白剤等の添加剤を含んでいてもよい。これらの添加剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　（合わせガラス用中間膜の他の詳細）
　上記合わせガラス用中間膜は、第１の合わせガラス部材と第２の合わせガラス部材との間に配置されて用いられる。
　上記合わせガラス用中間膜は、建築物又は車両において、外部空間（第１の空間）と該外部空間から熱線が入射される内部空間（第２の空間）との間の開口部に取り付ける合わせガラスを得るために用いられることが好ましい。この場合に、上記第１，第２の樹脂層のうち、上記第１の樹脂層が上記外部空間側に位置するように配置されることが好ましい。
　上記合わせガラス用中間膜の厚みは特に限定されない。実用面の観点、並びに遮熱性を充分に高める観点からは、中間膜の厚みは、好ましくは０．１ｍｍ以上、より好ましくは０．２５ｍｍ以上、好ましくは３ｍｍ以下、より好ましくは１．５ｍｍ以下である。中間膜の厚みが上記下限以上であると、合わせガラスの耐貫通性が高くなる。
　上記赤外線反射層の厚みは、好ましくは０．０１ｍｍ以上、より好ましくは０．０４ｍｍ以上、更に好ましくは０．０７ｍｍ以上、好ましくは０．３ｍｍ以下、より好ましくは０．２ｍｍ以下、更に好ましくは０．１８ｍｍ以下、特に好ましくは０．１６ｍｍ以下である。上記赤外線反射層の厚みが上記下限以上であると、合わせガラスの遮熱性がより一層高くなる。上記赤外線反射層の厚みが上記上限以下であると、合わせガラスの透明性がより一層高くなる。
　上記第１，第２の樹脂層の厚みはそれぞれ、好ましくは０．１ｍｍ以上、より好ましくは０．２ｍｍ以上、更に好ましくは０．２５ｍｍ以上、特に好ましくは０．３ｍｍ以上、好ましくは１．０ｍｍ以下、より好ましくは０．６ｍｍ以下、より一層好ましくは０．５ｍｍ以下、更に好ましくは０．４５ｍｍ以下、特に好ましくは０．４ｍｍ以下である。上記第１，第２の樹脂層の厚みが上記下限以上であると、合わせガラスの耐貫通性がより一層高くなる。上記第１，第２の樹脂層の厚みが上記上限以下であると、合わせガラスの透明性がより一層高くなる。
　上記中間膜の製造方法は特に限定されない。該中間膜の製造方法として、従来公知の方法を用いることができる。例えば、上述した各成分を混練し、中間膜を成形する製造方法等が挙げられる。連続的な生産に適しているため、押出成形する製造方法が好ましい。特に、上記第１，第２の樹脂層は、押出成形により形成することが好ましい。
　上記混練の方法は特に限定されない。この方法として、例えば、押出機、プラストグラフ、ニーダー、バンバリーミキサー又はカレンダーロール等を用いる方法が挙げられる。なかでも、連続的な生産に適しているため、押出機を用いる方法が好適であり、二軸押出機を用いる方法がより好適である。
　なお、本発明に係る合わせガラス用中間膜を得る際に、第１の樹脂層と赤外線反射層と第２の樹脂層とを別々に作製した後、第１の樹脂層と赤外線反射層と第２の樹脂層とを積層して中間膜を得てもよく、積層する方法は特に限定されない。例えば積層する方法として、ヒートラミネート法等が挙げられる。
　また、第１の樹脂層と赤外線反射層と第２の樹脂層とを共押出により積層して中間膜を得てもよい。また、第１の樹脂層と赤外線反射層とを共押出にて作製した共押出物の赤外線反射層側に第２の樹脂層を積層して中間膜を得てもよい。第２の樹脂層と赤外線反射層とを共押出にて作製した共押出物の赤外線反射層側に第１の樹脂層を積層して中間膜を得てもよい。
　また、赤外線反射層の表面に、第１，第２の樹脂層を形成するための組成物を塗工して、第１，第２の樹脂層を形成して、中間膜を得てもよい。
　中間膜の製造効率が優れることから、第１の樹脂層と第２の樹脂層とが、同一のポリビニルアセタール樹脂を含むことが好ましく、同一のポリビニルアセタール樹脂及び同一の可塑剤を含むことがより好ましく、同一の樹脂組成物により形成されていることが更に好ましい。一方で、遮熱性をより一層高める観点からは、第１の樹脂層と第２の樹脂層とが、異なる樹脂組成物により形成されていることが好ましい。
　（合わせガラス）
　本発明に係る合わせガラスは、第１の合わせガラス部材と、第２の合わせガラス部材と、該第１，第２の合わせガラス部材の間に配置された中間膜とを備える。該中間膜が、上述した合わせガラス用中間膜である。上記中間膜における上記第１の樹脂層の外側に、上記第１の合わせガラス部材が配置されている。上記中間膜における上記第２の樹脂層の外側に上記第２の合わせガラス部材が配置されている。上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率は、上記第２の合わせガラス部材と上記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い。
　上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の上記赤外線透過率は、上記第１の合わせガラス部材と上記第１の樹脂層との２つの層の積層体の赤外線透過率である。上記第２の合わせガラス部材と上記第２の樹脂層との２つの層全体の上記赤外線透過率は、上記第２の合わせガラス部材と上記第２の樹脂層との２つの層の積層体の赤外線透過率である。
