WO2006106775A1 - インモールド成形用ラベル及びそれを用いた成形品 - Google Patents

インモールド成形用ラベル及びそれを用いた成形品 Download PDF

Info

Publication number
WO2006106775A1
WO2006106775A1 PCT/JP2006/306554 JP2006306554W WO2006106775A1 WO 2006106775 A1 WO2006106775 A1 WO 2006106775A1 JP 2006306554 W JP2006306554 W JP 2006306554W WO 2006106775 A1 WO2006106775 A1 WO 2006106775A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
label
heat seal
mold molding
mold
Prior art date
Application number
PCT/JP2006/306554
Other languages
English (en)
French (fr)
Inventor
Masaki Shiina
Kazuyuki Kimura
Takatoshi Nishizawa
Original Assignee
Yupo Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yupo Corporation filed Critical Yupo Corporation
Priority to CN2006800109192A priority Critical patent/CN101156192B/zh
Priority to EP06730502A priority patent/EP1865482A4/en
Priority to US11/909,878 priority patent/US8021727B2/en
Publication of WO2006106775A1 publication Critical patent/WO2006106775A1/ja

Abstract

　本発明は、成形品の素材を問わずラベルと成形品の密着が強固で、また広範囲の成形品成形条件に対応可能で、且つ印刷の仕上がり性に優れたインモールド成形用ラベルを提供する。本発明は、ヒートシール層と印刷層を含む樹脂フィルムを含有するインモールド成形用ラベルであって、該ヒートシール層の表面開口率が６～３０％、印刷層のドットスキップが５％以下、かつ印刷層のベック平滑度（ＪＩＳ－Ｐ－８１１９）が６５０～２００００秒であることを特徴とするインモールド成形用ラベル及びそれを用いた成形品に関する。

Description

明 細 書
インモールド成形用ラベル及びそれを用いた成形品
技術分野
[0001] 本発明は、印刷面の仕上がりが高精細であるインモールド成形に用いるラベルに 関する。また本発明は、該ラベルを貼着したラベル付き成形品に関する。
背景技術
[0002] 従来から、ラベルが貼着した榭脂成形体を一体成形によって製造する方法として、 インモールド成形法が知られている。この方法は、金型の内壁に予めラベルを装着し ておき、ポリエチレン榭脂ゃポリプロピレン榭脂などの成形用榭脂を溶融して該金型 内に直接供給し、射出成形、中空成形、差圧成形または発泡成形などで成形すると ともにラベルを貼着するものである（例えば、特許文献 1、特許文献 2参照)。この様な インモールド成形用ラベルとしては、グラビア印刷された榭脂フィルム、オフセット多 色印刷された合成紙 (例えば、特許文献 3、特許文献 4参照）、或いは、アルミニウム 箔の裏面に高圧法低密度ポリエチレン、エチレン '酢酸ビニル共重合体などをラミネ ートし、その箔の表面にグラビア印刷したアルミニウムラベルなどが知られている。
[0003] しかしながら、これらのインモールド成形用ラベルを用いてインモールド成形により 加飾されたラベル貼合成形品を製造する方法にぉ ヽては、ラベルのヒートシール層 榭脂として高圧法低密度ポリエチレンを用いたものは、成形品の素材が高密度ポリエ チレン成形品の場合はラベルと成形品の密着性が強固で良好であるが成形品の素 材がポリプロピレンやポリスチレン等の他素材である場合はラベルと成形品の密着性 が低ぐ輸送途中にラベルが成形品より剥がれてしまうといった欠点があった。ラベル と成形品の密着性を強固とするには、成形品と同素材の榭脂をラベルのヒートシール 層として用いたラベルを各々用意する必要があり、ラベルの在庫管理が複雑ィ匕すると いった問題や、成形品の成形温度が低いと成形品とラベルに十分な密着強度が得ら れず、それ故成形品の成形温度を高く設定する必要があり成形品の成形温度が極 端に限定され生産性が低下するといつた問題も指摘されている。
