US20110033732A1 - Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet - Google Patents

Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet Download PDF

Info

Publication number
US20110033732A1
US20110033732A1 US12/854,472 US85447210A US2011033732A1 US 20110033732 A1 US20110033732 A1 US 20110033732A1 US 85447210 A US85447210 A US 85447210A US 2011033732 A1 US2011033732 A1 US 2011033732A1
Authority
US
United States
Prior art keywords
magnetic sheet
magnetic
curing agent
sheet composition
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/854,472
Other languages
English (en)
Inventor
Keisuke Aramaki
Yoshihisa Shinya
Katsuhiko Komuro
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dexerials Corp
Original Assignee
Sony Chemical and Information Device Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sony Chemical and Information Device Corp filed Critical Sony Chemical and Information Device Corp
Assigned to SONY CHEMICAL & INFORMATION DEVICE CORPORATION reassignment SONY CHEMICAL & INFORMATION DEVICE CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: KOMURO, KATSUHIKO, SHINYA, YOSHIHISA, ARAMAKI, KEISUKE
Publication of US20110033732A1 publication Critical patent/US20110033732A1/en
Priority to US13/447,432 priority Critical patent/US8668792B2/en
Assigned to DEXERIALS CORPORATION reassignment DEXERIALS CORPORATION CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: SONY CHEMICAL & INFORMATION DEVICE CORPORATION
Priority to US14/227,533 priority patent/US20140212578A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K9/00—Screening of apparatus or components against electric or magnetic fields
    • H05K9/0073—Shielding materials
    • H05K9/0081—Electromagnetic shielding materials, e.g. EMI, RFI shielding
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
    • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
    • C08G59/68—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used
    • C08G59/687—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used containing sulfur
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/36—Sulfur-, selenium-, or tellurium-containing compounds
    • C08K5/37—Thiols
    • C08K5/372—Sulfides, e.g. R-(S)x-R'
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/49—Phosphorus-containing compounds
    • C08K5/50—Phosphorus bound to carbon only
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/14—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys
    • H01F1/20—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of particles, e.g. powder
    • H01F1/22—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of particles, e.g. powder pressed, sintered, or bound together
    • H01F1/24—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of particles, e.g. powder pressed, sintered, or bound together the particles being insulated
    • H01F1/26—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of particles, e.g. powder pressed, sintered, or bound together the particles being insulated by macromolecular organic substances
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
    • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
    • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
    • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
    • H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
    • H01F1/34—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials non-metallic substances, e.g. ferrites
    • H01F1/36—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials non-metallic substances, e.g. ferrites in the form of particles
    • H01F1/37—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials non-metallic substances, e.g. ferrites in the form of particles in a bonding agent
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K9/00—Screening of apparatus or components against electric or magnetic fields
    • H05K9/0073—Shielding materials
    • H05K9/0075—Magnetic shielding materials
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/16—Nitrogen-containing compounds
    • C08K5/20—Carboxylic acid amides
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/16—Nitrogen-containing compounds
    • C08K5/34—Heterocyclic compounds having nitrogen in the ring
    • C08K5/3467—Heterocyclic compounds having nitrogen in the ring having more than two nitrogen atoms in the ring
    • C08K5/3477—Six-membered rings
    • C08K5/3492—Triazines
    • C08K5/34924—Triazines containing cyanurate groups; Tautomers thereof
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L63/00—Compositions of epoxy resins; Compositions of derivatives of epoxy resins
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T156/00—Adhesive bonding and miscellaneous chemical manufacture
    • Y10T156/10—Methods of surface bonding and/or assembly therefor
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T156/00—Adhesive bonding and miscellaneous chemical manufacture
    • Y10T156/10—Methods of surface bonding and/or assembly therefor
    • Y10T156/1002—Methods of surface bonding and/or assembly therefor with permanent bending or reshaping or surface deformation of self sustaining lamina
    • Y10T156/1043—Subsequent to assembly
    • Y10T156/1044—Subsequent to assembly of parallel stacked sheets only
    • Y10T156/1048—Subsequent to assembly of parallel stacked sheets only to form dished or receptacle-like product

