Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
  • C08J5/005—Reinforced macromolecular compounds with nanosized materials, e.g. nanoparticles, nanofibres, nanotubes, nanowires, nanorods or nanolayered materials
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y20/00—Nanooptics, e.g. quantum optics or photonic crystals
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2363/00—Characterised by the use of epoxy resins; Derivatives of epoxy resins
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
  • Y10T428/2982—Particulate matter [e.g., sphere, flake, etc.]

Definitions

• the present invention relates to polymers and nanoparticles.
• the present invention relates to polymer nanocomposites and methods producing the same.
• Nano-sized materials have been investigated for use in mechanically enhancing or stabilizing polyolefins materials.
• Semiconducting materials have been widely used for optical and electrical applications. Additionally, as the size reduces to several nanometers (quantum scale), semiconducting materials show size-dependent optical, electric and thermal properties different from the bulk semiconductor materials, known as quantum size effects, which make the semiconductor nanocrystals attractive for industrial applications and may give rise to new opportunities for functional polymer/semiconductor nanocomposites.
• Incorporating semiconductor nanocrystals into polymeric matrices is a common way to fabricate optical and electrical devices, such as solar cells, light-emitting diodes (LED) and photovoltaic devices.
• optical and electrical devices such as solar cells, light-emitting diodes (LED) and photovoltaic devices.
• LED light-emitting diodes
• photovoltaic devices without special surface functionalization, no current methods have been able to disperse semiconductor nanocrystals in polymers under nano-scale conditions and control the nanoparticles dispersion. Instead, large aggregates have been observed to form in polymers that limit the use of semiconductor nanocrystals in polymers for optical and electrical applications with desired mechanical and thermal properties and stability.
• ZnO zinc oxide
• ZnO is an important and attractive semiconducting material because of its distinguished properties in optics, photonics and electronics.
• ZnO particles are used as an UV absorber in sunscreens and cosmetics.
• ZnO is also much more resistant to radiation damage than other semi-conductor materials.
• ZnO is produced through wet-chemistry, which offers greater processing potential for use with polymers.
• ZnO particles were used as a mechanical reinforcement agent for polyolefins.
• the amount of ZnO particles used was of such an amount considered unacceptable for practical and economic purposes.
• ZnO particles blended with polyethylene to improve thermal stability have also been required in an amount considered unacceptable for practical and economic purposes.
• Alternative methods, such as preparing ZnO nanocomposites with organic modified ZnO to improve thermal stability were found to be too expensive and impractical for mass production.
• ZnO particles that have been investigated as a UV stabilizer for polyolefins were also observed to have detrimental effects on other properties of the materials including lost of transparency of composites.
• ZnO nanoparticles are observed to have inhomogeneous dispersion into polymer matrices by conventional processes, such as melt blending processes. Further, polymer matrices from conventional processes are observed to have large ZnO aggregates and both the size distribution ranging from 30-200 nm and the shapes of ZnO nanoparticles were not uniform. The presence of aggregates results in less than desired optical and/or electrical properties in the form of composites.
• a novel polymer nanocomposite includes a nanoparticle, an inorganic nanoplatelet, and a polymer material.
• a method is provided for forming a polymer nanocomposite. The method involves dispersing nanoparticles into a polymeric material by using inorganic nanoplatelets.
• a polymer nanocomposite comprising: inorganic nanoparticles; inorganic nanoplatelets; and a polymer material.
• polymer comprises one or more polymer materials selected from the group consisting of a (meth)acrylic resin, styrenic resin, polycarbonate resin, polyester resin, epoxy resin, epoxidized phenolic resin, phenylenevinylene resin, fluorene resin, fluorenevinylene resin, phenylene resin, thiophene resin, and combinations thereof.
• polymer comprises one or more polymer material selected from the group consisting of a polymethylmethacrylate, polybutylacrylate, methlymethacrylate-butylacrylate copolymer, metylmethacrylate-styrene copolymer, polystyrene, styrene-acrylonitrile copolymer, styrene-isobutyrene copolymer, styrene-butylacrylate copolymer, polyethylene terephalate, polybutylene terephthalate, bisphenol-A epoxy resin, bisphenol-F epoxy resin, poly(2-methoxy-5-ethylhexyloxy-l,4- phenylenevinylene), poly(9,9-di-(2-ethylhexyl)-fluorenyl 2,7-diyl), poly(9,9-dioctylfluoren
• FIG. 1 is a X-ray diffraction (XRD) pattern of colloidal zinc oxide (ZnO) nanoparticles
• FIG. 2 is a X-ray diffraction (XRD) pattern of alpha zirconium phosphate ( ⁇ -ZrP) nanoplatelets;
• FIG. 3 is a ultraviolet and visible (UV -vis) spectra of a transmittance versus wavelength of one embodiment of a nanocomposite having nanoplatelets and one embodiment of a nanocomposite without nanoplatelets;
• UV -vis ultraviolet and visible
• FIG. 4 is a UV-vis spectra of transmittance versus wavelength of epoxy, an epoxy-ZnO nanoparticle nanocomposite, an epoxy-nanoplatelet nanocomposite, and an epoxy-ZnO nanoparticle-nanoplatelet nanocomposite containing nanoplatelets with different amounts of nanoparticles;
• FIG. 5 is a UV-vis spectra of neat diaminodiphenylsulfone (DDS) cured epoxy and nanocomposites of transmittance versus wavelength.
