WO2006009135A1 - 脂肪族ポリエステル系樹脂反射フィルム及び反射板 - Google Patents
脂肪族ポリエステル系樹脂反射フィルム及び反射板 Download PDFInfo
- Publication number
- WO2006009135A1 WO2006009135A1 PCT/JP2005/013235 JP2005013235W WO2006009135A1 WO 2006009135 A1 WO2006009135 A1 WO 2006009135A1 JP 2005013235 W JP2005013235 W JP 2005013235W WO 2006009135 A1 WO2006009135 A1 WO 2006009135A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aliphatic polyester
- film
- reflective film
- titanium oxide
- mass
- Prior art date
Abstract
Description
Claims