WO2013090464A1 - Rubber compositions comprising graphene and reinforcing agents and articles made therefrom - Google Patents
Rubber compositions comprising graphene and reinforcing agents and articles made therefrom Download PDFInfo
- Publication number
- WO2013090464A1 WO2013090464A1 PCT/US2012/069304 US2012069304W WO2013090464A1 WO 2013090464 A1 WO2013090464 A1 WO 2013090464A1 US 2012069304 W US2012069304 W US 2012069304W WO 2013090464 A1 WO2013090464 A1 WO 2013090464A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- graphene sheets
- phr
- composition
- minutes
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B60—VEHICLES IN GENERAL
- B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
- B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
- B60C1/0008—Compositions of the inner liner
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B60—VEHICLES IN GENERAL
- B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
- B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
- B60C1/0016—Compositions of the tread
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B60—VEHICLES IN GENERAL
- B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
- B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
- B60C1/0025—Compositions of the sidewalls
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
- C08K3/042—Graphene or derivatives, e.g. graphene oxides
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/34—Silicon-containing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/34—Silicon-containing compounds
- C08K3/36—Silica
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L7/00—Compositions of natural rubber
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L9/00—Compositions of homopolymers or copolymers of conjugated diene hydrocarbons
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B60—VEHICLES IN GENERAL
- B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
- B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
- B60C2001/0066—Compositions of the belt layers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K2201/00—Specific properties of additives
- C08K2201/002—Physical properties
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K2201/00—Specific properties of additives
- C08K2201/011—Nanostructured additives
Definitions
- the present invention relates to rubber compositions comprising graphene and reinforcing agents, and articles comprising the compositions.
- Rubber goods are used in all areas of life, including tires, belts, industrial applications, automotive components, clothing, etc.
- Enhanced physical properties of rubbers such as wear resistance, durability, etc. are desirable for many of these applications.
- Considerable research and development work is being done to increase the fuel efficiency of vehicles.
- a significant contributor to decreased fuel efficiency is the energy lost through rolling resistance between tires and the road surface.
- a portion of rolling resistance is caused by hysteresis, i.e., the energy dissipated when tire components deform and then recover as the tire rolls. It would be desirable to obtain a rubber composition having improved mechanical properties, such as decreased hysteresis.
- compositions comprising graphene sheets, at least one silicon containing reinforcing agent, and at least one rubber and articles, such as tired made therefrom. Further disclosed and claimed is a method of making a rubber composition, comprising the step of blending graphene sheets, at least one silicon containing reinforcing agent, and at least one rubber.
- reinforcing agents include mineral fillers.
- mineral fillers include silicon-containing compounds, such as silicas, silicates, clays, nanoclays, etc.
- examples include glasses, aluminum silicates, wollastonites, kaolins, montmorillonites (including nanoclays), halloysite (including nanoclays), chlorite, calcined clay, etc.
- mineral fillers examples include talc, mica, carbonates (such as calcium carbonate, precipitated calcium carbonate, magnesium carbonate, barium carbonate, dolomites, huntite, hydromagnesite, etc.), sulfates (such as barium sulfate), barites, brucite, magnesium hydroxide, alumina trihydrate, etc.
- Reinforcing agents can include polymers (such as polyaramides (including Kevlar®), ultra high molecular weight polyethylene (including Dynema®), etc.
- Reinforcing agents can be carbon fillers other than graphene sheets, including carbon black, carbon nanotubes, etc.
- compositions may also comprise carbon black, including low- and high- structure carbon blacks. Carbon blacks may be surface modified.
- Reinforcing agents can be in the form of fibers, including chopped fibers (such as glass, carbon, polyaramide, ultra high molecular weight polyethylene), nanotubes (including carbon nanotubes (such as single- and double-walled nanotubes), silicates, etc.), etc. They can be in the form of mats or weaves of fibers.
- silica examples include, but are not limited to, pyrogenic silicas, crystalline silicas, amorphous silicas, precipitated silicas, quartz, etc.. They may be formed by the acidification of a silicate such as sodium silicate, etc.
- the silicas include conventional, easily dispersible or semi-HD, and highly dispersible (HD) silicas.
- the silicas may be nanosilicas.
- the reinforcing agents can be surface modifiers.
- the composition may comprise from about 1 phr to about 100 phr of filler, or about 10 to about 100 phr of filler, or about 20 to about 100 phr of filler, or about 30 to about 100 phr of filler, or about 40 to about 100 phr of filler, or about 50 to about 100 phr of filler, or about 60 to about 100 phr of filler, or about 10 to about 80 phr of filler, or about 20 to about 80 phr of filler, or about 30 to about 80 phr of filler, or about 40 to about 80 phr of filler, or about 50 to about 80 phr, or about 60 to about 90 phr of filler.
- low surface area fillers such as mineral fillers, silicon-containing agents, carbon blacks, graphite
- Some preferred loadings for carbon black include 0.1 to about 100 phr, or about 1 to about 80 phr, or about 5 to about 80 phr, or about 10 to about 80 phr, or about 5 to about 60 phr, or about 10 to about 80 phr, or about 20 to about 80 phr, or about 30 to about 80 phr, or about 15 to about 60 phr, or about 20 to about 60 phr, or about 15 to about 50 phr, or about 20 to about 40 phr.
- the composition may comprise from about 0.5 phr to about 10 phr, or about 1 to about 8 phr, or about 1 to about 5 phr, or about 2 to about 4 phr, or about 2 to about 3 phr of filler.
- Preferred fillers include blends of carbon black with one or more other fillers, silicon containing compounds, silicas, and blends of silicon containing compounds and silicas with carbon black.
- Rubbers can be thermosets, thermoplastics, etc.
- examples of rubbers include one or more of natural rubbers, polyisoprene, c/ ' s-1 ,4-polyisoprene, high c/ ' s-1 ,4- polyisoprene, isoprene/isobutylene rubbers, isoprene/butadiene polymers,
- acrylonitrile/butadiene rubber hydrogenated acrylonitrile/butadiene rubber (HNBR), acrylic rubber, ethylene/acrylic elastomers, isobutylene-co-para-methylisoprene, brominated isobutylene-co-para-methylisoprene, neoprene (chloroprene), polybutadiene, 1 ,4-polybutadiene, high cis-1 ,4-polybutadiene rubbers, low cis-1 ,4-polybutadiene rubbers, high-vinyl polybutadiene rubbers, ethylene/propylene/diene rubbers (EPDM), ethylene/propylene rubbers (EPM), chlorosulfonated polyethylene (CSM), styrenic copolymers, styrenic block copolymers, styrene/isoprene/styrene (SIS) rubbers,
- HNBR
- SBR /butadiene rubbers
- styrene-butadiene rubbers prepared by solution polymerization, styrene/ethylene/butadiene/styrene copolymer (SEBS), ethylene/vinyl acetate (EVA) polymers, butyl rubbers, chlorobutyl rubbers, bromobutyl rubbers, chlorohalogenated butyl rubbers, branched butyl rubbers, star-branched butyl rubbers, ethylene/propylene rubbers, chlorosulfonated polyethylenes, nitrile rubbers, hydrogenated nitrile rubbers, carboxylated nitrile rubbers, acrylic rubbers, hydrin rubbers, fluoroelastomers, fluorocarbon rubbers, polyphosphazenes, polysulfide rubber, polyurethane rubbers, polysiloxanes, natural rubber and solution SBR blends, low Tg polybutadiene and SBR blends, etc.
