US20180180994A1 - Substituted triazines - Google Patents
Substituted triazines Download PDFInfo
- Publication number
- US20180180994A1 US20180180994A1 US15/738,892 US201615738892A US2018180994A1 US 20180180994 A1 US20180180994 A1 US 20180180994A1 US 201615738892 A US201615738892 A US 201615738892A US 2018180994 A1 US2018180994 A1 US 2018180994A1
- Authority
- US
- United States
- Prior art keywords
- photopolymer
- alkyl
- formula
- compounds
- holographic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 0 [1*]C1=C(C2=NC(CC)=NC(CC)=N2)C([4*])=C([3*])C(C(=O)O[5*])=C1[2*] Chemical compound [1*]C1=C(C2=NC(CC)=NC(CC)=N2)C([4*])=C([3*])C(C(=O)O[5*])=C1[2*] 0.000 description 7
- JQEYPOSCIAPAKK-UHFFFAOYSA-M CCCCC(CC)COC(=O)CC(C(=O)OCC(CC)CCCC)S(=O)(=O)[O-].CN1C2=CC=CC=C2C(C)(C)/C1=C/C=C(/C#N)C1=[N+](C)C2=C(C=C(Cl)C=C2)C1(C)C Chemical compound CCCCC(CC)COC(=O)CC(C(=O)OCC(CC)CCCC)S(=O)(=O)[O-].CN1C2=CC=CC=C2C(C)(C)/C1=C/C=C(/C#N)C1=[N+](C)C2=C(C=C(Cl)C=C2)C1(C)C JQEYPOSCIAPAKK-UHFFFAOYSA-M 0.000 description 1
- CNWCZUCZBDXFKC-WUXMJOGZSA-N CN1C2=CC=C(Cl)C=C2C(C)(C)/C1=C\C#N Chemical compound CN1C2=CC=C(Cl)C=C2C(C)(C)/C1=C\C#N CNWCZUCZBDXFKC-WUXMJOGZSA-N 0.000 description 1
- GCECACVNILMTRD-WQLSENKSSA-N [H]C(=O)/C=C1\N(C)C2=CC=CC=C2C1(C)C Chemical compound [H]C(=O)/C=C1\N(C)C2=CC=CC=C2C1(C)C GCECACVNILMTRD-WQLSENKSSA-N 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07D—HETEROCYCLIC COMPOUNDS
- C07D251/00—Heterocyclic compounds containing 1,3,5-triazine rings
- C07D251/02—Heterocyclic compounds containing 1,3,5-triazine rings not condensed with other rings
- C07D251/12—Heterocyclic compounds containing 1,3,5-triazine rings not condensed with other rings having three double bonds between ring members or between ring members and non-ring members
- C07D251/14—Heterocyclic compounds containing 1,3,5-triazine rings not condensed with other rings having three double bonds between ring members or between ring members and non-ring members with hydrogen or carbon atoms directly attached to at least one ring carbon atom
- C07D251/24—Heterocyclic compounds containing 1,3,5-triazine rings not condensed with other rings having three double bonds between ring members or between ring members and non-ring members with hydrogen or carbon atoms directly attached to at least one ring carbon atom to three ring carbon atoms
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C253/00—Preparation of carboxylic acid nitriles
- C07C253/30—Preparation of carboxylic acid nitriles by reactions not involving the formation of cyano groups
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C255/00—Carboxylic acid nitriles
- C07C255/49—Carboxylic acid nitriles having cyano groups bound to carbon atoms of six-membered aromatic rings of a carbon skeleton
- C07C255/57—Carboxylic acid nitriles having cyano groups bound to carbon atoms of six-membered aromatic rings of a carbon skeleton containing cyano groups and carboxyl groups, other than cyano groups, bound to the carbon skeleton
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C67/00—Preparation of carboxylic acid esters
- C07C67/02—Preparation of carboxylic acid esters by interreacting ester groups, i.e. transesterification
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/0005—Production of optical devices or components in so far as characterised by the lithographic processes or materials used therefor
- G03F7/001—Phase modulating patterns, e.g. refractive index patterns
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
- G03F7/028—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds with photosensitivity-increasing substances, e.g. photoinitiators
- G03F7/029—Inorganic compounds; Onium compounds; Organic compounds having hetero atoms other than oxygen, nitrogen or sulfur
-
- G—PHYSICS
- G03—PHOTOGRAPHY; CINEMATOGRAPHY; ANALOGOUS TECHNIQUES USING WAVES OTHER THAN OPTICAL WAVES; ELECTROGRAPHY; HOLOGRAPHY
- G03F—PHOTOMECHANICAL PRODUCTION OF TEXTURED OR PATTERNED SURFACES, e.g. FOR PRINTING, FOR PROCESSING OF SEMICONDUCTOR DEVICES; MATERIALS THEREFOR; ORIGINALS THEREFOR; APPARATUS SPECIALLY ADAPTED THEREFOR
- G03F7/00—Photomechanical, e.g. photolithographic, production of textured or patterned surfaces, e.g. printing surfaces; Materials therefor, e.g. comprising photoresists; Apparatus specially adapted therefor
- G03F7/004—Photosensitive materials
- G03F7/027—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds
- G03F7/028—Non-macromolecular photopolymerisable compounds having carbon-to-carbon double bonds, e.g. ethylenic compounds with photosensitivity-increasing substances, e.g. photoinitiators
- G03F7/031—Organic compounds not covered by group G03F7/029
-
- G—PHYSICS
- G11—INFORMATION STORAGE
- G11B—INFORMATION STORAGE BASED ON RELATIVE MOVEMENT BETWEEN RECORD CARRIER AND TRANSDUCER
- G11B7/00—Recording or reproducing by optical means, e.g. recording using a thermal beam of optical radiation by modifying optical properties or the physical structure, reproducing using an optical beam at lower power by sensing optical properties; Record carriers therefor
- G11B7/24—Record carriers characterised by shape, structure or physical properties, or by the selection of the material
- G11B7/2403—Layers; Shape, structure or physical properties thereof
- G11B7/24035—Recording layers
- G11B7/24044—Recording layers for storing optical interference patterns, e.g. holograms; for storing data in three dimensions, e.g. volume storage
-
- G—PHYSICS
- G11—INFORMATION STORAGE
- G11B—INFORMATION STORAGE BASED ON RELATIVE MOVEMENT BETWEEN RECORD CARRIER AND TRANSDUCER
- G11B7/00—Recording or reproducing by optical means, e.g. recording using a thermal beam of optical radiation by modifying optical properties or the physical structure, reproducing using an optical beam at lower power by sensing optical properties; Record carriers therefor
- G11B7/24—Record carriers characterised by shape, structure or physical properties, or by the selection of the material
- G11B7/241—Record carriers characterised by shape, structure or physical properties, or by the selection of the material characterised by the selection of the material
- G11B7/242—Record carriers characterised by shape, structure or physical properties, or by the selection of the material characterised by the selection of the material of recording layers
- G11B7/244—Record carriers characterised by shape, structure or physical properties, or by the selection of the material characterised by the selection of the material of recording layers comprising organic materials only
- G11B7/245—Record carriers characterised by shape, structure or physical properties, or by the selection of the material characterised by the selection of the material of recording layers comprising organic materials only containing a polymeric component
Definitions
- the present invention relates to aromatic 4,6-bis-trichloromethyl-s-triazin-2-yl compounds of formula (I).
- a photopolymer formulation comprising a photopolymerizable component and at least one aromatic 4,6-bis-trichloromethyl-s-triazin-2-yl compound of formula (I) and a photopolymer comprising matrix polymers, a writing monomer, a photoinitiator and at least one aromatic 4,6-bis-trichloromethyl-s-triazin-2-yl compound of formula (I), a holographic medium comprising the corresponding photopolymer of the present invention, a hologram comprising a holographic medium of the present invention, a process for producing a hologram via pulsed laser radiation, and also to the use of a holographic medium of the present invention to record holograms.
