USH674H - Silver halide photographic light-sensitive material capable of super-rapid processing - Google Patents
Silver halide photographic light-sensitive material capable of super-rapid processing Download PDFInfo
- Publication number
- USH674H USH674H US07/116,229 US11622987A USH674H US H674 H USH674 H US H674H US 11622987 A US11622987 A US 11622987A US H674 H USH674 H US H674H
- Authority
- US
- United States
- Prior art keywords
- sup
- group
- silver halide
- layer
- photographic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- -1 Silver halide Chemical class 0.000 title claims abstract description 134
- 229910052709 silver Inorganic materials 0.000 title claims abstract description 122
- 239000004332 silver Substances 0.000 title claims abstract description 122
- 239000000463 material Substances 0.000 title claims abstract description 79
- 238000012545 processing Methods 0.000 title claims abstract description 31
- 239000000839 emulsion Substances 0.000 claims abstract description 115
- 238000000576 coating method Methods 0.000 claims abstract description 49
- 108010010803 Gelatin Proteins 0.000 claims abstract description 45
- 239000008273 gelatin Substances 0.000 claims abstract description 45
- 229920000159 gelatin Polymers 0.000 claims abstract description 45
- 235000019322 gelatine Nutrition 0.000 claims abstract description 45
- 235000011852 gelatine desserts Nutrition 0.000 claims abstract description 45
- 239000011248 coating agent Substances 0.000 claims abstract description 41
- 238000001035 drying Methods 0.000 claims abstract description 17
- 150000001875 compounds Chemical class 0.000 claims description 25
- 230000001235 sensitizing effect Effects 0.000 claims description 24
- 150000003839 salts Chemical class 0.000 claims description 17
- 239000006224 matting agent Substances 0.000 claims description 16
- 125000000217 alkyl group Chemical group 0.000 claims description 15
- 125000003118 aryl group Chemical group 0.000 claims description 11
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical group [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 10
- 150000001450 anions Chemical class 0.000 claims description 9
- 125000004429 atom Chemical group 0.000 claims description 9
- 125000001424 substituent group Chemical group 0.000 claims description 9
- 125000004964 sulfoalkyl group Chemical group 0.000 claims description 9
- 125000003342 alkenyl group Chemical group 0.000 claims description 6
- 125000004181 carboxyalkyl group Chemical group 0.000 claims description 5
- 125000004435 hydrogen atom Chemical group [H]* 0.000 claims description 3
- 125000002768 hydroxyalkyl group Chemical group 0.000 claims description 3
- 230000001976 improved effect Effects 0.000 abstract description 2
- 239000010410 layer Substances 0.000 description 146
- 239000002245 particle Substances 0.000 description 101
- 238000000034 method Methods 0.000 description 81
- 239000000243 solution Substances 0.000 description 41
- 239000000975 dye Substances 0.000 description 40
- 230000035945 sensitivity Effects 0.000 description 28
- 230000008569 process Effects 0.000 description 24
- JKFYKCYQEWQPTM-UHFFFAOYSA-N 2-azaniumyl-2-(4-fluorophenyl)acetate Chemical compound OC(=O)C(N)C1=CC=C(F)C=C1 JKFYKCYQEWQPTM-UHFFFAOYSA-N 0.000 description 21
- 229910021612 Silver iodide Inorganic materials 0.000 description 21
- 229940045105 silver iodide Drugs 0.000 description 21
- ZUNKMNLKJXRCDM-UHFFFAOYSA-N silver bromoiodide Chemical compound [Ag].IBr ZUNKMNLKJXRCDM-UHFFFAOYSA-N 0.000 description 20
- 239000004094 surface-active agent Substances 0.000 description 19
- 238000001556 precipitation Methods 0.000 description 18
- 239000011241 protective layer Substances 0.000 description 18
- 206010070834 Sensitisation Diseases 0.000 description 17
- 239000011247 coating layer Substances 0.000 description 17
- 239000013078 crystal Substances 0.000 description 17
- 230000008313 sensitization Effects 0.000 description 16
- 239000000084 colloidal system Substances 0.000 description 14
- XMBWDFGMSWQBCA-UHFFFAOYSA-N hydrogen iodide Chemical compound I XMBWDFGMSWQBCA-UHFFFAOYSA-N 0.000 description 13
- IOLCXVTUBQKXJR-UHFFFAOYSA-M potassium bromide Chemical compound [K+].[Br-] IOLCXVTUBQKXJR-UHFFFAOYSA-M 0.000 description 12
- NLKNQRATVPKPDG-UHFFFAOYSA-M potassium iodide Chemical compound [K+].[I-] NLKNQRATVPKPDG-UHFFFAOYSA-M 0.000 description 12
- 239000000126 substance Substances 0.000 description 12
- BQCADISMDOOEFD-UHFFFAOYSA-N Silver Chemical compound [Ag] BQCADISMDOOEFD-UHFFFAOYSA-N 0.000 description 6
- 229910021607 Silver chloride Inorganic materials 0.000 description 6
- 230000000694 effects Effects 0.000 description 6
- 238000011160 research Methods 0.000 description 6
- ADZWSOLPGZMUMY-UHFFFAOYSA-M silver bromide Chemical compound [Ag]Br ADZWSOLPGZMUMY-UHFFFAOYSA-M 0.000 description 6
- HKZLPVFGJNLROG-UHFFFAOYSA-M silver monochloride Chemical compound [Cl-].[Ag+] HKZLPVFGJNLROG-UHFFFAOYSA-M 0.000 description 6
- 238000011282 treatment Methods 0.000 description 6
- 239000003795 chemical substances by application Substances 0.000 description 5
- 238000000586 desensitisation Methods 0.000 description 5
- 239000004848 polyfunctional curative Substances 0.000 description 5
- 230000001681 protective effect Effects 0.000 description 5
- QGZKDVFQNNGYKY-UHFFFAOYSA-O Ammonium Chemical compound [NH4+] QGZKDVFQNNGYKY-UHFFFAOYSA-O 0.000 description 4
- KDLHZDBZIXYQEI-UHFFFAOYSA-N Palladium Chemical compound [Pd] KDLHZDBZIXYQEI-UHFFFAOYSA-N 0.000 description 4
- 125000001931 aliphatic group Chemical group 0.000 description 4
- 229940095054 ammoniac Drugs 0.000 description 4
- 239000012298 atmosphere Substances 0.000 description 4
- 230000001276 controlling effect Effects 0.000 description 4
- 238000011161 development Methods 0.000 description 4
- 238000009826 distribution Methods 0.000 description 4
- 150000004820 halides Chemical class 0.000 description 4
- 230000001965 increasing effect Effects 0.000 description 4
- 230000003287 optical effect Effects 0.000 description 4
- 238000002360 preparation method Methods 0.000 description 4
- 230000005070 ripening Effects 0.000 description 4
- SQGYOTSLMSWVJD-UHFFFAOYSA-N silver(1+) nitrate Chemical compound [Ag+].[O-]N(=O)=O SQGYOTSLMSWVJD-UHFFFAOYSA-N 0.000 description 4
- GGCZERPQGJTIQP-UHFFFAOYSA-N sodium;9,10-dioxoanthracene-2-sulfonic acid Chemical compound [Na+].C1=CC=C2C(=O)C3=CC(S(=O)(=O)O)=CC=C3C(=O)C2=C1 GGCZERPQGJTIQP-UHFFFAOYSA-N 0.000 description 4
- 230000008093 supporting effect Effects 0.000 description 4
- ZCYVEMRRCGMTRW-UHFFFAOYSA-N 7553-56-2 Chemical compound [I] ZCYVEMRRCGMTRW-UHFFFAOYSA-N 0.000 description 3
- QGZKDVFQNNGYKY-UHFFFAOYSA-N Ammonia Chemical compound N QGZKDVFQNNGYKY-UHFFFAOYSA-N 0.000 description 3
- YCKRFDGAMUMZLT-UHFFFAOYSA-N Fluorine atom Chemical compound [F] YCKRFDGAMUMZLT-UHFFFAOYSA-N 0.000 description 3
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 3
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 3
- 229920002472 Starch Polymers 0.000 description 3
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 description 3
- 239000002250 absorbent Substances 0.000 description 3
- 230000002745 absorbent Effects 0.000 description 3
- 239000002253 acid Substances 0.000 description 3
- 239000003945 anionic surfactant Substances 0.000 description 3
- 238000005859 coupling reaction Methods 0.000 description 3
- 230000007547 defect Effects 0.000 description 3
- 238000003745 diagnosis Methods 0.000 description 3
- 150000002148 esters Chemical class 0.000 description 3
- 229910052731 fluorine Inorganic materials 0.000 description 3
- 239000011737 fluorine Substances 0.000 description 3
- 239000000499 gel Substances 0.000 description 3
- PCHJSUWPFVWCPO-UHFFFAOYSA-N gold Chemical compound [Au] PCHJSUWPFVWCPO-UHFFFAOYSA-N 0.000 description 3
- 229910052737 gold Inorganic materials 0.000 description 3
- 239000010931 gold Substances 0.000 description 3
- 229910052740 iodine Inorganic materials 0.000 description 3
- 239000011630 iodine Substances 0.000 description 3
- 239000000203 mixture Substances 0.000 description 3
- 229920003229 poly(methyl methacrylate) Polymers 0.000 description 3
- 239000004926 polymethyl methacrylate Substances 0.000 description 3
- 230000002265 prevention Effects 0.000 description 3
- 239000008107 starch Substances 0.000 description 3
- 238000003860 storage Methods 0.000 description 3
- 229910052717 sulfur Inorganic materials 0.000 description 3
- 239000011593 sulfur Substances 0.000 description 3
- 150000003568 thioethers Chemical class 0.000 description 3
- 238000012546 transfer Methods 0.000 description 3
- CDAWCLOXVUBKRW-UHFFFAOYSA-N 2-aminophenol Chemical class NC1=CC=CC=C1O CDAWCLOXVUBKRW-UHFFFAOYSA-N 0.000 description 2
- QTBSBXVTEAMEQO-UHFFFAOYSA-N Acetic acid Chemical compound CC(O)=O QTBSBXVTEAMEQO-UHFFFAOYSA-N 0.000 description 2
- NLXLAEXVIDQMFP-UHFFFAOYSA-N Ammonia chloride Chemical compound [NH4+].[Cl-] NLXLAEXVIDQMFP-UHFFFAOYSA-N 0.000 description 2
- VTYYLEPIZMXCLO-UHFFFAOYSA-L Calcium carbonate Chemical compound [Ca+2].[O-]C([O-])=O VTYYLEPIZMXCLO-UHFFFAOYSA-L 0.000 description 2
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 2
- FOIXSVOLVBLSDH-UHFFFAOYSA-N Silver ion Chemical compound [Ag+] FOIXSVOLVBLSDH-UHFFFAOYSA-N 0.000 description 2
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 description 2
- ZJCCRDAZUWHFQH-UHFFFAOYSA-N Trimethylolpropane Chemical compound CCC(CO)(CO)CO ZJCCRDAZUWHFQH-UHFFFAOYSA-N 0.000 description 2
- 238000002441 X-ray diffraction Methods 0.000 description 2
- 125000002947 alkylene group Chemical group 0.000 description 2
- 150000001412 amines Chemical class 0.000 description 2
- 125000004103 aminoalkyl group Chemical group 0.000 description 2
- 229910021529 ammonia Inorganic materials 0.000 description 2
- TZCXTZWJZNENPQ-UHFFFAOYSA-L barium sulfate Chemical compound [Ba+2].[O-]S([O-])(=O)=O TZCXTZWJZNENPQ-UHFFFAOYSA-L 0.000 description 2
- 125000003178 carboxy group Chemical group [H]OC(*)=O 0.000 description 2
- 239000007795 chemical reaction product Substances 0.000 description 2
- 239000012792 core layer Substances 0.000 description 2
- 239000007771 core particle Substances 0.000 description 2
- 238000010168 coupling process Methods 0.000 description 2
- 238000002405 diagnostic procedure Methods 0.000 description 2
- 239000006185 dispersion Substances 0.000 description 2
- 125000004185 ester group Chemical group 0.000 description 2
- 238000005562 fading Methods 0.000 description 2
- 238000001879 gelation Methods 0.000 description 2
- 229910052741 iridium Inorganic materials 0.000 description 2
- GKOZUEZYRPOHIO-UHFFFAOYSA-N iridium atom Chemical compound [Ir] GKOZUEZYRPOHIO-UHFFFAOYSA-N 0.000 description 2
- 230000001788 irregular Effects 0.000 description 2
- 238000002844 melting Methods 0.000 description 2
- 230000008018 melting Effects 0.000 description 2
- UHOVQNZJYSORNB-UHFFFAOYSA-N monobenzene Natural products C1=CC=CC=C1 UHOVQNZJYSORNB-UHFFFAOYSA-N 0.000 description 2
- 229910052755 nonmetal Inorganic materials 0.000 description 2
- 150000002894 organic compounds Chemical class 0.000 description 2
- 229910052763 palladium Inorganic materials 0.000 description 2
- 239000004014 plasticizer Substances 0.000 description 2
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical compound [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 description 2
- 229920000233 poly(alkylene oxides) Polymers 0.000 description 2
- 229920000728 polyester Polymers 0.000 description 2
- 230000001105 regulatory effect Effects 0.000 description 2
- 239000000837 restrainer Substances 0.000 description 2
- 230000002441 reversible effect Effects 0.000 description 2
- 229910052703 rhodium Inorganic materials 0.000 description 2
- 239000010948 rhodium Substances 0.000 description 2
- 229910001961 silver nitrate Inorganic materials 0.000 description 2
- AKHNMLFCWUSKQB-UHFFFAOYSA-L sodium thiosulfate Chemical compound [Na+].[Na+].[O-]S([O-])(=O)=S AKHNMLFCWUSKQB-UHFFFAOYSA-L 0.000 description 2
- 235000019345 sodium thiosulphate Nutrition 0.000 description 2
- 230000003595 spectral effect Effects 0.000 description 2
- 230000006641 stabilisation Effects 0.000 description 2
- 238000011105 stabilization Methods 0.000 description 2
- 235000019698 starch Nutrition 0.000 description 2
- 229910052716 thallium Inorganic materials 0.000 description 2
- BKVIYDNLLOSFOA-UHFFFAOYSA-N thallium Chemical compound [Tl] BKVIYDNLLOSFOA-UHFFFAOYSA-N 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 2
- ZSLUVFAKFWKJRC-IGMARMGPSA-N 232Th Chemical compound [232Th] ZSLUVFAKFWKJRC-IGMARMGPSA-N 0.000 description 1
- VHUUQVKOLVNVRT-UHFFFAOYSA-N Ammonium hydroxide Chemical compound [NH4+].[OH-] VHUUQVKOLVNVRT-UHFFFAOYSA-N 0.000 description 1
- CPELXLSAUQHCOX-UHFFFAOYSA-M Bromide Chemical compound [Br-] CPELXLSAUQHCOX-UHFFFAOYSA-M 0.000 description 1
- 229920008347 Cellulose acetate propionate Polymers 0.000 description 1
- 239000001856 Ethyl cellulose Substances 0.000 description 1
- ZZSNKZQZMQGXPY-UHFFFAOYSA-N Ethyl cellulose Chemical compound CCOCC1OC(OC)C(OCC)C(OCC)C1OC1C(O)C(O)C(OC)C(CO)O1 ZZSNKZQZMQGXPY-UHFFFAOYSA-N 0.000 description 1
- 239000005909 Kieselgur Substances 0.000 description 1
- SPAGIJMPHSUYSE-UHFFFAOYSA-N Magnesium peroxide Chemical compound [Mg+2].[O-][O-] SPAGIJMPHSUYSE-UHFFFAOYSA-N 0.000 description 1
- 229920000881 Modified starch Polymers 0.000 description 1
- 229920003171 Poly (ethylene oxide) Polymers 0.000 description 1
- 229920002319 Poly(methyl acrylate) Polymers 0.000 description 1
- ZLMJMSJWJFRBEC-UHFFFAOYSA-N Potassium Chemical compound [K] ZLMJMSJWJFRBEC-UHFFFAOYSA-N 0.000 description 1
- 101150108015 STR6 gene Proteins 0.000 description 1
- 101100386054 Saccharomyces cerevisiae (strain ATCC 204508 / S288c) CYS3 gene Proteins 0.000 description 1
- 206010039737 Scratch Diseases 0.000 description 1
- 229910052776 Thorium Inorganic materials 0.000 description 1
- 229910052770 Uranium Inorganic materials 0.000 description 1
- 208000027418 Wounds and injury Diseases 0.000 description 1
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 1
- LHLMOSXCXGLMMN-CLTUNHJMSA-M [(1s,5r)-8-methyl-8-propan-2-yl-8-azoniabicyclo[3.2.1]octan-3-yl] 3-hydroxy-2-phenylpropanoate;bromide Chemical compound [Br-].C([C@H]1CC[C@@H](C2)[N+]1(C)C(C)C)C2OC(=O)C(CO)C1=CC=CC=C1 LHLMOSXCXGLMMN-CLTUNHJMSA-M 0.000 description 1
- 229960000583 acetic acid Drugs 0.000 description 1
- 125000002252 acyl group Chemical group 0.000 description 1
- 239000000654 additive Substances 0.000 description 1
- 150000001298 alcohols Chemical class 0.000 description 1
- 125000005907 alkyl ester group Chemical group 0.000 description 1
- 150000001413 amino acids Chemical class 0.000 description 1
- 235000011114 ammonium hydroxide Nutrition 0.000 description 1
- SOIFLUNRINLCBN-UHFFFAOYSA-N ammonium thiocyanate Chemical compound [NH4+].[S-]C#N SOIFLUNRINLCBN-UHFFFAOYSA-N 0.000 description 1
- 238000004458 analytical method Methods 0.000 description 1
- 229920006318 anionic polymer Polymers 0.000 description 1
- 125000003289 ascorbyl group Chemical class [H]O[C@@]([H])(C([H])([H])O*)[C@@]1([H])OC(=O)C(O*)=C1O* 0.000 description 1
- 230000006399 behavior Effects 0.000 description 1
- 150000001555 benzenes Chemical class 0.000 description 1
- 239000011230 binding agent Substances 0.000 description 1
- 238000004061 bleaching Methods 0.000 description 1
- 238000007664 blowing Methods 0.000 description 1
- GDTBXPJZTBHREO-UHFFFAOYSA-N bromine Substances BrBr GDTBXPJZTBHREO-UHFFFAOYSA-N 0.000 description 1
- 229910052794 bromium Inorganic materials 0.000 description 1
- 150000001661 cadmium Chemical class 0.000 description 1
- 229910000019 calcium carbonate Inorganic materials 0.000 description 1
- 125000003917 carbamoyl group Chemical group [H]N([H])C(*)=O 0.000 description 1
- 239000011111 cardboard Substances 0.000 description 1
- 229920006317 cationic polymer Polymers 0.000 description 1
- 239000003093 cationic surfactant Substances 0.000 description 1
- 239000001913 cellulose Substances 0.000 description 1
- 229920002678 cellulose Polymers 0.000 description 1
- 229920002301 cellulose acetate Polymers 0.000 description 1
- ZUIVNYGZFPOXFW-UHFFFAOYSA-N chembl1717603 Chemical compound N1=C(C)C=C(O)N2N=CN=C21 ZUIVNYGZFPOXFW-UHFFFAOYSA-N 0.000 description 1
- 238000006243 chemical reaction Methods 0.000 description 1
- 125000001309 chloro group Chemical group Cl* 0.000 description 1
- 238000005354 coacervation Methods 0.000 description 1
- 229910017052 cobalt Inorganic materials 0.000 description 1
- 239000010941 cobalt Substances 0.000 description 1
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 description 1
- 239000007859 condensation product Substances 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 229920001577 copolymer Polymers 0.000 description 1
- 230000008878 coupling Effects 0.000 description 1
- 238000007766 curtain coating Methods 0.000 description 1
- 230000007423 decrease Effects 0.000 description 1
- 238000010612 desalination reaction Methods 0.000 description 1
- 230000006866 deterioration Effects 0.000 description 1
- 230000009034 developmental inhibition Effects 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 150000002009 diols Chemical class 0.000 description 1
- 238000003618 dip coating Methods 0.000 description 1
- 238000002845 discoloration Methods 0.000 description 1
- 239000004815 dispersion polymer Substances 0.000 description 1
- 239000002355 dual-layer Substances 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 150000002170 ethers Chemical class 0.000 description 1
- 235000019325 ethyl cellulose Nutrition 0.000 description 1
- 229920001249 ethyl cellulose Polymers 0.000 description 1
- 238000011156 evaluation Methods 0.000 description 1
- 238000007765 extrusion coating Methods 0.000 description 1
- 230000002349 favourable effect Effects 0.000 description 1
- 239000010419 fine particle Substances 0.000 description 1
- 238000005189 flocculation Methods 0.000 description 1
- 230000016615 flocculation Effects 0.000 description 1
- 239000006081 fluorescent whitening agent Substances 0.000 description 1
- 230000006870 function Effects 0.000 description 1
- LNTHITQWFMADLM-UHFFFAOYSA-N gallic acid Chemical class OC(=O)C1=CC(O)=C(O)C(O)=C1 LNTHITQWFMADLM-UHFFFAOYSA-N 0.000 description 1
- 239000012362 glacial acetic acid Substances 0.000 description 1
- 239000011521 glass Substances 0.000 description 1
- PDMYFWLNGXIKEP-UHFFFAOYSA-K gold(3+);trithiocyanate Chemical compound [Au+3].[S-]C#N.[S-]C#N.[S-]C#N PDMYFWLNGXIKEP-UHFFFAOYSA-K 0.000 description 1
- 125000000687 hydroquinonyl group Chemical class C1(O)=C(C=C(O)C=C1)* 0.000 description 1
- 150000002460 imidazoles Chemical class 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 230000001939 inductive effect Effects 0.000 description 1
- 208000015181 infectious disease Diseases 0.000 description 1
- 230000002458 infectious effect Effects 0.000 description 1
- 229910017053 inorganic salt Inorganic materials 0.000 description 1
- 238000007689 inspection Methods 0.000 description 1
- 239000002563 ionic surfactant Substances 0.000 description 1
- 238000003475 lamination Methods 0.000 description 1
- 239000007791 liquid phase Substances 0.000 description 1
- 238000011068 loading method Methods 0.000 description 1
- 239000000314 lubricant Substances 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 229920000609 methyl cellulose Polymers 0.000 description 1
- 239000001923 methylcellulose Substances 0.000 description 1
- 235000010981 methylcellulose Nutrition 0.000 description 1
- 239000003094 microcapsule Substances 0.000 description 1
- 238000002156 mixing Methods 0.000 description 1
- 235000019426 modified starch Nutrition 0.000 description 1
- 230000007935 neutral effect Effects 0.000 description 1
- 229910052759 nickel Inorganic materials 0.000 description 1
- 239000002736 nonionic surfactant Substances 0.000 description 1
- 235000012149 noodles Nutrition 0.000 description 1
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 1
- 239000000123 paper Substances 0.000 description 1
- 239000011087 paperboard Substances 0.000 description 1
- 239000012071 phase Substances 0.000 description 1
- 150000004986 phenylenediamines Chemical class 0.000 description 1
- 239000000049 pigment Substances 0.000 description 1
- 229910052697 platinum Inorganic materials 0.000 description 1
- 229920001467 poly(styrenesulfonates) Polymers 0.000 description 1
- 229920002239 polyacrylonitrile Polymers 0.000 description 1
- 229920006267 polyester film Polymers 0.000 description 1
- 229920005862 polyol Polymers 0.000 description 1
- 150000003077 polyols Chemical class 0.000 description 1
- 229960002796 polystyrene sulfonate Drugs 0.000 description 1
- 239000011970 polystyrene sulfonate Substances 0.000 description 1
- 229920001343 polytetrafluoroethylene Polymers 0.000 description 1
- 239000004810 polytetrafluoroethylene Substances 0.000 description 1
- 229920002689 polyvinyl acetate Polymers 0.000 description 1
- 239000011118 polyvinyl acetate Substances 0.000 description 1
- 239000011591 potassium Substances 0.000 description 1
- 229910052700 potassium Inorganic materials 0.000 description 1
- 230000000063 preceeding effect Effects 0.000 description 1
- 230000001737 promoting effect Effects 0.000 description 1
- NDGRWYRVNANFNB-UHFFFAOYSA-N pyrazolidin-3-one Chemical compound O=C1CCNN1 NDGRWYRVNANFNB-UHFFFAOYSA-N 0.000 description 1
- JUJWROOIHBZHMG-UHFFFAOYSA-O pyridinium Chemical class C1=CC=[NH+]C=C1 JUJWROOIHBZHMG-UHFFFAOYSA-O 0.000 description 1
- 150000003242 quaternary ammonium salts Chemical class 0.000 description 1
- 239000001397 quillaja saponaria molina bark Substances 0.000 description 1
- MHOVAHRLVXNVSD-UHFFFAOYSA-N rhodium atom Chemical compound [Rh] MHOVAHRLVXNVSD-UHFFFAOYSA-N 0.000 description 1
- 238000007761 roller coating Methods 0.000 description 1
- 229930182490 saponin Natural products 0.000 description 1
- 150000007949 saponins Chemical class 0.000 description 1
- 229910052594 sapphire Inorganic materials 0.000 description 1
- 239000010980 sapphire Substances 0.000 description 1
- 238000004626 scanning electron microscopy Methods 0.000 description 1
- 238000006748 scratching Methods 0.000 description 1
- 230000002393 scratching effect Effects 0.000 description 1
- 239000000377 silicon dioxide Substances 0.000 description 1
- 235000012239 silicon dioxide Nutrition 0.000 description 1
- XNRABACJWNCNEQ-UHFFFAOYSA-N silver;azane;nitrate Chemical compound N.[Ag+].[O-][N+]([O-])=O XNRABACJWNCNEQ-UHFFFAOYSA-N 0.000 description 1
- 239000002356 single layer Substances 0.000 description 1
- 239000006104 solid solution Substances 0.000 description 1
- 239000002904 solvent Substances 0.000 description 1
- 239000012798 spherical particle Substances 0.000 description 1
- 239000007921 spray Substances 0.000 description 1
- 230000003068 static effect Effects 0.000 description 1
- 101150035983 str1 gene Proteins 0.000 description 1
- 229910052712 strontium Inorganic materials 0.000 description 1
- CIOAGBVUUVVLOB-UHFFFAOYSA-N strontium atom Chemical compound [Sr] CIOAGBVUUVVLOB-UHFFFAOYSA-N 0.000 description 1
- 235000000346 sugar Nutrition 0.000 description 1
- 150000008163 sugars Chemical class 0.000 description 1
- 125000000020 sulfo group Chemical group O=S(=O)([*])O[H] 0.000 description 1
- 229920001059 synthetic polymer Polymers 0.000 description 1
- BRNULMACUQOKMR-UHFFFAOYSA-N thiomorpholine Chemical compound C1CSCCN1 BRNULMACUQOKMR-UHFFFAOYSA-N 0.000 description 1
- 239000004408 titanium dioxide Substances 0.000 description 1
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 description 1
- 229910052721 tungsten Inorganic materials 0.000 description 1
- 239000010937 tungsten Substances 0.000 description 1
- DNYWZCXLKNTFFI-UHFFFAOYSA-N uranium Chemical compound [U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U][U] DNYWZCXLKNTFFI-UHFFFAOYSA-N 0.000 description 1
- 150000003672 ureas Chemical class 0.000 description 1
- 150000003673 urethanes Chemical class 0.000 description 1
- 229920002554 vinyl polymer Polymers 0.000 description 1
- 229910052725 zinc Inorganic materials 0.000 description 1
- 239000011701 zinc Substances 0.000 description 1
Images
Classifications
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C5/00—Photographic processes or agents therefor; Regeneration of such processing agents
- G03C5/16—X-ray, infrared, or ultraviolet ray processes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05C—APPARATUS FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05C5/00—Apparatus in which liquid or other fluent material is projected, poured or allowed to flow on to the surface of the work
- B05C5/007—Slide-hopper coaters, i.e. apparatus in which the liquid or other fluent material flows freely on an inclined surface before contacting the work
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/005—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/005—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein
- G03C1/06—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein with non-macromolecular additives
- G03C1/38—Dispersants; Agents facilitating spreading
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/005—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein
- G03C1/46—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein having more than one photosensitive layer
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/74—Applying photosensitive compositions to the base; Drying processes therefor
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05C—APPARATUS FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05C9/00—Apparatus or plant for applying liquid or other fluent material to surfaces by means not covered by any preceding group, or in which the means of applying the liquid or other fluent material is not important
- B05C9/04—Apparatus or plant for applying liquid or other fluent material to surfaces by means not covered by any preceding group, or in which the means of applying the liquid or other fluent material is not important for applying liquid or other fluent material to opposite sides of the work
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/005—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein
- G03C1/06—Silver halide emulsions; Preparation thereof; Physical treatment thereof; Incorporation of additives therein with non-macromolecular additives
- G03C1/08—Sensitivity-increasing substances
- G03C1/10—Organic substances
- G03C1/12—Methine and polymethine dyes
- G03C1/14—Methine and polymethine dyes with an odd number of CH groups
- G03C1/18—Methine and polymethine dyes with an odd number of CH groups with three CH groups
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/76—Photosensitive materials characterised by the base or auxiliary layers
- G03C1/95—Photosensitive materials characterised by the base or auxiliary layers rendered opaque or writable, e.g. with inert particulate additives
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C1/00—Photosensitive materials
- G03C1/74—Applying photosensitive compositions to the base; Drying processes therefor
- G03C2001/7425—Coating on both sides
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03C—PHOTOSENSITIVE MATERIALS FOR PHOTOGRAPHIC PURPOSES; PHOTOGRAPHIC PROCESSES, e.g. CINE, X-RAY, COLOUR, STEREO-PHOTOGRAPHIC PROCESSES; AUXILIARY PROCESSES IN PHOTOGRAPHY
- G03C2200/00—Details
- G03C2200/52—Rapid processing
Definitions
- the present invention relates to a silver halide photographic light-sensitive material, in particular, a silver halide photographic light-sensitive material which does not incur disadvantages in the coating process, and allows super-rapid photographic processing.
- the diagnostic result should be notified to a case as soon as possible.
- the super-rapid processing however, often incurs disadvantages, such as (a) insufficient density or deterioration in sensitivity, contrast, and maximum density, (b) in sufficient fixing, (c) insufficient water rinsing of films, and (d) insufficient drying of films.
- the insufficient fixing or water rinsing can result in discoloration as a film is stored, and hence the deteriorated image quality.
- the term "super-rapid processing” means the photographic processing whose total duration is within a range of 20 to 60 seconds; within this duration, the leading edge of film is introduced into an automatic developing unit, and transferred via a dveloping bath, interface portion, fixing bath, interface portion, water-rinsing bath, interface portion, then a drying portion, and the same edge is eventually ejected from the drying portion, wherein the duration equals a quotient in sec. obtained by dividing a line transportation rate in m/sec. by a total length of processing line in m.
- the reason for why the periods associated with the interface portions should be included is well known in the photographic art; even in the interface portions, a gelatin layer in the photographic material contains a processing solution employed in a preceeding process and, accordingly, the photographic treatment substantially proceeds.
- the current X-ray photography requires a high-precision photographic technique involving smaller exposure dose. This need in turn necessitates the development of a photographic material being capable of providing a high-precision image with a smaller X-ray dosage, in other words, a more sensitive photographic material.
- the first object of the invention is to solve the above mentioned problems prior art incurs when the super-rapid processing with the total processing duration of 20 to 60 seconds is performed, in order to provide a silver halide photographic light-sensitive material which excels in the sensitivity, contrast, maximum density, fixing properties, drying properties and other properties.
- the second object of the invention is to provide a silver halide photographic light-sensitive material having a limited amount of gelatin and seldom incurring failures even in applying a coating solution which has a smaller surface tension.
- the third object of the invention is to provide a silver halide photographic light-sensitive material less possibly incurring scratch-induced blackening even if a smaller amount of gelatin is used.
- a silver halide photographic light-sensitive material comprising a support having the first photographic structural layer comprising one or more layers on a side of the support and the second photographic structural layer comprising one or more layers on the other side of the support, wherein at least one of the photographic structural layers comprises a silver halide light-sensitive emulsion layer, the total amount of gelatin contained in the photographic structural layer comprising the silver halide emulsion layer is within the range of from 2.25 g/m 2 to 3.15 g/m 2 , the uppermost layer of the photographic structural layer comprising the silver halide emulsion layer is formed by coating of a solution having a surface tension of from 15 to 26 dyn/cm, and the second photographic structural layer is coated and gelled simultaneously with coating and drying of the first photographic structural layer.
- the silver halide photographic light-sensitive material the invention contains a matting agent of which mattnesss is preferably 40 to 150 mmHg.
- the silver halide photographic light-sensitive material should be preferably processed with an automatic developing unit whose total processing time is 20 to 60 seconds.
- FIG. 1 is a cross sectional drawing illustrating a coating apparatus useful in embodying the invention, wherein the two-layer coating method using a slide hopper is used to continuously applying coating solutions on both surfaces of a support.
- FIG. 2 is a longitudinal cross section illustrating one example of air blower.
- FIG. 3 is a graph illustrating a pattern of controlling pAg while preparing various types of silver halide particles respectively involving various percentages of silver iodide.
- the term "outermost layer” literally means the upper outermost layer.
- such an outermost layer may be further coated with coating such as super cost which is applied, for example, by means of spray.
- the "outermost layer” of the invention may be either a light-sensitive layer or a non-light-sensitive layer.
- a support there is disposed, on at least one surface of a support, at least one silver halide emulsion layer.
- the support may have, on the other surface, either a light-sensitive silver halide layer or non-light-sensitive layer. If more than two silver halide emulsion layers on one surface of the support are formed, a non-light-sensitive layer may be provided between any of these emulsion layers. However, at least, the support should have on its both surfaces a light-sensitive silver halide emulsion layer and on the other surface a non-light-sensitive layer.
- the term “amount of gelatin” means the total amount of gelatin present in the light-sensitive and non-light-sensitive layers both on the light-sensitive layer surface of a support. If the support have a light-sensitive layer on both surfaces, the term “amount of gelatin” means the total amount of gelatin present on one specific surface.
- the term "light-sensitive layer” means a layer sensitive to light, for example, a light-sensitive silver halide emulsion layer.
- non-light-sensitive layer means a layer not sensitive to light, for example, a subbing layer, intermediate layer, protective layer, antihalation layer, filter layer or the like.
- a preferred silver halide photographic light-sensitive material has in the silver halide emulsion layer the silver halide particles whose average particle diameter is 0.30 to 1.50 ⁇ m, more specifically, 0.40 to 1.30 ⁇ m, and most specifically, 0.40 to 1.10 ⁇ m.
- a preferred silver halide photographic light-sensitive material has multi-layered silver halide particles which are substantially made of silver iodo-bromide, wherein the difference in average iodine contents between two arbitrary, independently uniform, adjacent layers, between two coating layers, or between the internal core and a coating layer, is more than 10 mol %, and the average iodine content in the outermost layer is less than 10 mol %, and the material has been chemically sensitized.
- Such multi-layered silver halide particles individually comprise an internal core coated with a layer of an arbitrary halide composition.
- the layer may comprise one layer, or more than two layers, for example, the lamination of three or four layers. However, the preferred number of layers is less than five.
- Silver halides useful as internal core and coating layers are silver bromide, silver iodo-bromide and silver iodide. However, any of such silver halides may involve a limited amount of silver chloride. To be more concrete, the silver halide may contain less than 10 mol %, more favorably, less than 5 mol % of silver chloride.
- each silver halide particle should be substantially made of silver bromide, or silver iodo-bromide containing less than 10% of iodide, and may contain less than several % of chlorine atoms.
- the preferred average iodide content in whole silver halide particles of the invention is less than 10 mol %, or, more specifically, less than 6 mol %.
- the iodide content in an X-ray photographic light-sensitive material, the iodide content sometimes worsens the problems such as development inhibition, infectious development and the like. Accordingly, in practice, the iodide content should be preferably limited below a specific level. In any cases, the method according to the invention decreases the stress fogging. However, because of the above reason, the preferred total iodide content in whole silver halide particles is less than 10 mol %, or, more specifically, less than 7 mol %, or, most specifically, less than 5 mol %.
- the core should preferably be made of a uniform solid solution.
- the condition of using a diffractometer is ⁇ r/r ⁇ 10, where the scanning rate of goniometer is ⁇ (deg/min), time constant is r(sec), and receiving slit width if r(mm).
- the preferred average iodine content is less than 40 mol %, in particular, 0 to 20 mol %.
- the preferred difference in average iodide contents between two adjacent layers is more than 10 mol %, and more specifically, more than 20 mol %, and most specifically, more than 25 mol %.
- the preferred silver iodide content in the coating layers other than the outermost coating layer is 10 to 100 mol %.
- an individual silver halide particle comprises more than three layers, and at the same time, if the coating layers are made of silver iodo-bromide, all the layers are preferably made of uniform silver iodo-bromide, though it is compulsory that these layers are made of uniform silver iodo-bromide.
- Such a coating layer or an internal core having high iodide content should be preferably present below the outermost layer, in the case of negative-type silver halide emulsion.
- the similar coating layer may be present either on or within the surface of individual silver halide particle.
- the preferred silver iodide content in the outermost coating layer of the silver halide particle is less than 10 mol %, in particular, 0 to 5 mol %.
- the iodide contents in the internal core and coating layers of individual silver halide particles which are used in embodying the invention may be determined by a method, for example, disclosed in "X-ray analysis with TEM/ATEM” Scanning Electron Microscopy (1977), by J. I. Goldstein and D. B. Williams, vol. I. IIT Research Institute, p. 651 (May, 1977).
- the internal core has the higher iodide content than the outer layer.
- a coating layer other than the outermost layer, or the internal core should preferably have the higher iodide content than the outermost layer.
- the present invention is advantageously applied to the chemically sensitized silver halide particles. This is because non-sensitized particles have extremely low sensitivity, and, naturally, seldom incurs scratch-induced fogging and pressure desensitization.
- the silver halide particles used in embodying the invention are whichever positive-type or negative-type.
- the preferred criterion of chemical sensitization is as follows; sensitivity corresponding to a point "fogging +0.1" in the optical density curve is more than 60% of optimum sensitization degree.
- the preferred criterion of chemical sensitization for the interior of individual particles is as follows; sensitivity corresponding to a point "fogging-0.1" in the optical density curve is more than 60% of optimum sensitization degree.
- the average particle size of silver halide particles used in the invention is expressed as the average length of edges on imaginary cubes whose volumes are equal to corresponding particles.
- the outermost layer of light-sensitive material is formed with a coating solution having a surface tension of less than 26 dyn/cm.
- a coating solution having a surface tension of less than 26 dyn/cm.
- an arrangement to incorporate at least one surfactant into the uppermost layer is available.
- a layer immediately below the uppermost layer may or may not contain a surfactant.
- Surfactants used respectively in the uppermost layer and the layer immediately below are either identical or different.
- the surface tension for a coating solution to form the uppermost layer is less than 26 dyn/cm.
- the lower limit it is advantageous to set the lower limit at 15 dyn/cm.
- nonionic surfactants such as saponin, alkylene oxide derivative, aliphatic esters of multivalent alcohols, alkyl esters of sugars, and others
- anionic surfactants having an acid group such as carboxy group, sulfo group, phospho group, sulfuric ester group, phosphoric ester group, or the like
- ampholytic surfactants such as amino acids, aminoalkyl sulfonic acids, aminoalkyl sulfuric esters, aminoalkyl phosphoric esters, alkylbetaines, amine oxides and the like.
- cationic surfactants including alkyl amine salts, aliphatic or aromatic quaternary ammonium salts, and heterocyclic quaternary ammonium salts of pyridinium or the like, and aliphatic or heterocyclic phosphonium salts, and aliphatic or heterocyclic sulfonium salts; fluorine-containing surfactants such as those containing polyoxyethylene group.
- alkylene oxide surfactant examples are disclosed, for example, in Japanese Patent Publication No. 9610/1976, DT-2648746, Japanese Patents Open to Public Inspection (hereinafter referred to as Japanese Patent O.P.I. Publications) Nos. 129623/1978, 89624/1979, 98235/1979, 208743/1983, 80848/1985 and 94126/1985.
- fluorine-containing surfactant examples include compounds disclosed in Japanese Patent Publications Nos. 9303/1972, 43130/1973, 25087/1977 and 1230/1982, Japanese Patent O.P.I. Publications Nos. 46733/1974, 16525/1975, 34233/1975, 32322/1976, 14224/1979, 111330/1979, 557762/1980, 19042/1981, 41093/1981 34856/1981, 11341/1982, 29691/1982, 64228/1982, 146248/1982, 14944/1981, 11945/1981, 196544/1983, 200235/1983, 109548/1975 and 136534/1982, U.S. Pat. Nos. 3,589,906, 3,775.126 and 4,292,402, RD-16630 and others, as well as compounds disclosed in Japanese Patent O.P.I. Publication No. 164738/1985.
