US20180223409A1 - Steel Sheet Coated with a Metallic Coating based on Aluminum - Google Patents

Steel Sheet Coated with a Metallic Coating based on Aluminum Download PDF

Info

Publication number
US20180223409A1
US20180223409A1 US15/748,033 US201615748033A US2018223409A1 US 20180223409 A1 US20180223409 A1 US 20180223409A1 US 201615748033 A US201615748033 A US 201615748033A US 2018223409 A1 US2018223409 A1 US 2018223409A1
Authority
US
United States
Prior art keywords
steel sheet
sheet according
weight
coating comprises
metallic coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US15/748,033
Other languages
English (en)
Inventor
Christian Allely
Tiago Machado Amorim
Joost DE STRYCKER
Krista Godelieve Oscar Van Den Bergh
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ArcelorMittal SA
Original Assignee
ArcelorMittal SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ArcelorMittal SA filed Critical ArcelorMittal SA
Assigned to ARCELORMITTAL reassignment ARCELORMITTAL ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ALLELY, CHRISTIAN, MACHADO AMORIM, Tiago, DE STRYCKER, Joost, VAN DEN BERGH, Krista Godelieve Oscar
Publication of US20180223409A1 publication Critical patent/US20180223409A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B15/043—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/18—Layered products comprising a layer of metal comprising iron or steel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/20—Layered products comprising a layer of metal comprising aluminium or copper
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/005—Modifying the physical properties by deformation combined with, or followed by, heat treatment of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/02—Alloys based on aluminium with silicon as the next major constituent
    • C22C21/04—Modified aluminium-silicon alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/06—Alloys based on aluminium with magnesium as the next major constituent
    • C22C21/08—Alloys based on aluminium with magnesium as the next major constituent with silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/10—Alloys based on aluminium with zinc as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/12—Alloys based on aluminium with copper as the next major constituent
    • C22C21/14—Alloys based on aluminium with copper as the next major constituent with silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/12—Alloys based on aluminium with copper as the next major constituent
    • C22C21/16—Alloys based on aluminium with copper as the next major constituent with magnesium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/12—Alloys based on aluminium with copper as the next major constituent
    • C22C21/18—Alloys based on aluminium with copper as the next major constituent with zinc
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/026—Deposition of sublayers, e.g. adhesion layers or pre-applied alloying elements or corrosion protection
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C23C30/005—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process on hard metal substrates
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12431—Foil or filament smaller than 6 mils
    • Y10T428/12438—Composite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y10T428/12757—Fe
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/12764—Next to Al-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y10T428/12979—Containing more than 10% nonferrous elements [e.g., high alloy, stainless]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
    • Y10T428/2495—Thickness [relative or absolute]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
    • Y10T428/2495—Thickness [relative or absolute]
    • Y10T428/24967—Absolute thicknesses specified
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
    • Y10T428/264—Up to 3 mils
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
    • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
    • Y10T428/264—Up to 3 mils
    • Y10T428/265—1 mil or less

Definitions

  • the present invention relates to a steel sheet coated with a metallic coating.
  • the invention is particularly well suited for the manufacture of automotive vehicles.
  • Zinc-based coatings are generally used because they allows for a protection against corrosion thanks to barrier protection and cathodic protection.
  • the barrier effect is obtained by the application of a metallic coating on steel surface.
  • metallic coatings prevent the contact between steel and corrosive atmosphere.
  • the barrier effect is independent from the nature of coating and substrate.
  • sacrificial cathodic protection is based on the fact that zinc is a metal less noble that steel. Thus, if corrosion occurs, zinc is consumed preferentially to steel. Cathodic protection is essential in areas where steel is directly exposed to corrosive atmosphere, like cut edges where surrounding zinc will be consumed before steel.
  • the coating comprises, in terms of weight %, Al: at least 45% and no greater than 70%, Mg: at least 1% and less than 5%, Si: at least 0.5% and less than 3%, with the remainder Zn and unavoidable impurities, wherein the Al/Zn ratio is 0.89-2.75 and the plating layer contains a scaly Mg 2 Si phase.
  • Mg 2 Si phases scaly or bulky
  • Mg 2 Si phases are complex. Indeed, it depends on the size and on the ratio of the short diameter mean size with respect to the long diameter of Mg 2 Si phases, as observed with a 5° polished cross-section. The size is affected most predominantly by the cooling rate after hot-dip plating.
  • the fabrication of Mg 2 Si phases also depends on the quantity of Mg and Si.
  • Mg 2 Si phases can be difficult to obtain because of these specifics criteria. Therefore, there is a risk that the desired Mg 2 Si phase is not obtained.
  • the purpose of the invention is to provide a coated steel sheet easy to form having a reinforced protection against corrosion, i.e. a sacrificial cathodic protection in addition to barrier protection, before and after the forming.
  • electrochemical potential has to be at least 50 mV more negative than the potential of steel, i.e. a maximum potential of ⁇ 0.78V with respect to a saturated calomel electrode (SCE). It is preferable not to decrease the potential at a value of ⁇ 1.4V/SCE, even ⁇ 1.25V/SCE which would involve a fast consumption and would finally decrease the period of protection of steel.
  • a steel sheet coated with a metallic coating comprising from 2.0 to 24.0% by weight of zinc, from 7.1 to 12.0% by weight of silicon, optionally from 1.1 to 8.0% by weight of magnesium, and optionally additional elements chosen from Pb, Ni, Zr, or Hf, the content by weight of each additional element being less than 0.3% by weight, the balance being aluminum and optionally unavoidable impurities and residuals elements, wherein the ratio Al/Zn is above 2.9.
  • the invention also provides parts made from the steel sheet coated with the metallic.
  • the invention further provides a coated part for the manufacture of an automotive.
  • FIG. 1 illustrates one corrosion cycle corresponding to 168 hours of the norm VDA 233-102.
  • any steel can be advantageously used in the scope of the invention.
  • steel having high mechanical strength is needed, in particular for parts of structure of automotive vehicle, steel having a tensile resistance superior to 500 MPa, advantageously between 500 and 2000 MPa before or after heat-treatment, can be used.
  • the weight composition of steel sheet is preferably as follows: 0.03% ⁇ C ⁇ 0.50%; 0.3% ⁇ Mn ⁇ 3.0%; 0.05% ⁇ Si ⁇ 0.8%; 0.015% ⁇ Ti ⁇ 0.2%; 0.005% ⁇ Al ⁇ 0.1%; 0% ⁇ Cr ⁇ 2.50%; 0% ⁇ S ⁇ 0.05%; 0% ⁇ P ⁇ 0.1%; 0% ⁇ B ⁇ 0.010%; 0% ⁇ Ni ⁇ 2.5%; 0% ⁇ Mo ⁇ 0.7%; 0% ⁇ Nb ⁇ 0.15%; 0% ⁇ N ⁇ 0.015%; 0% ⁇ Cu ⁇ 0.15%; 0% ⁇ Ca ⁇ 0.01%; 0% ⁇ W ⁇ 0.35%, the balance being iron and unavoidable impurities from the manufacture of steel.
  • the steel sheet is 22MnB5 with the following composition: 0.20% ⁇ C ⁇ 0.25%; 0.15% ⁇ Si ⁇ 0.35%; 1.10% ⁇ Mn ⁇ 1.40%; 0% ⁇ Cr ⁇ 0.30%; 0% ⁇ Mo ⁇ 0.35%; 0% ⁇ P ⁇ 0.025%; 0% ⁇ S ⁇ 0.005%; 0.020% ⁇ Ti ⁇ 0.060%; 0.020% ⁇ Al ⁇ 0.060%; 0.002% ⁇ B ⁇ 0.004%, the balance being iron and unavoidable impurities from the manufacture of steel.
  • the steel sheet can be Usibor®2000 with the following composition: 0.24% ⁇ C ⁇ 0.38%; 0.40% ⁇ Mn ⁇ 3%; 0.10% ⁇ Si ⁇ 0.70%; 0.015% ⁇ Al ⁇ 0.070%; 0% ⁇ Cr ⁇ 2%; 0.25% ⁇ Ni ⁇ 2%; 0.020% ⁇ Ti ⁇ 0.10%; 0% ⁇ Nb ⁇ 0.060%; 0.0005% ⁇ B ⁇ 0.0040%; 0.003% ⁇ N ⁇ 0.010%; 0.0001% ⁇ S ⁇ 0.005%; 0.0001% ⁇ P ⁇ 0.025%; it being understood that the contents of titanium and nitrogen satisfy Ti/N>3.42; and that the contents of carbon, manganese, chromium and silicon satisfy:
  • the composition optionally comprising one or more of the following: 0.05% ⁇ Mo ⁇ 0.65%; 0.001% ⁇ W ⁇ 0.30%; 0.0005% ⁇ Ca ⁇ 0.005%, the balance being iron and unavoidable impurities from the manufacture of steel.
  • the steel sheet is Ductibor®500 with the following composition: 0.040% ⁇ C ⁇ 0.100%; 0.80% ⁇ Mn ⁇ 2.00%; 0% ⁇ Si ⁇ 0.30%; 0% ⁇ S ⁇ 0.005%; 0% ⁇ P ⁇ 0.030%; 0.010% ⁇ Al ⁇ 0.070%; 0.015% ⁇ Nb ⁇ 0.100%; 0.030% ⁇ Ti ⁇ 0.080%; 0% ⁇ N ⁇ 0.009%; 0% ⁇ Cu ⁇ 0.100%; 0% ⁇ Ni ⁇ 0.100%; 0% ⁇ Cr ⁇ 0.100%; 0% ⁇ Mo ⁇ 0.100%; 0% ⁇ Ca ⁇ 0.006%, the balance being iron and unavoidable impurities from the manufacture of steel.
  • Steel sheet can be obtained by hot rolling and optionally cold rolling depending on the desired thickness, which can be for example between 0.7 and 3.0 mm.
  • the invention provides a steel sheet coated with a metallic coating comprising from 2.0 to 24.0% by weight of zinc, from 7.1 to 12.0% by weight of silicon, optionally from 1.1 to 8.0% by weight of magnesium, and optionally additional elements chosen from Pb, Ni, Zr, or Hf, the content by weight of each additional element being less than 0.3% by weight, the balance being aluminum and optionally unavoidable impurities and residuals elements, wherein the ratio Al/Zn is above 2.9.
  • Metallic coatings according to the invention have a high sacrificial protection.
  • the metallic coating does not comprise elements selected among Cr, Mn, Ti, Ce, La, Nd, Pr, Ca, Bi, In, Sn and Sb or their combinations.
  • the metallic coating does not comprise any of the following compounds: Cr, Mn, Ti, Ce, La, Nd, Pr, Ca, Bi, In, Sn and Sb. Indeed, without willing to be bound by any theory, it seems that when these compounds are present in the coating, there is a risk that the properties of the coating, such as electrochemical potential, are altered, because of their possible interactions with the essential elements of the coatings.
  • the ratio Al/Zn is below or equal to 8.5.
  • the ratio Al/Zn is between 3.0 and 7.5, advantageously between 4.0 and 6.0. Without willing to be bound by any theory, it seems that if these conditions are not met, there is a risk that the sacrificial protection decreases because zinc rich phases are not in sufficient amount in the coating.
  • the coating layer further comprises an Al—Zn phase.
  • the metallic coating comprises from 10.0 to 20.0%, preferably from 10.0 to 15.0%, by weight of zinc.
  • the metallic coating comprises from 8.1 to 10.0% by weight of silicon.
  • the coating comprises from 3.0 to 8.0% by weight of magnesium, preferably, from 3.0 to 5.0% by weight of magnesium. Without willing to be bound by any theory, it has been found that the addition of magnesium in the above range further improve the anti-corrosion properties.
  • the microstructure of said coating comprising a Mg 2 Si phase.
  • the microstructure of said coating further comprises a MgZn 2 phase.
  • the amount of aluminum is above 71%, preferably above 76%, by weight.
  • the coating can be deposited by any methods known to the man skilled in the art, for example hot-dip galvanization process, electrogalvanization process, physical vapour deposition such as jet vapor deposition or sputtering magnetron.
  • the coating is deposited by hot-dip galvanization process. In this process, the steel sheet obtained by rolling is dipped in a molten metal bath.
  • the bath comprises zinc, silicon, aluminum and optionally magnesium. It can comprise additional elements chosen from Pb, Ni, Zr, or Hf, the content by weight of each additional element being less than 0.3% by weight. These additional elements can improve among others ductibility, coating adhesion on the steel sheet.
  • the bath can also contain unavoidable impurities and residuals elements from feeding ingots or from the passage of the steel sheet in the molten bath.
  • Residual element can be iron with a content up to 3.0% by weight.
  • the thickness of the coating is usually between 5 and 50 ⁇ m, preferably between 10 and 35 ⁇ m, advantageously between 12 and 18 ⁇ m or between 26 to 31 ⁇ m.
  • the bath temperature is usually between 580 and 660° C.
  • the steel sheet is usually wiped with nozzles ejecting gas on both sides of the coated steel sheet.
  • the coated steel sheet is then cooled.
  • the cooling rate is above or equal to 15° C.s ⁇ 1 between the beginning of the solidification and the end of the solidification.
  • the cooling rate between the beginning and the end of the solidification is superior or equal to 20° C.s ⁇ 1 .
  • a skin-pass can be realized and allows work hardening the coated steel sheet and giving it a roughness facilitating the subsequent shaping.
  • a degreasing and a surface treatment can be applied in order to improve for example adhesive bonding or corrosion resistance.
  • coated steel sheet according to the invention can be shaped by any method known to the man skilled in the art, for example cold-stamping and/or hot-forming.
  • the part is obtained by cold-stamping.
  • the coated steel sheet is cut to obtain a blank and then cold-stamped in order to obtain a part.
  • the part coated is obtained by a press hardening process including the hot-forming.
  • this method comprises the following steps:
  • a thermal treatment is applied to the blank in a furnace under non protective atmosphere at an austenitization temperature Tm usually between 840 and 950° C., preferably 880 to 930° C.
  • Tm austenitization temperature
  • said blank is maintained during a dwell time tm between 1 to 12 minutes, preferably between 3 to 9 minutes.
  • the coating forms an alloy layer having a high resistance to corrosion, abrasion, wear and fatigue.
  • the blank is then transferred to a hot-forming tool and hot-formed at a temperature between 600 and 830° C.
  • the hot-forming comprises the hot-stamping and the roll-forming.
  • the blank is hot-stamped.
  • the part is then cooled in the hot-forming tool or after the transfer to a specific cooling tool.
  • the cooling rate is controlled depending on the steel composition, in such a way that the final microstructure after the hot-forming comprises mostly martensite, preferably contains martensite, or martensite and bainite, or is made of at least 75% of equiaxed ferrite, from 5 to 20% of martensite and bainite in amount less than or equal to 10%.
  • a coated part according to the invention can thus obtained by cold or hot forming but also by any suitable combination of cold-stamping and hot-forming.
  • the part is a press hardened steel part having a variable thickness
  • the press hardened steel part of the invention can have a thickness which is not uniform but which can vary. Indeed, it is possible to achieve the desired mechanical resistance level in the zones which are the most subjected to external stresses, and to save weight in the other zones of the press hardened part, thus contributing to the vehicle weight reduction.
  • the parts with non-uniform thickness can be produced by continuous flexible rolling, i.e. by a process wherein the sheet thickness obtained after rolling is variable in the rolling direction, in relationship with the load which has been applied through the rollers to the sheet during the rolling process.
  • the part can be a front rail, a seat cross member, a side sill member, a dash panel cross member, a front floor reinforcement, a rear floor cross member, a rear rail, a B-pillar, a door ring or a shotgun.
  • the part is dipped in an e-coating bath.
  • the thickness of the phosphate layer is between 1 and 2 ⁇ m and the thickness of the e-coating layer is between 15 and 25 ⁇ m, preferably less than or equal to 20 ⁇ m.
  • the cataphoresis layer ensures an additional protection against corrosion.
  • paint layers can be deposited, for example, a primer coat of paint, a basecoat layer and a top coat layer.
  • the part Before applying the e-coating on the part, the part is previously degreased and phosphated so as to ensure the adhesion of the cataphoresis.
  • steel sheets used are 22MnB5.
  • All coatings were deposited by hot-dip galvanization process. All coatings have a thickness of 15 ⁇ m.
  • Trials according to the invention have a lower coupling potential than a coating comprising aluminum and 9% by weight of silicon. Coupling potentials of Trials 1 to 3 are under ⁇ 0.78V/SCE as required.
  • Trials 5 to 12 were prepared and subjected to a corrosion test to evaluate the cut edge protection of the coated steel sheets.
  • Trials 5 to 11 have very good protection against corrosion on the cut edges of coated steel sheet. By contrast, Trial 12 does not show enough corrosion resistance on the cut edges.
  • Trials 13 to 15 are sacrificial such as zinc coating. Coupling potential are under ⁇ 0.78V/SCE as required.
  • Trials 17 to 20 were prepared and subjected to a corrosion test to evaluate the protection of the coated steel sheets.
  • FIG. 1 illustrates one cycle corresponding to 168 hours, i.e. one week.
  • Trials 17 to 19 show excellent protection against corrosion, in particular when the coating comprises magnesium (Trials 18 and 19).
  • Trials 21 to 24 were prepared and subjected to a corrosion test to evaluate the protection of the coated steel sheets.
  • Thickness Coating ( ⁇ m) Number of cycles Trials Al Si Zn Mg 15 1 2 3 4 5 6 21* 81 9 10 — 15 0 0 0.5 1 2 3 22* 77 9 10 4 15 0 0 0 0 0 23* 73 9 10 8 15 0 0 0 0 0 0.5 24 0.2 — 99.8 — 10 0 0 0 1 2 3 *examples according to the invention.
  • Trials according to the invention have an excellent protection against corrosion, in particular when the coating comprises magnesium (Trial 22 and 23).
  • Trials 25 to 28 were prepared and subjected to a corrosion test to evaluate the protection of the coated steel sheets after austenitization treatment.
  • Trials 25 to 27 show good protection against corrosion compared to the coating comprising aluminum and silicon (Trial 28).
  • Trials 29 to 40 were prepared and subjected to an electrochemical potential test after austenitization treatment.
  • Trials 32 to 39 according to the present invention are and remain sacrificial protection over time.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Articles (AREA)
  • Laminated Bodies (AREA)
  • Shaping Metal By Deep-Drawing, Or The Like (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
US15/748,033 2015-07-30 2016-07-08 Steel Sheet Coated with a Metallic Coating based on Aluminum Abandoned US20180223409A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
IBPCT/IB2015/001281 2015-07-30
PCT/IB2015/001281 WO2017017483A1 (en) 2015-07-30 2015-07-30 Steel sheet coated with a metallic coating based on aluminum
PCT/IB2016/000977 WO2017017513A1 (en) 2015-07-30 2016-07-08 Steel sheet coated with a metallic coating based on aluminum

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2016/000977 A-371-Of-International WO2017017513A1 (en) 2015-07-30 2016-07-08 Steel sheet coated with a metallic coating based on aluminum

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US16/359,751 Continuation US10889884B2 (en) 2015-07-30 2019-03-20 Steel sheet coated with a metallic coating based on aluminum
US17/834,335 Continuation US12012655B2 (en) 2015-07-30 2022-06-07 Steel sheet coated with a metallic coating based on aluminum

Publications (1)

Publication Number Publication Date
US20180223409A1 true US20180223409A1 (en) 2018-08-09

Family

ID=54015125

Family Applications (3)

Application Number Title Priority Date Filing Date
US15/748,033 Abandoned US20180223409A1 (en) 2015-07-30 2016-07-08 Steel Sheet Coated with a Metallic Coating based on Aluminum
US16/359,751 Active US10889884B2 (en) 2015-07-30 2019-03-20 Steel sheet coated with a metallic coating based on aluminum
US17/834,335 Active US12012655B2 (en) 2015-07-30 2022-06-07 Steel sheet coated with a metallic coating based on aluminum

Family Applications After (2)

Application Number Title Priority Date Filing Date
US16/359,751 Active US10889884B2 (en) 2015-07-30 2019-03-20 Steel sheet coated with a metallic coating based on aluminum
US17/834,335 Active US12012655B2 (en) 2015-07-30 2022-06-07 Steel sheet coated with a metallic coating based on aluminum

Country Status (16)

Country Link
US (3) US20180223409A1 (ko)
EP (2) EP3521481B1 (ko)
JP (2) JP6728332B2 (ko)
KR (2) KR102246752B1 (ko)
CN (3) CN107849673A (ko)
BR (1) BR112018000446B1 (ko)
CA (1) CA2990366C (ko)
ES (2) ES2792117T3 (ko)
HU (2) HUE044565T2 (ko)
MA (2) MA46383B1 (ko)
MX (1) MX2018001305A (ko)
PL (2) PL3521481T3 (ko)
RU (1) RU2684801C1 (ko)
UA (1) UA120721C2 (ko)
WO (2) WO2017017483A1 (ko)
ZA (1) ZA201708501B (ko)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190218651A1 (en) * 2015-07-30 2019-07-18 Arcelormittal Steel Sheet Coated with a Metallic Coating based on Aluminum
US11162153B2 (en) 2015-07-30 2021-11-02 Arcelormittal Method for the manufacture of a hardened part which does not have LME issues
US11414737B2 (en) 2015-07-30 2022-08-16 Arcelormittal Method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminum
US20220411899A1 (en) * 2021-06-25 2022-12-29 Tenneco Inc. Bearing formed of an aluminum alloy material and method of manufacturing

Families Citing this family (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102153164B1 (ko) 2017-12-26 2020-09-07 주식회사 포스코 열간 프레스 성형용 도금강판 및 이를 이용한 성형부재
KR102451642B1 (ko) 2018-06-22 2022-10-11 닛폰세이테츠 가부시키가이샤 강판, 테일러드 블랭크, 열간 프레스 성형품, 강관, 중공상 ??칭 성형품, 강판의 제조 방법, 테일러드 블랭크의 제조 방법, 열간 프레스 성형품의 제조 방법, 강관의 제조 방법 및 중공상 ??칭 성형품의 제조 방법
KR102153172B1 (ko) * 2018-08-30 2020-09-07 주식회사 포스코 열간 성형성 및 내식성이 우수한 알루미늄-아연 합금 도금강판 및 그 제조방법
WO2020053736A1 (en) 2018-09-13 2020-03-19 Arcelormittal A welding method for the manufacture of an assembly of at least 2 metallic substrates
US11919102B2 (en) 2018-09-13 2024-03-05 Arcelormittal Assembly of at least 2 metallic substrates
EP3849738A1 (en) 2018-09-13 2021-07-21 ArcelorMittal An assembly of at least 2 metallic substrates
KR102354447B1 (ko) * 2018-09-27 2022-03-21 주식회사 포스코 용접액화취성에 대한 저항성과 도금밀착성이 우수한 고내식 도금강판
WO2020109849A1 (en) 2018-11-30 2020-06-04 Arcelormittal Wire injection
WO2020136402A1 (en) 2018-12-24 2020-07-02 Arcelormittal Method for producing a welded steel blank and associated welded steel blank
WO2020208399A1 (en) * 2019-04-09 2020-10-15 Arcelormittal Assembly of an aluminium component and of a press hardened steel part having an alloyed coating comprising silicon, iron, zinc, optionally magnesium, the balance being aluminum
WO2021084305A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
WO2021084304A1 (en) * 2019-10-30 2021-05-06 Arcelormittal A press hardening method
KR102311503B1 (ko) 2019-12-20 2021-10-13 주식회사 포스코 가공성 및 내식성이 우수한 알루미늄계 합금 도금강판 및 이의 제조방법
KR102307954B1 (ko) 2019-12-20 2021-09-30 주식회사 포스코 가공성 및 내식성이 우수한 알루미늄계 합금 도금강판 및 이의 제조방법
DE102020112829A1 (de) * 2020-05-12 2021-11-18 Eaton Intelligent Power Limited Erdungselement und Elektroinstallationsbauteil mit einem Erdungselement
CN117136252A (zh) * 2020-12-18 2023-11-28 浦项股份有限公司 热压成型用镀覆钢板及其制造方法
WO2022154082A1 (ja) 2021-01-14 2022-07-21 日本製鉄株式会社 めっき鋼材
CN116710579A (zh) 2021-01-14 2023-09-05 日本制铁株式会社 热压构件
WO2023063048A1 (ja) 2021-10-12 2023-04-20 日本製鉄株式会社 ホットスタンプ成形体