Definitions

  • the present invention relates to a magnetic sheet, which is capable of suppressing undesirable electromagnetic waves emitted from an electronic equipment, and inhibiting electromagnetic disorders caused due to the interference of the undesirable electromagnetic waves, and also relates to a production method thereof which is efficient and low cost.
  • the magnetic sheets are used for depression of noise, or for RFID.
  • depression of noise along with rapid developments of electronic equipments, e.g. personal computers and mobile phones, such as down sizing and higher frequency, these electronic equipments suffer from a noise interference due to outer electromagnetic waves and interference of noises occurred within the electronic equipment.
  • various countermeasures have been taken for the noises.
  • a magnetic sheet (noise depressing sheet) is disposed adjacent to a noise emitting source or a noise receiving source.
  • the magnetic sheet is formed by adding alloy (magnetic powder) such as Fe—Si—Al to an epoxy resin, acrylic resin, or the like, and then being cured to form into a sheet by hot pressing.
  • alloy magnetic powder
  • the magnetic powder inhibits noise, and functions as a so-called noise depressor. The better the effect of inhibiting the noise of the magnetic sheet is, the larger an imaginary part ⁇ ′′ of the magnetic permeability of the magnetic sheet is.
  • Radio Frequency Identification RFID
  • various conductors such as a metal casing or metal parts are disposed adjacent to an antenna element for transmitting and receiving due to downsizing of the mobile information terminal.
  • a magnetic field usable for the transmission is largely attenuated because of the metal present adjacent to the antenna element, and as a result, a communication distance for RFID transmission in an electromagnetic induction system may be shortened, or transmission or receiving of a radio frequency may become difficult because a resonance frequency is shifted.
  • a magnetic sheet is placed between the antenna element and the conductor.
  • the magnetic sheet has a large real part ⁇ ′ of the magnetic permeability, and a small imaginary part ⁇ ′′ of the magnetic permeability.
  • a curing agent i.e. a crosslinking agent for curing a thermosetting organic resin is generally added to a magnetic sheet composition that is a material of the magnetic sheet.
  • the magnetic sheet is hardened by adding the curing agent to the magnetic sheet composition.
  • the thickness of the magnetic sheet undesirably changes depending on the fluctuations in the environment such as temperature and humidity.
  • the curing temperature is set high and the curing duration is set long. In this case, a large volume of water is consumed as the cooling duration becomes long according to the long and high temperature curing, and moreover the production efficiency decreases. If the curing temperature is set high and the curing duration is set short to solve the aforementioned problem, a problem occurs in the heat resistance of an insulating support.
  • a sulfonium-based cationic curing agent has been commonly used as the conventional curing agent, but the sulfonium-based cationic curing agent contains antimony that is toxic. Therefore, use of such curing agent gives an adverse influence to the environment. Furthermore, as in this antimony-containing sulfonium-based cationic curing agent, a counter ion has a Sb—F bond, which has weak bonding force, a F ⁇ 1 ion tends to be free. For this reason, in the case where the magnetic sheet containing the antimony-containing cationic curing agent is used around a wiring, the free F ⁇ 1 ion reacts with water to form hydrofluoric acid, which causes corrosion of the wiring.
  • JP-A Japanese Patent Application Laid-Open
  • JP-A No. 2007-95829 describes photocuring of a magnetic binder containing a photocuring cationic curing agent, and discloses an electromagnetic-wave-absorbing sheet having a concentration distribution of magnetic filler from the surface of the sheet towards the depth direction thereof.
  • the curing of this electromagnetic-wave-absorbing sheet is performed by a drum device.
  • an object of the present invention is to provide a magnetic sheet composition, which is a material of a magnetic sheet, capable of reducing unnecessary electromagnetic waves released from an electronic equipment, is capable of inhibiting electromagnetic disorders caused by an interference of unnecessary electromagnetic waves within an electronic equipment, prevents liberation of halogen ions to thereby prevent corrosion of wirings when it is used around the wirings, and does not give any adverse influence to the environment.
  • Another object of the present invention is to provide a method for producing a magnetic sheet using such magnetic sheet composition, and a magnetic sheet produced by such method for producing a magnetic sheet.
  • the inventors of the present invention have intensively studied to solve the problems, and come to the following insights. Namely, the inventors have found a magnetic sheet composition containing at least a binder which contains a thermosetting organic resin, a magnetic powder, and a curing agent which contains a sulfonium borate complex expressed by General Formula 1 can produce a magnetic sheet which realizes low-temperature-high-speed curing, prevents libration of halogen ions so as to prevent corrosion of wirings when it is used around the wirings, gives less environmental load.
  • R 1 is an aralkyl group
  • R 2 is a lower alkyl group
  • X is a halogen atom
  • n is an integer of 0 to 3.
  • the present invention has been made based upon the insight of the present inventors, and means for solving the aforementioned problems are as follows.
  • a magnetic sheet composition containing:
  • binder contains a thermosetting organic resin
  • curing agent contains a sulfonium borate complex expressed by General Formula 1:
  • R 1 is an aralkyl group
  • R 2 is a lower alkyl group
  • X is a halogen atom
  • n is an integer of 0 to 3.
  • the magnetic sheet composition according to ⁇ 1> contains the curing agent, which does not contain antimony, it will provide a less load to the environment. Moreover, as the bonding energy of X (halogen atom) and a phenyl group in the sulfonium borate complex expressed by General Formula 1, the bond between X (halogen atom) and the phenyl group is unlikely broken, and thus the isolation of X (halogen atom) ions is prevented. Therefore, the generation of acid such as hydrofluoric acid as a result of the reaction between free X (halogen atom) ions and water or the like is prevented. For this reason, corrosion of wirings can be prevented even when a magnetic sheet formed using the magnetic sheet composition is used around the wirings. Furthermore, a cationic curing magnetic sheet curable at low temperature and at high speed can be provided.
  • ⁇ 2> The magnetic sheet composition according to ⁇ 1>, wherein R 1 is a benzyl group, an o-methyl benzyl group, or a (1-naphthyl)methyl group.
  • R 1 is a benzyl group, an o-methyl benzyl group, or a (1-naphthyl)methyl group.
  • R 2 is a methyl group.
  • ⁇ 4> The magnetic sheet composition according to any one of ⁇ 1> to ⁇ 3>, wherein the sulfonium borate complex is contained in an amount of 2 parts by mass to 15 parts by mass relative to 106.1 parts by mass of the binder.
  • thermosetting the dried magnetic sheet composition thermosetting the dried magnetic sheet composition.
  • ⁇ 8> A magnetic sheet, obtained by the method as defined in any of ⁇ 6> or ⁇ 7>.
  • a magnetic sheet composition which is a material of a magnetic sheet, capable of reducing unnecessary electromagnetic waves released from an electronic equipment, is capable of inhibiting electromagnetic disorders caused by an interference of unnecessary electromagnetic waves within an electronic equipment, prevents libration of halogen ions to thereby prevent corrosion of wirings when it is used around the wirings, and does not give any adverse influence to the environment, as well as providing a method for producing a magnetic sheet using such magnetic sheet composition, and a magnetic sheet produced by such method for producing a magnetic sheet.
  • FIG. 1 is a 1 H-NMR chart of the sulfonium borate complex expressed by the formula 1a.
  • FIG. 2 is a 1 H-NMR chart of the sulfonium borate complex expressed by the formula 1b.
  • FIG. 3A is a photograph showing a cross-section of the magnetic sheet sample (Example 1) after the corrosion test.
  • FIG. 3B is a photograph showing a cross-section of the magnetic sheet sample (Comparative Example 8) after the corrosion test.
  • FIG. 4 is a diagram for explaining the method for measuring the transmission loss.
  • the magnetic sheet composition of the present invention contains at least a binder, a magnetic powder, and a curing agent, and may further contain other components, if necessary.
  • the curing agent is suitably selected depending on the intended purpose without any restriction, provided that it contains the sulfonium borate complex expressed by General Formula 1:
  • R 1 is an aralkyl group
  • R 2 is a lower alkyl group
  • X is a halogen atom
  • n is an integer of 0 to 3.
  • Examples of the aralkyl group expressed as R 1 include a benzyl group, an o-methyl benzyl group, a (1-naphthyl)methyl group, a pyridyl methyl group, and an anthracenyl methyl group.
  • the (1-naphthyl)methyl group is preferable as it provides the curing agent with excellent and fast curing ability, and it is readily available.
  • Examples of the lower alkyl group expressed as R 2 include a methyl group, an ethyl group, a propyl group, and a butyl group.
  • the methyl group is preferable as it provides the curing agent with excellent and fast curing ability, and it is readily available.
  • n is an integer of 0 to 3, where n denotes a number of hydroxyl group(s) contained in phenyl group(s) bonded to the sulfonium residue.
  • examples of such phenyl group include a 4-hydroxyl phenyl group, a 2-hydroxyl phenyl group, and a 3-hydroxyl phenyl group.
  • examples of such phenyl group include a 2,4-dihydroxyl phenyl group, a 2,6-dihydroxyl phenyl group, a 3,5-dihydroxyl phenyl group, and a 2,3-dihydroxyl phenyl group.
  • n 3
  • examples of such phenyl group include a 2,4,6-trihydroxy phenyl group, a 2,4,5-trihydroxy phenyl group, and a 2,3,4-trihydroxy phenyl group.
  • the 4-hydroxy phenyl group is preferable, as it provides the curing agent with excellent and fast curing ability, and it is readily available.
  • halogen atom expressed as X examples include a fluorine atom, chlorine atom, bromine atom, and iodine atom. Among them, the fluorine atom having high electron-withdrawing properties is preferable for improving the reactivity.
  • the sulfonium borate complex expressed by General Formula 1 can be produced in accordance with the following reaction formula.
  • R 1 is an aralkyl group
  • R 2 is a lower alkyl group
  • X is a halogen atom
  • n is an integer of 0 to 3.
  • the sulfonium antimonate complex (see JP-A No. 10-245378 for a synthesis method thereof) expressed by General Formula 2 is made dissolved in an organic solvent such as ethyl acetate, and a solution of sodium borate (see JP-A No. 10-310587 for a synthesis method thereof) expressed by General Formula 3 is mixed to the aforementioned solution in the equimolecular amount.
  • the obtained two-layered mixture is stirred at the temperature of 20° C. to 80° C. for 1 hour to 3 hours so as to allow the sulfonium antimonate complex expressed by General Formula 2 to react with the sodium borate expressed by General Formula 3 to thereby obtain a sulfonium borate complex expressed by General Formula 1.
  • the isolation of the sulfonium borate complex expressed by General Formula 1 can be performed in the following manner. Specifically, the organic solvent layer is separated and dried, and the organic solvent is evaporated to remove under the reduced pressure so that the specified substance can be obtained as the evaporated residue.
  • the sulfonium borate complex expressed by General Formula 1 can be used as a thermal cationic polymerization initiator for a common epoxy resin.
  • an epoxy resin composition in the form of a paste or film
  • containing 100 parts by mass of an epoxy resin and 0.1 parts by mass to 10 parts by mass of the sulfonium borate complex expressed by General Formula 1 as the thermal cationic polymerization initiator is heated at 50° C. to 150° C. so as to provide a cured product which is excellent in electrolytic corrosion resistance, and is cured at high speed and low temperature.
  • the binder is suitably selected depending on the intended purpose without any restriction.
  • examples thereof include acrylic rubber containing a thermosetting organic resin, which will be mentioned later.
  • the acrylic rubber preferably contains epoxy groups.
  • the epoxy groups are reacted with a curing agent, so as to improve reliability.
  • the acrylic rubber preferably further contains hydroxyl groups. The hydroxyl groups are contained in the acrylic rubber, so as to improve adhesion.
  • the mass average molecular mass of the acrylic rubber is 10,000 to 450,000 in terms of excellent coating ability.
  • the mass average molecular mass is less than 10,000, the viscosity of the magnetic sheet composition decreases, and it becomes hard to apply the magnetic sheet composition containing the magnetic powder having a large mass.
  • the mass average molecular mass is more than 450,000, the viscosity of the magnetic sheet composition becomes large, and it becomes hard to apply the magnetic sheet composition having a large viscosity.
  • the glass transition temperature of the acrylic rubber is preferably ⁇ 50° C. to +15° C.
  • the glass transition temperature When the glass transition temperature is lower than ⁇ 50° C., the reliability at a high temperature or in a high temperature and high humidity environment may become poor. When the glass transition temperature is higher than +15° C., the magnetic sheet tends to be hard.
  • one or more acrylic rubbers may be used in combination.
  • thermosetting organic resin examples include an epoxy resin.
  • an epoxy resin having a small molecular mass When an epoxy resin having a small molecular mass is added, the melt viscosity of the binder is further decreased upon compressing (forming) the magnetic sheet. Thus, the magnetic properties can be increased.
  • a polyfunctional epoxy resin by using a polyfunctional epoxy resin, the reliability of the magnetic sheet after curing can be further improved.
  • Examples of the epoxy resin include a cation-curing epoxy resin.
  • the epoxy resin may be used independently, or in combination.
  • the magnetic powder is suitably selected depending on the intended purpose without any restriction.
  • Examples of the shape of the magnetic powder include a flat, lump, fiber, sphere, and irregular shape. Of these, the flat shape is preferable as the magnetic powder of such shape can be easily orientated in a predetermined direction and high magnetic permeability can be attained.
  • Examples of the magnetic powder include soft magnetic metal, ferrite, and pure iron particles.
  • the soft magnetic metal examples include magnetic stainless steel (i.e., Fe—Cr—Al—Si alloy), Sendust (i.e., Fe—Si—Al alloy), permalloy (i.e., Fe—Ni alloy), silicon copper (i.e., Fe—Cu—Si alloy), Fe—Si alloy, Fe—Si—B(—Cu—Nb) alloy, Fe—Ni—Cr—Si alloy, Fe—Si—Cr alloy, Fe—Si—Al—Ni—Cr alloy, and amorphous metal.
  • magnetic stainless steel i.e., Fe—Cr—Al—Si alloy
  • Sendust i.e., Fe—Si—Al alloy
  • permalloy i.e., Fe—Ni alloy
  • silicon copper i.e., Fe—Cu—Si alloy
  • Fe—Si alloy Fe—Si—B(—Cu—Nb) alloy
  • Fe—Ni—Cr—Si alloy Fe—
  • the magnetic powder may be used independently, or in combination.
  • the amounts of the binder, magnetic powder, and curing agent are each suitably selected depending on the intended purpose without any restriction. It is preferred that the amount of the magnetic powder be 400 parts by mass to 1,400 parts by mass and the amount of the sulfonium borate complex as the curing agent be 2 parts by mass to 15 parts by mass, both relative to 106.1 parts by mass of the binder. Note that, the proportion of the magnetic powder in the magnetic sheet is preferably 60% by weight to 95% by weight.
  • the amount of the magnetic powder is less than 400 parts by mass relative to 106.1 parts by mass of the binder, excellent magnetic properties may not be obtained.
  • the amount thereof is more than 1,400 parts by mass relative to 106.1 parts by mass of the binder, it becomes hard to bind the magnetic powder with the binder. Consequently, the thickness variation of the magnetic sheet becomes large in a high temperature and high humidity environment, and the flame retardant may bleed out on the surface of the magnetic sheet.
  • the magnetic sheet becomes brittle, and the magnetic powder falls off (powder falling) not only from an edge face of the magnetic sheet but also from a surface of the magnetic sheet.
  • the other components are suitably selected from various known additives depending on the intended purpose without any restriction, as long as the effect of the present invention is not impaired.
  • a solvent may be added for the purpose of improving the coating ability (i.e. adjusting the viscosity) of a magnetic composition, which is prepared by adding the magnetic powder and the flame retardant to the binder.
  • ketenes such as acetone, methylethyl ketone, methylisobutyl ketone, and cyclohexanone
  • alcohols such as methanol, ethanol, propanol, butanol, isopropyl alcohol
  • esters such as methyl acetate, ethyl acetate, propyl acetate, butyl acetate, ethyl lactate, and ethyl glycol acetate
  • ethers such as diethylene glycol dimethyl ether, 2-ethoxy ethanol, tetrahydrofurane, and dioxane
  • aromatic hydrocarbon compounds such as benzene, toluene, and xylene
  • halogenated hydrocarbon compounds such as methylene chloride, ethylene chloride, carbon tetrachloride, chloroform, chlorobenzene.
  • additives such as a flame retardant (e.g. melamine cyanurate, and red phosphorous), a dispersant, stabilizer, lubricant, silane or titanate coupling agent, filler, plasticizer, and antioxidant may be added.
  • a flame retardant e.g. melamine cyanurate, and red phosphorous
  • a dispersant e.g. melamine cyanurate, and red phosphorous
  • the amounts of the other components are suitably selected depending on the amounts of the binder, the magnetic powder and the curing agent, without any restriction.
  • the presence of the carboxylic acid amide in the carboxylic acid amide-containing melamine cyanurate can be confirmed, for example, by pyrolysis gas chromatography analysis (Py-GC-MS).
  • the number average particle size of the carboxylic acid amide-containing melamine cyanurate is suitably selected depending on the intended purpose without any restriction. It is preferably 1 ⁇ m or less.
  • the number average particle size is more than 1 ⁇ m, the close alignment of the magnetic powder is blocked, and the magnetic properties of the magnetic sheet may be degraded, and the thickness variation of the magnetic sheet may become large at high temperature or in a high temperature and high humidity environment.
  • the number average particle size of the carboxylic acid amide-containing melamine cyanurate can be obtained, for example, from a particle size distribution thereof measured by laser diffraction.
  • the carboxylic acid amide-containing melamine cyanurate may be a commercially available product or arbitrarily prepared product.
  • Examples of the commercially available product include MC-5F (manufactured by SAKAI CHEMICAL INDUSTRY, CO., LTD.).
  • a method for producing the carboxylic acid amide-containing melamine cyanurate is suitably selected depending on the intended purpose without any restriction. For example, a method for treating a surface of the melamine cyanurate using fatty acid is preferably used.
  • a surface treatment method is suitably selected from known methods depending on the intended purpose without any restriction. For example, a method of mixing and stirring the melamine cyanurate and the fatty acid is used.
  • the fatty acid is suitably selected depending on the intended purpose without any restriction.
  • examples thereof include lauric acid, isostearic acid, stearic acid, palmitic acid, oleic acid, and linolenic acid. These may be used independently, or in combination.
  • lauric acid is preferred, in terms of high hydrophobicity and favorable dispersibility.
  • the flame retardant preferably contains red phosphorus, in addition to the silicon atom-containing melamine cyanurate and the carboxylic acid amide-containing melamine cyanurate. This is advantageous in terms of further improving the flame retardant of the magnetic sheet.
  • the red phosphorus is suitably selected depending on the intended purpose without any restriction, and may be a commercially available product or arbitrarily prepared product. It is preferred that the surface of the red phosphorus be coated for providing excellent humidity resistance, and favorable stability owing to no spontaneous combustion upon mixing.
  • red phosphorus whose surface is coated red phosphorus whose surface is treated with aluminum hydroxide is exemplified.
  • the amount of the red phosphorus is suitably selected depending on the intended purpose without any restriction. It is preferably 6 parts by mass to 19 parts by mass, relative to the 100 parts by mass of the binder.
  • the amount is less than 6 parts by mass, the obtainable effect of improving the flame resistance cannot be obtained.
  • the amount is more than 19 parts by mass, the total amount of the magnetic powder and the flame retardant increases relative to the binder. This makes difficult to keep binding the magnetic powder and the flame retardant together with the binder, the proportion of the magnetic powder in the magnetic sheet is decreased, causing decrease in the magnetic permeability.
  • the method for producing a magnetic sheet of the present invention is suitably selected from those known in the art depending on the intended purpose without any restriction, but the magnetic sheet is suitably produced by the following method.
  • the method for producing a magnetic sheet contains at least applying the magnetic sheet composition on a substrate, drying the magnetic sheet composition applied on the substrate, and thermosetting the dried magnetic sheet composition, and may further contain other steps, if necessary.
  • the magnetic sheet composition contains at least a binder, a magnetic powder, and a curing agent, and may further contain other components.
  • the binder contains a thermosetting organic resin
  • the curing agent contains a sulfonium borate complex expressed by General Formula 1.
  • binder the details of the binder, magnetic powder, curing agent, and other components are as mentioned above.
  • the substrate is suitably selected depending on the intended purpose without any restriction, but it is preferably a polyester film a surface of which is lubrication processed (a release PET) as the formed magnetic layer can be easily peeled from the substrate.
  • a method for coating is suitably selected depending on the intended purpose without any restriction.
  • examples thereof include spin coating, dip coating, kneader coating, curtain coating, blade coating, and doctor blade coating.
  • the blade coating, and the doctor blade coating are preferable, in terms of excellent coating efficiency.
  • a method for drying is suitably selected depending on the intended purpose without any restriction.
  • Examples thereof include methods using a dry oven, a drier, a hot press, and a heating automation.
  • the method using the dry oven is particularly preferable as the process thereof is easy, and it is advantageous in terms of the cost for the facilities.
  • thermosetting (forming) the magnetic sheet is suitably selected depending on the intended purpose without any restriction.
  • the magnetic sheet can be formed by hot pressing.
  • a method of hot pressing is suitably selected depending on the intended purpose without any restriction.
  • both sides of a layer, which is formed by applying the magnetic composition onto the substrate are sandwiched with press plates respectively via buffer materials, and heated and pressed.
  • the conditions for the hot pressing are suitably adjusted depending on the intended purpose without any restriction.
  • the temperature is preferably 80° C. to 190° C.
  • the pressure is preferably 5 MPa to 20 MPa
  • the duration is preferably 1 minute to 20 minutes.
  • the structure, thickness, and material of the buffer material are suitably selected depending on the indented purpose without any restriction.
  • the buffer material may be a commercially available product or arbitrarily prepared product.
  • the commercially available product include a high quality paper (product name: OK Prince High Quality 70, manufacturer: Oji Paper Co., Ltd., Bekk smoothness: 6.2 sec/mL), a cushioned paper (product name: TF190, manufacturer: THE TOYO FIBRE CO., LTD., Bekk smoothness: 1.7 sec/mL), nylon mesh (product name: N-NO. 110S, manufacturer: TOKYO SCREEN CO., LTD., Bekk smoothness: less than 0.1 sec/mL), cotton cloth (product name: Kanakin No.
  • Bekk smoothness expresses the time required for a certain amount of air to pass through the surface having some irregularities of a sheet member such as paper and a cloth.
  • Bekk smoothness is measured, for example, by Bekk Smoothness Tester (manufactured by TESTER SANGYO CO., LTD.).
  • the magnetic sheet composition is applied onto the substrate, the applied magnetic sheet composition on the substrate is dried, and the dried magnetic sheet composition is thermoset, to thereby produce a magnetic sheet.
  • the magnetic sheet is obtained in such a state that the magnetic sheet is laminated on the substrate (release PET), but the magnetic sheet can be peeled from the substrate and used.
  • steps are suitably selected depending on the intended purpose without any restriction. Examples thereof include a pattern-transferring step.
  • the pattern transferring step is stacking a convex-concave forming layer and a pattern transferring material on a surface of the magnetic layer, which has been formed by thermosetting the magnetic sheet composition, in this order, and hot pressing the stacked layers so as to bond the convex-concave forming layer with the magnetic layer to form a stacked body, as well as to transfer a surface configuration of the pattern transferring material to a surface of the laminate of the convex-concave forming layer and the magnetic layer.
  • the structure, thickness, and material of the convex-concave forming layer are suitably selected depending on the intended purpose without any restriction. The details thereof are as mentioned earlier.
  • the surface configuration of the convex-concave forming layer is not particularly limited, and one surface thereof may be surface-treated, or no surface treatment may be performed.
  • a surface treatment a matte processing, lubrication processing without using a silicone resin and the like are preferable.
  • a lubricity of the surface is improved compared to the surface without any surface treatment.
  • silicone resin is not used, silicone oligomers do not bleed out under the condition of high temperature and/or high humidity, and thus it is suitably used inside of an electronic equipment.
  • the matte processing is suitably selected depending on the intended purpose without any restriction. Examples thereof include a sand matte processing, chemical matte processing, surface emboss processing and the like. By these processing, the convex-concave pattern is formed on the convex-concave forming layer and as a result, a lubricity thereof is improved.
  • the convex-concave forming layer preferably has Bekk smoothness of 200 sec/mL or less before hot pressing.
  • the structure, thickness and material of the pattern-transferring material are suitably selected depending on the intended purpose without any restriction. For example, those having a convex-concave pattern on the surface thereof and excellent air permeability are preferable.
  • the convex-concave pattern is formed on the surface of the convex-concave forming layer, and as a result, Bekk smoothness of the convex-concave forming layer is lowered and lubricity of the convex-concave forming layer is improved.
  • the surface irregularities of the pattern transferring material can be evaluated by the value of Bekk smoothness.
  • the structure of the pattern transferring material may be a monolayered structure or laminate structure.
  • the thickness of the pattern transferring material is preferably 25 ⁇ m to 200 ⁇ m.
  • the thickness thereof When the thickness thereof is less than 25 ⁇ m, it may not be able to attain a magnetic sheet of low Bekk smoothness. When the thickness thereof is more than 200 ⁇ m, heat does not easily transfer to the magnetic layer at the time of hot pressing, and thus the reliability may be lowered.
  • the material of the pattern transferring material is, for example, paper, synthetic fibers, or natural fibers.
  • the pattern-transferring material may be a commercially available product or arbitrarily prepared product.
