WO2012011188A1 - 太陽電池およびその製造方法、並びに太陽電池の製造装置 - Google Patents

太陽電池およびその製造方法、並びに太陽電池の製造装置 Download PDF

Info

Publication number
WO2012011188A1
WO2012011188A1 PCT/JP2010/062420 JP2010062420W WO2012011188A1 WO 2012011188 A1 WO2012011188 A1 WO 2012011188A1 JP 2010062420 W JP2010062420 W JP 2010062420W WO 2012011188 A1 WO2012011188 A1 WO 2012011188A1
Authority
WO
WIPO (PCT)
Prior art keywords
solar cell
cyan
silicon substrate
containing solution
less
Prior art date
Application number
PCT/JP2010/062420
Other languages
English (en)
French (fr)
Inventor
小林　光
Original Assignee
株式会社Ｋｉｔ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社Ｋｉｔ filed Critical 株式会社Ｋｉｔ
Priority to JP2012525285A priority Critical patent/JP5717743B2/ja
Priority to PCT/JP2010/062420 priority patent/WO2012011188A1/ja
Priority to TW100125049A priority patent/TWI544653B/zh
Publication of WO2012011188A1 publication Critical patent/WO2012011188A1/ja

Abstract

　本発明の１つの太陽電池の製造方法は、シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内に、シリコン基板又はそのシリコン基板から形成される太陽電池を浸漬する浸漬工程を含んでいる。この製造方法により、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面及び／又はｐｎ接合表面領域に存在する欠陥準位の低減化が図られる。また、シアン化物イオン（ＣＮ－）の存在によって、シリコン基板表面上に存在した金属等の汚染も適切に除去される。その結果、太陽電池の高効率化が図られる。

Description

太陽電池およびその製造方法、並びに太陽電池の製造装置
　本発明は、太陽電池および太陽電池の製造方法、並びに太陽電池の製造装置に関する。本発明は、特に、表面の金属等による汚染が低減された半導体を備える太陽電池およびその製造方法、並びにその太陽電池の製造装置に関するものである。
　半導体等の基板表面の金属等による汚染を除去することの可能なシアン（ＣＮ）含有洗浄液としては、すでに幾つかの溶液が開示されている。例えば、シアン化水素（ＨＣＮ）を、純水、超純水、アルコール系溶媒、ケトン系溶媒、ニトリル系溶媒、芳香族炭化水素系溶媒、四塩化炭素、エーテル系溶媒、脂肪族アルカン系溶媒、またはこれらの混合溶媒に溶解させた溶液が洗浄液として存在する。加えて、その洗浄液は、所定濃度に希釈されるともに、アンモニア水溶液等を用いて、その洗浄液中の水素イオン濃度指数、いわゆるｐＨ値を、５～１２、好ましくは６～９の範囲に調整して用いられる。その結果、半導体等の基板表面の銅（Ｃｕ）等の汚染金属の除去作用が得られることが開示されている（特許文献１参照）。