• DDS diaminodiphenylsulfone
• a polymer nanocomposite comprises a polymer containing dispersed nanoparticles and nanoplatelets.
• the polymer nanocomposite may be formed by mixing a first composition of nanoparticles, a second composition of nanoplatelets, and a third composition of a polymer material.
• further processing steps to form the nanocomposite may be performed, such as precipitation and/or curing.
• the nanoparticles may comprise inorganic particles.
• Suitable inorganic particles include one or more materials selected from the group consisting of oxides, elemental metals, and combinations thereof, of which oxides are preferred.
• suitable oxide nanoparticles include one or more materials selected from the group consisting of zinc oxide, titanium oxide, and combinations thereof.
• suitable elemental metals include one or more materials selected from the group consisting of gold, silver, and combinations thereof.
• the nanoparticles may comprise up to about 50 wt.% of the nanocomposite, such as up to about 30 wt.% of the nanocomposite.
• the nanoparticles may comprise between about 0.05 weight percent (wt.%) and about 5 wt.% of the polymer nanocomposite, such as between about 0.1 wt.% and about 4 wt.% of the polymer nanocomposite, for example, about 1 wt.%.
• the nanoparticles may comprise organic materials including phase-separated nanoparticles including, but not limited to, polyethersulfone and teflon, and rubber based nanoparticles, including, but not limited to, butadiene rubber.
• a nanoparticle may be defined herein as a particle of material having three dimensions less than 100 nm.
• a nanoparticle may have length, width, and height of less than 50 nm each.
• the nanoparticle may have length, width, and height of about 20 nm or less respectively.
• the nanoparticle may also be defined as a particle having three dimensions within a ratio of about 1:1 to 2:1 of the respective dimensions.
• a nanoparticle may have a length, width, and height ratio of between about 1:1:1 and 2:1 :1, 1 :2:1, 1:1:2, 2:2:1, 1 :2:2, or 2:1 :2.
• Nanoparticles may be in the shape of spheres, ovoids, cubes, pyramidal, or other three-dimensional shapes having the dimensions and/or ratios described herein.
• Suitable nanoparticles may have a number-average particle size between about 0.1 nanometer and less than about 100 nanometers, such as between about 1 nanometer and about 20 nanometers, with the size being the average of the three dimensions of the particle, height, width, and length.
• Suitable nanoparticles have a number-average particle size between about 1 nanometer and about 10 nanometers, such as between about 2 nanometer and about 6 nanometers.
• the nanoparticles may have a standard deviation in particle size distribution between about 0.1 nanometers and about 5.0 nanometers, such as between about 0.1 nanometers and about 3.0 nanometers.
• Suitable nanoparticles may include aggregates of nanoparticles if the aggregates have the number-average particle size and the particle size distribution described above and may have aggregate sizes up to about 100 nm, such as between about 1 nm and about 50 nm.
• a nanoplatelet may be defined herein as a particle of material having one dimension less than 100 nm and two dimensions of about 100 nm or greater.
• a nanoplatelet may have a height or thickness less than 50 nm, such as less than 20 nm, for example, between about 0.01 nm and less than about 5 nm, and a length and width of about 100 nm or greater.
• the nanoplatelet may also be defined as a particle having three dimensions with one of the respective dimensions having a ratio to the other dimensions of less than 1:2:2.
• a nanoplatelet having a height, width, and length may have a ratio of height to width to length of less than 1 :2:2, such as between about 1 :10000:10000 and about 1 :3:3, including between about 1 :200:200 and about 1 :10:10 for example, between about 1:100:100 and about 1:30:30.
• An example of a nanoplatelet having a height to width to length ratio of about 1:20:20 is a nanoparticle having a height or thickness of about 5 nm and a width and a length of about 100 nm.
• Nanoplatelets may be in the shape of rectangles, square-shaped, hexagons, circles, or irregular features with the dimension stated herein.
• An example of such a structure having the ratios described herein is a clay structure, for example, the structure of montmorillonite clay.
• Suitable inorganic nanoplatelets may have a number-average thickness between about 0.1 nanometer and about 5 nanometer and a number-average length (long side) between about 10 nanometer and about 1000 nanometers.
• Preferred inorganic nanoplatelets may have a number-average thickness less than 50 nanometers, such as between about 0.5 nanometer and about 1.5 nanometers, for example, at about 1 nanometer and may have a number- average length between 50 nanometers and about 500 nanometers, for example, at about 100 nanometers.
• Observed TEM images of nanoplatelets formed by the processes described herein had an average length and width of approximately 100 run.