- European application EP13198913.9 discloses light-sensitive photopolymers which comprise polyurethane matrix polymers, an acrylate-based writing monomer and also photoinitiators comprising two coinitiators and a dye.
- the uses of photopolymers are decisively determined by the refractive index modulation ⁇ n produced by holographic exposure.
- the interference field of signal light beam and reference light beam (that of two plane waves in the simplest case) is mapped into a refractive index grating by the local photopolymerization of writing monomers such as, for example, high-refractive acrylates at loci of high intensity in the interference field.
- the refractive index grating in the photopolymer contains all the information of the signal light beam. Illuminating the hologram with only the reference light beam will then reconstruct the signal. The strength of the signal thus reconstructed relative to the strength of the incident reference light is called the diffraction efficiency, DE in what follows.
- the DE is the ratio of the intensity of the light diffracted on reconstruction to the sum total of the intensities of diffracted light and nondiffracted light.
- the matrix polymers and the writing monomers of a photopolymer formulation should in principle be chosen such that there is a very large difference in their refractive indices.
- One possible way to realize this is to use matrix polymers having a very low refractive index and writing monomers having a very high refractive index.
- Suitable matrix polymers of low refractive index are, for example, polyurethanes obtainable by reaction of a polyol component with a polyisocyanate component.
- holographic media In addition to high DE and ⁇ n values, however, another important requirement for holographic media from photopolymer formulations is that the matrix polymers be highly crosslinked in the final medium. When the degree of crosslinking is too low, the medium will lack adequate stability. One consequence of this is to appreciably reduce the quality of holograms inscribed in the media. In the worst case, the holograms may even be subsequently destroyed.
- a further possible way to achieve large-area exposure of holograms consists in using very short pulses of light, for example from pulsed lasers or continuous wave lasers in conjunction with very fast shutters.
- Pulse durations with pulsed lasers are typically 500 ns or less.
- Pulse durations with continuous wave lasers and very fast shutters are typically 100 ⁇ s or less. In effect, the same amount of energy can be introduced here as with continuous lasers in seconds.
- Holograms can be written in this way dot by dot.
- the photopolymers known from European application EP 13198913,9 are generally usable for writing holograms with pulsed lasers but a further increase in sensitivity of the photopolymer is desirable for broad industrial utility.
- the problem addressed by the present invention was therefore that of providing a compound useful in the production of photopolymers whereinto bright holograms can be written with pulsed lasers by reason of higher photosensitivity.
- X is halogen and R 1 , R 2 , R 3 and R 4 are each independently hydrogen, halogen, alkyl, alkoxy, alkenyl, alkynyl, alkylthio, alkylseleno, wherein R 1 and R 2 and/or R 3 and R 4 may combine to form a 3 to 5-membered saturated or unsaturated bridge optionally substituted with up to 2 heteroatoms and R 5 is linear C 5 to C 20 alkyl which is optionally substituted in any manner by halogen and/or C 1 to C 10 alkyl and/or C 1 to C 10 alkoxy and in which up to six carbon atoms may be replaced by oxygen, in which case at least two carbon atoms shall be present between two oxygen atoms and the R 5 moiety starts with at least two carbon atoms, wherein the terminal methyl group of the linear C 5 to C 20 alkyl moiety shall be unsubstituted.
- R 1 , R 2 , R 3 and R 4 are each independently hydrogen, halogen, alkyl, alkoxy, alkenyl, alkynyl, alkylthio, alkylseleno, wherein R 1 and R 2 and/or R 3 and R 4 may combine to form a 3 to 5-membered saturated or unsaturated bridge optionally substituted with up to 2 heteroatoms and R 5 is linear C 5 to C 20 alkyl which is optionally substituted in any manner by halogen and/or C 1 to C 10 alkyl and/or C 1 to C 10 alkoxy and in which up to six carbon atoms may be replaced by oxygen, in which case at least two carbon atoms shall be present between two oxygen atoms and the R 5 moiety starts with at least two carbon atoms, wherein the terminal methyl group of the linear C 5 to C 20 alkyl moiety shall be unsubstituted, wherein the compound of formula I where R 5 is C 5 alkyl,
- X is halogen and R 1 , R 2 , R 3 and R 4 are each independently hydrogen, halogen, alkyl, alkoxy, alkenyl, alkynyl, alkylthio, alkylseleno, wherein R 1 and R 2 and/or R 3 and R 4 may combine to form a 3 to 5-membered saturated or unsaturated bridge optionally substituted with up to 2 heteroatoms and R 5 is linear C 5 to C 20 alkyl which is optionally substituted in any manner by halogen and/or C 1 to C 10 alkyl and/or C 1 to C 10 alkoxy and in which up to six carbon atoms may be replaced by oxygen, in which case at least two carbon atoms shall be present between two oxygen atoms and the R 5 moiety starts with at least two carbon atoms, wherein the terminal methyl group of the linear C 6 to C 20 alkyl moiety shall be unsubstituted.
- media which comprise a compound of formula (I) according to the present invention have a higher level of photosensitivity and hence are very useful for exposure using pulsed lasers.
- the X moiety represents chlorine.
- R 1 , R 2 , R 3 and R 4 are each hydrogen.
- R 5 may in one embodiment of the invention be linear C 6 to C 20 alkyl which is optionally substituted in any manner by halogen and/or C 1 to C 4 alkyl and/or C 1 to C 4 alkoxy and in which up to six carbon atoms may be replaced by oxygen, in which case at least two carbon atoms shall be present between two oxygen atoms and the R 5 moiety starts with at least two carbon atoms, wherein the terminal methyl group of the linear C 6 to C 20 alkyl moiety shall be unsubstituted.
- the compound of formula (I) has an X moiety representing chlorine, the moieties R 1 , R 2 , R 3 and R 4 each representing H and R 5 representing 2-ethylhexanol.
- EP 0332 042 A2 4,6-bis-trichloromethyl-s-triazin-2-yl-phenyl derivatives are obtainable from aromatic nitriles and trichloroacetonitrile by cyclocotrimerization.
- the 3- or 4-cyano-substituted methyl benzoate or cinnamate esters are reacted with trichloroacetonitrile and then the resultant 4,6-bistrichloromethyl-s-triazine-substituted methyl benzoate or cinnamate ester is transesterified in a costly and inconvenient manner involving in some instances multiple steps.
- R 1 to R 5 are each as defined under formula (I), R 5 is methyl or ethyl or isomeric propyl, and A is a catalyst A, in a one-pot process wherein component (III) is used in excess, components V, III and IV are distillatively removed in the stated order in three steps by adjusting the pressure and the temperature, and the difference in the boiling points of compounds (V) and (III) and in the boiling points of compounds (III) and (IV) is not less than 50° C. in either case.
- an ester of formula (II) where R 1 to R 4 are each as defined under formula (I) and R 6 are methyl or ethyl or the isomeric propyls is converted in the presence of an alcohol (III) where R 5 is as defined above and in the presence of a catalyst A, by heating in a first step at an internal temperature of 100-150° C. and a pressure of 300-1000 mbar with an excess of 1.1 to 10 equivalents of (III) until the conversion of (II) is complete and distillatively removing (V) from the reaction mixture and a subsequent step of distillatively removing excess alcohol (III) at a overhead temperature of 50-150° C. and a pressure of 1-300 mbar followed in a subsequent step by the distillation of product (IV) at an overhead temperature of 100-250° C. and a pressure of 0.01-1 mbar, leaving catalyst A behind in the pot.
- an alcohol (III) where R 5 is as defined above and in the presence of a catalyst A by heating in a first step at
- Step 1 utilizes an internal temperature of 100-150° C., preferably 110-145° C., more preferably 120-140° C. at a pressure of 300-1000 mbar, preferably 350-800 mbar, more preferably 400-600 mbar with an excess of 1.1 to 10 equivalents of (III), preferably of 1.2 to 5 equivalents, more preferably of 1.3 to 2 equivalents.
