WO2007024114A1 - Tole d'acier pour galvanisation a excellente usinabilite, et procede de fabrication - Google Patents

Tole d'acier pour galvanisation a excellente usinabilite, et procede de fabrication Download PDF

Info

Publication number
WO2007024114A1
WO2007024114A1 PCT/KR2006/003348 KR2006003348W WO2007024114A1 WO 2007024114 A1 WO2007024114 A1 WO 2007024114A1 KR 2006003348 W KR2006003348 W KR 2006003348W WO 2007024114 A1 WO2007024114 A1 WO 2007024114A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
steel sheet
steel
temperature
range
Prior art date
Application number
PCT/KR2006/003348
Other languages
English (en)
Other versions
WO2007024114A9 (fr
Inventor
Il-Ryoung Sohn
Kwang-Geun Chin
Hee-Jae Kang
Sung-Il Kim
Original Assignee
Posco
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Posco filed Critical Posco
Priority to US12/064,653 priority Critical patent/US20110073223A1/en
Priority to JP2008527851A priority patent/JP5388577B2/ja
Priority to EP06783735A priority patent/EP1929059A4/fr
Priority to CN2006800305520A priority patent/CN101243198B/zh
Publication of WO2007024114A1 publication Critical patent/WO2007024114A1/fr
Publication of WO2007024114A9 publication Critical patent/WO2007024114A9/fr

Abstract

Cette invention concerne une tôle d'acier ductile à haute résistance à étirage très profond utilisée principalement pour la fabrication de plaques intérieures et extérieures de carrosseries d'automobile, ainsi qu'un procédé de fabrication. La composition de cette tôle d'acier est, en pourcentage de poids, la suivante. C: 0,010 % ou moins; S: 0,1 % ou moins; Mn: 0,06 ~ 1,5 %, P: 0,15 % ou moins, S: 0,020 %ou moins, sol. Al: 0,10 ~ 0,40 %, N: 0,010 % ou moins, Ti: 0,003 ~ 0,010 %, Nb: 0,003 ~ 0,040 %, B: 0,0002 ~ 0,0020 %, Mo: 0.05 % ou moins, l'un ou les deux de Sb: 0,005 ~ 0,05 % et Sn: 0,005 ~ 0,05 %, la teneur totale en Sb et Sn se situant dans la plage de 0,005 ~ 0,1 % lorsque Sb et Sn sont ajoutés à la fois, le restant étant constitué par Fe et autres impuretés inévitables. La tôle d'acier comporte des agglomérats de surface d'un diamètre moyen de 1 D ou moins, pour une résistance à la traction de 28 - 50 Df/D.
PCT/KR2006/003348 2005-08-25 2006-08-24 Tole d'acier pour galvanisation a excellente usinabilite, et procede de fabrication WO2007024114A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
US12/064,653 US20110073223A1 (en) 2005-08-25 2006-08-24 Steel sheet for galvanizing with excellent workability, and method for manufacturing the same
JP2008527851A JP5388577B2 (ja) 2005-08-25 2006-08-24 加工性に優れた亜鉛メッキ用鋼板及びその製造方法
EP06783735A EP1929059A4 (fr) 2005-08-25 2006-08-24 Tole d'acier pour galvanisation a excellente usinabilite, et procede de fabrication
CN2006800305520A CN101243198B (zh) 2005-08-25 2006-08-24 用于电镀的具有优异的可加工性的钢板及其制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020050078433A KR100711356B1 (ko) 2005-08-25 2005-08-25 가공성이 우수한 아연도금용 강판 및 그 제조방법
KR10-2005-0078433 2005-08-25

Publications (2)

Publication Number Publication Date
WO2007024114A1 true WO2007024114A1 (fr) 2007-03-01
WO2007024114A9 WO2007024114A9 (fr) 2009-12-03

Family

ID=37771816

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2006/003348 WO2007024114A1 (fr) 2005-08-25 2006-08-24 Tole d'acier pour galvanisation a excellente usinabilite, et procede de fabrication

Country Status (6)

Country Link
US (1) US20110073223A1 (fr)
EP (1) EP1929059A4 (fr)
JP (1) JP5388577B2 (fr)
KR (1) KR100711356B1 (fr)
CN (1) CN101243198B (fr)
WO (1) WO2007024114A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1960562A1 (fr) * 2005-12-09 2008-08-27 Posco Tole d'acier laminee a froid de haute resistance possedant une excellente propriete de formabilite et de revetement, tole d'acier plaquee de metal a base de zinc fabriquee a partir de cette tole et procede de fabrication de celle-ci
EP2554687A4 (fr) * 2010-03-26 2017-02-15 JFE Steel Corporation Procédé de fabrication d'une tôle d'acier à haute résistance présentant de meilleures caractéristiques d'emboutissage profond

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100797238B1 (ko) * 2006-12-26 2008-01-23 주식회사 포스코 가공성이 우수한 심가공용 박강판의 제조방법
CN102791895B (zh) * 2009-12-04 2014-12-24 Posco公司 具有优异耐热性的加工用冷轧钢板及其制造方法
KR20120127095A (ko) * 2011-05-13 2012-11-21 주식회사 포스코 표면특성이 우수한 고강도 고인성 선재 및 그 제조방법
GB2529174A (en) 2014-08-12 2016-02-17 Ibm Batch compression management of messages
CN112654723B (zh) * 2018-11-02 2023-04-04 日本制铁株式会社 无取向电磁钢板

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02163346A (ja) * 1988-12-15 1990-06-22 Nisshin Steel Co Ltd プレス成形性に優れた溶融亜鉛めっき高張力冷延鋼板およびその製造方法
JPH06122939A (ja) * 1992-08-31 1994-05-06 Nippon Steel Corp 焼付硬化性と成形性とに優れた冷延鋼板あるいは溶融亜鉛メッキ冷延鋼板およびそれらの製造方法
JPH10280092A (ja) * 1997-04-10 1998-10-20 Nippon Steel Corp プレス成形性の時効劣化が小さい塗装焼付硬化性に優れた溶融亜鉛めっき鋼板とその製造方法
JP2001064750A (ja) 1999-08-27 2001-03-13 Nippon Steel Corp 曲げ性と深絞り性に優れた高強度冷延鋼板と高強度亜鉛めっき冷延鋼板およびその製造方法
JP2001288550A (ja) 2000-01-31 2001-10-19 Kobe Steel Ltd 溶融亜鉛めっき鋼板
JP2002146475A (ja) * 2000-11-02 2002-05-22 Kawasaki Steel Corp 合金化溶融亜鉛めっき鋼板
JP2002146477A (ja) 2000-11-14 2002-05-22 Nippon Steel Corp 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP2002155317A (ja) 2000-11-16 2002-05-31 Kawasaki Steel Corp 深絞り性および耐２次加工脆性に優れた高強度溶融亜鉛めっき鋼板の製造方法

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62250126A (ja) * 1986-04-23 1987-10-31 Kawasaki Steel Corp プレス成形性の優れた冷延鋼板の製造方法
JPS63243226A (ja) * 1987-03-31 1988-10-11 Kawasaki Steel Corp 耐２次加工脆性に優れた超深絞り用冷延鋼板の製造方法
US5041166A (en) * 1989-09-11 1991-08-20 Kawasaki Steel Corporation Cold-rolled steel sheet for deep drawing and method of producing the same
JPH0441658A (ja) * 1990-06-07 1992-02-12 Nippon Steel Corp 耐パウダリング性に優れた焼付硬化性高強度合金化溶融亜鉛めっき鋼板およびその製造方法
JPH0570838A (ja) * 1991-09-13 1993-03-23 Kawasaki Steel Corp 深絞り用熱延鋼板の製造方法
JP2800541B2 (ja) * 1992-02-21 1998-09-21 日本鋼管株式会社 深絞り用高強度溶融亜鉛メッキ鋼板の製造方法
JPH0657337A (ja) * 1992-08-10 1994-03-01 Nippon Steel Corp 成形性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法
KR960013481B1 (ko) * 1993-06-29 1996-10-05 니홍고오깡 가부시키가이샤 표면처리강판 및 그 제조방법
JP3229921B2 (ja) * 1994-11-21 2001-11-19 川崎製鉄株式会社 耐孔あき性に優れる深絞り用の鋼板および表面処理鋼板
TW415967B (en) * 1996-02-29 2000-12-21 Kawasaki Steel Co Steel, steel sheet having excellent workability and method of the same by electric furnace-vacuum degassing process
EP0903419A4 (fr) * 1996-12-24 2000-03-22 Kawasaki Steel Co Tole d'acier mince ayant une aptitude elevee a l'emboutissage en tube rectangulaire, et procede de fabrication associe
EP1160346B1 (fr) * 1999-02-22 2006-03-08 Nippon Steel Corporation Plaque d'acier galvanise a haute resistance, d'excellent comportement pour l'adhesion des placages de metal et la mise en forme sous presse, et plaque d'acier allie galvanise a haute resistance, et procede de production correspondant
US6398884B1 (en) * 1999-02-25 2002-06-04 Kawasaki Steel Corporation Methods of producing steel plate, hot-dip steel plate and alloyed hot-dip steel plate
JP4356132B2 (ja) * 1999-03-04 2009-11-04 Ｊｆｅスチール株式会社 缶用鋼板用熱延母板およびその製造方法
KR100419080B1 (ko) * 1999-09-28 2004-02-18 제이에프이 엔지니어링 가부시키가이샤 고장력 열연강판 및 그 제조방법
JP4258918B2 (ja) * 1999-11-01 2009-04-30 Ｊｆｅスチール株式会社 無方向性電磁鋼板の製造方法
JP3958921B2 (ja) * 2000-08-04 2007-08-15 新日本製鐵株式会社 塗装焼付硬化性能と耐常温時効性に優れた冷延鋼板及びその製造方法
JP4013505B2 (ja) * 2000-11-27 2007-11-28 住友金属工業株式会社 極低炭素薄鋼板とその製造方法
KR100478091B1 (ko) * 2002-05-24 2005-03-24 주식회사 포스코 용융아연도금강판의 제조방법
JP2004256895A (ja) * 2003-02-27 2004-09-16 Jfe Steel Kk 耐２次加工脆性に優れた高強度溶融亜鉛めっき鋼板の製造方法

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH02163346A (ja) * 1988-12-15 1990-06-22 Nisshin Steel Co Ltd プレス成形性に優れた溶融亜鉛めっき高張力冷延鋼板およびその製造方法
JPH06122939A (ja) * 1992-08-31 1994-05-06 Nippon Steel Corp 焼付硬化性と成形性とに優れた冷延鋼板あるいは溶融亜鉛メッキ冷延鋼板およびそれらの製造方法
JPH10280092A (ja) * 1997-04-10 1998-10-20 Nippon Steel Corp プレス成形性の時効劣化が小さい塗装焼付硬化性に優れた溶融亜鉛めっき鋼板とその製造方法
JP2001064750A (ja) 1999-08-27 2001-03-13 Nippon Steel Corp 曲げ性と深絞り性に優れた高強度冷延鋼板と高強度亜鉛めっき冷延鋼板およびその製造方法
JP2001288550A (ja) 2000-01-31 2001-10-19 Kobe Steel Ltd 溶融亜鉛めっき鋼板
JP2002146475A (ja) * 2000-11-02 2002-05-22 Kawasaki Steel Corp 合金化溶融亜鉛めっき鋼板
JP2002146477A (ja) 2000-11-14 2002-05-22 Nippon Steel Corp 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP2002155317A (ja) 2000-11-16 2002-05-31 Kawasaki Steel Corp 深絞り性および耐２次加工脆性に優れた高強度溶融亜鉛めっき鋼板の製造方法

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1960562A1 (fr) * 2005-12-09 2008-08-27 Posco Tole d'acier laminee a froid de haute resistance possedant une excellente propriete de formabilite et de revetement, tole d'acier plaquee de metal a base de zinc fabriquee a partir de cette tole et procede de fabrication de celle-ci
EP1960562A4 (fr) * 2005-12-09 2012-01-25 Posco Tole d'acier laminee a froid de haute resistance possedant une excellente propriete de formabilite et de revetement, tole d'acier plaquee de metal a base de zinc fabriquee a partir de cette tole et procede de fabrication de celle-ci
EP2554687A4 (fr) * 2010-03-26 2017-02-15 JFE Steel Corporation Procédé de fabrication d'une tôle d'acier à haute résistance présentant de meilleures caractéristiques d'emboutissage profond

Also Published As

Publication number Publication date
WO2007024114A9 (fr) 2009-12-03
CN101243198B (zh) 2010-12-29
JP5388577B2 (ja) 2014-01-15
EP1929059A4 (fr) 2012-06-13
EP1929059A1 (fr) 2008-06-11
US20110073223A1 (en) 2011-03-31
KR20070023995A (ko) 2007-03-02
KR100711356B1 (ko) 2007-04-27
JP2009506208A (ja) 2009-02-12
CN101243198A (zh) 2008-08-13

Similar Documents

Publication Publication Date Title
JP4464811B2 (ja) 延性に優れた高強度低比重鋼板の製造方法
EP2554699B1 (fr) Tôle d'acier présentant une résistance à la traction élevée et une meilleure ductilité et procédé de fabrication de cette dernière
KR101464844B1 (ko) 가공성 및 내충격 특성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
EP2753725B1 (fr) Acier à haute résistance, à faible densité, et procédé de fabrication dudit acier
JP4542515B2 (ja) 成形性と溶接性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板、並びに、高強度冷延鋼板の製造方法、高強度溶融亜鉛めっき鋼板の製造方法、高強度合金化溶融亜鉛めっき鋼板の製造方法
WO2011004779A1 (fr) Tôle d’acier à haute résistance et procédé de fabrication associé
KR20110018363A (ko) 초고강성강 강 제품 및 이의 제조방법
US9175374B2 (en) High strength hot-dip galvanized steel sheet having excellent deep drawability
KR101989726B1 (ko) 고강도 강판 및 그 제조 방법
JP2010502845A (ja) 機械的性質及び表面品質の優れた高強度亜鉛メッキ鋼板及びその製造方法
WO2017168957A1 (fr) Tôle d'acier mince, tôle d'acier plaquée, procédé de production de tôle d'acier laminée à chaud, procédé de production de tôle d'acier très dure laminée à froid, procédé de production de tôle d'acier mince, et procédé de production de tôle d'acier plaquée
US20110073223A1 (en) Steel sheet for galvanizing with excellent workability, and method for manufacturing the same
JP4924052B2 (ja) 高降伏比高張力冷延鋼板ならびにその製造方法
CN113348259A (zh) 高强度热浸镀锌钢板和其制造方法
WO2008078901A1 (fr) Procédé de production d'une tôle mince d'acier pour l'emboutissage profond présentant une excellente aptitude au façonnage
JP4710558B2 (ja) 加工性に優れた高張力鋼板およびその製造方法
WO2016157257A1 (fr) Tôle d'acier à haute résistance et procédé de production associé
CN110402297B (zh) 高强度热轧镀敷钢板
WO2007007983A1 (fr) Tôle d’acier pour emboutissage profond présentant une excellente résistance à la fragilisation par le réusinage et d’excellentes propriétés en matière de fatigue et de placage, et son procédé de fabrication
CN116507753A (zh) 延展性优异的超高强度钢板及其制造方法
JP5076480B2 (ja) 強度−延性バランスと深絞り性に優れた高強度鋼板およびその製造方法
KR101543836B1 (ko) 내충격 특성 및 성형성이 우수한 고강도 열연강판 및 그 제조방법
JP2022515107A (ja) 延性及び加工性に優れた高強度鋼板、及びその製造方法
KR102299558B1 (ko) 내식성이 우수한 핫스탬핑 부품 제조방법 및 이에 의해 제조된 핫스탬핑 부품
JPH021217B2 (fr)

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200680030552.0

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2008527851

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2340/DELNP/2008

Country of ref document: IN

WWE Wipo information: entry into national phase

Ref document number: 2006783735

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 12064653

Country of ref document: US