US20140357752A1 - Bio-degradable compositions and use thereof - Google Patents

Bio-degradable compositions and use thereof Download PDF

Info

Publication number
US20140357752A1
US20140357752A1 US14/344,643 US201114344643A US2014357752A1 US 20140357752 A1 US20140357752 A1 US 20140357752A1 US 201114344643 A US201114344643 A US 201114344643A US 2014357752 A1 US2014357752 A1 US 2014357752A1
Authority
US
United States
Prior art keywords
bio
degradable
composition
pot
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/344,643
Other languages
English (en)
Inventor
Chanoch Samet
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bioplasmar Ltd
Original Assignee
Bioplasmar Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bioplasmar Ltd filed Critical Bioplasmar Ltd
Assigned to BIOPLASMAR LTD. reassignment BIOPLASMAR LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SAMET, Chanoch
Publication of US20140357752A1 publication Critical patent/US20140357752A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D167/00—Coating compositions based on polyesters obtained by reactions forming a carboxylic ester link in the main chain; Coating compositions based on derivatives of such polymers
    • C09D167/04—Polyesters derived from hydroxycarboxylic acids, e.g. lactones
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
    • A—HUMAN NECESSITIES
    • A01—AGRICULTURE; FORESTRY; ANIMAL HUSBANDRY; HUNTING; TRAPPING; FISHING
    • A01G—HORTICULTURE; CULTIVATION OF VEGETABLES, FLOWERS, RICE, FRUIT, VINES, HOPS OR SEAWEED; FORESTRY; WATERING
    • A01G9/00—Cultivation in receptacles, forcing-frames or greenhouses; Edging for beds, lawn or the like
    • A01G9/02—Receptacles, e.g. flower-pots or boxes; Glasses for cultivating flowers
    • A—HUMAN NECESSITIES
    • A01—AGRICULTURE; FORESTRY; ANIMAL HUSBANDRY; HUNTING; TRAPPING; FISHING
    • A01G—HORTICULTURE; CULTIVATION OF VEGETABLES, FLOWERS, RICE, FRUIT, VINES, HOPS OR SEAWEED; FORESTRY; WATERING
    • A01G9/00—Cultivation in receptacles, forcing-frames or greenhouses; Edging for beds, lawn or the like
    • A01G9/02—Receptacles, e.g. flower-pots or boxes; Glasses for cultivating flowers
    • A01G9/021—Pots formed in one piece; Materials used therefor
    • A—HUMAN NECESSITIES
    • A01—AGRICULTURE; FORESTRY; ANIMAL HUSBANDRY; HUNTING; TRAPPING; FISHING
    • A01G—HORTICULTURE; CULTIVATION OF VEGETABLES, FLOWERS, RICE, FRUIT, VINES, HOPS OR SEAWEED; FORESTRY; WATERING
    • A01G9/00—Cultivation in receptacles, forcing-frames or greenhouses; Edging for beds, lawn or the like
    • A01G9/02—Receptacles, e.g. flower-pots or boxes; Glasses for cultivating flowers
    • A01G9/029—Receptacles for seedlings
    • A01G9/0291—Planting receptacles specially adapted for remaining in the soil after planting
    • A—HUMAN NECESSITIES
    • A47—FURNITURE; DOMESTIC ARTICLES OR APPLIANCES; COFFEE MILLS; SPICE MILLS; SUCTION CLEANERS IN GENERAL
    • A47G—HOUSEHOLD OR TABLE EQUIPMENT
    • A47G19/00—Table service
    • A47G19/02—Plates, dishes or the like
    • A47G19/03—Plates, dishes or the like for using only once, e.g. made of paper
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/02—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques
    • C08J3/09—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in organic liquids
    • C08J3/091—Making solutions, dispersions, lattices or gels by other methods than by solution, emulsion or suspension polymerisation techniques in organic liquids characterised by the chemical constitution of the organic liquid
    • C09D7/001—
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
    • C09J11/02—Non-macromolecular additives
    • C09J11/06—Non-macromolecular additives organic
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
    • C09J9/00—Adhesives characterised by their physical nature or the effects produced, e.g. glue sticks
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2300/00—Characterised by the use of unspecified polymers
    • C08J2300/16—Biodegradable polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2367/00—Characterised by the use of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Derivatives of such polymers
    • C08J2367/04—Polyesters derived from hydroxy carboxylic acids, e.g. lactones
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/02—Halogenated hydrocarbons
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/04—Oxygen-containing compounds
    • C08K5/07—Aldehydes; Ketones
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/04—Oxygen-containing compounds
    • C08K5/10—Esters; Ether-esters
    • C08K5/101—Esters; Ether-esters of monocarboxylic acids