さらにラベルに印刷を施す際、例えばグラビア印刷で印刷層表面に網点印刷した 場合、印刷層の表面が粗過ぎるとインキ抜けが多く発生し印刷外観が著しく低下する といった問題があった。
[0004] 特許文献 1：特開昭 58— 069015号公報
特許文献 2：特開平 01— 125225号公報
特許文献 3：特公平 02 - 007814号公報
特許文献 4：特開平 02— 084319号公報
発明の開示
発明が解決しょうとする課題
[0005] 本発明は、成形品の素材を問わずラベルと成形品の密着が強固で、また広範囲の 成形品成形条件に対応可能で、且つ印刷の仕上がり性に優れたインモールド成形 用ラベルを提供することを目的とする。
課題を解決するための手段
[0006] 本発明者らは、上記問題に鑑みて鋭意研究を重ねた結果、ラベルのヒートシール 層が特定の表面開口率である多孔質表面で、且つ印刷層に網点印刷した際のドット スキップが特定率以下の平滑な表面とすることで、ヒートシール層には成形品榭脂が 成形時の圧力でヒートシール層の表面開口部に入り込む投錨効果が得られる為、成 形品の素材を問わずラベルと成形品との密着が強固であり、さらに広範囲の成形品 成形条件でラベルの貼合が可能であり、且つ印刷層の印刷仕上がり性が優れるとの 知見を得て本発明を完成するに至った。
即ち本発明は、以下の構成を有する。
(1)ヒートシール層と印刷層を含む榭脂フィルムを含有するインモールド成形用ラベ ルであって、該ヒートシール層の表面開口率が 6〜30%、印刷層のドットスキップが 5 %以下、かつ印刷層のベック平滑度 (JIS— P— 8119)が 650〜20000秒であること を特徴とするインモールド成形用ラベル。
(2)ヒートシール層の透気度 (JIS— P— 8117)が 20000秒以内であることを特徴とす る上記（1)に記載のインモールド成形用ラベル。
(3)ヒートシール層が、熱可塑性榭脂 (A)と、無機微細粉末 (B)及び有機フィラー (B ' )の少なくとも 1つとを含有することを特徴とする上記（1)または（2)に記載のインモ 一ルド成形用ラベル。
(4)熱可塑性榭脂 (A)が、結晶性ポリオレフイン系榭脂であることを特徴とする上記（ 3)に記載のインモールド成形用ラベル。
(5)ヒートシール層力 少なくとも 1軸方向に延伸され、かつ面積延伸倍率が 2〜80 倍である上記（1)〜 (4)の 、ずれかに記載のインモールド成形用ラベル。
(6)ヒートシール層が、無機微細粉末 (B)及び有機フィラー (B， )の少なくとも 1つを 5 0〜80%含有し、熱可塑性榭脂 (A)としてポリプロピレン系榭脂を含み、且つ延伸温 度が該ポリプロピレン系榭脂の融点より 1〜60°C低 、温度で延伸されて 、ることを特 徴とする上記（3)〜（5)の 、ずれかに記載のインモールド成形用ラベル。
(7)印刷層が、ポリプロピレン系榭脂及びポリエチレン系榭脂を含み、ポリプロピレン 系榭脂とポリエチレン系榭脂の配合重量比率力 対 6から 6対 4であることを特徴とす る上記（1)〜（6)の 、ずれかに記載のインモールド成形用ラベル。
(8)上記（1)〜（7)の 、ずれかに記載のインモールド成形用ラベルを含有する成形
P
PPo
(9)ダイレクトブロー成形、延伸ブロー成形若しくはインジェクション成形により成形さ れた上記（8)に記載の成形品。
(10)成形品が、ポリプロピレン系榭脂、ポリエチレン系榭脂、ポリスチレン榭脂、ポリ エチレンテレフタレート榭脂、ポリアミド系榭脂、 ABS榭脂、ポリ塩化ビュル榭脂の群 より選ばれた少なくとも 1種の熱可塑性榭脂を含むことを特徴とする上記 (8)または（ 9)に記載の成形品。
発明の効果
[0007] 本発明により、印刷面の仕上がり性に優れ、且つ印刷が高精細であるインモールド 成形が可能であり、成形品の素材を問わずラベルと成形品との密着が強固であり、さ らに広範囲の成形品成形条件でラベルの貼合が可能であり、かつ、インモールド成 形後の成形品の外観も良好であるインモールド成形用ラベル及びそれを用いた成形 品が得られた。
発明を実施するための最良の形態
[0008] 本発明のインモールド成形用ラベルについてさらに詳細に説明する。 'ヒートシ一ノレ層
[1]熱可塑性榭脂 (A)
