WO2003033980A1 - Procede d'application de materiau refractaire monolithique et materiau refractaire monolithique utilise selon ce procede - Google Patents

Procede d'application de materiau refractaire monolithique et materiau refractaire monolithique utilise selon ce procede Download PDF

Info

Publication number
WO2003033980A1
WO2003033980A1 PCT/JP2002/010767 JP0210767W WO03033980A1 WO 2003033980 A1 WO2003033980 A1 WO 2003033980A1 JP 0210767 W JP0210767 W JP 0210767W WO 03033980 A1 WO03033980 A1 WO 03033980A1
Authority
WO
WIPO (PCT)
Prior art keywords
refractory
mass
irregular
amorphous
hopper
Prior art date
Application number
PCT/JP2002/010767
Other languages
English (en)
Japanese (ja)
Inventor
Sakae Nakai
Tetsunori Ikebe
Yoichi Furuta
Jun Kimonji
Norikazu Shirama
Kiyoshi Goto
Yukihiro Nakamura
Koji Kawano
Yasuhiro Yamada
Original Assignee
Krosakiharima Corporation
Nippon Steel Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Krosakiharima Corporation, Nippon Steel Corporation filed Critical Krosakiharima Corporation
Priority to KR10-2003-7009330A priority Critical patent/KR20040037277A/ko
Priority to KR1020037009267A priority patent/KR100773574B1/ko
Priority to JP2003536671A priority patent/JP4418233B2/ja
Priority to BRPI0212785A priority patent/BRPI0212785B1/pt
Publication of WO2003033980A1 publication Critical patent/WO2003033980A1/fr

Abstract

La présente invention concerne un matériau réfractaire monolithique et un procédé d'application qui favorise l'applicabilité du matériau réfractaire monolithique sur un récipient de métal en fusion, un appareil de traitement de métal en fusion, ou un four à haute température, et qui confère une excellente durée de vie utile au matériau appliqué en comparaison avec les procédés de pulvérisation classiquement utilisés. Selon le procédé de l'invention, on commence par ajouter de l'eau d'application à un poudre réfractaire ultrafine de silice volatile et/ou d'alumine calcinée stockée dans une trémie et on malaxe ensuite le mélange. On mélange le matériau réfractaire à un dispersant et à un agrégat réfractaire contenant de 1 à 30% massique de la poudre réfractaire ultrafine mélangée à l'eau d'application. On distribue le matériau réfractaire monolithique mélangé à une partie située sous la trémie tout en ajoutant un agent à prise rapide et on le projette par centrifugation. Etant donné que le matériau réfractaire monolithique est distribué à la partie située sous la trémie, ce dernier peut être d'une faible fluidité. Cela permet de réduire la quantité d'eau nécessaire à l'application et de faciliter l'application locale, dans la mesure où l'on peut projeter le matériau réfractaire monolithique dans une plage d'angles prédéterminée.
PCT/JP2002/010767 2001-10-17 2002-10-16 Procede d'application de materiau refractaire monolithique et materiau refractaire monolithique utilise selon ce procede WO2003033980A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
KR10-2003-7009330A KR20040037277A (ko) 2001-10-17 2002-10-16 부정형 내화물의 시공방법 및 그에 사용되는 부정형 내화물
KR1020037009267A KR100773574B1 (ko) 2001-10-17 2002-10-16 부정형 내화물의 시공방법 및 그에 사용되는 부정형 내화물
JP2003536671A JP4418233B2 (ja) 2001-10-17 2002-10-16 不定形耐火物の施工方法
BRPI0212785A BRPI0212785B1 (pt) 2001-10-17 2002-10-16 método de aplicar um material refratário monolítico a um recipiente para metais em fusão

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2001319941 2001-10-17
JP2001-319941 2001-10-17

Publications (1)

Publication Number Publication Date
WO2003033980A1 true WO2003033980A1 (fr) 2003-04-24

Family

ID=19137404

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2002/010767 WO2003033980A1 (fr) 2001-10-17 2002-10-16 Procede d'application de materiau refractaire monolithique et materiau refractaire monolithique utilise selon ce procede

Country Status (5)

Country Link
JP (1) JP4418233B2 (fr)
KR (2) KR100773574B1 (fr)
CN (1) CN100529628C (fr)
BR (1) BRPI0212785B1 (fr)
WO (1) WO2003033980A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008241236A (ja) * 2007-02-27 2008-10-09 Nippon Steel Corp 耐火物の連続施工装置
JP2009281697A (ja) * 2008-05-26 2009-12-03 Nippon Steel Corp 耐火物の連続混練装置
CN101942576A (zh) * 2010-09-02 2011-01-12 中信锦州铁合金股份有限公司 冶炼金属铬所用炉衬的制造方法
JP2019503964A (ja) * 2015-12-16 2019-02-14 カルデリス フランス ゼオライト微細構造を含むキャスタブル耐火性組成物およびその使用
JP2019131446A (ja) * 2018-02-01 2019-08-08 日本製鉄株式会社 アルミナ−マグネシア質キャスタブル耐火物の耐用性評価方法

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5767689B2 (ja) * 2013-12-11 2015-08-19 黒崎播磨株式会社 溶射装置
CN104058759B (zh) * 2014-06-26 2015-09-16 中材高新成都能源技术有限公司 一种新型的石英耐火材料
JP6454653B2 (ja) * 2016-02-12 2019-01-16 株式会社ヨータイ ポルトランドセメント質急結剤スラリー及び湿式吹き付け施工方法
KR101719306B1 (ko) 2017-01-09 2017-03-27 주식회사 유한정밀 스크류 피딩식 부정형 내화물 유입시공기
CN109520305B (zh) * 2018-12-31 2024-04-12 广西玉柴机器股份有限公司 一种工业熔炼炉窑炉嘴修筑设备及操作方法
CN111550810B (zh) * 2020-04-24 2022-06-14 中国电建集团河南工程有限公司 生活垃圾焚烧炉炉衬砌筑施工方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS4883006A (fr) * 1972-02-10 1973-11-06
JPS51151605A (en) * 1975-06-23 1976-12-27 Sumitomo Heavy Ind Ltd Automatic refractory agent projecting apparatus within a vessel contai ning molten metal
JPS5365311A (en) * 1976-11-25 1978-06-10 Gijiyutsu Shigen Kaihatsu Kk Device for lining cylindrical structures or metallurgical apparatus
JPH11159970A (ja) * 1997-11-25 1999-06-15 Harima Ceramic Co Ltd 耐火物吹付け施工方法
JPH11294965A (ja) * 1998-04-13 1999-10-29 Harima Ceramic Co Ltd 耐火物吹付け施工方法およびこの方法に使用する吹付材
JP2001255075A (ja) * 2000-03-14 2001-09-21 Nippon Steel Corp 溶融金属容器内張り耐火物の吹付け施工方法

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07315942A (ja) * 1994-05-18 1995-12-05 Nippon Steel Corp 溶融金属容器の内張り不定形耐火物
JPH09142945A (ja) * 1995-11-28 1997-06-03 Harima Ceramic Co Ltd 溶銑容器内張り用不定形耐火物とそれを用いた溶銑容器の内張り構造
CN2366816Y (zh) * 1999-01-06 2000-03-01 王世松 竖直旋转式喷补机

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS4883006A (fr) * 1972-02-10 1973-11-06
JPS51151605A (en) * 1975-06-23 1976-12-27 Sumitomo Heavy Ind Ltd Automatic refractory agent projecting apparatus within a vessel contai ning molten metal
JPS5365311A (en) * 1976-11-25 1978-06-10 Gijiyutsu Shigen Kaihatsu Kk Device for lining cylindrical structures or metallurgical apparatus
JPH11159970A (ja) * 1997-11-25 1999-06-15 Harima Ceramic Co Ltd 耐火物吹付け施工方法
JPH11294965A (ja) * 1998-04-13 1999-10-29 Harima Ceramic Co Ltd 耐火物吹付け施工方法およびこの方法に使用する吹付材
JP2001255075A (ja) * 2000-03-14 2001-09-21 Nippon Steel Corp 溶融金属容器内張り耐火物の吹付け施工方法

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008241236A (ja) * 2007-02-27 2008-10-09 Nippon Steel Corp 耐火物の連続施工装置
JP2009281697A (ja) * 2008-05-26 2009-12-03 Nippon Steel Corp 耐火物の連続混練装置
CN101942576A (zh) * 2010-09-02 2011-01-12 中信锦州铁合金股份有限公司 冶炼金属铬所用炉衬的制造方法
JP2019503964A (ja) * 2015-12-16 2019-02-14 カルデリス フランス ゼオライト微細構造を含むキャスタブル耐火性組成物およびその使用
US11130711B2 (en) 2015-12-16 2021-09-28 Imertech Sas Castable refractory compositions comprising zeolithic microstructures and uses thereof
JP2022075664A (ja) * 2015-12-16 2022-05-18 カルデリス フランス ゼオライト微細構造を含むキャスタブル耐火性組成物およびその使用
JP7340930B2 (ja) 2015-12-16 2023-09-08 カルデリス フランス ゼオライト微細構造を含むキャスタブル耐火性組成物およびその使用
JP2019131446A (ja) * 2018-02-01 2019-08-08 日本製鉄株式会社 アルミナ−マグネシア質キャスタブル耐火物の耐用性評価方法

Also Published As

Publication number Publication date
JP4418233B2 (ja) 2010-02-17
BR0212785A (pt) 2007-01-09
KR20040039191A (ko) 2004-05-10
CN100529628C (zh) 2009-08-19
CN1489683A (zh) 2004-04-14
JPWO2003033980A1 (ja) 2005-02-03
BRPI0212785B1 (pt) 2015-10-27
KR20040037277A (ko) 2004-05-06
KR100773574B1 (ko) 2007-11-05

Similar Documents

Publication Publication Date Title
CN101544505A (zh) 纳米Al2O3、MgO复合陶瓷结合尖晶石-镁质耐火浇注料及其制备方法
JP4418233B2 (ja) 不定形耐火物の施工方法
CN1077558C (zh) 用于生产致密浇注耐火材料的可浇注耐火材料组合物及其湿式喷射法
CN1199736C (zh) 不定形耐火材料的喷涂施工方法
JP2005154180A (ja) アルミナセメント組成物及び不定形耐火物
JP4141158B2 (ja) 耐食性、耐スポーリング性、乾燥性に優れた不定形耐火物用ＳｉＣ、及び不定形耐火物原料
JPH10118762A (ja) 緻密質流し込み耐火組成物の湿式吹付け施工方法
JP2604310B2 (ja) 流し込み施工耐火物
JP2831976B2 (ja) 湿式吹付け施工法
JP6454653B2 (ja) ポルトランドセメント質急結剤スラリー及び湿式吹き付け施工方法
JP5283849B2 (ja) 耐火物の連続混練方法、耐火物の連続施工方法、耐火物の連続混練装置、及び耐火物の連続施工装置
EP0798279B1 (fr) Méthode de projection humide
JP3449673B2 (ja) 吹付け施工方法
JP2000016874A (ja) 耐火物用急結剤及びそれを用いた吹付施工方法
JP4204246B2 (ja) 乾燥性と耐食性に優れた不定形耐火物用炭化けい素原料及び不定形耐火物原料
WO2013100049A1 (fr) Procédé de construction continue de matériau résistant au feu, matériau résistant au feu et dispositif de construction continue
JP2004307293A (ja) 不定形耐火組成物
JP2007099545A (ja) アルミナセメント組成物及びそれを用いた不定形耐火物
JP4575852B2 (ja) 不定形耐火物の施工方法
JPH1030885A (ja) 不定形耐火物の吹付け施工方法及びその施工体
JP4456193B2 (ja) 耐火物吹付け施工方法
JP3981433B2 (ja) 耐火物吹付け施工方法
JP2002071278A (ja) 湿式吹付施工方法
JP2005154191A (ja) 湿式吹付け用不定形耐火物及びその施工方法
JPH11310470A (ja) 湿式吹付用不定形耐火物

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): BR CN JP

WWE Wipo information: entry into national phase

Ref document number: 2003536671

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 1020037009267

Country of ref document: KR

Ref document number: 1020037009330

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 028041356

Country of ref document: CN

WWP Wipo information: published in national office

Ref document number: 1020037009330

Country of ref document: KR

WWP Wipo information: published in national office

Ref document number: 1020037009267

Country of ref document: KR

ENP Entry into the national phase

Ref document number: PI0212785

Country of ref document: BR