• the nanoparticles may be synthesized by various techniques, for example, by a sol-gel method.
• the sol-gel method involves the mechanism of a transition of a system from a liquid sol into a solid gel phase.
• the liquid sol is substantially a suspension of small particles in a liquid known as a substantially a colloidal suspension.
• the nanoparticles may be synthesized by reacting, under sol-gel conditions, a precursor with an alcohol-based composition and an alkali metal hydroxide.
• the nanoparticles may be manufactured by other processes known in the art, and the sol-gel conditions described herein are used to illustrate the invention and should not be construed or interpreted as limiting the scope of the invention.
• Suitable oxide precursors may be any compound that can be converted into an oxide by reaction.
• Suitable oxide precursors include metal salts selected from the group consisting of acetates, carboxylates, dichlorides, nitrates, oleates, and their respective hydrates.
• ZnO nanoparticles may be derived from a zinc acetate dihydrate precursor. If a hydrate is added to the reaction, the hydrate may be hydrolyzed in an alcohol-based composition prior to exposure to the alkali metal hydroxide.
• the alcohol-based composition may be any composition that contains alcohol and, optionally, a secondary component.
• the alcohol-based composition may have a secondary component comprising between about 1 wt.% and less than about 50 wt.%, such as between about 1 wt.% and less than about 30 wt.%, of the composition to be processed into a sol gel.
• Suitable alcohols may be selected from the group consisting of methanol, ethanol, propanol, 2-propanol, and combinations thereof.
• Suitable secondary components include water and organic solvents such as acetone, methylethylketone and tetrahydrofuran.
• Suitable alkali metal hydroxides are selected from the group of lithium hydroxide, sodium hydroxide, potassium hydroxide, rubidium hydroxide, cesium hydroxide, francium hydroxide, and combinations thereof. The inventors believe that the alkali metal hydroxide aids in converting the precursor into the nanoparticles.
• Reaction parameters generally include the pH, temperature, and pressure of the reaction.
• the pH of the reaction mixture may be at least about 7.0. Alternatively, the pH of the reaction mixture is between about 7.5 and about 10.5.
• the reaction temperature may be between about 10°C and about 100°C.
• the reaction pressure may range from a vacuum to 2 MPa. Alternatively, the reaction pressure may be atmospheric pressure.
• the reaction may be performed in a chemically inert atmosphere.
• colloidal ZnO nanoparticles were prepared by hydrolyzing zinc acetate dehydrate (Zn(OAc)*2H 2 0) in the basic methanol composition.
• KOH Potassium hydroxide
• Sigma-Aldrich Potassium hydroxide
• a composition of zinc acetate dihydrate (99%, Fluka) / methanol was added directly into the basic methanol composition to form a starting sol.
• the reaction stoichiometry of the zinc acetate dihydrate to the KOH in the reaction mixture may be between about 1:0.1 and about 1 :3, for example, at about 1 :2.
• This starting sol having the colloid can then be concentrated between about 3 and about 20 times, such as by 10 times. A rotary evaporation under vacuum may be used to concentrate the sol.
• the pH of the composition was maintained at neutral and basic pH levels of about 7.0 or higher.
• the ZnO can then be precipitated from the colloid.
• ZnO nanoparticles may be precipitated by adding an organic non-solvent, such as hexane and isopropanol into the concentrated ZnO methanol colloid.
• the volume ratio of hexane: concentrated ZnO methanol colloid:isopropanol may be between about 3:1:1 and about 10:1:1, for example, at a volume ratio of about 5:1 :1.
• the ZnO precipitate is then separated by a suitable process such as centrifugation.
• the ZnO precipitate may then be re-dispersed in an alcohol-based composition to purify the ZnO nanoparticles.
• the purified ZnO nanoparticles may then be re- dispersed in methanol for nanocomposites preparation.
• the nanoplatelets may be a nature-layered, or layered, material, such as clay, or a synthetic material, such as zirconium phosphate (ZrP).
• Suitable inorganic nanoplatelets comprise materials having one or more elements selected from the group consisting of aluminum, silicon, magnesium, zirconium, titanium, halfhium, rutherfordium, and combinations thereof.
• suitable inorganic nanoplatelets include one or more materials selected from the group consisting of alpha-zirconium phosphate, titanium phosphate, halfhium phosphate, montmorrillonites, smectites, bentonites, and combinations thereof.
• the nanoplatelets may comprise between about 0.05 wt.% and about 20 wt.% of the polymer nanocomposite, such as between about 0.1 wt.% and about 10 wt.% of the polymer nanocomposite including between about 0.1 wt.% and about 4 wt.% of the polymer nanocomposite, for example, about 0.5 wt.%. It is believed that the nanoplatelets improve the dispersion of nanoparticles in a polymer allowing a more effective use of nanoparticles in nanocomposite polymers as compared to conventional nanocomposite polymer. Alternatively, other particles, such as needle-shaped particles, in the nano-sized ranges disclosed herein may be added or substitute the nanoplatelets described herein.