　また、本願発明者は、環境負荷を軽減するために、溶液中のシアン化水素（ＨＣＮ）を０．１ｍＭ（ミリモル）、すなわち約２．７ｐｐｍまで希薄した上で、ｐＨ１０とし、かつ２５℃の室温下において、Ｃｕの表面濃度の低減に成功している。具体的には、本願発明者は、洗浄処理前のＣｕの表面濃度１０１３～１０１４原子／ｃｍ２を、その洗浄処理によって、全反射蛍光Ｘ線分析装置による銅の検出限界（～３×１０９原子／ｃｍ２）以下にまで低減できることを示した（例えば、非特許文献１参照）。
　また、本願発明者は、球状シリコン（Ｓｉ　ｂａｌｌｓ）に対して、シアン化水素（ＨＣＮ）水溶液を用いた洗浄処理を行い、その洗浄能力が高いことを確認した（例えば、非特許文献２参照）。
特開平２００５－３９１９８号公報
東裕子、外３名，「極低濃度欠陥消滅型半導体洗浄液によるＳｉＯ２表面上の汚染Ｃｕの除去」，２００８年（平成２０年）秋季第６９回応用物理学会学術講演会講演予稿集，　２００８年９月，　Ｎｏ．２，　ｐ．６９２ 高橋昌男（Ｍ．　Ｔａｋａｈａｓｈｉ）、外４名，"Ｓｉｌｉｃｏｎ　ｃｌｅａｎｉｎｇ　ａｎｄ　ｄｅｆｅｃｔ　ｐａｓｓｉｖａｔｉｏｎ　ｅｆｆｅｃｔｓ　ｏｆ　ｈｙｄｒｏｇｅｎ　ｃｙａｎｉｄｅ　ａｑｕｅｏｕｓ　ｓｏｌｕｔｉｏｎ"，Ｓｏｌｉｄ　Ｓｔａｔｅ　Ｃｏｍｍｕｎｉｃａｔｉｏｎｓ，　ＥＬＳＥＶＩＥＲ　Ｌｔｄ．，　２００５年１２月１日，　Ｖｏｌ．１３７，　ｐ．２６３－２６７
　しかしながら、上述のシアン化水素の溶液を用いた処理は、上述の半導体等の基板表面洗浄のみならず欠陥準位の低減にも寄与するため、処理対象物（半導体等）の種類、あるいはその用途に適合する活用方法を見出すことが容易でない場合があることが明らかとなってきた。特に、日進月歩の開発が進む単結晶シリコンや多結晶シリコンを用いた太陽電池のさらなる高効率化に向けて上述の処理を活用するためには、より一層の工夫が要求される。
　本発明は、太陽電池の高性能化に大きく貢献するものである。
　本願発明者は、太陽電池に用いられる半導体の表面や裏面、及び／又はｐｎ接合界面やｐｎ接合表面の適切な制御が太陽電池の高効率化に少なからず寄与すると判断し、鋭意研究を行った。その結果、本願発明者は、これまでの研究結果とは別の特殊な手段を採用することにより、高効率化に悪影響を及ぼす半導体表面や裏面、及び／又はｐｎ接合界面やｐｎ接合表面やｐｎ接合表面近傍の欠陥準位を可能な限り低減する有効な道筋を見出した。さらに、研究を重ねた結果、半導体表面形状に対する配慮を行いつつ、その欠陥準位の低減を実現する手段も見出された。本願発明は、そのような観点から創出された。
本発明の１つの太陽電池の製造方法は、シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内にシリコン基板又はそのシリコン基板から形成される太陽電池を浸漬する浸漬工程を含む。
　この太陽電池の製造方法によれば、少な過ぎない適度な量のシアン化物イオン（ＣＮ－）の存在によって、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面及び／又はｐｎ接合界面に存在するダングリングボンド等に起因する欠陥準位の低減化が図られる。また、シアン化物イオン（ＣＮ－）の存在によって、シリコン基板表面上に存在した金属等の汚染も適切に除去される。その結果、太陽電池の高効率化が図られる。また、前述のとおり、シアン化物イオン（ＣＮ－）の濃度が比較的高いため、ＣＮ－イオンがシリコン内に浸透し、シリコン内の欠陥消滅と金属除去が行われ得る。
　なお、上述の浸漬工程において、上述のシリコン基板又は上述の太陽電池が反射防止膜を備えるとともに、上述のシアン含有溶液の水素イオン濃度指数（ｐＨ）が、９．５以上１４以下であることは、より好ましい一態様である。ｐＨが高ければＨＣＮの電離確率が増加するため、太陽電池の高効率化の妨げとなる欠陥の消滅や、基板表面の金属汚染の除去に寄与するシアン化物イオン（ＣＮ－）の濃度が増加する。一方で、ｐＨが高いほど、シアン含有溶液によってシリコン基板がエッチングされるために高効率化の障害となる可能性が高まる。そこで、上述の太陽電池が反射防止膜を備えることにより、その反射防止膜が、シアン含有溶液によるシリコン基板のエッチングに対する防壁の役割を果たすことになる。他方、ｐＨが１４を超える設定にすることは困難であるとともに、ｐＨが１３～１４においてＨＣＮの電離確率がほぼ１００％になるため、ｐＨが１４を超える必要性に乏しい。