本発明のヒートシール層に用いられる熱可塑性榭脂素材としては、ポリプロピレン 系榭脂、高密度ポリエチレン、中密度ポリエチレン、直鎖線状低密度ポリエチレンな どの結晶性ポリオレフイン系榭脂、エチレン '酢酸ビュル共重合体、エチレン'アタリ ル酸共重合体、エチレン 'アクリル酸アルキルエステル共重合体、エチレン 'メタクリル 酸アルキルエステル共重合体（アルキル基の炭素数は 1〜8)、エチレン 'メタクリル酸 共重合体の金属塩、ポリ 4ーメチルー 1 ペンテン、エチレン一環状ォレフイン共重 合体等の結晶性ポリオレフイン系榭脂、ポリエチレンテレフタレート榭脂、ポリ塩化ビ -ル榭脂、ナイロンー6、ナイロン—6, 6、ナイロン—6, 10、ナイロン—6, 12等のポ リアミド系榭脂、 ABS榭脂、アイオノマー榭脂等のフィルムを挙げることができるが、 好ましくはポリプロピレン系榭脂、高密度ポリエチレン、ポリエチレンテレフタレート榭 脂等の融点が 130〜280°Cの範囲の熱可塑性榭脂であり、これらの榭脂は 2種以上 混合して用いることもできる。
これらの中でも、耐薬品性や生産コスト等の観点より、結晶性ポリオレフイン系榭脂 を用いることが好ましぐポリプロピレン系榭脂、高密度ポリエチレンを用いることがより 好ましい。結晶性ポリオレフイン系榭脂は、結晶性を示すものであり、その結晶化度 は、通常 20%以上が好ましぐ 35〜75%がより好ましい。結晶性を示すものを用い れば、延伸により榭脂フィルム表面に空孔（開口）が十分に形成されるため好ましい。 該結晶化度は X線回折、赤外線スペクトル分析等の方法によって測定することができ る。
ポリプロピレン系榭脂としては、プロピレンを単独重合させたァイソタクティック重合 体またはシンジォタクティック重合体を用いることが好ましい。また、エチレン、 1—ブ テン、 1—へキセン、 1—ヘプテン、 4—メチル 1—ペンテン等の α ォレフィンとプ ロピレンとを共重合させた様々な立体規則性を有するプロピレンを主成分とする共重 合体を使用することもできる。共重合体は 2元系でも 3元系以上の多元系でもよぐま たランダム共重合体でもブロック共重合体でもよい。
本発明におけるヒートシール層中の熱可塑性榭脂 (Α)の含有量は、通常 20〜50 重量％、好ましくは 25〜50重量％、特に好ましくは 35〜50重量％である。熱可塑性 榭脂 (A)の含有量が、 50重量％を超えると、所望の表面開口率が得られずにインモ 一ルド成形で成形品とラベル密着改善が不十分になる傾向がある。逆に、熱可塑性 榭脂 (A)の含有量が 20重量％未満だと、延伸が困難になる傾向がある。
[0010] [2]無機微細粉末 (B)、有機フィラー (Β' )
本発明のヒートシール層に用いられる無機微細粉末及び/又は有機フィラーの種 類は特に限定されない。無機微細粉末としては、重質炭酸カルシウム、軽質炭酸力 ルシゥム、焼成クレー、タルク、硫酸バリウム、珪藻土、酸化マグネシウム、酸化亜鉛、 酸化チタン、酸ィ匕珪素などが挙げられ、またこれらは脂肪酸等で表面処理されてい ても良い。なかでも、重質炭酸カルシウム、焼成クレー、タルク力 安価で成形性が良 く好ましい。
[0011] 有機フィラー（Β，）としては、ポリエチレンテレフタレート、ポリブチレンテレフタレート 、ポリアミド、ポリカーボネート、ポリエチレンナフタレート、ポリスチレン、メラミン榭月旨、 ポリエチレンサルファイト、ポリイミド、ポリェチルエーテルケトン、ポリエーテルエーテ ルケトン、ポリフエ-レンサルファイト、ポリ一 4—メチル 1—ペンテン、ポリメチルメタ タリレート、環状ォレフィンの単独重合体や環状ォレフィンとエチレンとの共重合体等 で、融点が 120〜300°C、ないしはガラス転移温度が 120〜280°Cを有するものなど が挙げられる。上記の無機微細粉末及び Z又は有機フィラーの中から 1種を選択し てこれを単独で使用してもょ 、し、 2種以上を組み合わせて使用してもょ 、。
本発明のヒートシール層中の無機微細粉末 (B)及び Z又は有機フィラー（Β' )の含 有量は、通常 50〜80重量0 /0、好ましくは 50〜75重量0 /0、特に好ましくは 50〜65重 量％である。（Β)及び Ζ又は（Β' )の含有量が 80重量％を超えると、延伸が困難に なる傾向がある。逆に 50重量％未満だと、所望の表面開口率が得られずにインモー ルド成形で成形品とラベル密着改善が不十分になる傾向がある。
[0012] [3]分散剤 (C)
本発明のヒートシール層には、必要により分散剤を添加することが可能であり、例え ば、酸変性ポリオレフイン、シラノール変性ポリオレフインなどを例示することができる 。この中でも酸変性ポリオレフインを用いることが好ましい。酸変性ポリオレフインとし ては、無水マレイン酸をランダム共重合もしくはグラフト共重合した無水カルボン酸基 含有ポリオレフイン、あるいはメタクリル酸、アクリル酸などの不飽和カルボン酸をラン ダム共重合もしくはグラフト共重合したカルボン酸基含有ポリオレフイン、グリシジルメ タクリレートをランダム共重合もしくはグラフト共重合したエポキシ基含有ポリオレフィ ンなどが挙げられる。具体例としては、無水マレイン酸変性ポリプロピレン、無水マレ イン酸変性ポリエチレン、アクリル酸変性ポリプロピレン、エチレン 'メタクリル酸ランダ ム共重合体、エチレン.グリシジルメタクリレートランダム共重合体、エチレン'グリシジ ルメタクリレートグラフト共重合体、グリシジルメタタリレート変性ポリプロピレンなどが 挙げられ、なかでも好ましくは無水マレイン酸変性ポリプロピレンおよび無水マレイン 酸変性ポリエチレンである。
[0013] 無水マレイン酸変性ポリプロピレンおよび無水マレイン酸変性ポリエチレンの具体 例としては、三菱ィ匕学 (株）のモディック AP[P513V] (商品名）ゃモディック AP[M513] ( 商品名）、三洋化成工業 (株）の Yumexl001、 1010 (商品名）や Yumex2000 (商品名） 、三井 'デュポンポリケミカル (株）の HPR[VR101] (商品名）が挙げられる。
酸変性ポリオレフインの酸変性率は、 0. 01〜20%が好ましぐ 0. 05〜15%力より 好ましぐ 0. 1〜10%がさらに好ましい。 酸変性率が 0. 01%未満では、表面処理 した無機微細粉末の熱可塑性榭脂中への分散効果が不十分になる傾向があり、 20 %を超えると酸変性ポリオレフインの軟ィ匕点が低くなりすぎて熱可塑性榭脂との混合 が困難になる傾向がある。
[0014] ，印刷層
本発明の印刷層は、少なくとも熱可塑性榭脂を含む層であることが好ましい。印刷 層の素材としては、特に限定されず、ヒートシール層の項で前述した熱可塑性榭脂（ A)、無機微細粉末 (B)及び Z又は有機フィラー (Β' )、分散剤 (C)等を任意に配合 して所望の平滑な表面とすることが可能で、特に好ましい配合としては、熱可塑性榭 脂にはポリプロピレン系榭脂としてのプロピレン単独重合体またはプロピレン共重合 体、ポリエチレン系榭脂としての高密度ポリエチレンの両者を組み合わせた配合が好 ましく使用でさる。
プロピレン単独重合体またはプロピレン共重合体等のポリプロピレン系榭脂と高密 度ポリエチレン等のポリエチレン系榭脂の配合比率としては 4対 6から 6対 4が好ましく 、 5対 5が更に好ましい。プロピレン系榭脂の比率が多過ぎると印刷層の平滑度が高 過ぎて印刷物の耐擦過性が劣る傾向にあり、またポリエチレン系榭脂の配合比が多 過ぎると印刷層の平滑度が低過ぎてドッドスキップ不良が発生しやすい。
[0015] 本発明の印刷層は、網点柄を印刷した際のドットスキップ (網点の一部が印刷層に 転写しない現象）が 5%以下であり、 0〜3%であることが好ましい。また該印刷層の ベック平滑度 (JIS -P-8119)としては 650〜20000秒であり、 700〜5000秒であ ることが好ましい。ベック平滑度が 650秒未満であると、例えば、グラビア印刷で網点 柄を印刷した際のドットスキップ (網点の一部が印刷面に転移しな 、現状）が 5%を越 えて印刷外観が著しく低下する為実用上問題となる。また 20000秒を越えると印刷 物の耐擦過性が不足しインキが脱落する傾向にあり実用上問題となる。
また、本発明では、印刷層の表面に、鏡面または梨地等の加工が施されたロール で加熱圧着処理することで、印刷層を目的とする平滑度にすることもできる。
[0016] ，任意成分
本発明の榭脂フィルムでは、任意成分として目的とするヒートシール性や印刷性等 を阻害しな 、範囲で公知の他の榭脂用添加剤を任意に添加することができる。該添 加剤としては、脂肪酸アミドなどのスリップ剤、アンチブロッキング剤、染料、可塑剤、 離型剤、酸化防止剤、難燃剤、紫外線吸収剤等を挙げることができる。
•コア層、中間層
本発明の榭脂フィルムでは、印刷時の寸法安定性、ラベルの金型内への供給性、 熱収縮防止性などの面力もヒートシール層と印刷層の間にコア層または中間層を設 けても良ぐ例えば、印刷層 Zコア層 Zヒートシール層、印刷層 Zコア層 Z中間層 Z ヒートシール層、印刷層 Z中間層 Zコア層 Z中間層 Zヒートシール層といった構成を 例示することが出来る。
[0017] ·ラベル全厚み
本発明の榭脂フィルムであるラベル全厚みは、 30〜250 111カ 子ましく、さらに好 ましくは 35〜150 μ mである。 250 μ mを超えると剛度が高すぎてラベルを金型へ固 定することが困難となる傾向があり好ましくない。また、 25 m未満では剛度が低く過 ぎて枚葉でのオフセット印刷性が劣るといった欠点やインモールド成形時にシヮが発 生するといつた問題が発生する。
'樹脂フィルムの製造
本発明のインモールド成形用ラベルの榭脂フィルムは、当業者間で公知の種々の 方法を組み合わせることによって製造することができる。いかなる方法により製造され た榭脂フィルムであっても、本発明の構成要件を満たすものである限り本発明の範囲 内に包含される。
[0018] 本発明のインモールド成形用ラベルを構成する榭脂フィルムは少なくとも 1軸方向 に延伸されているものが好ましぐさらに 2軸方向に延伸されていてもよい。例えば、コ ァ層として無機微細粉末 (B)を 0〜40重量％、好ましくは 3〜33重量％含有する結 晶性ポリオレフイン系榭脂フィルムを該榭脂の融点より低 、温度で 1方向に延伸して 得られる 1軸方向に配向した榭脂フィルムに、ヒートシール層として熱可塑性榭脂 (A ) 20〜50重量％および無機微細粉末 (B)と有機フィラー（Β' )の合計量が 80〜50 重量％からなる榭脂組成物に、分散剤 (C)を前記熱可塑性榭脂 (Α)と無機微細粉 末 (Β)及び Ζ又は有機フィラー（Β' )の合計 100重量部に対して通常 0. 01〜100 重量部を含有する榭脂組成物の溶融フィルムをコア層の片面に積層し、さらに印刷 層として熱可塑性榭脂 (Α)力もなる結晶性ポリオレフイン系榭脂フィルムをヒートシ一 ル層とは反対側のコア層面に積層し、次 、で前記延伸方向と直角方向にこの積層フ イルムを延伸することにより、最外層は横 1軸方向に配向し、コア層が 2軸方向に配向 した積層構造物の榭脂フィルムが得られる。好ましい製造方法は各々の榭脂フィル ムを積層した後にまとめて延伸する工程を含むものである。別個に延伸して積層する 場合に比べると簡便であり製造コストも安くなる。
[0019] 延伸には、公知の種々の方法を使用することができる。
延伸の具体的な方法としては、ロール群の周速差を利用したロール間延伸、テンタ 一オーブンを利用したクリップ延伸などを挙げることができる。
ロール間延伸によれば、延伸倍率を任意に調整して、任意の剛性、不透明度、光 沢度のフィルムを得ることが容易であるので好まし 、。延伸倍率は特に限定されるも のではなぐ本発明の榭脂フィルムの使用目的と、用いる榭脂の特性を考慮して決定 する。通常は 2〜： L I倍であり、好ましくは 3〜10倍、更に好ましくは 4〜7倍である。 テンターオーブンを利用したクリップ延伸の場合は 4〜： L 1倍であり、好ましくは 5〜 1 0倍である。面積延伸倍率としては、 2〜80倍であり、好ましくは 3〜60倍、より好まし くは 4〜50倍である。面積倍率が 2倍未満では、榭脂フィルム表面に所定の表面開 口率が得られず、インモールド成形時に成形品とラベルで十分な密着が得られなく なる傾向がある。
[0020] 本発明のインモールド成形用ラベルのヒートシール層は、熱可塑性榭脂 (A)と無機 微細粉末 (B)及び Z又は有機フィラー (Β' )を所定の割合で混合し、押出し等の方 法により製膜する。その後、熱可塑性榭脂 (Α)としてのポリプロピレン系榭脂の融点 より 1〜60°C低い温度、より好ましくは 3〜55°C低い温度、で 1軸方向または 2軸方向 に延伸を行うことにより、無機微細粉末 (B)及び Z又は有機フィラー (Β' )を核として 榭脂フィルム内部には微細な空孔 (ボイド）を有し、フィルム表面には微細な亀裂 (表 面開口）を有した多孔質な表面が得られる。
またヒートシール層の延伸温度がポリプロピレン系榭脂の融点を越えると、所望の 表面開口率が得られず、成形品と接着が低下する為好ましくない。
このような方法により製造した本発明の榭脂フィルムにおけるヒートシール層は、以 下の手法により測定される最外層の表面開口率が 6〜30%、好ましくは 7%〜29% である。表面開口率が 6%未満ではインモールド成形時に成形品とラベルに十分な 投錨効果が得られず成形品とラベルの密着強度が低下し好ましくな!/、。また表面開 口率が 30%を越えてはラベルの表面強度が低すぎて容易に表面で材料破壊が起こ るため高い密着強度が得られず実用上問題となる。
ヒートシール層の面積延伸倍率としては、 2〜80倍であり、好ましくは 3〜60倍、より 好ましくは 4〜50倍である。面積延伸倍率が 2倍未満では、榭脂フィルム表面に所定 の表面開口率が得られず、インモールド成形時に成形品とラベルで十分な密着が得 られなくなる傾向がある。
[0021] 表面開口率は、本発明における榭脂フィルムの表面を電子顕微鏡で観察した領域 の空孔（開口）が占める面積割合を示す。
具体的には、榭脂フィルム試料より任意の一部を切り取り、観察試料台に貼り付け、 その観察面に金ないしは金—パラジウム等を蒸着して電子顕微鏡 (例えば、 日立製 作所 (株)製の走査型顕微鏡 S— 2400)を使用して観察しやす!/ヽ任意の倍率 (例え ば、 500倍〜 3000倍に拡大）にて表面の空孔を観察する。さらに観察した領域を写 真等に撮影し、空孔をトレーシングフィルムにトレースして塗りつぶした図を画像解析 装置 (二レコ (株)製：型式ルーゼッタス IID)で画像処理を行!、、空孔の面積率を榭脂 フィルム表面の開口率とする。
また、本発明のインモールド成形用ラベルのヒートシール層を構成する榭脂フィル ム層の透気度 (JIS— P— 8117)は 20000秒以内であることが好ましく、さらに好まし くは 15000秒以内である。透気度が 20000秒を越えると中空成形用のインモールド ラベルとした場合にエアー抜けによるプリスターの改善効果が期待できなくなる。
[0022] ，印刷
これらのインモールド成形用ラベルは、コロナ放電処理や、フレームプラズマ処理 等の表面加工を施すことにより、印刷を施す印刷層の表面の印刷性を改善しておく ことが好ましい。印刷は、グラビア印刷、オフセット印刷（油性、 UV)、フレキソ印刷、 レタープレス (UV)、スクリーン印刷、インクジェット印刷、電子写真印刷等を施して、 バーコード、製造元、販売会社名、キャラクター、商品名、使用方法などを記入する。 印刷されたラベルは打抜カ卩ェにより必要な形状寸法のラベルに分離される。このィ ンモールド成形用ラベルは、通常はカップ状成形品の側面を取巻くブランクとして、 中空成形では瓶状成形品の表側及び Z又は裏側に貼着されるラベルとして製造さ れる。
[0023] ，成形品
このインモールド成形用ラベルは、該ラベルを差圧成形金型の下雌金型の内面に ラベルの印刷面が接するように設置した後、吸引により金型内壁に固定させ、次いで 成形品成形材料用の榭脂シートの溶融物が下雌金型の上方に導かれ、常法により 差圧成形され、ラベルが成形品外壁に一体に融着されたラベル貼合成形品が成形 される。差圧成形は、真空成形、圧空成形のいずれも採用できるが、一般には両者 を併用し、かつプラグアシストを利用した差圧成形が好ましい。
また本発明のインモールド成形用ラベルは、溶融榭脂パリソンを圧空により金型内 壁に圧着するダイレクトブロー成形やプリフォームを用いた延伸ブロー成形に、又は 射出装置で金型内に溶融榭脂を注入し冷却固化するインジェクション成形に好適に 使用できる。中でも本発明のインモールド成形用ラベルラベルは、ダイレクトブロー成 形、インジェクション成形に好適である。このようにして製造されたラベルが貼着一体 化した成形品は、ラベルが金型内で固定された後に、ラベルと榭脂成形品が一体に 成形されるので、ラベルの変形もなぐ成形品とラベルの密着強度が強固であり、プリ スターもなぐラベルにより加飾された外観が良好な成形品が得られる。成形品として は、例えばボトノレ、容器などが挙げられる。
実施例
[0024] 以下に実施例、比較例および試験例を挙げて本発明の特徴をさらに具体的に説 明する。
以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣 旨を逸脱しない限り適宜変更することができる。したがって、本発明は以下に示す具 体例などにより何等限定されるものではな 、。以下の実施例および比較例で使用す る材料を表 1にまとめて示す。なお、表中の MFRはメルトフローレートを意味する。 ，物性の測定方法と評価方法
実施例及び比較例における物性の測定と評価は、以下に示す方法によって実施し た。
，物性の測定
(ィ)表面開口率:榭脂フィルムの表面を電子顕微鏡で観察した領域の空孔 (開口） が占める面積割合を示す。
[0025] 具体的には、榭脂フィルム試料より任意の一部を切り取り、観察試料台に貼り付け、 その観察面に金ないしは金 パラジウム等を蒸着して電子顕微鏡 (例えば日立製作 所 (株)製の走査型顕微鏡 S— 2400)を使用して観察しやす!/ヽ任意の倍率 (例えば 5 00倍〜 3000倍に拡大）にて表面の空孔を観察することができる。さらに観察した領 域を写真等に撮影し、空孔をトレーシングフィルムにトレースして塗りつぶした図を画 像解析装置 (二レコ (株)製：型式ルーゼッタス IID)で画像処理を行!、、空孔の面積 率を榭脂フィルム表面の開口率とした。 (口)透気度： JIS— P— 8117に準拠して測定した。
(ハ)ベック平滑度： JIS— P— 8119に準拠して測定した。
(二） MFR:JIS— K— 7210に準拠して測定した。
[0026] 以下の手順に従って本発明の榭脂フィルム（実施例 1〜7)および比較用の榭脂フ イルム (比較例 1〜4)を製造した。表 1に各榭脂フィルムの製造にあたって使用した 材料の種類を示し、表 2で各配合量 (重量％)と延伸条件および各層の厚みを示した
(実施例 1)
表 2に記載の配合物 [a]を 260°Cに設定された押出機で溶融混練して押出成形し 、冷却装置にて 70°Cまで冷却して単層の無延伸シートを得た。
この無延伸シートを表 2に記載の延伸温度（1)に加熱した後、縦方向にロール間で 5倍に延伸し、縦一軸延伸フィルムを得た。次いで配合物 [b]を 250°Cに設定された 押出機で溶融混練して、前記縦一軸延伸された榭脂フィルムの片面に積層した後、 更に配合物 [c]と配合物 [d]をそれぞれ別の押出機を用い 250°Cで溶融混練して前 記で積層した反対面に配合物 [d]が外側になるように積層して、配合物 [b] Z配合 物 [a] Z配合物 [c] Z配合物 [d] (印刷層 Zコア層 Z中間層 Zヒートシール層）の積 層物とした。さらに次いで前記積層物を表 2に記載の延伸温度（2)に加熱してテンタ 一延伸機を用 、て横方向に 8倍延伸し、 1軸 Z2軸 Z 1軸 Z 1軸に延伸された 4層の 榭脂フィルムを得た。
[0027] (実施例 2〜5及び比較例 1)
実施例 1において、配合物 [d]の配合を表 2記載のものに変更した以外は、実施例 1に記載と同様の方法で榭脂フィルムを得た。
(実施例 6〜8)
実施例 1において、配合物 [b]の配合を表 2記載のものに変更した以外は、実施例 1に記載と同様の方法で榭脂フィルムを得た。
(比較例 2)
実施例 4において、延伸温度（2)を表 2記載の温度に変更した以外は、実施例 4に 記載と同様の方法で榭脂フィルムを得た。 (比較例 3〜4)
実施例 1において、配合物 [b]の配合を表 2記載のものに変更した以外は、実施例 1に記載と同様の方法で榭脂フィルムを得た。
[0028] 印刷：上記で作成した榭脂フィルムを熊谷理機工業 (株)製グラビア印刷試験機を 使用して、インキは大日精ィ匕工業 (株)製 CSUP (商品名）を用い、網点率 10%柄の 版月同で A4サイズに断裁した基材を成形品とラベルが貼着される面とは反対の面に 印刷を行った。印刷適性としては以下項目を評価して実施した。
ドットスキップ:ルーペを使用して印刷層にインキが転写しな力つた網点 100個中ド ット個数を数えて以下の基準で評価した。
〇： 0〜3個：ドットスキップが目視できず、実用上問題な 、レベル △ :4〜5個：ドットスキップが肉眼で目立ち、実用上問題となるレベル X : 6個以上：ドットスキップが非常に目立ち、実用上問題があるレベル
[0029] 耐擦過適性：スガ試験機 (株)製の学震型摩擦試験機を使用し、印刷された表面同 士を 200gの荷重をかけて 1000回擦り、擦過後のインキ脱落状態を以下の基準で評 価し 7こ。
〇：インキが脱落せず良好なレベル
△：インキの脱落が見られ実用上問題あるレベル
X：インキ脱落が多く絵柄が見えず実用上使用ができないレベル 次いで該印刷が施された延伸榭脂フィルムを打ち抜きカ卩ェして、横 70mm、縦 90 mmのインモールド成形用ラベルを得た。
[0030] インモールド成形：
1) (株)新潟鐡ェ所製の射出成形機 (NV50STZ型締め 50トン、縦型配置式)を 使用し、製品の成形品のサイズが横 130mm、縦 150mm、肉厚 lmmの平板となる 射出成形用割型を用い、下部固定盤側に取り付けられた雌型の金型表面に印刷面 側が金型と接するようにラベルを固定し、次いで割型を型締めした後、 230°Cに設定 した射出装置よりポリプロピレン（日本ポリプロ (株)製、「ノバテック PP、 MA3、 MFR 11 [230°C、 2. 16kg荷重]」）を 745kgfZcm2の圧力でゲート部より型内に注入し 溶融榭脂を冷却固化させるとともにラベルを融着させた後、型開きをしてラベルが貼 着した平板状の PP製射出成形品を得た。
[0031] 2)成形品の素材を直鎖状低密度ポリエチレン（日本ポリエチレン (株)製、「ノバテツ ク LL、 UJ990、 MFR35 [190。C、 2. 16kg荷重]」）に変更し、射出装置の温度を 22 0°Cと 180°Cの 2条件で前記と同様に成形しラベルが貼着した PE製射出成形品を得 た。
3)さらに成形品の素材をポリスチレン（PSジャパン (株）製、「HIPS、 433、 MFR2 1 [200°C、 5kg荷重]」）に変え、射出装置の温度を 230°Cとし同様の方法でラベル が貼着した PS製射出成形品を得た。 4) (株)プラコ一製のダイレ外中空成形機（ V— 50型)を使用し、ぺんてる (株)製の自動ラベル供給装置を用いて、打ち抜きカロ ェしたインモールド成形用ラベル (横 62mm、縦 124mm)を、ブロー成形用割型 (容 量 400ml)の一方に真空を利用して印刷面側が金型と接するように固定した後、ぺッ ト（日本ュ-ペット (株)製、「RD383、融点 235°C、密度 1. 40gZcm3」）のノ リソンを 250°Cで溶融押出し、次いで割型を型締めした後、 4. 9kg/cm2の圧空をパリソン 内に供給し、ノ^ソンを膨張させて型に密着させて容器状とすると共にインモールド 用ラベルと融着させ、次いで該型を冷却した後、型開きをしてラベルが貼着したポリ エチレンテレフタレート（PET)製ダイレクト中空容器を取り出した。
[0032] ラベルと成形品の密着強度：
上記で作成した成形品に貼着したラベルを 15mm幅に切り取り、ラベルと成形品と の間の接着強度を、島津製作所製の引張試験機「オートグラフ、 AGS— D形」を用 い、 300mmZ分の引張速度で、 T字剥離することにより求めた。ラベル使用上の判 断基準は次の通りである。
〇： 400 (g/ 15mm)以上であり、接着が強固で実用上全く問題がな!、レベル △： 200以上〜 400未満 (gZl5mm)であり、やや接着性が弱く成形品の形状に よっては衝撃で剥がれてしまいやや実用上問題となるレベル
X : 200未満 (gZ 15mm)であり、容易にラベルが剥がれてしまうため実用上問題 であるレベル
各試験結果を表 3にまとめて示した。
[0033] [表 1] 【 表 1 】
Figure imgf000016_0001
表 2
〔¾
Figure imgf000017_0001
¾3004
Figure imgf000018_0001
[0036] 本発明を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲を 逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らか である。
本出願は、 2005年 3月 30日出願の日本特許出願 (特願 2005— 096646号）に基 づくものであり、その内容はここに参照として取り込まれる。
産業上の利用可能性
[0037] 本発明により、印刷面の仕上がりが高精細であるインモールド成形が可能となり、且 つインモールド成形後の成形品の外観も良好であるインモールド成形用ラベル及び それを用いた成形品が得られた。
本発明の該ラベルは、溶融した熱可塑性榭脂を射出成形して、あるいは溶融した 熱可塑性榭脂シートを真空成形もしくは圧空成形してラベル貼合成形品を製造する インモールド成形に用いるラベルであり、榭脂を成形する産業分野で好適に用いら れる。

Claims

請求の範囲
[1] ヒートシール層と印刷層を含む榭脂フィルムを含有するインモールド成形用ラベル であって、該ヒートシール層の表面開口率が 6〜30%、印刷層のドットスキップが 5% 以下、かつ印刷層のベック平滑度 (JIS— P— 8119)が 650〜20000秒であることを 特徴とするインモールド成形用ラベル。
[2] ヒートシール層の透気度 (JIS— P— 8117)が 20000秒以内であることを特徴とする 請求項 1に記載のインモールド成形用ラベル。
[3] ヒートシール層が、熱可塑性榭脂 (A)と、無機微細粉末 (B)及び有機フィラー (Β' ) の少なくとも 1つとを含有することを特徴とする請求項 1または 2に記載のインモールド 成形用ラベル。
[4] 熱可塑性榭脂 (Α)が、結晶性ポリオレフイン系榭脂であることを特徴とする請求項 3 に記載のインモールド成形用ラベル。
[5] ヒートシール層が、少なくとも 1軸方向に延伸され、かつ面積延伸倍率が 2〜80倍 である請求項 1〜4のいずれかに記載のインモールド成形用ラベル。
[6] ヒートシール層が、無機微細粉末 (Β)及び有機フィラー（Β' )の少なくとも 1つを 50 〜80%含有し、熱可塑性榭脂 (Α)としてポリプロピレン系榭脂を含み、且つ延伸温 度が該ポリプロピレン系榭脂の融点より 1〜60°C低 、温度で延伸されて 、ることを特 徴とする請求項 3〜5のいずれかに記載のインモールド成形用ラベル。
[7] 印刷層が、ポリプロピレン系榭脂及びポリエチレン系榭脂を含み、ポリプロピレン系 榭脂とポリエチレン系榭脂の配合重量比率力 対 6から 6対 4であることを特徴とする 請求項 1〜6のいずれかに記載のインモールド成形用ラベル。
[8] 請求項 1〜7の!ヽずれかに記載のインモールド成形用ラベルを含有する成形品。
[9] ダイレクトブロー成形、延伸ブロー成形若しくはインジェクション成形により成形され た請求項 8に記載の成形品。
[10] 成形品が、ポリプロピレン系榭脂、ポリエチレン系榭脂、ポリスチレン榭脂、ポリェチ レンテレフタレート榭脂、ポリアミド系榭脂、 ABS榭脂、ポリ塩ィ匕ビュル榭脂の群より 選ばれた少なくとも 1種の熱可塑性榭脂を含むことを特徴とする請求項 8または 9〖こ 記載の成形品。
PCT/JP2006/306554 2005-03-30 2006-03-29 インモールド成形用ラベル及びそれを用いた成形品 WO2006106775A1 (ja)