　従来、中間膜を用いた合わせガラスの遮熱性が低いことがあり、Ｔｔｓ（Ｔｏｔａｌ　ｓｏｌａｒ　ｅｎｅｒｇｙ　ｔｒａｎｓｍｉｔｔｅｄ　ｔｈｒｏｕｇｈ　ａ　ｇｌａｚｉｎｇ）が高いことがあった。さらに、従来の合わせガラスでは、低いＴｔｓと高い可視光線透過率（Ｖｉｓｉｂｌｅ　Ｔｒａｎｓｍｉｔｔａｎｃｅ）とを両立することは困難であるという問題があった。
　これに対して、上記合わせガラスが第１，第２の合わせガラス部材の間に配置された中間膜を備えており、該中間膜が上記赤外線反射層と上記第１，第２の樹脂層とを備えており、上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の合わせガラス部材と上記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い場合には、合わせガラスの遮熱性を高くすることができる。さらに、上記合わせガラスの可視光線透過率を高くすることができる。本発明では、遮熱性の指標であるＴｔｓが低い合わせガラスを得ることができ、更に上記可視光線透過率が高い合わせガラスを得ることができる。例えば、合わせガラスのＴｔｓを６０％以下にし、かつ可視光線透過率を６５％以上にすることができる。さらに、Ｔｔｓを５５％以下にすることもでき、Ｔｔｓを５０％以下にすることもでき、更に可視光線透過率を７０％以上にすることができる。
　また、上記合わせガラスでは、上述した構成が備えられているので、遮熱性の指標であるＴｄｓ（Ｓｏｌａｒ　Ｄｉｒｅｃｔ　Ｔｒａｎｓｍｉｔｔａｎｃｅ）を低くすることができる。例えば、合わせガラスのＴｄｓを５０％以下にすることができ、４５％以下にすることもでき、更に４０％以下にすることができ、更に３９％以下にすることができる。
　上記第１の合わせガラス部材と上記第１の樹脂層との２つの層は全体で、赤外線を比較的多く透過する。さらに、上記第１の合わせガラス部材と上記第１の樹脂層とを透過した多くの赤外線は、上記赤外線反射層に至る。上記赤外線反射層に至った赤外線は、上記赤外線反射層により反射される。また、上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の赤外線透過率が高いことから、上記赤外線反射層により反射された赤外線の多くは、上記第１の樹脂層と上記第１の合わせガラス部材とを透過する。この結果、中間膜に赤外線が入射された際の中間膜の温度上昇を抑制できる。このため、上記合わせガラス用中間膜の遮熱性が高くなり、更に耐光性に優れているので高い可視光線透過率を長期間に渡り維持できる。また、上記合わせガラスを建築物又は車両の開口部に取り付けることで、建築物又は車両の内部空間の温度上昇を効果的に抑制できる。
　一方で、仮に上記第１の合わせガラス部材と上記第１の樹脂層と上記赤外線反射層とを赤外線の一部が透過した場合には、透過した赤外線は、上記第２の樹脂層又は上記第２の合わせガラス部材に至る。上記第２の樹脂層と上記第２の合わせガラス部材との２つの層全体の赤外線透過率は比較的低いので、上記第２の樹脂層及び上記第２の合わせガラス部材は、赤外線の透過を効果的に遮断する。このため、合わせガラス全体を通過する熱線の量を低減できる。このことによっても、合わせガラスの遮熱性が高くなり、該合わせガラスを建築物又は車両の開口部に取り付けることで、建築物又は車両の内部空間の温度上昇を効果的に抑制できる。
　また、上記第２の樹脂層に至る赤外線の量を低減できる結果、上記第２の樹脂層の劣化を抑えることができ、合わせガラス全体での耐光性が高くなる。このため、高い可視光線透過率を長期間に渡り維持できる。さらに、上記第２の樹脂層が遮熱粒子などの遮熱性化合物を含む場合に、該遮熱性化合物の劣化も抑制でき、高い遮熱性を長期間に渡り維持できる。
　本発明に係る合わせガラスは、建築物又は車両において、外部空間と上記外部空間から熱線が入射される内部空間との間の開口部に取り付ける合わせガラスであることが好ましい。この場合に、上記第１，第２の合わせガラス部材のうち、上記第１の合わせガラス部材が上記外部空間側に位置するように配置されることが好ましい。
　図１に、本発明の一実施形態に係る合わせガラスの一例を断面図で示す。
　図１に示す合わせガラス１１は、中間膜１と、第１，第２の合わせガラス部材２１，２２とを備える。中間膜１は、第１，第２の合わせガラス部材２１，２２の間に挟み込まれている。中間膜１の第１の表面１ａに、第１の合わせガラス部材２１が積層されている。中間膜１の第１の表面１ａとは反対の第２の表面１ｂに、第２の合わせガラス部材２２が積層されている。中間膜１における第１の樹脂層３の外側の表面３ａに第１の合わせガラス部材２１が積層されている。中間膜１における第２の樹脂層４の外側の表面４ａに第２の合わせガラス部材２２が積層されている。
　上記第１の合わせガラス部材と上記第１の樹脂層との２つの層全体の上記赤外線透過率を、上記第２の合わせガラス部材と上記第２の樹脂層との２つの層全体の上記赤外線透過率よりも高くすることが容易であることから、上記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いか、又は、上記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いことが好ましい。この場合に、上記第１の樹脂層の上記赤外線透過率が、上記第２の樹脂層の上記赤外線透過率よりも高く、かつ、上記第１の合わせガラス部材の上記赤外線透過率が、上記第２の合わせガラス部材の上記赤外線透過率よりも高くてもよい。