• Layered material nanoplatelets such as montmorrillonites, smectites, bentonites, and combinations thereof, may be exfoliated in colloids, which colloids are defined herein as dispersed and exfoliated nanoplatelets in a media.
• the nanoplatelets may be prepared by a gel process or formed from a clay material. In one embodiment of a gel process, the nanoplatelets may be synthesized by exfoliating, under sol-gel conditions, a prepared nanoplatelet material with a basic hydroxide. Exfoliated nanoplatelets are defined herein as nanoplatelets individually dispersed in a media without a regular, or irregular, spacing between the nanoplatelets.
• Suitable base hydroxides include alkylamine hydroxides.
• suitable alkyl amine hydroxides include Jeffamine, alkyl ammonium hydroxides, such as tetra-n-butylammonium hydroxide, and combinations thereof.
• the nanoplatelet material may be prepared from a precursor.
• Suitable precursors may be any compound that can be converted into a phosphate by reaction.
• Suitable precursors include metal salts selected from the group consisting of nitrates, chlorides, and the respective hydrates.
• alpha-zirconium phosphate may be derived from a zirconium chloride hydrate (ZrOCl 2 -8H 2 O) precursor.
• ⁇ -ZrP nanoplatelets were synthesized by refluxing zirconyl chloride (ZrOCl 2 SH 2 O, Fluka) in the presence of phosphoric acid (H 3 PO 4 ). The ⁇ -ZrP material was then washed and collected. The ⁇ -ZrP material was then dried and ground into fine powders.
• the prepared synthetic material, ⁇ -ZrP, or clay-based materials may then be exfoliated by a base hydroxide, such as tetra-n-butylammonium hydroxide (TBA + OH " ) in water.
• a base hydroxide such as tetra-n-butylammonium hydroxide (TBA + OH " ) in water.
• the molar ratio of ⁇ -ZrP to base hydroxide may be between about 1 :0.6 and about 1 :1.2, for example at a molar ratio of ⁇ -ZrP:TBA of about 1 :0.8.
• the exfoliated ⁇ -ZrP nanoplatelets may then be centrifuged, collected, and condensed as a gel form. The supernatant of the gel may then be removed, and the ⁇ -ZrP nanoplatelets may then be mixed with an organic solvent, such as acetone, to remove the remaining water and to obtain exfoliated ⁇ -ZrP nanoplatelets.
• the polymer material may comprise one or more polymeric materials.
• the polymeric material may include thermoplastic resins and thermosetting resins.
• Suitable thermoplastic resin polymeric materials include polymeric materials having a number average molecular weight (Mn) of greater than about 5,000.
• Suitable thermosetting resin polymeric materials, such as epoxy resin include epoxy materials having a molecular weight between about 100 and about 5000. The Mn of the polymer is measured by gel permeation chromatography with a calibration of standard polystyrenes.
• the nanoparticles and nanoplatelets may be used with additional polymeric materials and non-polymeric materials, and the above-described polymeric materials are provided to illustrate the invention and should not be construed or interpreted as limiting the scope of the invention.
• thermoplastic resin examples include (meth)acrylic resin, such as polymethylmethacrylate, polybutylacrylate, methlymethacrylate-butylacrylate copolymer, and metylmethacrylate-styrene copolymer, styrenic resin, such as polystyrene, styrene-acrylonitrile copolymer, styrene-isobutyrene copolymer, and styrene-butylacrylate copolymer, polycarbonate resin, polyester resin, such as polyethylene terephalate and polybutylene terephthalate, phenylenevinylene resin, such as poly(2-methoxy-5- ethylhexyloxy-l,4-phenylenevinylene), fluorene resin, such as poly(9,9-di-(2-ethylhexyl)- fluorenyl 2,7-diyl) and poly(methacrylic resin
• thermoplastic resin examples include epoxy resin, such as bisphenol-A epoxy resins, bisphenol-F epoxy resin and epoxidized phenolic resin, and phenolic resin, such as resole and novolac.
• epoxy resin such as bisphenol-A epoxy resins, bisphenol-F epoxy resin and epoxidized phenolic resin
• phenolic resin such as resole and novolac.
• specific resins include Diglycidyl ether of bisphenol-A (DGEBA) epoxy resin (D.E.R.TM 332 epoxy resin, The Dow Chemical Company), which has an average epoxide equivalent weight of 174 and D.E.R 331 DGEBA epoxy resin (The Dow Chemical Company), which has an average epoxide equivalent weight of 190.
• the polymer material is preferably dissolved before the nanoparticles and polymer material are mixed in an alcohol-based composition. If the polymer material is insolvent or has limited solubility in the alcohol-based composition, an organic solvent may be used to dissolve the polymer material. The polymer material may be dissolved in the organic solvent before it is added to the alcohol-based composition or the organic solvent can be added to the alcohol-based composition prior to the addition of the polymer material and the nanoparticles and inorganic platelets.
• Suitable organic solvents include acetone, dichloromethane, methylethylketone, tetrahydrofuran, toluene, and combinations thereof.
• the polymer material may be dissolved in the presence of a solvent and the nanoplatelets.
• the nanoplatelets are dissolved in acetone and the polymer material may be dissolved in the same solvent, the polymer material and inorganic nanoplatelets may be dissolved in the same solvent, such as acetone.
• some polymeric materials are soluble in an alcohol-based composition. In these cases, the nanoparticles, inorganic platelets, and polymer material may be added directly to the alcohol- based composition, wherein the polymer material will dissolve and mix with the nanoparticles and inorganic platelets.
• the respective components are mixed together according to the methods described herein and a composition of the polymer material, the nanoparticles, the nanoplatelets and the solvent is obtained.
• the polymer nanocomposite may be isolated by evaporation of the solvent.
• the composition may be poured into an organic solvent to precipitate the polymer nanocomposite, which precipitates can then be isolated by means of centrifugation and decantation and then dried.
• Polymer nanocomposites formed from epoxy resins may be cured.
• a curing agent may then be added into the polymer nanocomposite as necessary in stoichiometric amount.
• a curing agent is added to the epoxy resin stoichiometrically.
• Suitable curing agents include sulfones, such as 4,4'-diamino-diphenyl sulfone (DDS), 2-ethyl-4-methyl Imidiazol, triethylenetetramine, Ancamine 1618 (from Air Products), aliphatic amines, such as tetraethylene pentamine (TEPA), and combinations thereof.
• the cure condition is changed depending on the type of epoxy resin and curing agent.
• an epoxy containing nanoparticles, such as zinc oxide, and nanoplatelets, such as zirconium phosphate was poured into a pre-heated mold, cured at 80°C for 24 hrs, and then post-cured at 100 °C for 3 hrs in the oven. After curing, the sample was left in the oven until cooled to room temperature.
• the resulting polymer nanocomposite comprises cured epoxy/ZnO/ ⁇ -ZrP.
• Technical data sheet of an epoxy resin and a curing agent which is provided by the suppliers, would suggest a suitable condition.
• an average particle size of ZnO particles in an alcohol based composition may be based the following equation provided by Meulenkamp [E.A. Meulenkamp, J. Phys Chem. B, 102, 5566-5572 (1998)] to convert the measured values of ⁇ m (the wavelength at which the absorption is the half of that at the shoulder) into particle sizes based on the size determination result from TEM micrographs and XRD line broadening:
• UV absorption was measured in UV-vis spectrophotometer (UV 1601) made by SHIMADZU CO.
• High resolution transmission electron microscopy (HR-TEM) of purified ZnO nanoparticles and epoxy nanocomposites was carried out using a JEOL 2010 transmission electron microscope operated at 200 kV.
• Purified ZnO nanoparticles were first re-dispersed in methanol and diluted, followed by placing a droplet of the composition onto a 400-mesh carbon-coated copper grid. The grid was then dried in a desiccator for one day before imaging.
• the epoxy nanocomposites for HR-TEM were prepared by using ultramicrotomy.
• a Reichert-Jung Ultracut-E microtome was utilized to prepare thin sections with the thickness of around 70-100 nm.
• TEM Transmission electron microscopy
• TEM pictures were observed to find the average particle size and the particle size distribution of ZnO particles dispersed within the polymer nanocomposites.
• TEM images were recorded using a JEOL JEM-1200EX instrument (8OkV). Heat-pressed samples were cut into ultra thin sections for use in the TEM. The TEM image analysis was conducted using more than 200 particles in the image with a magnification of 400,000.
• UV-vis spectra of neat epoxy and nanocomposites were recorded on an Ocean Optics USB2000-DT-Mini Spectrometer.
• the samples were cut and polished using #1200, #2400, and #4000 sand papers sequentially to achieve surface smoothness for investigation.
• Final polishing of the sample surface was done by using 1 ⁇ m diamond paste on a cloth for transmittance measurements.
• the sample thickness was prepared to be within 2 ⁇ 0.05 mm.
• T g Glass transition temperature
• EXAMPLE 1 Synthesis and purification of colloidal ZnO nanoparticles.
• Colloidal ZnO nanoparticles were prepared by hydrolyzing zinc acetate dehydrate (Zn(O Ac)*2H 2 0) in the basic methanol composition.
• Zn(O Ac)*2H 2 0 zinc acetate dehydrate
• 50 mL of 0.16M zinc acetate dihydrate (99%, Fluka) / methanol composition was added directly into the basic methanol composition.
• the reaction stoichiometry of the zinc acetate dihydrate to the KOH in the reaction mixture was 1 :2.
• This starting sol was then aged at 60 °C with refluxing and stirring. After 2 hours of reaction, the colloid was concentrated by 10 times at 40 °C via rotary evaporation under vacuum. During the reaction, the pH of the composition was maintained at 7.0 or higher, and the final pH was 8.7.
• the purified ZnO nanoparticles were re-dispersed in methanol for nanocomposites preparation.
• the yield of the purified ZnO nanoparticles was calculated by drying the appropriate volume of the ZnO/methanol composition in air, baking in an oven at 110 °C, and weighing the leftover ZnO powder. The amount of ZnO nanoparticles added into the polymers was estimated through the calculated yield.
• FIG. 1 is the XRD powder pattern (FIG.
• EXAMPLE 2 Synthesis and exfoliation of ⁇ -ZrP nanoplatelets.
• the ⁇ -ZrP nanoplatelets were synthesized through a refluxing method in which 20.O g ZrOCl 2 SH 2 O (Fluka) was refluxed in 200.0 mL 3.0 M H 3 PO 4 in a Pyrex glass flask with stirring at 100°C for 24 hrs. After the reaction, the products were washed and collected by centrifugation three times. Then, the ⁇ -ZrP nanoplatelets were dried at 65°C in an oven for 24 hrs. The dried ⁇ -ZrP was ground with a set of mortar and pestle into fine powders.
• TBA tetra-n-butylammonium hydroxide
• the well-exfoliated ⁇ -ZrP nanoplatelets in water were first centrifuged at 12,000 rpm to collect exfoliated ⁇ -ZrP nanoplatelets. These exfoliated ⁇ -ZrP nanoplatelets were condensed as a gel form after centrifugation and the supernatant could then be easily removed. After the removal of supernatant, the same amount of acetone was mixed with the ⁇ -ZrP gel obtained from the centrifugation.
• the mixture was sonicated for one hour and then shaken overnight to re- disperse ⁇ -ZrP nanoplatelets into acetone. This centrifugation and re-dispersion process was repeated three times to remove most of water and to obtain exfoliated ⁇ -ZrP nanoplatelets in acetone.
• the supernatants separated after each of the three centrifugations were collected and heated in an oven at 120°C to remove solvent and obtain the ⁇ -ZrP left in the supernatants.
• the exact amount of ⁇ -ZrP that was exchanged into acetone can be calculated.
• FIG. 2 shows the typical XRD powder pattern of ⁇ -ZrP nanoplatelets.
• the sharp diffraction peaks indicate that a high crystallinity has been formed.
• ⁇ -ZrP nanoplatelets synthesized from refluxing zirconyl chloride in 3 M phosphoric acid at 100°C for 24 hrs have an average long-dimension of around 100 nm.
• the ⁇ -ZrP single nanoplatelet was confirmed to be an average length of around 100 nm by TEM observation.
• Diglycidyl ether of bisphenol- A (DGEBA) epoxy resin (D.E.R.TM 332 epoxy resin, The Dow Chemical Company) with an average epoxide equivalent weight of 174 was first dissolved in acetone with exfoliated ⁇ -ZrP nanoplatelets in a flask, and then the methanol containing re- dispersed ZnO nanoparticles was added into the above composition. Subsequently, the solvents were removed in a under vacuum at 80°C. After solvent evaporation, the epoxy resin containing both nanoparticles and nanoplatelets was degassed at 100°C for 1 hr.
• DGEBA bisphenol- A
• DDS-cured epoxy is herein referred to as epoxy-D and ancamine-cured epoxy is herein referred to as epoxy-A.
• epoxy-D/ZnO/ ⁇ -ZrP polymer nanocomposites.
• neat epoxy sample without nano-materials (neat epoxy-D), epoxy with only ZnO nanoparticles (Epoxy-D/ZnO), epoxy with only ⁇ -ZrP nanoplatelets (Epoxy-D/ ⁇ -ZrP), and epoxy with ZnO nanoparticles and TBA (Epoxy-D/ZnO/TBA) were prepared through the same curing procedure.
• DGEBA epoxy resin (D.E.R.TM 331 epoxy resin, The Dow Chemical Company) with an average epoxide equivalent weight of 190 was first dissolved in acetone with exfoliated ⁇ -ZrP nanoplatelets in a flask, and then the methanol containing re-dispersed ZnO nanoparticles was added into the above composition. Subsequently, the solvents were removed in a rotary evaporator under vacuum at 80 0 C. After solvent evaporation, the epoxy resin containing both nanoparticles and nanoplatelets was degassed at 80 °C for 1 hr and then cooled to room temperature. The curing agent, Ancamine 1618 (Air Products), was added into the epoxy resin according to the manufacture's recommendation.
• Ancamine 1618 Air Products
• This polymer nanocomposite sample was designated as epoxy- A/ZnO/ ⁇ -ZrP.
• the epoxy-A/ZnO/ ⁇ -ZrP nanocomposite comprises 0.5 wt.% of ZnO nanoparticles and 0.5 wt.% of ⁇ -ZrP nanoplatelets of the nanocomposite.
• FIG. 3 shows the ultraviolet-visible light (UV-vis) spectra of the neat epoxy-D, the epoxy- D/ZnO/ ⁇ -ZrP nanocomposite that contains 0.5 wt.% of ZnO and 0.5 wt.% of ⁇ -ZrP, and the epoxy-D/ZnO nanocomposite (0.5 wt.%) at the wavelength from 250 to around 900 nm.
• UV-vis ultraviolet-visible light
• Transmittance of the neat epoxy-D at the wavelength of above 370 nm increases as increasing the wavelength and saturates at around 91 % when the wavelength is longer than 600 nm.
• the epoxy-D/ZnO/ ⁇ -ZrP nanocomposites have a similar spectrum to the neat epoxy-D except that at the wavelength from 370 to 600 nm, the polymer nanocomposite shows a little bit lower transmittance than the neat epoxy. While having the wavelength above 600 nm, the transmittance of the polymer nanocomposites is slightly higher than that of the neat epoxy. In contrast, the epoxy-D/ZnO nanocomposite shows a much lower transmittance than either the neat epoxy or the polymer nanocomposite.
• T 1n (I -R) 2 exp(-ad) (1)
• R is the surface reflection and is given by
• n the refractive index of the pure epoxy matrix.
• the UV-vis spectrum of epoxy-D/ZnO/ ⁇ -ZrP nanocomposite is very similar to that of the neat epoxy-D. This is due to the effective dispersion of the nanoparticles and nanoplatelets, especially the ZnO nanoparticles because the ZnO nanoparticles normally tend to form large aggregates as shown in epoxy-D/ZnO nanocomposite (Fig. 3).
• the transmittance of epoxy- D/ZnO nanocomposite is much lower than that of the neat epoxy-D and the epoxy-D/ZnO/ ⁇ - ZrP nanocomposite since large ZnO aggregates have a micro-scaled size that is comparable with the wavelength of light to significantly cause light scattering to take place.
• the sizes of the dispersed nanoparticles and nanoplatelets are reduced to the nanometer-scale, such as epoxy-D/ZnO/ ⁇ -ZrP nanocomposites where the average size of the ZnO aggregate is less than about 15 nm, and an effective overall dispersion of nanoparticles is reached, light scattering due to the aggregation of ZnO nanoparticles becomes negligible.
• the exfoliated ⁇ -ZrP nanoplatelets in the epoxy matrices have an average diameter of 100 nm.
• the slightly lower transmittance of the epoxy-D/ZnO/ ⁇ -ZrP nanocomposites than that of the neat epoxy-D at the wavelength from 370 to 600 nm is believed to be due to the light scattering from the well exfoliated ⁇ -ZrP nanoplatelets in the epoxy matrix.
• the wavelength below 370 nm all the samples show a similar UV absorption due to the UV absorption from the epoxy matrix cured from DDS is overlapped with that from ZnO nanoparticles.
• FIG. 4 shows the UV-vis spectra of the neat epoxy- A, epoxy- A/ZnO nanocomposites (1.0 wt.% ZnO), epoxy- A/ ⁇ -ZrP nanocomposites (0.5 wt.% ⁇ -ZrP), and epoxy- A/ZnO/ ⁇ -ZrP nanocomposites containing 0.5 wt.% of ⁇ -ZrP nanoplatelets and 0.5, 1.0, and 2.0 wt.% of ZnO nanoparticles, respectively, at the wavelength from 250 to around 900 nm.
• Transmittance of the neat epoxy- A at the wavelength of above 300 nm increases as increasing the wavelength and saturates at around 91% when the wavelength is longer than 600 nm.
• Transmittance of the epoxy- A/ ⁇ -ZrP nanocomposite is very similar to that of the neat epoxy- A, indicating an effective dispersion of exfoliated ⁇ -ZrP nanoplatelets with no additional UV absorption after introducing ⁇ -ZrP nanoplatelets into the epoxy matrix. Additionally, all the polymer nanocomposites show extra UV absorption compared with the neat epoxy-A and the epoxy-A/ ⁇ -ZrP nanocomposites, but are still highly transparent after the addition of ZnO nanoparticles.
• the UV-vis spectra of the epoxy-A/ZnO/ ⁇ -ZrP nanocomposites show three transitions with the increase of the ZnO concentration from 0.5 to 1.0, and then to 2.0 wt.%.
• the first transition at the UV absorption onset, ⁇ shows red-shifting as the ZnO concentration increases.
• the UV absorption of the ZnO nanoparticles will shift towards the higher wavelength as the particle size increases, known as quantum size effects.
• all the ZnO nanoparticles used in this study have been prepared from the same procedure and the average particle size is around 5 nm.
• the shifting is not believed to be due to the variation of the particle size, and is believed instead that the reduction of the inter-particle distances and the increase of the degree of aggregation are likely to account for the red- shifting of the UV absorption onset as the ZnO concentration increases.
• the second transition at the wavelength from ⁇ to around 650 nm a gradual decrease of the transmittance with the increase of the ZnO concentration is observed. This is believed to be understood that as the concentration increases, the ZnO nanoparticles get closer to each other and more aggregates are formed, thus more light with the relatively shorter wavelengths is scattered.
• the third transition when the wavelength is longer than 650 nm the polymer nanocomposites containing the higher concentration of ZnO nanoparticles tend to have a higher transmittance. This unique property would be useful in optical applications.
• the epoxy and nanocomposite samples cured by DDS are chosen to study the dispersion mechanisms of the ZnO nanoparticles and ⁇ -ZrP nanoplatelets in epoxy.
• TEM micrographs of the nanocomposites with various concentrations of the two nanoparticles and nanoplatelets were analyzed when the concentration of ZnO nanoparticles is fixed at 0.5 wt.%.
• the TEM analyzes revealed that the samples become more and more transparent with an increase in the concentration of ⁇ -ZrP nanoplatelets (0, 0.1, 0.3, and 0.5 wt.%).
• a gradual decrease of the degree of the aggregation of ZnO nanoparticles with the increase of the concentration of ⁇ - ZrP nanoplatelets could also be observed from the TEM observation, which accounts for the increase in transparency.
• concentration of ⁇ -ZrP nanoplatelets is fixed to 0.5 wt.%, and the concentrations of ZnO nanoparticles are 0.5 and 0.25 wt.%, both samples were observed to be as transparent as the neat epoxy, and the 0.25 wt.% of ZnO nanoparticles nanocomposite was observed to have improved dispersion (individually dispersed in the epoxy matrix) when compared to the 0.5 wt.% of ZnO nanoparticles nanocomposites (small aggregates of ZnO nanoparticles with the average size of less than 20 run).
• FIG. 5 illustrates the UV-vis spectra of the nanocomposites with different concentrations of nanoparticles and nanoplatelets, as well as the neat epoxy-D.
• the increase of the transmittance with the increase of the concentration of ⁇ -ZrP nanoplatelets can be seen. It is observed that the existence of ⁇ -ZrP nanoplatelets improves the dispersion of ZnO nanoparticles in the epoxy matrix since the transmittance increases, which correlates to effective dispersion, with increased transmittance.
• the state of dispersion can be controlled by addition of ⁇ -ZrP nanoplatelets and that a high concentration of ZnO nanoparticles, such as up to 50% nanoparticles by weight, with the good dispersion in the polymer can be achieved by incorporating high concentration of ⁇ -ZrP nanoplatelets.
• the Young's modulus of the epoxy-D/ZnO nanocomposites is similar to that of the epoxy- D/ZnO/TBA nanocomposites, and is slightly lower than that of the neat epoxy-D, while the epoxy-D/ ⁇ -ZrP nanocomposites have a higher Young's modulus than the neat epoxy-D.
• the epoxy-D/ZnO/ ⁇ -ZrP nanocomposites have a similar Young's modulus to the epoxy- D/ ⁇ -ZrP nanocomposites, indicating that the effect of nanoscale dispersed ZnO nanoparticles on the Young's modulus of the epoxy matrix is negligible.
• Polyacrylonitrile(PAN)/ZnO and polystyrene(PS)/ZnO nanocomposites have higher Young's moduli than the polymer matrices when the ZnO concentration is 5 wt.%, and do not show obvious increase of Young's moduli when the ZnO concentration decreases to 1 wt.%.
• the increase in Young's modulus for the PAN/ZnO nanocomposite is much higher than that of the PS/ZnO nanocomposite. It is observed that the Young's modulus of the polymer/ZnO nanocomposites is strongly related to the nature of the polymer matrices. In the case of the epoxy/ZnO nanocomposites, a decrease of Young's modulus shown in this study could be that the large ZnO aggregates affecting the curing of the epoxy matrix, resulting in an incomplete cure of epoxy matrix.
• nano-scaled dispersion of semiconductor nanocrystals into polymer matrices has been easily achieved with inorganic nanoplatelets.
• the polymer nanocomposites formed thereof have a higher transmittance than the neat polymer in the higher wavelengths region because of the presence of ZnO nanoparticles also indicate that the polymer nanocomposites have UV-blocking characteristics.
• the onset of UV absorption shows red-shifting as the ZnO concentration is increased.
• the higher the concentration of ⁇ -ZrP nanoplatelets the improved the dispersion of ZnO nanoparticles in the epoxy matrix.
• polymer nanocomposites can at least maintain the mechanical properties of the epoxy matrix without losing the transparency.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Nanotechnology (AREA)
• Manufacturing & Machinery (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Physics & Mathematics (AREA)
• Composite Materials (AREA)
• Condensed Matter Physics & Semiconductors (AREA)
• General Physics & Mathematics (AREA)
• Crystallography & Structural Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (1)

Applications Claiming Priority (2)

Publications (1)

Family

ID=40281662

Family Applications (1)

Country Status (3)

Cited By (4)

Families Citing this family (6)

Citations (2)

Family Cites Families (74)

• 2007
  • 2007-07-24 US US11/880,820 patent/US8344054B2/en not_active Expired - Fee Related
• 2008
  • 2008-07-22 WO PCT/US2008/008880 patent/WO2009014685A1/en not_active Ceased
  • 2008-07-22 JP JP2010518207A patent/JP5210382B2/ja not_active Expired - Fee Related