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001214280A (ja) * 2000-01-28 2001-08-07 Nippon Steel Corp 潤滑性に優れたＣｒを使用しない皮膜を被覆するＳｎ系，Ａｌ系めっき鋼板
JP2005290418A (ja) * 2004-03-31 2005-10-20 Jfe Steel Kk プレス加工性に優れた溶融Ａｌ−Ｚｎ系めっき鋼板及びその製造方法
JP2008038168A (ja) * 2006-08-02 2008-02-21 Nippon Steel Corp めっき性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2010229483A (ja) * 2009-03-26 2010-10-14 Nisshin Steel Co Ltd 耐食性に優れたＺｎ−Ａｌ系めっき鋼板およびその製造方法
US20120186705A1 (en) * 2009-09-01 2012-07-26 Thyssenkrupp Steel Europe Ag Method and Device for Producing a Metal Component
WO2013156688A1 (fr) * 2012-04-17 2013-10-24 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier munie d'un revêtement à protection cathodique sacrificielle, procédé de fabrication d'une pièce par mise en oeuvre d'une telle tôle et pièce ainsi obtenue
US20140377584A1 (en) * 2011-10-07 2014-12-25 Jfe Steel Corporation High-strength hot-dipped galvanized steel sheet having excellent formability and impact resistance, and method for producing same