- SEBS styrene/ethylene
- thermoplastic elastomers such as thermoplastic polyurethane, polyvinyl chloride) (PVC), PVC/nitrile rubber blends, styrenic block copolymers, copolyester elastomers, copolyetherester elastomers, thermoplastic vulcanizates (e.g.,
- the graphene sheets are graphite sheets preferably having a surface area of from about 100 to about 2630 m 2 /g.
- the graphene sheets primarily, almost completely, or completely comprise fully exfoliated single sheets of graphite (these are approximately ⁇ 1 nm thick and are often referred to as "graphene"), while in other embodiments, at least a portion of the graphene sheets may comprise partially exfoliated graphite sheets, in which two or more sheets of graphite have not been exfoliated from each other.
- the graphene sheets may comprise mixtures of fully and partially exfoliated graphite sheets.
- Graphene sheets are distinct from carbon nanotubes.
- Graphene sheets may have a "platey" (e.g. two-dimensional) structure and do not have the needle-like form of carbon nanotubes.
- the two longest dimensions of the graphene sheets may each be at least about 10 times greater, or at least about 50 times greater, or at least about 100 times greater, or at least about 1000 times greater, or at least about 5000 times greater, or at least about 10,000 times greater than the shortest dimension (i.e. thickness) of the sheets.
- Graphene sheets may be made using any suitable method. For example, they may be obtained from graphite, graphite oxide, expandable graphite, expanded graphite, etc.. They may be obtained by the physical exfoliation of graphite, by for example, peeling, grinding, milling, graphene sheets. They made be made by sonication of precursors such as graphite. They may be made by opening carbon nanotubes. They may be made from inorganic precursors, such as silicon carbide. They may be made by chemical vapor deposition (such as by reacting a methane and hydrogen on a metal surface). They may be made by epitaxial growth on substrates such as silicon carbide and metal substrates and by growth from metal-carbon melts.
- They made by made They may be may by the reduction of an alcohol, such ethanol, with a metal (such as an alkali metal like sodium) and the subsequent pyrolysis of the alkoxide product (such a method is reported in Nature Nanotechnology (2009), 4, 30-33). They may be made from small molecule precursors such as carbon dioxide, alcohols (such as ethanol, methanol, etc.), alkoxides (such as ethoxides, methoxides, etc., including sodium, potassium, and other alkoxides). They may be made by the exfoliation of graphite in dispersions or exfoliation of graphite oxide in dispersions and the subsequently reducing the exfoliated graphite oxide.
- Graphene sheets may be made by the exfoliation of expandable graphite, followed by intercalation, and ultrasonication or other means of separating the intercalated sheets (see, for example, Nature Nanotechnology (2008), 3, 538-542). They may be made by the intercalation of graphite and the subsequent exfoliation of the product in suspension, thermally, etc. Exfoliation processes may be thermal, and include exfoliation by rapid heating, using microwaves, furnaces, hot baths, etc.
- Graphene sheets may be made from graphite oxide (also known as graphitic acid or graphene oxide). Graphite may be treated with oxidizing and/or intercalating agents and exfoliated. Graphite may also be treated with intercalating agents and
- Graphene sheets may be formed by ultrasonically exfoliating suspensions of graphite and/or graphite oxide in a liquid (which may contain surfactants and/or intercalants). Exfoliated graphite oxide dispersions or suspensions can be subsequently reduced to graphene sheets. Graphene sheets may also be formed by mechanical treatment (such as grinding or milling) to exfoliate graphite or graphite oxide (which would subsequently be reduced to graphene sheets).
- Graphene sheets may be made by the reduction of graphite oxide. Reduction of graphite oxide to graphene may be done by thermal reduction/annealing, chemical reduction, etc. and may be carried out on graphite oxide in a solid form, in a dispersion, etc.
- useful chemical reducing agents include, but are not limited to, hydrazines (such as hydrazine (in liquid or vapor forms, ⁇ /,/V-dimethylhydrazine, etc.), sodium borohydride, citric acid, hydroquinone, isocyanates (such as phenyl isocyanate), hydrogen, hydrogen plasma, etc..
- a dispersion or suspension of exfoliated graphite oxide in a carrier can be made using any suitable method (such as ultrasonication and/or mechanical grinding or milling) and reduced to graphene sheets.
- Reduction can be solvothermal reduction, in solvents such as water, ethanol, etc. This can for example be done in an autoclave at elevated temperatures (such as those above about 200 °C).
- Graphite oxide may be produced by any method known in the art, such as by a process that involves oxidation of graphite using one or more chemical oxidizing agents and, optionally, intercalating agents such as sulfuric acid.
- oxidizing agents include nitric acid, sodium and potassium nitrates, perchlorates, hydrogen peroxide, sodium and potassium permanganates, phosphorus pentoxide, bisulfites, etc.
- Preferred oxidants include KCI0 4 ; HN0 3 and KCI0 3 ; KMn0 4 and/or NaMn0 4 ; KMn0 4 and NaN0 3 ; K 2 S 2 0 8 and P 2 0 5 and KMn0 4 ; KMn0 4 and HN0 3 ; and HN0 3 .
- Preferred intercalation agents include sulfuric acid.
- Graphite may also be treated with intercalating agents and electrochemically oxidized. Examples of methods of making graphite oxide include those described by Staudenmaier (Ber. Stsch. Chem. Ges. (1898), 31, 1481 ) and Hummers (J. Am. Chem. Soc. (1958), 80, 1339).
- graphene sheets are oxidize graphite to graphite oxide, which is then thermally exfoliated to form graphene sheets (also known as thermally exfoliated graphite oxide), as described in US 2007/0092432, the disclosure of which is hereby incorporated herein by reference.
- the thusly formed graphene sheets may display little or no signature corresponding to graphite or graphite oxide in their X-ray diffraction pattern.
- the thermal exfoliation may be carried out in a continuous, semi-continuous batch, etc. process.
- Heating can be done in a batch process or a continuous process and can be done under a variety of atmospheres, including inert and reducing atmospheres (such as nitrogen, argon, and/or hydrogen atmospheres). Heating times can range from under a few seconds or several hours or more, depending on the temperatures used and the characteristics desired in the final thermally exfoliated graphite oxide. Heating can be done in any appropriate vessel, such as a fused silica, mineral, metal, carbon (such as graphite), ceramic, etc. vessel. Heating may be done using a flash lamp. During heating, the graphite oxide may be contained in an essentially constant location in single batch reaction vessel, or may be transported through one or more vessels during the reaction in a continuous or batch mode. Heating may be done using any suitable means, including the use of furnaces and infrared heaters.
