WO2006016672A1 - フラットバンドシフトの少ないシリカ質膜およびその製造法 - Google Patents

フラットバンドシフトの少ないシリカ質膜およびその製造法 Download PDF

Info

Publication number
WO2006016672A1
WO2006016672A1 PCT/JP2005/014819 JP2005014819W WO2006016672A1 WO 2006016672 A1 WO2006016672 A1 WO 2006016672A1 JP 2005014819 W JP2005014819 W JP 2005014819W WO 2006016672 A1 WO2006016672 A1 WO 2006016672A1
Authority
WO
WIPO (PCT)
Prior art keywords
aluminum
siliceous film
perhydropolysilazane
group
compound
Prior art date
Application number
PCT/JP2005/014819
Other languages
English (en)
French (fr)
Inventor
Yasuo Shimizu
Masaaki Ichiyama
Teruno Nagura
Original Assignee
Az Electronic Materials (Japan) K.K.
Az Electronic Materials Usa Corp.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Az Electronic Materials (Japan) K.K., Az Electronic Materials Usa Corp. filed Critical Az Electronic Materials (Japan) K.K.
Priority to EP05780260.5A priority Critical patent/EP1785459B1/en
Priority to US11/629,592 priority patent/US20070259106A1/en
Publication of WO2006016672A1 publication Critical patent/WO2006016672A1/ja

Abstract

　絶縁特性に優れたシリカ質膜の製造法とそれに用いられるコーティング組成物を提供する。 　本発明によるコーティング組成物は、数平均分子量が１００～５０，０００の、パーヒドロポリシラザンまたは変性パーヒドロポリシラザンと、ケイ素原子に対するアルミニウム原子のモル比で１０ｐｐｂ以上１００ｐｐｍ以下のアルミニウム化合物とを含んでなり、それを基板に塗布し、水蒸気、酸素、またはそれらの混合ガスを含む雰囲気中で焼成することによりシリカ質膜を製造する。

Description

明 細 書
フラットバンドシフトの少ないシリカ質膜およびその製造法
技術分野
[0001] 本発明は、シリカ質膜の製造法に関するものである。より詳しくは、フラットバンドシ フト値の小さい、絶縁特性に優れたシリカ質膜の製造法に関するものである。
背景技術
[0002] 一般に、半導体装置の様な電子デバイスにおいては、半導体素子、例えばトランジ スタ、抵抗、およびその他、が基板上に配置されている力 これらは電気的に絶縁さ れている必要がある。したがって、これら素子の間には、素子を分離するための領域 が必要であり、これをアイソレーション領域と呼ぶ。このようなアイソレーション領域を 形成させるための材料としてシリカ質膜が一般的に使用されている。
[0003] シリカ質膜を製造するための方法は、種々検討されている。これらのうち、ポリシラ ザン薄膜を焼成することによってシリカ質膜を製造する技術が検討されている (例え ば特許文献 1または 2)。
[0004] し力しながら、これらの方法で製造されたシリカ質膜は、原料のポリシラザンや溶剤 に起因すると考えられる窒素、炭素、水素の残存によって、 CVカーブのフラットバン ドシフトが高密度プラズマ CVD法により形成されたシリカ質膜に比べて高ぐ絶縁特 性に改良の余地があった。ここで、特に適用する基板の耐熱性、耐酸化性の制限に より加熱温度を低く抑える必要がある場合、窒素、炭素、または水素の残存が増加す る傾向にあった。
[0005] 一方、ポリシラザンィ匕合物に対してアルミニウム化合物を添加したり、ポリシラザン化 合物の構造中にアルミニウムを組み込む技術も知られて ヽる（特許文献 3および 4)。 しかし、これらはそれにより形成されるシリカ質膜のフラットバンドシフトについて検討 されていない。
特許文献 1：特許第 3511024号
特許文献 2：特許第 3178412号
特許文献 3：特開平 8— 5963号明細書 特許文献 4:特開平 11 105185号明細書
特許文献 5 :特開平 4 63833号明細書
特許文献 6 :特開平 9 31333号明細書
特許文献 7 :特開平 8— 176511号明細書
特許文献 8 :特開平 8— 176512号明細書
特許文献 9：特開平 5— 345826号明細書
発明の開示
発明が解決しょうとする課題
[0006] 本発明は、このような問題を解決し、フラットバンドシフト値を小さい、すなわち絶縁 特性などの電気特性に優れたシリカ質膜の製造法を提供するものである。
課題を解決するための手段
[0007] 本発明によるコーティング組成物は、数平均分子量が 100〜50, 000の、パーヒド 口ポリシラザンおよび変性パーヒドロポリシラザン力もなる群力 選択される 1つ以上の ポリシラザン化合物と、アルミニウム化合物と、溶媒とを含み、アルミニウム含有量が 前記ポリシラザン化合物に含まれるケィ素原子に対するアルミニウム原子のモル比で lOppb以上 lOOppm以下であること、を特徴とするものである。
[0008] また、本発明によるシリカ質膜の製造法は、数平均分子量が 100〜50, 000の、パ ーヒドロポリシラザンおよび変性パーヒドロポリシラザン力もなる群力も選択される 1つ 以上のポリシラザンィ匕合物と、アルミニウム化合物と、溶媒とを含み、アルミニウム含 有量が前記ポリシラザンィ匕合物に含まれるケィ素原子に対するアルミニウム原子のモ ル比で lOppb以上 lOOppm以下である塗布液を基板に塗布し、水蒸気、酸素、また はそれらの混合ガスを含む雰囲気中で焼成すること、を特徴とするものである。
[0009] また、本発明によるシリカ質膜は、ポリシラザンィ匕合物とアルミニウム化合物とを含ん でなる塗布液を基板に塗布し、酸化雰囲気下で焼成することによって得られたシリカ 質膜であって、アルミニウム含有量がケィ素原子に対するアルミニウム原子のモル比 で lOppb以上 lOOppm以下であること、を特徴とするものである。
発明の効果 [0010] 本発明によれば、フラットバンドシフト値の小さ 、シリカ質膜を製造することが可能と なり、これにより電気特性に優れた半導体素子、例えば絶縁特性に優れた素子分離 膜やゲート絶縁膜、を形成させることが可能となる。
発明を実施するための最良の形態
[0011] コーティング組成物
本発明によるコーティング組成物にぉ 、て、パーヒドロポリシラザンまたは変性パー ヒドロポリシラザン力もなる群力 選択される 1つ以上のポリシラザンィ匕合物は必要に 応じて任意のものを用いることができる。本発明において、パーヒドロポリシラザンは 以下の一般式 (I)で表されるものである。
H—（SiH -NH) H (I)
2 n
ここで nは重合度を表す数である。
[0012] 本発明によるコーティング組成物においては、前記一般式 (I)のパーヒドロポリシラ ザンをシラザンィ匕合物、アルコール、またはァミンにより変性させた変性パーヒドロポリ シラザンを用いることができる。本発明においては、コーティング組成物を用いて得ら れるシリカ質膜のフラットバンドシフトを低減させるために、パーヒドロポリシラザンを用 いることが好ましい。これは水素以外の有機基を主鎖に含むような、有機基を比較的 多く含むポリシラザンィ匕合物を用いた場合には、その有機基に由来する炭素等の原 子がシリカ質膜中に残存し、本発明の効果を低減させることがあるためである。
[0013] 一方、製造時における塗布液の塗布性、保存時の安定性等の観点から、パーヒド 口ポリシラザンの一部を変性させた変性パーヒドロポリシラザンを用いることが好まし い場合もある。このようにパーヒドロポリシラザンを変性させる化合物としては、へキサ メチルジシラザン、メチルアルコール、エチルアルコール、エチレンジァミンなどのィ匕 合物が挙げられる。これらを用いてパーヒドロポリシラザンの水素の一部、特に末端 水素を置換させることで変性パーヒドロポリシラザンが得られる。このような変性パーヒ ドロポリシラザンについては、特許文献 5〜9に記載されている。
[0014] 本発明によるコーティング組成物にぉ 、て用いられる前記のパーヒドロポリシラザン または変性パーヒドロポリシラザンの重量平均分子量は、コーティング組成物の塗布 性、特にスピンコーティング法により塗布をする際の塗布性の観点から 100〜50, 00 0、好まし <は 500〜20, 000、である。
[0015] 本発明によるコーティング組成物においては、これらのポリシラザンィ匕合物は溶媒 に溶解される。このとき用いられる溶媒は活性水素を有しな ヽ不活性有機溶媒を用 いることが好ましい。このような有機溶媒として、ベンセン、トルエン、キシレン、ェチル ベンゼン、ジェチルベンゼン、トリメチルベンゼン、トリェチルベンゼン等の芳香族炭 化水素系溶媒；シクロへキサン、シクロへキセン、デカヒドロナフタレン、ェチルシクロ へキサン、メチルシクロへキサン、 p—メンタン、ジペンテン（リモネン）、ピネン等の脂 環族炭化水素系溶媒; n ペンタン、 i ペンタン、 n—へキサン、 i一へキサン、 n— ヘプタン、 i—ヘプタン、 n オクタン、 i—オクタン、 n—ノナン、 iーノナン、 n—デカン 、 i デカン等の飽和炭化水素化合物、ジプロピルエーテル、ジブチェルエーテル等 のエーテル系溶媒;メチルイソブチルケトン等のケトン系溶媒；プロピレングリコールモ ノメチルエーテルアセテート等のエステル系溶媒等が挙げられる。これらのうち、後述 するアルミニウム化合物を十分溶解させることのできるものが特に好ましい。
[0016] 本発明において用いることのできるアルミニウム化合物は特に限定されないが、ポリ シラザン溶液中に溶存していることが好ましい。従って、コーティング組成物に用いら れる溶媒に応じて適宜選択することができる。
[0017] 本発明に用いることができるアルミニウム化合物は、例えば下記一般式で表すこと ができる。
AKZ1) (Z2) (Z3) (A)
ここで、 Τ、
Figure imgf000005_0001
および Ζ3はそれぞれ独立に、水素、水酸基、ハロゲン原子、アルキ ル基、シクロアルキル基、ァリール基、ァルケ-ル基、シクロアルケ-ル基、アルコキ シ基、ァセチルァセトネート基カも選ばれる基であり、
Figure imgf000005_0002
および Ζ3のうち 2つまた は 3つが環状構造を形成していてもよい。また、 Ζ\ Ζ2、および Ζ3がケィ素を含む有 機基であってもよい。
[0018] 本発明においてアルミニウム化合物はこれらのうち、下記一般式 (Α— 1)〜(Α— 3 )で表されるものが好ましい。
Al (OR1) (OR2) (OR3) (A- l)
AKR1) (R2) (R3) (A- 2) AKX1) (X2) (X3) (A— 3)
ここで 、 R2、および R3はそれぞれ独立に、水素、炭素数 1〜20のアルキル基、シ クロアルキル基、またはァリール基であり、 X1、 X2、および X3はそれぞれ独立に、フッ 素、塩素、またはヨウ素である。
[0019] より具体的には、本発明において用いられるアルミニウム化合物としては、トリメトキ シアルミニウム、トリエトキシアルミニウム、トリイソプロポキシアルミニウム、トリ n—プロ ポキシアルミニウム、トリメチルアルミニウム、トリェチルアルミニウム、トリイソプロピルァ ルミ-ゥム、トリ n—プロピルアルミニウム、フッ化アルミニウム、塩化アルミニウム、ヨウ 化アルミニウム、トリァセチルァセトナートアルミニウム、トリェチルァセトアセテートァ ルミ-ゥム、およびその他が挙げられる。また、ケィ素を含むアルミニウム化合物、例 えばジ一 s—ブトキシアルミノキシ一トリエトキシシランなどを用いることもできる。
[0020] これらのアルミニウム化合物の添力卩量は本発明の効果を損なわな 、範囲であれば 、特に限定されない。し力しながら、本発明の効果をより顕著に発現させるためには、 ポリシラザン化合物に含まれるケィ素原子に対するアルミニウム原子のモル比で ΙΟρ pb以上であることが好ましぐ lOOppb以上であることがより好ましい。また、耐電圧特 性を良好に保つという観点から、ポリシラザンィ匕合物に含まれるケィ素原子に対する アルミニウム原子のモル比で lOOppm以下であることが好ましく、 lOppm以下である ことがより好ましい。なお、このようなアルミニウム化合物の添加量は、特許文献 3また は 4に記載されているものよりも遙かに少ないものであり、そのようなごく少量のアルミ -ゥム化合物によって、得られるシリカ質膜の特性が劇的に改良されることは驚くべき ことであった。
[0021] 本発明によるコーティング組成物にぉ 、て、アルミニウム化合物は任意の方法でコ 一ティング組成物に添加することができる。具体的にはコーティング組成物に固体状 のアルミニウム化合物を添加して溶解させたり、アルミニウム化合物を溶媒に溶解さ せてカゝらコーティング組成物に混合することができる。アルミニウム化合物を溶媒に溶 解させる場合には、前記のポリシラザン化合物を溶解する際に使用することができる 溶媒を用いることができる。このとき、ポリシラザンィ匕合物の溶解に用いる溶媒と、アル ミニゥム化合物の溶液を調製する際に用いる溶媒とが異なって 、てもよ 、。アルミ- ゥム化合物を添加するときの温度や圧力には特に制限はないが、一般に 0〜200°C
、常圧〜 10kg/cm2Gにて添加する。
[0022] シリカ晳膜の製造法
本発明によるシリカ質膜の製造法は、前記したコーティング組成物を基板に塗布し
、焼成することによりシリカ質膜を形成させるものである。
[0023] 用いられる基板の表面材質は特に限定されないが、例えばベアシリコン、必要に応 じて熱酸ィ匕膜ゃ窒化珪素膜を成膜したシリコンウェハー、などが挙げられる。必要に 応じて、基板上にトレンチアイソレーション溝などの構造が形成されていてもよい。
[0024] 基板表面に対するコーティング組成物の塗布方法としては、従来公知の方法、例 えば、スピンコート法、ディップ法、スプレー法、転写法等が挙げられる。
[0025] 基板表面に形成された塗布膜を、必要に応じて過剰の有機溶媒を除去 (乾燥)した あと、水蒸気、酸素、またはその混合ガスを含む雰囲気中、すなわち酸化雰囲気中 で焼成する。ここで、本発明の効果を損なわない範囲で、雰囲気中に窒素やヘリウム などの不活性ガスが混在して ヽてもよ 、。
[0026] 本発明の方法においては、焼成条件はシリカ質膜中に残存する不純物元素、例え ば炭素、水素、窒素などをできるだけ少なくするために、比較的強い酸ィ匕条件で行う ことが好ましい。本発明においては、特に焼成を酸素を含む雰囲気下で焼成すること が好ましい。ここで、酸素の含有率は体積を基準として 1%以上であることが好ましく
、 10%以上であることがより好ましい。
[0027] また、本発明の方法において、水蒸気を含む雰囲気下で焼成を行う場合には、体 積を基準として 0. 1%以上であることが好ましぐ 1%以上であることがより好ましい。 本発明においては、特に酸素と水蒸気とを含む混合ガス雰囲気下で焼成を行うこと が好ましい。
[0028] 焼成温度は、ポリシラザンィ匕合物がシリカ質膜に添加し得る温度で行うことが必要 である。一般的には 100〜1, 200。C、好まし <は 300〜1, 000。C、で焼成を行う。こ こで、焼成温度が低いほど、従来の製造法に比べてフラットバンドシフト改良効果が 顕著となる傾向がある。また、焼成温度が高いほど、フラットバンドシフトが小さい、優 れた電気特性を有するシリカ質膜が得られる傾向がある。 [0029] 焼成時間は焼成温度に応じて適切に選択することができる力 一般に 5分〜 10時 間である。ここで、製造における生産効率の観点から 1時間以下であることが好ましい
[0030] 本発明による製造法によって製造されたシリカ質膜は、フラットバンドシフト値が小さ い。このような特性は、形成されたシリカ質膜中にアルミニウム化合物に由来する酸 化アルミニウムが均質に分散しているためと推察される。このため、本発明によるシリ 力質膜は電気特性、例えば絶縁特性に優れて ヽる。
[0031] シリカ 膜、およびシリカ 膜付^:某板
本発明によるシリカ質膜およびシリカ質膜付き基板は、例えば前記した方法により 製造することができる。通常、前記シリカ質膜の製造において、原料として用いられる アルミニウム化合物中のアルミニウム原子とポリシラザンィ匕合物中に含まれるケィ素 原子の比率は、最終的に得られるシリカ質膜においても変化しない。このため、製造 時に用いるアルミニウム化合物をケィ素原子に対するアルミニウム原子の比率を ΙΟρ pb以上 lOOppm以下としておくことで、本発明のシリカ質膜を製造することができる。 また、前記した方法において、例えばアルミニウム含有量の少ないシリカ質膜を形成 させ、そのシリカ質膜に別の手段、例えばイオン注入など、によってアルミニウム原子 を膜中に導入し、最終的なアルミニウム含有量を lOppb以上 lOOppm以下としてもよ い。
[0032] これらのシリカ質膜またはシリカ質膜付き基板は、電気特性に優れ、各種の半導体 素子、例えば素子分離膜、プリメタルディエレクトリック膜やインターメタルディエレクト リック膜などの層間絶縁膜、液晶等表示デバイスのゲート絶縁膜に有用なものである
[0033] 参考合成例 1 パーヒドロポリシラザンの合成
内容積 2リットルの四つ口フラスコにガス吹き込み管、メカ-カルスターラー、ジュヮ 一コンデンサーを装着した反応器を用意した。この反応器内部を乾燥窒素で置換し た後、四つ口フラスコに乾燥ピリジンを 1500ml導入し、これを氷冷した。次に、ピリジ ンにジクロロシラン lOOgを加えると、白色固体状のァダクト（SiH CI - 2C H N)が生
2 2 5 5 成した。この反応混合物をさらに氷冷し、撹拌しながらアンモニア 70gを反応混合物 中に吹き込んだ。引き続いて乾燥窒素を反応混合物中に 30分間吹き込み、余剰の アンモニアを除去した。
[0034] 得られた反応混合物をブフナーロートを用いて乾燥窒素雰囲気下で減圧濾過し、 濾液 1200mlを得た。この濾液カもエバポレーターによりピリジンを留去して 40gのパ ーヒドロポリシラザンを得た。
[0035] 得られたパーヒドロポリシラザンを CDC1を展開液としたゲル浸透クロマトグラフィー
3
により測定したところ、ポリスチレン換算の数平均分子量は 800であった。また、この パーヒドロポリシラザンの赤外線吸収スペクトルを測定したところ、波数 (cm—1) 3350 および 1180の N—H結合に基づく吸収、 2170の Si— H結合に基づく吸収、 1020 〜820の Si— N— Si結合に基づく吸収が観測された。
[0036] 比較例 1
参考合成例 1で調製したパーヒドロポリシラザン 20gをモレキュラーシーブで脱水し たジブチルエーテル 80gに溶解させ、これを濾過精度 0.： L mのアドバンテック社製 PTFEシリンジフィルターで濾過した。
[0037] 直径 8インチの p型シリコンウェハー上に lOnmの熱酸ィ匕膜を成膜した基板を準備し 、その上に前記のポリシラザン溶液をスピンコーターを用いてメインスピン lOOOrpm Z20秒の条件で塗布した。塗布後、基板をホットプレート上で 150°CZ3分間加熱し て乾燥させた。引き続きこの基板を加熱して、膜厚 500nmのシリカ質膜を形成させた 。加熱条件は以下の通りであった。
加熱条件 1： 水蒸気濃度 80体積％、酸素濃度 20体積％の雰囲気下、 400°Cで 1 5分間加熱。
加熱条件 2 : 水蒸気濃度 80体積％、酸素濃度 20体積％の雰囲気下、 800°Cで 1 5分間加熱。
加熱条件 3 : 水蒸気濃度 80体積％、酸素濃度 20体積％の雰囲気下、 400°Cで 1 5分間加熱した後、さらに乾燥窒素雰囲気下 800°Cで 30分間加熱。
加熱条件 4 : 窒素雰囲気下、 400°Cで 30分間加熱。
[0038] 得られたそれぞれの基板につ!、て、フラットバンドシフトの測定を行った。まず、そ れぞれの基板をエリプソメーター (J. A. Woolam社製 Model— M44)にて膜厚が 5 OOnmであることを確認し、さらに自動水銀プローブ CVZIV測定装置（日本エス ·ェ ス'ェム株式会社製 SSM495型）を用いて CVカーブおよびそれに基づくフラットバ ンドシフト値を測定した。 CV測定の印加電圧は— 100〜+ 100Vの範囲とした。
[0039] 比較例 2
高密度プラズマ CVD膜について、比較例 1と同様にしてフラットバンド値を測定し た。
[0040] 実施例 1
トリ（イソプロポキシ）アルミニウム lgを脱水したジブチルエーテル lOOgに混合してト リ（イソプロボキシ)アルミニウム溶液を得た。
[0041] 参考合成例 1で調整したパーヒドロポリシラザン 20gをモレキュラーシーブで脱水し たジブチルエーテル 80gに溶解させた。この溶液に前記のトリ（イソプロボキシ)アルミ
-ゥムを含むアルミニウム化合物溶液 27mgを添加し、混合溶液を濾過精度 0. 1 μ mのアドバンテック社製 PTFEシリンジフィルターで濾過した。
[0042] この混合溶液を用いて、比較例 1と同様にフラットバンド値を測定した。
[0043] 実飾 12
トリ（イソプロポキシ）アルミニウムをトリ（ァセチルァセトナート）アルミニウムに代え、 アルミニウム化合物溶液の添加量を 43mgに代えた他は、実施例 1と同様にフラット バンド値を測定した。
[0044] 実飾 13
トリ（イソプロポキシ）ァノレミ-ゥムを（ェチノレアセトアセテート）ジ (イソプロポキシ）ァ ルミ-ゥムに代え、アルミニウム化合物溶液の添力卩量を 34mgに代えた他は、実施例 1と同様にフラットバンド値を測定した。
[0045] 実施例 4
トリ（イソプロボキシ)アルミニウムをトリ（ェチルァセトアセテート）アルミニウムに代え 、アルミニウム化合物溶液の添加量を 56mgに代えた他は、実施例 1と同様にフラット バンド値を測定した。
[0046] 実施例 5
トリ（イソプロボキシ)アルミニウムを塩ィ匕アルミニウムに代え、アルミニウム化合物溶 液の添加量を 18mgに代えた他は、実施例 1と同様にフラットバンド値を測定した。
[0047] 実施例 6
トリ（イソプロポキシ）アルミニウムをジ一 s—ブトキシアルミノキシ一トリエトキシシラン に代え、アルミニウム化合物溶液の添加量を 47mgに代えた他は、実施例 1と同様に フラットバンド値を測定した。
[0048] 比較例 3
ジブチルエーテルに溶解させるトリ（イソプロポキシ）アルミニウムの量を 0. OOlgに 代えた他は、実施例 1と同様にフラットバンド値を測定した。
[0049] 比較例 4
ポリシラザン溶液に添加するトリ（イソプロボキシ）アルミニウム溶液の量を 2. 7gに代 えた他は、実施例 1と同様にフラットバンド値を測定した。
[0050] 実施例 7
メチルアルコール 10gを脱水したジブチルエーテル 90gに混合し、よく溶解させた。 この溶液を 10g採取し、比較例 1で調製したパーヒドロポリシラザン溶液 100gを撹拌 しながら徐々に添加した。この混合溶液を窒素雰囲気中 80°Cで 1時間加熱した後、 放冷した。この反応によりエチルアルコールで変性された変性パーヒドロポリシラザン 溶液を得た。
[0051] この変性パーヒドロポリシラザン溶液を用いてた他は実施例 1と同様にフラットバンド 値を測定した。
[0052] M ¾
比較例 1〜2および実施例 1〜6により得られた結果は下記の示すとおりであった。
[表 1] 加熱条件 4
AI含有量 * 加熱条件 1 加熱条件 2 加熱条件 3
(比較） 比較例 1 0 -18.5 —13.0 -22.0 -45.2 比較例 2 0 一 7.0〜- 15.0
実施例 1 3ppm -1 1.2 - 8.5 - 9.5 -38.2 実施例 2 3ppm -10.0 - 6.2 -1 1.0 -44.0 実施例 3 3ppm -9.3 -9.0 -10.1 -40.5 実施例 4 3ppm -1 1.0 -7.8 - 10.2 -46.2 実施例 5 «jppm -9.9 -7.2 -8.9 -39.5 実施例 6 3ppm -10.4 -8.8 -10.4 -50.2 比較例 3 3ppb -19.0 -13.4 —22.4
比較例 4 300ppm 測定不能 測定不能 測定不能
実施例 7 3ppm -1 1 .4 -6.2 一 8.0
単位： V
AI含有量はケィ素に対するアルミニウムの原子数比率
[0053] なお、実施例 1および 4にお 、て、各焼成条件で得たシリカ質膜のアルミニウム含 有量を二次イオン質量分析計（Physical Electronics社製 6650型）および触針式 表面形状測定器 (SLDAN社製 DEKTAK8000型）により測定したところ、塗布液と ほぼ一致するアルミニウム含有量が測定され、コーティング組成物のアルミニウム含 有量は、そのコーティング組成物を用いて製造されたシリカ質膜におけるアルミ-ゥ ム含有量と一致することがわ力つた。また、アルミニウム含有量はシリカ質膜の厚さ方 向で一定であり、シリカ質膜中にアルミニウム原子が均一に分布していることが分か つた o
産業上の利用可能性
[0054] 本発明による製造法は、フラットバンドシフト値が小さ 、シリカ質膜、すなわち絶縁 特性に優れたシリカ質膜を実現するものであり、この製造法により製造されたシリカ質 膜は、半導体素子、例えば素子分離膜、プリメタルディエレクトリック膜やインターメタ ルディエレクトリック膜などの層間絶縁膜、液晶等表示デバイスのゲート絶縁膜などに 利用可能なものである。

Claims

請求の範囲
[1] 数平均分子量が 100〜50, 000の、パーヒドロポリシラザンおよび変性パーヒドロポ リシラザン力 なる群力 選択される 1つ以上のポリシラザン化合物と、アルミニウム化 合物と、溶媒とを含み、アルミニウム含有量が前記ポリシラザンィ匕合物に含まれるケィ 素原子に対するアルミニウム原子のモル比で lOppb以上 lOOppm以下であることを 特徴とするコ一ティング組成物。
[2] 変性パーヒドロポリシラザン力 パーヒドロポリシラザンをシラザン化合物、アルコー ルまたはァミンにより変性させたものである、請求項 1に記載のコーティング組成物。
[3] 前記アルミニウム化合物力 下記一般式 (A)で表されるものである、請求項 1または 2に記載のコ一ティング組成物。
AKZ1) (Z2) (Z3) (A)
(ここで、
Figure imgf000013_0001
および Z3はそれぞれ独立に、水素、水酸基、ハロゲン原子、アルキ ル基、シクロアルキル基、ァリール基、ァルケ-ル基、シクロアルケ-ル基、アルコキ シ基、ァセチルァセトネート基カも選ばれる基であり、
Figure imgf000013_0002
および Z3のうち 2つまた は 3つが環状構造を形成していてもよぐ
Figure imgf000013_0003
および Z3がケィ素を含む有機基で あってもよい。 )
[4] 前記塗布液のアルミニウム含有量が前記ポリシラザンィ匕合物に含まれるケィ素原子 に対するアルミニウム原子のモル比で lOOppb以上 lOppm以下である、請求項 1〜 3のいずれか 1項に記載のコーティング組成物。
[5] 数平均分子量が 100〜50, 000の、パーヒドロポリシラザンおよび変性パーヒドロポ リシラザン力 なる群力 選択される 1つ以上のポリシラザン化合物と、アルミニウム化 合物と、溶媒とを含み、アルミニウム含有量が前記ポリシラザンィ匕合物に含まれるケィ 素原子に対するアルミニウム原子のモル比で lOppb以上 lOOppm以下である塗布 液を基板に塗布し、水蒸気、酸素、またはそれらの混合ガスを含む雰囲気中で焼成 することを特徴とするシリカ質膜の製造法。
[6] 酸素、または酸素と水蒸気の混合ガスを含む雰囲気下で焼成を行う、請求項 5に記 載のシリカ質膜の製造法。
[7] 請求項 5または 6に記載の方法により製造されたシリカ質膜。
[8] ポリシラザンィ匕合物とアルミニウム化合物とを含んでなる塗布液を基板に塗布し、酸 化雰囲気下で焼成することによって得られたシリカ質膜であって、アルミニウム含有 量がケィ素原子に対するアルミニウム原子のモル比で lOppb以上 lOOppm以下であ ることを特徴とするシリカ質膜。
[9] 請求項 5または 6に記載の方法により製造されたシリカ質膜を基板表面の少なくとも 一方に具備してなる、シリカ質膜付き基板。
[10] 前記シリカ質膜が、素子分離膜、層間絶縁膜またはゲート絶縁膜である、請求項 9 に記載のシリカ質膜付き基板。
PCT/JP2005/014819 2004-08-13 2005-08-12 フラットバンドシフトの少ないシリカ質膜およびその製造法 WO2006016672A1 (ja)