Definitions

  • the invention relates to biodegradable compositions and their use, especially as sealants or adhesives in agriculture.
  • a sealant is usually used to prevent the penetration of substances or pollutants (such as air, gas, dust, fire, smoke or liquid) from one location through a barrier into another.
  • pollutants such as air, gas, dust, fire, smoke or liquid
  • desirable properties of sealants include insolubility, corrosion resistance, and adhesion.
  • Sealants are used in many industries including in agriculture and in home gardening, typically for preventing moisture from penetrating through barriers.
  • the inside of terra-cotta plant pots may include a layer of sealant to reduce water loss from the pot.
  • Plant pots are commonly used by nurseries and green houses to grow plants for commercial use. Plants are grown in pots until they are mature enough to be distributed to retail outlets or to consumers. Typically, molded plastic pots are used for growing plants. Consumers that purchase plants in pots usually transplant the plants into soil at their home, discarding the plastic pot. The pots then end up in landfills or garbage dumps, where they remain for a very long time because they are not biodegradable.
  • Biodegradable pots made of paper (cellulose fibers), peat and other organic waste are known. These pots are designed to degrade relatively quickly when buried in soil. This allows consumers to simply bury the pot with the plant in it, rather than having to remove the plant from the pot before planting.
  • the biodegradable pots must also be substantially resistant to saturation by liquids so that they do not begin to disintegrate prior to being buried in soil.
  • Some biodegradable pots include a thermoplastic polymer layer which faces an interior of the plant pot which is exposed to soil placed in the plant pot.
  • methods of irrigation and the humid environment in many nurseries cause the external surfaces of pots to be exposed to moisture, so that a sealant on the interior of a plant pot does not prevent degradation of the pot while still on the shelf in the nursery.
  • Nurseries also use plug trays for plant transplants.
  • each transplant grows in an individual cell avoiding competition among plants and providing uniformity of the plants.
  • Several other advantages of plugs (also called rooting plugs) over bare-root transplants include a smaller amount of water required for plugs over bare-root transplants, a mechanical multiple-row plug transplanter can be used for planting, there is minimal root damage during transplanting and plant survival is greater.
  • the growing media in plug trays is typically a soilless mix generally made up of a combination of peat, vermiculite and horticultural perlite and sometimes fertilizer which is packaged in a thin degradable wrap. Sometimes adhesives are used for supporting and hardening the plugs.
  • seepage irrigation also known as sub-irrigation
  • sub-irrigation is a method of irrigation that allows the soil to be moistened from below the plants' root zone. Water is delivered from below, absorbed upwards, and the excess collected for recycling. Typically, a solution of water and nutrients floods a container or flows through a trough for a short period of time, 10-20 minutes, and is then pumped back into a holding tank for reuse. The bottom parts of plant pots and plugs irrigated this way are almost constantly submerged in water.
  • Embodiments of the invention provide bio-degradable compositions that can be used as a sealant or adhesive for use in agriculture and home gardening and which overcome the drawbacks of known sealants.
  • the compositions according to embodiments of the invention enable bio-degradation at different rates such that stability of articles coated by these compositions can be tailored to need.
  • compositions according to embodiments of the invention comprise a bio-degradable polymer or co-polymer, and an organic non hydroxylic solvent.
  • the composition comprises at least two solvents, one of the solvents acting as a modifier to enhance desired properties (e.g., elasticity) of the composition.
  • a bio-degradable composition comprising 0.2%-10% w/w bio-degradable polymer and an organic non hydroxylic solvent.
  • the composition comprises a plurality of organic non hydroxylic solvents.
  • one of the organic non hydroxylic solvents is an organic ester or a ketone.
  • the organic non hydroxylic solvent has a boiling point of less than 80° C.
  • bio-degradabale polymer is poly lactic acid (PLA) and the organic non hydroxylic solvent is dichloromethane (DCM).
  • the composition comprises PLA, DCM and Ethyl Acetate (EtOAc).
  • the composition may optionally include acetone.
  • the composition includes 0.2%-10% w/w PLA and up to 50% DCM and up to 50% EtOAc. Some embodiments include about 0.2% w/w bio-degradable polymer. Other embodiments include about 1% w/w bio-degradable polymer. Yet other embodiments include about 2% w/w bio-degradable polymer. Some other embodiments include about 6% w/w bio-degradable polymer and yet other embodiments include about 10% w/w bio-degradable polymer.
  • compositions described herein in the preparation of a coating for bio-degradable articles.
  • a method for preparing a rooting plug comprising mixing a composition according to embodiments of the invention with plug mix.
  • the composition comprises 1-2% w/w bio-degradable polymer.
  • the method may further include creating a hollow in the plug mix and mixing the composition with the plug mix at the hollow.
  • a bio-degradable article such as a plant pot or food-ware which includes an article body and a coating of the article body.
  • the coating may include 0.2%-10% w/w bio-degradable polymer and an organic non hydroxylic solvent.
  • the coating comprises a plurality of organic non hydroxylic solvents.
  • one of the organic non hydroxylic solvents is an organic ester or a ketone.
  • the organic non hydroxylic solvent has a boiling point of less than 80° C.
  • bio-degradable polymer is PLA and the organic non hydroxylic solvent is DCM.
  • the coating comprises PLA, DCM and EtOAc. In some embodiments the coating comprises acetone
  • the coating may include 1%-10% w/w PLA and up to 50% DCM and up to 50% EtOAc. In one embodiment the coating comprises about 1% w/w bio-degradable polymer.
  • the article comprises more than one type of coating. In some embodiments one type of coating comprises a higher percent of polymer than a second type of coating.
  • the article body may be partially coated.
  • a bio-degradable plant pot comprising calcium carbonate.
  • the pot may further include a cellulose containing material and optionally a starch and/or sulfate lignin and/or molasses.
  • the pot may include a coating, said coating comprising 0.2%-10% w/w bio-degradable polymer and an organic non hydroxylic solvent.
  • FIG. 1 is a schematic illustration of a plant pot coated with a sealant according to one embodiment of the invention
  • FIG. 2 is a schematic illustration of plant pot differentially coated with a sealant according to an embodiment of the invention
  • FIG. 3 is a schematic illustration of a plug including an adhesive according to embodiments of the invention.
  • FIG. 4 is a schematic illustration of food ware coated with a sealant according to an embodiment of the invention.
  • Embodiments of the invention provide bio-degradable compositions that can be used as a sealant or adhesive for use in agriculture and home gardening. According to other embodiments the compositions may be used in other fields of industry.
  • compositions according to embodiments of the invention comprise a bio-degradable polymer or co-polymer, and an organic non hydroxylic solvent.
  • the composition comprises at least two solvents, one of the solvents possibly acting as a modifier.
  • bio-degradable polymers or co-polymers examples include poly lactic acid (PLA) or poly lactic-co-glycolic acid (PLGA) and typically naturally occurring polyesters including polyhydroxyalkanoates, such as poly hydroxyl butyrate (PHB).
  • PHA poly lactic acid
  • PHA poly lactic-co-glycolic acid
  • PHB poly hydroxyl butyrate
  • Other suitable bio-degradable polymers may be used.
  • solvents examples include dichloromethane (DCM), dichloroethane, tetrachloroethylene, tetrahydrochloride, dimethylformamide (DMF), acetonitrile, dimethyl sulfoxide (DMSO), organic esters such as: ethyl acetate (EtOAc), butyl acetate and ethyl propionyl, and ketons such as acetone and cyclohexanone.
  • DCM dichloromethane
  • dichloroethane tetrachloroethylene
  • tetrahydrochloride dimethylformamide
  • acetonitrile dimethyl sulfoxide
  • DMSO dimethyl sulfoxide
  • organic esters such as: ethyl acetate (EtOAc), butyl acetate and ethyl propionyl, and ketons such as acetone and cyclohexanone.
  • EtOAc ethyl a
  • compositions are prepared by mixing, in room temperature (about 25° C.), a polymer (possibly in the form of a resin) into a solvent or mixture of solvents until the polymer is dissolved. The mixture may then be heated to remove excess solvent. In one embodiment the composition is heated only up to about 80° C.
  • compositions may include a mixture of solvents, one solvent having a higher boiling point than the other.
  • DCM and EtOAc may be both used as solvents in a composition, the DCM evaporating more rapidly than the EtOAc due to its lower boiling point.
  • the slower evaporating EtOAc may then enable certain properties of the composition to be expressed. For example, a higher percent of EtOAc relative to DCM may be used in a composition to obtain a more elastic coating.
  • compositions resulting from the mixtures described above are fluids which become film-like upon drying.
  • Compositions according to embodiments of the invention can be used for coating articles (e.g., by immersion or by spraying) typically biodegradable articles, such as No-degradable plant pots, bio-degradable food- ware (plates, bowels, cups and other utensils) and other suitable articles.
  • Bio-degradable articles often single-use articles, are usually designed to rapidly disintegrate once buried in soil. However, when coated, the rate of degradation of the coating typically determines the degradation of the whole article.
  • compositions comprise 0.2%-10% w/w polymer in solvent. Viscosity and durability of the composition are directly proportional to the percent of polymer in the composition.
  • compositions and coatings according to embodiments of the invention can be designed to disintegrate at different rates such that stability of articles coated according to embodiments of the invention, can be tailored to need.
  • composition having a higher percent of polymer may be used.
  • several coat layers may be used for overall longer durability of the coating.
  • disposable food ware such as a plate
  • a plate is expected to be kept in relatively dry conditions until it is used.
  • the plate is expected to be exposed to liquids and after its use (typically, a matter of hours) the plate is discarded.
  • a coating designed to disintegrate within hours or days of exposure to moisture may be appropriate.
  • the pots are expected to be kept in a moist environment for a period of several weeks up to several months prior to being discarded or being planted in soil (e.g., in the nursery or in a consumer's house prior to the plant being transferred to soil).
  • soil e.g., in the nursery or in a consumer's house prior to the plant being transferred to soil.
  • the pot may disintegrate more rapidly.
  • rapid disintegration of a plantable pot is advantageous in facilitating plant growth due to release of the plant's roots from the enclosure of the plant pot walls.
  • coating of plant pots is designed for several weeks' up to several months' durability on the shelf in a nursery but quicker disintegration in soil.
  • compositions according to embodiments of the invention enable to produce a bio-degradable plant pot that can withstand extreme moisture conditions, such as the conditions prevailing in nurseries, for example nurseries employing seepage irrigation.
  • Plant pots coated according to embodiments of the invention may be differentially coated.
  • a bottom part (floor) of a pot may be coated with a more durable composition (e.g., higher percentage of polymer) than the surrounding walls of the pot or the interior of a pot may be coated with a more durable composition relative to the exterior of the pot.
  • a more durable composition e.g., higher percentage of polymer
  • rooting plugs may include growth media (also referred to as plug mix) mixed with a composition according to embodiments of the invention.
  • Compositions according to embodiments of the invention may be used as an adhesive to produce a firmer (and thus more easily handled) plug than currently used plugs.
  • Plugs can be designed to be durable for a longer period and/or the solidity or firmness of each plug may be designed to need based upon the specific composition used.
  • FIG. 1 One embodiment of the invention is schematically illustrated in FIG. 1 in which a bio-degradable plant pot ( 10 ) is coated with a sealant according to embodiments of the invention to prevent degradation of the pot while in use.
  • a sealant according to embodiments of the invention to prevent degradation of the pot while in use.
  • degradation of the sealant starts at a pre-designed time after coating of the pot, eventually enabling environment friendly degradation of the whole pot.
  • a bio-degradable pot may be made of agriculture residues such as bamboo pulp or husks, composted manure, saw dust, different starches and other organic, typically renewable, matter.
  • a plant pot (or other article) may be made of a mixture of calcium carbonate (typically used in industry to entrap impurities, such as in the sugar production industry) and sawdust or other cellulose containing material.
  • a small amount of starch, sulfate lignin or molasses is added to the calcium carbonate-cellulose mixture to act as an adhesive. Other suitable adhesives may be added. Water is then added to the mixture to obtain a dough-like composition that may be shaped into pots or other articles. The articles are then dried (possibly while heating).
  • the calcium carbonate—cellulose—adhesive mixture (or other suitable mixtures) is shaped into a pot by press forming or by thermoforming. Other methods may be used for preparing pot.
  • bio-degradable pots may be made of mixture comprising 40% calcium carbonate, 40% sawdust and 20% flour. Other percentages of calcium carbonate and cellulose containing materials and starch containing materials may be used.
  • a typical plant pot ( 10 ) includes drainage holes ( 11 ) in its bottom part ( 12 ).
  • a plant pot ( 10 ) is coated by spraying a composition according to embodiments of the invention on it to completely cover the pot with a coating of composition or to partially cover the pot. Any other suitable methods of coating may be used.
  • the pot is then dried in the open air until the formation of a film-like coating ( 13 ) over all the surfaces of the pot.
  • the pot may be dried under other conditions, such as by being heated, typically, not more than 80° C.
  • the coating ( 13 ) serves as a sealant to prevent early degradation of the organic matter composing the pot.
  • a plant pot ( 10 ) or other article may include a weakened zone ( 15 ) for easy breaking/tearing of the pot (or other article).
  • the weakened zone ( 15 ) may include a thinning of the pot wall so that the pot may be easily broken or torn along the weakened zone ( 15 ).
  • Other techniques for weakening an area of the pot may be used.
  • the weakened zone ( 15 ) may be located on the pot ( 10 ) such that the bottom part ( 12 ) of the pot may be broken off, for example, prior to planting the pot in soil, to enable free growth of roots through the bottom area of the pot into the ground.
  • weakened zones may be located along side the pot walls or in any other desired location.
  • compositions according to embodiments of the invention enable to coat different areas of a pot in different types of coatings.
  • An example—of this differential coating is schematically illustrated in FIG. 2 .
  • the bottom part ( 22 ) of a plant pot ( 20 ) is coated by a more durable composition than the surrounding walls ( 24 ) of the pot.
  • the bottom part ( 22 ) of the pot ( 20 ) may be submerged in a first liquid composition comprising a high percent of polymer.
  • the liquid composition will reach the inner part of the pot through the drainage holes ( 21 ) and will thus flow over the inner bottom part ( 22 ) of the pot.
  • the surrounding walls ( 24 ) of the pot may be coated with a second composition, by spraying or any other suitable method of applying a liquid composition.
  • the second composition typically comprises a lower percentage of polymer than the first composition.
  • the whole pot ( 20 ) may be coated by a first composition.
  • additional coats of the first composition (or of another composition) may be applied on the bottom part ( 22 ) to achieve a more durable coating of the bottom part ( 22 ) than the coating of the rest of the pot.
  • Having a particularly durable coating on the bottom part of a pot may be useful especially in cases where seepage irrigation is used.
  • the inner part ( 24 a ) of the surrounding walls ( 24 ) of a pot may be sprayed or otherwise coated by a more durable composition than the outer part ( 24 b ) of the surrounding walls ( 24 ).
  • This type of differential coating may be especially useful in cases where a plant is watered by a drip or other irrigation system from the top of the pot which wets the soil in the pot such that the inner parts of the pot are more exposed to moisture than the outer part of the pot.
  • some areas of the pot ( 20 ) may be coated while other areas are left uncoated.
  • a weakened zone (such as weakened zone 15 in FIG. 1 ) may be coated by a different, less durable, composition than other parts of the pot ( 20 ).
  • a zone may be weakened by being left uncoated or by being coated by a relatively less durable composition than other areas of the pot ( 20 ).
  • a composition according to another embodiment of the invention may be used as an adhesive to be mixed in the media of a rooting plug.
  • a plug ( 30 ) which includes a soilless mix ( 31 ) or any other suitable mix, includes a hollow ( 32 ) for accepting a seed, seedling, shoot, grafts or other suitable types of plants.
  • compositions according to embodiments of the invention may be blended into the plug mix ( 31 ). Upon drying, the composition will confer firmness to the plug which is advantageous for handling by a mechanical transplanter.
  • liquid compositions may be sprayed or otherwise applied to the hollow ( 32 ), to confer rigidity to the structure of the hollow ( 32 ).
  • plug trays which are usually made of plastic, may be made of bio-degradable materials coated by compositions according to embodiments of the invention.
  • compositions according to embodiments of the invention may be used in fields other than agriculture.
  • the compositions may be used for coating bio-degradable disposables such as food ware or table ware.
  • FIG. 4 shows a plate ( 42 ) and cup ( 44 ) which are coated by compositions according to embodiments of the invention.
  • Bio-degradable plates or cups may be made of organic materials such as sugar cane and/or other starches. Durability of plates, cups and other bio-degradable table-ware may be strengthened by being coated with compositions according to embodiments of the invention, thereby enhancing their shelf-life without diminishing their friendliness to the environment.
  • compositions I-VIII were prepared by mixing PLA resin (IngeoTM by NatureWorks, USA) into a mixture of solvents at room temperature (about 25° C.) until full dissolution of the resin. Resulting compositions were fluid, in different levels of viscosity. Viscosity of each composition was directly proportional to the percent of polymer in the composition.
  • composition I 1 gr PLA 40 ml EtOAc 10 ml DCM
  • Rooting plugs of 2 ⁇ 3 cm were prepared using an Ellegaard system. A finger sized hollow was made in the center of each plug. Each hollow was sprayed with 0.5 cc of composition I using a syringe. Control plugs were left untreated. The plugs were dried in RT over night and a Gypsophila (Baby's Breath) shoot was placed in each of the plugs' hollows. Plugs were irrigated for one month with irrigation from on top.
  • Plant Development Plant Development was better in treated plugs. Plants grown in treated plugs had more root mass than the plants grown in control plugs, possibly due to better water retention in the treated plugs.
  • composition stability Treatment of treated plugs was observed upon planting in soil (within days of planting).
  • composition II 0.5 gr PLA 35 ml EtOAc 10 ml DCM 5 ml acetone
  • Rooting plugs of 2 ⁇ 3 cm were prepared using an EllegaardTM system. A finger sized hollow was made in the center of each plug. Each hollow was sprayed with 0.5 cc of composition II using a syringe. Control plugs were left untreated. The plugs were dried over night. A tomato plant was placed in each plug's hollow. Plugs were irrigated for two weeks with irrigation from on top.
  • Plant Development Plant Development was better in treated plugs as described above.
  • composition stability Teated plugs were stable for two weeks in trays. Degradation started after two weeks.
  • composition III 4 gr PLA 160 ml EtOAc 40 ml DCM
  • Composition IV 4 gr PLA 180 ml EtOAc 20 ml DCM
  • Composition V 4 gr PLA 160 ml EtOAc 20 ml DCM 20 ml acetone
  • compositions were also left to dry in the beaker to examine their different characteristics when dried films
  • composition stability composition IV dried to form a more elastic film than composition III.
  • Composition V could be diluted in water as opposed to compositions III and IV which could not be easily dissolved in water.
  • Coated plant pots were stable for three months. After being buried in soil for two days the framework of the pots began to deteriorate. After three days of being buried in soil the pot framework was completely disintegrated.
  • composition VI 12 gr PLA 100 ml EtOAc 100 ml DCM
  • composition VII 20 gr PLA 100 ml EtOAc 100 ml DCM
  • composition stability Plant pots coated with composition VI were stable for three months. Plant pots coated with composition VII were stable for over three months. After being buried in soil for two days the framework of all the pots began to deteriorate. After three days of being buried in soil the pot framework was completely disintegrated. The pots having two layers of coating disintegrated only after being buried for 5-6 days.
  • composition VIII 0.1 gr PLA 45 ml EtOAc 5 ml DCM
  • Paper plates coated with composition VIII are expected to have a long shelf life and to disintegrate a few days after being continuously exposed to moisture (e.g., the environment in a garbage dump).

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Environmental Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Wood Science & Technology (AREA)
  • Materials Engineering (AREA)
  • Dispersion Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Medicinal Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • General Chemical & Material Sciences (AREA)
  • Food Science & Technology (AREA)
  • Cultivation Receptacles Or Flower-Pots, Or Pots For Seedlings (AREA)
  • Pretreatment Of Seeds And Plants (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Paints Or Removers (AREA)
  • Adhesives Or Adhesive Processes (AREA)
  • Biological Depolymerization Polymers (AREA)
US14/344,643 2011-09-18 2011-09-18 Bio-degradable compositions and use thereof Abandoned US20140357752A1 (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IL2011/000739 WO2013038399A1 (fr) 2011-09-18 2011-09-18 Compositions biodégradables et leur utilisation

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/IL2011/000739 A-371-Of-International WO2013038399A1 (fr) 2011-09-18 2011-09-18 Compositions biodégradables et leur utilisation

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/090,011 Continuation US9951248B2 (en) 2011-09-18 2016-04-04 Bio-degradable compositions and use thereof

Publications (1)

Publication Number Publication Date
US20140357752A1 true US20140357752A1 (en) 2014-12-04

Family

ID=47882699

Family Applications (5)

Application Number Title Priority Date Filing Date
US14/344,643 Abandoned US20140357752A1 (en) 2011-09-18 2011-09-18 Bio-degradable compositions and use thereof
US15/090,011 Active US9951248B2 (en) 2011-09-18 2016-04-04 Bio-degradable compositions and use thereof
US15/959,633 Active 2031-09-21 US10752802B2 (en) 2011-09-18 2018-04-23 Bio-degradable compositions and use thereof
US17/000,733 Active US11453801B2 (en) 2011-09-18 2020-08-24 Bio-degradable compositions and use thereof
US17/950,369 Pending US20230021518A1 (en) 2011-09-18 2022-09-22 Bio-degradable compositions and use thereof

Family Applications After (4)

Application Number Title Priority Date Filing Date
US15/090,011 Active US9951248B2 (en) 2011-09-18 2016-04-04 Bio-degradable compositions and use thereof
US15/959,633 Active 2031-09-21 US10752802B2 (en) 2011-09-18 2018-04-23 Bio-degradable compositions and use thereof
US17/000,733 Active US11453801B2 (en) 2011-09-18 2020-08-24 Bio-degradable compositions and use thereof
US17/950,369 Pending US20230021518A1 (en) 2011-09-18 2022-09-22 Bio-degradable compositions and use thereof

Country Status (8)

Country Link
US (5) US20140357752A1 (fr)
EP (2) EP4039375A1 (fr)
JP (1) JP2014531485A (fr)
AU (1) AU2011377134B2 (fr)
CA (1) CA2848331C (fr)
ES (1) ES2913942T3 (fr)
PL (1) PL2758183T4 (fr)
WO (1) WO2013038399A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150013610A1 (en) * 2013-07-12 2015-01-15 Wanda M. Weder and William F. Straeter, not indv. but solely as Trustees of the Fam. Trust U/T/A Compositions and methods for causing, enhancing, and/or expediting biodegradation of articles
CN106069310A (zh) * 2016-08-16 2016-11-09 梁文涛 一种可降解花盆及其制备方法
CN108076905A (zh) * 2017-12-18 2018-05-29 杭州之江园林绿化艺术有限公司 一种灌木小苗可降解栽培容器制备工艺
US20230301243A1 (en) * 2022-03-22 2023-09-28 Torkild Benn Vennesland Biodegradable planter pots comprising starch and an outer silicon layer

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011161685A2 (fr) 2010-06-26 2011-12-29 Hcl Cleantech Ltd. Mélanges de sucres, méthodes de production et d'utilisation associées
IL206678A0 (en) 2010-06-28 2010-12-30 Hcl Cleantech Ltd A method for the production of fermentable sugars
IL207329A0 (en) 2010-08-01 2010-12-30 Robert Jansen A method for refining a recycle extractant and for processing a lignocellulosic material and for the production of a carbohydrate composition
IL207945A0 (en) 2010-09-02 2010-12-30 Robert Jansen Method for the production of carbohydrates
GB2524906B8 (en) 2011-04-07 2016-12-07 Virdia Ltd Lignocellulose conversion processes and products
US20140357752A1 (en) * 2011-09-18 2014-12-04 Bio Plasmar Ltd. Bio-degradable compositions and use thereof
US9617608B2 (en) 2011-10-10 2017-04-11 Virdia, Inc. Sugar compositions
US11078548B2 (en) 2015-01-07 2021-08-03 Virdia, Llc Method for producing xylitol by fermentation
NL2014834B1 (nl) * 2015-02-13 2016-10-13 Janus Appels Gerbrandus Kweekplug voorzien van een zaadkorrel, alsmede werkwijze voor het vervaardigen van de kweekplug en werkwijze voor het kweken van een gewas met behulp van de kweekplug.
CN106579971A (zh) * 2016-12-27 2017-04-26 上海贝儿康婴童用品有限公司 搅拌塞体
CN110024661A (zh) * 2019-03-19 2019-07-19 中国农业大学 一种提高大钵体成坨性的育苗方法及其配套的育苗穴盘
CN110432028A (zh) * 2019-08-17 2019-11-12 黄启柳 有机自释花盆生产工艺
JP1677980S (fr) * 2019-10-11 2021-02-01
JP1677992S (fr) * 2019-10-31 2021-02-01

Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4096125A (en) * 1976-05-26 1978-06-20 Union Carbide Corporation Polycaprolactone derivatives and coating compositions thereof
US6024784A (en) * 1998-03-05 2000-02-15 Instituut Voor Agrotechnologisch Onderzoek (Ato-Dlo) Poly (3-hydroxyalkanoate) paint and method for the preparation thereof
US20020012705A1 (en) * 1998-04-08 2002-01-31 Chondros, Inc. Polymer constructs
US20030073804A1 (en) * 2001-04-27 2003-04-17 Takeshi Imamura Polyhydroxyalkanoate, producing method therefor charge control agent containing such polyhydroxyalkanoate, toner containing such charge control agent and image forming method and image forming apparatus utilizing such toner
US20040018240A1 (en) * 2000-12-01 2004-01-29 Yoshihiro Ohmachi Method for producing preparation containing bioactive substance
US20040099979A1 (en) * 2002-01-02 2004-05-27 Jui-Hsiang Chen Process for preparing porous material having interconnected pores
US20070213424A1 (en) * 2004-03-22 2007-09-13 Chandrasekaran Margam Method for Obtaining Graded Pore Structure in Scaffolds for Tissues and Bone, and Scaffolds with Graded Pore Structures for Tissue and Bone
US20080213590A1 (en) * 2004-05-28 2008-09-04 Andreas Greiner Invention Concerning Agricultural Active Substances
US20090068463A1 (en) * 2005-10-19 2009-03-12 Katsuhiko Mochizuki Crimped Yarn, Method for Manufacture thereof, and Fiber Structure
US20100120145A1 (en) * 2007-04-20 2010-05-13 Fraunhofer-Gresellschaft Zur Forderung Der Angewandten Forschung E.V. Three-dimensional biocompatible skeleton structure containing nanoparticles
US20100173000A1 (en) * 2007-05-14 2010-07-08 Sustained Nano Systems Llc Controlled release implantable dispensing device and method
US20110009522A1 (en) * 2009-07-10 2011-01-13 National University Corporation Nagoya Institute Of Technology Material for filling bone defects and production method thereof
US20110245922A1 (en) * 2010-03-31 2011-10-06 National University Corporation Nagoya Institute Of Technology Material for filling bone defects and production method thereof
US20110262683A1 (en) * 2008-12-26 2011-10-27 Toray Industries, Inc. Polymer alloy fiber and fiber structure
US20110311746A1 (en) * 2010-06-02 2011-12-22 The Regents Of The University Of Michigan Scaffolds and methods of forming the same
US20120015891A1 (en) * 2010-01-04 2012-01-19 Mapi Pharma Ltd. Depot systems comprising glatiramer or a pharmacologically acceptable salt thereof
US20130165957A1 (en) * 2010-08-31 2013-06-27 Politecnico Di Torino Implantable Prosthetic Devices and Solvent-Casting Methods for Manufacturing Same
US8641960B1 (en) * 2009-09-29 2014-02-04 The United States Of America, As Represented By The Secretary Of Agriculture Solution blow spinning

Family Cites Families (50)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3644167A (en) * 1969-07-14 1972-02-22 Georgia Pacific Corp Preparation of corrugating linerboard
US3973355A (en) * 1974-01-18 1976-08-10 Agritec Co. Self-contained hydrophilic plant growth matrix and method
US3914900A (en) * 1974-07-01 1975-10-28 Lavell M Bigelow Means and method for planting and growing plants and crops
JPH0737560B2 (ja) * 1990-10-09 1995-04-26 工業技術院長 微生物分解性プラスチック成形品
JP2513091B2 (ja) * 1991-05-10 1996-07-03 株式会社島津製作所 生分解性複合材料およびその製造法
US5928741A (en) * 1992-08-11 1999-07-27 E. Khashoggi Industries, Llc Laminated articles of manufacture fashioned from sheets having a highly inorganically filled organic polymer matrix
US5762230A (en) * 1993-03-11 1998-06-09 Policappelli; Nini Laminated container
JPH0797545A (ja) * 1993-09-30 1995-04-11 Kanegafuchi Chem Ind Co Ltd 耐水性を有する生分解性コーティング剤および食品用生分解性容器
JP3676374B2 (ja) * 1995-05-01 2005-07-27 サム・ヤン・カンパニー・リミテッド 移植用生体内分解性遮蔽膜および製造方法
JPH0998671A (ja) 1995-10-04 1997-04-15 Dainippon Printing Co Ltd 生分解性育苗ポット
JPH09205895A (ja) * 1996-01-30 1997-08-12 Nisshinbo Ind Inc 生分解性育苗ポット
US5883199A (en) * 1997-04-03 1999-03-16 University Of Massachusetts Polyactic acid-based blends
US6164011A (en) * 1998-02-02 2000-12-26 Cascades Multi-Pro Inc. Biodegradable and biocompatible agricultural mulch and method of preparing same
JP2000191930A (ja) 1998-12-24 2000-07-11 Daicel Chem Ind Ltd 生分解性樹脂組成物およびその成形物
JP2001145428A (ja) 1999-09-09 2001-05-29 Mikuni Color Ltd マルチシート形成用組成物および形成方法
US6515054B1 (en) * 1999-11-02 2003-02-04 Nippon Shokubai Co., Ltd. Biodegradable resin composition and its molded product
JP2002012258A (ja) * 2000-06-30 2002-01-15 Kankyo Kagaku Kk 生分解性容器およびその製造方法
CA2419834C (fr) * 2000-09-01 2010-01-12 Reckitt Benckiser (Uk) Limited Procede de nettoyage
JP3667266B2 (ja) 2000-09-07 2005-07-06 三島製紙株式会社 育苗ブロック成形用生分解性シート材
NL1017460C2 (nl) * 2001-02-28 2002-09-03 Sluis Cigar Machinery B V V D Kweekmedium.
JP4716589B2 (ja) 2001-03-06 2011-07-06 ユニチカ株式会社 生分解性育苗用根カバー及びその製造方法
JP2002338796A (ja) 2001-05-21 2002-11-27 Teijin Ltd 生分解性ガスバリア材料
JP3954838B2 (ja) * 2001-10-02 2007-08-08 東洋紡績株式会社 生分解性ヒートシールラッカー組成物および生分解性複合体
KR20030061675A (ko) * 2002-01-11 2003-07-22 뉴 아이스 리미티드 생분해성 또는 부패성 컨테이너
JP4092924B2 (ja) * 2002-02-18 2008-05-28 東レ株式会社 生分解性接着剤
JP2003250350A (ja) 2002-02-26 2003-09-09 Gunze Ltd 長尺育苗マット
US7037983B2 (en) * 2002-06-14 2006-05-02 Kimberly-Clark Worldwide, Inc. Methods of making functional biodegradable polymers
JP4000022B2 (ja) 2002-07-11 2007-10-31 ユニチカ株式会社 ポリ乳酸系長繊維不織布の製造方法
WO2004073749A1 (fr) * 2003-02-19 2004-09-02 Takeda Pharmaceutical Company Limited Agent dispersant destine a des preparations a liberation soutenue
JP2005089537A (ja) 2003-09-12 2005-04-07 Daicel Chem Ind Ltd 生分解性樹脂組成物、農業用マルチフィルム、成形体、並びに土中分解性抑制方法
MXPA06012241A (es) 2004-04-23 2007-03-07 Amgen Inc Polimeros de acido polilactico de bajo peso molecular.
JP2006082494A (ja) * 2004-09-17 2006-03-30 Nisshinbo Ind Inc 生分解性被記録材
US20060147491A1 (en) * 2005-01-05 2006-07-06 Dewitt David M Biodegradable coating compositions including multiple layers
CN101151150B (zh) * 2005-03-28 2010-06-16 株式会社吴羽 聚乙醇酸树脂类叠层片及其制备方法
US8778375B2 (en) * 2005-04-29 2014-07-15 Advanced Cardiovascular Systems, Inc. Amorphous poly(D,L-lactide) coating
JP2009504929A (ja) * 2005-08-18 2009-02-05 スミス アンド ネフュー ピーエルシー 高強度デバイス及び複合材料
JP2009524553A (ja) * 2005-11-28 2009-07-02 ニユー・アイス・リミテツド 生物分解性もしくは堆肥化可能な容器をフィルム加工するための方法
US8552111B2 (en) * 2007-01-12 2013-10-08 Kittrich Corporation Environmentally friendly polymeric textile coating
WO2009011905A1 (fr) * 2007-07-18 2009-01-22 Leonard Kosinski Milieu de croissance végétale
US20090025290A1 (en) * 2007-07-25 2009-01-29 Ball Horticultural Company Bottomless plant container
EP2179842B1 (fr) * 2007-08-14 2016-11-09 Toyo Seikan Kaisha, Ltd. Conteneur en résine biodégradable comportant un film déposé et procédé pour la formation de film déposé
WO2009043580A1 (fr) * 2007-10-03 2009-04-09 Universidad De Concepcion Composition biodégradable, procédé de préparation et leur application dans la fabrication de conteneurs fonctionnels pour l'utilisation agricole et/ou forestière
CN101503869B (zh) * 2008-02-05 2010-12-15 伟盟工业股份有限公司 生物可分解防水复合纸及其制造方法
US8076001B2 (en) * 2008-09-02 2011-12-13 Ppg Industries Ohio, Inc Crosslinked coatings comprising lactide
US9861096B2 (en) * 2008-10-01 2018-01-09 Cornell University Biodegradable chemical delivery system
US9333163B2 (en) * 2008-10-06 2016-05-10 Massachusetts Institute Of Technology Particles with multiple functionalized surface domains
GB0822892D0 (en) * 2008-12-16 2009-01-21 Univ Nottingham Degradable composite
WO2010099292A2 (fr) * 2009-02-25 2010-09-02 North Carolina State University Médicament biodégradable ou autre système d'administration d'actif
US20110076396A1 (en) * 2009-09-28 2011-03-31 Limin Guan Method of forming a calcium phosphate coating within a porous material
US20140357752A1 (en) * 2011-09-18 2014-12-04 Bio Plasmar Ltd. Bio-degradable compositions and use thereof

Patent Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4096125A (en) * 1976-05-26 1978-06-20 Union Carbide Corporation Polycaprolactone derivatives and coating compositions thereof
US6024784A (en) * 1998-03-05 2000-02-15 Instituut Voor Agrotechnologisch Onderzoek (Ato-Dlo) Poly (3-hydroxyalkanoate) paint and method for the preparation thereof
US20020012705A1 (en) * 1998-04-08 2002-01-31 Chondros, Inc. Polymer constructs
US20040018240A1 (en) * 2000-12-01 2004-01-29 Yoshihiro Ohmachi Method for producing preparation containing bioactive substance
US20030073804A1 (en) * 2001-04-27 2003-04-17 Takeshi Imamura Polyhydroxyalkanoate, producing method therefor charge control agent containing such polyhydroxyalkanoate, toner containing such charge control agent and image forming method and image forming apparatus utilizing such toner
US20040099979A1 (en) * 2002-01-02 2004-05-27 Jui-Hsiang Chen Process for preparing porous material having interconnected pores
US20070213424A1 (en) * 2004-03-22 2007-09-13 Chandrasekaran Margam Method for Obtaining Graded Pore Structure in Scaffolds for Tissues and Bone, and Scaffolds with Graded Pore Structures for Tissue and Bone
US20080213590A1 (en) * 2004-05-28 2008-09-04 Andreas Greiner Invention Concerning Agricultural Active Substances
US20090068463A1 (en) * 2005-10-19 2009-03-12 Katsuhiko Mochizuki Crimped Yarn, Method for Manufacture thereof, and Fiber Structure
US20100120145A1 (en) * 2007-04-20 2010-05-13 Fraunhofer-Gresellschaft Zur Forderung Der Angewandten Forschung E.V. Three-dimensional biocompatible skeleton structure containing nanoparticles
US20100173000A1 (en) * 2007-05-14 2010-07-08 Sustained Nano Systems Llc Controlled release implantable dispensing device and method
US20110262683A1 (en) * 2008-12-26 2011-10-27 Toray Industries, Inc. Polymer alloy fiber and fiber structure
US20110009522A1 (en) * 2009-07-10 2011-01-13 National University Corporation Nagoya Institute Of Technology Material for filling bone defects and production method thereof
US8641960B1 (en) * 2009-09-29 2014-02-04 The United States Of America, As Represented By The Secretary Of Agriculture Solution blow spinning
US20120015891A1 (en) * 2010-01-04 2012-01-19 Mapi Pharma Ltd. Depot systems comprising glatiramer or a pharmacologically acceptable salt thereof
US20110245922A1 (en) * 2010-03-31 2011-10-06 National University Corporation Nagoya Institute Of Technology Material for filling bone defects and production method thereof
US20110311746A1 (en) * 2010-06-02 2011-12-22 The Regents Of The University Of Michigan Scaffolds and methods of forming the same
US20130165957A1 (en) * 2010-08-31 2013-06-27 Politecnico Di Torino Implantable Prosthetic Devices and Solvent-Casting Methods for Manufacturing Same

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Bognitzki et al., Advanced Materials, 2001, 13(1), 70-72 *

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150013610A1 (en) * 2013-07-12 2015-01-15 Wanda M. Weder and William F. Straeter, not indv. but solely as Trustees of the Fam. Trust U/T/A Compositions and methods for causing, enhancing, and/or expediting biodegradation of articles
CN106069310A (zh) * 2016-08-16 2016-11-09 梁文涛 一种可降解花盆及其制备方法
CN108076905A (zh) * 2017-12-18 2018-05-29 杭州之江园林绿化艺术有限公司 一种灌木小苗可降解栽培容器制备工艺
US20230301243A1 (en) * 2022-03-22 2023-09-28 Torkild Benn Vennesland Biodegradable planter pots comprising starch and an outer silicon layer
US11895957B2 (en) * 2022-03-22 2024-02-13 Torkild Benn Vennesland Biodegradable planter pots comprising starch and an outer silicon layer

Also Published As

Publication number Publication date
ES2913942T3 (es) 2022-06-06
US20230021518A1 (en) 2023-01-26
US20180237655A1 (en) 2018-08-23
US9951248B2 (en) 2018-04-24
CA2848331C (fr) 2020-07-21
US11453801B2 (en) 2022-09-27
EP2758183B1 (fr) 2022-02-09
US20200385606A1 (en) 2020-12-10
EP2758183A4 (fr) 2015-09-02
AU2011377134A1 (en) 2014-04-03
EP4039375A1 (fr) 2022-08-10
PL2758183T3 (pl) 2022-10-10
PL2758183T4 (pl) 2022-10-10
US20160215166A1 (en) 2016-07-28
JP2014531485A (ja) 2014-11-27
EP2758183A1 (fr) 2014-07-30
US10752802B2 (en) 2020-08-25
AU2011377134B2 (en) 2017-10-05
WO2013038399A1 (fr) 2013-03-21
CA2848331A1 (fr) 2013-03-21

Similar Documents

Publication Publication Date Title
US11453801B2 (en) Bio-degradable compositions and use thereof
KR101031365B1 (ko) 생분해성 액상 멀칭용 조성물, 이의 제조 방법 및 이를 이용한 멀칭 방법
JP2015517588A (ja) 生分解性物品のための混合物
TW201325432A (zh) 適用於植物之生長基質
JP3157622U (ja) 肥料用容器
EP1365641B1 (fr) Milieu de culture
KR101174501B1 (ko) 친환경 기능성 원예용 포트
JPH02286013A (ja) 生分解性移植用ポット
JP2742347B2 (ja) 生分解性不織布成型容器
CN113939491A (zh) 用于种子和肥料的控释可生物降解包衣
JP2017035085A (ja) 生分解性組成物およびその使用
JP5921824B2 (ja) 土壌表面乾燥防止材
Treinytea et al. Properties and behaviour of starch and rapeseed cake based composites in horticultural applications
US11895957B2 (en) Biodegradable planter pots comprising starch and an outer silicon layer
Malinconico Different applications of biodegradable and compostable materials in agriculture
RU2796683C1 (ru) Способ интенсивного выращивания картофеля с обогащением почвы питательными веществами и сбора колорадского жука и его личинок
JPH1014408A (ja) 苗木栽培容器
US10472295B2 (en) Composite material for enriching natural sports playing fields
CN2465455Y (zh) 椰纤维抗旱节水保苗钵衣
JP2002017170A (ja) マット栽培用植栽容器と緑化方法
JP2016136853A (ja) 植物を移植して育成する方法
JPH0898628A (ja) 播種、育苗用ポット
WO2024083309A1 (fr) Substrat de croissance pour culture hors-sol
WO2023203563A1 (fr) Compositions moulables par injection et articles les comprenant
JP2007124967A (ja) パルプモウルド製育苗用ポット製造法及び育苗用ポット

Legal Events

Date Code Title Description
AS Assignment

Owner name: BIOPLASMAR LTD., ISRAEL

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SAMET, CHANOCH;REEL/FRAME:032425/0089

Effective date: 20140312

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION