WO2006134141A2 - Verfahren zur herstellung von nanopartikulären lanthanoid/bor-verbindungen oder von nanopartikuläre lanthanoid/bor-verbindungen enthaltenden feststoffgemischen - Google Patents
Verfahren zur herstellung von nanopartikulären lanthanoid/bor-verbindungen oder von nanopartikuläre lanthanoid/bor-verbindungen enthaltenden feststoffgemischen Download PDFInfo
- Publication number
- WO2006134141A2 WO2006134141A2 PCT/EP2006/063235 EP2006063235W WO2006134141A2 WO 2006134141 A2 WO2006134141 A2 WO 2006134141A2 EP 2006063235 W EP2006063235 W EP 2006063235W WO 2006134141 A2 WO2006134141 A2 WO 2006134141A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- boron
- compounds
- lanthanoid
- nanoparticulate
- group
- Prior art date
Abstract
Description
Claims