WO2011099766A2 - 하드코팅 형성 방법 - Google Patents
하드코팅 형성 방법 Download PDFInfo
- Publication number
- WO2011099766A2 WO2011099766A2 PCT/KR2011/000861 KR2011000861W WO2011099766A2 WO 2011099766 A2 WO2011099766 A2 WO 2011099766A2 KR 2011000861 W KR2011000861 W KR 2011000861W WO 2011099766 A2 WO2011099766 A2 WO 2011099766A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- resin
- coating layer
- sheet
- substrate
- molded article
- Prior art date
Abstract
Description
실시예 1 | 실시예 2 | |
연필 경도(H) | 5 | 5 |
Claims (18)
- 기재; 및 상기 기재상에 형성되고, 에폭시기 및 (메타)아크릴로일기를 가지는 수지 및 티올계 경화제를 포함하는 수지 조성물의 열경화물을 함유하는 코팅층을 가지는 시트를 사용하여, 상기 시트의 코팅층을 성형품에 전사 또는 접착시키는 단계; 및상기 코팅층에 광을 조사하여, 상기 코팅층을 경화시키는 단계를 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트는, 기재의 일면에 형성된 이형층을 추가로 포함하고, 코팅층이 상기 이형층상에 형성되어 있는 하드코팅 형성 방법.
- 제 1 항에 있어서, 수지는 에폭시 당량이 200 g/eq 내지 20,000 g/eq이고, (메타)아크릴로일 당량이 100 g/eq 내지 1,000 g/eq인 하드코팅 형성 방법.
- 제 1 항에 있어서, 수지는 중량평균분자량이 5,000 내지 100,000인, 하드코팅 형성 방법.
- 제 5 항에 있어서, R1 내지 R4는, 각각 독립적으로 수소, 탄소수 1 내지 4의 알킬 또는 -A-B-C-D-SH이고, R1 내지 R4 중 2개 이상은 -A-B-C-D-SH이며,상기에서 A는 단일 결합 또는 탄소수 1 내지 4의 알킬렌이고, B는 -OC(=O)- 또는 -O-E-OC(=O)-이며, C는 단일 결합 또는 탄소수 1 내지 4의 알킬렌이고, D는 단일 결합 또는 하기 화학식 4의 2가 잔기이며, 상기에서 E는 탄소수 1 내지 4의 알킬렌인, 하드코팅 형성 방법:[화학식 4]상기 화학식 4에서 n은 0 내지 10의 정수를 나타낸다.
- 제 1 항에 있어서, 수지 조성물은, 티올계 경화제를 수지 100 중량부에 대하여, 0.1 중량부 내지 10 중량부로 포함하는, 하드코팅 형성 방법.
- 제 1 항에 있어서, 수지 조성물이 광개시제, 다관능성 아크릴레이트, 산화 방지제, 활제, 자외선 흡수제, 열경화용 촉매, 필러 또는 이소시아네이트 화합물로 이루어진 군으로부터 선택된 하나 이상을 추가로 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트는 코팅층; 또는 기재에서 상기 코팅층의 반대면측에 형성된 접착층을 추가로 포함하는, 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트는 코팅층; 또는 기재에서 상기 코팅층의 반대면측에 형성된 도안층을 추가로 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트는 코팅층; 또는 기재에서 상기 코팅층의 반대면측에 형성된 증착층을 추가로 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트의 코팅층을 성형품의 표면에 접착시키는 단계; 기재를 박리하는 단계; 및 광조사를 통해 코팅층을 경화시키는 단계를 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트의 코팅층이 성형품과 접촉할 수 있도록 상기 시트를 사출 금형 내에 설치하는 단계; 상기 사출 금형 내의 공동으로 용융 수지를 사출하는 단계; 상기 시트로부터 기재를 박리하는 단계; 및 광조사를 통해 코팅층을 경화시키는 단계를 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트를 기재측이 성형품의 표면을 향하도록 배치하는 단계; 상기 시트를 가열하여, 기재를 연화시키는 단계; 상기 시트를 하방으로부터 진공 흡인하여, 성형품의 표면에 접착시키는 단계; 및 광조사를 통해 코팅층을 경화시키는 단계를 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 시트의 기재가 성형품과 접촉할 수 있도록 상기 시트를 사출 금형 내에 설치하는 단계; 상기 금형 내의 공동으로 용융 수지를 사출하는 단계; 및 광조사를 통해 코팅층을 경화시키는 단계를 포함하는 하드코팅 형성 방법.
- 제 1 항에 있어서, 성형품은, 폴리스티렌계 수지, 폴리올레핀계 수지, ABS 수지, AS 수지, AN 수지, 폴리페닐렌옥시드·폴리스티렌계 수지, 폴리카보네이트계 수지, 폴리아세탈계 수지, 아크릴계 수지, 폴리카보네이트 변성 폴리페닐렌에테르 수지, 폴리에틸렌테레프탈레이트 수지, 폴리부틸렌테레프탈레이트 수지, 초고분자량 폴리에틸렌 수지, 폴리술폰 수지, 폴리페닐렌설파이드계 수지, 폴리페닐렌옥시드계 수지, 폴리아크릴레이트 수지, 폴리에테르이미드 수지, 폴리이미드 수지, 액정 폴리에스테르 수지 또는 폴리아릴계 내열 수지를 포함하는 조성물로부터 형성된 수지 성형품인, 하드코팅 형성 방법.
- 제 1 항에 있어서, 광조사는, 파장이 300 nm 내지 400 nm인 자외선을 사용하여, 조도 80 mW/cm2 내지 200 mW/cm2 및 광량 1,000 mJ/cm2 내지 2,000 mJ/cm2의 조건에서 1초 내지 5분 동안 수행하는, 하드코팅 형성 방법.