  • the commercially available product include a high quality paper (product name: OK Prince High Quality 70, manufacturer: Oji Paper Co., Ltd., Bekk smoothness: 6.2 sec/mL), a cushioned paper (product name: TF190, manufacturer: THE TOYO FIBER CO., LTD., Bekk smoothness: 1.7 sec/mL), nylon mesh (product name: N-No. 110S, manufacturer: TOKYO SCREEN CO., LTD., Bekk smoothness: less than 0.1 sec/mL), cotton cloth (product name: Kanakin No.
  • the method for an arrangement of stacked layers is suitably selected depending on the purpose without any restriction, provided that the convex-concave forming layer and the pattern transferring material are stacked on at least one surface of the magnetic layer in this order. It is preferred that a release layer and the pattern transferring material are further stacked on the other surface of the magnetic layer in this order. As the pattern transferring material are stacked on the other surface of the magnetic layer with the release layer being placed in between, the other surface of the magnetic layer is protected and prevented from closely attaching to the pattern transferring material at the time of hot pressing mentioned later, and the pattern transferring layer is easily peeled from the magnetic layer along with the release layer after hot pressing.
  • the surface configuration of the pattern transferring material is transfer to the surface of the magnetic layer which is present at the side of the releasing layer, and at this time, air bubbles present in the resin composition of the magnetic layer are easily released, and thus the reliability of the obtained magnetic sheet is improved.
  • the pattern transferring material is not used at the side of the release layer, magnetic permeability of the magnetic sheet is improved.
  • the release layer is suitably selected depending on the intended purpose without any restriction, provided that it functions to prevent the close attachment between the other surface of the magnetic layer and the pattern transferring material at the time of hot pressing.
  • the release layer is preferably a polyester film a surface of which is lubrication processed (lubrication processed PET), as it is easily peeled from the magnetic layer after hot pressing.
  • the method for hot pressing is suitably selected depending on the intended purpose without any restriction. For example, it is performed by sandwiching stacked layers of the magnetic layer, the convex-concave forming layer and the pattern transferring layer with a laminator or press the stacked layers from the both sides thereof, then heating and pressing the same.
  • the surface configuration (convex-concave pattern) of the pattern transferring material is transferred to surfaces of the convex-concave forming layer and magnetic layer, and also the convex-concave forming layer and the magnetic layer are directly bonded to each other without using an adhesive or the like.
  • the conditions for hot pressing are suitably adjusted depending on the intended purpose without any restriction.
  • the temperature is preferably 80° C. to 190° C.
  • the pressure is preferably 5 MPa to 20 MPa
  • the duration is preferably 1 minute to 20 minutes.
  • Bekk smoothness of the convex-concave forming layer after hot pressing is preferably 70 sec/mL or less, more preferably 1 sec/mL to 60 sec/mL.
  • the surface lubricity of the convex-concave forming layer may be insufficient, and as a result, the magnetic sheet and a member which is brought into contact with the magnetic sheet may be adhered.
  • the surface configuration of the pattern transferring material is transferred to the surfaces of the convex-concave forming layer and magnetic layer at the same time as the convex-concave forming layer and the magnetic layer are bonded to each other.
  • a magnetic sheet containing the magnetic layer and the convex-concave forming layer is obtained.
  • the magnetic sheet obtained in the aforementioned manner has the convex-concave forming layer a surface of which has the surface configuration transferred from the surface configuration (convex-concave surface pattern) of the pattern transferring material and is roughened, and thus Bekk smoothness thereof is low and the lubricity thereof is excellent.
  • a surface configuration of the pattern transferring material is transferred to surfaces of the convex-concave forming layer and magnetic layer by hot pressing, and thus a surface of the convex-concave forming layer is roughened, Bekk smoothness thereof is reduced, and the lubricity is improved.
  • Bekk smoothness of the convex-concave forming layer can be suitably controlled in the desirable range regardless of the original value of Bekk smoothness of the convex-concave forming layer, and thus the selection of the material used for the convex-concave forming layer is widened. In addition, the control of Bekk smoothness can be performed easily.
  • the magnetic sheet is suitably selected depending on the intended purpose without any restriction, provided that it is produced by the method for producing a magnetic sheet mentioned earlier.
  • the method for using the magnetic sheet of the present invention is suitably selected depending on the intended purpose without any restriction.
  • the magnetic sheet may be cut into a desirable size, and disposed in an electronic equipment so that the magnetic sheet is placed adjacent to a noise source of the electronic equipment.
  • the magnetic sheet of the present invention can be suitably applied for electromagnetic noise depressors, electromagnetic wave absorbers, magnetic shielding, electronic equipments having IC tag functions such as Radio Frequency Identification (RFID), and non-contact IC cards.
  • RFID Radio Frequency Identification
  • the magnetic sheet can be suitably used for RFID functioned mobile phones.
  • Sulfonium anthimonate complexes respectively expressed by the formula 1d, 1e and 1f (see JP-A No. 10-245378 for synthesis methods thereof) were each made dissolved in ethyl acetate to prepare a 10% by mass ethyl acetate solution of each complex.
  • a 10% solution of sodium borate expressed by the formula 3 was prepared separately to above.
  • the 10% by mass solution of the sodium borate expressed by the formula 3 was mixed in the 10% by mass ethyl acetate solution of the complex in an equimolecular amount at room temperature, and the mixture was stirred for 30 minutes. Thereafter, the ethyl acetate layer was separated from the reacted mixed solution, and dried. The ethyl acetate was then removed under the reduced pressure.
  • the sulfonium borate complex (4-hydroxyphenyl-methyl-1-naphthylmethyl sulfonium tetrakis(pentafluorophenyl) borate) expressed by the formula 1a
  • the sulfornium borate complex (4-hydroxyphenyl-methyl-(2-methylbenzyl)sulfonium tetrakis(pentafluorophenyl) borate) expressed by the formula 1b
  • the sulfonium borate complex (4-hydroxyphenyl-methyl-benzylsulfonium tetrakis(pentafluorophenyl)borate) expressed by the formula 1c were each obtained as an evaporated residue.
  • the sulfonium borate complexes 1a and 1b were each subjected to mass spectrometry (measuring device: AQUITY HPLC System, manufacturer: Nihon Waters K.K.), an elemental analysis (measuring device: PHOENIX, manufacturer: EDAX Inc.), an IR analysis (measuring device: 7000e FT-IR, manufacturer: Varian Technologies Japan Limited), and 1 H-NMR analysis (measuring device: MERCURY PLUS, manufacturer: Varian Technologies Japan Limited). As a result, these complexes found to be targeted compounds.
  • the sulfonium borate complexes 1a to 1c and sulfonium antimonate complexes 1d to 1f were each subjected to the measurement of the fluorine-ion concentration under the same temperature condition to that of thermal cationic polymerization in the manner described below. Moreover, a thermal cationic polymerization composition was prepared using each complex, and the prepared composition was subjected to a differential thermal analysis (DSC) at the temperature rising rate of 10° C./min.
  • DSC differential thermal analysis
  • a fluid epoxy resin (Epikote 828, manufactured by Japan Epoxy Resins Co., Ltd.) the complexes of Examples 1 and 2, and Comparative Examples 1 to 4 were each mixed to prepare a thermal cationic polymerization composition.
  • the complexes of Examples 1 and 2 were each mixed in an amount of 1 part by mass
  • the complex of Comparative Example 1 was mixed in an amount of 3 parts by mass
  • the complexes of Comparative Examples 2 to 4 were each mixed in an amount of 5 parts by mass.
  • Each thermal cationic polymerization composition was subjected to a differential thermal analysis (heating onset temperature, peak temperature, calorific value) by means of a thermal analysis equipment (DSC 5100, manufactured by Seiko Instruments Inc.). The results are shown in Table 1.
  • the heating onset temperature is temperature at which protons are generated from the complex to initiate cationic polymerization.
  • the low-temperature curing ability is more enhanced as the heat onset temperature is lower.
  • the storage stability tends to decrease. Therefore, it is preferably 80° C. to 110° C.
  • the thermal peak temperature is excessively low, the storage stability reduced. When it is excessively high, curing failures tend to occur. Therefore, the thermal peak temperature is preferably 100° C. to 140° C.
  • the calorific value is corresponded to heat of the reaction, and is preferably 200 J/g or larger as curing failures tend to occur with the excessively small calorific value.
  • the obtained magnetic sheet composition was applied onto a polyester film a surface of which had been lubricated processed (a release PET) (38GS manufactured by Lintec Corporation, thickness of 38 ⁇ m) as a substrate using a bar coater (i.e., the magnetic sheet composition was applied on the surface which had been lubricated processed), to form a layer having a thickness of 100 ⁇ m to 200 ⁇ m.
  • a release PET 38GS manufactured by Lintec Corporation, thickness of 38 ⁇ m
  • the applied coat was dried at room temperature for 10 minutes, and then dried at 60° C. for 10 minutes.
  • the release PET on the lubrication-processed surface of which a layer formed of the magnetic sheet composition (a magnetic layer) had been formed was cut into the size of 250 mm ⁇ 250 mm, to thereby obtain 4 pieces of the release PET on the lubrication-processed surface of which the magnetic layer had been formed in the size of 250 mm ⁇ 250 mm.
  • the release PET was removed from the magnetic layer, to thereby obtain two pieces of the 250 mm ⁇ 250 mm magnetic layer.
  • the two magnetic layers (each in the size of 250 mm ⁇ 250 mm) were placed and stacked on the magnetic layer side of the release PET on the lubrication-processed surface of which the magnetic sheet in the size of 250 mm ⁇ 250 mm had been formed.
  • one piece of the release PET on the lubrication-processed surface of which the magnetic layer in the size of 250 mm ⁇ 250 mm had been formed was placed and stacked (so that the magnetic layers were facing each other), to thereby obtain a release PET in which four magnetic layers were stacked and both surfaces of the stacked layers were both held with a pair of the release PETs (i.e. the lubrication-processed surfaces of the two release PET were arranged so as to be in contact with the magnetic layers).
  • the two release PET were removed from the magnetic layer formed by curing the laminated four magnetic layers, to thereby obtain a magnetic sheet.
  • Magnetic sheets of Examples 2 to 7 were each prepared in the same manner as in Example 1, provided that at least one of the formulated amount of the cationic curing agent A, the press retaining temperature, and the press retaining duration were changed as presented in Table 2.
  • a magnetic sheet of Example 8 was prepared in the same manner as in Example 1, provided that as the curing agent, a cationic curing agent C (4-hydroxyphenyl-methyl-benzyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1c)) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthylmethyl sulfonium tetrakis(pentafluorophenyl) borate; the formula (1a)).
  • a cationic curing agent C 4-hydroxyphenyl-methyl-benzyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1c)
  • Magnetic sheets of Examples 9 and 10 were each prepared in the same manner as in Example 8, provided that at least one of the formulated amount of the cationic curing agent C, the press-retaining temperature, and the press-duration were changed as presented in Table 3.
  • Example 11 A magnetic sheet of Example 11 was prepared in the same manner as in Example 2, provided that as the curing agent, the cationic curing agent B (4-hydroxyphenyl-methyl-(2-methylbenzyl) sulfonium tetrakis(pentafluorophenyl) borate; the formula (1b)) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1a)).
  • the cationic curing agent B (4-hydroxyphenyl-methyl-(2-methylbenzyl) sulfonium tetrakis(pentafluorophenyl) borate; the formula (1b)
  • the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl)borate; the
  • a magnetic sheet of Example 12 was prepared in the same manner as in Example 2, provided that as the magnetic powder, a flat magnetic powder (SP-1, manufactured by MATE CO., LTD.) was used instead of the flat magnetic powder (JEM-S, manufactured by Mitsubishi Materials Corporation).
  • SP-1 manufactured by MATE CO., LTD.
  • JEM-S manufactured by Mitsubishi Materials Corporation
  • a magnetic sheet of Example 13 was prepared in the same manner as in Example 1, provided that as the magnetic powder, a flat magnetic powder (SP-1, manufactured by MATE CO., LTD.) was used instead of the flat magnetic powder (JEM-S, manufactured by Mitsubishi Materials Corporation).
  • SP-1 manufactured by MATE CO., LTD.
  • JEM-S manufactured by Mitsubishi Materials Corporation
  • a magnetic sheet of Example 14 was prepared in the same manner as in Example 1, provided that as the magnetic powder, 900 parts by mass of a flat magnetic powder (EMS10, manufactured by Mitsubishi Materials Corporation) was used instead of 550 parts by mass of the flat magnetic powder (JEM-S, manufactured by Mitsubishi Materials Corporation), and the formulated amount of the cationic curing agent A was changed from 6.9 parts by mass to 8 parts by mass.
  • EMS10 flat magnetic powder
  • JEM-S manufactured by Mitsubishi Materials Corporation
  • a magnetic sheet of Example 15 was prepared in the same manner as in Example 1, provided that the formulated amount of the flat magnetic powder (JEM-S, manufactured by Mitsubishi Materials Corporation) was changed from 550 parts by mass to 1,600 parts by mass, the formulated amount of the cationic curing agent A was changed from 6.9 parts by mass to 10 parts by mass, and a convex-concave forming layer and a pattern-transferring material were stacked in this order on one plane of the magnetic layer, which had bee formed by thermosetting the magnetic sheet composition, followed by hot-pressing to transfer the pattern.
  • the formulated amount of the flat magnetic powder JEM-S, manufactured by Mitsubishi Materials Corporation
  • the formulated amount of the cationic curing agent A was changed from 6.9 parts by mass to 10 parts by mass
  • a convex-concave forming layer and a pattern-transferring material were stacked in this order on one plane of the magnetic layer, which had bee formed by thermosetting the magnetic sheet composition, followed by hot-pressing to transfer the pattern.
  • a matte-surface treated polyester film (matte-processed PET) (product name: LUMIRRORX44-#25, manufacturer: Toray Industries, Inc., thickness: 25 ⁇ m, Bekk smoothness: 101.8 sec/mL) serving as a convex-concave forming layer, and a high quality paper (product name: OK Prince High Quality 70, manufacturer: Oji Paper Co., Ltd., thickness: 100 ⁇ m, Bekk smoothness: 6.2 sec/mL) serving as a pattern transferring material were stacked on a surface of the magnetic layer so that the convex-concave forming layer and the pattern transferring material were stacked in this order from the side of the magnetic layer.
  • a high quality paper product name: OK Prince High Quality 70, manufacturer: Oji Paper Co., Ltd., thickness: 100 ⁇ m, Bekk smoothness: 6.2 sec/mL
  • a surface-lubrication-processed polyester film manufactured by Lintec Corporation serving as a release layer
  • a high quality paper product name: OK Prince High Quality 70, manufacturer: Oji Paper Co., Ltd., thickness: 100 ⁇ m, Bekk smoothness: 6.2 sec/mL
  • the stacked body was subjected to hot pressing using a vacuum press (manufactured by KITAGAWA SEIKI CO., LTD.) at temperature of 170° C., and pressure of 9 MPa, for 10 minutes, by sandwiching the stacked body from both sides thereof with press plates to form the magnetic layer having a thickness of 80 ⁇ m.
  • a vacuum press manufactured by KITAGAWA SEIKI CO., LTD.
  • the convex-concave forming layer and the magnetic layer were bonded, and at the same time, the surface configuration of the pattern transferring material was transferred to a surface of the laminate of the convex-concave forming layer and the magnetic layer.
  • the processes mentioned above were corresponded to the pattern transferring step.
  • the laminate which had been hot-pressed, was cut into a sample size of 250 mm ⁇ 250 mm.
  • the pattern transferring material and the release layer were released from the convex-concave forming layer and the magnetic layer to thereby obtain a magnetic sheet having a thickness of 105 ⁇ m.
  • the Bekk smoothness thereof after the hot-pressing was 26.3 sec./mL.
  • a magnetic sheet of Example 16 was prepared in the same manner as in Example 1, provided that the formulated amount of the flat magnetic powder (JEM-S, manufactured by Mitsubishi Materials Corporation) as the magnetic powder was changed from 550 parts by mass to 1,200 parts by mass, the formulated amount of the cationic curing agent A was changed from 6.9 parts by mass to 10 parts by mass, and 10 parts by mass of red phosphorous (manufactured by Rinkagaku Kogyo Co., Ltd.) and 90 parts by mass of carboxylic acid amide-containing melamine cyanurate (MC-5F, manufactured by Sakai Chemical Industry Co., Ltd.) were further added.
  • the formulated amount of the flat magnetic powder JEM-S, manufactured by Mitsubishi Materials Corporation
  • the formulated amount of the cationic curing agent A was changed from 6.9 parts by mass to 10 parts by mass
  • 10 parts by mass of red phosphorous manufactured by Rinkagaku Kogyo Co., Ltd.
  • M-5F carboxylic acid amide-containing melamine cyanurate
  • a magnetic sheet of Example 17 was prepared in the same manner as in Example 1, provided that as the magnetic powder, 900 parts by mass of a flat magnetic powder (EMS 10, manufactured by Mitsubishi Materials Corporation) was used instead of 550 parts by mass of the flat magnetic powder (JEM-S, manufactured by Mitsubishi Materials Corporation), the formulated amount of the cationic curing agent A was changed from 6.9 parts by mass to 8 parts by mass, and 10 parts by mass of red phosphorous (manufactured by Rinkagaku Kogyo Co., Ltd.) and 90 parts by mass of carboxylic acid amide-containing melamine cyanurate (MC-5F, manufactured by Sakai Chemical Industry Co., Ltd.) were further added.
  • EMS 10 manufactured by Mitsubishi Materials Corporation
  • JEM-S manufactured by Mitsubishi Materials Corporation
  • a magnetic sheet of Comparative Example 1 was prepared in the same manner as in Example 1, provided that as the curing agent, an imidazole-based curing agent (HX3748, manufactured by Asahi Kasei Chemicals Corporation) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1a)).
  • an imidazole-based curing agent HX3748, manufactured by Asahi Kasei Chemicals Corporation
  • a magnetic sheet of Comparative Example 2 was prepared in the same manner as in Example 2, provided that as the curing agent, an imidazole-based curing agent (HX3748, manufactured by Asahi Kasei Chemicals Corporation) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1a)).
  • an imidazole-based curing agent HX3748, manufactured by Asahi Kasei Chemicals Corporation
  • a magnetic sheet of Comparative Example 3 was prepared in the same manner as in Example 3, provided that as the curing agent, an imidazole-based curing agent (HX3748, manufactured by Asahi Kasei Chemicals Corporation) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl) borate; the formula (1a)).
  • an imidazole-based curing agent HX3748, manufactured by Asahi Kasei Chemicals Corporation
  • a magnetic sheet of Comparative Example 4 was prepared in the same manner as in Example 4, provided that as the curing agent, an imidazole-based curing agent (HX3748, manufactured by Asahi Kasei Chemicals Corporation) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl) borate; the formula (1a)).
  • an imidazole-based curing agent HX3748, manufactured by Asahi Kasei Chemicals Corporation
  • a magnetic sheet of Comparative Example 5 was prepared in the same manner as in Example 5, provided that as the curing agent, an imidazole-based curing agent (HX3748, manufactured by Asahi Kasei Chemicals Corporation) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl) borate; the formula (1a)).
  • an imidazole-based curing agent HX3748, manufactured by Asahi Kasei Chemicals Corporation
  • a magnetic sheet of Comparative Example 6 was prepared in the same manner as in Example 6, provided that as the curing agent, an imidazole-based curing agent (HX3748, manufactured by Asahi Kasei Chemicals Corporation) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl) borate; the formula (1a)).
  • an imidazole-based curing agent HX3748, manufactured by Asahi Kasei Chemicals Corporation
  • a magnetic sheet of Comparative Example 7 was prepared in the same manner as in Comparative Example 1, provided that the press-retaining duration and the press duration were both changed as presented in Table 6.
  • a magnetic sheet of Comparative Example 8 was prepared in the same manner as in Example 1, provided that as the curing agent, an antimony-based cationic curing agent (San-Aid SI-60L, manufactured by Sanshin Chemical Industry Co., Ltd.) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1a).
  • an antimony-based cationic curing agent (San-Aid SI-60L, manufactured by Sanshin Chemical Industry Co., Ltd.) was used instead of the cationic curing agent A (4-hydroxyphenyl-methyl-1-naphthyl sulfonium tetrakis(pentafluorophenyl)borate; the formula (1a).
  • a ring sample which had been cut out so as to have an outer diameter of 7.05 mm, and an inner diameter of 2.945 mm, was prepared.
  • a lead-wire was then wound around the ring sample 5 times, and then it was soldered to a terminal.
  • the length between the bottom of the terminal and the bottom of the ring sample was set 20 mm.
  • the inductance and resistance thereof at 1 MHz were measured using an impedance analyzer (4294A, manufactured by Agilent Technologies, Inc.), and the obtained values were converted into magnetic permeability.
  • ⁇ ′ denotes a real part of complex magnetic permeability.
  • ⁇ ′ are different depending on the intended use of a magnetic sheet. For example, in the case where it is used for improving a correspondence of a RFID device, it is preferred that the value of is high and the value of ⁇ ′′ (an imaginary part of complex magnetic permeability) is low at the frequency of 20 MHz or lower.
  • the magnetic sheet of the present invention is usable in the frequency range of KHz to GHz.
  • a thickness of the magnetic sheet was measured. Then, the magnetic sheet was placed in an oven, and heated at 85° C., and 60% RH for 96 hours. After taking the magnetic sheet out from the oven, the thickness of the magnetic sheet was measured again, and a rate of the change in the thickness of the magnetic sheet before and after heating was measured.
  • a magnetic sheet sample (about 0.2 g) of Example 1 and a magnetic sheet sample (about 0.2 g) of Comparative Example 8 were each separately added to a PP container having 10 mL of ultrapure water. The container was then placed in an oven set at 100° C., and was left there for 10 hours. Thereafter, 10 mL of an extract was taken out from the container, and was subjected to the measurement of a fluorine (F ⁇ 1 ) ion concentration ( ⁇ g/mL). Based on the obtained fluorine (F ⁇ 1 ) ion concentration ( ⁇ g/mL) of the extract, a fluorine (F ⁇ 1 ) ion concentration ( ⁇ g/g) per g of the magnetic sheet sample was calculated using the following formula (1). The results are shown in Table 7.
  • a magnetic sheet sample (about 0.2 g) of Example 1 and a magnetic sheet sample (about 0.2 g) of Comparative Example 8 were each separately added to a plastic container (DESCUP) containing 50 mL of tap water. Then, the container was placed in an oven set at 85° C. and 85% RH, and was left there for 16 hours. Thereafter, the magnetic sheet sample was taken out from the plastic container containing 50 mL of tap water, and the cross-sectional plane of the magnetic sheet was observed under a microscope. The results are shown in FIGS. 3A and 3B , and Table 7.
  • Magnetic sheet samples of Example 16 and Example 17 were both subjected to the combustion test in the following manner.
  • the combustion test a UL94V test (a combustion test for a plastic material of machinery parts) was carried out.
  • the UL94V test was a method for evaluating flame resistance based on the afterflame time, after placing a certain size of a sample directly in a flame of a burner for 10 seconds with the sample held vertically. The results were evaluated based on the following criteria.
  • V-0 The afterflame time of each sample was 10 seconds or shorter, and the total afterflame time of 5 samples was 50 seconds or shorter.
  • V-1 The afterflame time of each sample was 30 seconds or shorter but longer than 10 seconds, and the total afterflame time of 5 samples was 250 seconds or shorter but longer than 50 seconds.
  • V-2 The combustion time (afterflame time?) was the same as V-1, but there were flame-droppings.
  • afterflame time means a length of time showing how long flame combustion of the test sample continues after an ignition source is moved away.
  • Magnetic sheets of Examples 16 and 17 were each subjected to the measurement of LOSS properties (transmission loss) in the following manner.
  • a microstripline having an impedance Z of 50 ⁇ was used for measurement of transmission loss.
  • the use of the microstripline line was a commonly used method for measuring transmission loss of adjacent noise, because of its structure suitable for mounting a surface-mounting component and production easiness.
  • the shape of the microstripline 2 used is shown in FIG. 4 .
  • the transmission loss was measured in such a manner that a linear conductor path was provided on a surface of an insulator substrate, and a magnetic sheet was placed on the conductor path for measurement. Both ends of the conductor path were connected to a network analyzer 1.
  • incident amount reflection S11+loss+permeation S21.
  • Example 16 100 MHz 2.58 3.25 500 MHz 22.1 28.4 1 GHz 55.48 62.1
  • the magnetic sheet of Example 1 could suppress elution of fluorine ions more than the magnetic sheet of Comparative Example 8, so that the magnetic sheet of Example 1 could prevent corrosion of the magnetic sheet.
  • the corrosion seen on the surface of the magnetic sheet of FIG. 3B is the magnetic powder corroded by impurity ions (fluorine ions).
  • the magnetic sheet of Example 1 can prevent corrosion of wirings even when it is used around the wirings, as the magnetic sheet of Example 1 prevents elution of fluorine ions.
  • the magnetic sheet of Example 15 was usable even through it contained a large amount of the magnetic powder, which would easily cause cracking. This is because the magnetic sheet of Example 15 has a convex-concave forming layer (PET), and thus the magnetic sheet of Example 15 could maintain the shape thereof (as it was protected by the convex-concave forming layer (PET)).
  • PET convex-concave forming layer
  • Examples 16 and 17 showed high flame resistance in the combustion test (Table 4), and high electromagnetic wave-absorbing abilities in the measurement of LOSS properties (transmission loss) (Table 8).
  • the magnetic sheet of the present invention is suitably used for, for example, an electromagnetic noise depressor, an electromagnetic wave absorber, a magnetic shielding material, an electronic equipment having an IC tag function such as RFID and non-contact IC card, and is particularly suitably used for a RFID functioned mobile phone.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Polymers & Plastics (AREA)
  • Health & Medical Sciences (AREA)
  • Organic Chemistry (AREA)
  • Medicinal Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Dispersion Chemistry (AREA)
  • Power Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Spectroscopy & Molecular Physics (AREA)
  • Electromagnetism (AREA)
  • Shielding Devices Or Components To Electric Or Magnetic Fields (AREA)
  • Hard Magnetic Materials (AREA)
  • Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
  • Soft Magnetic Materials (AREA)
US12/854,472 2008-02-18 2010-08-11 Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet Abandoned US20110033732A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US13/447,432 US8668792B2 (en) 2008-02-18 2012-04-16 Method for producing magnetic sheet
US14/227,533 US20140212578A1 (en) 2008-02-18 2014-03-27 Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2008-036349 2008-02-18
JP2008036349 2008-02-18
PCT/JP2009/052720 WO2009104616A1 (ja) 2008-02-18 2009-02-17 磁性シート組成物、磁性シート、及び磁性シートの製造方法

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/052720 Continuation WO2009104616A1 (ja) 2008-02-18 2009-02-17 磁性シート組成物、磁性シート、及び磁性シートの製造方法

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US13/447,432 Division US8668792B2 (en) 2008-02-18 2012-04-16 Method for producing magnetic sheet
US14/227,533 Division US20140212578A1 (en) 2008-02-18 2014-03-27 Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet

Publications (1)

Publication Number Publication Date
US20110033732A1 true US20110033732A1 (en) 2011-02-10

Family

ID=40985495

Family Applications (3)

Application Number Title Priority Date Filing Date
US12/854,472 Abandoned US20110033732A1 (en) 2008-02-18 2010-08-11 Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet
US13/447,432 Active US8668792B2 (en) 2008-02-18 2012-04-16 Method for producing magnetic sheet
US14/227,533 Abandoned US20140212578A1 (en) 2008-02-18 2014-03-27 Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet

Family Applications After (2)

Application Number Title Priority Date Filing Date
US13/447,432 Active US8668792B2 (en) 2008-02-18 2012-04-16 Method for producing magnetic sheet
US14/227,533 Abandoned US20140212578A1 (en) 2008-02-18 2014-03-27 Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet

Country Status (7)

Country Link
US (3) US20110033732A1 (ko)
JP (1) JP4901889B2 (ko)
KR (1) KR101178385B1 (ko)
CN (1) CN101946291B (ko)
HK (1) HK1149627A1 (ko)
TW (1) TWI400266B (ko)
WO (1) WO2009104616A1 (ko)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120306824A1 (en) * 2011-06-06 2012-12-06 Wacom Co., Ltd. Position detecting device, display appratus, and portable apparatus
US9656512B1 (en) 2014-09-26 2017-05-23 Ellis Graphics, Inc. Circumferential magnetic device covers and methods of manufacture
US10269477B2 (en) 2013-10-22 2019-04-23 Nitto Denko Corporation Soft magnetic resin composition and soft magnetic film

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2013216731A (ja) * 2012-04-05 2013-10-24 Kyoritsu Kagaku Sangyo Kk カチオン硬化型樹脂組成物
KR20140116678A (ko) * 2013-03-25 2014-10-06 삼성전기주식회사 박막형 공통모드필터 및 그 제조방법
CN107369550A (zh) * 2017-08-03 2017-11-21 中南大学 一种各向异性FeSiAl磁芯的制备方法及产品

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2727416A1 (fr) * 1994-11-24 1996-05-31 Rhone Poulenc Chimie Nouveaux amorceurs cationiques thermoactivables, de polymerisation et/ou de reticulation et compositions monomeres et/ou polymeres fonctionnels les mettant en oeuvre
JPH09176112A (ja) * 1995-12-28 1997-07-08 Toyo Ink Mfg Co Ltd 感エネルギー線酸発生剤、感エネルギー線酸発生剤組成物および硬化性組成物
EP1533343A1 (en) * 2003-11-20 2005-05-25 Mitsubishi Engineering-Plastics Corporation Flame-retardant polyamide resin composition
JP2005350526A (ja) * 2004-06-09 2005-12-22 Nok Corp アクリルゴム磁性材料
JP2006274150A (ja) * 2005-03-30 2006-10-12 Hitachi Chem Co Ltd 硬化性樹脂組成物、プリプレグ、基板、金属箔張積層板及びプリント配線板
JP2007095829A (ja) * 2005-09-27 2007-04-12 Nitta Ind Corp 電磁波吸収シートおよび電磁波吸収シートの製造方法
US20070154820A1 (en) * 2005-12-30 2007-07-05 Hyun Jung Kang Photosensitive resin composition and black matrix using the same
US7829743B2 (en) * 2007-06-07 2010-11-09 Sony Corporation Sulfonium borate complex
US8431654B2 (en) * 2007-06-15 2013-04-30 Sony Chemical & Information Device Corporation Epoxy resin composition

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2797024B2 (ja) * 1989-10-13 1998-09-17 三新化学工業株式会社 スルホニウム化合物
US5084586A (en) * 1990-02-12 1992-01-28 Minnesota Mining And Manufacturing Company Novel initiators for cationic polymerization
JP2706833B2 (ja) * 1990-02-14 1998-01-28 三新化学工業株式会社 カチオン重合開始剤および重合性組成物
JP2789051B2 (ja) * 1990-04-16 1998-08-20 株式会社日立ホームテック 燃焼器の室温制御装置
FR2688783A1 (fr) * 1992-03-23 1993-09-24 Rhone Poulenc Chimie Nouveaux borates d'onium ou de complexe organometallique amorceurs cationiques de polymerisation.
JPH0641215A (ja) * 1992-07-23 1994-02-15 Nippon Kayaku Co Ltd カチオン発生剤溶液
DE60002428T2 (de) * 1999-09-28 2004-01-15 Nec Tokin Corp Magnetische kompositfolie und herstellungsverfahren
JP2002164688A (ja) * 2000-09-12 2002-06-07 Dainippon Printing Co Ltd 電波吸収体
US20050003079A1 (en) * 2003-03-17 2005-01-06 Tdk Corporation Production method of laminated soft magnetic member, production method of soft magnetic sheet, and method for heat treating laminated soft magnetic member
JP2005236219A (ja) * 2004-02-23 2005-09-02 Daido Steel Co Ltd 複合磁性シート

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2727416A1 (fr) * 1994-11-24 1996-05-31 Rhone Poulenc Chimie Nouveaux amorceurs cationiques thermoactivables, de polymerisation et/ou de reticulation et compositions monomeres et/ou polymeres fonctionnels les mettant en oeuvre
JPH09176112A (ja) * 1995-12-28 1997-07-08 Toyo Ink Mfg Co Ltd 感エネルギー線酸発生剤、感エネルギー線酸発生剤組成物および硬化性組成物
EP1533343A1 (en) * 2003-11-20 2005-05-25 Mitsubishi Engineering-Plastics Corporation Flame-retardant polyamide resin composition
JP2005350526A (ja) * 2004-06-09 2005-12-22 Nok Corp アクリルゴム磁性材料
JP2006274150A (ja) * 2005-03-30 2006-10-12 Hitachi Chem Co Ltd 硬化性樹脂組成物、プリプレグ、基板、金属箔張積層板及びプリント配線板
JP2007095829A (ja) * 2005-09-27 2007-04-12 Nitta Ind Corp 電磁波吸収シートおよび電磁波吸収シートの製造方法
US20070154820A1 (en) * 2005-12-30 2007-07-05 Hyun Jung Kang Photosensitive resin composition and black matrix using the same
US7829743B2 (en) * 2007-06-07 2010-11-09 Sony Corporation Sulfonium borate complex
US8431654B2 (en) * 2007-06-15 2013-04-30 Sony Chemical & Information Device Corporation Epoxy resin composition

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120306824A1 (en) * 2011-06-06 2012-12-06 Wacom Co., Ltd. Position detecting device, display appratus, and portable apparatus
US9052785B2 (en) * 2011-06-06 2015-06-09 Wacom Co., Ltd. Position detecting device, display apparatus, and portable apparatus
US10269477B2 (en) 2013-10-22 2019-04-23 Nitto Denko Corporation Soft magnetic resin composition and soft magnetic film
US9656512B1 (en) 2014-09-26 2017-05-23 Ellis Graphics, Inc. Circumferential magnetic device covers and methods of manufacture

Also Published As

Publication number Publication date
HK1149627A1 (en) 2011-10-07
KR101178385B1 (ko) 2012-08-29
JP4901889B2 (ja) 2012-03-21
KR20100119792A (ko) 2010-11-10
TWI400266B (zh) 2013-07-01
TW200940589A (en) 2009-10-01
US20120205025A1 (en) 2012-08-16
CN101946291B (zh) 2012-09-19
WO2009104616A1 (ja) 2009-08-27
US20140212578A1 (en) 2014-07-31
JP2009224768A (ja) 2009-10-01
CN101946291A (zh) 2011-01-12
US8668792B2 (en) 2014-03-11

Similar Documents

Publication Publication Date Title
US8828264B2 (en) Magnetic sheet
US20140212578A1 (en) Magnetic sheet composition, magnetic sheet, and method for producing magnetic sheet
US8357257B2 (en) Magnetic sheet and production method thereof
JP4811607B2 (ja) 軟磁性材料
WO2010024166A1 (ja) 磁性シート組成物、磁性シート、及び磁性シートの製造方法
JPWO2007007834A1 (ja) 難燃性軟磁性シート
WO2016088826A1 (ja) 複合型電磁波抑制体
JP2009295671A (ja) 磁性シート及び磁性シートの製造方法
JPWO2019189811A1 (ja) 熱硬化性樹脂組成物、プリプレグ、樹脂付き金属箔、積層体、プリント配線板及び半導体パッケージ
JP5570105B2 (ja) 磁性シート
JP5138623B2 (ja) 磁性シート及びその製造方法
JP2009224749A (ja) 磁性シート及び磁性シートの製造方法
JP2005126566A (ja) 変性ポリイミド樹脂組成物ならびにそれを用いたプリプレグ、積層板および配線板
JP2005236219A (ja) 複合磁性シート

Legal Events

Date Code Title Description
AS Assignment

Owner name: SONY CHEMICAL & INFORMATION DEVICE CORPORATION, JA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:ARAMAKI, KEISUKE;SHINYA, YOSHIHISA;KOMURO, KATSUHIKO;SIGNING DATES FROM 20100715 TO 20100726;REEL/FRAME:024824/0058

AS Assignment

Owner name: DEXERIALS CORPORATION, JAPAN

Free format text: CHANGE OF NAME;ASSIGNOR:SONY CHEMICAL & INFORMATION DEVICE CORPORATION;REEL/FRAME:029778/0641

Effective date: 20120928

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION