WO2007083596A1 - 繊維構造物 - Google Patents

繊維構造物 Download PDF

Info

Publication number
WO2007083596A1
WO2007083596A1 PCT/JP2007/050410 JP2007050410W WO2007083596A1 WO 2007083596 A1 WO2007083596 A1 WO 2007083596A1 JP 2007050410 W JP2007050410 W JP 2007050410W WO 2007083596 A1 WO2007083596 A1 WO 2007083596A1
Authority
WO
WIPO (PCT)
Prior art keywords
containing compound
compound
fiber structure
fiber
grade
Prior art date
Application number
PCT/JP2007/050410
Other languages
English (en)
French (fr)
Inventor
Masao Seki
Rumi Karasawa
Wataru Abe
Toshiaki Shimizu
Takashi Kawasaki
Masanobu Sato
Original Assignee
Toray Industries, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Industries, Inc. filed Critical Toray Industries, Inc.
Priority to US12/160,944 priority Critical patent/US20100192272A1/en
Priority to JP2007508200A priority patent/JPWO2007083596A1/ja
Priority to EP07706744A priority patent/EP1978151A4/en
Publication of WO2007083596A1 publication Critical patent/WO2007083596A1/ja

Abstract

【課題】洗濯耐久性に優れた撥水・撥油性、防汚性を有する繊維構造物を安定して供給する。 【解決手段】単繊維表面が、トリアジン環含有化合物含有樹脂被膜または有機フッ素化合物およびトリアジン環含有化合物含有樹脂被膜を介して、有機フッ素系化合物含有樹脂被膜で被覆された繊維を用いてなる繊維構造物であって、該繊維構造物の洗濯２０回後の撥水性が４級以上、撥油性が４級以上であることを特徴とする繊維構造物。

Description

明 細 書
繊維構造物
技術分野
[0001] 本発明は、耐久性に優れた撥水性、撥油性および防汚性を有する繊維構造物に 関するものである。
背景技術
[0002] 従来から合成繊維、天然繊維およびその混用繊維からなる布帛などに、撥水性、 撥
油性を付与する方法としてフッ素系化合物やシリコン系化合物などで布帛を処理す ることが数多く行われて 、る。
[0003] 近年、消費者の撥水性や撥油性能に関する要求が一段と高まり、特にウィンドブレ 一力一、ゴルフウェアー、スキーウェアーなどのスポーツ衣料分野で洗濯耐久性に 優れるものの要求が強ぐコート、ブラウス、スラックス、スカートなどの婦人衣料用途 や作業衣、制服などのユニホーム衣料分野では耐久性ある撥水性、撥油性に加えて 、防汚性、特に食品に対する汚れにくさや付着した汚れが洗濯で落ちやすいものの 要求が高まっている。
[0004] 繊維布帛に洗濯耐久性のある撥水性、撥油性を付与する手段として、イソシァネー ト系化合物を混合する方法 (特許文献 1)、イソシァネート系化合物で処理した後に撥 水剤で処理する方法 (特許文献 2)、重合性ビニル基と縮合性メチロール基を含有す る化合物で処理する方法 (特許文献 3)、水系のフッ素系撥水撥油剤で処理した後に 溶剤系のフッ素系撥水撥油剤で処理する方法 (特許文献 4)、洗濯時の耐摩耗性を 改善する方法 (特許文献 5)などが挙げられるが、 V、ずれも洗濯耐久性が不十分であ り、かつ防汚性を兼ね備えたものの提案はされて 、な 、。
