CN104058759B - 一种新型的石英耐火材料 - Google Patents

一种新型的石英耐火材料 Download PDF

Info

Publication number
CN104058759B
CN104058759B CN201410291650.6A CN201410291650A CN104058759B CN 104058759 B CN104058759 B CN 104058759B CN 201410291650 A CN201410291650 A CN 201410291650A CN 104058759 B CN104058759 B CN 104058759B
Authority
CN
China
Prior art keywords
parts
oxide
water
powder
magnesium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410291650.6A
Other languages
English (en)
Other versions
CN104058759A (zh
Inventor
付伟峰
窦涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
High-New Chengdu Of Middle Material Enertech Co Ltd
Original Assignee
High-New Chengdu Of Middle Material Enertech Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by High-New Chengdu Of Middle Material Enertech Co Ltd filed Critical High-New Chengdu Of Middle Material Enertech Co Ltd
Priority to CN201410291650.6A priority Critical patent/CN104058759B/zh
Publication of CN104058759A publication Critical patent/CN104058759A/zh
Application granted granted Critical
Publication of CN104058759B publication Critical patent/CN104058759B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于耐火材料制造领域，具体涉及耐火材料的生产，尤其涉及一种新型的石英耐火材料，其特征在于：包括熔融石英粉、硼化锆粉、乙醇、水、聚乙烯醇溶液、碳化硅、氧化铝、氧化镁、氧化钙、氧化铬、氧化锆、硅酸钠、硅酸镁、酚醛树脂。

Description

一种新型的石英耐火材料
技术领域
本发明属于耐火材料制造领域，具体涉及耐火材料的生产，尤其涉及一种新型的石英耐火材料。
背景技术
耐火度不低于1580℃的一类无机非金属材料。耐火度是指耐火材料锥形体试样在没有荷重情况下，抵抗高温作用而不软化熔倒的摄氏温度。但仅以耐火度来定义已不能全面描述耐火材料了，1580℃并不是绝对的。现定义为凡物理化学性质允许其在高温环境下使用的材料称为耐火材料。耐火材料广泛用于冶金、化工、石油、机械制造、硅酸盐、动力等工业领域，在冶金工业中用量最大，占总产量的50%～60%。
耐火材料应用于钢铁、有色金属、玻璃、水泥、陶瓷、石化、机械、锅炉、轻工、电力、军工等国民经济的各个领域，是保证上述产业生产运行和技术发展必不可少的基本材料，在高温工业生产发展中起着不可替代的重要作用。
但是在现有技术中耐火材料在潮湿的环境下使用周期不长，并且不稳定，极易出安全问题。
发明内容
为了解决现有技术的缺陷，本发明提供了一种新型的石英耐火材料。
一种新型的石英耐火材料，其特征在于：包括熔融石英粉、硼化锆粉、乙醇、水、聚乙烯醇溶液、碳化硅、氧化铝、氧化镁、氧化钙、氧化铬、氧化锆、硅酸钠、硅酸镁、酚醛树脂。
所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  10-15份
硼化锆粉                                                  15-25份
乙醇                                                     20-25份
水                                                        15-30份
聚乙烯醇溶液                                             12-15份
碳化硅                                                  15-18份
氧化铝                                                  20-35份
氧化镁                                                  15-22份
氧化钙                                                  10-24份
氧化铬                                                  10-20份
氧化锆                                                  10-15份
硅酸钠                                                  20-30份
硅酸镁                                                  25-45份
酚醛树脂                                                 20-30份。
所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  10份
硼化锆粉                                                  15份
乙醇                                                     20份
水                                                        15份
聚乙烯醇溶液                                             12份
碳化硅                                                  15份
氧化铝                                                  20份
氧化镁                                                  15份
氧化钙                                                  10份
氧化铬                                                  10份
氧化锆                                                  10份
硅酸钠                                                  20份
硅酸镁                                                  25份
酚醛树脂                                                 20份。
所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  15份
硼化锆粉                                                  25份
乙醇                                                     25份
水                                                        30份
聚乙烯醇溶液                                             15份
碳化硅                                                  18份
氧化铝                                                  35份
氧化镁                                                  22份
氧化钙                                                  24份
氧化铬                                                  20份
氧化锆                                                  15份
硅酸钠                                                  30份
硅酸镁                                                  45份
酚醛树脂                                                 30份。
具体实施方式
实施例1
一种新型的石英耐火材料，其特征在于：包括熔融石英粉、硼化锆粉、乙醇、水、聚乙烯醇溶液、碳化硅、氧化铝、氧化镁、氧化钙、氧化铬、氧化锆、硅酸钠、硅酸镁、酚醛树脂。
所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  10-15份
硼化锆粉                                                  15-25份
乙醇                                                     20-25份
水                                                        15-30份
聚乙烯醇溶液                                             12-15份
碳化硅                                                  15-18份
氧化铝                                                  20-35份
氧化镁                                                  15-22份
氧化钙                                                  10-24份
氧化铬                                                  10-20份
氧化锆                                                  10-15份
硅酸钠                                                  20-30份
硅酸镁                                                  25-45份
酚醛树脂                                                 20-30份。
实施例2
一种新型的石英耐火材料，其特征在于：包括熔融石英粉、硼化锆粉、乙醇、水、聚乙烯醇溶液、碳化硅、氧化铝、氧化镁、氧化钙、氧化铬、氧化锆、硅酸钠、硅酸镁、酚醛树脂。
所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  10份
硼化锆粉                                                  15份
乙醇                                                     20份
水                                                        15份
聚乙烯醇溶液                                             12份
碳化硅                                                  15份
氧化铝                                                  20份
氧化镁                                                  15份
氧化钙                                                  10份
氧化铬                                                  10份
氧化锆                                                  10份
硅酸钠                                                  20份
硅酸镁                                                  25份
酚醛树脂                                                 20份。
实施例3
一种新型的石英耐火材料，其特征在于：包括熔融石英粉、硼化锆粉、乙醇、水、聚乙烯醇溶液、碳化硅、氧化铝、氧化镁、氧化钙、氧化铬、氧化锆、硅酸钠、硅酸镁、酚醛树脂。
所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  15份
硼化锆粉                                                  25份
乙醇                                                     25份
水                                                        30份
聚乙烯醇溶液                                             15份
碳化硅                                                  18份
氧化铝                                                  35份
氧化镁                                                  22份
氧化钙                                                  24份
氧化铬                                                  20份
氧化锆                                                  15份
硅酸钠                                                  30份
硅酸镁                                                  45份
酚醛树脂                                                 30份。

Claims (3)

1.一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  10-15份
硼化锆粉                                                  15-25份
乙醇                                                     20-25份
水                                                        15-30份
聚乙烯醇溶液                                             12-15份
碳化硅                                                  15-18份
氧化铝                                                  20-35份
氧化镁                                                  15-22份
氧化钙                                                  10-24份
氧化铬                                                  10-20份
氧化锆                                                  10-15份
硅酸钠                                                  20-30份
硅酸镁                                                  25-45份
酚醛树脂                                                 20-30份。
2.根据权利要求1所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  10份
硼化锆粉                                                  15份
乙醇                                                     20份
水                                                        15份
聚乙烯醇溶液                                             12份
碳化硅                                                  15份
氧化铝                                                  20份
氧化镁                                                  15份
氧化钙                                                  10份
氧化铬                                                  10份
氧化锆                                                  10份
硅酸钠                                                  20份
硅酸镁                                                  25份
酚醛树脂                                                 20份。
3.根据权利要求1所述的一种新型的石英耐火材料，其特征在于：包括如下组分，按照质量份数计算如下：
熔融石英粉                                                  15份
硼化锆粉                                                  25份
乙醇                                                     25份
水                                                        30份
聚乙烯醇溶液                                             15份
碳化硅                                                  18份
氧化铝                                                  35份
氧化镁                                                  22份
氧化钙                                                  24份
氧化铬                                                  20份
氧化锆                                                  15份
硅酸钠                                                  30份
硅酸镁                                                  45份
酚醛树脂                                                 30份。
CN201410291650.6A 2014-06-26 2014-06-26 一种新型的石英耐火材料 Expired - Fee Related CN104058759B (zh)