WO2015002035A1 - Dispositif d'extrusion à double vis et procédé de production d'un film - Google Patents

Dispositif d'extrusion à double vis et procédé de production d'un film Download PDF

Info

Publication number
WO2015002035A1
WO2015002035A1 PCT/JP2014/066747 JP2014066747W WO2015002035A1 WO 2015002035 A1 WO2015002035 A1 WO 2015002035A1 JP 2014066747 W JP2014066747 W JP 2014066747W WO 2015002035 A1 WO2015002035 A1 WO 2015002035A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
temperature
refrigerant
film
cylinder
Prior art date
Application number
PCT/JP2014/066747
Other languages
English (en)
Japanese (ja)
Inventor
山田　晃
圭 原田
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to CN201480035773.1A priority Critical patent/CN105339156B/zh
Priority to KR1020157036538A priority patent/KR101810856B1/ko
Publication of WO2015002035A1 publication Critical patent/WO2015002035A1/fr

Abstract

L'invention concerne un dispositif d'extrusion à double vis comprenant : un cylindre pourvu d'un orifice d'extrusion qui assure l'extrusion de la résine à l'état fondu ; deux vis d'un diamètre externe (φ) de 100mm minimum disposées à l'intérieur du cylindre de manière à pouvoir tourner ; un système de refroidissement qui est installé sur la paroi de cylindre, et qui présente un premier orifice d'alimentation/évacuation d'un agent réfrigérant et un canal parcouru par un agent réfrigérant, qui assure l'échange de chaleur avec la résine à l'état fondu ; un moyen de détection de température qui assure la détection de la résine à l'état fondu extrudée par l'orifice d'extrusion, et qui est situé côté aval de l'orifice d'extrusion du cylindre dans la direction d'écoulement de la résine à l'état fondu, et côté amont d'un dispositif de production d'un film qui assure le moulage de la résine à l'état fondu ; et un moyen de commande de la température de résine, qui assure l'ajustement du dosage de l'agent réfrigérant cédé au premier orifice d'alimentation/évacuation de l'agent réfrigérant, et la commande de la différence de température entre une température nominale de résine et la température de résine à l'état fondu détectée par le moyen de détection de température, cette différence de température étant commandée de manière à être égale ou inférieure à la valeur seuil prédéfinie.
PCT/JP2014/066747 2013-07-02 2014-06-24 Dispositif d'extrusion à double vis et procédé de production d'un film WO2015002035A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201480035773.1A CN105339156B (zh) 2013-07-02 2014-06-24 双螺杆挤出装置及薄膜制造方法
KR1020157036538A KR101810856B1 (ko) 2013-07-02 2014-06-24 2축 압출 장치 및 필름 제조 방법

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2013-139304 2013-07-02
JP2013139304 2013-07-02
JP2014037490A JP6049648B2 (ja) 2013-07-02 2014-02-27 二軸押出装置及びフィルム製造方法
JP2014-037490 2014-02-27

Publications (1)

Publication Number Publication Date
WO2015002035A1 true WO2015002035A1 (fr) 2015-01-08

Family

ID=52143614

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/066747 WO2015002035A1 (fr) 2013-07-02 2014-06-24 Dispositif d'extrusion à double vis et procédé de production d'un film

Country Status (4)

Country Link
JP (1) JP6049648B2 (fr)
KR (1) KR101810856B1 (fr)
CN (1) CN105339156B (fr)
WO (1) WO2015002035A1 (fr)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101680006B1 (ko) * 2016-03-10 2016-12-06 (주)한도기공 압출실린더 내부에 냉각수 순환홀을 구비한 이동식 압출기
DE102018112939A1 (de) * 2018-05-30 2019-12-05 Inmex Gmbh Plastifizierzylinder eines Kunststoffextruders und Kunststoffextruder mit einem solchen Plastifizierzylinder
CN108705804A (zh) * 2018-06-13 2018-10-26 鲍振宇 一种自动化生物燃料成型装置
KR102086085B1 (ko) * 2019-01-21 2020-04-23 구승회 특수형 코니컬 트윈 스크류 압출성형장치
JP7252432B2 (ja) * 2019-10-16 2023-04-05 株式会社瑞光 回転押出機
JP7459735B2 (ja) 2019-11-27 2024-04-02 Ａｇｃ株式会社 フィルムの製造方法、及び積層体の製造方法
JP7391183B2 (ja) * 2020-03-10 2023-12-04 マクセル株式会社 生分解性樹脂の分解装置
CN112248395A (zh) * 2020-09-25 2021-01-22 安徽德尔电气集团有限公司 一种电缆生产用挤出机温度控制系统

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63104814A (ja) * 1986-10-22 1988-05-10 Sekisui Chem Co Ltd 押出機における樹脂温度制御装置
JPH07144354A (ja) * 1993-11-24 1995-06-06 Japan Steel Works Ltd:The シリンダの温度制御方法及び装置
JP2012091494A (ja) * 2010-09-27 2012-05-17 Fujifilm Corp ポリエステルフィルムの製造方法及び太陽電池部材用ポリエステルフィルム

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN2518666Y (zh) * 2000-03-17 2002-10-30 莱芜市模具厂 塑料熔体泵
JP4316109B2 (ja) 2000-06-12 2009-08-19 大日本印刷株式会社 冷却ロールの温度制御方法及び制御装置並びに制御システム
JP4025772B2 (ja) * 2004-12-28 2007-12-26 株式会社日本製鋼所 温度調整装置および可塑化樹脂製造方法
CN101920552B (zh) * 2009-06-17 2013-02-06 北京化工大学 一种螺杆挤出机机筒及其温度控制方法
CN101947847A (zh) * 2010-09-15 2011-01-19 南京欧立挤出机械有限公司 双螺杆挤出机
CN202079765U (zh) * 2011-04-28 2011-12-21 嘉兴市博腾塑业有限公司 一种挤出机水冷系统
CN202129978U (zh) * 2011-06-20 2012-02-01 宁波康润机械科技有限公司 一种塑料挤出机的自动冷却装置
WO2013027678A1 (fr) * 2011-08-25 2013-02-28 富士フイルム株式会社 Film polyester à étirage suivant deux axes, procédé permettant de produire celui-ci et module de cellules solaires

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63104814A (ja) * 1986-10-22 1988-05-10 Sekisui Chem Co Ltd 押出機における樹脂温度制御装置
JPH07144354A (ja) * 1993-11-24 1995-06-06 Japan Steel Works Ltd:The シリンダの温度制御方法及び装置
JP2012091494A (ja) * 2010-09-27 2012-05-17 Fujifilm Corp ポリエステルフィルムの製造方法及び太陽電池部材用ポリエステルフィルム

Also Published As

Publication number Publication date
CN105339156B (zh) 2017-04-05
JP6049648B2 (ja) 2016-12-21
KR101810856B1 (ko) 2017-12-20
JP2015027785A (ja) 2015-02-12
KR20160015278A (ko) 2016-02-12
CN105339156A (zh) 2016-02-17

Similar Documents

Publication Publication Date Title
JP6049648B2 (ja) 二軸押出装置及びフィルム製造方法
KR102013606B1 (ko) 열가소성 수지 필름의 제조 방법 및 환상 올레핀 수지 필름
TW201714915A (zh) 含有呋喃二甲酸酯單元之聚酯膜
CN101664991B (zh) 用于制备膜的方法和光学膜
JP6651398B2 (ja) 光学フィルムの製造方法及び製造装置
JP5738792B2 (ja) ポリエステルフィルムの製造方法並びにポリエステルフィルム、太陽電池用保護シート及び太陽電池モジュール
JP5512749B2 (ja) ポリエステルフィルムの製造方法
US20230331983A1 (en) Liquid crystal polymer film and substrate for high-speed communication
WO2013015041A1 (fr) Procédé de production de film de polyester, film de polyester, feuille de support pour cellule solaire, et module de cellules solaires
KR102051724B1 (ko) 폴리에스터 필름 및 그 제조 방법, 태양 전지용 이면 보호 시트와, 태양 전지 모듈
JP5547142B2 (ja) ポリエステルフィルムの製造方法
JP2014193604A (ja) シートの製造方法およびシートの製造装置
JP5653951B2 (ja) ポリエステルフィルムの製造方法
KR20100063727A (ko) 용융 압출 장치 및 열가소성 수지 필름의 제조방법
JP5676526B2 (ja) ポリエステル樹脂の製造方法、太陽電池用保護シート、及び太陽電池モジュール
JP2010234737A (ja) 光学フィルムの製造方法及び製造装置、並びに光学補償フィルム
US20230257533A1 (en) Heat-shrinkable polyester-based film roll
US20230022144A1 (en) Polymer film and substrate for communication
JP4967997B2 (ja) 熱可塑性樹脂フィルムの製造方法
JP2013043411A (ja) ポリエステルフィルム、ポリエステルフィルムの製造方法、太陽電池用バックシート、及び太陽電池モジュール
JP2012256632A (ja) 樹脂フィルムの製造方法、ポリエステルフィルム、太陽電池用バックシート、及び太陽電池モジュール
JP2017140758A (ja) フィルムの製造方法
JP2014151510A (ja) 押出方法、及び熱可塑性樹脂フィルムの製造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201480035773.1

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14820243

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20157036538

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14820243

Country of ref document: EP

Kind code of ref document: A1