WO1999011722A1 - Noir de carbone et procede de production - Google Patents
Noir de carbone et procede de production Download PDFInfo
- Publication number
- WO1999011722A1 WO1999011722A1 PCT/JP1998/003862 JP9803862W WO9911722A1 WO 1999011722 A1 WO1999011722 A1 WO 1999011722A1 JP 9803862 W JP9803862 W JP 9803862W WO 9911722 A1 WO9911722 A1 WO 9911722A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon black
- less
- furnace
- temperature
- reaction zone
- Prior art date
Description
Claims