US20100215643A1 - Anti-infective functionalized surfaces and methods of making same - Google Patents

Anti-infective functionalized surfaces and methods of making same Download PDF

Info

Publication number
US20100215643A1
US20100215643A1 US12/712,031 US71203110A US2010215643A1 US 20100215643 A1 US20100215643 A1 US 20100215643A1 US 71203110 A US71203110 A US 71203110A US 2010215643 A1 US2010215643 A1 US 2010215643A1
Authority
US
United States
Prior art keywords
acid
infective agent
oxide
metal
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/712,031
Other languages
English (en)
Inventor
Randell Clevenger
Jeffrey Schwartz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ORTHOBOND CORP
Original Assignee
ORTHOBOND CORP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ORTHOBOND CORP filed Critical ORTHOBOND CORP
Priority to US12/712,031 priority Critical patent/US20100215643A1/en
Assigned to ORTHOBOND CORP. reassignment ORTHOBOND CORP. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CLEVENGER, RANDELL, SCHWARTZ, JEFFREY
Publication of US20100215643A1 publication Critical patent/US20100215643A1/en
Priority to US15/497,909 priority patent/US10596304B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
    • A61L31/14—Materials characterised by their function or physical properties, e.g. injectable or lubricating compositions, shape-memory materials, surface modified materials
    • A61L31/16—Biologically active materials, e.g. therapeutic substances
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L27/00—Materials for grafts or prostheses or for coating grafts or prostheses
    • A61L27/28—Materials for coating prostheses
    • A—HUMAN NECESSITIES
    • A01—AGRICULTURE; FORESTRY; ANIMAL HUSBANDRY; HUNTING; TRAPPING; FISHING
    • A01N—PRESERVATION OF BODIES OF HUMANS OR ANIMALS OR PLANTS OR PARTS THEREOF; BIOCIDES, e.g. AS DISINFECTANTS, AS PESTICIDES OR AS HERBICIDES; PEST REPELLANTS OR ATTRACTANTS; PLANT GROWTH REGULATORS
    • A01N25/00—Biocides, pest repellants or attractants, or plant growth regulators, characterised by their forms, or by their non-active ingredients or by their methods of application, e.g. seed treatment or sequential application; Substances for reducing the noxious effect of the active ingredients to organisms other than pests
    • A01N25/08—Biocides, pest repellants or attractants, or plant growth regulators, characterised by their forms, or by their non-active ingredients or by their methods of application, e.g. seed treatment or sequential application; Substances for reducing the noxious effect of the active ingredients to organisms other than pests containing solids as carriers or diluents
    • A—HUMAN NECESSITIES
    • A01—AGRICULTURE; FORESTRY; ANIMAL HUSBANDRY; HUNTING; TRAPPING; FISHING
    • A01N—PRESERVATION OF BODIES OF HUMANS OR ANIMALS OR PLANTS OR PARTS THEREOF; BIOCIDES, e.g. AS DISINFECTANTS, AS PESTICIDES OR AS HERBICIDES; PEST REPELLANTS OR ATTRACTANTS; PLANT GROWTH REGULATORS
    • A01N25/00—Biocides, pest repellants or attractants, or plant growth regulators, characterised by their forms, or by their non-active ingredients or by their methods of application, e.g. seed treatment or sequential application; Substances for reducing the noxious effect of the active ingredients to organisms other than pests
    • A01N25/08—Biocides, pest repellants or attractants, or plant growth regulators, characterised by their forms, or by their non-active ingredients or by their methods of application, e.g. seed treatment or sequential application; Substances for reducing the noxious effect of the active ingredients to organisms other than pests containing solids as carriers or diluents
    • A01N25/10—Macromolecular compounds
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L2/00—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor
    • A61L2/16—Methods or apparatus for disinfecting or sterilising materials or objects other than foodstuffs or contact lenses; Accessories therefor using chemical substances
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L31/00—Materials for other surgical articles, e.g. stents, stent-grafts, shunts, surgical drapes, guide wires, materials for adhesion prevention, occluding devices, surgical gloves, tissue fixation devices
    • A61L31/02—Inorganic materials
    • A61L31/022—Metals or alloys
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61P—SPECIFIC THERAPEUTIC ACTIVITY OF CHEMICAL COMPOUNDS OR MEDICINAL PREPARATIONS
    • A61P31/00—Antiinfectives, i.e. antibiotics, antiseptics, chemotherapeutics
    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07F—ACYCLIC, CARBOCYCLIC OR HETEROCYCLIC COMPOUNDS CONTAINING ELEMENTS OTHER THAN CARBON, HYDROGEN, HALOGEN, OXYGEN, NITROGEN, SULFUR, SELENIUM OR TELLURIUM
    • C07F9/00—Compounds containing elements of Groups 5 or 15 of the Periodic Table
    • C07F9/02—Phosphorus compounds
    • C07F9/28—Phosphorus compounds with one or more P—C bonds
    • C07F9/38—Phosphonic acids [RP(=O)(OH)2]; Thiophosphonic acids ; [RP(=X1)(X2H)2(X1, X2 are each independently O, S or Se)]
    • C07F9/3804—Phosphonic acids [RP(=O)(OH)2]; Thiophosphonic acids ; [RP(=X1)(X2H)2(X1, X2 are each independently O, S or Se)] not used, see subgroups
    • C07F9/3808—Acyclic saturated acids which can have further substituents on alkyl
    • C07F9/3821—Acyclic saturated acids which can have further substituents on alkyl substituted by B, Si, P or a metal
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L2202/00—Aspects relating to methods or apparatus for disinfecting or sterilising materials or objects
    • A61L2202/20—Targets to be treated
    • A61L2202/21—Pharmaceuticals, e.g. medicaments, artificial body parts
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L2300/00—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices
    • A61L2300/20—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices containing or releasing organic materials
    • A61L2300/204—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices containing or releasing organic materials with nitrogen-containing functional groups, e.g. aminoxides, nitriles, guanidines
    • A61L2300/208—Quaternary ammonium compounds
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L2300/00—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices
    • A61L2300/40—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices characterised by a specific therapeutic activity or mode of action
    • A61L2300/404—Biocides, antimicrobial agents, antiseptic agents