- the preferred anionic surfactants not having a polyalkylene oxide are typified by the following 1 - 1 through 1 - 10. ##STR1##
- the preferred flourine containing surfactants are typified by the following 2 - 1 through 2 - 82. ##STR2##
- the examples of commercial fluorine containing surfactants include Unidyne manufactured by Daikin Kogyo Co., Ltd. and Florado manufactured by Sumitomo 3M.
- the particles employed in embodying the invention are hereinunder described.
- the size distribution of particles employed may be either small or large.
- the size distribution of silver halide particles within a photographic emulsion is arbitrarily selected, and the emulsion may be a monodisperse type.
- the "term-monodisperse” means a dispersion system where sizes of 95% of total particles correspond a range of less than ⁇ 60%, or, more favorably, less than ⁇ 40% of number average particle size.
- number average particle size is the number average diameter of the projected areas of silver halide particles.
- the silver halide particles in a photographic emulsion may have a regular crystal configuration such as cube, octahedron, tetradecahedron or dodecahedron, or an irregular configuration such as spheric and tabular ones, or a combination or any of these crystal configurations. Also, silver halide particles may simultaneously involve various crystal configurations.
- the silver halide particles may be any of the following crystals: combined silver halide crystals formed by bonding oxide crystals such as of PbO with silver halide crystals such as of silver chloride; epitaxially grown silver halide crystals (for example, on individual silver bromide crystals, silver chloride, silver iodo-bromide, silver iodide or the like is epitaxially grown); crystals comprising hexagonal or regular octagonal silver iodide particles overlapped with regular octagonal silver chloride crystals.
- the above regular silver halide particles may be incorporated into the emulsion.
- the latter type of particles should not preferably exceed 50% in terms of weight or number of particles.
- the total amount of silver halide particles involve at least 60 to 70 weight % of regular silver halide particles.
- the silver halide particles used in the silver halide emulsion are prepared in compliance with any of the neutral method, acid method, ammonium method, normal precipitation method, reverse precipitation method, double jet precipitation method, controlled double jet precipitation method, conversion method, core/shell method and the like disclosed in the literatures such as The Theory of the Photographic Process, 4th edition, by T. H. James, published from MacMillan (1977); Chimie et Physique Photographique, by P. Glfkides, published from Paul Montel (1967); Photographic Emulsion Chemistry, by G. F. Duffin, published from The Focal Press (1966); Making and Coating Photographic Emulsion, by V. L. Zelikman et al, published from The Focal Press (1964); and others.
- a triple jet precipitation method where soluble halides of different compositions, for example, soluble silver salt, soluble bromide and soluble iodide, are independently added, is also useful.
- a method to form particles in the presence of excess silver ions may be used.
- the controlled double jet method which keeps pAg level constant in the liquid phase where silver halide is formed, is also useful.
- silver halide solvents are useful: ammonium, potassium rhodate, ammonium rhodate and thioether compounds, disclosed for example in U.S. Pat. Nos. 3,271,157, 3,574,628, 3,704,130, 4,297,439 and 4,276,374; thionic compounds, disclosed for example in Japanese Patent O.P.I. Publications Nos. 144,319/1978, 82,408/1978 and 77,737/1980; amine compounds disclosed for example in Japanese Patent O.P.I. Publication No. 100,717/1979; and others.
- ammonium is advantageous for this purpose.
- More than two independently prepared silver halide emulsions may be mixed together to prepare one emulsion.
- These silver halide particles or silver halide emulsions should preferably contain at least one salt (soluble salt) of iridium, thallium, palladium, rhodium, zinc, nickel, cobalt, uranium, thorium, strontium, tungsten or platinum.
- the preferred amount of such a salt is 10 -6 to 10 -1 mol per mol Ag.
- the particles or emulsions contain at least one salt selected from those of thallium, palladium and iridium. These salts may be either independently or combinedly used. The timing of adding such a salt is arbitrarily selected. By incorporating such a salt, various effects may be resulted; for example, improvement of flash exposure characteristics, prevention of pressure desensitization, prevention of fading of the latent image, and sensitization.
- the preferred example is such that the pAg level of parent solution containing protective colloid, while particles are allowed to grow, as mentioned above, prior to the chemical sensitization, is at least 10.5.
- the parent solution is subjected at least once to an atmosphere of pAg level more than 11.5 with excess bromine ions.
- This arrangement increases the (111) faces and makes individual particles more spheric, thus further enhancing the effects of the present invention.
- the (111) faces of particles should preferably account for more than 5% of the total surface area of particles.
- the increase in (111) faces should be preferably more than 10%, in particular, 10 to 20%.
- the above-mentioned pAg level should be preferably reached after approximately two thirds of the total amount of silver have been added and before the desalination process which is usually performed prior to the chemical sensitization. This is because this arrangement is useful in providing a monodisperse emulsion having a smaller particle size distribution.
- the ripening in an atmosphere having the pAg level of more than 10.5 is preferably performed for more than two minutes.
- Controlling the pAg in this manner increases the (111) face more than 5%, and individual particles becomes more spheric, thus providing advantageous particles whose (111) faces account for more than 5% of total surface areas of particles.
- noodle water-rinsing method where the removal is effected by promoting the gelation of gelatin
- flocculation method which uses an inorganic salt, anionic surfactant, anionic polymer such as polystyrene sulfonate or gelatin derivative such as acyl gelatin, carbamoyl gelatin.
- anionic surfactant anionic polymer such as polystyrene sulfonate or gelatin derivative such as acyl gelatin, carbamoyl gelatin.
- the silver halide emulsion is preferably chemically sensitized, but it may not be sensitized.
- chemical sensitizing the emulsion for instance, the methods described in Die Unen der Photographischen Saw mit Silberhalogenieden, Akademishe Verlagegeselshaft, 1968, p.67-734 can be used.
- the silver halide emulsion useful in the invention may be optically sensitized with a dye known in the photographic art as a sensitizing dye so that it may be particularly sensitive in a required wavelength range.
- Sensitizing dyes may be independently used, or otherwise, more than two of them may be combinedly used.
- the emulsion may contain a supersensitizer which is a dye not providing spectral sensitizing function or a compound not absorbing visible light but enhances the sensitizing action of sensitizing dye.
- sensitizing dye used in the blue-sensitive silver halide emulsion layer or as a sensitizing dye used in the green-sensitive silver halide emulsion layer, or as a red-sensitive silver halide emulsion layer, various dyes are available. These dyes may be independently used, or otherwise, various combinations of dyes may be used. The combination of sensitizing dyes is often used especially for the supersensitizing purpose.
- the aromatic organic acid-formardehyde condensation products for example, those disclosed in U.S. Pat. No. 3,437,510
- cadmium salts azaindene compound, and aminostylbene compounds having a nitrogen-containing heterocyclic substituent.
- One preferred embodiment of the invention is provided by incorporating, into a light-sensitive silver halide emulsion layer, at least one sensitizing dye selected from a group of compounds which are expressed by the following formula [I], [II] or [III].
- R 1 , R 2 and R 3 independently represent an alkyl group, alkenyl group or aryl group each of which is allowed to have a substituent, and at least one of R 1 and R 2 is a sulfoalkyl group or carboxyalkyl group.
- X 1 - represents an anion
- Z 1 and Z 2 independently represent a group of non-metal atoms necessary to complete a substituted or unsubstituted carbon ring
- n represents 1 or 2 (if forming an intramolecular salt, n represents 1)].
- R 4 and R 5 independently represent an alkyl group, alkenyl group or aryl group each of which is allowed to have a substituent, and at least one of R 4 and R 5 is a sulfoalkyl group or carboxyalkyl group.
- R 6 represents a hydrogen atom, lower alkyl group or aryl group.
- X 2 31 represents an anion
- Z 1 and Z 2 independently represent a group of non-metal atoms necessary to complete a substituted or unsubstituted carbon ring, and n represents 1 or 2, if forming an intramolecular salt, n represents 1].
- R 7 and R 8 independently represent a lower alkyl group each of which may have a substituent
- R 9 and R 10 independently represent a lower alkyl group, a hydroxyalkyl group, a sulfoalkyl group or a carboxyalkyl group
- X 3 - is an anion
- Z 1 and Z 2 independently represent a group of non-metallic atoms necessary to complete a substituted or unsubstituted carbon ring
- n is an integer of 1 or 2 provided that n is 1 when an intramolecular salt is formed.
- the carbon ring Z 1 or Z 2 forms should be preferably an aromatic ring such as a substituted or unsubstituted benzene or haphthalene ring.
- the total amount of adding compounds expressed by any of the above formulas [I] through [III] is within a range of 50 mg to 1200 mg per mol silver halide. However, the amount of 100 mg to 1000 mg is particularly advantageous.
- the timing for adding the compound expressed by any of the above formulas [I], [II] and [III] is arbitrarily selected from any time points within the preparation of light-sensitive material.
- the compound is incorporated into the material prior to the chemical ripening, during the chemical ripening, after the chemical ripening or before the coating process.
- Into the photographic emulsion used in the invention may be incorporated various compounds in order to prevent the fogging during the preparation, storage and photographic processing of the light-sensitive material, or to ensure stable photographic performance.
- a plasticizer may be added to the silver halide emulsion layer and/or other hydrophilic colloid layer of the light-sensitive material according to the invention.
- trimethylolpropane is advantageous.
- the preferred amount of addition per amount of gelatin is 0.01 to 100 weight %, in particular, 0.1 to 100 weight %, or more specifically, 0.1 to 10 weight %.
- various compounds may be incorporated into the photographic emulsion used in embodying the invention.
- a water-soluble dye may be added for various purposes; for example, as a filter dye to a hydrophilic colloid layer, or for the prevention of irradiation and halation.
- the light-sensitive material of the invention contains in a hydrophilic colloid layer a dye, ultraviolet absorbent and the like, these compounds may be mordanted with a cationic polymer or the like.
- the dyes useful for this purpose are those disclosed in "Absorbing and Filter dyes" in Research Disclosure, vol. 176, pp. 23-26.
- the photographic emulsion layer in the photographic light-sensitive material of the invention may contain, for example, any of the following compounds: polyalkylene oxide or ether derivative, ester derivative or amine derivative thereof; thioether compound, thiomorpholine, quaternary ammonium chloride, urethane derivative, urea derivative, imidazole derivative, 3-pyrazolidone and the like.
- Gelatin is advantageous as a binder or protective colloid which may be used in the emulsion layer and intermediate layer of the light-sensitive material of the invention.
- another hydrophilic colloid may be independently, or together with gelatin, used.
- the photographic light-sensitive material of the invention may, in the photographic emulsion layer and other hydrophilic colloid layers, contain an inorganic or organic hardener.
- the photographic light-sensitive material of the invention may, in the photographic emulsion layer and other hydrophilic colloid layers, contain a water-soluble or slightlysoluble synthetic polymer dispersion.
- the protective layer is made of a hydrophilic colloid, thereby the useful hydrophilic colloid is selected from the previously mentioned examples.
- the protective layer may comprise either a single layer or a plurality of layers.
- a matting agent and/or lubricant may be added to the emulsion layer or protective layer of the silver halide photographic light-sensitive material of the invention.
- One example of silver halide photographic light-sensitive material embodying the invention contains a matting agent, and the mattness is 40 to 150 mmHg.
- the term "mattness” means a value expressed in mmHg which is determined under a specific condition by measuring a suction force on an unprocessed light-sensitive material (the so-called raw film) which has been treated to provide a constant humidity for three hours under 23° C. and 48%Rh. The larger the value is, the greater the degree of mattness.
- the Smoostar manufactured by Toei Denshi Kogyo Co., Ltd. was used.
- a matting agent should be contained preferably in the outermost layer of light-sensitive material or a layer functioning as the outermost layer, or a layer in the vicinity of outermost layer, and in a layer functioning as a protective layer.
- the preferred amount of added matting agent is 10 to 500 mg/m 2 , in particular, 20 to 300 mg/m 2 , or more specifically, 20 to 200 mg/m 2 per one side of the light-sensitive material. Additionally, an identical type of, or different types of matting agent may be added to more than two layers. In this case, a layer to contain the matting agent may be arbitrarily selected from the emulsion layer and protective layer, as well as the subbing layer and intermediate layer which are provided according to a specific requirement.
- the size distribution of particles of matting agent used in the invention may be either small or large, however, the use of monodisperse matting agent is advantageous.
- the "monodisperse matting agent” means a matting agent in which the quantity of particles whose diameters being within a range of ⁇ 20% of average particle size accounts for 90% of the whole particles.
- the type of matting agent is arbitrarily selected, for example, from the known agents.
- the useful matting agent comprises water-insoluble organic or inorganic fine particles with an arbitrarily particle size.
- the agent with a particle size of 1 ⁇ m to 10 ⁇ m is used.
- organic compound examples include as follows: water-dispersion vinyl polymers such as polymethyl acrylate, polymethyl methacrylate, polyacrylonitrile, acrylonitrile- ⁇ -methylstyrene copolymer, polyvinyl acetate, polyethylene carbonate and polytetrafluoroethylene; cellulose derivatives such as methyl cellulose, ethyl cellulose, cellulose acetate and cellulose acetate propionate; starch derivatives such as carboxy starch, carboxy nitrophenyl starch and urea-formadehyde-starch reaction product; gelatin hardened with a known hardener; hardened gelatin which are formed into hollow micro-capsules by hardening with coacervation; and others.
- water-dispersion vinyl polymers such as polymethyl acrylate, polymethyl methacrylate, polyacrylonitrile, acrylonitrile- ⁇ -methylstyrene copolymer, polyvinyl acetate, polyethylene carbonate and polytetra
- organic compound examples include silicon dioxide, titanium dioxide, magnesium dioxide, aluminum oxide, barium sulfate and calcium carbonate; silver chloride and silver bromide both being desensitized with a known method; glass, diatomaceous earth and others. Any of the above matting agents may be used as mixed with a different type of material according to a specific requirement.
- the photographic light-sensitive material of the invention may contain various additives in compliance with a requirement.
- a dye, development accelerator, fluorescent whitening agent, color-fog restrainer, ultraviolet absorbent and the like More specifically, those useful for this purpose are disclosed in Research Disclosure, vol. 176, pp. 22-31 (RD-17643, 1978).
- the silver halide photographic light-sensitive material of the invention may; be provided with an anti-halation layer, intermediate layer, filter layer and others.
- the layers including the photographic emulsion layer are formed by coating on a single side or both sides of a flexible support which is usually employed in a photographic light-sensitive material.
- the support may be colored with a dye or pigment. To shield light, the support may be provided with dark shade.
- the surface of a support is usually subbed to ensure better adherence to a photographic emulsion layer and the like.
- the surface of a support may be subjected to corona discharge, ultraviolet irradiation, flame treatment or the like before or after the subbing treatment. More specifically, the treatments to be used are disclosed in "Supports" in Research Disclosure, vol. 176, p. 25.
- the hydrophilic colloid layers including the photographic emulsion layer are formed by coating methods on the support or another layer.
- the useful coating methods include the dip coating method, roller coating method, curtain coating method, extrusion coating method and others. More specifically, the applicable methods are disclosed in "Coating Procedures" in Research Disclosure, vol. 176, pp. 27-28.
- FIG. 1 illustrates one example of coating apparatus suitable for coating process for the silver halide light-sensitive material of the invention, wherein a coater and an air blower substantially opposing to each other are disposed across a continuously fed support, thereby the position of support is maintained by means of air blowing from the air blower onto the support while the coater is applying a coating solution.
- FIG. 1 is a longitudinal cross section of a coating apparatus, wherein a two-layer coating method by a slide hopper is exercised to continuously apply coating solutions for photographic structural layers onto both sides of a support.
- FIG. 2 is a longitudinal cross section illustrating one example of air blower associated with the coating apparatus.
- the support 2 is passed through a cool air zone 8.
- the cool air is blown onto the coated surface 4 via a slit plate or a group of small holes 7.
- the other surface of support 2 not coated should be contacted with an array of rollers 6 which are disposed within a central box 5 and in which the rollers are arranged at 2 to 3 mm intervals, and that the suction force is exerted from behind the array of rollers 6 so as to enlarge the contact area between the array of rollers 6 and the support 2.
- an air blower 3' one side the support 2 already provided with a gel layer on the other side is formed a layer 11 by means of a coater 1' which is disposed as opposed to the air blower 3' across the support 2.
- the air blower 3' may be variously configured. However, a rollerconfigured blower, which appears to be used most widely because it will allow easy manufacturing procedure, is described below.
- the air blower 3' having a hollow roller constitution has, in its outer shell serving as the non-contact supporting portion, a plurality of through holes 10 to eject air.
- the air supplied into the interior of the roller is blown from the external circumferential surface of the roller 9 onto the gel layer 4 via the through holes 10, in order to exert lifting force onto the support 2 on the non-contact basis.
- the fluctuation in thickness of formed emulsion layer whether it is wet or dry should be less than ⁇ 1%. Accordingly, it is necessary that the gap or distance of between the tip of coater 1' and the surface on the support 2 to be coated with an emulsion should be maintained as constant as possible.
- the allowable fluctuation in the gap is preferably within several, or, 10 ⁇ at the maximum.
- an air blower 3' comprises a hollow roller having through holes 10
- the means to control the fluctuation in distance of floatation it is possible to set not only a specific value for the ratio between the supporting static pressure (back pressure) and source pressure at a specific value between 1/10 and 1/1000 but the distance of floatation at the area in contact with a coating solution at a specific value between 20 ⁇ m and 500 ⁇ m, by deliberately designating the diameter d (FIG. 2) and length l (FIG.
- the correlation between the support and the amount of blown air should be preferably regulated to satisfy W 2 ⁇ Q ⁇ 5 ⁇ lO 5 , where W is the width of support (cm), Q is the amount of blown air per unit area (Nml/min ⁇ cm 2 )
- the silver halide photographic light-sensitive material of the invention is typically used as an X-ray light-sensitive material, lith light-sensitive material, monochromatic film, color negative light-sensitive material color reversal light-sensitive material or color printing paper, or for the colloid transfer process, silver salt diffusion transfer process, dye transfer process, silver dye bleaching process, or as a printout sensitive material, light-sensitive material for thermal developing, or the like.
- An ordinary exposure method may be used to obtain a photographic image with the light-sensitive material of the invention.
- the light-sensitive material of the invention may be photographically processed with any of the methods and various processing solutions disclosed, for example, in Research Disclosure, Vol. 176, pp. 25-30, (RD-17,643).
- the photographic process may be a photographic process to form either a silver image (monochromatic photographic process) or a dye image (color photographic process), in accordance with a specific requirement.
- the processing temperature is usually selected from a range of 18° C. to 50° C. However, the temperature may be lower than 18° C. or higher than 50° C.
- the photographic emulsion layer of the photographic light-sensitive material of the invention may contain a dye forming coupler which is a compound being capable of forming a dye, in the course of color developing, by oxidization-coupling with an aromatic primary amine developing agent (for example, a phenylenediamine derivative, aminophenol derivative and the like).
- a dye forming coupler which is a compound being capable of forming a dye, in the course of color developing, by oxidization-coupling with an aromatic primary amine developing agent (for example, a phenylenediamine derivative, aminophenol derivative and the like).
- the similar emulsion layer may contain a non-color DIR coupling compound, which releases development restrainer, whose coupling-reaction product has no color.
- the silver halide photographic light-sensitive material of the invention may contain, as an anti-fogging agent, a hydroquinone derivative, aminophenol derivative, gallic acid derivative, ascorbic acid derivative or the like.
- the silver halide photographic light-sensitive material of the invention may contain in the hydrophilic colloid layer an ultraviolet absorbent.
- an anti-fading agent may be also used.
- silver iodo-bromide emulsion E - 1 containing 2.0 mol % silver iodide was prepared by the full-ammonia normal precipitation method.
- the average particle size of the silver iodide in the emulsion was 1.10 ⁇ m.
- Chloroauric acid, sodium thiosulfate and ammonium thiocyanate were added to the silver iodo-bromide emulsion E - 1 in order to perform the optimized gold/sulfur sensitization, then the emulsion was stabilized with 4-hydroxy-6-methyl-1,3,3a-7-tetrazaindene.
- the two layers were simultaneously formed on one face (front side) of a support made of polyester film having a subbing layer; one layer is a protective layer which containing a hardener, and the other is the silver halide emulsion layer disposed between the protective layer on the support. Then, the layers were allowed to set the gel, and dried, then wound up with a tension of 10.5 kg/36 cm.
- the other face of support (rear face) was coated in compliance with the conditions identical to those of the front face, then the two-layer coat was allowed to gelate and dried. Thus, samples No. 1 through No. 30 were prepared.
- the amount of applied silver in each of the prepared samples was at a rate of 54 mg/cm 2 , and the amount of hardener was regulated so that the melting time of approximately 7 minutes was attained.
- melting time means the duration where a sample of silver halide photographic light-sensitive material cut into 1 cm by 2 cm chip is immersed into 1.5 aqueous sodium hydroxide solution having a constant temperature of 50° C. and the emulsion layer eventually starts to melt.
- the number of coating defects for example, coating streak, coating mottle and the like
- evaluation was made using five grades, that is, 1 (poor) through 5 (excellent).
- the grades 3 through 5 satisfy the criteria for practical use, while the grades 1 and 2 fail to satisfy the similar criteria.
- the sensitivity was measured in the following manner; a sample was sandwiched between two optical wedges which are aligned with each other so that the density gradients constitute the symmetry relative to plane, thereby both faces were simultaneously exposed for 1/12.5 seconds with a light source having a color temperature of 5400° K.
- the photographic process comprised the following steps and employed a roller transporting type, automatic developing machine.
- the total processing time was 45 seconds.
- the developer used was XD-90, and the fixer used was XF, both manufactured by Konishiroku Photo Industry Co., Ltd.
- Tables 1-1, 1-2 and 2 demonstrate that one preferred example embodying the invention excels in coating properties (especially, the similar properties with the rear face), sensitivity and dying properties, and, therefore, that the super-rapid processing is feasible.
- the invention provides the processing capacity twice that of a conventional system, with the processing time reduced to the half, while maintaining the sensitivity of the conventional system.
- 3.2N aqueous ammoniac silver ion solution as well as aqueous halide solution were added, with the controlled flow rate, by means of the double jet precipitation method, in order to sequentially form a plurality of layers, each having a specific silver iodide content, onto individual core particles.
- the pAg was adjusted to 7.3, and the pH to 9.7.
- a layer having 0 mol % of silver iodide was formed by controllingly keeping the level of pAg at 9.0 or more than 9.0, as shown in FIG. 3. More specifically, as FIG.
- the emulsion prepared was monodisperse silver iodo-bromide emulsion in which the average size of silver halide particles was 0.85 ⁇ m, and the ratio of silver iodide to the total amount of silver halide was 2 mol %.
- the obtained emulsion E - 2 was subjected to the optimum sensitization with gold and sulfur in a manner identical to that of Example - 1, then stabilized with 4-hydroxy-6-methyl-1, 3,3a-7-tetrazaindene.
- the following sensitizing dye (I) was added to the emulsion at a ratio of 200 mg per mol silver halide.
- a protective layer containing a hardner and the emulsion layer were formed by coating in a manner identical to that of Example 1, to prepared the samples No. 61 through 120. With the samples Nos. 61 through 90, the front and rear faces were unsuccessively coated and dried; while both faces of the samples Nos. 91 through 120 were successively coated and simultaneously dried.
- emulsions E - 3 through E - 7 respectively having multi-layered silver halide particles is hereinunder described.
- the emulsion obtained was a monodisperse emulsion containing octahedral particles with an average size of 1.05 ⁇ m.
- the emulsion obtained was a monodisperse emulsion containing octahedral particles with an average size of 1.10 ⁇ m.
- the emulsion was designated E - 3.
- octahedral silver iodo-bromide emulsions containing silver iodide respectively at the rate of 5 mol %, 10 mol %, 20 mol % and 30 mol % were prepared by varying the ratio between potassium iodide and potassium bromide, by varying the core diameters in order to make constant the average content of silver iodide after the shell was formed onto individual cores, and by controlling the addition rate in the early phase of mixing in order to make identical the sizes of resultant particles.
- the emulsions each being a monodisperse emulsion having octahedral particles of an average size 1.10 ⁇ m. These emulsions were designated E - 4, E - 5, E - 6 and E - 7.
- each sample was subjected to moisture control with a temperature of 23° C. and humidity of 55% RH for four hours, then scratched using a 0.3 mm radius sapphire stylus with a continuously varied load, and developed, thereby a minimum load (in gram) being capable of inducing the fogging was determined.
- Table 4 lists the results. As can be understood from Table 4, when compared to particles in which the difference in iodide contents between the core and shell is less than 10 mol %, the particles in which the similar difference is more than 10 mol % are more resistant to the scratch-induced fogging with a smaller amount of gelatin, and provide excellent sensitivity.
- the second coating layer was formed onto individual particles, in a manner identical to that of E - 3, except that the pAg was 9.0.
- the monodisperse core/shell emulsions containing cubic silver iodo-bromide particles with an average size of 0.80 ⁇ m were prepared. These emulsions were designated E - 8, E - 9, E - 10 and E - 11.
- the average silver iodide content of each emulsion was 3 mol %.
- Example 2 These emulsion were chemically sensitized in a manner identical to that of Example 1, then to the emulsions was added the sensitizing dye (I) which was used in Example 2, or the following sensitizing dye (II), or the following sensitizing dye (III) serving as a comparison dye, thereby each emulsion was simultaneously applied to both faces of a support in a manner identical to that of Example 1.
- the samples Nos. 131 through 146 were prepared.
- a sample using the particles in which layers the difference in iodide contents between the core and shell is more than 10 mol % is more resistant, especially when the amount of gelatin is smaller, to the scratchinduced fogging and provides excellent sensitivity, even if the sample is a system having a sensitizing dye.
- the monodisperse emulsion of cubic particles of silver iodo-bromide containing particles of 2.0 mol % of silver iodobromide with an average size of 0.20 ⁇ m was prepared by the double jet precipitation method.
- core particles were grown up in the following manner.
- the first coating layer was formed onto individual particles; this layer contained 30 mol % of silver iodide.
- the second coating layer of pure silver bromide was formed onto individual particles in the emulsion, by adding ammoniac silver nitrate solution and potassium bromide solution with the double jet precipitation method.
- the monodisperse emulsion containing cubic silver iodo-bromide particles with an average size of 0.57 ⁇ m was prepared, and designated E - 12.
- the average silver iodide content was 2.5 mol %.
- the sensitizing dye (I) whose structure is described later was added to the emulsion E - 12 at a rate of 520 mg/molAg.
- To the emulsion was further added gold thiocyanate and sodium thiosulfate for the optimum gold/sulfur sensitization, then 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene was added for stabilization, thereby the gelatin content was adjusted as listed in Table 6.
- the coating solutions for emulsion layer were prepared.
- a monodisperse matting agent with an average particle size of 4 ⁇ m was used to attain mattness specified in Table 6 (for this purpose, polymethyl methacrylate PMMA was used), thereby the gelatin content was adjusted as specified in Table 6, then a compound described later and serving as a hardener was added.
- the coating solution for a protective layer was prepared.
- the dual layer consisted of an emulsion layer (viscosity, 15 cp; surface tension, 34 dyn/cm; coating thickness, 47 ⁇ m), directly upon the support, as well as the protective layer (viscosity, 10 cp; surface tension, 25 dyn/cm; coating thickness 18 ⁇ m) which being the outer layer.
- the samples No. 151 through 181 were prepared.
- the added amount of silver salt incorporated into each sample was, in both faces, 4.5 g/m 2 .
- the developer used was XD-90, and the fixer used was XF, both manufactured by Konishiroku Photo. Industry Co. LTD.
- the drying properties were evaluated in the following manner. After being subjected to the above 45 seconds automatic developing, and drying a sample was examined for handling touch, degree of sticking with another sample, and other items, thereby the performance was expressed using five grades, that is, 1 (poor) through 5 (excellent). The grades 3 through 5 satisfy the criteria for practical use, while the grades 1 and 2 fail to satisfy the similar criteria. Additionally, to determine the sensitivity with the conventional 90 seconds treatment, some of the samples were subjected to the process with the above-mentioned 45 seconds automatic developing machine whose line speed being reduced to 1/2 of the original
- each sample was evaluated in the following manner. Three sheets of a specific sample, respectively cut into 15 cm by 15 cm size, were first controllingly moistened under the conditions of 23° C. and 55% RH for siz hours. After being sandwiched with sheets of paper or cardboard and vacuum-sealed under specified conditions, each set of sample sheets was allowed to stand for three days at a temperature of 55° C. Then, with each sample sheet, the degree of sticking was evaluated using the intensity, area and the like of sticking as criteria, and the performance was represented by the five grades, that is, 1 (poor) through 5 (excellent). The grades 3 through 5 satisfy the criteria for practical use, while the grades 1 and 2 fail to satisfy the similar criteria.
- the matt pressure fogging was evaluated in the following manner.
- the sample developed without being subjected to exposure was evaluated with human vision, thereby the degree, intensity and number of fogs occurring around matting particles were represented by five grades, that is, 1 (poor) through 5 (excellent).
- the grades 3 through 5 satisfy the criteria for practical use, while the grades 1 and 2 fail to satisfy the similar criteria.
- a sample of the invention is highly sensitive (100 to 160), and excels in terms of the drying property, scratch-induced fogging, sticking, mattpressure fogging and the like (grades range from 3 to 5), and, apparently, suitable for the super-rapid processing. Furthermore, it is apparent that, when compared to the samples treated with the conventional 90 seconds process, a sample according to the invention permits a processing time, which is the half of the conventional processing time, and enables the processing capacity twice as large, though having sensitivity comparable to or better than a conventional system or sample.
Landscapes
- Chemical & Material Sciences (AREA)
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Spectroscopy & Molecular Physics (AREA)
- Silver Salt Photography Or Processing Solution Therefor (AREA)
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP26229586 | 1986-11-04 | ||
JP61-262295 | 1986-11-04 | ||
JP61-298499 | 1986-12-15 | ||
JP61298499A JP2613378B2 (ja) | 1986-12-15 | 1986-12-15 | 超迅速処理可能なハロゲン化銀写真感光材料 |
Publications (1)
Publication Number | Publication Date |
---|---|
USH674H true USH674H (en) | 1989-09-05 |
Family
ID=26545489
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US07/116,229 Abandoned USH674H (en) | 1986-11-04 | 1987-11-03 | Silver halide photographic light-sensitive material capable of super-rapid processing |
Country Status (3)
Country | Link |
---|---|
US (1) | USH674H (fr) |
EP (1) | EP0267019B1 (fr) |
DE (1) | DE3751257T2 (fr) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5153112A (en) * | 1988-09-05 | 1992-10-06 | Konica Corporation | Method of processing silver halide photographic materials |
USH1263H (en) | 1989-02-07 | 1993-12-07 | Konica Corporation | Image forming method and apparatus |
US5516627A (en) * | 1994-02-28 | 1996-05-14 | Konica Corporation | Method of processing silver halide light-sensitive photographic material |
US5576155A (en) * | 1994-10-07 | 1996-11-19 | Sterling Diagnostic Imaging, Inc. | Fast-processing photographic recording material for medical radiography |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3852089T2 (de) * | 1987-11-16 | 1995-06-01 | Konishiroku Photo Ind | Photographisches lichtempfindliches Silberhalogenidmaterial und Verfahren zu dessen Herstellung. |
JP2835344B2 (ja) * | 1988-10-25 | 1998-12-14 | コニカ株式会社 | 超迅速処理可能なcrt撮影用ハロゲン化銀写真感光材料 |
JP2821506B2 (ja) * | 1990-04-05 | 1998-11-05 | コニカ株式会社 | ハロゲン化銀写真感光材料の製造方法 |
JP2704457B2 (ja) * | 1990-09-20 | 1998-01-26 | 富士写真フイルム株式会社 | ハロゲン化銀写真用感光材料 |
JPH05289243A (ja) * | 1992-04-15 | 1993-11-05 | Konica Corp | ハロゲン化銀写真感光材料及び画像形成方法 |
EP0620483A1 (fr) * | 1993-04-13 | 1994-10-19 | Agfa-Gevaert N.V. | Traitement de films radiographiques industriels à l'halogénure d'argent |
DE69308014T2 (de) * | 1993-04-13 | 1997-08-14 | Agfa Gevaert Nv | Photographische industrielle Silberhalogenid-Röntgenfilme |
EP0620482A1 (fr) * | 1993-04-13 | 1994-10-19 | Agfa-Gevaert N.V. | Méthode de traitements de films radiographiques à l'halogénure d'argent pré-durcis |
FR2725536B1 (fr) * | 1994-10-05 | 1999-01-22 | Kodak Pathe | Procede d'enduction photographique |
US5576156A (en) * | 1995-05-22 | 1996-11-19 | Eastman Kodak Company | Low crossover radiographic elements capable of being rapidly processed |
Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3545971A (en) | 1966-06-28 | 1970-12-08 | Eastman Kodak Co | Rapid processing of photographic x-ray film |
US3754924A (en) | 1970-06-04 | 1973-08-28 | Agfa Gevaert Nv | Photographic silver halide element with an antistatic outer layer comprising a fluorinated surfactant and a polymethacrylate matting agent |
US3843368A (en) | 1971-10-08 | 1974-10-22 | Fuji Photo Film Co Ltd | Silver halide photographic light-sensitive element |
US4030924A (en) | 1967-10-11 | 1977-06-21 | Agfa-Gevaert N.V. | Method of producing photographic images |
US4272616A (en) | 1978-06-07 | 1981-06-09 | Fuji Photo Film Co., Ltd. | Photographic radiation-sensitive materials having improved antistatic property |
US4292402A (en) | 1979-02-28 | 1981-09-29 | Agfa-Gevaert, N.V. | Light-sensitive silver halide materials containing fluorine-containing surfactants |
US4409322A (en) | 1980-12-19 | 1983-10-11 | Konishiroku Photo Industry Co., Ltd. | Silver halide photosensitive material |
US4426445A (en) | 1980-05-07 | 1984-01-17 | Fuji Photo Film, Co., Ltd. | Silver halide photographic light-sensitive material |
US4659654A (en) | 1984-09-28 | 1987-04-21 | Konishiroku Photo Industry Co., Ltd. | Silver halide photographic light-sensitive emulsion |
US4675278A (en) | 1984-08-07 | 1987-06-23 | Fuji Photo Film Co., Ltd. | Silver halide photographic light-sensitive materials |
Family Cites Families (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5879566A (ja) * | 1981-11-04 | 1983-05-13 | Konishiroku Photo Ind Co Ltd | 塗布方法およびその装置 |
JPS6052415B2 (ja) * | 1982-01-12 | 1985-11-19 | コニカ株式会社 | 放射線用ハロゲン化銀写真感光材料 |
US4508764A (en) * | 1982-12-14 | 1985-04-02 | E. I. Du Pont De Nemours And Company | Coating process employs surfactants |
JPS59149357A (ja) * | 1983-02-15 | 1984-08-27 | Konishiroku Photo Ind Co Ltd | ハロゲン化銀写真感光材料 |
JPS61116349A (ja) * | 1984-11-11 | 1986-06-03 | Konishiroku Photo Ind Co Ltd | X線用写真感光材料 |
-
1987
- 1987-11-03 US US07/116,229 patent/USH674H/en not_active Abandoned
- 1987-11-04 EP EP87309756A patent/EP0267019B1/fr not_active Expired - Lifetime
- 1987-11-04 DE DE3751257T patent/DE3751257T2/de not_active Expired - Lifetime
Patent Citations (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3545971A (en) | 1966-06-28 | 1970-12-08 | Eastman Kodak Co | Rapid processing of photographic x-ray film |
US4030924A (en) | 1967-10-11 | 1977-06-21 | Agfa-Gevaert N.V. | Method of producing photographic images |
US3754924A (en) | 1970-06-04 | 1973-08-28 | Agfa Gevaert Nv | Photographic silver halide element with an antistatic outer layer comprising a fluorinated surfactant and a polymethacrylate matting agent |
US3843368A (en) | 1971-10-08 | 1974-10-22 | Fuji Photo Film Co Ltd | Silver halide photographic light-sensitive element |
US4272616A (en) | 1978-06-07 | 1981-06-09 | Fuji Photo Film Co., Ltd. | Photographic radiation-sensitive materials having improved antistatic property |
US4292402A (en) | 1979-02-28 | 1981-09-29 | Agfa-Gevaert, N.V. | Light-sensitive silver halide materials containing fluorine-containing surfactants |
US4426445A (en) | 1980-05-07 | 1984-01-17 | Fuji Photo Film, Co., Ltd. | Silver halide photographic light-sensitive material |
US4409322A (en) | 1980-12-19 | 1983-10-11 | Konishiroku Photo Industry Co., Ltd. | Silver halide photosensitive material |
US4675278A (en) | 1984-08-07 | 1987-06-23 | Fuji Photo Film Co., Ltd. | Silver halide photographic light-sensitive materials |
US4659654A (en) | 1984-09-28 | 1987-04-21 | Konishiroku Photo Industry Co., Ltd. | Silver halide photographic light-sensitive emulsion |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5153112A (en) * | 1988-09-05 | 1992-10-06 | Konica Corporation | Method of processing silver halide photographic materials |
USH1263H (en) | 1989-02-07 | 1993-12-07 | Konica Corporation | Image forming method and apparatus |
US5516627A (en) * | 1994-02-28 | 1996-05-14 | Konica Corporation | Method of processing silver halide light-sensitive photographic material |
US5576155A (en) * | 1994-10-07 | 1996-11-19 | Sterling Diagnostic Imaging, Inc. | Fast-processing photographic recording material for medical radiography |
Also Published As
Publication number | Publication date |
---|---|
DE3751257D1 (de) | 1995-05-24 |
EP0267019B1 (fr) | 1995-04-19 |
EP0267019A2 (fr) | 1988-05-11 |
EP0267019A3 (en) | 1989-07-19 |
DE3751257T2 (de) | 1995-11-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US4683192A (en) | Silver halide photographic emulsions and process for producing them | |
USH674H (en) | Silver halide photographic light-sensitive material capable of super-rapid processing | |
EP0178097B1 (fr) | Emulsion photographique à l'halogénure d'argent sensible à la lumière | |
JP2004309806A (ja) | ハロゲン化銀写真感光材料 | |
JPH0353619B2 (fr) | ||
EP0112162B2 (fr) | Matériel photographique photosensible aux halogénures d'argent | |
JPH0452449B2 (fr) | ||
US4604339A (en) | Method of developing silver halide photographic light-sensitive material | |
US4873182A (en) | Light-sensitive silver halide photographic materials and process for incorporating hydrophobic photographic additives into hydrophilic colloid compositions | |
EP0176325B1 (fr) | Matériau photographique couleur à l'halogénure d'argent sensible à la lumière | |
EP0577138B1 (fr) | Matériau photographique à l'halogénure d'argent | |
JP2613378B2 (ja) | 超迅速処理可能なハロゲン化銀写真感光材料 | |
EP0295439B1 (fr) | Matériaux photographiques à l'halogénure d'argent | |
EP0302528B1 (fr) | Procédé pour la préparation d'un matériau photographique à l'halogénure d'argent | |
EP0239363B1 (fr) | Matériau photographique à l'halogénure d'argent sensible à la lumière utilisable pour un traitement rapide | |
EP0307867A2 (fr) | Matériau photographique à l'halogénure d'argent sensible à la lumière ayant une finesse supérieure et utilisable pour un traitement ultra-rapide | |
US4506008A (en) | Silver halide photographic light-sensitive materials | |
EP0547912A1 (fr) | Emulsion photographique à l'halogénure d'argent et matériau photographique couleur à l'halogénure d'argent sensible à la lumière | |
US5223382A (en) | Silver halide photographic material | |
JPH01166031A (ja) | ハロゲン化銀写真材料 | |
US5206132A (en) | Direct positive silver halide photographic light-sensitive material | |
JP2676267B2 (ja) | ハロゲン化銀写真感光材料 | |
JPS61277947A (ja) | ハロゲン化銀写真感光材料 | |
EP0670517B1 (fr) | Méthode de traitement d'un matériau photographique à l'halogénure d'argent sensible à la lumière | |
JPS62131247A (ja) | ハロゲン化銀写真感光材料 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: KONICA CORPORATION, A CORP. OF JAPAN,JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAGASAKI, SATORU;SUZUKI, AKIO;YOSHIDA, EIJI;AND OTHERS;REEL/FRAME:004778/0106 Effective date: 19871022 |
|
STCF | Information on status: patent grant |
Free format text: PATENTED CASE |