Family Cites Families (52)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04293759A (ja) * 1991-03-20 1992-10-19 Nippon Steel Corp 耐食性に優れた溶融アルミニウムめっき鋼板
KR0146986B1 (ko) 1995-08-29 1998-11-02 서정욱 알루미늄 도금강판의 인산염처리성을 향상시키는 방법
JP3267178B2 (ja) 1996-12-18 2002-03-18 住友金属工業株式会社 加工性に優れたＺｎ−Ａｌ合金めっき鋼板
JPH11272973A (ja) 1998-03-19 1999-10-08 Aiphone Co Ltd セキュリティ装置
JPH11279735A (ja) * 1998-03-27 1999-10-12 Nisshin Steel Co Ltd Ａｌ−Ｓｉ−Ｍｇ−Ｚｎ系溶融Ａｌ基めっき鋼板
JP2000104153A (ja) 1998-09-28 2000-04-11 Daido Steel Sheet Corp 亜鉛−アルミニウム合金めっき鋼板
JP4199404B2 (ja) * 1999-03-15 2008-12-17 新日本製鐵株式会社 高耐食性めっき鋼板
KR100317680B1 (ko) 1999-04-29 2001-12-22 이계안 알루미늄 합금 및 강판을 동시에 처리할 수 있는 도장 하지용 표면처리제
JP4267184B2 (ja) 1999-06-29 2009-05-27 新日本製鐵株式会社 耐食性、外観に優れた溶融アルミめっき鋼板及びその製造法
JP4136286B2 (ja) 1999-08-09 2008-08-20 新日本製鐵株式会社 耐食性に優れたＺｎ−Ａｌ−Ｍｇ−Ｓｉ合金めっき鋼材およびその製造方法
JP2002012959A (ja) * 2000-04-26 2002-01-15 Nippon Steel Corp 加工部及び端面耐食性に優れたＡｌ系めっき鋼板
JP2002322527A (ja) 2001-04-25 2002-11-08 Nippon Steel Corp Ａｌ−Ｚｎ−Ｍｇ系合金めっき鉄鋼製品
RU2202649C1 (ru) 2001-12-26 2003-04-20 Закрытое акционерное общество "Межотраслевое юридическое агентство "Юрпромконсалтинг" Способ нанесения алюминиевых покрытий на изделия из чугуна и стали
JP2004339530A (ja) 2003-05-13 2004-12-02 Nippon Steel Corp 加工性に優れたＭｇ含有めっき鋼材およびその製造方法
PL1651789T3 (pl) 2003-07-29 2011-03-31 Voestalpine Stahl Gmbh Sposób wytwarzania hartowanych elementów konstrukcyjnych z blachy stalowej
JP2005060728A (ja) * 2003-08-11 2005-03-10 Nippon Steel Corp 低比重溶融アルミめっき鋼板及びそのプレス加工方法
JP2006051543A (ja) 2004-07-15 2006-02-23 Nippon Steel Corp 冷延、熱延鋼板もしくはＡｌ系、Ｚｎ系めっき鋼板を使用した高強度自動車部材の熱間プレス方法および熱間プレス部品
JP2006193776A (ja) * 2005-01-12 2006-07-27 Nisshin Steel Co Ltd 摺動性に優れたＺｎ−Ａｌ−Ｍｇ系合金めっき鋼板及び摺動部材
JP4410718B2 (ja) * 2005-04-25 2010-02-03 新日本製鐵株式会社 塗料密着性、塗装後耐食性に優れたＡｌ系めっき鋼板及びこれを用いた自動車部材並びにＡｌ系めっき鋼板の製造方法
JP4733522B2 (ja) 2006-01-06 2011-07-27 新日本製鐵株式会社 耐食性、耐疲労性に優れた高強度焼き入れ成形体の製造方法
WO2007118939A1 (fr) 2006-04-19 2007-10-25 Arcelor France Procede de fabrication d'une piece soudee a tres hautes caracteristiques mecaniques a partir d'une tole laminee et revetue
JP4919427B2 (ja) * 2006-10-03 2012-04-18 日新製鋼株式会社 溶融めっき鋼板の温間加工方法
CN101617059A (zh) * 2007-02-23 2009-12-30 克里斯塔尔公司 热机械形成具有很高强度的最终产品的方法及由此制备的产品
WO2008110670A1 (fr) 2007-03-14 2008-09-18 Arcelormittal France Acier pour formage a chaud ou trempe sous outil a ductilite amelioree
EP2025771A1 (en) 2007-08-15 2009-02-18 Corus Staal BV Method for producing a coated steel strip for producing taylored blanks suitable for thermomechanical shaping, strip thus produced, and use of such a coated strip
US8453482B2 (en) 2008-04-22 2013-06-04 Nippon Steel & Sumitomo Metal Corporation Plated steel sheet and method of hot-stamping plated steel sheet
JP5600868B2 (ja) * 2008-09-17 2014-10-08 Ｊｆｅスチール株式会社 溶融Ａｌ−Ｚｎ系めっき鋼板の製造方法
MY155139A (en) 2009-01-16 2015-09-15 Nippon Steel & Sumitomo Metal Corp Hot-dip zn-al-mg-si-cr alloy-coated steel material with excellent corrosion resistance
WO2010085983A1 (en) 2009-02-02 2010-08-05 Arcelormittal Investigacion Y Desarrollo S.L. Fabrication process of coated stamped parts and parts prepared from the same
JP4825882B2 (ja) 2009-02-03 2011-11-30 トヨタ自動車株式会社 高強度焼き入れ成形体及びその製造方法
DE102009007909A1 (de) 2009-02-06 2010-08-12 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines Stahlbauteils durch Warmformen und durch Warmformen hergestelltes Stahlbauteil
JP5851845B2 (ja) 2009-03-13 2016-02-03 ブルースコープ・スティール・リミテッドＢｌｕｅｓｃｏｐｅ Ｓｔｅｅｌ Ｌｉｍｉｔｅｄ Ａｌ／Ｚｎベースの被膜を有する腐食保護
DE102009017326A1 (de) 2009-04-16 2010-10-21 Benteler Automobiltechnik Gmbh Verfahren zur Herstellung von pressgehärteten Bauteilen
MX343388B (es) * 2009-08-06 2016-11-04 Nippon Steel & Sumitomo Metal Corp Lámina de metal para calentamiento por radiación, proceso para producir la misma, y metal procesado que tiene una porción con resistencia diferente y proceso para producir el mismo.
US9068255B2 (en) 2009-12-29 2015-06-30 Posco Zinc-plated steel sheet for hot pressing having outstanding surface characteristics, hot-pressed moulded parts obtained using the same, and a production method for the same
CN102011082A (zh) 2010-11-12 2011-04-13 上海大学 Al-Zn-Si-Mg合金镀层的热浸镀工艺方法
JP2012112010A (ja) * 2010-11-26 2012-06-14 Jfe Steel Corp 熱間プレス用めっき鋼板、それを用いた熱間プレス部材の製造方法および熱間プレス部材
RU2553128C2 (ru) * 2010-11-26 2015-06-10 ДжФЕ СТИЛ КОРПОРЕЙШН СТАЛЬНОЙ ЛИСТ С Al-Zn ПОКРЫТИЕМ, НАНЕСЁННЫМ СПОСОБОМ ГОРЯЧЕГО ОКУНАНИЯ, И СПОСОБ ЕГО ИЗГОТОВЛЕНИЯ
CA2818297C (en) 2010-11-26 2015-10-13 Jfe Steel Corporation Hot-dip al-zn coated steel sheet
CN103384726B (zh) 2010-12-24 2016-11-23 沃斯特阿尔派因钢铁有限责任公司 生产硬化的结构部件的方法
BR112013025401B1 (pt) 2011-04-01 2020-05-12 Nippon Steel Corporation Peça estampada a quente de alta resistência e método de produção da mesma
DE202012000616U1 (de) 2012-01-24 2012-02-29 Benteler Automobiltechnik Gmbh Struktur- und/oder Karosseriebauteil für ein Kraftfahrzeug mit verbesserten Crasheigenschaften und Korrosionsschutz
CA2864392C (en) 2012-02-14 2018-01-02 Nippon Steel & Sumitomo Metal Corporation Plated steel plate for hot pressing and hot pressing method of plated steel plate
JP6169319B2 (ja) 2012-02-15 2017-07-26 理想科学工業株式会社 封筒用紙
JP6001884B2 (ja) 2012-03-09 2016-10-05 株式会社神戸製鋼所 プレス成形品の製造方法およびプレス成形品
US20160168658A1 (en) 2012-10-17 2016-06-16 Bluescope Steel Limited Method of producing metal-coated steel strip
EP2848709B1 (de) 2013-09-13 2020-03-04 ThyssenKrupp Steel Europe AG Verfahren zum Herstellen eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils und Stahlbauteil
WO2016132165A1 (fr) 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
WO2017017484A1 (en) * 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
WO2017017485A1 (en) 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
DE202021000616U1 (de) 2021-02-18 2021-03-18 Frank Schiestel Elektronische Impfschutzkarte

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001214280A (ja) * 2000-01-28 2001-08-07 Nippon Steel Corp 潤滑性に優れたＣｒを使用しない皮膜を被覆するＳｎ系，Ａｌ系めっき鋼板
JP2005290418A (ja) * 2004-03-31 2005-10-20 Jfe Steel Kk プレス加工性に優れた溶融Ａｌ−Ｚｎ系めっき鋼板及びその製造方法
JP2008038168A (ja) * 2006-08-02 2008-02-21 Nippon Steel Corp めっき性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2010229483A (ja) * 2009-03-26 2010-10-14 Nisshin Steel Co Ltd 耐食性に優れたＺｎ−Ａｌ系めっき鋼板およびその製造方法
US20120186705A1 (en) * 2009-09-01 2012-07-26 Thyssenkrupp Steel Europe Ag Method and Device for Producing a Metal Component
US20140377584A1 (en) * 2011-10-07 2014-12-25 Jfe Steel Corporation High-strength hot-dipped galvanized steel sheet having excellent formability and impact resistance, and method for producing same
WO2013156688A1 (fr) * 2012-04-17 2013-10-24 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier munie d'un revêtement à protection cathodique sacrificielle, procédé de fabrication d'une pièce par mise en oeuvre d'une telle tôle et pièce ainsi obtenue

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190218651A1 (en) * 2015-07-30 2019-07-18 Arcelormittal Steel Sheet Coated with a Metallic Coating based on Aluminum
US10889884B2 (en) * 2015-07-30 2021-01-12 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
US11162153B2 (en) 2015-07-30 2021-11-02 Arcelormittal Method for the manufacture of a hardened part which does not have LME issues
US11414737B2 (en) 2015-07-30 2022-08-16 Arcelormittal Method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminum
US12012655B2 (en) 2015-07-30 2024-06-18 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
US20220411899A1 (en) * 2021-06-25 2022-12-29 Tenneco Inc. Bearing formed of an aluminum alloy material and method of manufacturing

Also Published As

Publication number Publication date
EP3521481A1 (en) 2019-08-07
EP3329028B1 (en) 2019-05-08
UA120721C2 (uk) 2020-01-27
KR102246752B1 (ko) 2021-04-30
WO2017017513A1 (en) 2017-02-02
PL3521481T3 (pl) 2020-09-21
CA2990366A1 (en) 2017-02-02
RU2684801C1 (ru) 2019-04-15
CA2990366C (en) 2020-01-07
CN107849673A (zh) 2018-03-27
CN112981298A (zh) 2021-06-18
JP2018528324A (ja) 2018-09-27
MA42515A (fr) 2019-05-08
JP6728332B2 (ja) 2020-07-22
MA42515B1 (fr) 2019-10-31
US12012655B2 (en) 2024-06-18
CN110512162A (zh) 2019-11-29
BR112018000446B1 (pt) 2021-12-21
ES2741361T3 (es) 2020-02-10
KR20180022928A (ko) 2018-03-06
US20220298618A1 (en) 2022-09-22
JP2020056099A (ja) 2020-04-09
HUE049700T2 (hu) 2020-10-28
KR20190105115A (ko) 2019-09-11
PL3329028T3 (pl) 2019-11-29
BR112018000446A2 (pt) 2018-09-18
US20190218651A1 (en) 2019-07-18
EP3521481B1 (en) 2020-04-15
ZA201708501B (en) 2020-09-30
JP6908659B2 (ja) 2021-07-28
CN112981298B (zh) 2023-12-19
MA46383B1 (fr) 2020-06-30
WO2017017483A1 (en) 2017-02-02
MX2018001305A (es) 2018-04-30
US10889884B2 (en) 2021-01-12
HUE044565T2 (hu) 2019-11-28
ES2792117T3 (es) 2020-11-10
EP3329028A1 (en) 2018-06-06

Similar Documents

Publication Publication Date Title
US12012655B2 (en) Steel sheet coated with a metallic coating based on aluminum
US20210395856A1 (en) Painted, hot formed, coated steel part
US20220356552A1 (en) Phosphatable Part Starting from a Steel Sheet Coated with a Metallic Coating Based on Aluminum
US10947608B2 (en) Steel sheet coated with a metallic coating based on aluminum and comprising titanium

Legal Events

Date Code Title Description
AS Assignment

Owner name: ARCELORMITTAL, LUXEMBOURG

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ALLELY, CHRISTIAN;MACHADO AMORIM, TIAGO;DE STRYCKER, JOOST;AND OTHERS;SIGNING DATES FROM 20180107 TO 20180110;REEL/FRAME:044787/0865

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: AMENDMENT AFTER NOTICE OF APPEAL

STCV Information on status: appeal procedure

Free format text: NOTICE OF APPEAL FILED

STCV Information on status: appeal procedure

Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED

STCV Information on status: appeal procedure

Free format text: ON APPEAL -- AWAITING DECISION BY THE BOARD OF APPEALS

STCV Information on status: appeal procedure

Free format text: BOARD OF APPEALS DECISION RENDERED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION