US20140221542A1 - Crosslinkable composition cross-linkable by real michael addition reaction and resins for use in said composition - Google Patents

Crosslinkable composition cross-linkable by real michael addition reaction and resins for use in said composition Download PDF

Info

Publication number
US20140221542A1
US20140221542A1 US14/246,229 US201414246229A US2014221542A1 US 20140221542 A1 US20140221542 A1 US 20140221542A1 US 201414246229 A US201414246229 A US 201414246229A US 2014221542 A1 US2014221542 A1 US 2014221542A1
Authority
US
United States
Prior art keywords
component
resin
reactive
crosslinkable
groups
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/246,229
Other languages
English (en)
Inventor
Richard Hendrikus Gerrit Brinkhuis
Antonius Johannes Wilhelmus Buser
Petrus Johannes Maria David Elfrink
Ferry Ludovicus Thys
Nicole MANGNUS-VERHAGEN
Elwin Aloysius Cornelius Adrianus DE WOLF
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Allnex Netherlands BV
Original Assignee
Nuplex Resins BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nuplex Resins BV filed Critical Nuplex Resins BV
Assigned to NUPLEX RESINS B.V. reassignment NUPLEX RESINS B.V. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: THYS, FERRY LUDOVICUS, MR, MANGNUS-VERHAGEN, NICOLE, MRS, DE WOLF, ELWIN ALOYSIUS CORNELIUS ADRIANUS, MR, BRINKHUIS, RICHARD HENDRIKUS GERRIT, MR, BUSER, ANTONIUS JOHANNES WILHELMUS, MR, ELFRINK, PETRUS JOHANNES MARIA DAVID, MR
Publication of US20140221542A1 publication Critical patent/US20140221542A1/en
Assigned to ALLNEX NETHERLANDS B.V. reassignment ALLNEX NETHERLANDS B.V. CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: NUPLEX RESINS B.V.
Priority to US15/889,291 priority Critical patent/US10647876B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D175/00—Coating compositions based on polyureas or polyurethanes; Coating compositions based on derivatives of such polymers
    • C09D175/04—Polyurethanes
    • C09D175/06—Polyurethanes from polyesters
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D167/00—Coating compositions based on polyesters obtained by reactions forming a carboxylic ester link in the main chain; Coating compositions based on derivatives of such polymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J31/00—Catalysts comprising hydrides, coordination complexes or organic compounds
    • B01J31/02—Catalysts comprising hydrides, coordination complexes or organic compounds containing organic compounds or metal hydrides
    • B01J31/0201—Oxygen-containing compounds
    • B01J31/0205—Oxygen-containing compounds comprising carbonyl groups or oxygen-containing derivatives, e.g. acetals, ketals, cyclic peroxides
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J31/00—Catalysts comprising hydrides, coordination complexes or organic compounds
    • B01J31/02—Catalysts comprising hydrides, coordination complexes or organic compounds containing organic compounds or metal hydrides
    • B01J31/0234—Nitrogen-, phosphorus-, arsenic- or antimony-containing compounds
    • B01J31/0235—Nitrogen containing compounds
    • B01J31/0239—Quaternary ammonium compounds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J31/00—Catalysts comprising hydrides, coordination complexes or organic compounds
    • B01J31/02—Catalysts comprising hydrides, coordination complexes or organic compounds containing organic compounds or metal hydrides
    • B01J31/0234—Nitrogen-, phosphorus-, arsenic- or antimony-containing compounds
    • B01J31/0255—Phosphorus containing compounds
    • B01J31/0267—Phosphines or phosphonium compounds, i.e. phosphorus bonded to at least one carbon atom, including e.g. sp2-hybridised phosphorus compounds such as phosphabenzene, the other atoms bonded to phosphorus being either carbon or hydrogen
    • B01J31/0268—Phosphonium compounds, i.e. phosphine with an additional hydrogen or carbon atom bonded to phosphorous so as to result in a formal positive charge on phosphorous
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/24—Crosslinking, e.g. vulcanising, of macromolecules
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00—Processes of treating or compounding macromolecular substances
    • C08J3/24—Crosslinking, e.g. vulcanising, of macromolecules
    • C08J3/246—Intercrosslinking of at least two polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/01—Use of inorganic substances as compounding ingredients characterized by their specific function
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/16—Nitrogen-containing compounds
    • C08K5/21—Urea; Derivatives thereof, e.g. biuret
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
    • C09D133/04—Homopolymers or copolymers of esters
    • C09D133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D167/00—Coating compositions based on polyesters obtained by reactions forming a carboxylic ester link in the main chain; Coating compositions based on derivatives of such polymers
    • C09D167/02—Polyesters derived from dicarboxylic acids and dihydroxy compounds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2231/00—Catalytic reactions performed with catalysts classified in B01J31/00
    • B01J2231/30—Addition reactions at carbon centres, i.e. to either C-C or C-X multiple bonds
    • B01J2231/34—Other additions, e.g. Monsanto-type carbonylations, addition to 1,2-C=X or 1,2-C-X triplebonds, additions to 1,4-C=C-C=X or 1,4-C=-C-X triple bonds with X, e.g. O, S, NH/N
    • B01J2231/341—1,2-additions, e.g. aldol or Knoevenagel condensations
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
    • C08G63/02—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds
    • C08G63/12—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from polycarboxylic acids and polyhydroxy compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2367/00—Characterised by the use of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Derivatives of such polymers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2367/00—Characterised by the use of polyesters obtained by reactions forming a carboxylic ester link in the main chain; Derivatives of such polymers
    • C08J2367/02—Polyesters derived from dicarboxylic acids and dihydroxy compounds
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2369/00—Characterised by the use of polycarbonates; Derivatives of polycarbonates
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2375/00—Characterised by the use of polyureas or polyurethanes; Derivatives of such polymers
    • C08J2375/04—Polyurethanes
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2375/00—Characterised by the use of polyureas or polyurethanes; Derivatives of such polymers
    • C08J2375/04—Polyurethanes
    • C08J2375/06—Polyurethanes from polyesters