　遮熱性をより一層効果的に高める観点からは、上記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いことが好ましい。
　遮熱性を更に一層効果的に高める観点からは、上記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、上記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いことが好ましい。
　上記第１，第２の合わせガラス部材としては、ガラス板及びＰＥＴ（ポリエチレンテレフタレート）フィルム等が挙げられる。上記合わせガラスには、２枚のガラス板の間に中間膜が挟み込まれている合わせガラスだけでなく、ガラス板とＰＥＴフィルム等との間に中間膜が挟み込まれている合わせガラスも含まれる。合わせガラスは、ガラス板を備えた積層体であり、少なくとも１枚のガラス板が用いられていることが好ましい。上記第１，第２の合わせガラス部材がそれぞれガラス板又はＰＥＴ（ポリエチレンテレフタレート）フィルムであり、かつ上記中間膜が、上記第１，第２の合わせガラス部材として、少なくとも１枚のガラス板を含むことが好ましい。上記第１，第２の合わせガラス部材の双方がガラス板であることが特に好ましい。
　上記ガラス板としては、無機ガラス及び有機ガラスが挙げられる。上記無機ガラスとしては、フロート板ガラス、熱線吸収板ガラス、熱線反射板ガラス、磨き板ガラス、型板ガラス、網入り板ガラス、線入り板ガラス及びグリーンガラス等が挙げられる。上記有機ガラスは、無機ガラスに代用される合成樹脂ガラスである。上記有機ガラスとしては、ポリカーボネート板及びポリ（メタ）アクリル樹脂板等が挙げられる。上記ポリ（メタ）アクリル樹脂板としては、ポリメチル（メタ）アクリレート板等が挙げられる。
　上記第１の合わせガラス部材及び上記第２の合わせガラス部材はそれぞれ、クリアガラス又は熱線吸収板ガラスであることが好ましい。赤外線透過率が高く、合わせガラスの遮熱性がより一層高くなることから、上記第１の合わせガラス部材は、クリアガラスであることが好ましい。赤外線透過率が低く、合わせガラスの遮熱性がより一層高くなることから、上記第２の合わせガラス部材は、熱線吸収板ガラスであることが好ましい。熱線吸収板ガラスは、グリーンガラスであることが好ましい。上記第１の合わせガラス部材が、クリアガラスであり、かつ上記第２の合わせガラス部材が熱線吸収板ガラスであることが好ましい。上記熱線吸収板ガラスは、ＪＩＳ　Ｒ３２０８に準拠した熱線吸収板ガラスである。
　上記第１，第２の合わせガラス部材の厚みは特に限定されないが、好ましくは１ｍｍ以上、好ましくは５ｍｍ以下である。上記合わせガラス部材がガラス板である場合に、該ガラス板の厚みは、好ましくは１ｍｍ以上、好ましくは５ｍｍ以下である。上記合わせガラス部材がＰＥＴフィルムである場合に、該ＰＥＴフィルムの厚みは、好ましくは０．０３ｍｍ以上、好ましくは０．５ｍｍ以下である。
　上記合わせガラスの製造方法は特に限定されない。例えば、上記第１，第２の合わせガラス部材の間に、上記中間膜を挟んで、押圧ロールに通したり、又はゴムバックに入れて減圧吸引したりして、第１，第２の合わせガラス部材と中間膜との間に残留する空気を脱気する。その後、約７０～１１０℃で予備接着して積層体を得る。次に、積層体をオートクレーブに入れたり、又はプレスしたりして、約１２０～１５０℃及び１～１．５ＭＰａの圧力で圧着する。このようにして、合わせガラスを得ることができる。
　上記合わせガラスは、自動車、鉄道車両、航空機、船舶及び建築物等に使用できる。上記合わせガラスは、建築用又は車両用の合わせガラスであることが好ましく、車両用の合わせガラスであることがより好ましい。上記合わせガラスは、これらの用途以外にも使用できる。上記合わせガラスは、自動車のフロントガラス、サイドガラス、リアガラス又はルーフガラス等に使用できる。遮熱性が高くかつ可視光線透過率が高いので、上記合わせガラスは、自動車に好適に用いられる。
　透明性により一層優れた合わせガラスを得る観点からは、合わせガラスの上記可視光線透過率は、好ましくは６０％以上、より好ましくは６５％以上、更に好ましくは７０％以上である。合わせガラスの可視光線透過率は、ＪＩＳ　Ｒ３２１１（１９９８）に準拠して測定できる。
　遮熱性により一層優れた合わせガラスを得る観点からは、合わせガラスの上記Ｔｔｓは、好ましくは６０％以下、より好ましくは５５％以下、更に好ましくは５３％以下、特に好ましくは５１％以下、最も好ましくは５０％以下である。上記Ｔｔｓは、ＩＳＯ　１３８３７に準拠して測定される。
　遮熱性により一層優れた合わせガラスを得る観点からは、合わせガラスの上記Ｔｄｓは、好ましくは５０％以下、より好ましくは４５％以下、更に好ましくは４３％以下、特に好ましくは４１％以下、最も好ましくは３９％以下である。上記Ｔｄｓは、ＩＳＯ　１３８３７に準拠して測定される。
　上記赤外線透過率（Ｔｉｒ）は、赤外線透過率を測定し、ＪＩＳ　Ｚ８７２２、及びＪＩＳ　Ｒ３１０６に記載の重価係数を用いて規格化することにより求められる。
　第１の合わせガラス部材と第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率Ｔ１は以下のように測定される。
　第１の合わせガラス部材と第１の樹脂層とクリアガラス（厚み２．５ｍｍ）とがこの順に積層された合わせガラスを作製する。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得る。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得る。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ１を算出する。
　第２の合わせガラス部材と第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率Ｔ２は以下のように測定される。
　第２の合わせガラス部材と第２の樹脂層とクリアガラス（厚み２．５ｍｍ）とがこの順に積層された合わせガラスを作製する。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得る。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得る。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ２を算出する。
　また、第１の樹脂層又は第２の樹脂層などの波長７８０～２１００ｎｍにおける赤外線透過率は、具体的には、以下のようにして測定される。
　第１の樹脂層又は第２の樹脂層（赤外線透過率の測定対象）などを２枚のクリアガラスの間に積層し、合わせガラスを作製する。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得る。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得る。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率を算出する。
　合わせガラスのヘーズ値は、好ましくは２％以下、より好ましくは１％以下、更に好ましくは０．５％以下、特に好ましくは０．４％以下である。合わせガラスのヘーズ値は、ＪＩＳ　Ｋ６７１４に準拠して測定できる。
　（合わせガラスの取り付け方法）
　本発明に係る合わせガラスの取り付け方法は、上述した合わせガラスを、建築物又は車両において外部空間と該外部空間から熱線が入射される内部空間との間の開口部に取り付ける方法である。
　具体的には、第１の合わせガラス部材が、外部空間側に位置するように、かつ第２の合わせガラス部材が、内部空間側に位置するように、合わせガラスを開口部に取り付ける。すなわち、外部空間／第１の合わせガラス部材／（他の層／）第１の樹脂層／（他の層／）赤外線反射層／（他の層／）第２の樹脂層／（他の層／）第２の合わせガラス部材／内部空間の順に配置されるように、合わせガラスを取り付ける。好ましくは、外部空間／第１の合わせガラス部材／第１の樹脂層／（他の層／）赤外線反射層／（他の層／）第２の樹脂層／第２の合わせガラス部材／内部空間の順に配置されることが好ましく、外部空間／第１の合わせガラス部材／（他の層／）第１の樹脂層／赤外線反射層／第２の樹脂層／（他の層／）第２の合わせガラス部材／内部空間の順に配置されることが好ましく、外部空間／第１の合わせガラス部材／第１の樹脂層／赤外線反射層／第２の樹脂層／第２の合わせガラス部材／内部空間の順に配置されることが好ましい。上記の配置形態には、外部空間と第１の合わせガラス部材との間に他の部材が配置されている場合が含まれ、内部空間と第２の合わせガラス部材との間に他の部材が配置されている場合が含まれる。
　上記積層構造において、上記他の層及び上記他の部材はそれぞれ存在していてもよく、存在していなくてもよい。外部空間から熱線を含む太陽光が合わせガラスに入射され、合わせガラスを通過した熱線を含む太陽光は内部空間に導かれる。上記のように合わせガラスを開口部に取り付けた場合には、第１の合わせガラス部材の外側の表面が熱線の入射面となる。また、第１の樹脂層に第２の樹脂層よりも早く熱線が入射する。
　以下、実施例を掲げて本発明を更に詳しく説明する。本発明は以下の実施例のみに限定されない。
　第１，第２の樹脂層を形成するために、以下の材料を用いた。
　熱可塑性樹脂：
　下記の表１に示すポリビニルブチラール樹脂ＰＶＢ１～ＰＶＢ７（いずれも、ｎ－ブチルアルデヒドによりアセタール化されているポリビニルブチラール樹脂（ＰＶＢ））を用意した。
Figure JPOXMLDOC01-appb-T000002
　可塑剤：
　３ＧＯ（トリエチレングリコールジ－２－エチルヘキサノエート）
　他の成分：
　ＢＨＴ（酸化防止剤、２，６－ジ－ｔ－ブチル－ｐ－クレゾール）
　Ｔ－４６０（２，４－ビス「２－ヒドロキシ－４－ブトキシフェニル］－６－（２，４－ジブトキシフェニル）－１，３－５－トリアジン、ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ４６０」）
　Ｔ－３２６（紫外線遮蔽剤、２－（２’－ヒドロキシ－３’－ｔ－ブチル－５－メチルフェニル）－５－クロロベンゾトリアゾール、ＢＡＳＦ社製「Ｔｉｎｕｖｉｎ３２６」）
　ＬＡＦ７０（紫外線遮蔽剤、トリアジン系紫外線遮蔽剤、ＡＤＥＫＡ社製「ＬＡ－Ｆ７０」）
　ＶＳＵ（紫外線遮蔽剤、２－エチル－２’－エトキシ－オキシアニリド、クラリアントジャパン社製「Ｓａｎｄｕｖｏｒ　ＶＳＵ」）
　ＰＲ２５（紫外線遮蔽剤、マロン酸［（４－メトキシフェニル）－メチレン］－ジメチルエステル、クラリアントジャパン社製「Ｈｏｓｔａｖｉｎ　ＰＲ－２５」）
　ＩＴＯ（ＩＴＯ粒子、錫ドープ酸化インジウム粒子）
　ＣＷＯ（ＣＷＯ粒子、セシウムドープ酸化タングステン（Ｃｓ０．３３ＷＯ３）粒子）
　４３Ｖ（成分Ｘ、フタロシアニン化合物、中心金属としてバナジウムを含有する、山田化学社製「ＮＩＲ－４３Ｖ」）
　ＳＧ－５Ａ１２５７（成分Ｘ、銅を含有するフタロシアニン化合物、住化カラー社製「ＢＬＵＥ　ＳＧ－５Ａ１２５７」）
　金属塩（接着力調整剤、酢酸マグネシウム四水和物）
　また、以下の赤外線反射層を用意した。
　ＸＩＲ－７５（金属箔付き樹脂フィルム、Ｓｏｕｔｈｗａｌｌ　Ｔｅｃｈｎｏｌｏｇｉｅｓ社製「ＸＩＲ－７５」）
　多層フィルム（３Ｍ、多層樹脂フィルム、住友スリーエム社製「マルチレイヤー　Ｎａｎｏ　８０Ｓ」）
　また、以下の合わせガラス部材（ガラス）を用意した。
　クリアガラス（縦１００ｃｍ×横１００ｃｍ×厚み２ｍｍ）
　グリーンガラス（ＪＩＳ　Ｒ３２０８に準拠した熱線吸収板ガラス、縦１００ｃｍ×横１００ｃｍ×厚み２ｍｍ）
　（樹脂層Ａ１の作製）
　ポリビニルブチラール樹脂（ＰＶＢ１）１００重量部に対し、可塑剤（３ＧＯ）４０重量部と、紫外線遮蔽剤（Ｔ－３２６）０．８重量部と、酸化防止剤（ＢＨＴ）０．２重量部と、酢酸マグネシウム四水和物を得られる樹脂層Ａ１中で金属元素濃度が４５．６ｐｐｍとなる量とを添加し、ミキシングロールで充分に混練し、組成物を得た。
　得られた組成物を押出機により押出して、厚み３８０μｍの単層の樹脂層Ａ１を得た。
　（樹脂層Ａ２～Ａ１０の作製）
　配合成分の種類及び配合量を下記の表２に示すように設定したこと以外は樹脂層Ａ１と同様にして、厚み３８０μｍの単層の樹脂層Ａ２～Ａ１０を得た。
Figure JPOXMLDOC01-appb-T000003
　（樹脂層Ｂ１の作製）
　可塑剤（３ＧＯ）４０重量部と、ＩＴＯを得られる樹脂層Ｂ１中で０．３９重量％となる量とを添加し、充分に混練し、可塑剤分散液を得た。ポリビニルブチラール樹脂（ＰＶＢ１）１００重量部に対し、可塑剤分散液全量と、酸化防止剤（ＢＨＴ）０．２重量部と、酢酸マグネシウム四水和物を得られる樹脂層Ｂ１中で金属元素濃度が９４．３ｐｐｍとなる量とを添加し、ミキシングロールで充分に混練し、組成物を得た。
　得られた組成物を押出機により押出して、厚み３８０μｍの単層の樹脂層Ｂ１を得た。
　（樹脂層Ｂ２～Ｂ２８の作製）
　配合成分の種類及び含有量を下記の表３に示すように設定したこと以外は樹脂層Ｂ１と同様にして、厚み３８０μｍの単層の樹脂層Ｂ２～Ｂ２８を作製した。
　なお、上記表２及び下記の表３において、ＰＶＢ１、３ＧＯ、ＢＨＴ、Ｔ－３２６、Ｔ－４６０、ＬＡＦ７０、ＶＳＵ及びＰＲ２５の配合量は、ポリビニルブチラール樹脂（ＰＶＢ）１００重量部に対する配合量（重量部）を示す。ＩＴＯ、ＣＷＯ、４３Ｖ及びＳＧ－５Ａ１２５７の配合量は、樹脂層１００重量％中での配合量（重量％）を示す。金属塩の配合量は、樹脂層中での金属元素濃度を示す。
Figure JPOXMLDOC01-appb-T000004
　（実施例１）
　（１）合わせガラス用中間膜の作製
　赤外線反射層として、ＸＩＲ－７５（金属箔付き樹脂フィルム、Ｓｏｕｔｈｗａｌｌ　Ｔｅｃｈｎｏｌｏｇｉｅｓ社製「ＸＩＲ－７５」）を用意した。
　用意したＸＩＲ－７５を赤外線反射層として用いて、該赤外線反射層を得られた樹脂層Ａ１と得られた樹脂層Ｂ３との間に挟み込んで、中間膜を得た。
　（２）合わせガラスの作製
　得られた中間膜を、縦３０ｃｍ×横３０ｃｍの大きさに切断した。また、１枚のクリアガラス（縦３０ｃｍ×横３０ｃｍ×厚み２ｍｍ）と、１枚のグリーンガラス（ＪＩＳ　Ｒ３２０８に準拠した熱線吸収板ガラス、縦３０ｃｍ×横３０ｃｍ×厚み２ｍｍ）とを用意した。このクリアガラスとグリーンガラスとの間に、得られた中間膜を挟み込み、真空ラミネーターにて９０℃で３０分間保持し、真空プレスし、積層体を得た。積層体において、ガラス板からはみ出た中間膜部分を切り落とし、合わせガラスを得た。
　（実施例２～４４）
　第１，第２の樹脂層の種類、赤外線反射層の種類、並びに第１，第２の合わせガラス部材（ガラス）の種類を下記の表４に示すように設定したこと以外は実施例１と同様にして、中間膜及び合わせガラスを作製した。
　（比較例１）
　赤外線反射層を用いずに、得られた樹脂層Ａ１と得られた樹脂層Ａ１とを積層して、中間膜を得た。得られた中間膜を用いたこと以外は実施例１と同様にして、合わせガラスを得た。
　（比較例２）
　実施例１と同じ赤外線反射層を、得られた樹脂層Ａ１と得られた樹脂層Ａ１との間に挟み込んで、中間膜を得た。得られた中間膜を用いたこと、並びに第２の合わせガラス部材としてクリアガラスを用いたこと以外は実施例１と同様にして、合わせガラスを得た。
　（比較例３）
　赤外線反射層として、多層フィルム（３Ｍ、多層樹脂フィルム、住友スリーエム社製「マルチレイヤー　Ｎａｎｏ　８０Ｓ」）を用意した。
　用意した多層フィルムを単独で赤外線反射層として用いて、該赤外線反射層を、得られた樹脂層Ａ１と得られた樹脂層Ａ１との間に挟み込んで、中間膜を得た。得られた中間膜を用いたこと、並びに第２の合わせガラス部材としてクリアガラスを用いたこと以外は実施例１と同様にして、合わせガラスを得た。
　（比較例４）
　赤外線反射層として、多層フィルム（３Ｍ、多層樹脂フィルム、住友スリーエム社製「マルチレイヤー　Ｎａｎｏ　８０Ｓ」）を用意した。
　用意した多層フィルムを単独で赤外線反射層として用いて、該赤外線反射層を、得られた樹脂層Ａ１と得られた樹脂層Ａ１との間に挟み込んで、中間膜を得た。得られた中間膜を用いたこと、並びに第１の合わせガラス部材をグリーンガラスに変更したこと以外は実施例１と同様にして、合わせガラスを得た。
　（評価）
　（１）可視光線透過率（Ａ光Ｙ値、Ａ－Ｙ（３８０～７８０ｎｍ））の測定
　分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３２１１（１９９８）に準拠して、得られた合わせガラスの波長３８０～７８０ｎｍにおける上記可視光線透過率を測定した。
　（２）Ｔｄｓ（ｄｉｒｅｃｔ　ｓｏｌａｒ　ｅｎｅｒｇｙ　ｔｒａｎｓｍｉｔｔｅｄ　ｔｈｒｏｕｇｈ　ａ　ｇｌａｚｉｎｇ）の測定
　分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＩＳＯ　１３８３７に準拠して、得られた合わせガラスの波長３００～２５００ｎｍでのＴｄｓを測定した。
　（３）Ｔｔｓ（Ｔｏｔａｌ　ｓｏｌａｒ　ｅｎｅｒｇｙ　ｔｒａｎｓｍｉｔｔｅｄ　ｔｈｒｏｕｇｈ　ａ　ｇｌａｚｉｎｇ）の測定
　ＩＳＯ　１３８３７に準拠して、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、波長３００～２５００ｎｍの透過率／反射率を測定して、Ｔｔｓを算出した。
　（４）耐貫通性
　得られた合わせガラス（縦３０ｃｍ×横３０ｃｍ）を、表面温度が２３℃となるように調整した。次いで、ＪＩＳ　Ｒ３２１２に準拠して、５ｍの高さから、６枚の合わせガラスに対してそれぞれ、質量２２６０ｇ及び直径８２ｍｍの剛球を、合わせガラスの中心部分に落下させた。６枚の合わせガラス全てについて、剛球が衝突した後５秒以内に剛球が貫通しなかった場合を合格（○）とした。剛球が衝突した後５秒以内に剛球が貫通しなかった合わせガラスが３枚以下であった場合は不合格（×）とした。４枚の場合には、新しく６枚の合わせガラスの耐貫通性を評価した。５枚の場合には、新しく１枚の合わせガラスを追加試験し、剛球が衝突した後５秒以内に剛球が貫通しなかった場合を合格とした。同様の方法で、５ｍ及び６ｍ及び７ｍの高さから、６枚の合わせガラスに対してそれぞれ、質量２２６０ｇ及び直径８２ｍｍの剛球を、合わせガラスの中心部分に落下させ、合わせガラスの耐貫通性を評価した。なお、金属塩を含まない樹脂層を用いた実施例３５及び３６については、他の実施例と比較して、ガラスの破片が大きくなる傾向があった。
　合わせガラスの積層構成及び評価結果を下記の表４，５に示す。また、下記の表５の赤外線透過率の「２つの層」の欄には、第１の合わせガラス部材と第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率をＴ１、第２の合わせガラス部材と第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率をＴ２としたときに、Ｔ１とＴ２との関係を記載した。下記の表５の赤外線透過率の「樹脂層」の欄には、第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率をＴｘ１、第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率をＴｘ２としたときに、Ｔｘ１とＴｘ２との関係を記載した。下記の表５の赤外線透過率の「合わせガラス部材」の欄には、第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率をＴｙ１、第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率をＴｙ２としたときに、Ｔｙ１とＴｙ２との関係を記載した。
　なお、第１の合わせガラス部材と第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率Ｔ１は以下のように測定した。第１の合わせガラス部材と第１の樹脂層とクリアガラス（厚み２．５ｍｍ）とがこの順に積層された合わせガラスを作製した。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された７８０～２１００ｎｍの重価係数を使用し、赤外線透過率の新たな重価係数として、規格化した。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得た。得られた分光透過率を、新たに規格化した重価係数を乗じて加重平均として求め、波長７８０～２１００ｎｍの赤外線透過率Ｔ１を算出した。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得た。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得た。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ１を算出した。
　第２の合わせガラス部材と第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率Ｔ２は以下のように測定した。第２の合わせガラス部材と第２の樹脂層とクリアガラス（厚み２．５ｍｍ）とがこの順に積層された合わせガラスを作製した。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された７８０～２１００ｎｍの重価係数を使用し、赤外線透過率の新たな重価係数として、規格化した。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得た。得られた分光透過率を、新たに規格化した重価係数を乗じて加重平均として求め、波長７８０～２１００ｎｍの赤外線透過率Ｔ２を算出した。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得た。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得た。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔ１を算出した。
　また、第１の樹脂層又は第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率Ｔｘ１，Ｔｘ２は以下のようにして測定した。第１の樹脂層又は第２の樹脂層を２枚のクリアガラス（厚み２．５ｍｍ）の間に積層し、合わせガラスを作製した。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された７８０～２１００ｎｍの重価係数を使用し、赤外線透過率の新たな重価係数として、規格化した。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得た。得られた分光透過率を、新たに規格化した重価係数を乗じて加重平均として求め、波長７８０～２１００ｎｍの赤外線透過率を算出した。ＪＩＳ　Ｒ３１０６（１９９８）の付表２に示された３００～２１００ｎｍの重価係数のうち、７８０～２１００ｎｍの重価係数を使用し、７８０～２１００ｎｍの各々の重価係数を、その７８０～２１００ｎｍの重価係数の合計値で割ることで、７８０～２１００ｎｍにおける赤外線透過率の新たに規格化された重価係数を得た。次いで、分光光度計（日立ハイテク社製「Ｕ－４１００」）を用いて、ＪＩＳ　Ｒ３１０６（１９９８）に準拠して、合わせガラスの波長７８０～２１００ｎｍにおける分光透過率を得た。得られた分光透過率に、新たに規格化された重価係数を乗じることにより、波長７８０～２１００ｎｍの赤外線透過率Ｔｘ１，Ｔｘ２を算出した。
Figure JPOXMLDOC01-appb-T000005
Figure JPOXMLDOC01-appb-T000006
　また、下記の表６には、Ｔ１’については参考値として、各実施例及び各比較例において、第１の合わせガラス部材と第１の樹脂層と第１の合わせガラス部材とが積層された合わせガラスの波長７８０～２１００ｎｍにおける赤外線透過率を示した。Ｔ２’については参考値として、各実施例及び各比較例において、第２の合わせガラス部材と第２の樹脂層と第２の合わせガラス部材とが積層された合わせガラスの波長７８０～２１００ｎｍにおける赤外線透過率を示した。Ｔｘ１’については参考値として、各実施例及び各比較例において、クリアガラス（厚み２．５ｍｍ）と第１の樹脂層とクリアガラス（厚み２．５ｍｍ）とが積層された合わせガラスの波長７８０～２１００ｎｍにおける赤外線透過率を示した。Ｔｘ２’については参考値として、各実施例及び各比較例において、クリアガラス（厚み２．５ｍｍ）と第２の樹脂層とクリアガラス（厚み２．５ｍｍ）とが積層された合わせガラスの波長７８０～２１００ｎｍにおける赤外線透過率を示した。
Figure JPOXMLDOC01-appb-T000007
　１…中間膜
　１ａ…第１の表面
　１ｂ…第２の表面
　２…赤外線反射層
　２ａ…第１の表面
　２ｂ…第２の表面
　３…第１の樹脂層
　３ａ…外側の表面
　４…第２の樹脂層
　４ａ…外側の表面
　１１…合わせガラス
　２１…第１の合わせガラス部材
　２２…第２の合わせガラス部材

Claims (19)

  1. 　第１の合わせガラス部材と、
    　第２の合わせガラス部材と、
    　前記第１の合わせガラス部材と前記第２の合わせガラス部材との間に配置された中間膜とを備え、
    　前記中間膜が、赤外線を反射する赤外線反射層と、前記赤外線反射層の第１の表面側に配置されており、かつ熱可塑性樹脂を含む第１の樹脂層と、前記赤外線反射層の前記第１の表面とは反対の第２の表面側に配置されており、かつ熱可塑性樹脂を含む第２の樹脂層とを備え、
    　前記中間膜における前記第１の樹脂層の外側に、前記第１の合わせガラス部材が配置されており、かつ前記中間膜における前記第２の樹脂層の外側に、前記第２の合わせガラス部材が配置されており、
    　前記第１の合わせガラス部材と前記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材と前記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも１５％以上高い、合わせガラス。
  2. 　前記第１の合わせガラス部材と前記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材と前記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも２０％以上高い、請求項１に記載の合わせガラス。
  3. 　前記第１の合わせガラス部材と前記第１の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材と前記第２の樹脂層との２つの層全体の波長７８０～２１００ｎｍにおける赤外線透過率よりも３０％以上高い、請求項２に記載の合わせガラス。
  4. 　前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高いか、又は、
    　前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い、請求項１～３のいずれか１項に記載の合わせガラス。
  5. 　前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い、請求項４に記載の合わせガラス。
  6. 　前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い、請求項４に記載の合わせガラス。
  7. 　前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも高く、かつ、
    　前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも高い、請求項１～３のいずれか１項に記載の合わせガラス。
  8. 　前記第１の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の樹脂層の波長７８０～２１００ｎｍにおける赤外線透過率よりも１０％以上高く、かつ、
    　前記第１の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率が、前記第２の合わせガラス部材の波長７８０～２１００ｎｍにおける赤外線透過率よりも１０％以上高い、請求項７に記載の合わせガラス。
  9. 　前記赤外線反射層が、金属箔付き樹脂フィルム、樹脂層上に金属層及び誘電層が形成された多層積層フィルム、多層樹脂フィルム又は液晶フィルムである、請求項１～８のいずれか１項に記載の合わせガラス。
  10. 　前記第１の樹脂層と前記第２の樹脂層との内の少なくとも一方が、接着力調整剤を含む、請求項１～９のいずれか１項に記載の合わせガラス。
  11. 　前記第１の樹脂層と前記第２の樹脂層との双方が、前記接着力調整剤を含む、請求項１０に記載の合わせガラス。
  12. 　前記第２の樹脂層が金属酸化物粒子を含む、請求項１～１１のいずれか１項に記載の合わせガラス。
  13. 　前記金属酸化物粒子が、錫ドープ酸化インジウム粒子又は酸化タングステン粒子である、請求項１２に記載の合わせガラス。
  14. 　前記第２の樹脂層が、フタロシアニン化合物、ナフタロシアニン化合物及びアントラシアニン化合物の内の少なくとも１種を含む、請求項１～１３のいずれか１項に記載の合わせガラス。
  15. 　前記第１の樹脂層中の前記熱可塑性樹脂がポリビニルアセタール樹脂であり、
    　前記第２の樹脂層中の前記熱可塑性樹脂がポリビニルアセタール樹脂である、請求項１～１４のいずれか１項に記載の合わせガラス。
  16. 　前記第１の樹脂層が可塑剤を含み、
    　前記第２の樹脂層が可塑剤を含む、請求項１～１５のいずれか１項に記載の合わせガラス。
  17. 　前記第１の樹脂層が紫外線遮蔽剤を含む、請求項１～１６のいずれか１項に記載の合わせガラス。
  18. 　前記第２の樹脂層が紫外線遮蔽剤を含む、請求項１～１７のいずれか１項に記載の合わせガラス。
  19. 　請求項１～１８のいずれか１項に記載の合わせガラスを、建築物又は車両において、外部空間と前記外部空間から熱線が入射される内部空間との間の開口部に取り付ける方法であって、
    　前記第１の合わせガラス部材が、前記外部空間側に位置するように、かつ前記第２の合わせガラス部材が前記内部空間側に位置するように、前記合わせガラスを前記開口部に取り付ける、合わせガラスの取り付け方法。
PCT/JP2015/052774 2014-01-31 2015-01-30 合わせガラス及び合わせガラスの取り付け方法 WO2015115627A1 (ja)