WO2012111437A1 - Balle de golf - Google Patents

Balle de golf Download PDF

Info

Publication number
WO2012111437A1
WO2012111437A1 PCT/JP2012/052320 JP2012052320W WO2012111437A1 WO 2012111437 A1 WO2012111437 A1 WO 2012111437A1 JP 2012052320 W JP2012052320 W JP 2012052320W WO 2012111437 A1 WO2012111437 A1 WO 2012111437A1
Authority
WO
WIPO (PCT)
Prior art keywords
core
golf ball
intermediate layer
cover
outer cover
Prior art date
Application number
PCT/JP2012/052320
Other languages
English (en)
Japanese (ja)
Inventor
美文 宮田
中　裕里
二宮　徳数
藤川　良宏
雅史 宇田
淳之介 和田
Original Assignee
美津濃株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 美津濃株式会社 filed Critical 美津濃株式会社
Priority to JP2012557875A priority Critical patent/JPWO2012111437A1/ja
Publication of WO2012111437A1 publication Critical patent/WO2012111437A1/fr

Abstract

La présente invention concerne une balle de golf qui possède une excellente résistance aux rayures et d'excellentes performances de rotation ainsi qu'une bonne résilience. La balle est pourvue d'un noyau (3), d'une couche intermédiaire (5) formée afin de recouvrir le noyau (3), d'une couverture intérieure (7) formée afin de recouvrir la couche intermédiaire (5), et d'une couverture extérieure (15) formée afin de recouvrir la couverture intérieure (7). La couverture extérieure (15) comprend un produit neutralisé qui contient un terpolymère éthylène - acide carboxylique non saturé - alkyl (méth)acrylate qui possède un poids moléculaire moyen pondéral (Mw) de 80 000 à 500 000, et un copolymère éthylène - acide acrylique ou éthylène - acide méthacrylique qui possède un poids moléculaire moyen pondéral (Mw) de 2 000 à 30 000. La couverture intérieure (7) comprend également ledit produit neutralisé mélangé.
PCT/JP2012/052320 2011-02-17 2012-02-01 Balle de golf WO2012111437A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2012557875A JPWO2012111437A1 (ja) 2011-02-17 2012-02-01 ゴルフボール

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011032329 2011-02-17
JP2011-032329 2011-02-17

Publications (1)

Publication Number Publication Date
WO2012111437A1 true WO2012111437A1 (fr) 2012-08-23

Family

ID=46653213

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/052320 WO2012111437A1 (fr) 2011-02-17 2012-02-01 Balle de golf

Country Status (4)

Country Link
US (1) US20120214614A1 (fr)
JP (1) JPWO2012111437A1 (fr)
TW (1) TW201238625A (fr)
WO (1) WO2012111437A1 (fr)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140357422A1 (en) * 2013-05-31 2014-12-04 Nike, Inc. Thermoplastic multi-layer golf ball
US10016661B2 (en) * 2016-04-06 2018-07-10 Acushnet Company Methods for making golf ball components using three-dimensional additive manufacturing systems

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1189967A (ja) * 1997-09-16 1999-04-06 Bridgestone Sports Co Ltd ゴルフボール
WO2005120651A1 (fr) * 2004-06-09 2005-12-22 Mizuno Corporation Balle de golf multicomposant et méthode pour la fabriquer
JP2006500995A (ja) * 2002-09-27 2006-01-12 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー 柔軟で弾性のある二峰性アイオノマーのカバーを有するゴルフボール
JP2011005256A (ja) * 2009-06-26 2011-01-13 Acushnet Co 硬度が変化する特別領域を具備する単一層コアを有するゴルフボール

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3453024B2 (ja) * 1996-04-24 2003-10-06 ブリヂストンスポーツ株式会社 ゴルフボール
US6562906B2 (en) * 2000-08-11 2003-05-13 E. I. Du Pont De Nemours And Company Bi-modal ionomers
US6955613B2 (en) * 2003-01-10 2005-10-18 Mizuno Corporation Multi-piece golf ball and manufacturing method thereof
AU2004226529B2 (en) * 2003-03-31 2008-04-10 Mizuno Corporation Multi-piece golf ball, method of manufacturing the same, and molding die used for manufacturing the same
WO2005089883A1 (fr) * 2004-03-19 2005-09-29 Mizuno Corporation Balle de golf multipièce et procede de fabrication de ladite balle
US7744494B2 (en) * 2005-05-24 2010-06-29 Acushnet Company Multi-modal ionomeric golf ball compositions

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1189967A (ja) * 1997-09-16 1999-04-06 Bridgestone Sports Co Ltd ゴルフボール
JP2006500995A (ja) * 2002-09-27 2006-01-12 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー 柔軟で弾性のある二峰性アイオノマーのカバーを有するゴルフボール
WO2005120651A1 (fr) * 2004-06-09 2005-12-22 Mizuno Corporation Balle de golf multicomposant et méthode pour la fabriquer
JP2011005256A (ja) * 2009-06-26 2011-01-13 Acushnet Co 硬度が変化する特別領域を具備する単一層コアを有するゴルフボール

Also Published As

Publication number Publication date
TW201238625A (en) 2012-10-01
JPWO2012111437A1 (ja) 2014-07-03
US20120214614A1 (en) 2012-08-23

Similar Documents

Publication Publication Date Title
JP4214003B2 (ja) マルチピースソリッドゴルフボール
JP5538402B2 (ja) ゴルフボール
JP4373189B2 (ja) ゴルフボール
JP5247425B2 (ja) ゴルフボール
JP2004136075A (ja) マルチピースソリッドゴルフボール
JP4398351B2 (ja) ゴルフボール
JP5398167B2 (ja) ゴルフボール
JPWO2005120651A1 (ja) マルチピースゴルフボール及びその製造方法
US9005050B2 (en) Golf ball
JP2000300695A (ja) マルチピースソリッドゴルフボール
JP6451309B2 (ja) ゴルフボール用樹脂組成物及びゴルフボール
JP4072344B2 (ja) マルチピースソリッドゴルフボール
JP2007275268A (ja) ゴルフボール
JP4463694B2 (ja) ゴルフボール
JP4097517B2 (ja) マルチピースソリッドゴルフボール
US6723009B2 (en) Three-piece solid golf ball
CN103874531A (zh) 相对于低摆动在高挥杆速度下具有增加的初速度的多芯高尔夫球
WO2012111437A1 (fr) Balle de golf
JP5312292B2 (ja) ゴルフボール
JP5322571B2 (ja) ゴルフボール
JP2002355342A (ja) マルチピースソリッドゴルフボール
JP4463695B2 (ja) ゴルフボール
JP2004242850A (ja) マルチピースソリッドゴルフボール
JP2003325702A (ja) スリーピースソリッドゴルフボール
JP4948502B2 (ja) ゴルフボール

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12746768

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2012557875

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12746768

Country of ref document: EP

Kind code of ref document: A1