Definitions

  • the present invention relates to substrates with anti-infective surfaces.
  • methods are provided for functionalizing various material surfaces to include active surface regions for binding anti-infective agents.
  • An activated, or functionalized, layer that is bonded or otherwise disposed on the surface of a substrate is useful as an interface between the substrate and other materials such as organic or metallic materials.
  • This functionalized layer allows the substrate to react with and to bind to the organic or metallic material.
  • control of infection is a vital concern for many, from public health officials, hospital and school administrators and the like, to private citizens.
  • control of infection can be achieved by the topical application of disinfectants, antiseptics, antibacterials and the like to surfaces likely to be contacted by infectious agents.
  • Common disinfectants include active chlorine such as hypochlorites, chloramines, dichloroisocyanurate and trichloroisocyanurate, wet chlorine, chlorine dioxide and the like, active oxygen, including peroxides, such as peracetic acid, potassium persulfate, sodium perborate, sodium percarbonate and urea perhydrate, iodine compounds such as iodpovidone, iodine tincture, iodinated nonionic surfactants, concentrated alcohols such as ethanol, n-propanol and isopropanol and mixtures thereof; 2-phenoxyethanol and 1- and 2-phenoxypropanols, phenolic compounds, cresols, halogenated phenols, such as hexachlorophene, triclosan, trichlorophenol, tribromophenol, pentachlorophenol, Dibromol and salts thereof, cationic surfactants, including quaternary ammonium cations such as benzalkonium chlor
  • Antibiotics can be administered to stop infection in individuals. However, such administration is not always effective. Numerous medical applications, including orthopaedic, trauma, spine and general surgery applications, where the potential for infection is a serious concern, are not amenable to simple application of antiseptic or treatment with antibiotics. For example, infection can be a devastating complication of a total joint arthroplasty (TJA). While some infections may be treated by antibiotic suppression alone, more aggressive therapies, such as two-stage re-implantation, are often required. The treatment of post-arthroplasty infections in 1999 cost over $200 million in the US alone. Spangehl, M. J., et al., J. Bone Joint Surg. Am., 1999, 81(5), 672-682. TJA infections occur when bacteria colonize the surface of the implant. These species then form a resistant biofilm on the implant surface, which nullifies the body's normal antibody response.
  • TJA total joint arthroplasty
  • pedicle screws are first implanted in the bone of the vertebrae, and then rods are fixed into the heads of the screws to immobilize and stabilize the affected segments. Screws and rods pass through the patient's skin into the spine space via a cannulated channel. As in external fixation, screws and rods are also prone to pin-tract infections; due to the implants' pathway through the skin, the chance of contacting and/or passing harmful bacteria is greatly increased.
  • Catheters and shunts are placed in any number of body cavities and vessels to facilitate the injection, drainage, or exchange of fluids. Infections are common in catheter placements and are largely dependent on how long the patient is catheterized. For example, Kass reports an infection rate of virtually 100% for patients with indwelling urethral catheters draining into an open system for longer than 4 days. Kass, E. H., Trans. Assoc. Am. Physicians, 1956, 69, 56-63.
  • anti-infective surfaces that may be employed in locations particularly susceptible to hosting infectious agents, such as public places, common areas of buildings, fixtures and the like.
  • substrates and materials with anti-infective surfaces such as medical devices including implants, screws, rods, pins, catheters, stents, surgical tools and the like which could prevent infections by proactively killing bacteria that attempt to colonize the device surface both pre- and post-operatively.
  • a surface of interest is functionalized in accordance with a suitable functionalization method and an anti-infective agent is disposed on the functionalized surface.
  • any surface which may be functionalized is suitable for the inclusion of an anti-infective agent in accordance with the disclosed embodiments.
  • examples of such surfaces include metals, alloys, polymers, plastics, ceramics and glass. Therefore, the anti-infective surfaces as described herein may be applied universally through any environment, for example, in the environment of a surgical procedure or throughout an operating room or hospital, thereby eliminating many, if not all, sources of infection simultaneously and continuously.
  • Functionalization of substrates in accordance with the present invention may be achieved in a variety of ways.
  • a polymer substrate such as but not limited to polyamides, polyurethanes, polyesters, polyketones, polyethers, polyimides, aramides, polyfluoroolefins, epoxies, silicones or composites containing these polymers with an oxide, alkoxide or mixed oxide-alkoxide layer using an alkoxide precursor.
  • Such functionalized polymer surfaces can be used to covalently bond subsequent material or layers thereof on the surface, which in the present invention includes anti-infective moieties.
  • substrates that contain acidic protons such as —OH or —NH groups
  • an adherent coating layer that may be further functionalized with adherent species by heating a self-assembled layer of a functionalized phosphonic acid on the native oxide surface of a substrate or a deposited oxide derived from an alkoxide precursor.
  • a plurality of one or more anti-infective coating moieties may be bonded to the functional group of at least one functionalized organophosphonate moiety.
  • native oxides are found on metals including but not limited to titanium and its alloys; stainless steel; cobalt chrome alloys; and nickel, molybdenum, tantalum, zirconium, magnesium, and alloys containing them
  • anti-infective species to the functional group of a phosphonic acid before attaching said acid to a native oxide or an oxide derived from an alkoxide precursor.
  • native oxides are found on metals including but not limited to titanium and its alloys; stainless steel; cobalt chrome alloys; and nickel, molybdenum, tantalum, zirconium, magnesium, and alloys containing them
  • functionalization of a silicon surface may be achieved by a process wherein a self-assembled film of an organophosphonic acid is bonded to a native or synthesized oxide-coated Si surface as a film of the corresponding phosphonate.
  • the phosphonate film is functionalized to enable covalently coupling biological molecules, ranging in size from small peptides to large multi-subunit proteins, to the Si surface.
  • anti-infective peptide-modified surface-bound phosphonate films may be bonded to metal surfaces and polymer surfaces functionalized with alkoxide-derived oxides.
  • anti-infective surface modification methods described herein may eliminate the need for passivation, frequently a necessary step in the processing of metal implants.
  • Processes as disclosed herein provide layers bonded to metal surfaces and transform the surface oxides into chemically- and physically-robust species, thus eliminating the source of corrosion in devices such as metal implants.
  • Anti-infective agents as discussed herein may include bactericidal and bacteriostatic agents including disinfectants, antiseptics and antibiotics. Not all bactericidal and bacteriostatic agents may be used as antiseptics on mammalian tissue as they may have adverse effects thereon. Some embodiments of the present invention may apply to uses that do not involve contact of an anti-infective surface with mammalian tissue, such as interior surfaces of plumbing fixtures, building materials, ductwork, clean rooms, etc. In such applications certain anti-infective agents may be used, such as disinfectants, which would not be appropriate for use in applications in which contact with mammalian tissue was contemplated or possible.
  • compounds that may be used as antiseptics for use in humans include properly diluted chlorine preparations such as Daquin's solution, 0.5% sodium or potassium hypochlorite solution, pH-adjusted to pH 7-8, or 0.5-1% solution of sodium benzenesulfochloramide, some iodine preparations, such as iodopovidone, peroxides as urea perhydrate solutions and pH-buffered 0.1-0.25% peracetic acid solutions, alcohols with or without antiseptic additives, used mainly for skin antisepsis, weak organic acids such as sorbic acid, benzoic acid, lactic acid and salicylic acid, some phenolic compounds, such as hexachlorophene, triclosan and Dibromol, and cation-active compounds, such as 0.05-0.5% benzalkonium, 0.5-4% chlorhexidine, 0.1-2% octenidine solutions.
  • chlorine preparations such as Daquin's solution, 0.5% sodium or
  • anti-infective agents used in applications which involve possible contact with mammalian tissue may include quaternary ammonium compounds such as choline and choline derivatives, quaternary ammonium dendrimers, silver, copper, and cationic species; silver and copper.
  • the functionalization method employed to bond or otherwise attach a particular anti-infective agent in accordance with the present invention is dependent on the chemical nature of the anti-infective agent.
  • anti-infective surfaces thereof may kill bacterial species at the device-skin interface, thus preventing pin-site infections.
  • Devices including an anti-infective surface may prevent the colonization by infectious species of implanted surfaces, potentially reducing the incidence of deep infection, especially in high-risk populations.
  • catheters and shunts with anti-infective surfaces the potential for infection is minimized by killing bacteria traveling up the intubated pathway into the patient.
  • anti-infective hip stems may kill bacterial species and inhibit biofilm formation at the device-tissue interface, preventing the bacterial colonization of the hip replacement, which can lead to loosening due to infection and could require cost and painful hip revision surgery.
  • the anti-infective agent is highly stable under physiological conditions. The anti-infective agent does not leach from its material host, so there is no undesirable secondary result. Due to its nanometer scale, the anti-infective agent does not interfere with desired mechanical surface features that may be critical to the function of device such as an implant. The anti-infective agent is not visible to the naked eye and does not obscure identifying features including colored anodization or product markings.
  • Devices in accordance with the present disclosure are not limited to medical devices.
  • devices embodying the present disclosures may include fixtures, structures, fittings, barriers, and the like having anti-infective surfaces.
  • FIG. 1 depicts a schematic of an anti-infective agent bound to a surface in accordance with at least one embodiment of the present disclosure.
  • FIG. 2 depicts an anti-infective agent bound to a surface in accordance with at least one embodiment of the present disclosure.
  • FIG. 3 depicts a mode of action of an anti-infective agent in accordance with at least one embodiment of the present disclosure
  • methods are provided for functionalizing various material surfaces to include an active surface region to which are bound anti-infective agents.
  • a surface of interest is functionalized and an anti-infective agent is disposed on the functionalized surface to provide devices having anti-infective surfaces.
  • a surface 10 in accordance with the present disclosure includes a functionalizing layer 20 and an anti-infective agent 30 .
  • Surface 10 may be virtually any material which is amenable to receiving a functionalizing layer 20 .
  • materials include metals, alloys, polymers, plastics, ceramics, silicon, glass and surfaces with acidic protons, such as —OH or —NH groups.
  • Functionalizing layer 20 may be any layer suitable for a particular application.
  • the nature and composition of functionalizing layer 20 is dependent on the surface 10 that is intended to include an anti-infective agent 30 and the anti-infective agent 30 that is to be bound to the functionalizing layer 20 .
  • Such functionalized polymer surfaces can be used to covalently bond subsequent material or layers of anti-infective agent 30 on the surface.
  • Other functionalizing layers 20 may include functionalized phosphonic acids disposed on a native oxide of a substrate surface; functionalized phosphonic acids disposed onto an oxide layer, either directly deposited onto an underlying substrate or derived from an alkoxide precursor; for surfaces that contain acidic protons, such as —OH or —NH groups, reacting same with Group IV alkoxides; for surfaces with a silicon surface, a self-assembled film of a phosphonic acid bound to the native or synthesized oxide-coated Si surface as a film of the corresponding phosphonate; and the like.
  • Metal surfaces which may be employed include titanium and its alloys; stainless steels; cobalt chrome alloys; nickel, molybdenum, tantalum, zirconium, magnesium, manganese, niobium, and alloys containing them; and the like.
  • Anti-infective agents 30 may include bactericidal and bacteriostatic agents including disinfectants, antiseptics and antibiotics.
  • Disinfectants include active chlorine such as hypochlorites, chloramines, dichloroisocyanurate and trichloroisocyanurate, wet chlorine, chlorine dioxide and the like, active oxygen, including peroxides, such as peracetic acid, potassium persulfate, sodium perborate, sodium percarbonate and urea perhydrate, iodine compounds such as iodpovidone, iodine tincture, iodinated nonionic surfactants, concentrated alcohols such as ethanol, n-propanol and isopropanol and mixtures thereof; 2-phenoxyethanol and 1- and 2-phenoxypropanols, phenolic compounds, cresols, halogenated phenols, such as hexachlorophene, triclosan, trichlorophenol, tribromo
  • bactericidal and bacteriostatic agents may be used as antiseptics on mammalian tissue as they may have adverse effects thereon. It will be apparent to those skilled in the art that some embodiments of the present invention may apply to uses that do not involve contact of an anti-infective surface with mammalian tissue, such as the fabric used for surgical barriers and the interior surfaces of plumbing fixtures, building materials, ductwork, clean rooms, etc. In such applications certain anti-infective agents may be used, such as disinfectants, which would not be appropriate for use in applications in which contact with mammalian tissue would be contemplated or possible.
  • chlorine preparations such as Daquin's solution, 0.
  • anti-infective agents used in applications which involve possible contact with mammalian tissue include but are not limited to quaternary ammonium compounds such as choline and choline derivatives, quaternary ammonium dendrimers, silver, copper, and cationic species.
  • Quaternary ammonium compounds (“quats”) with long alkyl chains show proven biocidal properties by disruption of cell walls. Nakagawa, Y., et al., Appl. Environ. Microbiol., 1984, 47:3, 513-518, incorporated by reference herein in its entirety.
  • the quaternary ammonium cation functional group draws in and disrupts the cell membrane of the bacteria.
  • Quaternary ammonium dendrimers show similar biocidal activity naturally and when combined with functional groups or molecules with biocidal properties, can further enhance antimicrobial activity by increased loading.
  • Silver and copper have observed oligodynamic effects on microbes. Research suggests that silver and copper ions denature proteins in the target organism by binding to reactive groups. This binding results in precipitation and deactivation. Silver has also been shown to interfere with enzymes and metabolic processes. Cationic species are electrostatically attracted to bacterial cell walls, which are negatively charged. Cationic antimicrobial peptides have been shown to have inhibitory effects on the regulatory mechanisms of the target organism.
