WO2013135680A1 - Flammgeschütztes thermoplastisches polyurethan enthaltend umhüllte metallhydroxide, phosphor-haltige flammschutzmittel und/oder hydrotalkit bzw. schichtsilikat - Google Patents
Flammgeschütztes thermoplastisches polyurethan enthaltend umhüllte metallhydroxide, phosphor-haltige flammschutzmittel und/oder hydrotalkit bzw. schichtsilikat Download PDFInfo
- Publication number
- WO2013135680A1 WO2013135680A1 PCT/EP2013/054975 EP2013054975W WO2013135680A1 WO 2013135680 A1 WO2013135680 A1 WO 2013135680A1 EP 2013054975 W EP2013054975 W EP 2013054975W WO 2013135680 A1 WO2013135680 A1 WO 2013135680A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- flame retardant
- phosphorus
- polyurethane
- polyurethane according
- weight
- Prior art date
Abstract
Description
Claims