- atmospheres including inert and reducing atmospheres (such as nitrogen, argon, and/or hydrogen atmospheres). Heating times can range from under a few seconds or several hours or more, depending on the temperatures used and
- temperatures at which the thermal exfoliation of graphite oxide may be carried out are at least about 300 °C, at least about 400 °C, at least about 450 °C, at least about 500 °C, at least about 600 °C, at least about 700 °C, at least about 750 °C, at least about 800 °C, at least about 850 °C, at least about 900 °C, at least about 950 °C, and at least about 1000 °C.
- Preferred ranges include between about 750 about and 3000 °C, between about 850 and 2500 °C, between about 950 and about 2500 °C, and between about 950 and about 1500 °C.
- the time of heating can range from less than a second to many minutes.
- the time of heating can be less than about 0.5 seconds, less than about 1 second, less than about 5 seconds, less than about 10 seconds, less than about 20 seconds, less than about 30 seconds, or less than about 1 min.
- the time of heating can be at least about 1 minute, at least about 2 minutes, at least about 5 minutes, at least about 15 minutes, at least about 30 minutes, at least about 45 minutes, at least about 60 minutes, at least about 90 minutes, at least about 120 minutes, at least about 150 minutes, at least about 240 minutes, from about 0.01 seconds to about 240 minutes, from about 0.5 seconds to about 240 minutes, from about 1 second to about 240 minutes, from about 1 minute to about 240 minutes, from about 0.01 seconds to about 60 minutes, from about 0.5 seconds to about 60 minutes, from about 1 second to about 60 minutes, from about 1 minute to about 60 minutes, from about 0.01 seconds to about 10 minutes, from about 0.5 seconds to about 10 minutes, from about 1 second to about 10 minutes, from about 1 minute to about 10 minutes, from about 0.01 seconds to about 1 minute, from about 0.5 seconds to about 1 minute, from about 1 second to about 1 minute, no more than about 600 minutes, no more than about 450 minutes, no more than about 300 minutes, no more than about 180 minutes, no more than about 120
- Examples of the rate of heating include at least about 120 °C/min, at least about 200 °C/min, at least about 300 °C/min, at least about 400 °C/min, at least about 600 °C/min, at least about 800 °C/min, at least about 1000 °C/min, at least about 1200 °C/min, at least about 1500 °C/min, at least about 1800 °C/min, and at least about 2000 °C/min.
- Graphene sheets may be annealed or reduced to graphene sheets having higher carbon to oxygen ratios by heating under reducing atmospheric conditions (e.g., in systems purged with inert gases or hydrogen).
- Reduction/annealing temperatures are preferably at least about 300 °C, or at least about 350 °C, or at least about 400 °C, or at least about 500 °C, or at least about 600 °C, or at least about 750 °C, or at least about 850 °C, or at least about 950 °C, or at least about 1000 °C.
- the temperature used may be, for example, between about 750 about and 3000 °C, or between about 850 and 2500 °C, or between about 950 and about 2500 °C.
- the time of heating can be for example, at least about 1 second, or at least about
- the heating time will be at least about 15 minutes, or about 30 minutes, or about 45 minutes, or about 60 minutes, or about 90 minutes, or about 120 minutes, or about 150 minutes.
- the temperature may vary within these ranges.
- the heating may be done under a variety of conditions, including in an inert atmosphere (such as argon or nitrogen) or a reducing atmosphere, such as hydrogen (including hydrogen diluted in an inert gas such as argon or nitrogen), or under vacuum.
- the heating may be done in any appropriate vessel, such as a fused silica or a mineral or ceramic vessel or a metal vessel.
- the materials being heated including any starting materials and any products or intermediates) may be contained in an essentially constant location in single batch reaction vessel, or may be transported through one or more vessels during the reaction in a continuous or batch reaction. Heating may be done using any suitable means, including the use of furnaces and infrared heaters.
- the graphene sheets preferably have a surface area of at least about 100 m 2 /g to, or of at least about 200 m 2 /g, or of at least about 300 m 2 /g, or of least about 350 m 2 /g, or of least about 400 m 2 /g, or of least about 500 m 2 /g, or of least about 600 m 2 /g., or of least about 700 m 2 /g, or of least about 800 m 2 /g, or of least about 900 m 2 /g, or of least about 700 m 2 /g.
- the surface area may be about 400 to about 1 100 m 2 /g.
- the theoretical maximum surface area can be calculated to be 2630 m 2 /g.
- the surface area includes all values and subvalues therebetween, especially including 400, 500, 600, 700, 800, 900, 1000, 1 100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 2200, 2300, 2400, 2500, and 2630 m 2 /g.
- the graphene sheets can have number average aspect ratios of about 100 to about 100,000, or of about 100 to about 50,000, or of about 100 to about 25,000, or of about 100 to about 10,000 (where "aspect ratio” is defined as the ratio of the longest dimension of the sheet to the shortest).
- Surface area can be measured using either the nitrogen adsorption/BET method at 77 K or a methylene blue (MB) dye method in liquid solution.
- the difference between the amount of MB that was initially added and the amount present in solution as determined by UV-vis spectrophotometry is assumed to be the amount of MB that has been adsorbed onto the surface of the graphene sheets.
- the surface area of the graphene sheets are then calculated using a value of 2.54 m 2 of surface covered per one mg of MB adsorbed.
- the graphene sheets can have a bulk density of from about 0.01 to at least about 200 kg/m 3 .
- the bulk density includes all values and subvalues therebetween, especially including 0.05, 0.1 , 0.5, 1 , 5, 10, 15, 20, 25, 30, 35, 50, 75, 100, 125, 150, and 175 kg/m 3 .
- the graphene sheets may be functionalized with, for example, oxygen-containing functional groups (including, for example, hydroxyl, carboxyl, and epoxy groups) and typically have an overall carbon to oxygen molar ratio (C/O ratio), as determined by bulk elemental analysis, of at least about 1 :1 , or more preferably, at least about 3:2.
- oxygen-containing functional groups including, for example, hydroxyl, carboxyl, and epoxy groups
- C/O ratio carbon to oxygen molar ratio
- Examples of carbon to oxygen ratios include about 3:2 to about 85:15; about 3:2 to about 20:1 ; about 3:2 to about 30:1 ; about 3:2 to about 40:1 ; about 3:2 to about 60:1 ; about 3:2 to about 80:1 ; about 3:2 to about 100:1 ; about 3:2 to about 200:1 ; about 3:2 to about 500:1 ; about 3:2 to about 1000:1 ; about 3:2 to greater than 1000:1 ; about 10:1 to about 30:1 ; about 80:1 to about 100:1 ; about 20:1 to about 100:1 ; about 20:1 to about 500:1 ; about 20:1 to about 1000:1 ; about 50:1 to about 300:1 ; about 50:1 to about 500:1 ; and about 50:1 to about 1000:1 .
- the carbon to oxygen ratio is at least about 10:1 , or at least about 15:1 , or at least about 20:1 , or at least about 35:1 , or at least about 50:1 , or at least about 75:1 , or at least about 100:1 , or at least about 200:1 , or at least about 300:1 , or at least about 400:1 , or at least 500:1 , or at least about 750:1 , or at least about 1000:1 ; or at least about 1500:1 , or at least about 2000:1.
- the carbon to oxygen ratio also includes all values and subvalues between these ranges.
- the graphene sheets may contain atomic scale kinks. These kinks may be caused by the presence of lattice defects in, or by chemical functionalization of the two- dimensional hexagonal lattice structure of the graphite basal plane.
- the compositions may be electrically conductive.
- the surface resistivity of the compositions may be no greater than about 10000 ⁇ /square, or no greater than about 5000 ⁇ /square, or no greater than about 1000 ⁇ /square, or no greater than about 700 ⁇ /square, or no greater than about 500 ⁇ /square, or no greater than about 350 ⁇ /square, or no greater than about 200 ⁇ /square, or no greater than about 200 ⁇ /square, or no greater than about 150 ⁇ /square, or no greater than about 100 ⁇ /square, or no greater than about 75 ⁇ /square, or no greater than about 50 ⁇ /square, or no greater than about 30 ⁇ /square, or no greater than about 20 ⁇ /square, or no greater than about 10 ⁇ /square, or no greater than about 5 ⁇ /square, or no greater than about 1 ⁇ /square, or no greater than about 0.1 ⁇ /square, or no greater than about 0.01 ⁇ /square, or no greater than about 0.001 ⁇ /square.
- compositions may have an electrical conductivity of at least about 10 "8 S/m. They can can have a conductivity of about 10 "6 S/m to about 10 5 S/m, or of about 10 "5 S/m to about 10 5 S/m. In other embodiments of the invention, the compositions have conductivities of at least about 0.001 S/m, of at least about 0.01 S/m, of at least about 0.1 S/m, of at least about 1 S/m, of at least about 10 S/m, of at least about 100 S/m, or at least about 1000 S/m, or at least about 10,000 S/m, or at least about 20,000 S/m, or at least about 30,000 S/m, or at least about 40,000 S/m, or at least about 50,000 S/m, or at least about 60,000 S/m, or at least about 75,000 S/m, or at least about 10 5 S/m, or at least about 10 6 S/m.
- the compositions can have a thermal conductivity of about 0.1 to about 50 W/(m-K), or of about 0.5 to about 30 W/(m-K), or of about 1 to about 30 W/(m-K), or of about 1 to about 20 W/(m-K), or of about 1 to about 10 W/(m-K), or of about 1 to about 5 W/(m-K), or of about 2 to about 25 W/(m-K), or of about 5 to about 25 W/(m-K).
- the composition may comprise about 0.1 to about 20 phr, or about 0.5 to about 20 phr, or about 0.5 to about 15 phr, or about 0.5 to about 10 phr, or about 1 to about 15 phr, or about 1 to about 10 phr, or about 1 to about 7 phr, or about 1 to about 5 phr, or about 2 to about 5 phr of graphene sheets.
- compositions may further comprise one or more additional additives, such as cross-linkers, curing agents, and vulcanizers (including sulfur and sulfur-containing compounds, peroxides, epoxides, bisphenol, diamines, metal oxides, etc.), accelerators, stabilizers, antidegredation agents (including antioxidants, anti-ozone materials, etc.), zinc oxide, fatty acids (such as stearic acid), scorch inhibitors, tackifiers, waxes, oils, processing aids, fillers (such as clay, talc, etc.) other resins (including phenolics), peptizers, coupling agents (such as silane coupling agents), etc.
- additional additives such as cross-linkers, curing agents, and vulcanizers (including sulfur and sulfur-containing compounds, peroxides, epoxides, bisphenol, diamines, metal oxides, etc.), accelerators, stabilizers, antidegredation agents (including antioxidants, anti-ozone materials, etc.
- Sulfur and/or sulfur-containing compounds may in some instances be present in the compositions in from about 0.05 to about 5 phr, or from about 0.1 to about 5 phr, or from about 0.25 to about 5 phr, or from about 0.05 to about 2.5 phr, or from about 0.1 to about 2.5 phr, or from about 0.25 to about 2.5 phr, or from about 0.5 to about 2.5 phr, or from about 0.05 to about 1 phr, or from about 0.1 to about 1 phr, or from about 0.5 to about 1 phr.
- Coupling agents include organosilicon (silane) compounds, particularly those containing functional groups that can interact with the rubber.
- functional groups include mercapto, amino, vinyl, epoxy, sulfur, etc. groups.
- Examples include di- and polysulfides, b/ ' s-(trialkoxysilylalkyl) polysulfides having from 2 to about 8 connecting sulfur atoms in their sulfur bridge, b/s-(3-triethoxysilylpropyl) tetrasulfide (TESPT), bis-(3- triethoxysilylpropyl) trisulfide, b/s-(3-triethoxysilylpropyl) disulfide (TESPD), 3- chloropropyltriethoxysilane (CPTEO), 3-aminipropyltriethoxysilane (AMEO),
- vinyltrimethoxysilane vinyltriethoxysilane, 3-mercaptopropyltrimethoxysilane, 3- methacryloxypropyltrimethoxysilane, blocked silanes (such as blocked mercaptosilanes), etc.
- accelerators examples include /V-ie f-butyl-2-benzothiazole sulfonamide (TBBS), benzothiazyl disulfide (MBTS), /V-cyclohexy1 -2-benzothiazole sulfonamide (CBS), diphenylguanidine (DPG), etc.
- compositions may be prepared using any suitable method, including conventional rubber processing techniques. Some or all of the components may be blended and combined with one or more vulcanizing, crosslinking, or curing agents and heat treated. Graphene sheets and/or other components may be combined with the rubber by polymerizing the rubber in the presence of graphene sheets and/or other components (in situ polymerization). Rubber containing graphene sheets and/or other components may be blended with additional components, including additional graphene sheets and/or the other components. The compositions may be in vulcanized or unvulcanized form. Rubber (and/or rubber precursors), silica, graphene sheets, and any other components may be directly blended with each other in one or more steps.
- compositions may be formed into a variety of articles, including tires.
- tires is meant to include fully assembled tires as wells tire components, such as treads, belts, sidewalls, inner liners, etc. and fully assembled tires containing one or more of these components.
- Tires may be non-pneumatic tires and pneumatic tires, including radial tires, bias ply tires, tubeless tires, solid tires, run-flat tires, etc.
- the tires may be used in motorized vehicles, equipment, and accessories such as automobiles, trucks, racing vehicles, motorcycles, mopeds, all terrain vehicles, golf carts, off-read vehicles, construction equipment, earthmovers, dump trucks, lawn mowers, farm equipment, tractors, harvesters, trailers, wheelchairs, aircraft, forklifts, lift trucks, tanks, aviation (such as airplanes, helicopters, etc.), etc.
- They may be used in non-motorized motorized vehicles, equipment, and accessories such as bicycles, tricycles, unicycles, wheelchairs, wheel barrows, carts, etc.
- compositions may be used in footwear, including footwear soles.
- Footwear can include boots, athletic shoes, safety shoes, etc.
- They may be used in seals, cables, profiles, hoses, industrial rubber goods, belts, conveyer belts, power transmission belts, rollers, floor coverings, golf balls, windows, vibration control applications (such as earthquake protection equipment (such as rubber bearings), floors, walls, windows, helicopter vibration dampeners, etc.).
- vibration control applications such as earthquake protection equipment (such as rubber bearings), floors, walls, windows, helicopter vibration dampeners, etc.).
- stage 1 components in Table 1 are blended in a two-roll mill.
- stage 3 components in Table 1 are then added.
- graphene sheets are added to the compositions in the amounts indicated in Table 2. Sheets are rolled out of the mill and cured.
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Tires In General (AREA)
Priority Applications (4)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| JP2014547391A JP6404121B2 (ja) | 2011-12-12 | 2012-12-12 | グラフェン及び補強材を含むゴム組成物、並びにそれから作られる物品 |
| EP12858164.2A EP2790926A4 (en) | 2011-12-12 | 2012-12-12 | ROLLING COMPOSITIONS WITH GRAPHES AND REINFORCEMENTS, AND ARTICLES MADE THEREFROM |
| KR1020147015060A KR20140105732A (ko) | 2011-12-12 | 2012-12-12 | 그래핀 및 강화제를 포함하는 고무 조성물 및 그로부터 제조된 물품 |
| CN201280060998.3A CN104136237A (zh) | 2011-12-12 | 2012-12-12 | 包含石墨烯和增强剂的橡胶组合物和由其制成的制品 |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US201161569435P | 2011-12-12 | 2011-12-12 | |
| US61/569,435 | 2011-12-12 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| WO2013090464A1 true WO2013090464A1 (en) | 2013-06-20 |
Family
ID=48572578
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/US2012/069304 Ceased WO2013090464A1 (en) | 2011-12-12 | 2012-12-12 | Rubber compositions comprising graphene and reinforcing agents and articles made therefrom |
Country Status (6)
| Country | Link |
|---|---|
| US (1) | US20130150516A1 (enExample) |
| EP (1) | EP2790926A4 (enExample) |
| JP (2) | JP6404121B2 (enExample) |
| KR (1) | KR20140105732A (enExample) |
| CN (1) | CN104136237A (enExample) |
| WO (1) | WO2013090464A1 (enExample) |
Cited By (7)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN103408855A (zh) * | 2013-08-29 | 2013-11-27 | 滁州旭中化工有限公司 | 一种含氧化石墨烯橡胶复合材料 |
| CN104292528A (zh) * | 2013-07-18 | 2015-01-21 | 宁波大学 | 一种高强度橡胶及其制备方法 |
| JP2015517583A (ja) * | 2012-05-03 | 2015-06-22 | ピーピージー インダストリーズ オハイオ,インコーポレイティド | グラフェンカーボン粒子を含むゴム配合物 |
| KR101571666B1 (ko) * | 2013-12-31 | 2015-11-25 | 현대자동차주식회사 | 타이어 트레드용 고무 조성물 |
| CN105482201A (zh) * | 2016-01-04 | 2016-04-13 | 青岛双星轮胎工业有限公司 | 一种含氧化石墨烯的高性能轮胎 |
| JP2020007539A (ja) * | 2018-07-02 | 2020-01-16 | 株式会社ブリヂストン | 車椅子用タイヤのトレッド用ゴム組成物、及び車椅子用タイヤ |
| US11352465B2 (en) | 2016-02-10 | 2022-06-07 | Cabot Corporation | Elastomer compounds |
Families Citing this family (98)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US8796361B2 (en) | 2010-11-19 | 2014-08-05 | Ppg Industries Ohio, Inc. | Adhesive compositions containing graphenic carbon particles |
| JP2016523296A (ja) * | 2013-06-14 | 2016-08-08 | ビーエーエスエフ ソシエタス・ヨーロピアBasf Se | 電導性熱可塑性ポリウレタンから製造される加熱可能な成形品 |
| WO2014201368A1 (en) | 2013-06-15 | 2014-12-18 | Ronald Thompson | Annular ring and non-pneumatic tire |
| WO2015072183A1 (ja) * | 2013-11-12 | 2015-05-21 | 株式会社ブリヂストン | 非空気入りタイヤ |
| KR101647328B1 (ko) * | 2014-03-28 | 2016-08-23 | 한국타이어 주식회사 | 타이어 가류용 블래더 및 이를 이용하여 제조한 타이어 |
| TWI560144B (en) * | 2014-06-24 | 2016-12-01 | Graphene polymer composite material | |
| US9393462B2 (en) * | 2014-06-30 | 2016-07-19 | Acushnet Company | Golf ball with thin moisture vapor barrier layer |
| US20160053082A1 (en) | 2014-08-21 | 2016-02-25 | Azemi Samsuri | Rubber products based on improved nbr masterbatch |
| WO2016126983A1 (en) | 2015-02-04 | 2016-08-11 | Advancing Mobility, Llc. | Non-pneumatic tire and other annular devices |
| PL3271170T3 (pl) | 2015-03-20 | 2019-04-30 | Kongsberg Actuation Systems Ii Inc | Ogniotrwały zespół węża i dotyczący go sposób |
| CN104927100B (zh) * | 2015-03-27 | 2017-12-01 | 青岛科技大学 | 一种聚异戊二烯树脂复合共混材料的制备 |
| CN105525739A (zh) * | 2015-04-07 | 2016-04-27 | 上海加富新材料科技有限公司 | 防静电橡胶地板及其生产方法 |
| ITUB20153129A1 (it) * | 2015-08-14 | 2017-02-14 | Directa Plus Spa | Composizione elastomerica comprendente grafene e componenti di pneumatico comprendenti detta composizione. |
| CN105482211A (zh) * | 2015-11-20 | 2016-04-13 | 倪春仙 | 一种高尔夫练习球球心 |
| CN105348604A (zh) * | 2015-11-20 | 2016-02-24 | 青岛双星轮胎工业有限公司 | 一种采用石墨烯材料的高性能轮胎 |
| US20180272565A1 (en) * | 2015-12-03 | 2018-09-27 | Nanotek Instruments, Inc. | Chemical-free production of graphene-polymer pellets and graphene-polymer nanocomposite products |
| US11772975B2 (en) * | 2015-12-03 | 2023-10-03 | Global Graphene Group, Inc. | Chemical-free production of graphene materials |
| US11999419B2 (en) | 2015-12-16 | 2024-06-04 | Camso Inc. | Track system for traction of a vehicle |
| CN105968446B (zh) * | 2016-05-16 | 2017-10-13 | 苏州科迪流体控制设备有限公司 | 一种用于制造起重机多路阀密封垫的合成材料 |
| JP6809985B2 (ja) * | 2016-06-22 | 2021-01-06 | 三ツ星ベルト株式会社 | 摩擦伝動ベルト |
| CN105924694A (zh) * | 2016-06-28 | 2016-09-07 | 山东皓宇橡胶有限公司 | 一种用于全钢轮胎超耐磨的石墨烯材料的胎面配方 |
| CN109312137B (zh) * | 2016-07-05 | 2021-07-09 | 电化株式会社 | 丙烯酸类橡胶组合物 |
| CN106279853B (zh) * | 2016-08-10 | 2018-05-25 | 山东润通橡胶有限公司 | 一种高耐磨轮胎胎面胶的制备方法 |
| US10052524B1 (en) * | 2016-09-28 | 2018-08-21 | Callaway Golf Company | Process for incorporating graphene into a core of a golf ball |
| US10456629B1 (en) * | 2016-09-28 | 2019-10-29 | Callaway Golf Company | Graphene and carbon nanotube reinforced golf ball |
| US10039959B2 (en) * | 2016-09-28 | 2018-08-07 | Callaway Golf Company | Graphene core for a golf ball |
| US10308512B2 (en) | 2016-10-06 | 2019-06-04 | Lyten, Inc. | Microwave reactor system with gas-solids separation |
| US12281013B2 (en) | 2016-10-06 | 2025-04-22 | Lyten, Inc. | Microwave reactor system enclosing a self-igniting plasma |
| US9812295B1 (en) | 2016-11-15 | 2017-11-07 | Lyten, Inc. | Microwave chemical processing |
| FR3059668A1 (fr) * | 2016-12-02 | 2018-06-08 | Compagnie Generale Des Etablissements Michelin | Pneumatique pourvu d'un flanc externe comportant un ou plusieurs elastomeres thermoplastiques et un ou plusieurs elastomeres dieniques synthetiques |
| IT201600124360A1 (it) * | 2016-12-07 | 2018-06-07 | Bridgestone Corp | Pneumatico comprendente uno strato impermeabile ad elevata efficienza |
| CN106633259A (zh) * | 2016-12-10 | 2017-05-10 | 李晓光 | 一种船体用耐压密封圈 |
| IT201600128208A1 (it) * | 2016-12-19 | 2018-06-19 | Bridgestone Corp | Grafene come riempitivo per mescole in gomma per porzioni di pneumatico |
| FR3061188A1 (fr) * | 2016-12-22 | 2018-06-29 | Compagnie Generale Des Etablissements Michelin | Composition de caoutchouc renforcee |
| IT201700008307A1 (it) * | 2017-01-26 | 2018-07-26 | Bridgestone Corp | Nuovo agente plasticizzante per mescole in gomma |
| US9767992B1 (en) | 2017-02-09 | 2017-09-19 | Lyten, Inc. | Microwave chemical processing reactor |
| US9997334B1 (en) | 2017-02-09 | 2018-06-12 | Lyten, Inc. | Seedless particles with carbon allotropes |
| US10920035B2 (en) | 2017-03-16 | 2021-02-16 | Lyten, Inc. | Tuning deformation hysteresis in tires using graphene |
| JP7042282B2 (ja) * | 2017-03-16 | 2022-03-25 | ライテン・インコーポレイテッド | 炭素及びエラストマーの融合 |
| US9862606B1 (en) | 2017-03-27 | 2018-01-09 | Lyten, Inc. | Carbon allotropes |
| TWI614311B (zh) * | 2017-06-14 | 2018-02-11 | 台灣奈米碳素股份有限公司 | 用於製造彈性複合材料的配方、以及彈性複合材料之製造方法 |
| TWI672217B (zh) * | 2017-06-14 | 2019-09-21 | 台灣奈米碳素股份有限公司 | 胎面膠以及用於生產胎面膠的配方 |
| US11179969B2 (en) | 2017-06-15 | 2021-11-23 | Camso Inc. | Wheel comprising a non-pneumatic tire |
| CN107674252A (zh) * | 2017-09-01 | 2018-02-09 | 上海绿人生态经济环境保护研究所 | 氧化石墨烯的制备方法和产品以及轮胎胎面的制造方法 |
| US10465128B2 (en) | 2017-09-20 | 2019-11-05 | Lyten, Inc. | Cracking of a process gas |
| US11084726B2 (en) * | 2017-10-25 | 2021-08-10 | Enerage Inc. | Graphene additives and methods of preparing the same |
| GB2568723A (en) | 2017-11-24 | 2019-05-29 | Inoveight Ltd | A shoe sole with enhanced performance characteristics |
| WO2019126196A1 (en) | 2017-12-22 | 2019-06-27 | Lyten, Inc. | Structured composite materials |
| CN108003489A (zh) * | 2017-12-22 | 2018-05-08 | 恒力盛泰(厦门)石墨烯科技有限公司 | 一种含石墨烯的高导热性能轮胎内胎配方 |
| CN108129705A (zh) * | 2017-12-27 | 2018-06-08 | 四川远星橡胶有限责任公司 | 添加石墨烯的彩色胎冠胶及其制备方法 |
| WO2019132866A1 (en) * | 2017-12-27 | 2019-07-04 | Compagnie Generale Des Etablissements Michelin | Rubber compositions with reduced graphene oxide |
| WO2019143559A1 (en) | 2018-01-16 | 2019-07-25 | Lyten, Inc. | Microwave transparent pressure barrier |
| CN108641133B (zh) * | 2018-05-15 | 2020-04-24 | 浙江奋飞橡塑制品有限公司 | 抗灼烧输送带 |
| CN108841058A (zh) * | 2018-06-01 | 2018-11-20 | 湖南国盛石墨科技有限公司 | 一种高耐磨性橡胶的制备方法 |
| WO2020009887A1 (en) * | 2018-07-02 | 2020-01-09 | Callaway Golf Company | Graphene core for a golf ball with a soft cover |
| JP7247028B2 (ja) * | 2018-07-02 | 2023-03-28 | 株式会社ブリヂストン | 競技用途車椅子用タイヤのトレッド用ゴム組成物、及び競技用途車椅子用タイヤ |
| KR102733729B1 (ko) | 2018-08-09 | 2024-11-26 | 라이텐, 인코포레이티드 | 전자기 상태 감지 디바이스들 |
| KR101955161B1 (ko) * | 2018-09-18 | 2019-03-06 | 삼일전기공업 주식회사 | 그래핀 면진장치를 갖는 수배전반 |
| WO2020092794A1 (en) * | 2018-10-31 | 2020-05-07 | Compagnie Generale Des Etablissements Michelin | Non-rubber masterbatches of nanoparticles |
| JP7275559B2 (ja) * | 2018-12-18 | 2023-05-18 | 住友ゴム工業株式会社 | テニスボール用ゴム組成物 |
| JP7176396B2 (ja) * | 2018-12-18 | 2022-11-22 | 住友ゴム工業株式会社 | テニスボール用ゴム組成物 |
| US11555761B1 (en) | 2019-03-27 | 2023-01-17 | Lyten, Inc. | Sensors incorporated into elastomeric components to detect physical characteristic changes |
| US12313570B2 (en) | 2019-03-27 | 2025-05-27 | Lyten, Inc. | Leaky coaxial resonant sensor systems and methods |
| US11479062B2 (en) | 2019-03-27 | 2022-10-25 | Lyten, Inc. | Tuned radio frequency (RF) resonant materials and material configurations for sensing in a vehicle |
| US12270785B2 (en) | 2019-03-27 | 2025-04-08 | Lyten, Inc. | Water droplet sensing systems and methods |
| US11719582B2 (en) | 2019-03-27 | 2023-08-08 | Lyten, Inc. | Sensors incorporated into tire plies to detect reversible deformation and/or temperature changes |
| US12265058B2 (en) | 2019-03-27 | 2025-04-01 | Lyten, Inc. | Sensors incorporated into adhesive material |
| US12317466B2 (en) | 2019-03-27 | 2025-05-27 | Lyten, Inc. | Frequency selective metamaterial for protective enclosures |
| US12196636B2 (en) | 2019-03-27 | 2025-01-14 | Lyten, Inc. | Sensors incorporated into airborne vehicle components to detect physical characteristic changes |
| US12339272B2 (en) | 2019-03-27 | 2025-06-24 | Lyten, Inc. | Sensors incorporated into building materials to detect physical characteristic changes |
| US11965803B2 (en) | 2019-03-27 | 2024-04-23 | Lyten, Inc. | Field deployable resonant sensors |
| US11585731B2 (en) * | 2019-03-27 | 2023-02-21 | Lyten, Inc. | Sensors incorporated into semi-rigid structural members to detect physical characteristic changes |
| US11555748B2 (en) * | 2019-03-27 | 2023-01-17 | Lyten, Inc. | Sensors incorporated into tire plies to detect reversible deformation and/or temperature changes |
| US11472233B2 (en) | 2019-03-27 | 2022-10-18 | Lyten, Inc. | Tuned radio frequency (RF) resonant materials |
| CN111218068A (zh) * | 2019-04-23 | 2020-06-02 | 烟台桑尼橡胶有限公司 | 一种含石墨烯的高耐磨橡胶坝、气盾坝配方及其制备工艺 |
| CN110367649A (zh) * | 2019-06-01 | 2019-10-25 | 姜友文 | 单面上胶制鞋方法 |
| CN110628102B (zh) * | 2019-10-18 | 2021-05-18 | 福州大学 | 一种抗紫外光老化耐磨雨鞋的制备方法 |
| US11309545B2 (en) | 2019-10-25 | 2022-04-19 | Lyten, Inc. | Carbonaceous materials for lithium-sulfur batteries |
| US11489161B2 (en) | 2019-10-25 | 2022-11-01 | Lyten, Inc. | Powdered materials including carbonaceous structures for lithium-sulfur battery cathodes |
| KR102191484B1 (ko) * | 2019-11-13 | 2020-12-15 | 넥센타이어 주식회사 | 타이어 인너라이너 고무 조성물 및 이로부터 제조된 타이어 |
| CN111154152B (zh) * | 2020-01-15 | 2021-08-10 | 福建五持恒科技发展有限公司 | 石墨烯天然橡胶高分子登山鞋底复合发泡材料及其制备方法 |
| KR102509168B1 (ko) * | 2020-10-30 | 2023-03-13 | 금호타이어 주식회사 | 공기입 타이어용 비드 어셈블리 및 그 제조방법 |
| CN112625308A (zh) * | 2020-12-11 | 2021-04-09 | 福建五持恒科技发展有限公司 | 一种石墨烯抗静电医用鞋底复合材料及其制备方法 |
| US12428301B1 (en) | 2021-03-26 | 2025-09-30 | Alvin T. Rockhill | Graphene composition |
| US11655355B2 (en) | 2021-05-11 | 2023-05-23 | Akron Polymer Solutions, Inc. | Graphene as additive for rubber compounds and products |
| CN113337017A (zh) * | 2021-05-24 | 2021-09-03 | 福建五持恒科技发展有限公司 | 一种石墨烯橡胶高分子远红外线复合发泡材料 |
| US11738599B2 (en) | 2021-07-15 | 2023-08-29 | Akron Polymer Solutions, Inc. | Graphene as additive in silica tread applications |
| US11753529B2 (en) * | 2021-07-15 | 2023-09-12 | Akron Polymer Solutions, Inc. | Graphene as additive in sidewall applications |
| US11597821B2 (en) | 2021-07-15 | 2023-03-07 | Akron Polymer Solutions, Inc. | Graphene as additive in truck tire tread applications |
| US12344038B2 (en) | 2021-07-15 | 2025-07-01 | Akron Polymer Solutions, Inc | Aircraft tire |
| GB2610394A (en) * | 2021-09-01 | 2023-03-08 | Haydale Graphene Ind Plc | Shoe sole |
| WO2023114895A1 (en) * | 2021-12-16 | 2023-06-22 | Akron Polymer Solutions, Inc. | Aircraft tire |
| CN114517013B (zh) * | 2022-03-01 | 2022-08-05 | 青岛科技大学 | 一种阻燃输送带用滚筒摩擦助剂及其制备方法 |
| CN114773696A (zh) * | 2022-05-05 | 2022-07-22 | 江苏巨能橡塑科技有限公司 | 一种重载导静电实心轮胎胎面胶料及其制备方法 |
| US12031027B2 (en) | 2022-06-06 | 2024-07-09 | Akron Polymer Solutions, Inc. | Conveyor belt cover compound |
| CN114957813A (zh) * | 2022-06-09 | 2022-08-30 | 温州市利步达鞋业有限公司 | 一种石墨烯改性劳保鞋鞋底及其制作方法 |
| US20240273648A1 (en) | 2023-02-15 | 2024-08-15 | Lyten, Inc. | System and method for tracking indirect greenhouse gas emissions throughout a product's lifecycle |
| US12338339B2 (en) * | 2023-06-27 | 2025-06-24 | Contitech Deutschland Gmbh | Power transmission belt with conductive rubber mixture having graphene |
Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| WO2010107769A2 (en) * | 2009-03-16 | 2010-09-23 | Aksay Ilhan A | Tire cords |
| US20100324200A1 (en) * | 2007-12-18 | 2010-12-23 | Societe De Technologie Michelin | Rubber Composition in Particular for the Manufacture of Tires |
| US20110060086A1 (en) * | 2009-09-10 | 2011-03-10 | Michael Brendan Rodgers | Elastomeric Copolymers, Copolymer Compositions, and Their Use in Articles |
| US7999027B2 (en) * | 2009-08-20 | 2011-08-16 | Nanotek Instruments, Inc. | Pristine nano graphene-modified tires |
| US8047248B2 (en) * | 2005-10-14 | 2011-11-01 | The Trustees Of Princeton University | Tire containing thermally exfoliated graphite oxide |
Family Cites Families (9)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US7745528B2 (en) * | 2006-10-06 | 2010-06-29 | The Trustees Of Princeton University | Functional graphene-rubber nanocomposites |
| FR2916449B1 (fr) * | 2007-05-25 | 2009-08-21 | Michelin Soc Tech | Gomme interieure de pneumatique. |
| US9546092B2 (en) * | 2008-02-05 | 2017-01-17 | The Trustees Of Princeton University | Functionalized graphene sheets having high carbon to oxygen ratios |
| FR2929949B1 (fr) * | 2008-04-11 | 2010-04-16 | Michelin Soc Tech | Pneumatique ayant une gomme de bordure de nappe faiblement hysterique. |
| WO2010107763A1 (en) * | 2009-03-16 | 2010-09-23 | Aksay Ilhan A | Reinforced polymeric articles |