Definitions

  • the present invention relates to a crosslinkable composition cross-linkable by real Michael addition (RMA) reaction and resins for use in said composition.
  • RMA real Michael addition
  • Real Michael Addition is a reaction wherein a reactive component B with at least 2 activated unsaturated groups (hereafter also referred to as the RMA acceptor) and a reactive component A with at least 2 acidic protons C—H in activated methylene or methine groups (hereafter also referred to as the RMA donor) react in the presence of a strong base catalyst.
  • RMA chemistry can be tuned to give very fast curing compositions (also at lower curing temperatures) in coating compositions at acceptable or good pot lives and good material properties, which makes this chemistry very attractive as a basis for coating compositions. Details of RMA cross-linkable compositions using a latent based cross-linking catalyst are described by inventors of the present application in WO2011/055463 which is herewith incorporated by reference.
  • the drying profile (also referred to as the reaction profile or as the curing profile) is the progress of the cross-linking reaction as a function of time. It is required that the drying profile allows build-up of mechanical properties as fast as possible, to help the productivity of the coater.
  • crosslinkable compositions that can be simply cured in ambient conditions, as opposed to for example compositions comprising photo-latent amine catalysts, known from T. Jung et al Park and Lacke October 2003.
  • the object of the invention is to provide improved cross-linkable compositions that provide optimum coating properties in the delicate balance of these apparently counteracting requirements, in particular in crosslinkable compositions having a high solid content.
  • FIG. 1 illustrates the conversion of the acryloyl (as followed by FTIR at 809 cm ⁇ 1 ) in the preferred acryloyl/malonate system using succinimid as component D.
  • an RMA crosslinkable composition comprising at least one crosslinkable component comprising reactive components A and B, each comprising at least 2 reactive groups wherein the at least 2 reactive groups of component A are acidic protons (C—H) in activated methylene or methine groups and the at least 2 reactive groups of component B are activated unsaturated groups (C ⁇ C) and a base catalyst (C) which reactive components A and B crosslink by Real Michael Addition (RMA) reaction under action of the base catalyst, characterised in that the at least one crosslinkable component comprising reactive components A and B in the composition have a total hydroxy number of less than 60, preferably less than 40 and more preferably less than 20 mg KOH/g solids.
  • RMA Real Michael Addition
  • the catalyst C is a carbonate salt according to formula X+ROCO2 ⁇ , wherein X+ is a non-acidic cation, preferably quaternary ammonium or phosphonium, and R is hydrogen or a substituted or unsubstituted alkyl, aryl, or aralkyl group. Details of this latent base catalyst are described in WO2011/055463, which is herewith incorporated by reference.
  • the reactive components A and B can be in the form of separate molecules and each independently in the form of polymers, oligomers, dimers or monomers. Therefore, a “cross-linkable component comprising the active component A” is sometimes also referred to herein as component A.
  • Reactive components A and B can be combined in a single molecule.
  • catalyst C can be combined in a single molecule with reactive component A and/or B.
  • the cross-linkable composition comprises an oligomeric or polymeric resin A comprising reactive components A.
  • the invention also relates to oligomeric or polymeric resin A comprising reactive components A having a hydroxy number of less than 60, preferably less than 40, more preferably less than 20 and optionally even less than 10 mg KOH/g solids.
  • the invention further relates to oligomeric or polymeric resin B comprising reactive components B and having a hydroxy number of less than 60, preferably less than 40 and more preferably less than 20 mg KOH/g solids.
  • the invention further relates to the use of resin A or resin B or mixtures of resin A and B for the preparation of RMA cross-linkable compositions.
  • Suitable examples of components A containing activated methylene or methine groups are well known in the art.
  • the polymer is a polyester, polyurethane or polycarbonate.
  • the crosslinkable component comprising reactive components A preferably is a polymer comprising one or more reactive components A having a structure according to formula 2:
  • R is hydrogen or an alkyl, aralkyl or aryl substituent and Y and Y′ are same or different substituent groups, preferably alkyl, aralkyl or aryl (R*), alkoxy (—OR*) or a polymer backbone or wherein the —C( ⁇ O)—Y and/or —C( ⁇ O)—Y′ is replaced by CN or phenyl and which polymer has a hydroxy number of less than 60, preferably less than 40 and more preferably less than 20 mg KOH/g solids.
  • R is hydrogen
  • the CH2 is the activated methylene
  • R is not hydrogen
  • the C—H is the activated methine.
  • the activated C—H group containing component A is malonate (in Y and Y′ are —OR* in Formula 1) or acetoacetate (Y is —OR* and Y′ is —R* in Formula 1).
  • Preferably more than 50, preferably 60, 70, 80, 90 or 95% of the reactive components A in the crosslinkable component are malonate groups.
  • Components containing both malonate and acetoacetate groups in the same molecule are also suitable.
  • physical mixtures of malonate and acetoacetate group-containing components are suitable.
  • the cross-linkable component comprising reactive component A preferably is a polymer comprising an average of 2 to 20, preferably 4 to 10 active C—H functions per molecule.
  • component A is a malonate containing compound. It is preferred that in the crosslinkable composition the majority of the activated C—H groups are from malonate, that is more than 50%, preferably more than 60%, more preferably more than 70%, most preferably more than 80% of all activated C—H groups in the crosslinkable composition are from malonate.
  • the crosslinking composition comprises a component A, for example a polymer, wherein more than 50%, preferably more than 70%, more preferably more than 80% and most preferably more than 90% of the activated C—H groups are from malonate and a separate component, for example another polymer, oligomer or monomer, comprising activated C—H groups not from malonate, for example acetoacetate.
  • a component A for example a polymer, wherein more than 50%, preferably more than 70%, more preferably more than 80% and most preferably more than 90% of the activated C—H groups are from malonate and a separate component, for example another polymer, oligomer or monomer, comprising activated C—H groups not from malonate, for example acetoacetate.
  • malonate group-containing components for use with the present invention are the malonate group-containing oligomeric or polymeric esters, ethers, urethanes and epoxy esters containing 1-50, more preferably 2-10, malonate groups per molecule.
  • polyesters and polyurethanes are preferred.
  • Such malonate group-containing components have a number average molecular weight (Mn) in the range of from about 100 to about 5000, more preferably, 250-2500, and an acid number of about 2 or less.
  • monomalonates can be used as they have 2 reactive C—H per molecule.
  • Monomeric malonates can, in addition, be used as reactive diluents.
  • the invention also relates to a polymeric or oligomeric resin A, for use in a RMA cross-linkable composition, comprising one or more reactive components A having a structure according to formula 2:
  • R is hydrogen or an alkyl, aralkyl or aryl substituent and Y and Y′ are same or different substituent groups, preferably alkyl, aralkyl or aryl (R*), alkoxy (—OR*) or a polymer backbone or wherein the —C( ⁇ O)—Y and/or —C( ⁇ O)—Y′ is replaced by CN or phenyl and which polymeric or oligomeric resin A has a hydroxy number of less than 60, preferably less than 40 and more preferably less than 20 mg KOH/g solids.
  • the polymeric or oligomeric resin is a polyester, polyether, polyepoxy, polyurethane or polycarbonate, more preferably a polyether, polyester or polyurethane, comprising reactive components A, preferably malonate or acetoacetate and preferably in an amount that the resin comprises an average of 2 to 20, preferably 4 to 10 active C—H functions per molecule.
  • reactive components A preferably malonate or acetoacetate and preferably in an amount that the resin comprises an average of 2 to 20, preferably 4 to 10 active C—H functions per molecule.
  • more than 50, preferably 60, 70, 80, 90 or 95% of the reactive components A in the crosslinkable component are malonate groups.
  • Malonate containing resin A is preferred over for example acetoacetate containing resin A because it provides improved pot life and coating hardness.
  • the resin A typically has a number molecular weight between 100-20000 gr/mol, preferably between 250 and 10000 and in view of the rheology of the coating composition and the mechanical properties of the obtained coating more preferably between 300 and 6000 gr/mol and preferably an equivalent weight per reactive component A of 100-2000 gr/mol.
  • the resin acid number this preferably less than 4, preferably less than 3, 2 or 1 mg KOH/gr because a high acid number would result in inactivation of at least a part of the base catalyst.
  • Components B generally can be ethylenically unsaturated components in which the carbon-carbon double bond is activated by an electron-withdrawing group, e.g. a carbonyl group in the alpha-position.
  • Suitable components B are known in the art, for example acryloyl esters, acrylamides, alternatively polyesters based upon maleic, fumaric and/or itaconic acid (and maleic and itaconic anhydride and polyesters, polyurethanes, polyethers and/or alkyd resins containing pendant activated unsaturated groups. Acrylates, fumarates and maleates are preferred.
  • the component B is an unsaturated acryloyl functional component.
  • the acid number of the activated unsaturated group-containing components is sufficiently low to not substantially impair activity of the catalyst, so preferably less than about 2, most preferably less than 1 mg KOH/g.
  • these and other activated unsaturated group-containing components, and their methods of production are generally known to those skilled in the art, and need no further explanation here.
  • the functionality is 2-20
  • the equivalent weight (EQW: average molecular weight per reactive functional group) is 100-2000
  • the number average molecular weight preferably is Mn 200-5000.
  • compositions comprising not only a high solids content but also aimed at a high crosslinking density, with relative high concentrations and functionalities of functional groups, for example in case the component A is a compound, in particular an oligomer or polymer, comprising an average of 2 to 30, preferably 4 to 20 and more preferably 4-10 activate C—H per polymer chain.
  • component A is a compound, in particular an oligomer or polymer, comprising an average of 2 to 30, preferably 4 to 20 and more preferably 4-10 activate C—H per polymer chain.
  • concentrations of the functional groups in components A and B, and their relative stoichiometry, are chosen such that good film properties following cure may be expected, with efficient use of these functional groups.
  • stoichiometries C—H/C ⁇ C are chosen o be from 0.1 to 10, preferably 0.5 to 3, more preferably 0.7 to 3, most preferably 0.8/1.5.
  • the invention also relates to a polymeric or oligomeric resin B for use in a RMA cross-linkable composition
  • a polymeric or oligomeric resin B for use in a RMA cross-linkable composition
  • one or more reactive components B comprising activated unsaturated groups (C ⁇ C), preferably unsaturated acryloyl or maleate functional groups (preferably acryloyl) or an acrylamide and which polymeric or oligomeric resin has a hydroxy number of less than 60, preferably less than 40 and more preferably less than 20 mg KOH/g solids.
  • the resin B preferably is a polyester, polyether, polyepoxy, polyurethane or polycarbonate comprising reactive component B and preferably has a number molecular weight between 300 and 20000 gr/mol, preferably between 300 and 10000 or 6000 gr/mol.
  • the prior art commonly uses TMPTA which has a molecular weight of 296.
  • the resin B preferably has a equivalent weight per reactive component A or B of 100-2000 gr/mol and an acid number less than 4, preferably less than 3, 2 or 1 mg KOH/gr.
  • the invention also relates to a resin mixture of polymeric or oligomeric resin A and polymeric or oligomeric resin B as described above for use in a RMA cross-linkable compositions and to the use use of resin A or resin B or of a resin mixture of resin A and resin B as cross-linkable components in an RMA cross-linkable composition.
  • at least one of resin A or resin B comprise at least 3 reactive cross-linking groups for forming a three-dimensional cross-linked network and at least one of resin A or resin B comprises at least two reactive cross-linking groups and wherein resin A or B or both have an average of 3-30 reactive cross-linking groups per polymer or oligomer molecule.
  • the invention also relates to a process for the preparation of the RMA resins A and B according to the invention, in particular, to a process for the preparation of resin A comprising transesterification of a polyol with reactive component A in the form of an carboxylic acid ester (Y and Y′ are alkoxy (—OR*)) and to a process for the preparation of resin B comprising transesterification of a polyol with reactive component B, preferably an acryloyl, in the form of carboxylic acid ester or by direct esterification of a polyol with reactive component B in the form of carboxylic acid.
  • Y and Y′ are alkoxy (—OR*)
  • the relative amounts of the components in the reaction mixture and the reaction time in combination with the reaction temperature are chosen such that the resulting resin A or B has the required low hydroxy number of less than 60, preferably less than 40 and more preferably less than 20 mg KOH/g solids.
  • the hydroxy value will be high in the beginning of the reaction and will gradually decrease as hydroxy groups of the polyol react with reactive component A.
  • the skilled person can calculate the required amounts of components such that the resulting resin A on completion of the reaction has a very low hydroxy value and can determine by known techniques, such as acid-base titration whether the resulting resin has reacted sufficiently long to reduce the hydroxy value to the required level to form resin A or B.
  • the polyester resin used in the present invention can be prepared by copolymerisation of one or more polyols, one or more polyacids, and one ore more esters of malonic acid and/or etylacetoacetic acid.
  • a preferred way of preparing the polyesters of present invention is to prepare in a first step a hydroxylfunctional polyester, and in later step transesterifying the polyester of the first step with esters of malonic or ethylacetoacetic acid and a volatile alcohol, prefeably ethanol or methanol.
  • the hydroxyfunctional polyester can also be prepared by reacting a hydroxyl functional polyester polyol with chain extenders, preferably lactones such as caprolactone, valerolactone, and butyrolactone.
  • chain extenders preferably lactones such as caprolactone, valerolactone, and butyrolactone.
  • this hydroxypolyester can be prepared by reacting a polyester bearing both hydroxyl and acid groups with one or more mono or polyfunctional epoxy compounds.
  • Suitable mono or polyfunctional epoxy compounds are mono-, di- or polyglycidyl ethers of (cyclo)aliphatic or aromatic hydroxyl compounds such as allyl alcohol, butanol, cyclohexanol, phenol, butyl phenol, decanol, ethylene glycol, glycerol, cyclohexane diol, mononuclear di- or trifunctional phenols, bisphenols such as Bisphenol-A or Bisphenol-F, and multinuclear phenols.
  • the polyols of the first step can also be prepared by reacting a hydroxy functional polyester of the first step with a mono- or polyfunctional isocyanate compound.
  • a mono- or polyfunctional isocyanate compound As suitable at least trifunctional isocyanates may be mentioned a wide variety of monomeric and oligomeric polyfunctional isocyanates.
  • the polycarboxylic acids for the preparation of the polyester polyol are preferably selected from the group of acyclic or cyclic polycarboxylic acids, the esters or the anhydrides thereof. Cyclic polycarboxylic acids include aromatic polycarboxylic acids and cycloaliphatic polycarboxylic acids. Included in this polycarboxylic acids are fatty acids, their esters, dimers and higher oligomers and mixtures thereof.
  • esters or the anhydrides thereof such as dimethyl ester and diethyl ester of malonic acid, succinic anhydride, octenyl succinic anhydride (any isomer or mixture of isomers of 4-octenyl-5-hydro-1,3furandione), dodecenyl succinic anhydride (any isomer or mixture of isomers of 4-dodecenyl-5-hydro-1,3-furandione), and mixtures thereof.
  • succinic anhydride any isomer or mixture of isomers of 4-octenyl-5-hydro-1,3furandione
  • dodecenyl succinic anhydride any isomer or mixture of isomers of 4-dodecenyl-5-hydro-1,3-furandione
  • the optionally co-condensed monocarboxylic acids may be aliphatic, cycloaliphatic, aromatic or mixtures thereof.
  • the monocarboxylic acid contains 6 to 18 carbon atoms, most preferably 7 to 14 carbon atoms, such as octanoic acid, 2-ethylhexanoic acid, isononanoic acid, decanoic acid, dodecanoic acid, benzoic acid, hexahydrobenzoic acid, and mixtures thereof.
  • the polyol is a cycloaliphatic or aliphatic polyol having 2 to 15 carbon atoms.
  • Preferred diols include 1,2ethane diol, 1,2-propane diol, 1,3-propane diol, 3-methyl-1,3-propane diol, 2butyl-2-ethyl-1,3-propane diol, dimethylol propionic acid, and 1,4-cyclohexane dimethanol.
  • suitable monofunctional alcohols include alcohols with 6-18 carbon atoms such as 2-ethyl hexanol, dodecanol, cyclohexanol and trimethyl cyclohexanol.
  • the optionally co-condensed monocarboxylic acids may be aliphatic, cycloaliphatic, aromatic or mixtures thereof.
  • the monocarboxylic acid contains 6 to 18 carbon atoms, most preferably 7 to 14 carbon atoms, such as octanoic acid, 2-ethylhexanoic acid, isononanoic acid, decanoic acid, dodecanoic acid, benzoic acid, hexahydrobenzoic acid, and mixtures thereof.
  • Typical hydroxy acids that can be used include dimethylol propionic acid, hydroxypivalic acid, and hydroxystearic acid.
  • Suitable monofunctional epoxy compounds include the glycidyl esters of branched Monocarboxylic acids such as Cardura(R) E from Resolution.
  • Polyurethane, polyether polyols can be prepared in the known manner using suitable monomers as described above.
  • the oligomer or polymer constituents of resin A are chosen such that the glass transition temperature of the resin A is between ⁇ 25 and +25° C., more preferably between ⁇ 20 and +20° C. and most preferably between ⁇ 20 and +15° C.
  • the glass transition temperature of resin B can be chosen between wider ranges, preferably between ⁇ 50 and +25° C.
  • the resins can be aliphatic or a mix of aliphatic and aromatic constituents with an aromatic constituents percentage chosen in view of the envisaged application.
  • the amount of aromatic compounds in resin A and in resin B and also in a mixture of resin A and Resin B is preferably at most 60 wt % (relative to the total weight of the resin or resin mixture), preferably at most 40, 20 or 10 wt %. Good results were obtained in a preferred embodiment wherein resin A and resin B are aliphatic resins, i.e. comprising substantially no aromatic constituents (at most 5 wt %).
  • the acid number of resin A and B is preferably less than 1 mg KOH/g solids.
  • the molecular weight is preferably low between 300 and 6000 gr/mol.
  • the hydroxy number is preferably as low as possible; most preferably less than 20 and optionally even less than 10 mg KOH/g solids. Even though the molecular weight is relatively low, in view of the mechanical properties of the resulting coating, the Resins must have sufficient cross-linking functionality.
  • resin A and resin B have an average functionality of 3-30 reactive cross-linking groups per polymer or oligomer molecule.
  • the functionality is preferably between 5 and 30, more preferably between 10 and 30.
  • Suitable combinations can be a mixture of resin A with relatively high functionality and resin B with a relatively low functionality, in particular resin A with functionality between 10 and 30 and resin B with a functionality of 3-20 or 3-10.
  • the base catalyst C can in principle be any known catalyst suitable for catalyzing RMA reactions.
  • the cross-linking composition comprises a catalyst system C comprising a strong based blocked by a volatile acid which is activated by evaporation of this acid.
  • a suitable catalyst system C comprises a strong base blocked by a carbon dioxide, or the blocked catalytic species are of formula ROCO2 ⁇ , R being a optionally substituted alkyl, preferably C1-C4 radical or hydrogen, preferably the catalyst comprises a blocked base anion and a non-acidic cation, preferably a quaternary ammonium or phosphonium cation.
  • Suitable catalyst C is described in WO2011/055463 herewith incorporated by reference. It is preferred that the crosslinking catalyst is utilized in an amount ranging between 0.001 and 0.3 meq/g solids, preferably between 0.01 and 0.2 meq/g solids, more preferably between 0.02 and 0.1 meq/g solids (meq/g solids defined as mmoles base relative to the total dry weight of the crosslinkable composition, not counting particulate fillers or pigments).
  • the catalyst system C is activated by reaction of an epoxy component with a tertiary amine, or an anion.
  • component A is a malonate
  • which composition further comprises 0.1-10 wt %, preferably 0.1-5, more preferably 0.2-3 and most preferably 0.5-2 wt % water (relative to total weight of the coating composition).
  • the amount of water is chosen in an effective amount to increase gel time with at least 15 minutes, preferably at least 30 min, more preferably at least 1 h, even more preferably at least 5 h, and most preferably at least 24 h, 48 h. or at least 10%, 50% or 100% compared to the same composition without water.
  • the cross-linkable composition may comprise as an additive to improve appearance and or hardness of the coating an X—H group containing component (D) that is also a Michael addition donor reactable with component B under the action of catalyst C, wherein X is C, N, P, O or S, preferably C, N or P, preferably present in quantities of at least 50 mole % relative to base generated by component C, and less than 30 mole % of C—H active groups from component A.
  • X—H group containing component (D) that is also a Michael addition donor reactable with component B under the action of catalyst C, wherein X is C, N, P, O or S, preferably C, N or P, preferably present in quantities of at least 50 mole % relative to base generated by component C, and less than 30 mole % of C—H active groups from component A.
  • Component D as described in an catalysed RMA crosslinkable composition can create a reactivity profile comprising an initial induction time of lowered reaction rate directly after application and activation of the system, followed by a relative increase of reactivity in later stages.
  • This induction time can be tuned, to allow a “open time” the period allowing flow and solvent and entrapped air bubbles to escape.
  • the induction time allows a significantly higher amount of flow and levelling of the system, avoiding surface defects that may result from very fast cure without these additives, and better hardness build-up due to reduced solvent entrapment, while still benefiting from the full potential of the catalysts beyond this induction time, thus creating an acceleration of the reaction at later stages to complete crosslinking at higher rate than would be found if simply using lower catalyst levels. Also the high sensitivity of lower catalyst levels towards accidentally present acid contaminations is avoided.
  • the crosslinkable composition according to the invention is particularly suitable for making thick layers. Thick layers are considered to be layers having a cured dry thickness of at least 50 or more than 70 micrometers. In thick layer applications the risk of air and solvent inclusions is higher. This is particularly pronounced in RMA crosslinkable compositions that are cured at low temperature in the range from 10 to 60° C. where resins are more viscous and levelling is difficult.
  • the X—H group in component D has a higher acidity than the C—H groups in component A, preferably being characterized in that component D has a pKa (defined in aqueous environment) of at least one unit, preferably two units, less than that of component A.
  • the pKa of the X—H group in component D is lower than 13, preferable lower than 12, more preferably lower than 11 most preferably lower than 10.
  • An excessive acidity may create problems with components in the catalyst system; therefore hence the pKa is preferably higher than 7, more preferably higher than 7.5 and optionally higher than 8.
  • the acidity difference assures that on application of the coating, component D is activated (deprotonated) preferentially over component A.
  • component D is selected from one or more compounds from the group of Compounds D1 comprising C—H acidic protons (X is C) in activated methylene or methine groups and Compounds D2 comprising N—H acidic compound (X is N).
  • Suitable components D2 are an aza-acidic compounds (X is N) preferably comprising a molecule containing the N—H as part of a group Ar—NH—(C ⁇ O)—, —(C ⁇ O)—NH—(C ⁇ O)—, or of a group —NH—(O ⁇ S ⁇ O)— or a heterocycle in which the nitrogen of the N—H group is contained in a heterocyclic ring, more preferably component D2 is an imide derivative, preferably an (optionally substituted) succinimide or glutarimide.
  • Suitable components D2 are hydantoin derivatives, for example 5,5-dimethylhydrantoin, sulfonamides, for example aromatic sulfonamides as benzene- or toluenesulfonamide or heterocyclic compounds, for example triazoles or a pyrazoles, or a uracil derivative.
  • the X—H groups in component D are present in an amount corresponding to at least 50 mole %, preferable at least 100 mole %, most preferably at least 150 mole % relative to the amount of base to be generated by catalyst C.
  • the appropriate amount is very much determined by the acid base characteristics of component D relative to component A, and the reactivity of the corresponding anions relative to B, so may vary for different systems. It is noted that the open time improving effect can in some cases be obtained at very small amounts of component D, which is very advantageous because such small amounts do not or not significantly affect the properties of the resulting cured composition; for example the chemical and mechanical properties of a coating.
  • the X—H groups in component D are present in an amount corresponding to no more than 30 mole %, preferably no more than 20, optionally no more than 10 mole % relative to C—H donor groups from component A.
  • the X—H functionality (number of groups per molecule) of component D is low, preferably less than 4, more preferably less than 2, most preferably it is 1.
  • the crosslinkable composition may comprise next to one or more different components D a component D1 comprising acidic protons (C—H) in activated methylene or methine groups having a higher acidity than component A and which are also is reactive towards component B,
  • component D1 can also contribute to the open time improving effect, however in order to have a significant effect D1 should be typically be present in an amount between 10-40 mol % (relative to total RMA C—H), which is a significantly higher amount than for component D.
  • the difference in acidity of the two C—H acidic components A and D1 is chosen preferably in that wherein the pKa of component D1 is between 0.5 and 6, preferably between 1 and 5 and more preferably between 1.5 and 4 units lower than the pKa of component A.
  • component A is a malonate containing component and component D1 is an acetoacetate or acetylacetone containing component, preferably of low C—H functionality (preferably less than 10, more preferably less than 5, most preferably it is no more than 2.
  • Suitable components D and A2 are listed below with the pKa value.
  • succinimide 9.5 ethosuximide 9.3 5,5-dimethylhydantoin 10.2 1,2,4-triazole 10.2 1,2,3-triazole 9.4 benzotriazole 8.2 benzenesulfonamide 10.1 nitromethane 10.2 isatine 10.3 uracil 9.9 4-nitro-2-methylimidazole 9.6 phenol 10.0 ethylacetoacetate 10.7 acetylacetone 9.0 diethylmalonate 13.0
  • the invention also relates to the use of the component D as described above as an additive to RMA cross-linkable compositions.
  • the advantages of improved appearance and improved hardness can be obtained irrespective of the thickness of the layer but are particularly apparent in thick coating layers having a dry thickness of at least 50, preferably at least 60, 75, 100 and more preferably at least 125 micrometer, for the improvement of the open time of the crosslinkable composition and for the improvement of the appearance and hardness of the resulting cured composition, in particular a coating.
  • component D is chosen to yield, under the application and curing conditions chosen, an increase in time to get to a 30% conversion level, of at least 3, preferably 5, more preferably 10 minutes, preferably less than 60, more preferably less than 30 minutes, when compared to the same composition without component D.
  • the cross-linkable composition can be used without having any additional solvent. This would typically be the case when the cross-linkable components in the composition have sufficient low viscosity and all components together form a solution.
  • a solvent may be added for example to reduce the viscosity in case of high solids content of relatively high viscosity components, to mediate the reaction kinetics or in case the composition contains certain additives that would require the solvent.
  • the solvent can be water or can be an organic solvent or mixtures thereof. Most preferred is to use an organic solvent.
  • the organic solvent may contain (substantially) no water. However, it is sometimes preferred in view of increasing pot life to add in addition to organic solvent also a relatively small amount of water, preferably between 0.1 and 10 wt % (relative to the total weight of the cross-linkable composition).
  • the inventors further found that advantages can be achieved in pot life if in the crosslinkable composition at least part of the solvent is a primary alcohol solvent.
  • the solvent can be a mixture of a non-alcoholic solvent and an alcohol solvent.
  • the alcohol is present in an amount of at least 1, preferably 2, more preferably 3, most preferably at least 5, even more preferably at least 10 wt % relative to the total weight of the crosslinkable composition and in view of VOC constraints preferably at most 45, preferably at most 40 wt %, most preferably less than 30 wt %.
  • the alcohol solvent preferably is one or more primary alcohols, more preferably a mono-alcohol having 1 to 20, preferably 1-10, more preferably 1-6 carbon atoms, preferably selected from the group of ethanol, n-propanol, n-butanol, n-amyl alcohol and butylglycol
  • crosslinkable composition according to the invention comprises
  • the invention also relates to a kit of parts for the manufacture of the composition according to the invention comprising a part 1 comprising components A and B but not C and part 2 comprising component C.
  • a kit of parts for the manufacture of the composition according to the invention comprises a part 1 comprising the cross-linkable components comprising reactive components A and/or B but no C and part 2 comprising component C
  • the invention also relates to the use of the crosslinking composition according to the invention in a method for the manufacture of coating compositions, films or inks and to coating compositions, inks or films comprising the crosslinking composition according to the invention and further application oriented additives for example one or more coating additives like pigments, co-binder, solvents etc.
  • the invention also relates to a process for making a coating layer having a fully cured dry thickness of at least 70, 75, 80 or 100 and more preferably at least 125 micrometer and having a good surface appearance and hardness of the resulting cured composition
  • a process for making a coating layer having a fully cured dry thickness of at least 70, 75, 80 or 100 and more preferably at least 125 micrometer and having a good surface appearance and hardness of the resulting cured composition comprising mixing the components A, B with cayalyst C shortly before use to form a coating composition according to the invention, applying a layer of the coating composition on a substrate and allowing the curing thereof at temperature between 0 and 60° C.
  • Persoz hardness measurement Persoz pendulum hardness was measured in a climatized room at 23° C., and 55+/ ⁇ 5% relative humidity. Hardness is measured with a pendulum acc. Persoz as described in ASTM D 4366.
  • Drying time was determined by firmly pressing the thumb in the paint film. The time was recorded when there was no visible trace left in the paint film.
  • Paints were prepared according the composition in the table.
  • the pigment was dispersed in the mixture of Disperbyk and Sartomer (which is cross-linkable component B: DiTMPTA is di-trimethylolpropane-tetraacrylate) with a high shear stirrer for 15 minutes. Then the other ingredients were added under stirring. Prior to application the catalyst solution was added.
  • Disperbyk and Sartomer which is cross-linkable component B: DiTMPTA is di-trimethylolpropane-tetraacrylate
  • a catalyst solution was formed as follows: to 8.03 g of a 55% solution of tetra-butylammoniumhydroxide were added 11.05 g of diethylcarbonate and 6.74 g of isopropanol.
  • WO 2011/055463 describes in Example 4 Formulations made from a malonate polyester component A-1 and TMPA as the cross-linkable component B-1 and various catalysts.
  • the malonate polyester A-1 had an OH value of 83.2 mg KOH/g. Apart from the hydroxy value, the malonate polyester A-1 is similar to the above described malonate polyester I and II.
  • the catalyst C-5 tetrabutylammonium ethylcarbonate
  • the Perzos hardness was 65 after 1 month curing time, whereas the resin according to the invention having a low hydroxy value as a significantly higher hardness (88) already after three days curing time.
  • Molecular weights were measured by GPC in THF, and expressed in polystyrene equivalent weights. Viscosities were measured with a TA Instruments AR2000Rheometer, using a cone and plate setup (cone 4 cm 1°) at 1 Pa stress.
  • Tube and ball method for pot life determination A flat bottomed test tube (internal diameter 15 mm, length 12.5 cm), carrying two marks, 5 cm apart is filled with 20 ml of paint. A steel ball with a diameter of 8 mm is added, and the tube is closed with a snap cap. The tube is held under an angle of 10° and the steel ball is allowed to roll on the wall of the test tube. The time needed to roll between the two marks is taken as a measure for the viscosity. The time needed to double in viscosity is taken as the pot life. If necessary this time is calculated by linear interpolation between two measurements. This method was used for the pigmented formulations.
  • a glass test tube (length 12 cm, diameter 13 mm) was filled with a stainless steel ball of 12 mm diameter, and the formulation to be studied to leave a very limited head space, and closed. Time was recorded for the ball to fall and pass a distance of 5 cm when the tube was tilted vertically. An average was taken over 2 measurements.
  • Drying recorder drying time For determining the recorder drying time, paint was applied on a glass panel with a doctor blade with a 90 ⁇ gap. The drying time was measured with a Gardco electronic drying time recorder, type DT-5020, set on a cycle time of 60 minutes. Drying time was recorded as the time were the stylus left no more visible trace on the film.
  • TNO cotton ball drying times Dust-dry and tack-free times were measured according to the so-called TNO method with a wad of cotton-wool. Dust-dry time means the time needed for the coating after dropping the wad on the surface of the coating and after leaving it there for 10 seconds, to get no residue of the wool-cotton sticking onto the surface after blowing away the wad. For tack-free time the same holds but now a weight load of 1 kg is applied on the wad for 10 seconds.
  • Persoz hardness measurement Persoz pendulum hardness was measured in a climatized room at 23° C., and 55+/ ⁇ 5% relative humidity. Hardness is measured with a pendulum acc. Persoz as described in ASTM D 4366. For the gradient layer thickness panels, hardness is measured at different spots and corresponding layer thickness is measured. If necessary the hardness at a certain layer thickness is calculated by linear interpolation of the measurement at two different layer thicknesses. Layer thicknesses were measured with a Fischer Permascope MP40E-S.
  • Optical evaluation spayed pigmented paints Paint was sprayed with a devilbiss spraygun, nozzle FF-1.4 with an air pressure of 3.5 bar. The paint was prayed in a continuous layer over the entire surface of a 55 ⁇ 10 cm steel panel. A consecutive layer was sprayed starting 10 cm from the right edge. Several layers were built up, moving to the right so that a layer thickness gradient was build up from the left to right. Films were allowed to dry horizontally at 23° C., 45% RH. Layer thicknesses were measured with a Fischer Permascope MP40E-S. At 100 ⁇ layer thickness, a picture was taken with an Olympus SZX10 microscope (1 ⁇ magn) equipped with a digital camera.
  • Wavescan analysis The panels as described above were analyzed using the Wavescan II of Byk instruments. Data were stored using Autochart software from Byk. Analysis was done in the direction perpendicular to the thickness gradient. In this instrument the light of small laser diode is reflected by the surface of the sample under an angle of 60°, and the reflected light is detected at the gloss angle (60° opposite). During the measurement, the “wave-scan” is moved across the sample surface over a scan length of approx. 10 cm, with a data point being recorded every 0.027 mm. The surface structure of the sample modulates the light of the laser diode. The signal is divided into 5 wavelength ranges in the range of 0.1-30 mm and processed by mathematical filtering.
  • a characteristic value (Wa 0.1-0.3 mm, Wb 0.3-1.0 mm, We 1.0-3.0 mm, Wd 3.0-10 mm, We 10-30 mm) as well as the typical wave-scan-values longwave (LW, approx. 1-10 mm) and shortwave (SW, approx. 0.3-1 mm) is calculated.
  • Low values mean a smooth surface structure.
  • a LED light source is installed in the wave-scan DOI and illuminates the surface under 20 degrees after passing an aperture. The scattered light is detected and a so-called dullness value (du, ⁇ 0.1 mm) is measured.
  • a so-called dullness value (du, ⁇ 0.1 mm) is measured.
  • Disperbyk 163 is a dispersant commercially supplied by Byk;
  • Byk 310 and 315 are additives commercially supplied by ByK;
  • Catalyst solution was prepared by reacting 59.4 g a TBAH solution (40% in water) with 13.5 g DEC (reacting overnight at RT), with 14.5 g isopropanol as co-solvent, following the corresponding ethocarbonate species development. Titration indicated that blocking was complete, and that the concentration of blocked base was 0.83 meq/g solution.
  • Formulations were prepared based on a malonate donor resin A, DiTMPTA as acryloyl donor resin, and the indicated amount of succinimide, and thinned to a viscosity of 160 mPas with a mixture of MEK/BuAc 1:1 by volume. This was mixed with an amount of catalyst solution C1.
  • Catalyst amounts are 50 meq/g solids, water levels are 1.8 wt %, isopropanol at 0.7 wt %, ethanol level estimated at 0.2 wt %.
  • No-D example 1 shows an extremely fast drying
  • the actual Persoz hardness levels are low presumably due to solvent entrapment in the system.
  • the appearance of this No-D example 1 is poor.
  • succinimide significantly higher than the levels of catalyst used
  • some retardation of the drying is seen, but still giving drying times considered as fast; however, it can also be observed that the Persoz hardness development is strongly improved.
  • the example films with succinimide exhibit a better appearance than No-D example 1.
  • Example formulations 5-7, and No-D example formulations 2-3 were prepared as pigmented paints, having compositions as tabulated in Table C (amounts in grams).
  • Example 5 (with succinimide added) exhibits higher Persoz hardness, a better pot life, and a better appearance than No-D example 2 (not containing succinimide).
  • Example 8 was prepared and evaluated in a similar way as discussed above for example 5-7, the composition and results given below in table D (amounts in grams). It can be seen that the additional presence of 1,2,4-triazole (when compared to example 6) leads to a significant improvement in pot-life, other advantages being retained.
  • Example formulations 9 and 10, and No-D example formulations 4 and 5 were formulated and evaluated along similar lines, now also including Wavescan analysis to have a quantitative indication of the quality of the appearance. Compositions and results are given in Table E (amounts in grams).
  • Example formulation 9 can be compared with No-D formulation example 4
  • example formulation 10 can be compared with No-D formulation example 5, difference being the presence of low amounts of succinimide. It can from both comparisons be concluded that the presence of succinimide, besides the improved Persoz hardness, leads to significantly improved values for longwave and shortwave roughness, dullness and DOI.
  • the conversion of the acryloyls in the system can be followed by FTIR, focusing on the 809 cm ⁇ 1 band characteristic of the acryloyl. Doing that, the impact of added succinimide on total conversion can be made visible.
  • Two systems were formulated (according to compositions of No-D example 1 (without succinimide) and example formulation 1 (with 150% succinimide relative to solids).
  • FIG. 1 compares the conversion of these systems after application on top of an ATR crystal, the IR beam probing the deepest layers, close to the substrate. Initial conversion of the formulation without the succinimide is fast, which is also the cause for solvent entrapment and potential appearance problems.
  • succinimide 5 grams were dissolved in a mixture of 42 grams of butyl acrylate and 42 grams of methanol, and maintained at room temperature as such, or after adding a strong base (9.82 grams of a 1.12 meq/g solution of tetrabutylammonium hydroxide in methanol, 11 meq). Subsequently, the concentration of succinimide is determined as a function of time by taking samples, neutralizing with a known excess of HCl in water, and backtitration with a KOH solution. Without base initiation, no significant loss of succinimide N—H in this solution is observed in two weeks. With the base added, the succinimide concentration can be seen to decrease with time, as illustrated in the table F below. Succinimide concentration is expressed as % relative to the theoretical level based on used amounts.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Engineering & Computer Science (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Health & Medical Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Paints Or Removers (AREA)
  • Application Of Or Painting With Fluid Materials (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
  • Polyesters Or Polycarbonates (AREA)
US14/246,229 2011-10-07 2014-04-07 Crosslinkable composition cross-linkable by real michael addition reaction and resins for use in said composition Abandoned US20140221542A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US15/889,291 US10647876B2 (en) 2011-10-07 2018-02-06 Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
EP11184439.5 2011-10-07
EP11184439 2011-10-07
PCT/EP2012/069904 WO2013050622A1 (fr) 2011-10-07 2012-10-08 Composition réticulable réticulable par réaction d'addition de michael réelle et résines destinées à être utilisées dans ladite composition

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2012/069904 Continuation WO2013050622A1 (fr) 2011-10-07 2012-10-08 Composition réticulable réticulable par réaction d'addition de michael réelle et résines destinées à être utilisées dans ladite composition

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/889,291 Division US10647876B2 (en) 2011-10-07 2018-02-06 Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition

Publications (1)

Publication Number Publication Date
US20140221542A1 true US20140221542A1 (en) 2014-08-07

Family

ID=47002872

Family Applications (5)

Application Number Title Priority Date Filing Date
US14/246,229 Abandoned US20140221542A1 (en) 2011-10-07 2014-04-07 Crosslinkable composition cross-linkable by real michael addition reaction and resins for use in said composition
US14/246,257 Active US9260626B2 (en) 2011-10-07 2014-04-07 Crosslinkable composition
US14/938,885 Active US9834701B2 (en) 2011-10-07 2015-11-12 Crosslinkable composition
US14/989,961 Active US9587138B2 (en) 2011-10-07 2016-01-07 Crosslinkable composition
US15/889,291 Active US10647876B2 (en) 2011-10-07 2018-02-06 Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition

Family Applications After (4)

Application Number Title Priority Date Filing Date
US14/246,257 Active US9260626B2 (en) 2011-10-07 2014-04-07 Crosslinkable composition
US14/938,885 Active US9834701B2 (en) 2011-10-07 2015-11-12 Crosslinkable composition
US14/989,961 Active US9587138B2 (en) 2011-10-07 2016-01-07 Crosslinkable composition
US15/889,291 Active US10647876B2 (en) 2011-10-07 2018-02-06 Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition

Country Status (11)

Country Link
US (5) US20140221542A1 (fr)
EP (3) EP2764037B1 (fr)
JP (2) JP6194448B2 (fr)
KR (1) KR102131463B1 (fr)
CN (3) CN105985724A (fr)
DK (2) DK2764037T3 (fr)
ES (3) ES2639396T3 (fr)
PL (3) PL2764035T3 (fr)
SG (1) SG11201401321WA (fr)
SI (2) SI2995636T1 (fr)
WO (2) WO2013050624A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140235785A1 (en) * 2011-10-07 2014-08-21 Nuplex Resins B.V. Crosslinkable composition crosslinkable by real michael addition (rma) reaction
DE102015105983A1 (de) * 2015-04-20 2016-10-20 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Verbesserte Beschichtungssysteme, deren Verwendung zur Beschichtung von Bauteilen sowie damit beschichtete Bauteile für Land- und Baumaschinen
DE102015105979A1 (de) * 2015-04-20 2016-10-20 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Verbesserte Beschichtungssysteme, deren Verwendung zur Beschichtung von Bauteilen sowie damit beschichtete Bauteile für Windkraftanlagen
DE102015105987A1 (de) * 2015-04-20 2016-10-20 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Verbesserte Beschichtungssysteme, deren Verwendung zur Beschichtung von Bauteilen sowie damit beschichtete Bauteile für Schienen- und Luftfahrzeuge
US10604622B2 (en) 2013-04-08 2020-03-31 Allnex Netherlands B.V. Composition crosslinkable by Real Michael Addition (RMA) reaction
US10624833B2 (en) 2016-06-30 2020-04-21 Elementis Specialties, Inc. Crosslinkable coating compositions formulated with dormant carbamate initiator
US10647876B2 (en) 2011-10-07 2020-05-12 Allnex Netherlands B.V. Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition
US10759962B2 (en) 2015-04-17 2020-09-01 Allnex Netherlands B.V. Method for applying RMA crosslinkable coating on modified epoxy primer coating
US10767074B2 (en) * 2015-04-17 2020-09-08 Allnex Netherlands B.V. Process for the manufacture of a crosslinkable composition
US10774238B2 (en) 2015-04-17 2020-09-15 Allnex Netherlands B.V. Method for curing a RMA crosslinkable resin coating, RMA crosslinkable compositions and resins for use therein
US10894886B2 (en) 2017-06-13 2021-01-19 Elementis Specialties, Inc. Coating system
CN113861402A (zh) * 2021-10-27 2021-12-31 江苏富琪森新材料有限公司 一种水性聚酯树脂及其制备方法和应用
US11814536B2 (en) 2015-04-17 2023-11-14 Allnex Netherlands B.V. Floor coating compositions

Families Citing this family (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104387821B (zh) * 2014-11-24 2017-06-13 中山大桥化工集团有限公司 高固体份汽车罩光清漆及其制备方法
BR112019020480B1 (pt) 2017-04-04 2024-01-09 Swimc Llc Composição de revestimento, e, substrato metálico revestido
CA3058850A1 (fr) 2017-05-16 2018-11-22 Allnex Netherlands B.V. Systeme de revetement pour compositions de revetement reticulables par rma
WO2018213694A1 (fr) * 2017-05-19 2018-11-22 Swimc Llc Composition de revêtement polyuréthane
US11732165B2 (en) 2017-06-13 2023-08-22 Eastman Chemical Company Low-temperature curable compositions
US20200283647A1 (en) * 2017-08-23 2020-09-10 Kansai Paint Co., Ltd. Cationic electrodeposition coating composition and method for electrodeposition coating
KR20200116090A (ko) * 2018-01-26 2020-10-08 알넥스 네덜란드 비. 브이. 파우더 코팅 조성물
EP3663326A1 (fr) 2018-12-04 2020-06-10 Allnex Netherlands B.V. Polymère rma réticulable
CN113195634B (zh) 2018-12-11 2023-06-16 伊士曼化工公司 包含了含乙酰乙酰化树脂的可固化组合物的挠性基材
US11920050B2 (en) 2018-12-11 2024-03-05 Eastman Chemical Company Self-curable and low temperature curable coating compositions
CN109877025B (zh) 2019-01-29 2022-04-26 广东华润涂料有限公司 木制品及其制备方法
CN109909138B (zh) 2019-01-29 2022-07-12 广东华润涂料有限公司 木制品及其制备方法
EP3702423A1 (fr) 2019-02-26 2020-09-02 Allnex Netherlands B.V. Système de revêtement pour compositions de revêtement réticulables par rma
CN110105799B (zh) * 2019-05-07 2021-10-01 广东华润涂料有限公司 木器用涂料组合物以及由其制成的木制品
MX2022007244A (es) 2019-12-19 2022-07-13 Allnex Netherlands Bv Composicion reticulable no acuosa.
CN115836097A (zh) 2020-06-16 2023-03-21 广东华润涂料有限公司 可固化涂层组合物和涂覆制品
CN111793425B (zh) * 2020-07-01 2022-03-18 王俊宇 多涂层体系、涂覆方法、涂层结构以及被涂覆的基材
WO2022212457A1 (fr) 2021-03-31 2022-10-06 Sheboygan Paint Company Revêtements contenant de la triphénylphosphine présentant une adhérence améliorée à des surfaces non apprêtées
CN115466532B (zh) * 2021-06-10 2023-05-02 广东华润涂料有限公司 可迈克尔加成固化的组合物、包含该组合物的涂料组合物以及涂布制品
BR112023025747A2 (pt) 2021-06-22 2024-02-27 Allnex Netherlands Bv Composto particulado de poliureia a2), composição de resina a, composição reticulável, processo para revestir um artigo ou um substrato, e, substrato

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5959028A (en) * 1996-05-22 1999-09-28 Nippon Paint Co., Ltd. Curable resin composition for coating use
US20030023108A1 (en) * 2001-07-09 2003-01-30 Lonza Inc. In situ process for preparing quaternary ammonium bicarbonates and quaternary ammonium carbonates
WO2008157468A1 (fr) * 2007-06-18 2008-12-24 Ethicon, Inc. Dérivés de polymère de lactame
US8962725B2 (en) * 2010-04-07 2015-02-24 Nuplex Resins B.V. Crosslinkable composition crosslinkable with a latent base catalyst
US9260626B2 (en) * 2011-10-07 2016-02-16 Nuplex Resins B.V. Crosslinkable composition
US9284423B2 (en) * 2011-10-07 2016-03-15 Nuplex Resins B.V. Crosslinkable composition crosslinkable by real michael addition (RMA) reaction

Family Cites Families (99)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2635100A (en) 1949-11-15 1953-04-14 Du Pont Monoquaternary ammonium carbonates and their preparation
DE835809C (de) 1950-02-28 1952-04-03 Bayer Ag Verfahren zur Herstellung von Polyadditionsprodukten
US2759913A (en) 1952-05-20 1956-08-21 Hercules Powder Co Ltd Copolymers of compounds containing activated ethylene double bonds with active hydrogen compounds
US4102863A (en) 1976-11-24 1978-07-25 Ppg Industries, Inc. Cationic electrodeposition using aqueous dispersions of quaternary ammonium carbonate-containing polymers
US4223072A (en) 1977-12-23 1980-09-16 Dow Corning Corporation Flexible coating resins from siloxane resins having a very low degree of organic substitution
CA1116771A (fr) 1977-12-23 1982-01-19 Ronald H. Baney Enduit souple fait de resines de siloxane ayant un degre tres faible de substitution organique
DE2967531D1 (en) 1978-07-27 1985-11-21 Chemical Res & Licensin Catalytic distillation process and catalyst
US4217396A (en) 1979-05-10 1980-08-12 Armstrong Cork Company Acrylate-acetoacetate polymers useful as protective agents for floor coverings
US4268610A (en) 1979-11-05 1981-05-19 Hercules Incorporated Photoresist formulations
US4348431A (en) 1981-02-19 1982-09-07 General Electric Company Process for coating plastic films
NL8203502A (nl) 1982-09-08 1984-04-02 Ir Pieter Voogel Werkwijze voor het beschermen van metalen voorwerpen, alsmede een daarbij te gebruiken grondlak en deklak.
US4408018A (en) 1982-10-29 1983-10-04 Rohm And Haas Company Acetoacetate functionalized polymers and monomers useful for crosslinking formulations
US4938980A (en) 1983-03-30 1990-07-03 Nabisco Brands, Inc. Low sodium cake mix and process of preparing low sodium cake
US4529487A (en) 1983-09-29 1985-07-16 The Boeing Company Coating for increasing corrosion resistance and reducing hydrogen reembrittlement of metal articles
ZA852044B (en) 1984-03-29 1985-11-27 Akzo Nv Liquid coating composition curable at ambient temperature
EP0160824B2 (fr) 1984-04-04 1994-08-03 Hoechst Aktiengesellschaft Produit de réaction de composés ayant d'insaturations oléfiniques avec des composés ayant d'hydrogène actif, procédé pour leur préparation et vernis en deux composants dérivant de ceux-ci
NL8500476A (nl) * 1985-02-20 1986-09-16 Akzo Nv Thixotrope bekledingssamenstelling.
NL8500475A (nl) 1985-02-20 1986-09-16 Akzo Nv Thixotrope bekledingssamenstelling.
BR8606287A (pt) 1985-12-19 1987-10-06 Cook Paint & Varnish Inc Processo para a preparacao de um polimero reticulado
US4749728A (en) 1986-06-06 1988-06-07 The Glidden Company Epoxy/nucleophile transesterification catalysts and thermoset coatings
DE3733182A1 (de) 1987-10-01 1989-04-20 Hoechst Ag Haertungskomponente und deren verwendung
US5017649A (en) 1988-01-19 1991-05-21 Eastman Kodak Company Low temperature Michael addition reactions
ES2046291T3 (es) 1988-02-01 1994-02-01 Rohm And Haas Company Metodo de reaccion de dos componentes, composiciones, composiciones de recubrimientos y sus usos.
EP0448154A1 (fr) 1990-03-20 1991-09-25 Akzo Nobel N.V. Composition de revêtement contenant un catalyseur basique bloqué
US5137966A (en) 1991-02-25 1992-08-11 Miles Inc. Internal release agents, active hydrogen containing mixtures which contain such agents and the use thereof in a process for the production of molded products
BR9405802A (pt) 1993-03-30 1995-12-12 Shell Int Research Composição de éster epoxídico
AU672337B2 (en) 1993-10-27 1996-09-26 Nippon Paint Co., Ltd. Curable resin composition for coating uses
JPH08283657A (ja) * 1995-04-12 1996-10-29 Nippon Paint Co Ltd 塗料用硬化性樹脂組成物
US6265029B1 (en) 1995-05-04 2001-07-24 William Lewis Low-cost, user-friendly hardcoating solution, process and coating
PL185685B1 (pl) 1995-06-09 2003-07-31 Dsm Nv Kompozycja wiążąca zawierająca polimer silnie aktywowany karboanionowymi grupami funkcyjnymi, sposób wytwarzania kompozycji wiążącej i sposób nakładania powłoki opartej na kompozycji wiążącej
JPH1045993A (ja) 1996-05-22 1998-02-17 Nippon Paint Co Ltd 硬化性樹脂組成物および塗料
JPH1025437A (ja) * 1996-07-08 1998-01-27 Nippon Paint Co Ltd カチオン電着塗料用樹脂組成物および塗料
WO1998025989A1 (fr) 1996-12-11 1998-06-18 Minnesota Mining And Manufacturing Company Resine susceptible de durcir a temperature ambiante
US6262169B1 (en) 1998-05-14 2001-07-17 Eastman Chemical Company Protonated amines for controlled crosslinking of latex polymers
JP3882096B2 (ja) 1997-05-28 2007-02-14 日本ペイント株式会社 硬化性樹脂組成物
US6262161B1 (en) 1997-06-26 2001-07-17 The Dow Chemical Company Compositions having improved ignition resistance
US5990224A (en) 1997-09-18 1999-11-23 Eastman Chemical Company Stable low foam waterborne polymer compositions containing poly(alkyleneimines)
US6005035A (en) 1997-09-18 1999-12-21 Eastman Chemical Company Stable waterborne polymer compositions containing poly(alkylenimines)
US6201048B1 (en) 1997-09-18 2001-03-13 Eastman Chemical Company Stable waterborne polymer compositions containing poly(alkyleneimines)
US5945489A (en) * 1997-09-19 1999-08-31 Ashland, Inc. Liquid oligomers containing unsaturation
US6025410A (en) * 1997-09-19 2000-02-15 Ashland Inc. Liquid oligomers containing acrylate unsaturation
WO2000004106A1 (fr) 1998-07-13 2000-01-27 Shell Internationale Research Maatschappij B.V. Compositions de revetement en resine epoxy a base d'eau
BR0114858B1 (pt) 2000-10-25 2011-05-03 "composição para revestimento contida em água que pode ser fotoativada, processo de revestimento de um substrato e processos de aplicação de revestimento".
FR2818974B1 (fr) 2000-12-29 2003-10-24 Rhodia Chimie Sa (cyclo) condensation de composes isocyanates
JP2002285100A (ja) 2001-03-27 2002-10-03 Nippon Paint Co Ltd 熱硬化塗料組成物およびそれを用いた塗膜形成方法
US6897264B2 (en) * 2001-12-21 2005-05-24 Dainippon Ink And Chemicals, Inc. Curable mixtures
US6780523B2 (en) 2002-04-12 2004-08-24 Eastman Chemical Company Waterborne acetoacetate-functionalized alkyd coating compositions
CA2482470C (fr) 2002-04-19 2011-06-07 Ciba Specialty Chemicals Holding Inc. Durcissement de revetements induit par plasma
EP1371689A1 (fr) * 2002-06-14 2003-12-17 Dainippon Ink And Chemicals, Inc. Compositions de revêtement durcissables et stables au stockage
US6706414B1 (en) 2002-09-26 2004-03-16 Ashland Inc. Liquid uncrosslinked Michael addition oligomers prepared in the presence of a catalyst having both an epoxy moiety and a quaternary salt
US6878845B2 (en) 2002-10-15 2005-04-12 Ashland Inc. Oligomers from multifunctional acrylates
US8013068B2 (en) * 2003-01-02 2011-09-06 Rohm And Haas Company Michael addition compositions
WO2004099329A1 (fr) 2003-05-08 2004-11-18 The University Of Southern Mississippi Research Foundation Diluants reactifs en formulation d'enrobage
SI1641888T1 (sl) 2003-07-08 2012-06-29 Nuplex Resins Bv Aminokislinski derivati in njihova uporaba kot sredstvo za nadzor nad usedanjem
WO2005005557A1 (fr) * 2003-07-08 2005-01-20 Nuplex Resins B.V. Derives methylamine a substitution carbone et leur utilisation comme agents de controle de rheologie
JP4160459B2 (ja) * 2003-07-15 2008-10-01 日本ペイント株式会社 硬化塗膜の形成方法
GB2405149A (en) 2003-08-16 2005-02-23 Dow Corning Free flowing organosiloxane elastomer base powder
WO2005021672A1 (fr) 2003-08-28 2005-03-10 Advanced Elastomer Systems, L.P. Fixer des vulcanisats thermoplastiques sur des surfaces
KR20070097294A (ko) 2003-11-14 2007-10-04 앳슈랜드 라이센싱 앤드 인텔렉츄얼 프라퍼티 엘엘씨 자가-광개시 다관능성 아크릴레이트와 지환족 에폭시화합물의 이중 경화 반응 생성물
DE10357159A1 (de) 2003-12-06 2005-07-07 Bayer Materialscience Ag Polymerdispersionen in Polyesterpolyolen
JP2007533829A (ja) 2004-04-21 2007-11-22 アシュランド・ライセンシング・アンド・インテレクチュアル・プロパティー・エルエルシー 光硬化性高光沢オーバープリントワニス組成物
US7317061B2 (en) * 2004-04-29 2008-01-08 Ashland Licensing And Intellectual Property Llc Self-photoinitiating water-dispersible acrylate ionomers and synthetic methods
DE602005008661D1 (de) 2004-05-03 2008-09-18 Rohm & Haas Michael-addierungs Zusammensetzungen
US8013050B2 (en) 2004-06-11 2011-09-06 Nuplex Resins B.V. Waterborne multistage polymer dispersion
DE102004031759A1 (de) 2004-07-01 2006-01-26 Degussa Ag Strahlungshärtbare, haftungsverbessernde Zusammensetzung aus ungesättigten, amorphen Polyestern und Reaktivverdünnern
WO2006016625A1 (fr) 2004-08-10 2006-02-16 Chugoku Marine Paints, Ltd. Composition de revetement anticorrosion a haute teneur en solides, composition de revetement anticorrosion a durcissement rapide a haute teneur en solides, procede de revetement de navire ou analogue, film anticorrosion a haute teneur en solides et film anticorrosion a haute teneur en solides a durcissement rapide obtenu, e
DE102004048775A1 (de) 2004-10-07 2006-04-13 Degussa Ag Hoch reaktive uretdiongruppenhaltige Polyurethanzusammensetzungen
EP1647588A3 (fr) 2004-10-13 2006-11-02 Rohm and Haas Company Compositions durcissables par réaction d'addition du type Michael activé à la surface
CN101103060A (zh) * 2005-01-11 2008-01-09 树脂核动力工业有限公司 聚脲化合物
WO2006074895A1 (fr) 2005-01-11 2006-07-20 Nuplex Resins B.V. Melanges destines a une modification rheologique
US7335690B2 (en) 2005-01-25 2008-02-26 3M Innovative Properties Company Crosslinkable hydrophilic materials from polymers having pendent Michael donor groups
CA2610961A1 (fr) 2005-06-20 2007-01-04 Dow Global Technologies Inc. Revement protecteur pour les vitres de fenetres
US8207268B2 (en) 2005-06-28 2012-06-26 Nuplex Resins B.V. Polyurea product as thixotropic rheology modifying agent
US8481668B2 (en) 2005-09-16 2013-07-09 Momentive Performance Materials Inc. Silane-containing adhesion promoter composition and sealants, adhesives and coatings containing same
US20070173602A1 (en) 2006-01-25 2007-07-26 Brinkman Larry F Encapsulated Michael addition catalyst
US8124688B2 (en) 2006-03-30 2012-02-28 Akzo Novel Coatings International B.V. Coating composition comprising a reactive diluent of malonate
US8829151B2 (en) 2006-03-30 2014-09-09 Akzo Nobel Coatings International B.V. Coating composition comprising a reactive diluent of polyunsaturated alcohol ester
US7906561B2 (en) 2006-12-04 2011-03-15 Ingenia Polymers, Inc. Cross-linked polyolefin foam
EP2072520A1 (fr) 2007-12-19 2009-06-24 Sika Technology AG Composition d'agents adhésifs comprenant du nitrile
JP5370712B2 (ja) 2008-02-21 2013-12-18 日東電工株式会社 酸性水溶性標的物質吸着ポリマー及びその製造方法
EP2110410A1 (fr) 2008-04-16 2009-10-21 Cytec Surface Specialties Austria GmbH Pâte de résine pour pâte de pigment universel
CN201213230Y (zh) * 2008-06-01 2009-03-25 刘孝伟 蓄电池单体充电平衡电路
EP2438123B1 (fr) 2009-06-02 2014-01-15 Akzo Nobel Coatings International B.V. Composition de revêtement aqueux comportant un polyester et un sel métallique d'un acide gras
JP5196003B2 (ja) 2009-11-05 2013-05-15 トヨタ自動車株式会社 内燃機関の空燃比気筒間インバランス判定装置
KR101212177B1 (ko) 2010-04-08 2012-12-13 한국화학연구원 다수의 수산기를 포함하는 마이클 수용체, 이로부터 유도된 마이클 부가 생성물
CN101869844B (zh) 2010-06-07 2013-04-17 湖南大学 一种固体强碱催化剂及其制备与应用
CN101879457B (zh) 2010-06-07 2013-04-10 湖南大学 一种纳米固体强碱催化剂及其制备与应用
EP2532722A1 (fr) 2011-06-08 2012-12-12 Sika Technology AG Composition d'agent adhésif aqueuse à base de résine époxy
WO2012175622A1 (fr) 2011-06-21 2012-12-27 Dsm Ip Assets B.V. Polymère et procédé et utilisation s'y rapportant
EP2764036B9 (fr) 2011-10-07 2017-04-05 Nuplex Resins B.V. Catalyseur de base latente et composition réticulable comprenant ledit catalyseur de base latente
EP2776959B1 (fr) 2011-11-11 2021-08-11 Robert Beckman Traitement stratégique personnalisé contre le cancer
US8883897B2 (en) 2012-05-25 2014-11-11 New Functional Polymers LLC Functional norbornanyl ester derivatives, polymers and process for preparing same
US9464187B2 (en) 2012-08-17 2016-10-11 Metabolix, Inc. Biobased modifiers for polyvinylchloride blends
US10017607B2 (en) 2013-04-08 2018-07-10 Allnex Netherlands B.V. Composition crosslinkable by real michael addition (RMA) reaction
EP3283586B1 (fr) 2015-04-17 2022-12-28 Allnex Netherlands B.V. Composition réticulable rma avec adhérence améliorée
AU2016250029B2 (en) 2015-04-17 2020-12-24 Allnex Netherlands B.V. RMA crosslinkable compositions and RMA crosslinkable resins for easy to clean coatings
JP6837991B2 (ja) 2015-04-17 2021-03-03 オールネックス・ネザーランズ・ビー．ブイ．Ａｌｌｎｅｘ Ｎｅｔｈｅｒｌａｎｄｓ Ｂ．Ｖ． フロアコーティング組成物
CA2983148C (fr) 2015-04-17 2023-05-09 Allnex Netherlands B.V. Procede de production d'une composition reticulable
PL3085748T3 (pl) 2015-04-20 2018-07-31 Jotun A/S Powłoki

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5959028A (en) * 1996-05-22 1999-09-28 Nippon Paint Co., Ltd. Curable resin composition for coating use
US20030023108A1 (en) * 2001-07-09 2003-01-30 Lonza Inc. In situ process for preparing quaternary ammonium bicarbonates and quaternary ammonium carbonates
WO2008157468A1 (fr) * 2007-06-18 2008-12-24 Ethicon, Inc. Dérivés de polymère de lactame
US8962725B2 (en) * 2010-04-07 2015-02-24 Nuplex Resins B.V. Crosslinkable composition crosslinkable with a latent base catalyst
US9181452B2 (en) * 2010-04-07 2015-11-10 Nuplex Resins B.V. Crosslinkable composition crosslinkable with a latent base catalyst
US9181453B2 (en) * 2010-04-07 2015-11-10 Nuplex Resins B.V. Crosslinkable composition crosslinkable with a latent base catalyst
US9534081B2 (en) * 2010-04-07 2017-01-03 Nuplex Resins B.V. Crosslinkable composition crosslinkable with a latent base catalyst
US9260626B2 (en) * 2011-10-07 2016-02-16 Nuplex Resins B.V. Crosslinkable composition
US9284423B2 (en) * 2011-10-07 2016-03-15 Nuplex Resins B.V. Crosslinkable composition crosslinkable by real michael addition (RMA) reaction

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Braun, D. et al., Polymer Synthesis: Theory and Practice, 4th ed., 2005, pp. 64-66. *

Cited By (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9284423B2 (en) * 2011-10-07 2016-03-15 Nuplex Resins B.V. Crosslinkable composition crosslinkable by real michael addition (RMA) reaction
US20140235785A1 (en) * 2011-10-07 2014-08-21 Nuplex Resins B.V. Crosslinkable composition crosslinkable by real michael addition (rma) reaction
US10647876B2 (en) 2011-10-07 2020-05-12 Allnex Netherlands B.V. Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition
US10604622B2 (en) 2013-04-08 2020-03-31 Allnex Netherlands B.V. Composition crosslinkable by Real Michael Addition (RMA) reaction
US10767074B2 (en) * 2015-04-17 2020-09-08 Allnex Netherlands B.V. Process for the manufacture of a crosslinkable composition
US11713402B2 (en) 2015-04-17 2023-08-01 Allnex Netherlands B.V. RMA crosslinkable compositions and RMA crosslinkable resins for easy to clean coatings
US11814536B2 (en) 2015-04-17 2023-11-14 Allnex Netherlands B.V. Floor coating compositions
US11674055B2 (en) 2015-04-17 2023-06-13 Allnex Netherlands B.V. RMA crosslinkable compositions and RMA crosslinkable resins for easy to clean coatings
US11674054B2 (en) 2015-04-17 2023-06-13 Allnex Netherlands B.V. Method for curing a RMA crosslinkable resin coating, RMA crosslinkable compositions and resins for use therein
US10759962B2 (en) 2015-04-17 2020-09-01 Allnex Netherlands B.V. Method for applying RMA crosslinkable coating on modified epoxy primer coating
US11414565B2 (en) 2015-04-17 2022-08-16 Allnex Netherlands B.V. Process for the manufacture of a crosslinkable composition
US10774238B2 (en) 2015-04-17 2020-09-15 Allnex Netherlands B.V. Method for curing a RMA crosslinkable resin coating, RMA crosslinkable compositions and resins for use therein
US11072724B2 (en) 2015-04-17 2021-07-27 Allnex Netherlands B.V. Adhesion promotor for real michael addition crosslinkable compositions
US10920101B2 (en) 2015-04-17 2021-02-16 Allnex Netherlands B.V. RMA crosslinkable compositions and RMA crosslinkable resins for easy to clean coatings
US10738196B2 (en) 2015-04-20 2020-08-11 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Coating systems, use thereof for coating components and components coated therewith for rail vehicles and aircrafts
US10876007B2 (en) 2015-04-20 2020-12-29 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Coating systems, use thereof for coating components and thus coated components for wind power plants
US10870763B2 (en) 2015-04-20 2020-12-22 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Coating systems, use thereof for coating components and thus coated components for agricultural and construction machines
DE102015105983A1 (de) * 2015-04-20 2016-10-20 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Verbesserte Beschichtungssysteme, deren Verwendung zur Beschichtung von Bauteilen sowie damit beschichtete Bauteile für Land- und Baumaschinen
DE102015105987A1 (de) * 2015-04-20 2016-10-20 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Verbesserte Beschichtungssysteme, deren Verwendung zur Beschichtung von Bauteilen sowie damit beschichtete Bauteile für Schienen- und Luftfahrzeuge
DE102015105979A1 (de) * 2015-04-20 2016-10-20 Mankiewicz Gebr. & Co. Gmbh & Co. Kg Verbesserte Beschichtungssysteme, deren Verwendung zur Beschichtung von Bauteilen sowie damit beschichtete Bauteile für Windkraftanlagen
US10799443B2 (en) 2016-06-30 2020-10-13 Elementis Specialties, Inc. Crosslinkable coating compositions formulated with dormant carbamate initiator
US11318082B2 (en) 2016-06-30 2022-05-03 Elements Specialties, Inc. Crosslinkable coating compositions formulated with dormant carbamate initiator
US11801214B2 (en) 2016-06-30 2023-10-31 Elementis Specialties, Inc. Crosslinkable coating compositions formulated with dormant carbamate initiator
US10624833B2 (en) 2016-06-30 2020-04-21 Elementis Specialties, Inc. Crosslinkable coating compositions formulated with dormant carbamate initiator
US10894886B2 (en) 2017-06-13 2021-01-19 Elementis Specialties, Inc. Coating system
CN113861402A (zh) * 2021-10-27 2021-12-31 江苏富琪森新材料有限公司 一种水性聚酯树脂及其制备方法和应用

Also Published As

Publication number Publication date
US9260626B2 (en) 2016-02-16
CN103998493B (zh) 2017-11-24
US20180155573A1 (en) 2018-06-07
ES2617624T3 (es) 2017-06-19
ES2639396T3 (es) 2017-10-26
SI2995636T1 (sl) 2017-10-30
JP2014530279A (ja) 2014-11-17
ES2629029T3 (es) 2017-08-07
PL2764035T3 (pl) 2017-03-31
PL2995636T3 (pl) 2017-12-29
CN103998493A (zh) 2014-08-20
US20160115344A1 (en) 2016-04-28
JP6194448B2 (ja) 2017-09-13
SI2764037T1 (sl) 2017-08-31
JP2017141435A (ja) 2017-08-17
SG11201401321WA (en) 2014-08-28
DK2764037T3 (en) 2017-07-10
EP2764035B1 (fr) 2016-12-07
EP2764035A1 (fr) 2014-08-13
US9587138B2 (en) 2017-03-07
US9834701B2 (en) 2017-12-05
CN105985724A (zh) 2016-10-05
EP2995636A1 (fr) 2016-03-16
DK2995636T3 (en) 2017-10-23
KR20140080496A (ko) 2014-06-30
WO2013050624A1 (fr) 2013-04-11
KR102131463B1 (ko) 2020-07-08
US20160060482A1 (en) 2016-03-03
CN103974999A (zh) 2014-08-06
US10647876B2 (en) 2020-05-12
EP2764037B1 (fr) 2017-03-22
WO2013050622A1 (fr) 2013-04-11
CN103974999B (zh) 2016-01-20
EP2995636B1 (fr) 2017-07-05
US20140228507A1 (en) 2014-08-14
PL2764037T3 (pl) 2017-10-31
EP2764037A1 (fr) 2014-08-13
EP2764035B9 (fr) 2017-03-01

Similar Documents

Publication Publication Date Title
US10647876B2 (en) Crosslinkable composition cross-linkable by real Michael addition reaction and resins for use in said composition
US9284423B2 (en) Crosslinkable composition crosslinkable by real michael addition (RMA) reaction
EP2764036B1 (fr) Catalyseur de base latente et composition réticulable comprenant ledit catalyseur de base latente
JP2016194052A (ja) 架橋ポリウレタンを調製するための周囲温度硬化性のイソシアネート不含組成物
US20220041802A1 (en) Rma crosslinkable polymer
TW201331273A (zh) 藉真實麥可加成反應可交聯之可交聯組成物以及用於該組成物之樹脂

Legal Events

Date Code Title Description
AS Assignment

Owner name: NUPLEX RESINS B.V., NETHERLANDS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BRINKHUIS, RICHARD HENDRIKUS GERRIT, MR;BUSER, ANTONIUS JOHANNES WILHELMUS, MR;ELFRINK, PETRUS JOHANNES MARIA DAVID, MR;AND OTHERS;SIGNING DATES FROM 20121106 TO 20121119;REEL/FRAME:032651/0684

AS Assignment

Owner name: ALLNEX NETHERLANDS B.V., NETHERLANDS

Free format text: CHANGE OF NAME;ASSIGNOR:NUPLEX RESINS B.V.;REEL/FRAME:042162/0719

Effective date: 20170301

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION