WO2004110695A1 - オーステナイト系鋼溶接継手 - Google Patents
オーステナイト系鋼溶接継手 Download PDFInfo
- Publication number
- WO2004110695A1 WO2004110695A1 PCT/JP2004/008279 JP2004008279W WO2004110695A1 WO 2004110695 A1 WO2004110695 A1 WO 2004110695A1 JP 2004008279 W JP2004008279 W JP 2004008279W WO 2004110695 A1 WO2004110695 A1 WO 2004110695A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- less
- austenitic steel
- weld metal
- toughness
- welded joint
- Prior art date
Abstract
Description
Claims