- the second step utilizes an overhead temperature of 50-150° C., preferably 60-125° C., more preferably 70-100° C. and a pressure of 1-300 mbar, preferably 3-100 mbar, more preferably 5-50 mbar.
- the third step utilizes an overhead temperature of 100-250° C., preferably of 125-240° C., more preferably of 150-230° C. and a pressure of 0.01-1 mbar, preferably of 0.02-0.5 mbar.
- Alcohol (III) is suitably any compound having not less than five and up to 20 aliphatic optionally halogen- or oxygen-substituted carbon atoms bearing at least one methyl group. Preference is given to compounds having not less than six and up to 15 aliphatic optionally halogen- or oxygen-substituted carbon atoms bearing at least one methyl group. Particular preference is given to compounds having not less than seven and up to 10 aliphatic optionally halogen- or oxygen-substituted carbon atoms bearing at least one methyl group.
- Catalyst A is suitably, the fundamentally described in Methoden der organischen Chemie (Houben-Weyl), Volume E5, 1, III.a) ⁇ , ⁇ 1 (pp. 702 ff, Pielartzik, Irmscher-Pielartzik and Eicher), catalysts such as protic acids, basic catalysts (alkanoates, anion exchangers), titanium(IV) and zirconium(IV) alkanoates, alkoxytrialkyltin and also copper alkanoate/triphenylphosphane complexes.
- the catalysts are in liquid form, have a higher boiling point than the desired product and are effective in low concentration in ensuring rapid and complete conversion. Higher titanium(IV) and zirconium(IV) alkanoates are therefore particularly preferable. Particular preference is given especially to higher titanium(IV) and zirconium (IV) alkanoates wherein the alkanoate corresponds to that of compound (III).
- catalyst A is further preferable for catalyst A to be employed in an amount of 0.0001 to 0.1 equivalent relative to employed compound (II), more preferably of 0.0005 to 0.01 equivalent and yet more preferably 0.001 to 0.005 equivalent.
- the invention further provides a process for preparing compounds (I) which comprises utilizing the one-pot process to prepare para-disubstituted benzonitriles of formula (IV) in a first step and reacting the resulting para-disubstituted benzonitrile with trihaloacetonitrile in a second step.
- the invention further provides a photopolymer formulation comprising a photopolymerizable component and at least one compound of formula (I).
- the photopolymer formulation comprises matrix polymers, at least one writing monomer and a photoinitiator system comprising at least one compound of formula (I).
- the matrix polymers of the photopolymer formulation according to the present invention may be particularly in a crosslinked state and more preferably in a three-dimensionally crosslinked state.
- the matrix polymers may be polyurethanes, in which case the polyurethanes may be obtainable in particular by reacting at least one polyisocyanate component a) with at least one isocyanate-reactive component b).
- the polyisocyanate component a) preferably comprises at least one organic compound having at least two NCO groups. These organic compounds may especially be monomeric di- and triisocyanates, polyisocyanates and/or NCO-functional prepolymers.
- the polyisocyanate component a) may also contain or consist of mixtures of monomeric di- and triisocyanates, polyisocyanates and/or NCO-functional prepolymers.
- Monomeric di- and triisocyanates used may be any of the compounds that are well known per se to those skilled in the art, or mixtures thereof. These compounds may have aromatic, araliphatic, aliphatic or cycloaliphatic structures.
- the monomeric di- and triisocyanates may also comprise minor amounts of monoisocyanates, i.e. organic compounds having one NCO group.
- Suitable monomeric di- and triisocyanates are butane 1,4-diisocyanate, pentane 1,5-diisocyanate, hexane 1,6-diisocyanate (hexamethylene diisocyanate, HDI), 2,2,4-trimethylhexamethylene diisocyanate and/or 2,4,4-trimethylhexamethylene diisocyanate (TMDI), isophorone diisocyanate (IPDI), 1,8-diisocyanate-4-(isocyanatomethyl)octane, bis(4,4′-isocyanato-cyclohexyl)methane and/or bis(2′,4′isocyanatocyclohexyl)methane and/or mixtures thereof having any isomer content, cyclohexane 1,4-diisocyanate, the isomeric bis(isocyanatemethyl)-cyclohexanes, 2,4- and/or 2,6-diiso
- Suitable polyisocyanates are compounds which have urethane, urea, carbodiimide, acylurea, amide, isocyanurate, allophanate, biuret, oxadiazinetrione, uretdione and/or iminooxadiazinedione structures and are obtainable from the aforementioned di- or triisocyanates.
- the polyisocyanates are oligomerized aliphatic and/or cycloaliphatic di- or triisocyanates, it being possible to use especially the above aliphatic and/or cycloaliphatic di- or triisocyanates.
- polyisocyanates having isocyanurate, uretdione and/or iminooxadiazinedione structures, and biurets based on HDI or mixtures thereof.
- Suitable prepolymers contain urethane and/or urea groups, and optionally further structures formed through modification of NCO groups as specified above.
- Prepolymers of this kind are obtainable, for example, by reaction of the abovementioned monomeric di- and triisocyanates and/or polyisocyanates a1) with isocyanate-reactive compounds b1).
- Isocyanate-reactive compounds b1) used may be alcohols, amino or mercapto compounds, preferably alcohols. These may especially be polyols. Most preferably, isocyanate-reactive compounds b1) used may be polyester polyols, polyether polyols, polycarbonate polyols, poly(meth)acrylate polyols and/or polyurethane polyols.
- Suitable polyester polyols are, for example, linear polyester diols or branched polyester polyols, which can be obtained in a known manner by reaction of aliphatic, cycloaliphatic or aromatic di- or polycarboxylic acids or anhydrides thereof with polyhydric alcohols of OH functionality ⁇ 2.
- Suitable di- or polycarboxylic acids are polybasic carboxylic acids such as succinic acid, adipic acid, suberic acid, sebacic acid, decanedicarboxylic acid, phthalic acid, terephthalic acid, isophthalic acid, tetrahydrophthalic acid or trimellitic acid, and acid anhydrides such as phthalic anhydride, trimellitic anhydride or succinic anhydride, or any desired mixtures thereof.
- the polyester polyols may also be based on natural raw materials such as castor oil. It is likewise possible that the polyester polyols are based on homo- or copolymers of lactones, which can preferably be obtained by addition of lactones or lactone mixtures, such as butyrolactone, ⁇ -caprolactone and/or methyl- ⁇ -caprolactone onto hydroxy-functional compounds such as polyhydric alcohols of OH functionality ⁇ 2, for example of the abovementioned type.
- suitable alcohols are all polyhydric alcohols, for example the C 2 -C 12 diols, the isomeric cyclohexanediols, glycerol or any desired mixtures thereof.
- Suitable polycarbonate polyols are obtainable in a manner known per se by reaction of organic carbonates or phosgene with diols or diol mixtures.
- Suitable organic carbonates are dimethyl, diethyl and diphenyl carbonate.
- Suitable diols or mixtures comprise the polyhydric alcohols of OH functionality ⁇ 2 mentioned per se in the context of the polyester segments, preferably butane-1,4-diol, hexane-1,6-diol and/or 3-methylpentanediol. It is also possible to convert polyester polyols to polycarbonate polyols.
- Suitable polyether polyols are polyaddition products, optionally of blockwise structure, of cyclic ethers onto OH— or NH-functional starter molecules.
- Suitable cyclic ethers are, for example, styrene oxides, ethylene oxide, propylene oxide, tetrahydrofuran, butylene oxide, epichlorohydrin, and any desired mixtures thereof.
- Starters used may be the polyhydric alcohols of OH functionality ⁇ 2 mentioned per se in the context of the polyester polyols, and also primary or secondary amines and amino alcohols.
- Preferred polyether polyols are those of the aforementioned type based exclusively on propylene oxide, or random or block copolymers based on propylene oxide with further 1-alkylene oxides. Particular preference is given to propylene oxide homopolymers and random or block copolymers containing oxyethylene, oxypropylene and/or oxybutylene units, where the proportion of the oxypropylene units based on the total amount of all the oxyethylene, oxypropylene and oxybutylene units amounts to at least 20% by weight, preferably at least 45% by weight.
- Oxypropylene and oxybutylene here encompasses all the respective linear and branched C 3 and C 4 isomers.
- polyfunctional, isocyanate-reactive compounds are also low molecular weight (i.e. with molecular weights ⁇ 500 g/mol), short-chain (i.e. containing 2 to 20 carbon atoms), aliphatic, araliphatic or cycloaliphatic di-, tri- or polyfunctional alcohols.
- neopentyl glycol 2-ethyl-2-butylpropanediol, trimethylpentanediol, positionally isomeric diethyloctanediols, cyclohexanediol, 1,4-cyclohexanedimethanol, 1,6-hexanediol, 1,2- and 1,4-cyclohexanediol, hydrogenated bisphenol A, 2,2-bis(4-hydroxycyclohexyl)propane or 2,2-dimethyl-3-hydroxypropyl 2,2-dimethyl-3-hydroxypropionate.
- triols examples are trimethylolethane, trimethylolpropane or glycerol.
- Suitable higher-functionality alcohols are di(trimethylolpropane), pentaerythritol, dipentaerythritol or sorbitol.
- the polyol component is a difunctional polyether, polyester, or a polyether-polyester block copolyester or a polyether-polyester block copolymer having primary OH functions.
- amines as isocyanate-reactive compounds b1).
- suitable amines are ethylenediamine, propylenediamine, diaminocyclohexane, 4,4′-dicyclohexylmethane-diamine, isophoronediamine (IPDA), difunctional polyamines, for example the Jeffamines®, amine-terminated polymers, especially having number-average molar masses ⁇ 10 000 g/mol. Mixtures of the aforementioned amines can likewise be used.
- amino alcohols as isocyanate-reactive compounds b1).
- suitable amino alcohols are the isomeric aminoethanols, the isomeric aminopropanols, the isomeric aminobutanols and the isomeric aminohexanols, or any desired mixtures thereof.
- All the aforementioned isocyanate-reactive compounds b1) can be mixed with one another as desired.
- the isocyanate-reactive compounds b1) have a number-average molar mass of ⁇ 200 and ⁇ 10 000 g/mol, further preferably ⁇ 500 and ⁇ 8000 g/mol and most preferably ⁇ 800 and ⁇ 5000 g/mol.
- the OH functionality of the polyols is preferably 1.5 to 6.0, more preferably 1.8 to 4.0.
- the prepolymers of the polyisocyanate component a) may especially have a residual content of free monomeric di- and triisocyanates of ⁇ 1% by weight, more preferably ⁇ 0.5% by weight and most preferably ⁇ 0.3% by weight.
- the polyisocyanate component a) contains, entirely or in part, organic compound whose NCO groups have been fully or partly reacted with blocking agents known from coating technology.
- blocking agents are alcohols, lactams, oximes, malonic esters, pyrazoles, and amines, for example butanone oxime, diisopropylarnine, diethyl malonate, ethyl acetoacetate, 3,5-dimethylpyrazole, ⁇ -caprolactam, or mixtures thereof.
- the polyisocyanate component a) comprises compounds having aliphatically bonded NCO groups, aliphatically bonded NCO groups being understood to mean those groups that are bonded to a primary carbon atom.
- the isocyanate-reactive component b) preferably comprises at least one organic compound having an average of at least 1.5 and preferably 2 to 3 isocyanate-reactive groups.
- isocyanate-reactive groups are regarded as being preferably hydroxyl, amino or mercapto groups.
- the isocyanate-reactive component may especially comprise compounds having a numerical average of at least 1.5 and preferably 2 to 3 isocyanate-reactive groups.
- Suitable polyfunctional isocyanate-reactive compounds of component b) are for example the above-described compounds b1).
- the writing monomer c) comprises or consists of at least one mono- and/or one multifunctional writing monomer.
- the writing monomer may comprise or consist of at least one mono- and/or one multifunctional (meth)acrylate writing monomer.
- the writing monomer may comprise or consist of at least one mono- and/or one multifunctional urethane (meth)acrylate.
- Suitable acrylate writing monomers are especially compounds of the general formula (VI)
- n ⁇ 1 and n ⁇ 4 and R 7 is a linear, branched, cyclic or heterocyclic organic radical which is unsubstituted or else optionally substituted by heteroatoms and/or R 8 is hydrogen or a linear, branched, cyclic or heterocyclic organic radical which is unsubstituted or else optionally substituted by heteroatoms. More preferably, R 8 is hydrogen or methyl and/or R 7 is a linear, branched, cyclic or heterocyclic organic radical which is unsubstituted or else optionally substituted by heteroatoms.
- Acrylates and methacrylates refer, respectively, to esters of acrylic acid and methacrylic acid.
- Examples of acrylates and methacrylates usable with preference are phenyl acrylate, phenyl methacrylate, phenoxyethyl acrylate, phenoxyethyl methacrylate, phenoxyethoxyethyl acrylate, phenoxyethoxyethyl methacrylate, phenylthioethyl acrylate, phenylthioethyl methacrylate, 2-naphthyl acrylate, 2-naphthyl methacrylate, 1,4-bis(2-thionaphthyl)-2-butyl acrylate, 1,4-bis(2-thionaphthyl)-2-butyl methacrylate, bisphenol A diacrylate, bisphenol A dimethacrylate, and the ethoxylated analogue compounds thereof, N-carbazolyl acrylates
- Urethane acrylates are understood to mean compounds having at least one acrylic ester group and at least one urethane bond. Compounds of this kind can be obtained, for example, by reacting a hydroxy-functional acrylate or methacrylate with an isocyanate-functional compound.
- isocyanate-functional compounds usable for this purpose are monoisocyanates, and the monomeric diisocyanates, triisocyanates and/or polyisocyanates mentioned under a).
- suitable monoisocyanates are phenyl isocyanate, the isomeric methylthiophenyl isocyanates.
- Di-, tri- or polyisocyanates have been mentioned above, and also triphenylmethane 4,4′,4′′-triisocyanate and tris(p-isocyanatophenyl) thiophosphate or derivatives thereof with urethane, urea, carbodiimide, acylurea, isocyanurate, allophanate, biuret, oxadiazinetrione, uretdione, iminooxadiazinedione structure and mixtures thereof. Preference is given to aromatic di-, tri- or polyisocyanates.
- Useful hydroxy-functional acrylates or methacrylates for the preparation of urethane acrylates include, for example, compounds such as 2-hydroxyethyl (meth)acrylate, polyethylene oxide mono(meth)acrylates, polypropylene oxide mono(meth)acrylates, polyalkylene oxide mono(meth)acrylates, poly(c-caprolactone) mono(meth)acrylates, for example Tone® M100 (Dow, Schwalbach, DE), 2-hydroxypropyl (meth)acrylate, 4-hydroxybutyl (meth)acrylate, 3-hydroxy-2,2-dimethylpropyl (meth)acrylate, hydroxypropyl (meth)acrylate, 2-hydroxy-3-phenoxypropyl acrylate, the hydroxy-functional mono-, di- or tetraacrylates of polyhydric alcohols such as trimethylolpropane, glycerol, pentaerythritol, dipentaerythritol, ethoxylated, propoxylated
- hydroxyl-containing epoxy(meth)acrylates having OH contents of 20 to 300 mg KOH/g or hydroxyl-containing polyurethane (meth)acrylates having OH contents of 20 to 300 mg KOH/g or acrylated polyacrylates having OH contents of 20 to 300 mg KOH/g and mixtures thereof, and mixtures with hydroxyl-containing unsaturated polyesters and mixtures with polyester (meth)acrylates or mixtures of hydroxyl-containing unsaturated polyesters with polyester (meth)acrylates.
- urethane acrylates obtainable from the reaction of tris(p-isocyanatophenyl) thiophosphate and/or m-methylthiophenyl isocyanate with alcohol-functional acrylates such as hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate and/or hydroxybutyl (meth)acrylate.
- the writing monomer comprises or consists of further unsaturated compounds such as ⁇ , ⁇ -unsaturated carboxylic acid derivatives, for example maleates, fumarates, maleimides, acrylamides, and also vinyl ethers, propenyl ethers, allyl ethers and compounds containing dicyclopentadienyl units, and also olefinically unsaturated compounds, for example styrene, ⁇ -methylstyrene, vinyltoluene and/or olefins.
- further unsaturated compounds such as ⁇ , ⁇ -unsaturated carboxylic acid derivatives, for example maleates, fumarates, maleimides, acrylamides, and also vinyl ethers, propenyl ethers, allyl ethers and compounds containing dicyclopentadienyl units, and also olefinically unsaturated compounds, for example styrene, ⁇ -methylstyrene, vinyltoluene and
- Photoinitiators of component d) are compounds activatable typically by means of actinic radiation, which can trigger polymerization of the writing monomers.
- they are distinguished by their chemical nature as photoinitiators for free-radical, anionic, cationic or mixed types of polymerization.
- Type I photoinitiators for free-radical photopolymerization form free radicals on irradiation through unimolecular bond scission.
- type I photoinitiators are triazines, oximes, benzoin ethers, benzil ketals, bisimidazoles, aroylphosphine oxides, sulphonium salts and iodonium salts.
- Type II photoinitiators for free-radical polymerization consist of a dye as sensitizer and a coinitiator, and undergo a bimolecular reaction on irradiation with light matched to the dye. First of all, the dye absorbs a photon and transfers energy from an excited state to the coinitiator. The latter releases the polymerization-triggering free radicals through electron or proton transfer or direct hydrogen abstraction.
- Photoinitiator systems of this kind are described in principle in EP 0 223 587 A and consist preferably of a mixture of one or more dyes with ammonium alkylarylborate(s).
- Suitable dyes which, together with an ammonium alkylarylborate, form a type II photoinitiator are the cationic dyes described in WO 2012062655, in combination with the anions likewise described therein.
- Cationic dyes are preferably understood to mean those from the following classes: acridine dyes, xanthene dyes, thioxanthene dyes, phenazine dyes, phenoxazine dyes, phenothiazine dyes, tri(het)arylmethane dyes—especially diamino- and triamino(het)arylmethane dyes, mono-, di-, tri- and pentamethinecyanine dyes, hemicyanine dyes, externally cationic merocyanine dyes, externally cationic neutrocyanine dyes, zeromethine dyes—especially naphtholactam dyes, streptocyanine dyes.
- Dyes of this kind are described, for example, in H. Berneth in Ullmann's Encyclopedia of Industrial Chemistry, Azine Dyes, Wiley-VCH Verlag, 2008, H. Berneth in Ullmann's Encyclopedia of Industrial Chemistry, Methine Dyes and Pigments, Wiley-VCH Verlag, 2008, T. Gessner, U. Mayer in Ullmann's Encyclopedia of Industrial Chemistry, Triarylmethane and Diarylmethane Dyes, Wiley-VCH Verlag, 2000.
- phenazine dyes particularly preference is given to phenazine dyes, phenoxazine dyes, phenothiazine dyes, tri(het)arylmethane dyes—especially diamine- and triamino(het)arylmethane dyes, mono-, di-, tri- and pentamethinecyanine dyes, hemicyanine dyes, zeromethine dyes—especially naphtholactam dyes, streptocyanine dyes.
- cationic dyes are Astrazon Orange G, Basic Blue 3, Basic Orange 22, Basic Red 13, Basic Violet 7, Methylene Blue, New Methylene Blue, Azure A, 2,4-diphenyl-6-(4-methoxyphenyl)pyrylium, Safranin O, Astraphloxin, Brilliant Green, Crystal Violet, Ethyl Violet and thionine.
- Preferred anions are especially C 8 - to C 25 -alkanesulphonate, preferably C 13 - to C 25 -alkanesulphonate, C 3 - to C 18 -perfluoroalkanesulphonate, C 4 - to C 18 -perfluoroalkanesulphonate hearing at least 3 hydrogen atoms in the alkyl chain, C 9 - to C 25 -alkanoate, C 9 - to C 25 -alkenoate, C 8 - to C 25 -alkylsulphate, preferably C 13 - to C 25 -alkylsulphate, C 8 - to C 25 -alkenylsulphate, preferably C 13 - to C 25 -alkenylsulphate, C 3 - to C 18 -perfluoroalkylsulphate, C 4 - to C 18 -perfluoroalkylsulphate bearing at least 3 hydrogen atoms in the alkyl chain, polyether s
- the anion A ⁇ of the dye has an AC log P in the range from 1 to 30, more preferably in the range from 1 to 12 and especially preferably in the range from 1 to 6.5.
- AC log P is computed after J. Comput. Aid. [mol %] Des. 2005, 19, 453; Virtual Computational Chemistry Laboratory, http://www.vcclab.org.
- Suitable ammonium alkylarylborates are, for example (Cunningham et al., RadTech'98 North America UV/EB Conference Proceedings, Chicago, Apr. 19-22, 1998): tetrabutylammonium triphenylhexylborate, tetrabutylammonium triphenylbutylborate, tetrabutylammonium trinaphthyl-hexylborate, tetrabutylammonium tris(4-tert-butyl)phenylbutylborate, tetrabutylammonium tris(3-fluorophenyl)hexylborate hexylborate ([191726-69-9], CGI 7460, product from BASF SE, Basle, Switzerland), 1-methyl-3-octylimidazolium dipentyldiphenylborate and tetrabutylammonium tris(3-chloro-4-methylphenyl
- photoinitiators it may be advantageous to use mixtures of these photoinitiators.
- the type and concentration of photoinitiator has to be adjusted in the manner known to those skilled in the art. Further details are described, for example, in P. K. T. Oldring (Ed.), Chemistry & Technology of UV & EB Formulations For Coatings, Inks & Paints, vol. 3, 1991, SITA Technology, London, p. 61-328.
- the photoinitiator comprises a combination of dyes whose absorption spectra at least partly cover the spectral range from 400 to 800 nm, with at least one coinitiator matched to the dyes.
- At least one photoinitiator suitable for a laser light colour selected from blue, yellow, green and red is present in the photopolymer formulation.
- the photopolymer formulation contains one suitable photoinitiator each for at least two laser light colours selected from blue, green and red.
- the photopolymer formulation contains one suitable photoinitiator for each of the laser light colours blue, green and red.
- the photopolymer formulation additionally contains urethanes as additives, in which case the urethanes may especially be substituted by at least one fluorine atom.
- the urethanes may have the general formula (VII)
- R 10 and R 11 are linear, branched, cyclic or heterocyclic organic radicals which are unsubstituted or else optionally substituted by heteroatoms and/or R 10 , R 11 are each independently hydrogen, in which case preferably at least one of the R 9 , R 10 , R 11 radicals is substituted by at least one fluorine atom and, more preferably, R 9 is an organic radical having at least one fluorine atom. More preferably, R 10 is a linear, branched, cyclic or heterocyclic organic radical which is unsubstituted or else optionally substituted by heteroatoms, for example fluorine.
- the present invention further provides a photopolymer comprising a photopolymer formulation, in particular comprising matrix polymers, writing monomer and a photoinitiator system and further comprising a compound of formula (I).
- the matrix polymers of the photopolymer formulation according to the present invention may be particularly in a crosslinked state and more preferably in a three-dimensionally crosslinked state.
- the matrix polymers may be polyurethanes, in which case the polyurethanes may be obtainable in particular by reacting at least one polyisocyanate component with at least one isocyanate-reactive component.
- the invention also provides a holographic medium particularly in the form of a film comprising a photopolymer of the present invention or obtainable by using a photopolymer formulation of the present invention.
- the invention yet further provides for the use of a photopolymer formulation of the present invention in the production of holographic media.
- holographic information has been exposed into same.
- the inventive holographic media can be processed into holograms by means of appropriate exposure processes for optical applications over the entire visible and in the near UV range (300-800 nm).
- Visual holograms include all holograms which can be recorded by methods known to those skilled in the art. These include in-line (Gabor) holograms, off-axis holograms, full-aperture transfer holograms, white light transmission holograms (“rainbow holograms”), Denisyuk holograms, off-axis reflection holograms, edge-lit holograms and holographic stereograms. Preference is given to reflection holograms, Denisyuk holograms, transmission holograms.
- Possible optical functions of the holograms which can be produced with the inventive photopolymer formulations correspond to the optical functions of light elements such as lenses, mirrors, deflecting mirrors, filters, diffuser lenses, diffraction elements, diffusers light guides, waveguides, projection lenses and/or masks. It is likewise possible for combinations of these optical functions to be combined in one hologram independently of each other. These optical elements frequently have a frequency selectivity according to how the holograms have been exposed and the dimensions of the hologram.
- holographic images or representations for example for personal portraits, biometric representations in security documents, or generally of images or image structures for advertising, security labels, brand protection, branding, labels, design elements, decorations, illustrations, collectable cards, images and the like, and also images which can represent digital data, including in combination with the products detailed above.
- Holographic images can have the impression of a three-dimensional image, but they may also represent image sequences, short films or a number of different objects according to the angle from which and the light source with which (including moving light sources) etc. they are illuminated. Because of this variety of possible designs, holograms, especially volume holograms, constitute an attractive technical solution for the abovementioned application.
- the present invention accordingly further provides for the use of an inventive holographic medium for recording of in-line, off-axis, full-aperture transfer, white light transmission, Denisyuk, off-axis reflection or edge-lit holograms and also of holographic stereograms, in particular for production of optical elements, images or image depictions.
- the invention likewise provides holograms comprising the holographic medium of the present invention.
- the invention likewise provides a process for producing a hologram wherein pulsed laser radiation is used to expose the medium.
- the pulse duration is ⁇ 200 ns, preferably ⁇ 100 ns, more preferably ⁇ 60 ns.
- the pulse duration must not be less than 0.5 ns.
- a pulse duration of 4 ns is particularly preferable.
- the present invention further also provides a process for producing a holographic medium by using a photopolymer formulation of the present invention.
- the photopolymer formulations can especially be used for production of holographic media in the form of a film.
- a ply of a material or material composite transparent to light within the visible spectral range (transmission greater than 85% within the wavelength range from 400 to 780 nm) as carrier substrate is coated on one or both sides, and a cover layer is optionally applied to the photopolymer ply or plies.
- Preferred materials or material composites for the carrier substrate are based on polycarbonate (PC), polyethylene terephthalate (PET), polybutylene terephthalate, polyethylene, polypropylene, cellulose acetate, cellulose hydrate, cellulose nitrate, cycloolefin polymers, polystyrene, polyepoxides, polysulphone, cellulose triacetate (A), polyamide, polymethylmethacrylate, polyvinyl chloride, polyvinyl butyral or polydicyclopentadiene or mixtures thereof. They are more preferably based on PC, PET and CTA. Material composites may be film laminates or coextrudates.
- the materials or material composites of the carrier substrate may be given an antiadhesive, antistatic, hydrophobized or hydrophilized finish on one or both sides.
- the modifications mentioned serve the purpose, on the side facing the photopolymer, of making the photopolymer detachable without destruction from the carrier substrate.
- Modification of the opposite side of the carrier substrate from the photopolymer serves to ensure that the inventive media satisfy specific mechanical demands which exist, for example, in the case of processing in roll laminators, especially in roll-to-roll processes.
- the overhead temperature was determined in degrees Celsius (° C.) using a 4-20 mA calibrated transmitter and a PT100 thermocouple installed in the boiling equilibrium above a packed column.
- the internal temperature was determined in degrees Celsius (° C.) using a 4-20 mA calibrated transmitter and a PT100 thermocouple installed in the reaction space.
- the Denisyuk hologram of a mirror was recorded in a sample consisting of a glass plate laminated with a photopolymer film.
- the substrate of the photopolymer film and the glass substrate faced laser source and the mirror, respectively.
- the sample was exposed with its planar face perpendicular to the laser beam. The distance between the sample and the mirror was 3 cm.
- the laser used was a Brilliant b pulsed laser from Quantel of France.
- the laser in question was a Q-switched Nd-YAG laser equipped with a module for frequency doubling to 532 nm.
- the single frequency mode was guaranteed by a seed laser.
- Coherence length was arithmetically about 1 m.
- Pulse duration was 4 ns and average power output was 3 watts at a pulse repetition rate of 10 Hz.
- the electronically controlled shutter was used to ensure a single pulse exposure.
- the waveplate made it possible to rotate the polarization plane of the laser light and the subsequent polarizer was used to reflect the S-polarized portion of the laser light in the direction of the sample.
- the exposed area was adjusted by beam expansion.
- the waveplate and the beam expander were adjusted such that the sample was given an exposure dose of 100 mJ/cm 2 /pulse.
- the samples were each exposed with exactly one pulse. After exposure, the sample was bleached on a light table.
- a transmission spectrum was measured through the hologram of the bleached sample.
- An HR4000 spectrometer from Ocean Optics was used. The sample was placed perpendicularly to the light beam.
- the transmission spectrum showed a transmission collapse at a wavelength at which the Bragg condition was satisfied.
- the depth of the transmission collapse to the base line was evaluated as the diffraction efficiency DE of the Denisyuk hologram of the mirror ( FIG. 3 ).
- the solvents used were obtained commercially.
- Fomrez UL 28 Urethanization catalyst commercial product of Momentive Performance Chemicals, Wilton, CT, USA.
- Sodium bis(2- [45297-26-5] is available from Aldrich Chemie, ethylhexyl)- Steinheim. sulphosuccinate
- 2-Ethylhexanol was collected at a pressure of 8.8-9.6 mbar and an overhead temperature of 65.5-68.5° C. in an amount of 3.14 kg. After renewed emptying of the receiver, the internal temperature was raised to 185-190° C. and a pressure of 0.25 mbar was applied. 2-Ethylhexyl 4-cyanobenzoate was obtained at an overhead temperature of 150.0-155.0° C. as a colourless oil in an amount of 14.04 kg (96.9% of theory).
- a 1 l flask was initially charged with 0.18 g of tin octoate, 374.8 g of ⁇ -caprolactone and 374.8 g of a difunctional polytetrahydrofuran polyether polyol (equivalent weight 500 g/mol OH), which were heated to 120° C. and kept at this temperature until the solids content (proportion of nonvolatile constituents) was 99.5% by weight or higher. Subsequently, the mixture was cooled and the product was obtained as a waxy solid.
- a 500 mL round-bottom flask was initially charged with 0.1 g of 2,6-di-tert-butyl-4-methylphenol, 0.05 g of dibutyltin dilaurate (Desmorapid® Z, Bayer MaterialScience AG, Leverkusen, Germany) and 213.07 g of a 27% solution of tris(p-isocyanatophenyl) thiophosphate in ethyl acetate (Desmodur® RFE, product from Bayer MaterialScience AG, Leverkusen, Germany), which were heated to 60° C. Subsequently, 42.37 g of 2-hydroxyethyl acrylate were added dropwise and the mixture was still kept at 60° C. until the isocyanate content had fallen below 0.1%. This was followed by cooling and complete removal of the ethyl acetate under reduced pressure. The product was obtained as a semicrystalline solid.
- a 100 mL round-bottom flask was initially charged with 0.02 g of 2,6-di-tert-butyl-4-methylphenol, 0.01 g of Desmorapid® Z, 11.7 g of 3-(methylthio)phenyl isocyanate [28479-1-8], and the mixture was heated to 60° C. Subsequently, 8.2 g of 2-hydroxyethyl acrylate were added dropwise and the mixture was still kept at 60° C. until the isocyanate content had fallen below 0.1%. This was followed by cooling. The product was obtained as a colourless liquid.
- a 50 mL round-bottom flask was initially charged with 0.02 g of Desmorapid® Z and 3.6 g of 2,4,4-trimethylhexane 1,6-diisocyanate (TMDI), and the mixture was heated to 60° C. Subsequently, 11.9 g of 2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoroheptan-1-ol were added dropwise and the mixture was still kept at 60° C. until the isocyanate content had fallen below 0.1%. This was followed by cooling. The product was obtained as a colourless oil.
- TMDI 2,4,4-trimethylhexane 1,6-diisocyanate
- the two-phase mixture was stirred for 1 h and then transferred into a separating funnel.
- the aqueous phase was dropped and the organic phase was washed four times with 40 mL of water.
- the organic phase was diluted with 250 mL of butyl acetate and distilled water-free in a rotary evaporator under reduced pressure. About 200 mL of butyl acetate were also distilled off in the process, to finally leave 150.1 g of a red solution of the dye of the formula
- FIG. 1 shows the schematic set-up of the coating range used.
- the individual component parts have the following reference signs:
- the formulation was briefly heated at 60° C. to speed up the dissolving of the materials used.
- This mixture was imported into one of the two stock reservoir vessels 1 of the coating range.
- the polyisocyanate component (Desmodur® N 3900, commercial product of Bayer MaterialScience AG, Leverkusen, Germany, polyisocyanate based on hexane diisocyanate, at least 30% proportion of iminooxadiazinedione, NCO content: 23.5%).
- the two components were then each fed through the metering devices 2 in a ratio of 942.2 (component mixture) to 57.8 (isocyanate) to the vacuum degassing device 3 and degassed. From there they were then each passed through the filters 4 into the static mixer 5 , where the components were mixed to form the photopolymer formulation.
- the liquid material obtained was then sent to the coating device 6 .
- the coating device 6 in the present case was a doctor blade system known to a person skilled in the art. Alternatively, however, it is also possible to use a slot die. Said coating device 6 was used to apply the photopolymer formulation at a processing temperature of 20° C. to a carrier substrate 8 in the form of a 36 ⁇ m thick polyethylene terephthalate foil and dried in a circulating air dryer 7 at a crosslinking temperature of 80° C. for 5.8 minutes to obtain a medium in the form of a film which was then provided a 40 ⁇ m thick polyethylene foil as covering layer 9 and wound up.
- the desired target layer thickness of the film was preferably between 1 and 60 ⁇ m, preferably from 5 to 25 ⁇ m, more preferably from 10 to 15 ⁇ m.
- the production speed was preferably in the range from 0.2 m/min to 300 m/min and more preferably in the range from 1.0 m/min to 50 m/min.
- the layer thickness obtained for the film was 12 ⁇ m ⁇ 1 ⁇ m.
- Comparative medium I was without Example 1 as described above.
- the media obtained as described were tested for their holographic properties by using a measuring arrangement as per FIG. 2 in the manner described above (Determination of diffraction efficiency in pulsed exposure). The following measurements were obtained for DE at a fixed dose of 100 ml/cm 2 :
- Example medium 1 shows that the inventive formula (I) compounds used in the photopolymer formulations are very useful in holographic media to be exposed with pulsed laser. Comparative medium 1 is free from any formula (I) compound according to the invention and is unsuitable for use in holographic media to be exposed with pulsed laser.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Spectroscopy & Molecular Physics (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Polyurethanes Or Polyureas (AREA)
- Holo Graphy (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Polymerisation Methods In General (AREA)
- Diffracting Gratings Or Hologram Optical Elements (AREA)
- Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP15173235.1 | 2015-06-23 | ||
EP15173235 | 2015-06-23 | ||
PCT/EP2016/064304 WO2016207157A1 (fr) | 2015-06-23 | 2016-06-21 | Triazines substituées |
Publications (1)
Publication Number | Publication Date |
---|---|
US20180180994A1 true US20180180994A1 (en) | 2018-06-28 |
Family
ID=53487235
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/738,892 Abandoned US20180180994A1 (en) | 2015-06-23 | 2016-06-21 | Substituted triazines |
US15/738,905 Expired - Fee Related US10308619B2 (en) | 2015-06-23 | 2016-06-21 | Substituted triazines and a method for producing same |
US16/386,364 Abandoned US20190263761A1 (en) | 2015-06-23 | 2019-04-17 | Substituted triazines and a method for producing same |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/738,905 Expired - Fee Related US10308619B2 (en) | 2015-06-23 | 2016-06-21 | Substituted triazines and a method for producing same |
US16/386,364 Abandoned US20190263761A1 (en) | 2015-06-23 | 2019-04-17 | Substituted triazines and a method for producing same |
Country Status (7)
Country | Link |
---|---|
US (3) | US20180180994A1 (fr) |
EP (2) | EP3313827B1 (fr) |
JP (2) | JP7012535B2 (fr) |
KR (2) | KR20180019114A (fr) |
CN (2) | CN107922360B (fr) |
TW (2) | TW201718525A (fr) |
WO (2) | WO2016207158A1 (fr) |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP3313827B1 (fr) * | 2015-06-23 | 2019-11-06 | Covestro Deutschland AG | Triazines substituees |
TW201906882A (zh) * | 2017-05-09 | 2019-02-16 | 德商科思創德意志股份有限公司 | 含有用於全像照射的光聚合物層及高度耐性漆層之薄膜結構 |
EP3470466A1 (fr) * | 2017-10-13 | 2019-04-17 | LANXESS Deutschland GmbH | Nouveaux colorants méthyne |
ES2963992T3 (es) * | 2021-02-11 | 2024-04-03 | Xetos Ag | Sistema 2K |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE576228A (fr) | 1958-03-04 | |||
JPS5225785A (en) * | 1975-08-19 | 1977-02-25 | Mitsubishi Chem Ind Ltd | Preparation of 2-substituted-4- trichloromethyl-6-trifluoromethyl-s- t riazines |
DE3677527D1 (de) | 1985-11-20 | 1991-03-21 | Mead Corp | Ionische farbstoffe als initiatoren enthaltende fotosensitive materialien. |
DE3807378A1 (de) * | 1988-03-07 | 1989-09-21 | Hoechst Ag | Durch 4,6-bis-trichlormethyl-s-triazin-2-ylgruppen substituierte aromatische verbindungen, verfahren zu ihrer herstellung und ihre verwendung in lichtempfindlichen gemischen |
US5147758A (en) * | 1991-02-19 | 1992-09-15 | E. I. Du Pont De Nemours And Company | Red sensitive photopolymerizable compositions |
US5489499A (en) * | 1993-10-26 | 1996-02-06 | Fuji Photo Film Co., Ltd. | Photosensitive trihalomethyl-s-triazine compound and photopolymerizable composition |
US6010821A (en) * | 1997-05-23 | 2000-01-04 | Minnesota Mining And Manufacturing Company | Aqueous developable color proofing elements |
TWI331034B (en) | 2002-07-08 | 2010-10-01 | Piramal Life Sciences Ltd | Inhibitors of cyclin-dependent kinases and their use |
JP3830869B2 (ja) | 2002-07-12 | 2006-10-11 | 花王株式会社 | ポリエステル樹脂用可塑剤 |
CA2494668A1 (fr) | 2002-07-27 | 2004-02-05 | Astrazeneca Ab | Composes chimiques |
US7084182B2 (en) | 2003-03-13 | 2006-08-01 | Tokuyama Corporation | Photopolymerization initiator |
JP2005049608A (ja) * | 2003-07-29 | 2005-02-24 | Fuji Photo Film Co Ltd | 体積型ホログラム記録用感光性組成物及びそれを用いた体積型ホログラム記録媒体 |
EP1510862A3 (fr) | 2003-08-25 | 2006-08-09 | Fuji Photo Film Co., Ltd. | Procédé d'enregistrement d'hologrammes et matériau pour l'enregistrement d'hologrammes |
JP5225785B2 (ja) * | 2008-08-18 | 2013-07-03 | ローム株式会社 | 過電流保護回路及びこれを用いた電源装置 |
IL200997A0 (en) | 2008-10-01 | 2010-06-30 | Bayer Materialscience Ag | Special polyether-based polyurethane formulations for the production of holographic media |
WO2011084519A1 (fr) | 2009-12-17 | 2011-07-14 | Millennium Pharmaceuticals, Inc. | Procédés de synthèse d'inhibiteurs du facteur xa |
US9366957B2 (en) | 2010-02-02 | 2016-06-14 | Covestro Deutschland Ag | Photopolymer formulation having triazine-based writing monomers |
JP5757749B2 (ja) | 2010-05-19 | 2015-07-29 | 富士フイルム株式会社 | 重合性組成物 |
EP2450387A1 (fr) * | 2010-11-08 | 2012-05-09 | Bayer MaterialScience AG | Formule photopolymère pour la fabrication de supports holographiques |
EP2450893A1 (fr) | 2010-11-08 | 2012-05-09 | Bayer MaterialScience AG | Formule photopolymère pour la fabrication de supports holographiques dotés de polymères à matrice hautement réticulés |
JP5803401B2 (ja) | 2011-08-05 | 2015-11-04 | Tdk株式会社 | ホログラム記録材料及びホログラム記録媒体 |
FR2999572B1 (fr) | 2012-12-17 | 2014-11-28 | Arkema France | Procede de production d'acrylate d'alkyle. |
ITMI20130357A1 (it) * | 2013-03-08 | 2014-09-09 | 3V Sigma Spa | Forma cristallina di un derivato triazinico e relativo procedimento per la sua produzione |
JP2017504827A (ja) | 2013-12-20 | 2017-02-09 | コベストロ、ドイチュラント、アクチエンゲゼルシャフトCovestro Deutschland Ag | 改善された光感受性を備えるホログラフィック媒体 |
EP3313827B1 (fr) | 2015-06-23 | 2019-11-06 | Covestro Deutschland AG | Triazines substituees |
-
2016
- 2016-06-21 EP EP16733370.7A patent/EP3313827B1/fr active Active
- 2016-06-21 CN CN201680048949.6A patent/CN107922360B/zh not_active Expired - Fee Related
- 2016-06-21 JP JP2017566391A patent/JP7012535B2/ja active Active
- 2016-06-21 US US15/738,892 patent/US20180180994A1/en not_active Abandoned
- 2016-06-21 EP EP16730415.3A patent/EP3313826B1/fr active Active
- 2016-06-21 WO PCT/EP2016/064305 patent/WO2016207158A1/fr unknown
- 2016-06-21 JP JP2017566392A patent/JP6810925B2/ja active Active
- 2016-06-21 WO PCT/EP2016/064304 patent/WO2016207157A1/fr active Application Filing
- 2016-06-21 US US15/738,905 patent/US10308619B2/en not_active Expired - Fee Related
- 2016-06-21 KR KR1020177036652A patent/KR20180019114A/ko active IP Right Grant
- 2016-06-21 TW TW105119374A patent/TW201718525A/zh unknown
- 2016-06-21 CN CN201680037062.7A patent/CN107750246B/zh active Active
- 2016-06-21 TW TW105119379A patent/TW201708197A/zh unknown
- 2016-06-21 KR KR1020187001621A patent/KR20180019200A/ko unknown
-
2019
- 2019-04-17 US US16/386,364 patent/US20190263761A1/en not_active Abandoned
Also Published As
Publication number | Publication date |
---|---|
EP3313826A1 (fr) | 2018-05-02 |
EP3313827B1 (fr) | 2019-11-06 |
US20190263761A1 (en) | 2019-08-29 |
CN107922360A (zh) | 2018-04-17 |
JP7012535B2 (ja) | 2022-02-14 |
EP3313826B1 (fr) | 2020-01-08 |
JP6810925B2 (ja) | 2021-01-13 |
CN107750246B (zh) | 2021-10-22 |
WO2016207157A1 (fr) | 2016-12-29 |
CN107922360B (zh) | 2021-05-25 |
JP2018524328A (ja) | 2018-08-30 |
CN107750246A (zh) | 2018-03-02 |
JP2018526328A (ja) | 2018-09-13 |
TW201718525A (zh) | 2017-06-01 |
EP3313827A1 (fr) | 2018-05-02 |
KR20180019200A (ko) | 2018-02-23 |
US10308619B2 (en) | 2019-06-04 |
US20180186758A1 (en) | 2018-07-05 |
WO2016207158A1 (fr) | 2016-12-29 |
KR20180019114A (ko) | 2018-02-23 |
TW201708197A (zh) | 2017-03-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9804490B2 (en) | Holographic media with improved light sensitivity | |
US10241402B2 (en) | Naphthyl acrylates as writing monomers for photopolymers | |
JP6329600B2 (ja) | ホログラフィック媒体を製造するためのフォトポリマー処方物 | |
JP6259570B2 (ja) | 保護層および露光感光性ポリマー層を含んでなる積層構造物 | |
US10001703B2 (en) | Photopolymer formulation for production of holographic media comprising borates with low TG | |
US20190263761A1 (en) | Substituted triazines and a method for producing same | |
KR102382218B1 (ko) | 홀로그래픽 광중합체 배합물에서의 기록 단량체로서의 방향족 글리콜 에테르 | |
KR20120125270A (ko) | 트리아진-기재 기록 단량체를 갖는 광중합체 배합물 | |
KR20120124430A (ko) | 에스테르-기재 기록 단량체를 갖는 광중합체 배합물 | |
EP3233791B1 (fr) | Milieux holographiques résistants à l'humidité | |
US20180223100A1 (en) | Holographic media containing chain-substituted cyanine dyes | |
US20180180993A1 (en) | New triazine as photo initiators and their preparation |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: COVESTRO DEUTSCHLAND AG, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ROELLE, THOMAS;KAWAMURA, KOICHI;CHIOVETTA, GUISEPPE;SIGNING DATES FROM 20180115 TO 20180117;REEL/FRAME:045348/0574 |
|
AS | Assignment |
Owner name: COVESTRO DEUTSCHLAND AG, GERMANY Free format text: CORRECTIVE ASSIGNMENT TO CORRECT THE CORRESPONDENCE ADDRESS:222 DELAWARE AVENUE, STE. 1410, CREATIVE INDUSTRIAL PARK, GUIMO ROAD, GUILINWILMINGTON, US 19801-1621 PREVIOUSLY RECORDED ON REEL 045348 FRAME 0574. ASSIGNOR(S) HEREBY CONFIRMS THE ASSIGNMENT;ASSIGNORS:ROELLE, THOMAS;KAWAMURA, KOICHI;CHIOVETTA, GUISEPPE;SIGNING DATES FROM 20180115 TO 20180117;REEL/FRAME:045738/0746 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: ADVISORY ACTION MAILED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |