Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J163/00—Adhesives based on epoxy resins; Adhesives based on derivatives of epoxy resins
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
  • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
  • C08G59/40—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the curing agents used
  • C08G59/50—Amines
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/16—Nitrogen-containing compounds
  • C08K5/17—Amines; Quaternary ammonium compounds
  • C08K5/18—Amines; Quaternary ammonium compounds with aromatically bound amino groups

Definitions

• This invention relates to high temperature resistant epoxy-based adhesive films.
• Polyepoxide resins are monomers or prepolymers that react with curing agents to yield high performance resins. These resins have gained wide acceptance in structural adhesives because of their combination of characteristics such as thermal and chemical resistance, adhesion, and abrasion resistance.
• Cured epoxy resins are frequently required to have high glass transition temperatures in order to provide adhesives having structural properties at high temperatures.
• methods of achieving high glass transition temperatures in such polyepoxide resins include: preparing resins having a high crosslink density and a high concentration of polar groups as disclosed in U.S. Pat. No. 4,331,582; using epoxy resins compositions in which the epoxy-group containing compound contains a polycyclic structure, such as in U.S. Pat. Nos.
• compositions having a high glass transition temperature typically are highly crosslinked, and are brittle or have a low ductility.
• One method of improving the ductility of such cured resins is by adding a rubber component or toughening agent to the composition.
• compositions containing cured epoxy resins having a high glass transition temperature are incompatible with such toughening agents.
• the invention provides an adhesive composition comprising a mixture of polyepoxide resins comprising cycloaliphatic-containing polyepoxide resin and aromatic polyepoxide resin and an effective amount of 9,9-bis(3-methyl-4- aminophenyl)fluorene.
• the mixture of polyepoxide resins has a cycloaliphatic character of greater than 10 weight percent, as defined below.
• the cycloaliphatic-containing polyepoxide resin is present in the adhesive composition in an amount of at least 20 to 80 weight percent, based on the total weight of the polyepoxide resins.
• the aromatic polyepoxide resin is present in the adhesive composition in an amount of from 80 to 20 weight percent, based on the total weight of the polyepoxide resins.
• the adhesive composition further comprises a toughening agent.
• the adhesive compositions of the invention are useful for providing adhesives that rapidly cure to provide adhesive bonds having both high peel strength and high overlap shear strength at room temperature and at 120 °C to 150 °C or higher.
• the adhesive compositions of the invention contain at least one cycloaliphatic- containing polyepoxide resin.
• the cycloaliphatic-containing polyepoxide resins have epoxide moieties attached to, that is, pendent from, only aromatic groups and have cycloaliphatic groups between the aromatic groups.
• a general formula for such compounds is R(X n )-Rl-(R(Xp)-Rl) r -R(X n ), where each R is independently at least a divalent aromatic group, each X is an epoxide-containing moiety, each R is independently at least a divalent cycloaliphatic group, and p and r are > 0 and n is at least 1.
• cycloaliphatic groups include the divalent radicals of dicyclopentadiene, cyclopentadiene, norabornane, decalin, and hydrogenated analogs of naphthalene, anthracene, and biphenyl compounds, and combinations thereof.
• aromatic groups include mono- and divalent radicals of benzene, naphthalene, bisphenol-A, bisphenol-F, and biphenyl-type compounds, and combinations thereof. The aromatic groups may be substituted, for example, with alkyl groups on the aromatic rings.
• adhesives and adhesive compositions of the invention contain one or more dicyclopentadiene-containing polyepoxide resins.
• Such resins are generally prepared from the reaction of dicyclopentadiene phenol resin and epichlorohydrin under basic conditions. The detailed preparation procedure can be found in publicly available literature. Examples of useful dicyclopentadiene-containing polyepoxide resins have the formula:
• n is an integer from 0 to 7 and may be any integer or fraction in between 0 and 7.
• Epoxide equivalent weights range from 150 to 500.
• Commercially available dicyclopentadiene-based epoxy resins include HP-7200 from Dainippon Ink and
• Cycloaliphatic-containing polyepoxide resin is present in the compositions of the invention in an amount of from 20 to 80 weight percent of the total weight of the polyepoxide resins present in the adhesive composition, and may be present in any whole or fractional amount between 20 and 80 weight percent. In other embodiments, the cycloaliphatic-containing polyepoxide resin is present in the compositions of the invention in an amount of from 25 to 75 weight percent of the total weight of the polyepoxide resins present, and any whole or fractional amount between 25 and 75 weight percent.
• Suitable aromatic polyepoxide resins include those containing at least two 1,2- cyclic ethers. Such compounds can be aromatic or heteroaromatic, or can comprise combinations thereof.
• Suitable polyepoxide resins may be solid or liquid at room temperature.
• Aromatic polyepoxide resin is used in the adhesives and compositions of the invention to increase the Tg of the cured adhesive film and to provide heat resistance.
• Aromatic polyepoxide resins do not include polyepoxide resins having both aromatic and cycloaliphatic groups.
• polyepoxides Compounds containing at least two epoxide groups (that is, polyepoxides) are preferred.
• a combination of polyepoxide compounds may be employed, and an epoxide resin having a functionality of less than two may be used in a combination so long as the overall epoxide functionality of the mixture is at least two.
• the polymeric epoxides include linear polymers having terminal epoxide groups (for example, the diglycidyl ether of bisphenol-A) and polymers having pendent epoxy groups (for example, polyglycidyl ethers of phenolic novolak compounds). It is also within the scope of this invention to use a material with functionality in addition to epoxide functionality but which is essentially unreactive with the epoxide functionality, for example, a material containing both epoxide and acrylic functionality.
• Aromatic polyepoxides that is, compounds containing at least one aromatic ring structure, for example, a benzene ring, and at least two epoxide groups
• aromatic polyglycidyl ethers of polyhydric phenols such as Bisphenol-A or Bisphenol-F type resins and their derivatives
• aromatic polyglycidyl amines for example, polyglycidyl amines of benzenamines, benzene diamines, naphthylenamines, or naphthylene diamines
• polyglycidyl ethers of phenol formaldehyde resole or novolak resins resorcinol diglycidyl ether
• polyglycidyl derivatives of fluorene-type resins and glycidyl esters of aromatic carboxylic acids, for example, phthalic acid diglycidyl ester, isophthalic acid diglycidyl ester, trimellitic
• Preferred aromatic polyepoxides are the polyglycidyl ethers of polyhydric phenols, such as the series of diglycidyl ethers of Bisphenol-A, commercially available from Resolution Performance Products, Houston, TX, for example, under the trade designations "EPON 828" and "EPON 1001F” and the series of diglycidyl ethers of Bisphenol-A and Bisphenol F and their blends, commercially available from Resolution Performance
• aromatic epoxides include the "DER” series of Bisphenol epoxides and "DEN” series of epoxy novolak resins, available from Dow Chemical, Midland, MI; diglycidyl ether of fluorene Bisphenol, available from Resolution Performance Products, Houston, TX, under the trade designation "EPON HPT Resin 1079”; a triglycidyl derivative of p-aminophenol, commercially available from Ciba Performance Polymers, Brewster, NY, under the trade designation “MY 0500”; a tetraglycidyl derivative of methylene dianiline, commercially available from Ciba Performance Polymers, Brewster, NY, under the trade designation “MY 720"; and a polyfunctional aromatic epoxide resin commercially available from Resolution Performance Products under the trade designation "EPON SU-8.” Flame retardant