　また、本発明の１つの太陽電池の製造装置は、シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内に、シリコン基板又はそのシリコン基板から形成される太陽電池を浸漬する浸漬処理部を備えている。
　この太陽電池の製造装置によれば、少な過ぎない適度な量のシアン化物イオン（ＣＮ－）の存在によって、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面や裏面、及び／又はｐｎ接合界面やｐｎ接合表面に存在するダングリングボンド等に起因する欠陥準位の低減化が図られる。また、シアン化物イオン（ＣＮ－）の存在によって、シリコン基板表面上に存在した金属等の汚染も適切に除去される。その結果、太陽電池の高効率化が図られる。また、前述のとおり、シアン化物イオン（ＣＮ－）の濃度が比較的高いため、ＣＮ－イオンがシリコン内に浸透し、シリコン内の欠陥消滅と金属除去が行われ得る。なお、多結晶シリコン基板を用いた場合は、結晶粒界を通じてシアン化物イオン（ＣＮ－）が拡散され易いため、上述の効果がより高くなる。
　なお、反射防止膜を備える上述のシリコン基板又は上述の太陽電池を浸漬する上述の浸漬処理部を備えるとともに、上述のシアン含有溶液の水素イオン濃度指数（ｐＨ）が、９．５以上１４以下であることは、既に述べたとおり、ＨＣＮの電離確率が増加とシリコン基板表面のエッチング防止の観点から、より好ましい一態様である。
　また、本発明の１つの太陽電池は、シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内に、シリコン基板又はそのシリコン基板から形成される太陽電池を浸漬することにより形成される前述のシリコン基板の表面を備えている。
　この太陽電池は、少な過ぎない適度な量のシアン化物イオン（ＣＮ－）の存在によって、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面及び／又はｐｎ接合界面に存在するダングリングボンド等に起因する欠陥準位の低減化が図られている。また、シアン化物イオン（ＣＮ－）の存在によって、シリコン基板表面上に存在した金属等の汚染も適切に除去されているため、高効率化の太陽電池が得られる。また、前述のとおり、シアン化物イオン（ＣＮ－）の濃度が比較的高いため、ＣＮ－イオンがシリコン内に浸透によるシリコン内の欠陥消滅と金属除去がなされた太陽電池が得られる。
　ところで、本出願において「シリコン基板」とは、単結晶シリコン基板や多結晶シリコン基板のみならず、ガラス基板、プラスティック基板、金属基板等の表面上に公知の手法（プラズマＣＶＤ法など）によって形成されるシリコン層、シリコン薄膜も含まれる。
　本発明の１つの太陽電池の製造方法及び本発明の１つの太陽電池の製造装置によれば、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面や裏面、及び／又はｐｎ接合界面やｐｎ接合表面やｐｎ接合領域（ｐ型シリコン基板の場合は表面近傍のｎ型層）に存在する欠陥準位の低減化が図られる。また、シアン化物イオン（ＣＮ－）の存在によって、シリコン基板表面上に存在した金属等の汚染も適切に除去される。その結果、太陽電池の高効率化が図られる。また、本発明の１つの太陽電池によれば、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面及び／又はｐｎ接合領域（ｐ型シリコン基板の場合は表面近傍のｎ型層）に存在するダングリングボンド等に起因する欠陥準位の低減化が図られている。また、シアン化物イオン（ＣＮ－）の存在によって、シリコン基板表面上に存在した金属等の汚染も適切に除去されているため、高効率化の太陽電池が得られる。
本発明の第１の実施形態における太陽電池の主たる部分の断面構造の概要説明図である。 本発明の第２の実施形態における太陽電池の主たる部分の断面構造の概要説明図である。
　つぎに、本発明の実施形態を、添付する図面に基づいて詳細に述べる。尚、この説明に際し、全図にわたり、特に言及がない限り、共通する部分には共通する参照符号が付されている。なお、図中、本実施形態の要素は必ずしも互いの縮尺を保って記載されるものではない。
＜第１の実施形態＞
　本実施形態では、図１に示す構造を備える太陽電池を、シアン（ＣＮ）濃度が２７００ｐｐｍ（０．２７ｗｔ％）であって、水素イオン濃度指数（ｐＨ値）が１０に調整されたシアン化水素（ＨＣＮ）水溶液中に浸漬する前後における変換効率の変化を調べた。
　まず、本実施形態の太陽電池１００，２００の構造及びその製造方法について説明する。図１は、本実施形態の太陽電池１００，２００の主たる部分の断面構造の概要説明図である。本実施形態の太陽電池１００，２００の製造工程は次のとおりである。まず、ｐ型の単結晶シリコン基板１０（基板サイズ：１２５ｍｍ角、比抵抗：約１０Ω・ｃｍ）に対してｎ型拡散層２０が公知の手法を用いて形成されることにより、単結晶シリコン基板１０内にｐｎ接合が形成される。次に、そのｎ型拡散層２０の表面上に反射防止膜３０として二酸化チタン（ＴｉＯ２）膜が、図示しない公知の成膜手法（反射防止膜形成部）を用いて公知の手法（例えば、スピン塗布法）により形成される。
　その後、上述の反射防止膜３０上に、表面電極４０として銀電極が形成される。加えて、単結晶シリコン基板１０の裏面側に、裏面電極５０としてアルミニウム電極が形成される。
　上述のように形成された太陽電池１００について、擬似太陽光（ＡＭ１．５　１００ｍＷ／ｃｍ２）の照射下において電流－電圧曲線が観測された。
　その後、太陽電池１００が、シアン（ＣＮ）濃度が２７００ｐｐｍ（０．２７ｗｔ％）であって、水素イオン濃度指数（ｐＨ値）が１０に調整されたＨＣＮ水溶液を収容する浸漬処理部（図示しない）において浸漬処理される。このときのＨＣＮ水溶液の温度は、約２５℃（室温）であり、浸漬時間は２分間であった。このようにして、太陽電池２００が製造される。
　この太陽電池２００についても、擬似太陽光（ＡＭ１．５　１００ｍＷ／ｃｍ２）の照射下において電流－電圧曲線が観測された。
　表１は、上述のＨＣＮ水溶液中に浸漬する前後における太陽電池１００，２００の短絡光電流密度（Ａ／ｃｍ２）、開放光起電力（Ｖ）、曲線因子、及び変換効率（％）の変化を示している。なお、これらの測定の再現性を確認するために、上述の太陽電池１００，２００が２つずつ作製された。
Figure JPOXMLDOC01-appb-T000001
　表１から分かるように、ＨＣＮ水溶液への浸漬前の太陽電池１００に対して、ＨＣＮ水溶液への浸漬後の太陽電池２００は、短絡光電流密度（Ａ／ｃｍ２）、開放光起電力（Ｖ）、曲線因子、及び変換効率（％）のいずれの指標も顕著に向上している。特に、太陽電池１００に対して、太陽電池２００の変換効率が約１２％も向上することが分かった。
　従って、反射防止膜を備える太陽電池に対して、２７００ｐｐｍという比較的高濃度であり、かつｐＨ値が高く制御されたＨＣＮ水溶液を用いた浸漬処理を行うにより、太陽電池の高効率化に大きく寄与することが分かる。本願発明者は、このような現象が見られたのは、ＨＣＮ水溶液が比較的高濃度に設定されたこととｐＨ値の適切な制御による電離確率の増加とが相俟って、ＣＮ－イオンの一部が反射防止膜３０を通過して単結晶シリコン基板１０に到達し、欠陥準位を消滅させたためと考えている。
＜第２の実施形態＞
　本実施形態の太陽電池３００は、第１の実施形態における単結晶シリコン基板１０を多結晶シリコン基板３１０に代え、反射防止膜３３０として窒化シリコン膜を採用し、その窒化シリコン膜を形成する順序を変更したこと以外は第１の実施形態と同様に行われた。従って、第１の実施形態と重複する説明は省略され得る。
　図２は、本実施形態の太陽電池３００の主たる部分の断面構造の概要説明図である。本実施形態の太陽電池３００の製造工程は次のとおりである。まず、ｐ型の多結晶シリコン基板３１０（基板サイズ：１２５ｍｍ角、比抵抗：約１０Ω・ｃｍ）に対してｎ型拡散層３２０が公知の手法を用いて形成されることにより、多結晶シリコン基板３１０内にｐｎ接合が形成される。なお、表面電極と裏面電極が形成されれば、この段階でも実質的に太陽電池としての機能を発揮できる構造となる。従って、本出願においては、このｐｎ接合が形成された多結晶シリコン基板３１０も太陽電池に含まれるものとする。
　次に、本実施形態では、第１の実施形態における浸漬処理部において、ｐｎ接合が形成された多結晶シリコン基板３１０が、シアン（ＣＮ）濃度が５４０ｐｐｍであって、水素イオン濃度指数（ｐＨ値）が８．５に調整されたＨＣＮ水溶液中に浸漬される。このときのＨＣＮ水溶液の温度は、約２５℃（室温）であり、浸漬時間は２分間であった。なお、本実施形態では、この浸漬時間が、１分以上１０分程度までの実用的短時間内に行われることは特筆に値する。
　その後、ｎ型拡散層３２０の表面上に反射防止膜３３０として窒化シリコン膜が公知の手法（例えば、ＣＶＤ（Ｃｈｅｍｉｃａｌ　Ｖａｐｏｒ　Ｄｅｐｏｓｉｔｉｏｎ法）により形成される。
　本実施形態においても、比較的高濃度であり、かつｐＨ値が適切に制御されたＨＣＮ水溶液を用いた浸漬処理を行うにより、変換効率の高い太陽電池３００が得られる。
　なお、本実施形態では、ｐＨ値が８．５であったが、この範囲が５以上９．５未満であれば、本実施形態と同様の効果が奏され得る。なお、本実施形態のように反射防止膜が形成されていない場合、ＨＣＮ水溶液は直接シリコンに接触することになると、ＨＣＮ水溶液のｐＨ値が９．５以上であれば、シリコンがエッチングされてしまう可能性が高まる。従って、ｐＨ値を上述の範囲に設定することが好ましい。また、本実施形態では、反射防止膜３３０が形成される前に、ＨＣＮ水溶液による処理が行われた。これは、窒化シリコン膜が非常に緻密な膜であるため、その反射防止膜３３０を形成した後でＨＣＮ水溶液による処理を行っても、反射防止膜をシアン化物イオンが通過しにくいと考えられるためである。従って、特に多結晶シリコン太陽電池の場合は、反射防止膜３３０が緻密な膜であれば、それが形成される前にＨＣＮ水溶液による処理が行われることが、欠陥消滅を促進する観点から非常に有効であるといえる。
＜第３の実施形態＞
　本実施形態の太陽電池は、第２の実施形態におけるＨＣＮ水溶液中への浸漬処理が、ｐｎ接合が形成される前に行われる点を除き、第２の実施形態と同様に行われた。従って、第１及び第２の実施形態と重複する説明は省略され得る。
　本実施形態の太陽電池の断面構造の概要も、第１及び第２の実施形態の太陽電池と同様である。しかしながら、本実施形態では、ｐ型の多結晶シリコン基板３１０に対して、ｐｎ接合が形成される前に、第２実施形態のＨＣＮ水溶液を用いた浸漬処理と同様の処理が行われる。
　その後、多結晶シリコン基板３１０に対してｎ型拡散層３２０が公知の手法を用いて形成される。ここで、本実施形態では、多結晶シリコン基板３１０が採用されているため、その表面上に存在し得る金属不純物の洗浄効果とともに、その表面又はその表面から一定の深さ方向に渡る領域内の欠陥準位の低減効果が奏され得る。
　従って、ＨＣＮ水溶液を用いた浸漬処理は、ｐｎ接合が形成された後にその処理が行われる場合のみならず、ｐｎ接合が形成される前に行われる場合であっても、太陽電池の高効率化に寄与し得る。本実施形態の浸漬処理は、単結晶シリコン用いた太陽電池に対しても適用し得るが、欠陥準位が表面や結晶粒界により多く存在する多結晶シリコンを用いた太陽電池に対して特に好適であるといえる。
　なお、本実施形態におけるＨＣＮ水溶液による金属不純物の洗浄メカニズムは、次のように考えられる。まず、シアン化物イオン（ＣＮ－）がシリコン基板表面上の金属、例えば銅と反応して［Ｃｕ（ＣＮ）２］－を形成することにより、汚染銅が除去される。［Ｃｕ（ＣＮ）２］－はＨＣＮ水溶液中のＣＮ－イオンと反応し、ｐＨ１０では［Ｃｕ（ＣＮ）４］３－として安定に存在する。ＣＮ－イオンの錯イオン形成能は極めて大きいため、仮に極低濃度（例えば、３ｐｐｍ程度）のＨＣＮ水溶液であっても、ＣＮ－イオンが有効に反応して汚染銅の除去が可能である。このときの極低濃度の洗浄においてですら、洗浄前のシリコン基板表面銅濃度１０１２～１０１３原子／ｃｍ２に汚染されていたものが、２分間の浸漬処理後には、全反射蛍光Ｘ線分析装置による銅の検出限界（～３×１０９原子／ｃｍ２）以下にまで銅が除去されることを確認されている。
＜その他の実施形態＞
　なお、上述の実施形態では、反射防止膜として二酸化チタン（ＴｉＯ２）膜や窒化シリコン膜が用いられていたが、反射防止膜はこれに限定されない。例えば、ＳｉＯ２、Ａｌ２Ｏ３、Ｔａ２Ｏ５、ＭｇＯ、ＺｒＯ２、又は前述の各酸化物の複合材や、ＳｉＯ，ＳｉＯＮも、反射防止膜として適用され得る。特に、第２実施形態で採用した窒化シリコン膜のような緻密な膜を反射防止膜とする場合は、そのような反射防止膜が形成される前にシアン含有溶液による処理が行われることが、欠陥消滅を促進する観点から好ましい。
　また、上述の各実施形態のいずれにも該当し得るが、シアン含有溶液のｐＨの調製ないし安定のための手段としては、アンモニア、コリン、ＴＭＡＨ等を含む溶液をシアン含有溶液に混入することが好ましい。なお、ＫＯＨやＮａＯＨ等の金属原子を含むアルカリは上述の各実施形態には適さない。
　また、上述の各実施形態では、シアン含有溶液による金属汚染の除去に関する洗浄についてのみ言及しているが、その他の公知の洗浄工程が上述の各太陽電池の製造過程の中で適宜実施されても良い。代表的な洗浄工程には、ＲＣＡ洗浄工程や純水（又は超純水）による洗浄工程が挙げられる。
　さらに、上述の実施形態では、シアン含有溶液であるＨＣＮ水溶液の温度は、約２５℃（室温）であったが、これに限定されない。例えば、３０℃以上５０℃以下のＨＣＮ水溶液を用いて行った場合であっても、上述の実施形態と同様の効果が奏され得る。
　また、シアン含有溶液の温度が５０℃を超えると、温度上昇に伴う反応性の向上によりシアン含有溶液による洗浄効果が高まる利点はあるが、同溶液中のシアン（ＣＮ）の揮発（蒸発）が起こるため、毒性のＨＣＮの蒸発に対する安全対策が不可欠となる。従って、シアン（ＣＮ）の蒸発を抑制した上で、シアン含有溶液での汚染金属の除去という洗浄効果を十分に得る観点から言えば、シアン含有溶液の温度が２５℃以上４０℃以下であることが好ましい。
　また、上述の各実施形態では、シアン（ＣＮ）含有溶液としてＨＣＮ水溶液が用いられたが、その溶媒は水（純水、超純水）に限定されない。例えば、シアン含有溶液の溶媒が、シアン化水素を、純水、超純水、アルコール系溶媒、ケトン系溶媒、ニトリル系溶媒、芳香族炭化水素系溶媒、四塩化炭素、エーテル系溶媒、及び脂肪族アルカン系溶媒の群から選ばれる少なくとも１種類の溶媒であれば、上述の各実施形態の少なくとも一部の効果が奏され得る。但し、ＨＣＮの溶解度と溶媒の純度の観点から言えば、超純水、アルコール系溶媒、あるいは二トリル系溶媒を前述の溶媒とすることは好ましい一態様である。
　加えて、シアン（ＣＮ）含有溶液の濃度については、浸漬処理の対象となる太陽電池が反射防止膜を備えているか否か、より一般的には、シリコン表面が直接的にシアン（ＣＮ）含有溶液に触れるか否かで好ましい範囲が異なる。例えば、シリコン表面が直接シアン（ＣＮ）含有溶液に曝される構造を有する太陽電池を浸漬処理対象とする場合は、シリコンの不適切なエッチングを防止する観点から、ｐＨ値が５以上９．５未満であることが好ましい。他方、反射防止膜等によってシリコン表面がいわば「保護」され、シリコン表面が直接シアン（ＣＮ）含有溶液に曝されない構造を有する太陽電池を浸漬処理対象とする場合は、電離確率の増加を図ってＣＮ－イオンによる欠陥準位を消滅を促進する観点から、ｐＨ値が９．５以上であることが好ましい。
　また、上述の各実施形態では、シアン（ＣＮ）含有溶液におけるシアン（ＣＮ）濃度が２７００ｐｐｍ又は５４０ｐｐｍであったが、その濃度はこれらの値に限定されない。シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であれば、上述の各実施形態の少なくとも一部の効果が奏され得る。但し、シリコン基板又はそのシリコン基板から形成される太陽電池の、おそらく表面や裏面、及び／又はｐｎ接合界面やｐｎ接合表面に存在するダングリングボンド等に起因する欠陥準位の低減化を促進する観点から言えば、シアン（ＣＮ）濃度が、３００ｐｐｍ以上０．５％以下とすることはより好ましい一態様である。