  • the anti-infective agent may include an acid functionalized group, wherein the acid is for example an organophosphonic, carboxylic, sulfonic, sulfinic, phosphinic, phosphonic, phosphoric or hydroxamic acid.
  • an embodiment of an anti-infective surface employs a Self-Assembled Monolayer Phosphonate (AI-SAMP) surface modification 20 covalently bound to the surface 10 of an implantable material.
  • the anti-infective agent 30 is a quaternary ammonium cationic functional group which is bound to the surface via the SAMP. Covalent bonding creates an exceptionally strong attachment between the surface treatment and the material to which it is applied. Schwartz, J., et al., Mat. Sci. Engr. C, 2003, 23, 395-400, the entirety of which is incorporated herein by reference.
  • SAMP is one molecule thick, it completely covers the material to which it is applied and assures total implant coverage regardless of the type or texture of the implant material. Covalent binding of quaternary ammonium salts renders the quats insoluble, providing lasting anti-infective activity. See, e.g., Nakagawa, Y., et al., Appl. Environ. Microbiol., 1984, 47:3, 513-518.
  • the quaternary ammonium cation functional group draws in and disrupts the cell membrane of the bacteria.
  • a polymer substrate surface such as but not limited to surfaces of polyamides, polyurethanes, polyesters, polyketones, polyethers, polyimides, aramides, polyfluoroolefins, polyetheretherketones, polyetherketoneketones, epoxies, silicones or composites containing these polymers with an oxide, alkoxide or mixed oxide-alkoxide layer using an alkoxide precursor.
  • Such functionalized polymer surfaces can be used to covalently bond subsequent material or layers of anti-infective agent on the surface.
  • the polymer surface may be coated with a layer of metal oxide (oxide adhesion layer).
  • the polymer surface may be coated with a continuous oxide adhesion layer, i.e., a layer that is formed by a matrix of individual molecules that are chemically bonded and linked to each other, as opposed to individual molecules covering the surface.
  • a continuous oxide adhesion layer i.e., a layer that is formed by a matrix of individual molecules that are chemically bonded and linked to each other, as opposed to individual molecules covering the surface.
  • metal alkoxide molecules are bonded together on at least a portion of a polymer surface to form a continuous layer and then converted to an oxide functionalizing layer.
  • an adherent coating layer that may be further functionalized with adherent species by heating a self-assembled layer of a functionalized phosphonic acid on the native oxide surface of a substrate.
  • This process described in detail in U.S. Patent Application Publication 2004/0023048, the entirety of which is incorporated herein by reference, provides on the native oxide surface of a material a multi-segmented, phosphorous-based coating layer having a difunctional organophosphonic acid-based segment bonded to the native oxide surface of the material and a linking segment bonded to the organophosphonic acid-based segment.
  • a phosphorous-based coating layer may be provided having a plurality of functionalized organophosphonate moieties bonded to the native oxide surface of a substrate by a phosphonate bond and a plurality of one or more anti-infective coating moieties, each coating moiety being bonded to the functional group of at least one functionalized organophosphonate moiety.
  • the metal complex is further characterized by being derived from a metal reagent, preferably a metal alkoxide reagent.
  • Organic SAM's may be covalently bonded to the surface of metal oxide or silicon oxide substrates.
  • Forming a self-assembled organic monolayer on the surface of a metal oxide or silicon oxide substrate may entail providing a metal oxide or silicon oxide substrate overlayer having a surface layer of alkoxides of transition metals selected from Group IVB, Group VB or Group VIB of the Periodic Chart covalently bonded thereto, wherein the alkoxides are bonded at the transition metal atoms to the surface oxygens of the substrate overlayer; and reacting the transition metal alkoxide surface layer with an organic compound capable of reacting with the transition metal alkoxide to form an organic ligand covalently bonded to the transition metal, thereby forming an organic self-assembled monolayer on the surface of the substrate, covalently bonded at the transition metal atoms to the surface oxygens of the substrate.
  • Suitable acid functional groups that can react with metal alkoxides include for example carboxylic, sulfonic, sulfinic, phosphinic, phosphonic, phosphoric and hydroxamic acid.
  • methods described in detail in U.S. Pat. No. 6,645,644 include forming a phosphate or phosphonate ligand layer covalently bonded to the surface of a hydroxide-bearing substrate, which includes coating a hydroxide-bearing substrate with phosphoric acid or an organic phosphonic acid and heating the coated substrate until the phosphoric acid or organic phosphonic acid covalently bonds to the substrate.
  • the substrate is a metal or metal alloy
  • the phosphoric acid forms an inorganic phosphate coating that is rich in free hydroxyl groups.
  • the hydroxyl groups are available for the addition of an anti-infective agent.
  • functionalization of a silicon surface may be achieved by a process wherein a self-assembled film of an organophosphonic acid is bonded to a native or synthesized oxide-coated Si surface as a film of the corresponding phosphonate.
  • the phosphonate film is functionalized to enable covalently coupling biological molecules, ranging in size from small peptides to large multi-subunit proteins, to the Si surface.
  • the linking of antibodies to such surfaces enables the selective recognition of a wide range of molecules, including antigens on the surfaces of bacterial pathogens and parasites. This method is described in detail in Midwood et al., Easy and Efficient Bonding of Biomolecules to an Oxide Surface of Silicon. Langmuir 2004, 20, 5501-5505, incorporated herein by reference in its entirety. Experimental details appear at page 5501, col. 2-page 5502, col. 2; see also discussion at pages 5502-5504 and accompanying figures.
  • surface-bound phosphonate films may be used to functionalize titanium and alloys thereof (such as Ti-6Al-4V) to attach anti-infective peptides.
  • titanium and alloys thereof such as Ti-6Al-4V
  • anti-infective peptides As is known in the art titanium and its alloys have high mechanical strength and are resistant to chemical attack, and thus are favored materials for surgical implants which may contact bone. This method is described in detail in Gawalt et al., Bonding Organics to Ti Alloys: Facilitating Human Osteoblast Attachment and Spreading on Surgical Implant Materials” Langmuir 2003, 19, 200-204, incorporated herein by reference in its entirety. Experimental details appear at page 200 col. 2-page 201, col. 2; see also discussion at pages 201-204 and accompanying figures.
  • Metal oxide adhesion techniques involve an oxide adhesion layer bonded to a surface thereof via coordination groups, wherein the oxide adhesion layer is a metal alkoxide, generally M-O—R wherein M is a metal atom.
  • the oxide adhesion layer is one that has been subjected to a process such as but not limited to pyrolysis, microwaving, complete hydrolysis and/or partial hydrolysis.
  • the technique is well suited for example to polymers or metals.
  • Functionalized surfaces such as functionalized metals or polymers can be used to covalently bond subsequent material or layers of anti-infective agent on the surface.
  • Suitable polymeric substrates include any polymer that can be functionalized, and may include any of various substances comprising synthetic and/or natural polymer molecules.
  • suitable polymer substrates include, but are not limited to, polyamides, polyurethanes, polyureas, polyesters, polyketones, polyimides, polysulfides, polysulfoxides, polysulfones, polythiophenes, polypyridines, polypyrroles, polyethers, silicones, polysiloxanes, polysaccharides, fluoropolymers, amides, imides, polypeptides, polyethylene, polystyrene, polypropylene, glass reinforced epoxies, liquid crystal polymers, thermoplastics, bismaleimide-triazine (BT) resins, benzocyclobutene polymers, Ajinomoto Buildup Films (ABF), low coefficient of thermal expansion (CTE) films of glass and epoxies, and composites including these polymers.
  • Alkoxides of transition metals are particularly useful for the present invention.
  • Periodic Table Group 3-6 and 13-14 metals are desirable metals for compositions of the present invention.
  • the preferred metals are Zr, Al, Ti, Hf, Ta, Nb, V and Sn, with the most preferred metals being Zr, Ti and Ta.
  • the transition metal alkoxide will have from three to six alkoxide groups or a mixture of oxo and alkoxide groups.
  • Preferred alkoxide groups have from 2 to 4 carbon atoms, such as ethoxide, propoxide, iso-propoxide, butoxide, iso-butoxide, tert-butoxide and fluoronated alkoxide.
  • the most preferred metal alkoxides are zirconium tetra(tert-butoxide), titanium tetra(tert-butoxide), and tantalum pentaethoxide.
  • Methods of making compositions and devices in accordance with this embodiment include activating a polymer surface comprising the steps of a) contacting a metal alkoxide with the surface; and b) subjecting the metal alkoxide to conditions adequate to form an adhesion layer on the surface on the surface comprised of an oxide, alkoxide, or mixed oxide/alkoxide.
  • the contacting step may be achieved by any suitable technique known to those skilled in the art such as but not limited to vapor or immersion deposition.
  • the step of forming an oxide adhesion layer may be achieved by subjecting the metal alkoxide to conditions of pyrolysis, microwaving, complete hydrolysis or partial hydrolysis. When heating conditions are employed, it is preferred that the metal alkoxide is heated to between about 50° C. and the upper working temperature of the polymer.
  • metal alkoxide molecules may be bonded together on at least a portion of a polymer surface to form a continuous layer and then converted to an oxide functionalizing layer.
  • a continuous layer is that the entirety of the surface that is covered by the continuous metal oxide adhesion layer is activated.
  • This process provides functionalized polymer surfaces that can be used to covalently bond subsequent material or layers thereof on the surface.
  • the process involves depositing a metal alkoxide on a polymer, and heating the substrate, with or without hydrolysis (full or partial), so that the metal alkoxide molecules form a continuous metal oxide adhesion layer covalently attached to the polymer surface.
  • the molecules of metal alkoxide are first brought into reactive proximity to the polymer molecules such as by, but not limited to, vapor deposition, brush-on or immersion deposition methods known in the art. If an ultrathin layer is desired, vapor deposition is the preferred process.
  • the deposited metal alkoxide molecules are then heated to between about 50° C.
  • a polymer surface may include acidic functionality regions as well as regions coated with a metal alkoxide functionalized layer.
  • the metal alkoxide functionalized layer may be viewed as filling in the spaces between the regions of acidic functionality.
  • metal alkoxide functionalized layers may be applied to regions of polymer having acidic functionality.
  • compositions in accordance with this embodiment include anti-infective agents bound via the oxide adhesion layer to the polymer substrate.
  • additional anti-infective material may include but is not limited to quaternary ammonium compounds, quaternary ammonium dendrimers, silver, copper, and cationic species.
  • additional anti-infective material may include but is not limited to quaternary ammonium compounds, quaternary ammonium dendrimers, silver, copper, and cationic species.
  • additional anti-infective material are detailed hereinbelow. The usefulness of the additional anti-infective material will be apparent to those skilled in the art. For example, medical and orthopedic implant devices including anti-infective surface functionality minimizes infection. Likewise, anti-infective materials can be incorporated in clean room applications, water supply articles such as well pumps, water purification pipes and conduit and the like.
  • the anti-infective material may be introduced to the oxide adhesion layer by techniques know to those of skill in the art, including but not limited to covalent bonding, evaporative, sputter or, immersion deposition. In some embodiments it may be desirable to subject the oxide adhesion layer to complete or partial hydrolysis prior to deposition of the additional material. In some embodiments it may be desirable to subject the deposited additional material to heat or microwave treatment.
  • the adhesion layer may be disposed on the substrate in a pattern or micropattern.
  • the anti-infective material may be disposed on the adhesion layer in a pattern or micropattern as described in further detail hereinbelow.
  • the oxide adhesion layer is reacted with an anti-infective material as discussed above to bind the anti-infective material to the polymer surface via the oxide adhesion layer.
  • the additional material may be added by reaction with the oxide adhesion layer by various methods available in the art, such as but not limited to covalent bonding, evaporative, sputter, or immersion deposition.
  • the material may be added using lithography, printing or stamping techniques to lay a pattern of material on to the oxide adhesion layer.
  • the polymer surface may be completely coated with a photoresist, and exposed to UV light through a mask. The areas exposed to the UV light can be developed and removed, leaving openings in the photoresist and access to the polymer surface in small areas. These areas are functionalized with the metal oxide adhesion layer.
  • the photoresist is then dissolved away leaving small patterned areas in the polymer surface that include the adhesion layer.
  • the patterned areas are preferentially reactive toward anti-infective agents of choice.
  • the oxide adhesion layer may be subjected to complete or partial hydrolysis prior to deposition of the anti-infective material to achieve the oxide adhesion layer with one or more alkoxide groups remaining on the metal atoms.
  • Absorption of solutions of silver or copper salts, followed by reduction, enables the surface of the metal to be coated with particulate silver or copper, respectively.
  • Formation of an adhesion layer of zirconium oxide also enables metallization of for example, a PEEK surface by absorption of a solution of either a silver salt (such as silver nitrate) or a copper salt (such as copper sulfate) followed by reduction with a reducing agent.
  • diethylaminoborane or sodium borohydride reduce the aforementioned salts to silver and copper metals, respectively, which are included in the oxide adhesion layer matrix.
  • a zirconium oxide adhesion layer may also be grown on the native oxide surface of a metal such as titanium.
  • Activated polymers of polyimides, aramides and Gore-Tex composites were produced as follows:
  • Polymer substrates (nylon 6/6, PET or PEEK) were placed in a deposition chamber equipped with two stopcocks for exposure either to vacuum or to the vapor of zirconium tetra(tert-butoxide).
  • the chamber was evacuated at 10 ⁇ 3 ton for 1 hour and polymer slides were exposed to vapor of zirconium tetra(tert-butoxide) (with external evacuation) for 1 minute followed by 5 minutes exposure without external evacuation. This cycle was repeated twice, after which a heating tape was applied to the chamber, and the internal temperature of the chamber was raised to 60° C. and kept at that temperature for 5 minutes (without external evacuation).
  • the chamber was then allowed to cool and was then evacuated at 10 ⁇ 3 ton for 1 hour to ensure removal of excess zirconium tetra(tert-butoxide) and to give surface activated polymers.
  • AFM section analysis showed the zirconia film to be thin. IR analysis shows that some tert-butoxy groups remain in the deposited and pyrolyzed film.
  • zirconium tetra(tert-butoxide) employing the following polymers and resins were performed with good results: polyimide Kapton®, polylactide-co-glycolate (PLGA), poly-3-hydroxybutyrate-co-valerate (PHBCV), Gore-Tex, and Aramide. It is to be expected that similar treatment of other polymers will yield similar results.
  • Activated polymers as prepared were treated with an aqueous solution of a copper salt, which was absorbed onto the zirconium oxide adhesion layer. Treatment with either sodium borohydride or an amine borane gave a copper-coated polymer. Electron dispersive X-ray based analysis showed the presence of both copper and zirconium.
  • silver nitrate was used to deposit silver metal onto activated PET. It is to be expected that similar treatment of other polymers will yield similar results, as will the use of other metal salts using similar reducing agents.
  • a sample of Kapton treated first with the zirconium-based adhesion layer, then copper sulfate, and then diethylamineborane as described in Example 1 was placed in a copper plating bath at 60° C. under nitrogen.
  • a small amount of PEG 200 (2.5 mg) was added to a 50 ml bath.
  • the zirconium oxide/alkoxide adhesion layer nucleates the growth of copper metal on PET and Kapton® polyimide film surfaces; this approach provides a basis for patterned metallization of polymer-based device substrates.
  • the adhesion layer can serve as a matrix to enable polymer surface metallization.
  • Kapton® polyimide film was coated with a 5 nm thick layer of adhesion layer and was then soaked in a 200 mM aqueous solution of CuSO 4 . Samples were rinsed in deionized water, and EDX analysis confirmed the presence of Cu and S. After subsequent (slow) reduction by dimethylamine borane (1M, aqueous, 6 hrs, 50° C.), metallic copper was formed.
  • Metallization was also done using an adhesion layer patterned on Kapton® polyimide film. The metallized surface was subjected to sonication in water and physical rubbing with a Q-tip, which was followed by EDX. In this way it was shown that patterns of both Zr and Cu on the Kapton® polyimide film surface faithfully replicated the mask design.
  • a corresponding pattern was also observed by AFM.
  • the thickness of the generated copper “seed” was measured via AFM to be ca. 20 times thicker than the starting film of adhesion layer, indicating the adhesion layer nucleates the growth of CuSO 4 at the polyimide surface.
  • CuSO 4 -treated Kapton® polyimide film was reduced rapidly using aqueous sodium borohydride, which also gave copper metal; here, AFM analysis showed the Cu pattern to be buried into the polymer surface in pits, the tops of which in many cases were about 500 nm below the polymer surface. It is believed that the relatively faster borohydride reduction is sufficiently exothermic so that the polymer melts in the vicinity of the reduction reaction.
  • the adhesion layer is thin (ca. 5 nm), it is resistant to cracking by physically flexing the polymer, therefore the adhesion layer is a suitable matrix for polymer metallization with copper.
  • Copper “seed” layers can serve as nucleation sites for bulk copper growth by electroless deposition processes (Gu et al., Organic Solution Deposition of Copper Seed Layers onto Barrier Metals. Mat. Res. Soc. Symp. Proc. 2000, 612, D9.19.1-D9.19.6 (p. D9.19.2, lines 33-40; p. D9.19.5, lines 14-22)).
  • this further metallization of the polymer provides a means to prepare copper-based anti-infective compounds on a variety of flexible substrates under simple laboratory conditions.
  • Metallization of Kapton® polyimide film and PET Patterned or un-patterned copper metallization of the polymer surfaces was achieved by soaking an activated polymer surface in a 200 mM aqueous solution of CuSO 4 overnight, followed by reduction in 1M aqueous dimethylamine borane or sodium borohydride for 6 hrs. Copper metallization was confirmed by Energy Dispersive X-ray Analysis, which was done using a FEI XL30 FEG-SEM equipped with a PGT-IMIX PTS EDX system.
  • Substrates may be functionalized using functionalized organophosphorous techniques. See, U.S. Patent Application Publication 2004/0023048, incorporated herein by reference in its entirety.
  • the organophosphonic acid-based segment may be derived from a functionalized organophosphonic acid such as an omega-functionalized organophosphonic acid containing a hydrocarbon ligand having from about 2 to about 40 carbon atoms, wherein the hydrocarbon ligand is a linear or branched, saturated or unsaturated, substituted or unsubstituted, aliphatic or aromatic alkylene moiety.
  • Substituents on the hydrocarbon portion of phosphonic acids useful in accordance with the present disclosure may be appended to any carbon atom of the hydrocarbon ligand.
  • Useful substituents are, for example, reactive functional groups, for example, a hydroxyl group, carboxylic group, an amino group, a thiol group, a phosphonate group, and chemical derivatives thereof. It will be appreciated that any functional group which can participate in a further derivatization reaction can be employed.
  • an alkylene hydrocarbon ligand may contain within the structure or appended to the structure, reactive moieties, for example sites of unsaturation, which may be further reacted in a polymerization reaction with reactive substituents on the hydrocarbon ligands appended to other phosphonate sites bound to the surface of the native oxide during a phosphonate derivatizing reaction.
  • a phosphonate-organo-polymeric layer may be formed on the oxide surface.
  • An example of such a polymerization reaction is the preparation of a surface coating of an acrylic derivative of a phosphonic acid. When acrylate and methacrylate substituents are employed, the polymerization proceeds spontaneously upon exposure to light or air. For less reactive coatings, the polymerization can be performed by exposing the coating to conventional polymerization reagents and conditions.
  • coatings are formed from phosphonic acids having an organic ligand functionalized at a carbon of the ligand which is further reacted to form covalent bonds with anti-infective agents.
  • functionalized phosphonic acids the application of the acid to oxide surface generally results in a self-assembled phosphonic acid film with a carbon directed away from the substrate surface and available for covalent bonding or further chemical modification.
  • Preferred functional groups include hydroxyl, amino, carboxylate, thiol, and phosphonate groups.
  • the reactive substituents pendent on the organic portion of a phosphonate bound to the oxide surface can be further reacted with reagents which are subject to hydrolysis reactions.
  • reagents which are subject to hydrolysis reactions.
  • metal alkoxides examples of which are those having the structure M(O—R).sub.n, where M is a metal, R is a linear or branched, saturated or unsaturated, aliphatic or aromatic, substituted or unsubstituted hydrocarbon moiety, and “n” is equal to a stable valance state of the metal.
  • metal alkoxide compounds are zirconium tetra(tert-butoxide), titanium tetra(tert-butoxide), and silicon tetra(tert-butoxide) where R is a t-butyl group, M is respectively Zr, Ti, and Si, and “n” is four.
  • R is a t-butyl group
  • M is respectively Zr
  • Ti titanium
  • Si silicon
  • “n” is four.
  • hydrolytically reactive compounds which have two or more alkoxide ligands in addition to other ligands may also be utilized.
  • calcium alkoxides such as calcium bis(2-methoxy-ethoxide) may be employed.
  • alkoxide ligated metals in groups 2 through 14 will find utility in these secondary functionalization reactions with phosphonate coatings of the present development.
  • a process for forming a coated article by the foregoing technique may include (a) depositing a layer of a functionalized organophosphorous compound on an oxide substrate; (b) heating the substrate of step (a) to a temperature sufficient to bond the functionalized organophosphorous compound to the oxide substrate; (c) depositing a separate layer onto the layer produced by step (b); and (d) bonding the layers produced by steps (b) and (c) through the functional group.
  • Preferred functional groups are hydroxyl-, carboxylate-, amino-, thiol-, and phosphonato-functional groups, or these groups further derivatized by reaction with a metal or organo-metal reagent, for example an alkoxide.
  • the groups participate in further bonding with moieties of the organic, inorganic or bioactive coating layer, either through strong chemical bonding, for example, covalent bonding, or through weaker bonding interactions, for example, hydrogen bonding.
  • Preferred metal reagents for derivatizing functional groups are metal alkoxides, for example zirconium tetra(tert-butoxide), silicon tetra(tert-butoxide), titanium tetra(tert-butoxide), and calcium bis(2-methoxy-ethoxide).
  • a preferred method of attaching an anti-infective agent to a native oxide surface comprises providing a phosphorous-based coating layer as described above wherein the functionalized organophosphonate moieties are hydroxyl, amine or thiolate that have been derivatized with a cross-coupling reagent such as (p-nitrophenyl) chloroformate, and further reacted with an amino or hydroxylated moiety, wherein the amino or hydroxylated moieties are a diamine or aminoalcohol bonded by a carbon-nitrogen bond or a carbon-oxygen bond, respectively, to a carbonyl group, the reaction providing a urethane, carbonate, urea, thiocarbonate, or thiourea bond to the derivatized functional group; the terminal amino group is then quaternized.
  • a cross-coupling reagent such as (p-nitrophenyl) chloroformate
  • a method of bonding a layer of a phosphorous-based acid moiety to a surface such as but not limited to an oxide surface (such as titanium, zirconium and tantalum oxide) comprising coating said oxide surface with a phosphorous-based acid moiety self-assembled layer and heating said coated oxide surface until the self-assembled layer is bonded thereto, the phosphorous-based acid moiety comprising the self-assembled layer being selected from the group consisting of phosphoric acid and organophosphonic acids.
  • Preferred coatings are those which have been formed from alkyl, alkylene- and arylene-organophosphonic acids, including substituted alkyl, alkylene and arylene-phosphonic acids. More preferred are substituted alkyl and alkylene phosphonic acids with a reactive substituent to the phosphonic acid functional group.
  • Preferred oxide surfaces are the native oxide surfaces of titanium, zirconium and tantalum materials.
  • Self-assembled films of an organophosphonic acid may be bonded to the native or synthesized oxide-coated silicon surface as a film of the corresponding phosphonate.
  • the phosphonate film is functionalized to enable covalent coupling of biological molecules that may be anti-infective; covalent coupling of anti-infective agents or moieties; and/or covalent coupling of anti-infective agents or moieties to a biological molecule.
  • the functionalized surfaces and/or the anti-infective agents may be patterned on a substrate, depending on the particular application.
  • Peptide-modified surface-bound phosphonate films may be easily prepared with high surface coverage.
  • Anti-infective peptides may be bound to functionalized surfaces in accordance with the techniques described in Gawalt.
  • Organic anti-infective moieties that may be added to a functionalizing layer such as those described hereinabove include quaternary ammonium alkylamines, quaternary ammonium alkanols, usinic acid; cationic peptides such as cecropins neutrophil defensins, polyphemusin, gramicidins, thionins, histone-derived compounds, beta-hairpin, hemoglobin, lactoferrin; anionic peptides such as neuropeptide precursors, aromatic dipeptides, hemocyanin derivatives; other antimicrobial peptides such as bacteriacins, cathelicidin, thrombocidin, and histanins; antibodies, antibiotics, including tetracyclines, amphenicols, penicillins, cephalosporins, monobactams, carbapenems, sulfanomides, trimethoprim, macrolides, lincosamides, streptogramins, str
  • Inorganic anti-infective coating layers that may be bonded include silver, copper, zinc oxides, titanium oxides, zeolites, silicates, calcium hydroxide, iodine, sodium hypochlorite, sulfites, and sulfates.
  • Preferred anti-infective moieties are quaternary ammonium compounds, such as benzethonium chloride, cetrimonium bromide, cetrimonium chloride, dimethyldioctadecylammonium chloride, tetramethylammonium hydroxide; quaternary ammonium alkyl dendrimers, silver, copper, cationic species such as benzalkonium chloride, Bronidox; and alkylated choline.
  • compositions and devices in accordance with the present invention include but are not limited to any device(s) specific to an application by an orthopedic, cardiovascular, plastic, dermatologic, general, maxillofacial or neuro surgeon or physician including, but not limited to, cardiovascular or vascular implant device such as stents, replacement heart valves, replacement heart valve components, leaflets, sewing cuffs, orifices, annuloplasty rings, pacemakers, pacemaker polymer mesh bags, pacemaker leads, pacing wires, intracardiac patches/pledgets, vascular patches, vascular grafts, intravascular catheters, and defibrillators; tissue scaffolds; non-woven meshes, woven meshes, and foams; orthopedic implant devices including orthopedic trauma implants, joint implants, spinal implants, plates, screws, rods, plugs, cages, pins, nails, wires, cables, anchors, scaffolds, artificial joints selected from hand joints, wrist joints, elbow joints, shoulder joints, spine joints, hip joints, knee joints and ankle joints; bone replacement, bone fixation cerclage and dental
  • a zirconium oxide/alkoxide adhesion layer was deposited onto Nylon 6/6 and then reacted with a solution of 11-hydroxyundecylphosphonic acid to form an organophosphonate monolayer. See, Dennes, T. J. et al., High-Yield Activation of Scaffold Polymer Surfaces to Attach Cell Adhesion Molecules. J. Am. Chem. Soc. 2007, 129, 93-97, incorporated herein by reference in its entirety. Experimental details appear at page 95, col. 1-page 97, col. 1; see also discussion at pages 94-96 and accompanying figures.
  • the substrate was first immersed in a solution of 3-(maleimido)propanoic acid N-hydroxysuccinimide ester and then in an aqueous solution of RGDC to derivatize the phosphonate monolayer with an active peptide.
  • an anti-infective peptide may be bound to the phosphonate monolayer in place of RGD.
  • 11-Hydroxyundecylphosphonic acid was reacted with the surface of cleaned and prepared silicon wafers, forming a self-organized 11-hydroxyundecylphosphonate monolayer on SiO 2 . This was confirmed by QCM and AFM.
  • the omega-functional groups were derivatized using disuccinimidyl glutarate (DSG) in dry acetonitrile. Rabbit antimouse IgG (Pierce) was then coupled to the derivatized monolayer by incubating for 30 min at a concentration of 100/g/mL in PBS.
  • Antibody coupling was accomplished by incubation with 10/g/mL anti-R4 integrin antibody P1H4 (Chemicon) or anti-R5 integrin antibody SAM-1 (Cymbus Technology Ltd.) for 2 h. Antibody activity was confirmed by incubation of CHO ⁇ 4 or CHO ⁇ 5 cells; selective cell growth indicated appropriate activity.
  • a self-assembled monolayer of 11-hydroxyphosphonate is bonded to the native oxide surface of titanium and is then treated first with (p-nitrophenyl) chloroformate and then a solution of 1,12-diaminododecane (Aldrich) to give an aminododecyl urethane bonded to the titanium through the phosphonate interface.
  • the distal amino group is then quaternized using octyl iodide (Aldrich) to give the quaternary alkylammonium moiety covalently bonded to the substrate through the phosphonate interface.
  • a quaternary alkylammonium moiety may be bonded to a polymer such as PEEK by first preparing an adhesion layer of zirconium oxide on the PEEK surface followed by treatment with the 11-hydroxyphosphonic acid to give the 11-hydroxyphosphonate monolayer bonded to the PEEK.
  • the 11-hydroxyphosphonate monolayer is derivatized by reaction, sequentially, with (p-nitrophenyl) chloroformate, 1,12-diaminododecane, and octyl iodide.