[0005] また、撥水性、撥油性は水着に対しても要求されることが多く（特許文献 6、 7)、特 に競泳用水着などは低抵抗性を目的にしたり、一般水着では低水濡れ性による健康 上のエネルギーロスを抑えることを目的とされている。し力しながら、砂浜等で水着を 着用した際に、撥水性のない水着や、撥水性能があっても撥水性が低い水着などは 、水着および Zまたは砂が濡れて 、ると水着に砂が付着するため外観上の問題があ り、さらに一部の砂は一時的に付着するば力りでなぐ織編物の生地の隙間に入り込 んでしまい、洗濯しても除去できない等の問題があるが、この問題に着目した提案は 見あたらない。
特許文献 1 :特開昭 54— 133486号公報
特許文献 2：特開昭 54— 139641号公報
特許文献 3：特開昭 59— 130374号公報
特許文献 4：特開昭 60 - 151380号公報
特許文献 5：特開平 7 - 216749号公報
特許文献 6：特開平 11― 279810号公報
特許文献 7：特開 2002 - 294563号公報
発明の開示
発明が解決しょうとする課題
[0006] 本発明の目的は、力かる従来技術の背景に鑑み、洗濯耐久性に優れた撥水性、 撥油性と防汚性を兼ね備えた繊維構造物を提供することにある。
課題を解決するための手段
[0007] 本発明は、上記課題を解決するために、次のような手段を採用するものである。
(1)単繊維表面が、トリアジン環含有化合物含有榭脂被膜または有機フッ素化合物 およびトリアジン環含有化合物含有榭脂被膜を介して、有機フッ素系化合物含有榭 脂被膜で被覆された繊維を用いてなる繊維構造物であって、該繊維構造物の洗濯 2 0回後の撥水性力 級以上、撥油性が 4級以上であることを特徴とする繊維構造物。
(2)該トリアジン環含有化合物含有榭脂被膜、または有機含フッ素化合物およびトリ アジン環含有化合物含有榭脂被膜の膜厚が、 5〜： LOOnmである上記 (1)記載の繊維 構造物。
(3)該有機フッ素系化合物含有榭脂被膜がトリアジン環含有ィ匕合物または Zおよび イソシァネート系化合物を含有している上記 (1)または (2)に記載の繊維構造物。
(4)該繊維構造物の洗濯 20回後の食品汚れの汚染性が 3級以上で、洗濯除去性が 3級以上であることを特徴とする上記 (1)〜(3)のいずれかに記載の繊維構造物。 (5)該繊維構造物の洗濯 20回後の墨汁汚れの汚染性が 3級以上、洗濯除去性が 4 級以上であることを特徴とする上記 (1)〜(3)のいずれかに記載の繊維構造物。
(6)該繊維構造物の洗濯 20回後の砂付着防止性が 3級以上であることを特徴とする 上記 (1)〜(3)の 、ずれかに記載の繊維構造物。
(7)該繊維構造物の洗濯 20回後の泥汚れ除去性力 級以上であることを特徴とする 上記 (1)〜(3)の 、ずれかに記載の繊維構造物。
(8)上記 (6)記載の繊維構造物を用いてなる水着。
(9)布帛の少なくとも一部に、ポリウレタン系弾性糸および Zまたはポリトリメチレンテ レフタレート繊維を用いたことを特徴とする上記 (8)記載の水着。
発明の効果
[0008] 本発明によれば、繊維表面に極めて薄い重合膜を介してフッ素系撥水 ·撥油系化 合物の層が形成されたり、またはフッ素系撥水 ·撥油化合物を含有する極めて薄い 重合膜が形成されるので、洗濯耐久性に優れた撥水'撥油性、防汚性を有する繊維 構造物を安定して供給することができる。
[0009] 本発明の多機能を有する繊維構造物は、特にスポーツ衣料用途、ユニホーム衣料 用途、カジュアル衣料用途、一般衣料用途、寝装用途、インテリア用途などに有効に 使用できるものである。
発明を実施するための最良の形態
[0010] 本発明者らは、前記課題、すなわち洗濯耐久性に優れた撥水性、撥油性と防汚性 を兼ね備えた機能を付与することについて鋭意検討した結果、単繊維表面にトリアジ ン環含有化合物含有榭脂被膜を介して、有機フッ素系化合物含有榭脂被膜を層状 に被覆する、または単繊維表面に、有機フッ素化合物およびトリアジン環含有化合物 を含有する榭脂被膜を被覆することにより、カゝかる課題を一挙に解決することを究明 したものである。
[0011] 本発明の繊維構造物に使用される繊維素材としては、ポリエチレンテレフタレート、 ポリプロピレンフタレートおよびポリブチレンテレフタレートなどや、これらに第三成分 を共重合してなる芳香族ポリエステル系繊維、 L 乳酸を主成分とするもので代表さ れる脂肪族ポリエステル系繊維、ナイロン 6やナイロン 66などのポリアミド系繊維、ポリ アクリロニトリルを主成分とするアクリル系繊維、ポリエチレンやポリプロピレンなどのポ リオレフイン系繊維、ポリ塩ィ匕ビュル系繊維などの合成繊維、アセテートやレーヨンな どの半合成繊維、木綿、絹および羊毛などの天然繊維などが挙げられる。本発明で は、これらの繊維を単独または 2種以上の混合物として使用することができる力 ポリ エステル系繊維またはポリアミド系繊維を主成分にした繊維が好ましく使用される。
[0012] また、ポリウレタン系弾性糸やポリトリメチレンテレフタレート単独糸、粘度差や重合 度差、収縮性能差等を有する 2種以上のポリトリメチレンテレフタレートを用いてなる バイメタル構造に代表されるコンジュゲート糸、ポリメチレンテレフタレートとポリエチレ ンテレフタレートとのコンジユゲート糸等を使用することができる。
[0013] 本発明で用いられる繊維は、通常のフラットヤーン以外に、仮撚り加工糸、強撚糸 、タスランカ卩ェ糸、太細糸および混繊糸等のフィラメントヤーンであってもよぐステー プルファイバーやトウ、ある 、は紡績糸など各種形態の繊維であってもよ 、。
[0014] 本発明の繊維構造物には、前記繊維を使用してなる編物、織物または不織布など の布帛状物、あるいは紐状物等が含まれる。
[0015] 本発明は、上記繊維素材の単繊維表面に、トリアジン環含有化合物含有榭脂被膜 または、有機フッ素化合物およびトリアジン環含有化合物含有榭脂被膜が形成され ているものである。すなわち、トリアジン環含有化合物を必須成分として含有してなる 榭脂被膜または、有機フッ素化合物およびトリアジン環含有ィ匕合物を必須成分として 含有してなる榭脂被膜が、単繊維表面に形成されて 、るものである。
[0016] 本発明のトリアジン環含有ィ匕合物とはトリアジン環を含有し、重合性官能基を少なく とも 2個有する化合物であり、例えば下記一般式で示されるものが挙げられる。
[0017] [化 1] 〔〕
式中、 R0〜R2:-H、 -0H、 -C6H5、 -CnoH2nO+i(nO: 1〜2)、 -C00CnlH2ni+i(nl： 1〜20)、 -CONR3R4、 -NR3R4 ただし、 R3、 R4:-H、 -OCn3H2n3+l、 -
OCn3H2n3+l、 -CH2COOCn3H2n3+l (n3 : 1〜20)、 -CH2OH, -CH2CH20H, -
C0NH2、 -CONHCH20H-0-(X-0)n4-R6 (X： C2H4、 C3H6、 C4H8、 n4 : 1〜 1500 R5:-H、- CH3、-C3H7)
Figure imgf000006_0001
[0019] 本発明のトリアジン環含有ィ匕合物含有榭脂被膜または、有機フッ素化合物およびト リアジン環含有化合物含有榭脂被膜 (以下、「トリアジン環含有化合物等含有榭脂被 膜」と 、う）の形成方法は次のとおりである。
[0020] 上記榭脂被膜を形成するためのモノマーと、触媒力 なる水系液を繊維上に付与 した後、重合すべく熱処理を行う。
[0021] 力かる触媒としては、酢酸、蟻酸、アクリル酸、リンゴ酸、酒石酸、マレイン酸、フタル 酸、硫酸、過硫酸、塩酸、燐酸などの酸類およびこれらのアンモ-ゥム塩、ナトリウム 塩、カリウム塩、マグネシウム塩などであり、これらの一種以上を使用することができる 。中でも、触媒として過硫酸アンモ-ゥムと過硫酸カリウムが好ましく使用できる。かか る触媒の量は、モノマーの使用量に対して 0. 1〜20重量％で使用することが好まし い。
[0022] 力かる重合のための熱処理は、好ましくは 50〜180°Cの温度で 0. 1〜30分間の 条件で乾熱処理および蒸熱処理するものであるが、蒸熱処理の方が単繊維表面に 均一な被膜を形成しやすぐかつ、被膜形成後の風合いが柔軟である。かかる蒸熱 処理は、好ましくは 80〜160°Cの飽和水蒸気または過熱水蒸気が用いられ、より好 ましくは飽和水蒸気の場合は 90〜 130°Cの飽和水蒸気であり、または 110〜 160°C の温度の過熱水蒸気であり、いずれも数秒力 数分の処理を行う。かかる蒸熱処理 を行った後、未反応のモノマーや触媒を除去および染色堅牢度の確保のために、 5 0〜95°Cの温度で湯洗!ヽか、ノ-オン界面活性剤や炭酸ソーダを使用しての洗浄を 行うことが好ま ヽ。トリアジン環含有化合物等含有樹脂の付着量は繊維重量に対し て好ましくは 0. 5〜5重量％であり、より好ましくは 1〜3重量％である。
[0023] 本発明にお ヽて、有機フッ素化合物およびトリアジン環含有化合物含有榭脂被膜 を形成する場合、トリアジン環含有化合物と有機フッ素化合物の混合溶液を用いて、 前記と同様の処理を行うことにより被膜を形成することができる。該トリアジン環含有 化合物と有機フッ素化合物の混合重量比（トリアジン環含有ィ匕合物 Z有機フッ素化 合物）が、 I/O. 001〜1であることが好ましい。ただし、力かる処理の後に行う有機 含フッ素化合物の処理時に、該処理剤の濡れ性、浸透性を阻害しないよう、被膜形 成後に乾燥、熱処理を行う場合は撥水性を 3級以下、好ましくは 2級以下になるよう に混合比を決定することが好ましい。該有機フッ素化合物は、該処理の後に行う有機 フッ素化合物含有榭脂被膜に用いられるフッ素化合物と同種の化合物であっても、 また異種の化合物であっても使用することができる。
[0024] 本発明のトリアジン環含有化合物等含有榭脂被膜は、透過型電子顕微鏡 (TEM) を用い 100000倍で観察した厚みが 5〜： LOOnmであることが好ましい。上記の形成 方法で作成することにより、カゝかる膜厚の被膜が形成されるものである。本発明は、ト リアジン環含有ィ匕合物等含有榭脂被膜に無機粒子を含有させることができる。無機 粒子としては、酸ィ匕アルミニウム、酸化ケィ素、酸化チタン、カオリナイト、タルク、炭酸 カルシウム、珪酸カルシウム、酸ィ匕マグネシウム等が挙げられ、これらを単独あるいは 2種以上を混合して使用することができる。該粒子の粒子径としては、数平均粒子経 で 5〜400nmであることが好ましぐさらには 10〜100nmのものを使用することが好 ましい。無機粒子は水分散体の状態で使用するのが好ましい。本発明の無機粒子は 重合性モノマーの水溶液に混合して使用することができ、重合性モノマーとの重量 混合比は、モノマー 1に対して好ましくは 0. 03-1. 0であり、より好ましくは 0. 05〜 0. 5である。該粒子の混合により、トリアジン環含有化合物等含有榭脂被膜の形成 性が向上し、強靱な被膜を形成できるので耐久性を更に高めることができる。本発明 の被膜形成時に、本発明の効果を阻害しない範囲で他の化合物、例えば吸水剤、 吸湿剤、紫外線吸収剤、光安定剤、滑剤、増摩剤、有機粒子、制電剤、消臭剤、抗 菌剤、難燃剤、着色剤、深色剤、撥水剤、撥油剤、防汚剤などを添加してもカゝまわな い。
[0025] 本発明においては、上記トリアジン環等含有ィ匕合物含有榭脂被膜上に有機フッ素 化合物含有榭脂被膜が形成されているものである。有機フッ素化合物としては、下記 一般式で表されるパーフルォロアルキル基を含有するアタリレート系化合物が例示さ れる。
[0026] [化 2]
アルキル基を持ち、かつ水酸 基を含む基。 mは 1〜20の整数
Figure imgf000009_0001
含むものである。
[0028] 有機フッ素化合物含有榭脂被膜の加工方法としては、水系液または溶剤系液に、 トリアジン環含有ィ匕合物の被膜を形成した繊維構造物を浸潰して、目標とする付着 量になるようにマングルなどで絞り、好適には 100〜150°Cの温度で乾燥し、好適に は 160〜 190°Cの温度で熱処理する力 希釈液に浸漬したまま温度を 60〜 130°C にして繊維表面に吸着させることで製造することができるが、この方法に限定されるも のではない。有機フッ素化合物含有樹脂の付着量は、繊維重量に対して好ましくは 0. 1〜8重量％であり、より好ましくは 0. 5〜4重量％である。該有機フッ素化合物は 、トリアジン環含有化合物、イソシァネート系化合物のうちの少なくとも一種を含有し て被膜層を形成していることが好ましい。トリアジン環含有ィ匕合物としては、前記した 被膜形成に使用するものと同種のものを使用してもよぐ異種のものでも使用すること ができる。イソシァネート系化合物としては、イソシァネート基を亜硫酸ソーダ、メチル ェチルケトンノキシムなどのォキシム系化合物などによりブロック化したイソシァネート 基を 2個以上持つ化合物が使用できる。更に、本発明の効果を阻害しない範囲で他 の化合物、例えば、吸水剤、吸湿剤、紫外線吸収剤、光安定剤、滑剤、増摩剤、無 機粒子、有機粒子、制電剤、消臭剤、抗菌剤、難燃剤、着色剤、深色剤、撥水剤、 撥油剤、防汚剤などを添加することができる。
[0029] 本発明の繊維構造物は、洗濯 20回後の撥水性が 4級以上、撥油性が 4級以上で ある。有機フッ系化合物が単独で繊維に直接固着するのではなぐトリアジン環含有 化合物等榭脂被膜を介して固着することによって、または有機フッ系化合物がトリア ジン環含有化合物とともに榭脂に含有された状態で、単繊維に固着されることによつ て、有機フッ系化合物の洗濯耐久性が大幅に向上し、洗濯 20回後も撥水性、撥油 性が 4級以上と 、う高 、性能を示すものである。
[0030] さらに、力かるトリアジン環含有ィ匕合物等含有榭脂被膜の膜厚が 5〜： LOOnmであり 、薄膜構造を有するため、洗濯による樹脂の脱落が更に抑えられ、洗濯耐久性を格 段に向上させるものである。このような高い撥水性、撥油性を示すことから、本発明の 繊維構造物は優れた防汚性を示す。
[0031] 本発明の繊維構造物は、洗濯 20回後の食品汚れの汚染性、つまり付きにくさが 3 級以上、洗濯除去性が 3級以上である。有機フッ系化合物およびトリアジン環含有化 合物が繊維に均一に被膜形成されており、洗濯 20回後の撥水性、撥油性が 4級以 上という性能を有することにより、水系、油系の混在した食品汚れに対しても、汚染性 3級以上、洗濯除去性 3級以上と 、う性能を発揮するのである。
[0032] また、本発明の繊維構造物は洗濯 20回後の墨汁汚れの汚染性、つまり付きにくさ 力 S3級以上、洗濯除去性力 級以上である。墨汁は炭素の他に、にかわが含有され ており、粘着性の高い物質であるため、付着しやすく落ちにくい性質があるが、上記 と同様に有機フッ系化合物およびトリアジン環含有ィ匕合物が繊維に均一に被膜形成 されており、洗濯 20回後の撥水性、撥油性力 級以上という性能有することにより、か 力る墨汁の防汚性についても、汚染性 3級以上、洗濯除去性 4級以上という性能を発 揮するのである。
[0033] また、本発明の繊維構造物は洗濯 20回後の砂付着防止性、つまり付きにくさが 3 級以上である。
[0034] 繊維構造物を、たとえば砂浜等で水着として着用した際に、砂の付着が少ないとい うものであり、洗濯 20回後の撥水性力 級以上という性能を有することにより、かかる 砂の付着防止効果を向上させることができる。また、水着におけるサンオイルで包ま れた砂やサンオイルそのものの付着を考慮すると高 、撥油性も必要である力 本発 明の繊維構造物は、撥油性についても洗濯 20回後において 4級以上の性能を有す るため、砂付着防止性 3級以上の繊維構造物を得ることができるのである。したがつ て、本発明の繊維構造物は水着として好適に用いられる。
[0035] また、本発明の繊維構造物の洗濯 20回後の泥汚れ除去性は 4級以上である。泥 は水分や油を含んだ状態で日常生活やスポーツ時に、擦り込まれるように付着する ことが多い。このような場合、本発明においては、有機フッ素系化合物およびトリアジ ン環含有化合物を用いた被膜が繊維に均一に形成され、洗濯 20回後の撥水性、撥 油性力 級以上であることから、繊維に直接泥汚れが付着するのを防止することがで きょって力かる泥汚れ防汚性を向上させ、除去性が 4級以上の繊維構造物を得られ ることができるのである。
実施例 [0036] 次に、実施例により本発明を詳細に説明するが、本発明はこれらに限定されるもの ではない。なお、実施例中における各種性能は、下記の方法で評価したものである。 <撥水性 >
JIS L 1092「繊維製品の防水性試験方法」（1998)に規定されるスプレー法で測 し 7こ。
<撥油性 >
AATCC TM— 1966に規定される方法で測定した。
<防汚性>
1.食品汚れおよび墨汁については以下に示す方法で評価した。
(1)汚染剤
A.食品汚れ
(a)液体
•ウスターソース (力ゴメウスター醸熟)を常温で使用。
[0037] 'コーヒー（ネスカフェゴールドブレンド Zブライト Z砂糖)を 90°Cで使用。
[0038] ·醤油（キッコーマン)を常温で使用。
[0039] 'ゴマ油（かど屋純正ゴマ油）を常温で使用。
[0040] (b)ペースト
•ケチャップ (力ゴメトマトケチャップ)を常温で使用。
[0041] B.墨汁
(a)液体
• (株)呉竹清昇堂書道液 (呉竹清昇堂製)を常温で使用。
(2)試験手順
(a)lOcm X 10cmの試験片を採取する。
[0042] (b)試験片を lOcm X 10cmのガラス板上に置き、汚染剤を試験片の中央部に滴下 し、その上に厚さ lmmの 5cm X 5cmのガラス板を置き、該ガラス板の上に 200gの荷 重を乗せて 1分間放置する。
[0043] 汚染剤の滴下量は、液体のものは 0. lcc、ペースト状のものは 0. lgとする。
[0044] (c)荷重とガラス板を取り除いて、試験片を濾紙の上に移してティッシュペーパーを かぶせ、その上からローラー掛けして汚れを拭き取り、水平状態で 24時間放置して 自然乾燥する。
[0045] (d)汚染後の試験片の汚染性を JIS染色堅ロウ度用汚染判定用グレースケールで汚 染の程度を等級判定し、「汚染性」とする。
[0046] (e)汚染後の試験片を、自動反転渦巻き電気洗濯機に、 JIS K 337に規定される 弱アルカリ性合成洗剤を 0. 1%の濃度になるように溶解した液 25Lで、浴比 1 : 50で 40 ± 2°Cの温度で強条件で 5分間洗濯し、次いで排水し、水洗を 5分行う。洗濯後の 試験片を絞らずに取り出し、濾紙で軽く押さえて水を切り、水平状態で自然乾燥する
[0047] (£)乾燥した試験片の汚染性を JIS染色堅ロウ度用汚染判定用グレースケールで等 級判定し、「洗濯除去性」とする。
[0048] 2.砂付着性については以下に示す方法で評価した。
[0049] (1) 20 X 20cmのサンプルを採取し、完全に浸水した状態とする。
[0050] 完全に浸水した状態とは、洗濯機等を使用し、生地が水に沈むかあるいは水が生 地に浸透し、裏抜けする状態とする。
[0051] (2)撥水性試験器 (スプレー法)を用い、金属枠に完全浸水状態の生地を取り付ける
[0052] (3)通常の撥水性試験法 (スプレー法）に準じ、室温の水を生地に注ぐ。
[0053] (4)水がなくなった直後に乾燥した基準砂（トーョーマテラン (株)製、トーョー乾燥砂
6号)をまんべんなく生地に振りかける。
[0054] (5)金属枠を台から取り外し、その一端を持ち、垂直方向の状態で砂を軽く落とす。
[0055] (6)砂を落とした後の砂の残留状態を目視判定する。（砂付着の多 、物： 1級〜少な いもの 5級）
3.泥汚れ除去性につ!、ては以下に示す方法で評価した。
(1)汚染剤
赤玉土 Z黒土 Z水 = iZiZiの重量比で粉砕混合しで汚染剤を調合した。
(2)試験手順
(a)lOcmX 10cmの試験片を採取する。 [0056] (b)試験片を 10cm X 10cmのガラス板上に置き、汚染剤 20gをナイフコーターで塗 布し、 24時間放置，乾燥した後、汚染剤を手ではたき落とす。
[0057] (c)汚染後の試験片の汚染性を JIS染色堅ロウ度用汚染判定用グレースケールで汚 染の程度を等級判定し、「汚染性」とする。
[0058] (d)汚染後の試験片を、自動反転渦巻き電気洗濯機に、 JIS K 337に規定される 弱アルカリ性合成洗剤を 0. 1%の濃度になるように溶解した液 25Lで、浴比 1 : 50で 40 ± 2°Cの温度で強条件で 5分間洗濯し、次いで排水し、水洗を 5分行う。洗濯後の 試験片を絞らずに取り出し、濾紙で軽く押さえて水を切り、水平状態で自然乾燥する
[0059] (e)乾燥した試験片の汚染性を JIS染色堅ロウ度用汚染判定用グレースケールで等 級判定し、「洗濯除去性」とする。
<洗濯耐久性 >
上記の食品汚れの汚染性、洗濯除去性等は、以下に示す洗濯方法により 20回洗 濯後の繊維構造物の性能として測定されるものである。
[0060] 自動反転渦巻き電気洗濯機に、 JIS K 337に規定される弱アルカリ性合成洗剤を 0. 2%の濃度になるように溶解し、浴比 1 : 50で 40 ± 2°Cの温度で、強条件で 5分洗 濯し、次いで排水し、水洗を 5分する工程を 1回としてこれを 20回繰り返した後、風乾 した。
(実施例 1〜7、比較例 1〜6)
ポリエチレンテレフタレートからなる 84デシテックス、 72フィラメントの仮撚り加工糸を タテ糸、ョコ糸に使用して平織り物を製織した後、該織物を 95°Cの温度でオープンソ 一パー式連続精練機により精練し、次いで 60°Cの温度で湯洗、水洗し、次いで 130 °Cの温度で乾燥した後、液流染色で 130°Cの温度で薄い黄色に染色、湯水洗、 13 0°Cで乾燥し、 170°Cの温度でピンテンターセットして、タテ糸密度 Zョコ糸密度 138 Z90本 Z2. 54cmの織物を得た。該染色布に次に示す繊維表面被覆処理、有機フ ッ素含有化合物処理を施し得られた布帛の性能を評価した結果を表 1に示した。 <繊維表面被覆処理 >
(a)ペッカミン M— 3 (大日本インキ化学工業 (株)製 トリアジン環含有化合物 固形 分 80%)
(1)) ー200 ( (株)京絹化成製 フッ素系化合物 固形分 20%)
(c)NKガード SR— 108 (日華化学 (株)製 フッ素榭系脂 固形分 20%) 榭脂 (a)単独及び (a)に (b)または (c)を、表 1に示す割合で混合し、触媒として過 硫酸アンモ-ゥム 3gZLを溶解した水系液に染色布を浸漬し、水系液の付着量が 9 0重量％になるようにマンダルで絞り、 104°Cの飽和水蒸気雰囲気中で 5分の処理を 行った。
[0061] 次いで、 70°Cの温度で湯洗し、水洗し、 130°Cの温度で乾燥し、 160°Cの温度で ピンテンターセットした。
<有機フッ素含有化合物処理 >
(ィ) F— 470 ( (株)京絹化成製 フッ素系化合物 固形分 20%)
(口) F— 200 ( (株)京絹化成製 フッ素系化合物 固形分 20%)
(ハ) NKガード SR— 108 (日華化学 (株)製 フッ素榭系脂 固形分 20%) (二) AG— E061 (旭硝子 (株)製 フッ素系榭脂 固形分 20%)
上記化合物の少なくとも一種を表 1に示す割合で用いた水系液に、べッカミン M— 3 (大日本インキ (株)製 トリアジン環含有化合物 固形分 80%)を 2gZL、ペッカミ ンァクセレレータ ACX (大日本インキ化学工業 (株)製 触媒 固形分 35%) 0. 5gZ Lを溶解して処理液を調整し、染色布を浸漬して水系液の付着量が 90%〖こなるよう にマンダルで絞り、 130°Cの温度で乾燥し、 170°Cの温度でピンテンターセットした。
[0062] 表 1から、本発明によるものは、耐久性に優れた撥水性、撥油性、防汚性を兼ね備 えたものであることがわかる。
[0063] [表 1]
Figure imgf000016_0001
[0064] (実施例 8〜12、比較例 7〜： LO)
ポリエチレンテレフタレートからなる 44デシテックス、 36フィラメントと、オペロンテツ タス (株)製ポリウレタン弾性糸 44デシテックスを使用し、 32ゲージの 2枚箴シングルト リコット機にてフロント箴にポリエチレンテレフタレート糸、バック箴にポリウレタン糸を ポリエチレンテレフタレート糸 80重量0 /0、ポリウレタン糸 20重量％になるように供給し てハーフ組織に編成した。その後、該編地を 95°Cの温度でオープンソーパー式連 続精練機を用いて精練し、次いで 60°Cの温度で湯洗、水洗し、次いで 130°Cの温 度で乾燥した後、 190°Cでピンテンターセット後、液流染色で 130°Cの温度で薄べ一 ジュ色に染色、湯水洗、 130°Cで乾燥し、 160°Cの温度で再度ピンテンターセットし て、ゥエル密度 Xコース密度 62ケ Z2. 54cmX 10 /2. 54cm, 目付 220gZ m2の編地を得た。該染色布に次に示す繊維表面被覆処理、有機フッ素含有化合物 処理を施すことにより得られた編物の性能を評価した結果を表 2に示した。
[0065] <繊維表面被覆処理 >
(d)ペッカミン M— 3 (大日本インキ化学工業 (株)製 トリアジン環含有化合物 固 形分 80%)
( ー200 ( (株)京絹化成製 フッ素系化合物 固形分 20%)
(f)アサヒガード AG— 1100 (明成化学工業 (株)製 フッ素榭系脂 固形分 20%) 榭脂 (d)単独及び (d)に (e)または (f)を表 2に示す割合で混合し、触媒として過硫 酸アンモ-ゥムを 3gZLを溶解した水系液に染色布を浸漬し、水系液の付着量が 90 %になるようにマンダルで絞り、 104°Cの飽和水蒸気雰囲気中で 5分の処理を行った
[0066] 次いで、 70°Cの温度で湯洗し、水洗し、 130°Cの温度で乾燥し、 160°Cの温度で ピンテンターセットした。
<有機フッ素含有化合物処理 >
(ホ) F— 470 ( (株)京絹化成製 フッ素系化合物 固形分 20%)
(へ) AG— E061 (旭硝子 (株)製 フッ素系榭脂 固形分 20%)
上記化合物の少なくとも一種を表 2に示す割合で用いた水系液に、べッカミン M— 3
(大日本インキ化学工業 (株)製 トリアジン環含有化合物 固形分 80%)を 2gZL、 ペッカミンァクセレレータ ACX (大日本インキ化学工業 (株)製 触媒 固形分 35%) 0. 5gZLを溶解して処理液を調整し、 染色布を浸漬して水系液の付着量が 90% になるようにマンダルで絞り、 130°Cの温度で乾燥し、 170°Cの温度でピンテンター セットした。
[0067] 表 2から、本発明によるものは、耐久性に優れた撥水性、撥油性、防汚性を兼ね備 えたものであることがわかる。
[0068] [表 2]
2
Figure imgf000019_0001

Claims

請求の範囲
[1] 単繊維表面が、トリアジン環含有ィ匕合物含有榭脂被膜または有機フッ素化合物およ びトリアジン環含有化合物含有榭脂被膜を介して、有機フッ素系化合物含有榭脂被 膜で被覆された繊維を用いてなる繊維構造物であって、該繊維構造物の洗濯 20回 後の撥水性が 4級以上、撥油性が 4級以上であることを特徴とする繊維構造物。
[2] 該トリアジン環含有化合物含有榭脂被膜、または有機含フッ素化合物およびトリアジ ン環含有化合物含有榭脂被膜の膜厚が、 5〜： LOOnmである請求項 1記載の繊維構 造物。
[3] 該有機フッ素系化合物含有榭脂被膜がトリアジン環含有ィ匕合物または Zおよびイソ シァネート系化合物を含有している請求項 1または 2に記載の繊維構造物。
[4] 該繊維構造物の洗濯 20回後の食品汚れの汚染性が 3級以上で、洗濯除去性が 3級 以上であることを特徴とする請求項 1〜3のいずれかに記載の繊維構造物。
[5] 該繊維構造物の洗濯 20回後の墨汁汚れの汚染性が 3級以上、洗濯除去性力 級以 上であることを特徴とする請求項 1〜3のいずれかに記載の繊維構造物。
[6] 該繊維構造物の洗濯 20回後の砂付着防止性が 3級以上であることを特徴とする請 求項 1〜3のいずれかに記載の繊維構造物。
[7] 該繊維構造物の洗濯 20回後の泥汚れ除去性力 級以上であることを特徴とする請 求項 1〜3のいずれかに記載の繊維構造物。
[8] 請求項 6記載の繊維構造物を用いてなる水着。
[9] 布帛の少なくとも一部に、ポリウレタン系弾性糸および Zまたはポリトリメチレンテレフ タレート繊維を用いたことを特徴とする請求項 8記載の水着。
PCT/JP2007/050410 2006-01-18 2007-01-15 繊維構造物 WO2007083596A1 (ja)