WO2007102266A1 - グリース組成物及び軸受 - Google Patents

グリース組成物及び軸受 Download PDF

Info

Publication number
WO2007102266A1
WO2007102266A1 PCT/JP2006/325056 JP2006325056W WO2007102266A1 WO 2007102266 A1 WO2007102266 A1 WO 2007102266A1 JP 2006325056 W JP2006325056 W JP 2006325056W WO 2007102266 A1 WO2007102266 A1 WO 2007102266A1
Authority
WO
WIPO (PCT)
Prior art keywords
grease composition
mass
composition according
bearing
amine
Prior art date
Application number
PCT/JP2006/325056
Other languages
English (en)
French (fr)
Inventor
Osamu Saita
Yuji Onuki
Original Assignee
Kyodo Yushi Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kyodo Yushi Co., Ltd. filed Critical Kyodo Yushi Co., Ltd.
Priority to EP06834799A priority Critical patent/EP1995300A1/en
Publication of WO2007102266A1 publication Critical patent/WO2007102266A1/ja
Priority to US12/206,297 priority patent/US20080318819A1/en

Description

明 細 書
グリース組成物及び軸受
技術分野
[0001] 本発明は、基油、増ちよう剤、特定の酸化防止剤を含有するグリース組成物に関す る。詳しくは、高温条件にある転がり軸受に使用するのに好適な、潤滑寿命を向上し たグリース組成物、及びこれを封入した軸受に関する。
背景技術
[0002] グリース組成物の潤滑寿命を向上する為にグリース組成物に求められる性能は、熱 酸ィ匕安定性などであり、今までにもグリース組成物の性能向上に関する各種の提案 がなされている。
[0003] 潤滑基材に、アルキルチオ力ルバモイル基を有する化合物及びモリブデン化合物 を添加し、あるいはさらにエステルイ匕合物を添加することにより疲労寿命を改良した 疲労寿命改良潤滑剤が提案されている (例えば、特許文献 1参照)。また、（a)メチレ ンビス（ジ -η-ブチルジチォ力ルバメート）及び（b)トルトリアゾール又はべンゾトリァゾ 一ルのジフ ニルァミン誘導体力 成り、 (a)： (b)質量％比が約 4 : 1〜約 50 : 1の範 囲である改良された抗酸化性の抗磨耗性極圧組成物及びそれを含む潤滑剤が提案 されている（例えば、特許文献 2参照)。さらに、（a)潤滑油、（b)少なくとも 1個のヒドロ キシル基を含む炭素数 12〜24の脂肪族モノカルボン酸のリチウム塩、炭素数 2〜1 2の脂肪族ジカルボン酸の二リチウム塩、及び炭素数 12〜24の脂肪族モノカルボン 酸のリチウム塩力 なる群力 選ばれる少なくとも 1種の化合物、及び (c) 3- (N-サリ チロイル）ァミノ- 1, 2, 4-トリァゾール及びデカメチレン-ジカルボキシリックアシッド- ジサリチロイルヒドラジドからなる群力 選ばれる少なくとも 1種の化合物を含有するリ チウムグリース組成物が提案されている (例えば、特許文献 3参照)。
しかし、これらの添加剤を使用したグリース組成物を高温条件にある転がり軸受に 利用しても、熱酸ィ匕安定性及び潤滑寿命が不十分であり、ユーザーの満足するもの は未だ得られて 、な 、のが現状である。
[0004] 特許文献 1：特公平 03 - 31760 特許文献 2：特表 2005 - 509732
特許文献 3：特許第 2936084号
発明の開示
発明が解決しょうとする課題
[0005] 本発明の目的は、高温条件にある転がり軸受に好適であり、また安定した潤滑性を 長期間示すグリース組成物を提供することである。即ち、熱酸化安定性及び潤滑寿 命に優れているグリース組成物を提供することである。
本発明の他の目的は、上記グリース組成物を封入した軸受を提供することである。 課題を解決するための手段
[0006] 本発明者らは上記目的を達成するために鋭意研究の結果、基油、増ちよう剤、特 定の酸ィ匕防止剤、好ましくはさらに金属不活性化剤を用いることにより熱酸ィ匕安定性 及び潤滑寿命を改善し、高温下にある転がり軸受に好適であり、また安定した潤滑 性を長期間示すグリース組成物を完成させた。
[0007] 本発明は以下に示すグリース組成物及び軸受を提供するものである。
1. (a)基油、（b)増ちよう剤、（c)一般式（1)で表されるアルキルチオ力ルバモイル基 を有する化合物及び (d)ァミン-ケトン縮合物系酸化防止剤からなることを特徴とする グリース組成物。
(1)
Figure imgf000004_0001
(式中、 R、 R、 R、 Rは独立して炭素数 1〜20のアルキル基を示し、 Xは、 S、 S— S
1 2 3 4
、 S-CH— S、 S -CH CH— S、あるいは S— CH CH CH— Sを示す。 )
2 2 2 2 2 2
2.増ちよう剤がリチウム石けん及び複合リチウム石けん力もなる群力も選ばれる少な くとも 1種である上記 1記載のグリース組成物。
3.さらに、（e)金属不活性化剤を含有することを特徴とする上記 1又は 2記載のダリ ース組成物。
4.グリース糸且成物全体に対して、（a)基油 50質量％以上、（b)増ちよう剤 1〜30質 量％、（c)一般式（1)で表されるアルキルチォカルバモイル基を有する化合物 0. 1 〜10質量％、（d)アミン-ケトン縮合物系酸ィ匕防止剤 0. 1〜10質量％を含有する上 記 1〜 3の 、ずれ力ゝ 1項記載のダリース組成物。
5. (e)金属不活性化剤 0. 1〜10質量％を含むことを特徴とする上記 2〜4のいずれ 力 1項記載のダリース組成物。
6.上記 1〜5のいずれか 1項記載のグリース組成物を封入した軸受。
発明の効果
[0008] 本発明のグリース組成物は、改善された熱酸化安定性及び潤滑寿命を有し、高温 条件にある転がり軸受に使用するのに好適であり、また安定した潤滑性を長期間示 すため、非常に有用である。
[0009] 従来、基油とリチウム系グリース組成物と、これを封入した軸受において、特定の酸 化防止剤、及び金属不活性化剤を用いることにより、熱酸化安定性及び潤滑寿命を 改善し、高温下にある転がり軸受に好適であり、また安定した潤滑性を長期間示すグ リース組成物について、未だ満足する提案はされておらず、極めて有用な発明と言 える。
[0010] 本発明は、基油と増ちよう剤を含有するグリース組成物において、特定の酸化防止 剤、あるいはさらに特定の金属不活性化剤を使用し、さらに好ましくはその混合割合 を特定することにより、熱酸ィ匕安定性及び潤滑寿命が著しく向上するという知見に基 づ 、てなされたものである。
[0011] 本発明のグリース組成物が高温条件において潤滑寿命に優れている理由は、基油 と増ちよう剤力もなるグリース組成物に、特に選ばれた酸化防止剤、あるいはさらに金 属不活性化剤を用いたことにより、各成分の機能が十分に発揮され、さらに、適正な 配合処方も相俟って高温環境下にあるグリース組成物に優れた熱酸ィ匕安定性、潤滑 性及び潤滑寿命が付与されたものと考えられる。
発明を実施するための最良の形態
[0012] 以下本発明について詳細に説明する。
本発明のグリース組成物に使用される基油としては、鉱物油及び Z又は合成油の 群の少なくとも 1種類を含有するものが好ましい。合成油としては、エステル、ポリオ一 ルエステルに代表されるエステル系合成油、ポリ α—ォレフイン、ポリブテンに代表さ れる合成炭化水素油、アルキルジフエ-ルエーテル、ポリプロピレングリコールに代 表されるエーテル系合成油、シリコン油、フッ素化油などが挙げられ、潤滑油及びグ リース糸且成物に使用出来るものであれば特に限定されな 、。
本発明のグリース糸且成物に使用される増ちよう剤は、金属石けん系増ちよう剤、ジゥ レアに代表されるゥレア系増ちよう剤、有機化クレイやシリカに代表される無機系増ち よう剤、ポリテトラフルォロエチレン、及びメラミンシァヌレートに代表される有機系増ち よう剤力も選ばれる少なくとも 1種類である。好ましいのは、リチウム石けん及び複合リ チウム石けん力 なる群力 選ばれるものであり、特に好ましいのは、リチウム石けん
、例えば、ステアリン酸リチウムや 12—ヒドロキシステアリン酸リチウムである。
[0013] 本発明のグリース組成物に使用される酸ィ匕防止剤は、（c)一般式（1)で表されるァ ルキルチオ力ルバモイル基を有する化合物 (ATC)、及び (d)アミンーケトン縮合物 系酸化防止剤である。
(c)一般式（1)で表されるアルキルチオ力ルバモイル基を有する化合物 (ATC)の具 体例としては、メチレンビス（ジ -n-ブチルジチォ力ルバメート）、ビス（ジメチルカルバ モイル）モノスルフイド、ビス（ジメチルカルバモイル）ジスルフイド、ビス（ジブチルカル バモイル）ジスルフイド、ビス（ジアミルカルバモイル）ジスルフイド、ビス（ジォクチルカ ルバモイル）ジスルフイド等が挙げられる。
(d)アミン―ケトン縮合物系酸ィ匕防止剤としては、 JIS K6220— 3の略号で式（2)で 表される TMDQ (2, 2, 4-トリメチル - 1, 2 ジヒドロキノリン重合体）、式（3)で表され る ETMDQ (6-エトキシ -2, 2, 4-トリメチル 1, 2-ジヒドロキノリン）及び ADPAL ( ジフエニルァミンとアセトンの反応混合物）等が挙げられる。
[0014] TMDQ ;2,2,4-トリメチル -1,2-ジヒドロキノリン重合体
(2)
Figure imgf000007_0001
式中 nは 1〜10、好ましくは 1〜6、特に好ましくは 2〜3の数である。
ETMDQ ;6-エトキシ- 2,2,4-トリメチル -1,2-ジヒドロキノリン
(3)
Figure imgf000007_0002
[0016] 本発明のグリース組成物は好ましくは金属不活性化剤を含有する。金属不活性ィ匕 剤としては、シユウ酸誘導体，サリチル酸誘導体，ヒドラジン誘導体などが挙げられ、 特に式 (4)で表される 3- (N-サリチロイル)ァミノ- 1, 2, 4-トリァゾール、式（5)で表さ れるデカメチレンカルボン酸ジサリチロイルヒドラジド（MCSH)、式（6)で表される N, N-ビス [3- (3, 5-ジ -t-ブチル -4-ヒドロキシフエ-ル）プロピオ-ル]ヒドラジン、イソ フタル酸ビス（2-フエノキシプロピオ-ルヒドラジド）、 N-ホルミル- Ν'-サリシロイルヒド ラジン、 2, 2-ォキザミドビス- [ェチル -3- (3, 5-ジ -t-ブチル -4-ノヽイド口ォキシフエ -ル)プロピオネート]、オギザリル ビス一べンジリデン一ヒドラジドなどが举げられる
[0017] 3- (N-サリチロイル）ァミノ- 1, 2, 4-トリァゾール
(4)
Figure imgf000008_0001
MCSH：デカメチレンカルボン酸ジサリチロイルヒドラジド
(5)
Figure imgf000008_0002
N, N-t^[3- (3, 5-ジ -t-ブチル -4-ヒドロキシフエ-ル）プロピオ-ル]ヒドラジン (6)
Figure imgf000008_0003
本発明のグリース組成物は、グリース組成物全体に対して、（a)基油 50質量％以上 、好ましくは 60質量％以上、（b)増ちよう剤 1〜30質量％、好ましくは 5〜20質量％、 (c)一般式（1)で表されるアルキルチォカルバモイル基を有する化合物 0. 1〜： L0質 量0 /0、好ましくは 0. 5〜5質量0 /0、（d)アミン―ケトン縮合物系酸ィ匕防止剤 0. 1〜10 質量％、好ましくは 0. 5〜5質量％を含有する。また、上記配合の（a)〜（d)に (e)金 属不活性化剤 0. 1〜10質量％、好ましくは 0. 5〜5質量％を添加しても良い。
本発明は、上記グリース組成物を封入した軸受をも提供する。 [0021] 以下、実施例によって本発明をさらに詳述するが、下記の実施例は本発明を制限 するものでなぐ本発明の趣旨を逸脱しない範囲で変更実施することは全て本発明 の技術範囲に包含される。
実施例
[0022] 1.試験用グリース
表 1及び表 2に示した配合処方により、実施例 1〜8、比較例 1〜5のグリース組成 物を調製した。各成分の量は、質量％である。
[0023] 2.グリースの製造方法
基油 467. 5gの中に 12—ヒドロキシステアリン酸 82.5gを加え、完全に透明な液体 状態になる温度（80〜90°C)に加熱した。これに予め水 60gに水酸化リチウム 1水塩 11. 9gを添加して加熱溶解したものをカ卩え、激しく攪拌しながら 12—ヒドロキシステ アリン酸のけん化反応を行って 12—ヒドロキシステアリン酸のリチウム塩を形成した。 次に、ァゼライン酸 26gを加えて均一な状態になるまで攪拌を継続した。これに予め 水 60gに水酸化リチウム 1水塩 11. 9gを添加して加熱溶解したものをカ卩え、激しく攪 拌しながらァゼライン酸のけん化反応を行った。約 60分後赤外分光分析で未反応脂 肪酸の吸収が見られないことを確認してけん化反応を終了させた。次に、加熱工程 に入り内容物を 200°Cまで徐々に加熱した。 200°Cになった時点で残りの基油 400. 2gを添カ卩しそのまま室温まで冷却し、三段ロールを 2回通して、リチウムコンプレック スグリースを得た。最終の内容物の量は lOOOgとした。
基油としては、エーテル油（アルキルジフエ-ルエーテル：動粘度 40°C lOOmmVs, 100°C 12.5mm2/s)、エステル油（ペンタエリスリトールエステル：動粘度 40°C 102mm2 /s, 100°C 12.9mm2/s)、これらの 1 : 1混合物を使用した。
[0024] 3.分析方法及び評価試験方法
漏寿侖麵
ASTM D 3336に準拠した試験方法で行う。試験は 150°Cで行い、潤滑寿命を時間（ h)で表示する。
高温薄蹬試,験
60 X 80 X 1mmの SPCC鋼板にグリースを 2mm厚で塗布し、規定温度（160°C)、規定 時間（500h)後の全酸価を測定する。
[0025] 4.評価試験の結果
表 1及び表 2に実施例 1〜6、比較例 1〜5のダリース組成物の試験結果を示す。
[0026] [表 1]
Figure imgf000010_0001
* 1ATC：メチレンビス（ジ -n-ブチノレジチォカノレバメート）
* 2アミン系酸化防止剤： N—フエ-ルー 1, 1, 3, 3—テトラメチルブチルナフタレン 1ーァミン
* 3フエノール系酸化防止剤：ペンタエリスリトールテトラキス（3— (3, 5—ジ—tーブ チル— 4—ヒドロキシフエ-ル）プロピオネート
[表 2]
比較例 比較例 比較例 比較例 比較例
1 2 3 4 5
(a)エーテノレ油 41. 75 84. 0 42. 75 42. 0
(a)エステル油 41. 75 84. 0 ― 42. 75 42. 0
(b)增ちょ う剤 13. 0 13. 0 13. 0 13. 0 13. 0
(c) A T C * 1 ― ― ― 0. 5 ―
(d) T M D Q 2. 0
(e) M C S H 0. 5
アミン系酸化防止剤 * 2 2. 0 2. 0 2. 0
フエノ ル系酸化防止剤 * 3 1. 0 1. 0 1. 0 1. 0 1. 0
軸受潤滑寿命（150°C ) h 860 590 410 630 780
評価結果 X X X X X
咼温薄膜！^験刖 0. 05 0. 06 0. 06 0. 06 0. 05 全酸価 (mgKOH/g)
高温薄膜試験後 1. 90 2. 20 10. 6 1. 26 0. 68
全酸価 (mgKOH/g)
酸価の変化 (mgKOH/g) 1. 85 2. 14 10. 54 1. 20 0. 63
酸価の変化の評価結果 X X X X X
総合評価 X X X X X
[0028] 評価某準
酸価の変化（mgKOH/g) 〇 ： 0. 20以下、 X ： 0. 20超
軸受潤滑寿命 〇 ： 合格 1000h超、 X ： 不合格 1000以下
総合評価 〇 ： 酸価変化及ぴ軸受潤滑寿命の両方が合格 （O )
X ： 酸価変化又は/及ぴ軸受潤滑寿命が不合格 （X )
[0029] 試験結果
成分 (a)〜（d)を含有する実施例 1、 4、 7及び 8、成分 (a)〜（e)を含有する実施例 2、 3、 5及び 6のグリース組成物は、酸価の変化が少なく熱酸化安定性に優れ、軸受 潤滑寿命もすベて基準を達成し、総合評価にお!ヽて合格であった。
これに対して、実施例 1において成分 (d)を含有しない比較例 4では、酸価の変化 が大きく熱酸化安定性に劣り、軸受潤滑寿命も短い。
実施例 1にお!ヽて成分 (c)を含有しな!ヽ比較例 5では、酸価の変化が大きく熱酸化 安定性に劣り、軸受潤滑寿命も短い。
実施例 2にお 、て成分 (c)及び (d)の代わりに従来のアミン系酸化防止剤を含有さ せた比較例 1では、酸価の変化が大きく熱酸ィヒ安定性に劣り、軸受潤滑寿命が短い 基油としてエステル油を使用し、成分 (c)〜（e)の代わりに従来のアミン系酸ィ匕防止 剤を含有させた比較例 2では、酸価の変化が大きく熱酸ィヒ安定性に劣り、軸受潤滑 寿命がさらに短い。
基油としてエーテル油を使用し、成分 (c)〜（e)の代わりに従来のアミン系酸化防 止剤を含有させた比較例 3では、酸価の変化が大きく熱酸ィ匕安定性に劣り、軸受潤 滑寿命も最も短い。

Claims

請求の範囲 (a)基油、（b)増ちよう剤、（c)一般式（1)で表されるアルキルチオ力ルバモイル基を 有する化合物、及び (d)ァミン-ケトン縮合物系酸化防止剤を含有することを特徴とす るグリース組成物。
(1)
Figure imgf000013_0001
(式中、 R、 R、 R、 Rは独立して炭素数 1〜20のアルキル基を示し、 Xは、 S、 S— S
1 2 3 4
、 S-CH— S、 S -CH CH— S、あるいは S— CH CH CH— Sを示す。 )
2 2 2 2 2 2
[2] 増ちよう剤がリチウム石けん及び複合リチウム石けん力もなる群力 選ばれる少なく とも 1種である請求項 1記載のグリース組成物。
[3] さらに、（e)金属不活性化剤を含有することを特徴とする請求項 1記載のグリース組 成物。
[4] さらに、（e)金属不活性化剤を含有することを特徴とする請求項 2記載のグリース組 成物。
[5] グリース組成物全体に対して、（a)基油 50質量％以上、（b)増ちよう剤 1〜30質量 %、（c)一般式（1)で表されるアルキルチォカルバモイル基を有する化合物 0. 1〜1 0質量％、（d)アミン-ケトン縮合物系酸ィ匕防止剤 0. 1〜10質量％を含有する請求項 1記載のグリース組成物。
[6] グリース組成物全体に対して、（a)基油 50質量％以上、（b)増ちよう剤 1〜30質量 %、（c)一般式（1)で表されるアルキルチォカルバモイル基を有する化合物 0. 1〜1 0質量％、（d)アミン-ケトン縮合物系酸ィ匕防止剤 0. 1〜10質量％を含有する請求項 2記載のグリース組成物。
[7] (e)金属不活性化剤 0. 1〜10質量％を含むことを特徴とする請求項 5記載のダリ ース組成物。
[8] (e)金属不活性化剤 0. 1〜10質量％を含むことを特徴とする請求項 6記載のダリ ース組成物。 [9] 請求項 1〜8の 、ずれか 1項記載のグリース組成物を封入した軸受。
PCT/JP2006/325056 2006-03-08 2006-12-15 グリース組成物及び軸受 WO2007102266A1 (ja)