• Aromatic polyepoxide resin is present in the compositions of the invention in an amount of from 80 to 20 weight percent of the total weight of the polyepoxide resins present in the adhesive composition, and may be present in any whole or fractional amount between 80 and 20 weight percent. In other embodiments, the aromatic polyepoxide resin is present in the compositions of the invention in an amount of from 75 to 25 weight percent of the total weight of the polyepoxide resins present, and any whole or fractional amount between 75 and 25 weight percent.
• the combination of cycloaliphatic-containing polyepoxide and aromatic polyepoxide resins have a cycloaliphatic character of greater than 10 weight percent. In one embodiment, the cycloaliphatic character is at least 12 weight percent. In another embodiment, the cycloaliphatic character is at least 13.5 weight percent. In another embodiment, the combined polyepoxide resins have a cycloaliphatic character of not more than about 60 weight percent. In another embodiment, the combined polyepoxide resins have a cycloaliphatic character of not more than about 55 weight percent. In another embodiment, the combined polyepoxide resins have a cycloaliphatic character of not more than about 40 weight percent.
• the combined polyepoxide resins have a cycloaliphatic character of from greater than 10 weight percent to about 60 weight percent; at least 12 weight percent to about 55 weight percent; and from 13.5 weight percent to 40.5 weight percent, and may be any whole or fractional weight percent in between 12 and 60 weight percent.
• Weight percent cycloaliphatic character is determined by calculating the weight percent cycloaliphatic groups of the cycloaliphatic-containing polyepoxide, excluding the epoxide-containing moieties attached to the aromatic groups. The value, expressed as a percentage, is then multiplied by the weight percent of cycloaliphatic-containing polyepoxide present in the total amount of polyepoxide resin present in the adhesive composition.
• o-TBAF 9,9-bis(3- methyl-4-aminophenyl)fluorene
• the curative is used in the adhesive films and compositions of the invention in a stoichiometric ratio of 0.8 to 1.7 amino hydrogen (NH) equivalents per epoxide equivalent. In one embodiment, a stoichiometric ratio of 1.0 to 1.65 amino hydrogen equivalents per epoxide equivalent is employed. In another embodiment, a stoichiometric ratio of 1.25 to 1.65 amino hydrogen equivalents per epoxide equivalent is used.
• the adhesives and adhesive compositions of the invention may contain one or more tougheners or toughening agents.
• the toughening agent can be introduced as a latex of dispersed or synthetic rubber as is disclosed in U.S. Pat. No. 3,316,195 or a graded rubber or core shell rubber particle as disclosed in U.S. Pat. Nos. 3,833,683; 3,856,883; and 3,864,426.
• the toughening agent can also be introduced into the epoxy resin composition by dissolving reactive elastomers into the epoxy resin which phase-separate during curing. The technique is exemplified by U.S. Pat. Nos. 4,107,116 and 3,894,112.
• toughening agents in epoxy resin is to be found in the Advances in Chemistry Series 208 titled "Rubbery-Modified Thermoset Resins" edited by C. K. Riew and J. K. Gillham, American Chemical Society, Washington, 1984.
• One specific toughening agent is the insoluble in situ polymerized elastomeric particles that are formed from amine terminated polyethers, for example, diprimary amine endcapped poly(tetramethyleneoxides).
• Other examples include amine-terminated butadiene/nitrile rubbers, carboxyl-terminated butadiene/nitrile rubbers, and core shell materials.
• the adhesive compositions of the invention may contain from 3 to 20 weight percent of the total weight of the composition of toughening agent. In other embodiments, the adhesive compositions of the invention may contain from 3 to 10 weight percent toughening agent based on the total weight of the composition.
• Various other adjuvants can also be added the compositions of the invention to alter the characteristics of the cured adhesive. Useful adjutants include fumed silica, pigments, silica, alumina, magnesium sulfate, calcium sulfate, bentonite, glass beads, glass bubbles, and organic and inorganic fibers. Amounts of up to 80 weight percent of the total weight of the composition adjuvant can be used.
• the adhesive compositions of the invention are generally useful for bonding substrate where both high peel strength and high shear strength at high temperatures are desired.
• the shear strength of the adhesive films of the present invention was determined by bonding two aluminum substrates together using the adhesive film and measuring the shear strength of the resulting construction. More specifically, overlap shear strength was determined according to ASTM D-1002 with the following modifications.
• the adherends were 2024-T3 bare aluminum panels measuring 7 inches long x 4 inches wide x 0.063 inches thick (178 mm x 102 mm x 1.60 mm).
• the panels were prepared in the following manner. The panels were first degreased by immersing in alkaline degreaser ("Oakite Aluminum Cleaner 164", Oakite Products Inc., Berkeley Heights, NJ) at about 88 °C for about 10 minutes, followed by rinsing with tap water. The degreased panels were then oxidized by immersing them in a
• the panels were further treated as follows.
• the etched panels were anodized by immersion in phosphoric acid at 22 °C with an applied voltage of 15 Volts for
• anodized aluminum panels were immediately primed within 24 hours of treatment.
• the anodized panels were primed with a corrosion inhibiting primer for aluminum (3MTM Scotch-WeldTM Structural Adhesive Primer EC-3983, obtained from Minnesota Mining and Manufacturing Company, St. Paul, MN) according to the manufacturer's instructions to give a dried primer thickness of between 0.00010 and
• the primed panels were bonded to one another in an overlapping relationship along their lengthwise dimension using a 15.9 mm wide strip of adhesive film.
• the scrim-supported film was applied to the first adherend by hand using a small rubber roller in such a manner as to exclude entrapped air and insure intimate contact between the exposed adhesive and the substrate.
• the second adherend was placed in contact with the exposed adhesive surface to give an assembly with an overlap area of 0.5 inches (12.7 mm). The resulting assembly was fastened together using tape and cured in an autoclave in the following manner.
• the bonded panels were sawn across their width into 1 inch (2.54 cm) wide strips and evaluated for overlap shear strength in accordance with ASTM D-1002 using a grip separation rate of 0.05 inches/minute (1.3 millimeters/minute) using a tensile tester. Testing was conducted at two different test temperatures (room temperature and 177 °C). Samples tested at the elevated temperature were equilibrated for between 10 and 15 minutes prior to testing.
• the primed panels were bonded together using the same film adhesive and cure cycle employed for the overlap shear samples, then evaluated for floating roller peel strength in accordance with ASTM D-3167-76 with the following modification. Test strips measuring 0.5 inch (12.7 cm) wide were cut along the lengthwise direction of the bonded aluminum panels.
• DER 332 a liquid bisphenol-A based epoxy resin having an epoxide equivalent of from 172 to 176, available from Dow Chemical
• EPONTM SU-8 a solid polymeric aromatic epoxy resin having an average epoxide group functionality of around 8, available from Resolution
• TACTIX XP-71756 a dicyclopentadienyl-based epoxy resin, available from Vantico,
• UVR 6105 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexylcarboxylate, having an epoxide equivalent of from 130-135 obtained from Union Carbide, Danbury, CT.
• DICY dicyandiamide available as AmicureTM CG-1200 from Air Products and Chemicals, Incorporated, Allentown, PA.
• o-TBAF 9,9-bis(3-methyl-4-aminophenyl)fluorene having a theoretical amine hydrogen equivalent weight of 94.5 grams/equivalent.
• Alumina atomized alumina powder available as MD-201 from Alcan Metal Powders, Union, NJ.
• TACTIXTM XP-71756 and SU-8 polyepoxide resins were charged into a 1 gallon (3.8 liter) kneader mixer.
• the polyepoxide resin mixture was heated, using a steam jacket, to 300 °F (149 °C) with mixing.
• the DERTM 332 polyepoxide resin was then added with stirring.
• a rubber toughening agent preheated to 160 °F (71 °C) was slowly added to the polyepoxide mixture over a period of about 15 minutes.
• the polyepoxide resin/rubber toughening agent blend was mixed at 300 °F (149 °C)
• the heated composition from the "Preparation of Resin Compositions" procedure above was coated onto a 0.005 inch (0.13 mm) thick paper liner, having a silicone coating on one side and a polyethylene coating on the opposite side using a knife-over-bed coating station having a gap setting of 0.007 inches (0.18 millimeters) greater than the release liner thickness and a bed and knife temperature of 160 °F (71 °C).
• the adhesive composition was coated onto the silicone-treated side of the liner to give a liner supported adhesive film.
• the adhesive-coated liner was wound up on itself, allowed to stand for 24 hours at room temperature (about 70 °F (21 °C)), then stored at -20 °F (-29 °C) until further use.
• This lay-up was passed between two rubber-coated, heated nip rollers at a pressure of about 40 pounds and a temperature between about 140 °F and 160 °F (60 °C and 71 °C) to give a glass scrim-supported adhesive film, also described as an adhesive film having a glass scrim embedded therein, having release liner on each side.
• Examples 1-7 and Comparative Examples (CE) 1-9 in Tables 1 and 2 below demonstrate the range of amount of cycloaliphatic epoxy resin that can be used in the compositions of the present invention.
• the amounts are given in parts by weight (pbw), wherein the combined amounts of all components is 100 pbw.
• the weight percent aliphatic character was calculated as described above.
• Comparative Examples 7-9 were prepared as described above except CAF was used as the curative in place of o-TBAF and UVR 6105 was used in place of TACTIX 71756 in Comparative Example 7. Additionally, Comparative Examples 7 and 8 were also prepared and evaluated using a post cure of 2 hours at 350 °F (177 °C).
• Comparative Example 7 employed the cycloaliphatic resin UVR 6105 in place of TACTIX XP-71756.
• compositions of the invention that is, those whose epoxide component contains above 10% cycloaliphatic character (as defined herein) and whose curing agent is o-TBAF, exhibit a combination of overlap shear values at 350 °F (177 °C) (of at least about 1900 pounds/inch 2 (psi) (13.1 megaPascals) and Floating Roller Peel Strength peel values (at room temperature) of at least about 20 pounds/inch width (piw) (3.5 Newtons/millimeter).
• compositions containing essentially only difunctional aromatic epoxide resin (for example, DER 332) or a combination of multifunctional and essentially difunctional aromatic epoxide resins (for example, DER 332 and SU-8) do not exhibit such characteristics.
• compositions employing a cycloaliphatic epoxide component falling outside the definition of cycloaliphatic-containing polyepoxide resin used herein does not exhibit such performance characteristics.
• the use of an alternative fluorene' amine curing agent (CAF) in the adhesive compositions does not exhibit such performance characteristics.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Epoxy Resins (AREA)
• Adhesive Tapes (AREA)
• Pharmaceuticals Containing Other Organic And Inorganic Compounds (AREA)
• Medicines Containing Material From Animals Or Micro-Organisms (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=21716455

Family Applications (1)

Country Status (10)

Cited By (13)

Families Citing this family (33)

Citations (4)

Family Cites Families (23)

• 2001
  • 2001-11-08 US US10/005,556 patent/US6624213B2/en not_active Expired - Lifetime
• 2002
  • 2002-09-23 CN CN02822191.5A patent/CN1256396C/zh not_active Expired - Fee Related
  • 2002-09-23 AT AT02778311T patent/ATE437932T1/de not_active IP Right Cessation
  • 2002-09-23 EP EP02778311A patent/EP1442090B1/en not_active Expired - Lifetime
  • 2002-09-23 DE DE60233153T patent/DE60233153D1/de not_active Expired - Lifetime
  • 2002-09-23 ES ES02778311T patent/ES2330926T3/es not_active Expired - Lifetime
  • 2002-09-23 BR BRPI0213751-8A patent/BR0213751B1/pt not_active IP Right Cessation
  • 2002-09-23 JP JP2003542292A patent/JP4242771B2/ja not_active Expired - Fee Related
  • 2002-09-23 WO PCT/US2002/030155 patent/WO2003040251A1/en not_active Ceased
  • 2002-09-23 CA CA002462454A patent/CA2462454C/en not_active Expired - Fee Related