　上述の各実施形態では、ｐ型の単結晶シリコン基板やｐ型の多結晶シリコン基板が当初用いられているが、基板の種類もこれらに限定されない。ｐ型の代わりにｎ型の各種基板が採用されても、上述の各実施形態の効果と同様の効果が奏され得る。
　上述の各実施形態の開示は、それらの実施形態の説明のために記載したものであって、本発明を限定するために記載したものではない。加えて、各実施形態の他の組合せを含む本発明の範囲内に存在する変形例もまた、特許請求の範囲に含まれるものである。
　本発明の太陽電池の製造方法、太陽電池の製造装置、及び太陽電池は、その太陽電池の高い変換効率から、エネルギーの枯渇を憂う各種の産業分野において広く利用され得る。
　１０，３１０　　　シリコン基板（ｐ型）
　２０，３２０　　　ｎ型拡散層
　３０，３３０　　　反射防止膜
　４０　　　表面電極
　５０　　　裏面電極
　１００，２００，３００　　太陽電池

Claims (13)

  1. 　シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内に、シリコン基板又は前記シリコン基板から形成される太陽電池を浸漬する浸漬工程を含む、
    　太陽電池の製造方法。
  2. 　前記浸漬工程において、前記シリコン基板又は前記太陽電池が反射防止膜を備え、かつ
    　前記シアン含有溶液の水素イオン濃度指数（ｐＨ）が、９．５以上１４以下である、
    　請求項１に記載の太陽電池の製造方法。
  3. 　前記シアン含有溶液の水素イオン濃度指数（ｐＨ）が、５以上９．５未満であり、
    　前記浸漬工程の後に、反射防止膜を形成する工程を含む、
    　請求項１に記載の太陽電池の製造方法。
  4. 　前記シアン（ＣＮ）濃度が、３００ｐｐｍ以上０．５％以下である、
    　請求項１乃至請求項３のいずれか１項に記載の太陽電池の製造方法。
  5. 　前記シアン含有溶液の温度が、２０℃以上４０℃以下である、
    　請求項１乃至請求項３のいずれか１項に記載の太陽電池の製造方法。
  6. 　前記シアン含有溶液の溶媒が、シアン化水素を、純水、超純水、アルコール系溶媒、ケトン系溶媒、ニトリル系溶媒、及びエーテル系溶媒の群から選ばれる少なくとも１種類の溶媒である、
    　請求項１乃至請求項３のいずれか１項に記載の太陽電池の製造方法。
  7. 　前記シリコン基板が、単結晶シリコン又は多結晶シリコンである、
    　請求項１乃至請求項３のいずれか１項に記載の太陽電池の製造方法。
  8. 　シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内に、シリコン基板又は前記シリコン基板から形成される太陽電池を浸漬する浸漬処理部を備える、
    　太陽電池の製造装置。
  9. 　反射防止膜を備える前記シリコン基板又は前記太陽電池を浸漬する前記浸漬処理部を備え、かつ
    　前記シアン含有溶液の水素イオン濃度指数（ｐＨ）が、９．５以上１４以下である、
    　請求項８に記載の太陽電池の製造装置。
  10. 　前記シアン含有溶液の水素イオン濃度指数（ｐＨ）が、５以上９．５未満であり、
    　前記浸漬処理部を経た前記シリコン基板又は前記太陽電池に反射防止膜を形成する反射防止膜形成部をさらに備える、
    　請求項８に記載の太陽電池の製造装置。
  11. 　前記シアン（ＣＮ）濃度が、３００ｐｐｍ以上０．５％以下である、
    　請求項８乃至請求項１０のいずれか１項に記載の太陽電池の製造装置。
  12. 　前記シアン含有溶液の温度が、３０℃以上４０℃以下である、
    　請求項８乃至請求項１０のいずれか１項に記載の太陽電池の製造装置。
  13. 　シアン（ＣＮ）濃度が１００ｐｐｍ超５％以下であって、５℃以上５０℃以下のシアン含有溶液内に、シリコン基板又は前記シリコン基板から形成される太陽電池を浸漬することにより形成される前記シリコン基板の表面を備える、
    　太陽電池。
PCT/JP2010/062420 2010-07-23 2010-07-23 太陽電池およびその製造方法、並びに太陽電池の製造装置 WO2012011188A1 (ja)