| US9117568B2 (en) * | 2009-04-03 | 2015-08-25 | Vorbeck Materials Corp. | Polymer compositions containing carbonaceous fillers |
| JP5440028B2 (ja) * | 2009-08-27 | 2014-03-12 | 横浜ゴム株式会社 | 空気入りタイヤ |
| KR20110091254A (ko) * | 2010-02-05 | 2011-08-11 | 넥센타이어 주식회사 | 기계적 물성 및 전기 전도도를 향상시킨 타이어 트레드용 고무 조성물 |
| US20130296479A1 (en) * | 2012-05-03 | 2013-11-07 | Ppg Industries Ohio, Inc. | Rubber formulations including graphenic carbon particles |
-
2012
- 2012-12-12 CN CN201280060998.3A patent/CN104136237A/zh active Pending
- 2012-12-12 US US13/712,948 patent/US20130150516A1/en not_active Abandoned
- 2012-12-12 WO PCT/US2012/069304 patent/WO2013090464A1/en not_active Ceased
- 2012-12-12 EP EP12858164.2A patent/EP2790926A4/en not_active Withdrawn
- 2012-12-12 KR KR1020147015060A patent/KR20140105732A/ko not_active Ceased
- 2012-12-12 JP JP2014547391A patent/JP6404121B2/ja not_active Expired - Fee Related
-
2018
- 2018-05-07 JP JP2018089135A patent/JP2018150549A/ja active Pending
Patent Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US8047248B2 (en) * | 2005-10-14 | 2011-11-01 | The Trustees Of Princeton University | Tire containing thermally exfoliated graphite oxide |
| US20100324200A1 (en) * | 2007-12-18 | 2010-12-23 | Societe De Technologie Michelin | Rubber Composition in Particular for the Manufacture of Tires |
| WO2010107769A2 (en) * | 2009-03-16 | 2010-09-23 | Aksay Ilhan A | Tire cords |
| US7999027B2 (en) * | 2009-08-20 | 2011-08-16 | Nanotek Instruments, Inc. | Pristine nano graphene-modified tires |
| US20110060086A1 (en) * | 2009-09-10 | 2011-03-10 | Michael Brendan Rodgers | Elastomeric Copolymers, Copolymer Compositions, and Their Use in Articles |
Non-Patent Citations (1)
| Title |
|---|
| See also references of EP2790926A4 * |
Cited By (8)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JP2015517583A (ja) * | 2012-05-03 | 2015-06-22 | ピーピージー インダストリーズ オハイオ,インコーポレイティド | グラフェンカーボン粒子を含むゴム配合物 |
| CN104292528A (zh) * | 2013-07-18 | 2015-01-21 | 宁波大学 | 一种高强度橡胶及其制备方法 |
| CN103408855A (zh) * | 2013-08-29 | 2013-11-27 | 滁州旭中化工有限公司 | 一种含氧化石墨烯橡胶复合材料 |
| KR101571666B1 (ko) * | 2013-12-31 | 2015-11-25 | 현대자동차주식회사 | 타이어 트레드용 고무 조성물 |
| CN105482201A (zh) * | 2016-01-04 | 2016-04-13 | 青岛双星轮胎工业有限公司 | 一种含氧化石墨烯的高性能轮胎 |
| US11352465B2 (en) | 2016-02-10 | 2022-06-07 | Cabot Corporation | Elastomer compounds |
| JP2020007539A (ja) * | 2018-07-02 | 2020-01-16 | 株式会社ブリヂストン | 車椅子用タイヤのトレッド用ゴム組成物、及び車椅子用タイヤ |
| JP7213152B2 (ja) | 2018-07-02 | 2023-01-26 | 株式会社ブリヂストン | 車椅子用タイヤのトレッド用ゴム組成物、及び車椅子用タイヤ |
Also Published As
| Publication number | Publication date |
|---|---|
| EP2790926A1 (en) | 2014-10-22 |
| CN104136237A (zh) | 2014-11-05 |
| US20130150516A1 (en) | 2013-06-13 |
| JP2015501873A (ja) | 2015-01-19 |
| JP2018150549A (ja) | 2018-09-27 |
| JP6404121B2 (ja) | 2018-10-10 |
| EP2790926A4 (en) | 2015-04-15 |
| KR20140105732A (ko) | 2014-09-02 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US20130150516A1 (en) | Rubber Compositions Comprising Graphene and Reinforcing Agents and Articles Made Therefrom | |
| RU2602142C2 (ru) | Резиновые композиции, включающие в себя графеновые углеродные частицы | |
| EP4013628B1 (en) | Silica-graphenic carbon composite particles and elastomeric materials including such particles | |
| EP2658910B1 (en) | Rubber composition with improved bis-silane reinforcement | |
| KR20030025875A (ko) | Bet/ctab 비가 높은 침강 실리카 | |
| EP3237529A1 (en) | Hemp oil-containing rubber compositions and related methods | |
| Blume et al. | Silica and silanes | |
| JP2009518487A (ja) | ゴム及び変性された層状の複水酸化物を含むナノコンポジット物質、その製造方法及びその使用 | |
| US11753529B2 (en) | Graphene as additive in sidewall applications | |
| US6852786B2 (en) | Rubber mixture that can be cross-linked by sulfur, method for the production thereof, and cross-linked rubber mixtures and shaped bodies that can be obtained therefrom | |
| EP3237526B1 (en) | Tire comprising an oil-containing rubber composition | |
| US11597821B2 (en) | Graphene as additive in truck tire tread applications | |
| US11535725B1 (en) | Azodicarboxy additives for rubber compositions | |
| US11738599B2 (en) | Graphene as additive in silica tread applications | |
| EP4198082B1 (en) | Rubber composition and tire containing graphene | |
| Zaeimoedin | Development of ENR-based compounds for green tyre tread applications with improved performance, processing characteristics and sustainability | |
| CN120283020A (zh) | 再生炭黑、橡胶组合物和轮胎 | |
| TW202110737A (zh) | 二氧化矽-石墨烯碳複合粒子及包括此等粒子之彈性體材料 | |
| JP2009155483A (ja) | ジエン系ゴム組成物 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| 121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 12858164 Country of ref document: EP Kind code of ref document: A1 |
|
| ENP | Entry into the national phase |
Ref document number: 20147015060 Country of ref document: KR Kind code of ref document: A |
|
| ENP | Entry into the national phase |
Ref document number: 2014547391 Country of ref document: JP Kind code of ref document: A |
|
| NENP | Non-entry into the national phase |
Ref country code: DE |