WO1983001959A1 - Procede pour le durcissement bainitique au moins partiel de façon isothermique d'une piece en fonte - Google Patents
Procede pour le durcissement bainitique au moins partiel de façon isothermique d'une piece en fonte Download PDFInfo
- Publication number
- WO1983001959A1 WO1983001959A1 PCT/CH1982/000126 CH8200126W WO8301959A1 WO 1983001959 A1 WO1983001959 A1 WO 1983001959A1 CH 8200126 W CH8200126 W CH 8200126W WO 8301959 A1 WO8301959 A1 WO 8301959A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- bath
- temperature
- cooling
- intercooling
- workpiece
- Prior art date
Abstract
Le procédé pour le durcissement bainitique au moins partiel de façon isothermique d'une pièce en fonte est particulièrement adapté au traitement de pièces métalliques à parois épaisses. Les pièces après un traitement austénitique sont refroidies dans un bain intermédiaire et finalement soumises à une température de durcissement bainitique jusqu'à ce que le résultat recherché soit obtenu.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
BR8208004A BR8208004A (pt) | 1981-12-03 | 1982-12-02 | Processo de bainitizacao isotermica pelo menos parcial de pecas de ferro fundido |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CH7726/81-5811203 | 1981-12-03 | ||
CH7726/81A CH648350A5 (de) | 1981-12-03 | 1981-12-03 | Verfahren zum isothermen bainitisieren von werkstuecken aus eisenwerkstoffen. |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1983001959A1 true WO1983001959A1 (fr) | 1983-06-09 |
Family
ID=4329552
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CH1982/000126 WO1983001959A1 (fr) | 1981-12-03 | 1982-12-02 | Procede pour le durcissement bainitique au moins partiel de façon isothermique d'une piece en fonte |
Country Status (6)
Country | Link |
---|---|
EP (1) | EP0095470A1 (fr) |
BR (1) | BR8208004A (fr) |
CA (1) | CA1210672A (fr) |
CH (1) | CH648350A5 (fr) |
IT (1) | IT1153659B (fr) |
WO (1) | WO1983001959A1 (fr) |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2590508A1 (fr) * | 1985-11-27 | 1987-05-29 | Pont A Mousson | Procede d'obtention de pieces moulees en fonte a graphite spheroidal et fonte obtenue par ce procede |
EP0271688A1 (fr) * | 1986-11-20 | 1988-06-22 | Necchi Societa Per Azioni | Procédé pour la fabrication de pièces moulées en fonte bainitique modulaire |
FR2697535A1 (fr) * | 1992-11-02 | 1994-05-06 | Schissler Jean Marie | Procédé amélioré de traitement thermique d'alliages ferreux ou non-ferreux, et son application à l'élaboration de fonte bainitique. |
EP0622466A1 (fr) * | 1993-04-26 | 1994-11-02 | Mercedes-Benz Ag | Procédé de durcissement de pièces en fonte à graphite sphéroidal |
US6149743A (en) * | 1997-08-01 | 2000-11-21 | Ovako Steel Ab | Method of complete bainite hardening |
WO2008071157A2 (fr) * | 2006-12-14 | 2008-06-19 | Schaeffler Kg | Procédé de traitement thermique de composants de palier de roulement en acier bainitique durci pour paliers de roulement |
CN104294014A (zh) * | 2013-07-18 | 2015-01-21 | 首都航天机械公司 | 中碳硅锰铬镍系低合金钢的贝氏体等温热处理方法 |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2258566A (en) * | 1940-07-30 | 1941-10-07 | American Steel & Wire Co | Hardenable steel heat treatment |
GB601588A (en) * | 1943-07-06 | 1948-05-10 | Charles Greiner Purnell | Improvements in and relating to heat treatment of hardenable steel |
DE872956C (de) * | 1943-08-28 | 1953-04-09 | Deutsche Edelstahlwerke Ag | Zwischenstufenverguetung von unlegierten und legierten Staehlen |
DE2054416A1 (en) * | 1970-11-05 | 1972-05-31 | Foerderung Der Eisenhuettentec | Heat treatment of steel workpieces - comprising cooling from the austenitisation temp in a heated bath |
US3784416A (en) * | 1972-09-29 | 1974-01-08 | Canron Ltd | Manufacture of white cast iron |
FR2192184A1 (fr) * | 1972-07-12 | 1974-02-08 | Kymin Oy Kymmene Ab | |
FR2358465A1 (fr) * | 1976-07-13 | 1978-02-10 | Bochumer Eisen Heintzmann | Procede et dispositif pour fabriquer des segments de profile d'acier utilises pour le soutenement de galeries souterraines |
EP0018445A1 (fr) * | 1978-12-13 | 1980-11-12 | Horst Dr. Mühlberger | Procédé pour la fabrication de pièces coulée en fonte nodulaire |
-
1981
- 1981-12-03 CH CH7726/81A patent/CH648350A5/de not_active IP Right Cessation
-
1982
- 1982-11-23 IT IT24385/82A patent/IT1153659B/it active
- 1982-12-02 EP EP82903445A patent/EP0095470A1/fr not_active Withdrawn
- 1982-12-02 WO PCT/CH1982/000126 patent/WO1983001959A1/fr not_active Application Discontinuation
- 1982-12-02 CA CA000416913A patent/CA1210672A/fr not_active Expired
- 1982-12-02 BR BR8208004A patent/BR8208004A/pt unknown
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2258566A (en) * | 1940-07-30 | 1941-10-07 | American Steel & Wire Co | Hardenable steel heat treatment |
GB601588A (en) * | 1943-07-06 | 1948-05-10 | Charles Greiner Purnell | Improvements in and relating to heat treatment of hardenable steel |
DE872956C (de) * | 1943-08-28 | 1953-04-09 | Deutsche Edelstahlwerke Ag | Zwischenstufenverguetung von unlegierten und legierten Staehlen |
DE2054416A1 (en) * | 1970-11-05 | 1972-05-31 | Foerderung Der Eisenhuettentec | Heat treatment of steel workpieces - comprising cooling from the austenitisation temp in a heated bath |
FR2192184A1 (fr) * | 1972-07-12 | 1974-02-08 | Kymin Oy Kymmene Ab | |
US3784416A (en) * | 1972-09-29 | 1974-01-08 | Canron Ltd | Manufacture of white cast iron |
FR2358465A1 (fr) * | 1976-07-13 | 1978-02-10 | Bochumer Eisen Heintzmann | Procede et dispositif pour fabriquer des segments de profile d'acier utilises pour le soutenement de galeries souterraines |
EP0018445A1 (fr) * | 1978-12-13 | 1980-11-12 | Horst Dr. Mühlberger | Procédé pour la fabrication de pièces coulée en fonte nodulaire |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2590508A1 (fr) * | 1985-11-27 | 1987-05-29 | Pont A Mousson | Procede d'obtention de pieces moulees en fonte a graphite spheroidal et fonte obtenue par ce procede |
EP0271688A1 (fr) * | 1986-11-20 | 1988-06-22 | Necchi Societa Per Azioni | Procédé pour la fabrication de pièces moulées en fonte bainitique modulaire |
FR2697535A1 (fr) * | 1992-11-02 | 1994-05-06 | Schissler Jean Marie | Procédé amélioré de traitement thermique d'alliages ferreux ou non-ferreux, et son application à l'élaboration de fonte bainitique. |
EP0622466A1 (fr) * | 1993-04-26 | 1994-11-02 | Mercedes-Benz Ag | Procédé de durcissement de pièces en fonte à graphite sphéroidal |
US6149743A (en) * | 1997-08-01 | 2000-11-21 | Ovako Steel Ab | Method of complete bainite hardening |
WO2008071157A2 (fr) * | 2006-12-14 | 2008-06-19 | Schaeffler Kg | Procédé de traitement thermique de composants de palier de roulement en acier bainitique durci pour paliers de roulement |
WO2008071157A3 (fr) * | 2006-12-14 | 2009-05-14 | Schaeffler Kg | Procédé de traitement thermique de composants de palier de roulement en acier bainitique durci pour paliers de roulement |
CN104294014A (zh) * | 2013-07-18 | 2015-01-21 | 首都航天机械公司 | 中碳硅锰铬镍系低合金钢的贝氏体等温热处理方法 |
CN104294014B (zh) * | 2013-07-18 | 2016-12-28 | 首都航天机械公司 | 中碳硅锰铬镍系低合金钢的贝氏体等温热处理方法 |
Also Published As
Publication number | Publication date |
---|---|
IT8224385A0 (it) | 1982-11-23 |
IT8224385A1 (it) | 1984-05-23 |
IT1153659B (it) | 1987-01-14 |
EP0095470A1 (fr) | 1983-12-07 |
CH648350A5 (de) | 1985-03-15 |
BR8208004A (pt) | 1983-10-18 |
CA1210672A (fr) | 1986-09-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE19849681C1 (de) | Verfahren zur Wärmebehandlung von Bauteilen aus Stahl oder Gußeisen | |
DE2439338B1 (de) | Verfahren zur Wärmebehandlung von Schienen | |
WO1983001959A1 (fr) | Procede pour le durcissement bainitique au moins partiel de façon isothermique d'une piece en fonte | |
DE3701815A1 (de) | Verfahren zum herstellen eines plattierten formkoerpers | |
WO2006013055A1 (fr) | Procede de traitement thermique de pieces en acier | |
DE2023064C3 (de) | Verfahren zur Herstellung von Lagerringen | |
CH648353A5 (de) | Gussteile mit hoher schlagzaehigkeit und ein verfahren zu deren herstellung. | |
DE19612818C2 (de) | Verfahren zur Kühlung walzwarmer Stahlprofile | |
DE3804654A1 (de) | Verfahren zum herstellen von waelzlagerelementen aus einem mikrolegierten stahl | |
DE3037639C2 (de) | Vorrichtung und Verfahren zum Abschrecken von Werkstücken aus Stahl in einem Flüssigkeits-, insbesondere Ölbad | |
DE4327440A1 (de) | Verfahren zur thermochemisch-thermischen Behandlung von Einsatzstählen, Vergütungsstählen und Wälzlagerstählen | |
DE102004037074B3 (de) | Verfahren zur Wärmebehandlung von Werkstücken aus Stahl | |
DE2830153A1 (de) | Verfahren und vorrichtung zum waermebehandeln von zu ringen gehaspeltem draht oder band | |
DE2801066A1 (de) | Verfahren zur erzeugung von stahlstaeben | |
DE872956C (de) | Zwischenstufenverguetung von unlegierten und legierten Staehlen | |
EP0065678B1 (fr) | Procédé et appareil pour le traitement thermique par sections de pièces en métaux ferreux | |
DE3442130A1 (de) | Verfahren zur randschichthaertung in die bainitstufe von gussstuecken aus duktilen eisen-kohlenstoff-gusswerkstoffen | |
EP0418506A1 (fr) | Procédé pour tremper de l'acier au moyen de milieux refroidissement liquides | |
DE966869C (de) | Verfahren zur Oberflaechenhaertung von Staehlen | |
DE2746961A1 (de) | Vorrichtung und verfahren zur verguetung von warmgewalzten stahlstangen | |
DE587695C (de) | Verfahren zum Haerten von Herzstueckspitzen fuer Weichen | |
DE3525071C1 (de) | Verfahren zur Herstellung hochbelastbarer Maschinenteile aus mikro-legiertem Stahl mit zähem, hochfestem Kern und einer verschleißfesten Fe↓2↓B-Randschicht | |
DE102022126837A1 (de) | System und verfahren zum herstellen einer verbesserten bremsscheibe mit verbesserter verschleissfestigkeit | |
WO2022242793A1 (fr) | Procédé de fabrication d'un composant de palier à élément de roulement, composant de palier à élément de roulement et palier à élément de roulement | |
DE1583421B2 (de) | Verfahren zur waermebehandlung von schienen |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Designated state(s): BR JP US |
|
AL | Designated countries for regional patents |
Designated state(s): AT BE CH DE FR GB LU NL SE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1982903445 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1982903445 Country of ref document: EP |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1982903445 Country of ref document: EP |