Landscapes

  • Health & Medical Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • General Health & Medical Sciences (AREA)
  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Pest Control & Pesticides (AREA)
  • Plant Pathology (AREA)
  • Dentistry (AREA)
  • Wood Science & Technology (AREA)
  • Zoology (AREA)
  • Environmental Sciences (AREA)
  • Agronomy & Crop Science (AREA)
  • Toxicology (AREA)
  • Animal Behavior & Ethology (AREA)
  • Veterinary Medicine (AREA)
  • Public Health (AREA)
  • Epidemiology (AREA)
  • Organic Chemistry (AREA)
  • Medicinal Chemistry (AREA)
  • Vascular Medicine (AREA)
  • Surgery (AREA)
  • Heart & Thoracic Surgery (AREA)
  • Molecular Biology (AREA)
  • General Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Inorganic Chemistry (AREA)
  • Biomedical Technology (AREA)
  • Biochemistry (AREA)
  • Oral & Maxillofacial Surgery (AREA)
  • Transplantation (AREA)
  • Dermatology (AREA)
  • Oncology (AREA)
  • Communicable Diseases (AREA)
  • Pharmacology & Pharmacy (AREA)
  • Nuclear Medicine, Radiotherapy & Molecular Imaging (AREA)
  • Materials For Medical Uses (AREA)
  • Pharmaceuticals Containing Other Organic And Inorganic Compounds (AREA)
  • Prostheses (AREA)
  • Surgical Instruments (AREA)
  • Media Introduction/Drainage Providing Device (AREA)
US12/712,031 2009-02-25 2010-02-24 Anti-infective functionalized surfaces and methods of making same Abandoned US20100215643A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US12/712,031 US20100215643A1 (en) 2009-02-25 2010-02-24 Anti-infective functionalized surfaces and methods of making same
US15/497,909 US10596304B2 (en) 2009-02-25 2017-04-26 Anti-infective functionalized surfaces and methods of making same

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US15532409P 2009-02-25 2009-02-25
US12/712,031 US20100215643A1 (en) 2009-02-25 2010-02-24 Anti-infective functionalized surfaces and methods of making same

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/497,909 Continuation US10596304B2 (en) 2009-02-25 2017-04-26 Anti-infective functionalized surfaces and methods of making same

Publications (1)

Publication Number Publication Date
US20100215643A1 true US20100215643A1 (en) 2010-08-26

Family

ID=42631150

Family Applications (2)

Application Number Title Priority Date Filing Date
US12/712,031 Abandoned US20100215643A1 (en) 2009-02-25 2010-02-24 Anti-infective functionalized surfaces and methods of making same
US15/497,909 Active 2030-08-20 US10596304B2 (en) 2009-02-25 2017-04-26 Anti-infective functionalized surfaces and methods of making same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/497,909 Active 2030-08-20 US10596304B2 (en) 2009-02-25 2017-04-26 Anti-infective functionalized surfaces and methods of making same

Country Status (10)

Country Link
US (2) US20100215643A1 (ja)
EP (1) EP2401001B1 (ja)
JP (4) JP2012518497A (ja)
KR (2) KR20170121209A (ja)
CN (2) CN102365103A (ja)
AU (1) AU2010218035B2 (ja)
BR (1) BRPI1008796B1 (ja)
CA (1) CA2753423A1 (ja)
RU (1) RU2501572C2 (ja)
WO (1) WO2010099221A1 (ja)

Cited By (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110110986A1 (en) * 2006-02-21 2011-05-12 The Trustees Of Princeton University High-yield activation of polymer surfaces for covalent attachment of molecules
ES2395646A1 (es) * 2011-07-22 2013-02-14 Universidad De Zaragoza Composición bactericida y método de desinfección y/o esterilización que comprende dicha composición.
DE102011088951A1 (de) * 2011-12-19 2013-06-20 Beiersdorf Ag Wirkstoffkombinationen aus einer oder mehreren aromatischen Alkoholen und einer oder mehreren physiologisch unbedenklichen Hydroxamsäuren sowie kosmetische oder dermatologische Zubereitungen, solche Wirkstoffkombinationen enthaltend
US20130266626A1 (en) * 2010-09-13 2013-10-10 Universidade Federal Do Rio Grande Do Sul Active and intelligent additive, polymer and article
WO2014152649A1 (en) * 2013-03-15 2014-09-25 Difusion Technologies, Inc. Enhanced efficacy self-sterilizing orthopedic implants
CN104258462A (zh) * 2014-09-30 2015-01-07 广西中医药大学 一种医用不锈钢材料及其制备方法
US9107765B2 (en) 2010-05-07 2015-08-18 Difusion Technologies, Inc. Medical implants with increased hydrophilicity
US9132576B2 (en) 2009-12-11 2015-09-15 Difusion Technologies, Inc. Method of manufacturing antimicrobial implants of polyetheretherketone
WO2016065358A1 (en) 2014-10-24 2016-04-28 Orthobond, Inc. Quaternary phosphonium coated surfaces and methods of making the same
US20160208383A1 (en) * 2013-01-11 2016-07-21 The Aerospace Corporation Systems and methods for enhancing mobility of atomic or molecular species on a substrate at reduced bulk temperature using acoustic waves, and structures formed using same
US9492584B2 (en) 2009-11-25 2016-11-15 Difusion Technologies, Inc. Post-charging of zeolite doped plastics with antimicrobial metal ions
DE102015115024A1 (de) * 2015-09-08 2017-03-09 Schülke & Mayr GmbH Flüssigkonzentrat für die Konservierung von Kosmetika
ITUB20156321A1 (it) * 2015-12-04 2017-06-04 Maurizio Priori Metodo per sanificare un dispositivo medico, in particolare per il trattamento localizzato della cute
US9717657B2 (en) 2012-10-24 2017-08-01 Amy Dukoff Composition and method of using medicament for endodontic irrigation, stem cell preparations and tissue regeneration
EP3092278A4 (en) * 2014-01-07 2017-10-04 Orthobond, Inc. Surface adhesive for devices
US20180076403A1 (en) * 2016-08-19 2018-03-15 Purdue Research Foundation Amine-boranes as organic ligands for surface functionalization
US9925295B2 (en) 2012-05-09 2018-03-27 Amedica Corporation Ceramic and/or glass materials and related methods
US20180103643A1 (en) * 2016-10-17 2018-04-19 Orthobond Corporation Functional Surfaces
EP3273907A4 (en) * 2015-03-30 2018-04-25 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
WO2018075457A1 (en) 2016-10-17 2018-04-26 Orthobond Corporation Surfaces with oligomeric or polymeric antimicrobials
EP3363478A1 (en) 2017-02-16 2018-08-22 Cook Medical Technologies LLC Implantable medical device with differentiated luminal and abluminal characteristics
US10065029B2 (en) 2014-03-03 2018-09-04 Cook Medical Technologies Llc Mechanical dilator
US10150924B2 (en) * 2013-02-28 2018-12-11 Electrolab, Inc. Bonded layer treatment method for a device utilized in a crude oil service operation, and method of installing said device
WO2019108730A1 (en) * 2017-11-30 2019-06-06 The Trustees Of Princeton University Adhesion layer bonded to an activated surface
US10806831B2 (en) 2012-05-09 2020-10-20 Sintx Technologies, Inc. Antibacterial biomedical implants and associated materials, apparatus, and methods
US10834922B2 (en) 2014-11-26 2020-11-17 Microban Products Company Surface disinfectant with residual biocidal property
US10842147B2 (en) 2014-11-26 2020-11-24 Microban Products Company Surface disinfectant with residual biocidal property
CN112043364A (zh) * 2020-10-08 2020-12-08 江苏双羊医疗器械有限公司 一种可透视腕关节外固定支架
US10876217B2 (en) 2018-04-13 2020-12-29 Molecular Surface Technologies, Llc Electrochemical attachment of phosphonic acids to metallic substrates and osteoconductive medical devices containing same
US10925281B2 (en) 2014-11-26 2021-02-23 Microban Products Company Surface disinfectant with residual biocidal property
US11033023B2 (en) 2014-11-26 2021-06-15 Microban Products Company Surface disinfectant with residual biocidal property
US20210352907A1 (en) * 2020-05-13 2021-11-18 Vapor Technologies, Inc. Antimicrobial cu-based topcoat
WO2022067352A3 (en) * 2020-09-28 2022-04-28 The Trustees Of Princeton University Antimicrobial and antiviral treatments of materials
US11338109B2 (en) 2018-05-17 2022-05-24 Hollister Incorporated Hydrophilic medical products and hydration mediums for hydrating the same
CN115243545A (zh) * 2020-03-27 2022-10-25 三菱综合材料株式会社 抗菌部件
US11503824B2 (en) 2016-05-23 2022-11-22 Microban Products Company Touch screen cleaning and protectant composition
US11540514B2 (en) 2019-06-25 2023-01-03 Molecular Surface Technologies, Llc Electrochemical attachment of phosphonic acids to metallic substrates and antimicrobial medical devices containing same
US11730863B2 (en) 2018-07-02 2023-08-22 C. R. Bard, Inc. Antimicrobial catheter assemblies and methods thereof

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101116673B1 (ko) * 2010-12-13 2012-02-22 전남대학교병원 티타늄 산화물 박막코팅을 이용한 유전자 전달 스텐트 및 그 제조방법
DE102013214636A1 (de) * 2013-07-26 2015-01-29 Heraeus Medical Gmbh Bioresorbierbare Werkstoffverbunde, enthaltend Magnesium und Magnesiumlegierungen sowie Implantate aus diesen Verbunden
CN104120396B (zh) * 2014-07-29 2016-08-24 复旦大学附属华山医院 纳米银涂层修饰人工韧带的制备方法
CN104255725B (zh) * 2014-09-03 2016-04-13 江苏今日卫生用品有限公司 凉席消毒液
CN107496445B (zh) * 2017-08-25 2020-04-28 北京海洁海斯健康科技有限公司 一种去定植药物及其制备方法与应用
CN111225791B (zh) * 2017-10-11 2022-04-12 微仙美国有限公司 膦酸酯及其用途
WO2019078135A1 (ja) 2017-10-16 2019-04-25 Ｎｓマテリアルズ株式会社 量子ドット含有樹脂シート又はフィルム、及びその製造方法、並びに、波長変換部材
CN111705299B (zh) * 2019-03-01 2022-07-08 湖南早晨纳米机器人有限公司 一种纳米机器人的制备方法及纳米机器人
CN109999316B (zh) * 2019-04-29 2021-05-28 南通伊诺精密塑胶导管有限公司 一种具有显影标记功能的血管微导管
CN110037050B (zh) * 2019-05-08 2021-02-02 山西大学 一种高效复合碘溶液及其制备方法
US11944097B2 (en) 2019-07-01 2024-04-02 Aseptic Health, LLC Antimicrobial composition
CN110585482B (zh) * 2019-08-02 2022-03-01 大连理工大学 一种具有抗菌性能的杂萘联苯聚芳醚腈及其表面改性方法
JP7358886B2 (ja) * 2019-09-27 2023-10-11 Toto株式会社 衛生設備部材
CN110983275B (zh) * 2019-12-25 2022-02-01 南京华塑增材制造有限公司 一种petg矫治器表面银掺杂二氧化钛纳米抗菌复合涂层的低温制备方法
CN111118484B (zh) * 2020-01-17 2021-08-17 中山大学附属口腔医院 一种钛种植体表面的长效可再生抗菌涂层
JP2021154607A (ja) * 2020-03-27 2021-10-07 三菱マテリアル株式会社 透明抗菌部材
CN111647338B (zh) * 2020-05-07 2021-09-07 西北工业大学 一种高性能自清洁环氧树脂涂层及制备方法
CN113577442A (zh) * 2021-08-17 2021-11-02 吉林大学第一医院 一种具有抗凝、抗感染覆膜涂层的颈内中心静脉穿刺导管
CN114516655B (zh) * 2022-02-09 2023-07-04 广州科城环保科技有限公司 一种线路板废物生产氢氧化铜的方法
BR102022013123B1 (pt) * 2022-06-30 2023-04-25 Munir Salomão Tela de titânio recoberta por filme de polipropileno biocompatível para recobrimento e proteção de enxertos ósseos/biomateriais e processo de obtenção
CN115349492A (zh) * 2022-08-01 2022-11-18 重庆市畜牧技术推广总站 一种提高母猪高效繁殖的肌注方法及注射剂
CN115676779B (zh) * 2022-10-27 2024-01-30 中盐常州化工股份有限公司 一种次氯酸钠稳定剂及其制备方法

Citations (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4879135A (en) * 1984-07-23 1989-11-07 University Of Medicine And Dentistry Of New Jersey Drug bonded prosthesis and process for producing same
US5078782A (en) * 1986-04-24 1992-01-07 Berol Nobel (Suisse) S.A. Pesticidal concentrate compositions
US6146767A (en) * 1996-10-17 2000-11-14 The Trustees Of Princeton University Self-assembled organic monolayers
WO2001000034A1 (en) * 1999-06-28 2001-01-04 Ecosmart Technologies, Inc. Pesticidal compositions containing peppermint oil
US6645644B1 (en) * 1996-10-17 2003-11-11 The Trustees Of Princeton University Enhanced bonding of phosphoric and phosphoric acids to oxidized substrates
US20040023048A1 (en) * 1997-02-04 2004-02-05 Jeffrey Schwartz Enhanced bonding layers on native oxide surfaces
US20050027360A1 (en) * 2003-08-01 2005-02-03 Webb Scott A. Spinal implant
US20050147750A1 (en) * 2004-01-05 2005-07-07 Jacobs Simon J. MEMS passivation with phosphonate surfactants
US20060188537A1 (en) * 2005-02-22 2006-08-24 Lamba-Kohli Nina M Generation of antimicrobial surfaces using dendrimer biocides
US20060194008A1 (en) * 1999-09-22 2006-08-31 Princeton University Devices with multiple surface functionality
US20070077348A1 (en) * 2005-10-03 2007-04-05 Lu Helen S M Process for providing antimicrobial surfaces
US20070196663A1 (en) * 2006-02-21 2007-08-23 The Trustees Of Princeton University High-yield activation of polymer surfaces for covalent attachment of molecules
US20070292355A1 (en) * 2002-10-25 2007-12-20 Foamix Ltd. Anti-infection augmentation foamable compositions and kit and uses thereof
US20090010447A1 (en) * 2007-08-15 2009-01-08 Iowa State University Research Foundation, Inc. Active Noise Control System
US20090104474A1 (en) * 2007-10-17 2009-04-23 Princeton University Functionalized substrates and methods of making same
US20090232867A1 (en) * 2004-07-19 2009-09-17 Elutex Ltd. Modified conductive surfaces having active substances attached thereto

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2128024C1 (ru) * 1997-08-07 1999-03-27 Закрытое акционерное общество "Научно-производственный комплекс "Экофлон" Имплантируемый полый протез и способ его изготовления
US6440405B1 (en) * 1999-06-07 2002-08-27 University Of Delaware Quaternary ammonium functionalized dendrimers and methods of use therefor
US7459167B1 (en) 2000-07-27 2008-12-02 3M Innovative Properties Company Biocidal polyurethane compositions and methods of use
DE10114247A1 (de) * 2001-03-22 2002-10-10 Heraeus Kulzer Gmbh & Co Kg Antibiotikum-/Antibiotika-Polymer-Kombination
CA2530640C (en) * 2003-06-23 2013-08-13 Princeton University Carrier applied coating layers
JP2008506519A (ja) * 2004-07-16 2008-03-06 カリフォルニア インスティテュート オブ テクノロジー 機能強化デンドリマーろ過による水処理
RU2292224C1 (ru) * 2005-07-11 2007-01-27 Борис Яковлевич Басин Способ изготовления сетчатого протеза с антимикробными свойствами для герниопластики
CA2667307C (en) * 2006-10-27 2015-12-01 3M Innovative Properties Company Antimicrobial compositions comprising a c2-c5 lower alcohol, a cationic antimicrobial agent, and a fatty component containing free hydroxyl groups
CA2965670A1 (en) 2014-10-24 2016-04-28 Orthobond, Inc. Quaternary phosphonium coated surfaces and methods of making the same

Patent Citations (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4879135A (en) * 1984-07-23 1989-11-07 University Of Medicine And Dentistry Of New Jersey Drug bonded prosthesis and process for producing same
US5078782A (en) * 1986-04-24 1992-01-07 Berol Nobel (Suisse) S.A. Pesticidal concentrate compositions
US6146767A (en) * 1996-10-17 2000-11-14 The Trustees Of Princeton University Self-assembled organic monolayers
US6645644B1 (en) * 1996-10-17 2003-11-11 The Trustees Of Princeton University Enhanced bonding of phosphoric and phosphoric acids to oxidized substrates
US20040023048A1 (en) * 1997-02-04 2004-02-05 Jeffrey Schwartz Enhanced bonding layers on native oxide surfaces
WO2001000034A1 (en) * 1999-06-28 2001-01-04 Ecosmart Technologies, Inc. Pesticidal compositions containing peppermint oil
US20060194008A1 (en) * 1999-09-22 2006-08-31 Princeton University Devices with multiple surface functionality
US20070292355A1 (en) * 2002-10-25 2007-12-20 Foamix Ltd. Anti-infection augmentation foamable compositions and kit and uses thereof
US20050027360A1 (en) * 2003-08-01 2005-02-03 Webb Scott A. Spinal implant
US20050147750A1 (en) * 2004-01-05 2005-07-07 Jacobs Simon J. MEMS passivation with phosphonate surfactants
US20090232867A1 (en) * 2004-07-19 2009-09-17 Elutex Ltd. Modified conductive surfaces having active substances attached thereto
US20060188537A1 (en) * 2005-02-22 2006-08-24 Lamba-Kohli Nina M Generation of antimicrobial surfaces using dendrimer biocides
US20070077348A1 (en) * 2005-10-03 2007-04-05 Lu Helen S M Process for providing antimicrobial surfaces
US20070196663A1 (en) * 2006-02-21 2007-08-23 The Trustees Of Princeton University High-yield activation of polymer surfaces for covalent attachment of molecules
US20090010447A1 (en) * 2007-08-15 2009-01-08 Iowa State University Research Foundation, Inc. Active Noise Control System
US20090104474A1 (en) * 2007-10-17 2009-04-23 Princeton University Functionalized substrates and methods of making same

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
Amalric et al. Phosphate monolayers functionalized by silver thiolate species as antibacterial nanocoatings on titanium and stainless steel, 11/14/2008, Journals of Materials Chemitry, vol. 19, pp. 141-149. *
Dennes et al., A Nanoscale Adhesion Layer to Promote Cell Attachment on PEEK, 02/18/2009, J. AM. Chem. Soc., vol. 131, pp. 3456-7. *
Shard et al., "Surface Oxidation of Polyethylene, Polystyrene, and PEEK: The Synthon Approach", 1992, Macrmolecules, vol. 25, pp. 2053-2054. *

Cited By (66)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9056154B2 (en) * 2006-02-21 2015-06-16 The Trustees Of Princeton University High-yield activation of polymer surfaces for covalent attachment of molecules
US20110110986A1 (en) * 2006-02-21 2011-05-12 The Trustees Of Princeton University High-yield activation of polymer surfaces for covalent attachment of molecules
US9492584B2 (en) 2009-11-25 2016-11-15 Difusion Technologies, Inc. Post-charging of zeolite doped plastics with antimicrobial metal ions
US9132576B2 (en) 2009-12-11 2015-09-15 Difusion Technologies, Inc. Method of manufacturing antimicrobial implants of polyetheretherketone
US9375321B2 (en) 2010-05-07 2016-06-28 Difusion Technologies, Inc. Medical implants with increased hydrophilicity
US9107765B2 (en) 2010-05-07 2015-08-18 Difusion Technologies, Inc. Medical implants with increased hydrophilicity
US20130266626A1 (en) * 2010-09-13 2013-10-10 Universidade Federal Do Rio Grande Do Sul Active and intelligent additive, polymer and article
US9700054B2 (en) * 2010-09-13 2017-07-11 Braskem S.A. Active and intelligent additive, polymer and article
ES2395646A1 (es) * 2011-07-22 2013-02-14 Universidad De Zaragoza Composición bactericida y método de desinfección y/o esterilización que comprende dicha composición.
DE102011088951A1 (de) * 2011-12-19 2013-06-20 Beiersdorf Ag Wirkstoffkombinationen aus einer oder mehreren aromatischen Alkoholen und einer oder mehreren physiologisch unbedenklichen Hydroxamsäuren sowie kosmetische oder dermatologische Zubereitungen, solche Wirkstoffkombinationen enthaltend
US9925295B2 (en) 2012-05-09 2018-03-27 Amedica Corporation Ceramic and/or glass materials and related methods
US10806831B2 (en) 2012-05-09 2020-10-20 Sintx Technologies, Inc. Antibacterial biomedical implants and associated materials, apparatus, and methods
US9717657B2 (en) 2012-10-24 2017-08-01 Amy Dukoff Composition and method of using medicament for endodontic irrigation, stem cell preparations and tissue regeneration
US9945032B2 (en) * 2013-01-11 2018-04-17 The Aerospace Corporation Systems and methods for enhancing mobility of atomic or molecular species on a substrate at reduced bulk temperature using acoustic waves, and structures formed using same
US20160208383A1 (en) * 2013-01-11 2016-07-21 The Aerospace Corporation Systems and methods for enhancing mobility of atomic or molecular species on a substrate at reduced bulk temperature using acoustic waves, and structures formed using same
US10150924B2 (en) * 2013-02-28 2018-12-11 Electrolab, Inc. Bonded layer treatment method for a device utilized in a crude oil service operation, and method of installing said device
WO2014152649A1 (en) * 2013-03-15 2014-09-25 Difusion Technologies, Inc. Enhanced efficacy self-sterilizing orthopedic implants
US10449750B2 (en) 2014-01-07 2019-10-22 Orthobond Corporation Surface adhesive for devices
EP3092278A4 (en) * 2014-01-07 2017-10-04 Orthobond, Inc. Surface adhesive for devices
US10065029B2 (en) 2014-03-03 2018-09-04 Cook Medical Technologies Llc Mechanical dilator
CN104258462A (zh) * 2014-09-30 2015-01-07 广西中医药大学 一种医用不锈钢材料及其制备方法
US9868808B2 (en) 2014-10-24 2018-01-16 Orthobond, Inc. Quaternary phosphonium coated surfaces and methods of making the same
WO2016065358A1 (en) 2014-10-24 2016-04-28 Orthobond, Inc. Quaternary phosphonium coated surfaces and methods of making the same
US11134678B2 (en) 2014-11-26 2021-10-05 Microban Products Company Surface disinfectant with residual biocidal property
US10834922B2 (en) 2014-11-26 2020-11-17 Microban Products Company Surface disinfectant with residual biocidal property
US11134674B2 (en) 2014-11-26 2021-10-05 Microban Products Company Surface disinfectant with residual biocidal property
US11033023B2 (en) 2014-11-26 2021-06-15 Microban Products Company Surface disinfectant with residual biocidal property
US11026418B2 (en) 2014-11-26 2021-06-08 Microban Products Company Surface disinfectant with residual biocidal property
US10925281B2 (en) 2014-11-26 2021-02-23 Microban Products Company Surface disinfectant with residual biocidal property
US10842147B2 (en) 2014-11-26 2020-11-24 Microban Products Company Surface disinfectant with residual biocidal property
AU2016243634B2 (en) * 2015-03-30 2020-04-02 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
AU2020204445B2 (en) * 2015-03-30 2021-07-15 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
US20220347355A1 (en) * 2015-03-30 2022-11-03 C. R. Bard, Inc. Application of Antimicrobial Agents to Medical Devices
US11413376B2 (en) 2015-03-30 2022-08-16 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
EP3273907A4 (en) * 2015-03-30 2018-04-25 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
EP4062868A3 (en) * 2015-03-30 2022-12-21 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
US20230398263A1 (en) * 2015-03-30 2023-12-14 C. R. Bard, Inc. Application of Antimicrobial Agents to Medical Devices
US11759551B2 (en) * 2015-03-30 2023-09-19 C. R. Bard, Inc. Application of antimicrobial agents to medical devices
DE102015115024A1 (de) * 2015-09-08 2017-03-09 Schülke & Mayr GmbH Flüssigkonzentrat für die Konservierung von Kosmetika
WO2017093811A1 (en) * 2015-12-04 2017-06-08 Priori Maurizio Method for sanitizing a medical device, in particular for the local treatment of the skin
ITUB20156321A1 (it) * 2015-12-04 2017-06-04 Maurizio Priori Metodo per sanificare un dispositivo medico, in particolare per il trattamento localizzato della cute
US11503824B2 (en) 2016-05-23 2022-11-22 Microban Products Company Touch screen cleaning and protectant composition
US20180076403A1 (en) * 2016-08-19 2018-03-15 Purdue Research Foundation Amine-boranes as organic ligands for surface functionalization
US20180103643A1 (en) * 2016-10-17 2018-04-19 Orthobond Corporation Functional Surfaces
US10390533B2 (en) * 2016-10-17 2019-08-27 Orthobond Corporation Surfaces with oligomeric or polymeric antimicrobials
JP2020503368A (ja) * 2016-10-17 2020-01-30 オーソボンド コーポレーション オリゴマーまたはポリマー抗菌剤を含む表面
WO2018075457A1 (en) 2016-10-17 2018-04-26 Orthobond Corporation Surfaces with oligomeric or polymeric antimicrobials
AU2017346582B2 (en) * 2016-10-17 2021-10-21 Orthobond Corporation Surfaces with oligomeric or polymeric antimicrobials
US11154061B2 (en) * 2016-10-17 2021-10-26 Orthobond Corporation Functional surfaces
KR20190104020A (ko) * 2016-10-17 2019-09-05 오소본드 코포레이션 올리고머 또는 폴리머 항균제를 갖는 표면
KR102332048B1 (ko) 2016-10-17 2021-11-29 오소본드 코포레이션 올리고머성 또는 폴리머성 항미생물제를 갖는 표면
EP3363478A1 (en) 2017-02-16 2018-08-22 Cook Medical Technologies LLC Implantable medical device with differentiated luminal and abluminal characteristics
US10980923B2 (en) 2017-02-16 2021-04-20 Cook Medical Technologies Llc Implantable medical device with differentiated luminal and abluminal characteristics
WO2019108730A1 (en) * 2017-11-30 2019-06-06 The Trustees Of Princeton University Adhesion layer bonded to an activated surface
US20200360562A1 (en) * 2017-11-30 2020-11-19 The Trustees Of Princeton University Adhesion layer bonded to an activated surface
CN111937117A (zh) * 2017-11-30 2020-11-13 普林斯顿大学理事会 与活化表面键合的粘附层
US11332840B2 (en) 2018-04-13 2022-05-17 Molecular Surface Technologies, Llc Electrochemical attachment of phosphonic acids to metallic substrates and osteoconductive medical devices containing same
US10876217B2 (en) 2018-04-13 2020-12-29 Molecular Surface Technologies, Llc Electrochemical attachment of phosphonic acids to metallic substrates and osteoconductive medical devices containing same
US11338109B2 (en) 2018-05-17 2022-05-24 Hollister Incorporated Hydrophilic medical products and hydration mediums for hydrating the same
US11730863B2 (en) 2018-07-02 2023-08-22 C. R. Bard, Inc. Antimicrobial catheter assemblies and methods thereof
US11540514B2 (en) 2019-06-25 2023-01-03 Molecular Surface Technologies, Llc Electrochemical attachment of phosphonic acids to metallic substrates and antimicrobial medical devices containing same
CN115243545A (zh) * 2020-03-27 2022-10-25 三菱综合材料株式会社 抗菌部件
EP4129646A4 (en) * 2020-03-27 2024-04-24 Mitsubishi Materials Corporation ANTIBACTERIAL ELEMENT
US20210352907A1 (en) * 2020-05-13 2021-11-18 Vapor Technologies, Inc. Antimicrobial cu-based topcoat
WO2022067352A3 (en) * 2020-09-28 2022-04-28 The Trustees Of Princeton University Antimicrobial and antiviral treatments of materials
CN112043364A (zh) * 2020-10-08 2020-12-08 江苏双羊医疗器械有限公司 一种可透视腕关节外固定支架

Also Published As

Publication number Publication date
CN104069546B (zh) 2020-07-03
BRPI1008796A2 (pt) 2016-03-08
EP2401001A1 (en) 2012-01-04
CN102365103A (zh) 2012-02-29
EP2401001B1 (en) 2020-08-12
US20170224882A1 (en) 2017-08-10
JP2016163709A (ja) 2016-09-08
EP2401001A4 (en) 2014-03-19
KR101779617B1 (ko) 2017-09-18
JP2012518497A (ja) 2012-08-16
JP2017200602A (ja) 2017-11-09
CA2753423A1 (en) 2010-09-02
JP6174180B2 (ja) 2017-08-02
WO2010099221A1 (en) 2010-09-02
CN104069546A (zh) 2014-10-01
RU2501572C2 (ru) 2013-12-20
US10596304B2 (en) 2020-03-24
BRPI1008796B1 (pt) 2022-09-27
KR20110132397A (ko) 2011-12-07
JP6581624B2 (ja) 2019-09-25
RU2011139328A (ru) 2013-04-10
US20180099075A9 (en) 2018-04-12
KR20170121209A (ko) 2017-11-01
AU2010218035A1 (en) 2011-09-15
JP2015091368A (ja) 2015-05-14
AU2010218035B2 (en) 2014-05-15

Similar Documents

Publication Publication Date Title
US10596304B2 (en) Anti-infective functionalized surfaces and methods of making same
Wang et al. Universal antifouling and photothermal antibacterial surfaces based on multifunctional metal–phenolic networks for prevention of biofilm formation
AU2008312373B2 (en) Functionalized substrates with thin metal oxide adhesion layer
US20180134832A1 (en) Quaternary phosphonium coated surfaces and methods of making the same
Canepa et al. Anchoring of aminophosphonates on titanium oxide for biomolecular coupling
US20180168165A1 (en) Silver iodate compounds having antimicrobial properties
US20220266296A1 (en) Methods of Photografting to Surface Metal Oxides
Vasilev et al. Materials Today Chemistry
Zhang et al. Hydroxyapatite crystals biologically inspired on titanium by using an organic template based on the copolymer of acrylic acid and itaconic acid

Legal Events

Date Code Title Description
AS Assignment

Owner name: ORTHOBOND CORP., NEW JERSEY

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CLEVENGER, RANDELL;SCHWARTZ, JEFFREY;REEL/FRAME:024355/0320

Effective date: 20100503

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION