Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D183/00—Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
  • C09D183/04—Polysiloxanes
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J183/00—Adhesives based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Adhesives based on derivatives of such polymers
  • C09J183/04—Polysiloxanes
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J7/00—Adhesives in the form of films or foils
  • C09J7/20—Adhesives in the form of films or foils characterised by their carriers
  • C09J7/22—Plastics; Metallised plastics
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J7/00—Adhesives in the form of films or foils
  • C09J7/30—Adhesives in the form of films or foils characterised by the adhesive composition
  • C09J7/38—Pressure-sensitive adhesives [PSA]
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/56—Organo-metallic compounds, i.e. organic compounds containing a metal-to-carbon bond
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J2203/00—Applications of adhesives in processes or use of adhesives in the form of films or foils
  • C09J2203/306—Applications of adhesives in processes or use of adhesives in the form of films or foils for protecting painted surfaces, e.g. of cars
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J2467/00—Presence of polyester
  • C09J2467/006—Presence of polyester in the substrate
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J2483/00—Presence of polysiloxane
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/28—Web or sheet containing structurally defined element or component and having an adhesive outermost layer
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/28—Web or sheet containing structurally defined element or component and having an adhesive outermost layer
  • Y10T428/2813—Heat or solvent activated or sealable
  • Y10T428/2817—Heat sealable

Definitions

• the present invention relates to a protective sheet for a coating layer, more specifically to a protective sheet for a coating layer which does not allow coating layers applied on automotive bodies and parts of automobiles to change in quality or discolor and which is excellent in a stripping property after adhered for a long period of time.
• the protective sheet for a coating layer according to the present invention is a protective sheet capable of being applied as well to a coating layer of a urethane-based coating material in which a small amount of a solvent remains due to insufficient drying and which is insufficiently cured after drying, and it is particularly useful as a protective sheet for coated plastic-made parts such as bumpers and the like.
• the curing temperature can not be elevated in order to avoid adverse affections such as deterioration and deformation of the resin. Accordingly, the coating layers on the coated resin-made bumpers are insufficiently dried even after passing through a drying furnace, and therefore a small amount of the solvent remains or the curing reaction does not sufficiently proceed in a certain case.
• a protective sheet for a coating layer Proposed as a protective sheet for a coating layer are a sheet prepared by providing a layer of a polyisobutylene-based pressure-sensitive adhesive on a substrate for supporting (for example, a Patent Document 1), a sheet prepared by providing a layer of a pressure-sensitive adhesive comprising butyl rubber or a styrene-ethylene-butylene-styrene block copolymer on a substrate for supporting (for example, a Patent Document 2), a sheet prepared by providing a layer of a composition obtained by mixing a polyisobutylene-based pressure-sensitive adhesive with a small amount of an acrylic-based pressure-sensitive adhesive on a substrate for supporting (for example, a Patent Document 3), a sheet prepared by providing a layer of a composition obtained by blending an acrylic-based pressure-sensitive adhesive with a multifunctional isocyanate compound on a substrate for supporting (for example, a Patent Document 4), a sheet prepared by providing an ethylene-vinyl acetate-
• Patent Document 1 U.S. Pat. No. 2,701,020
• Patent Document 2 U.S. Pat. No. 3,668,322
• Patent Document 3 U.S. Pat. No. 2,832,565
• Patent Document 4 U.S. Pat. No. 3,342,977
• Patent Document 5 JP 1998-121002A
• Patent Document 6 JP 1998-121010A
• an object of the present invention is to solve the problems described above in a protective sheet for a coating layer by using a pressure-sensitive adhesive component totally different from the various pressure-sensitive adhesive components described above which have so far been used.
• the present invention provides the following items (1) to (7):
• a protective sheet for a coating layer comprising a substrate sheet and provided thereon a pressure-sensitive adhesive layer, wherein the pressure-sensitive adhesive layer comprises an addition reaction type silicone-based pressure-sensitive adhesive, (2) the protective sheet as described in the above item (1), wherein the addition reaction type silicone-based pressure-sensitive adhesive further contains a curing catalyst, (3) the protective sheet as described in the above item (1) or (2), wherein the curing catalyst is a platinum-based catalyst, (4) the protective sheet as described in the above item (1) or (2), wherein the substrate sheet is a polyethylene terephthalate sheet, (5) the protective sheet as described in the above item (1) or (2), wherein the pressure-sensitive adhesive layer is cross-linked by heating or irradiating with an active energy beam, (6) the protective sheet as described in the above item (1) or (2), wherein it is a protective sheet for a coating layer which is applied on cars and (7) the protective sheet as described in the above item (1) or (2), wherein it is a protective sheet for a urethane-based coating layer which is applied on
• a protective sheet for a coating layer which is less liable to allow coating layers applied on car bodies and parts of automobiles to change in quality or discolor and which is excellent in a stripping property after adhered for a long period of time.
• it is useful as a protective sheet for coating layers in which a small amount of a solvent remains due to insufficient drying immediately after drying in plastic-made parts such as coated bumpers and the like and which are insufficiently cured.
• the addition reaction type silicone-based adhesive which is provided on the protective sheet for a coating layer according to the present invention shall be explained.
• the addition reaction type silicone-based adhesive comprises a base resin and a cross-linking agent.
• the addition reaction type silicone-based pressure-sensitive adhesive in the present invention has the advantage that it can be used after only primary curing at low temperatures and does not require secondary curing at high temperatures.
• the addition reaction type silicone-based pressure-sensitive adhesive in the present invention has a low adhesive strength as compared with those of conventional peroxide curing type silicone-based pressure-sensitive adhesives, and therefore it has the preferred characteristic that it does not exert an adverse affection on the coating layer surface when peeled after finishing use of the protective sheet.
• the addition reaction type silicone-based pressure-sensitive adhesive in the present invention comprises usually a base resin comprising a mixture of a silicone resin component and a silicone rubber component, a hydrosilyl group (SiH)—containing cross-linking agent and a curing catalyst which is used if necessary.
• a base resin comprising a mixture of a silicone resin component and a silicone rubber component, a hydrosilyl group (SiH)—containing cross-linking agent and a curing catalyst which is used if necessary.
• the silicone resin component is an organopolysiloxane having a reticulate structure which is obtained by hydrolyzing an organochlorosilane or an organoalkoxysilane and then subjecting it to dehydration condensation reaction.
• the silicone rubber component is a diorganopolysiloxane having a straight chain structure.
• the organo group includes methyl, ethyl, propyl, butyl, phenyl and the like in both cases of the silicone resin component and the silicone rubber component.
• the organo groups described above are partially substituted with an unsaturated group such as a vinyl group, a hexenyl group, an allyl group, a butenyl group, a pentenyl group, an octenyl group, a (meth)acryloyl group, a (meth)acryloylmethyl group, a (meth)acryloylpropyl group, a cyclohexenyl group and the like.
• the silicone rubber components having a vinyl group which are readily available in an industrial scale are preferred.
• cross-linking proceeds by addition reaction of an unsaturated group with a hydrosilyl group, and a reticulate structure is formed, whereby a pressure-sensitive adhesiveness is developed.
• the number of the unsaturated group such as a vinyl group is usually 0.05 to 3.0 pieces, preferably 0.1 to 2.5 pieces based on 100 pieces of organo group.
• the number of the unsaturated group controlled to 0.05 piece or more prevents the reactivity with a hydrosilyl group from lowering to make curing less liable to proceed and provides the pressure-sensitive adhesive with a suited adhesive strength.
• the number thereof controlled to 3.0 pieces or less elevates a cross-linking density of the pressure-sensitive adhesive and increases an adhesive strength thereof, so that an adverse affection is prevented from being exerted on coating layers applied on car bodies and the like.
• the diorganopolysiloxane includes, to be specific, KS-3703 (having 0.6 piece of vinyl group based on 100 pieces of methyl group) manufactured by Shin-Etsu Chemical Co., Ltd. and BY23-753 (having 0.1 piece of vinyl group based on 100 pieces of methyl group) and BY24-162 (having 1.4 piece of vinyl group based on 100 pieces of methyl group) each manufactured by Dow Corning Toray Co., Ltd. Further, SD4560PSA, SD4570PSA, SD4580PSA, SD4584PSA, SD4585PSA, SD4587L and SD4592PSA each manufactured by Dow Corning Toray Co., Ltd. can be used as well.
• the organopolysiloxane which is the silicone resin component is used usually in a mixture with the silicone rubber component
• the silicone rubber component includes KS-3800 (having 7.6 pieces of vinyl group based on 100 pieces of methyl group) manufactured by Shin-Etsu Chemical Co., Ltd. and BY24-162 (having 1.4 piece of vinyl group based on 100 pieces of methyl group), BY24-843 (having no unsaturated groups) and SD-7292 (having 5.0 pieces of vinyl group based on 100 pieces of methyl group) each manufactured by Dow Corning Toray Co., Ltd.
• a blending ratio of the silicone resin component to the silicone rubber component is usually 250 parts by mass or less for the latter based on 100 parts by mass for the former.
• the blending ratio controlled to 250 parts by mass or less for the latter prevents an adverse affection from being exerted on coating layers applied on car bodies and the like.
• the cross-linking agent is blended so that the number of hydrogen atoms bonded to a silicon atom is usually 0.5 to 10, preferably 1 to 2.5 based on one group of an unsaturated group such as a vinyl group in the silicone resin component and the silicone rubber component.
• the number of hydrogen atoms controlled to 0.5 or more prevents reaction of an unsaturated group such as a vinyl group with a hydrosilyl group from not completely proceeding to make curing inferior.
• the number of hydrogen atoms controlled to 10 or less prevents the cross-linking agent from remaining without reacting to exert an adverse affection on coating layers applied on car bodies and the like.
• a curing catalyst is preferably blended with the pressure-sensitive adhesive applied on the protective sheet for a coating layer according to the present invention in addition to the addition reaction type silicone component (comprising the silicone resin component and the silicone rubber component) and the cross-linking agent each described above.
• the addition reaction type silicone-based adhesive in the present invention does not have a functional group such as a silanol group having a reactivity with an isocyanate group, and therefore it can be adhered even when a coating layer is insufficiently cured and does not exert an adverse affection on the coating layer when stripping the protective sheet.
• the above curing catalyst is used in order to accelerate hydrosilylation reaction of an unsaturated group in the silicone resin component and the silicone rubber component with an Si—H group in the cross-linking agent.
• the curing catalyst includes a platinum-based catalysts, that is, chloroplatinic acid, an alcohol solution of chloroplatinic acid, reaction products of chloroplatinic acid with an alcohol solution, reaction products of chloroplatinic acid with olefin compounds, reaction products of chloroplatinic acid with vinyl group-containing siloxane compounds, platinum-olefin complexes, platinum-vinyl group-containing siloxane complexes, platinum-phosphorus complexes and the like.
• a platinum-based catalysts that is, chloroplatinic acid, an alcohol solution of chloroplatinic acid, reaction products of chloroplatinic acid with an alcohol solution, reaction products of chloroplatinic acid with olefin compounds, reaction products of chloroplatinic acid with vinyl group-containing siloxane compounds, platinum-olefin complexes, platinum-vinyl group-containing siloxane complexes, platinum-phosphorus complexes and the like.
• SRX-212 manufactured by Dow Corning Toray Co., Ltd.
• PL-50T manufactured by Shin-Etsu Chemical Co., Ltd. and the like.
• An amount to be blended of the curing catalyst is usually 5 to 2000 ppm, preferably 10 to 500 ppm in terms of a platinum content based on the total amount of the silicone resin component and the silicone rubber component.
• An amount to be blended of the curing catalyst controlled to 5 ppm or more prevents the curing property from being reduced to result in a reduction in the cross-linking density, that is, a reduction in the cohesion.
• an amount to be blended thereof controlled to 2000 ppm or less prevents an increase in the cost and makes it possible to maintain a stability of the pressure-sensitive adhesive layer, and it prevents the curing catalyst which is used in excess from exerting an adverse affection on coating layers applied on car bodies and the like.
• additives can be added as optional components to the addition reaction type silicone-based adhesive in the present invention as long as characteristics required to the protective sheet for a coating layer are not damaged.
• the additives include non-reactive polyorganosiloxanes such as dimethylsiloxane and dimethyldiphenylsiloxane, antioxidants of a phenol base and others, light stabilizers of a benzotriazole base, flame retardants of a phosphoric ester base and others, antistatic agents such as cationic surfactants, inert solvents such as toluene and xylene which are used in order to reduce a viscosity when applying the pressure-sensitive adhesive, colorants and fillers.
• a pressure-sensitive adhesive strength is developed even at room temperature by blending the respective components described above, but it is preferred from the viewpoint of a stability of the pressure-sensitive adhesive strength to apply the above pressure-sensitive adhesive on a release sheet or a substrate sheet described later, stick both together and then heat or irradiate it with an active energy beam to accelerate cross-linking reaction of the silicone resin component with the silicone rubber component by the cross-linking agent.
• the energy beam means beams having an energy quantum among electromagnetic waves and charged particle beams, that is, an active light such as a UV ray or an electron beam.
• an active light such as a UV ray or an electron beam.
• a photopolymerization initiator is not required, but when cross-linking is carried out by irradiating with an active light such as a UV ray, a photopolymerization initiator is preferably allowed to be present.
• the photopolymerization initiator used when irradiated with a UV ray shall not specifically be restricted, and optional photopolymerization initiators suitably selected from photopolymerization initiators which have so far been conventionally used for UV ray-curing type resins can be used.
• the photopolymerization initiator includes, for example, benzoins, benzophenones, acetophenones, ⁇ -hydroxyketones, ⁇ -aminoketones, ⁇ -diketones, ⁇ -diketonedialkylacetals, anthraquinones, thioxanthones and other compounds.
• the photopolymerization initiators may be used alone or in combination of two or more kinds thereof.
• a use amount thereof is selected in a range of usually 0.01 to 30 parts by mass, preferably 0.05 to 20 parts by mass based on 100 parts by mass of the total amount of the addition reaction type silicone component which is used as a base resin and the cross-linking agent each described above.
• the protective sheet for a coating layer having a stable adhesive strength is obtained by heating or irradiating with an active energy beam for cross-linking.
• the pressure-sensitive adhesive on the release sheet After applying the pressure-sensitive adhesive on the release sheet, it may be stuck together with the substrate sheet, or after applying the pressure-sensitive adhesive on the substrate sheet, it may be stuck together with the release sheet.
• a polyethylene terephthalate sheet Used as the substrate sheet are a polyethylene terephthalate sheet, a polyethylene naphthalate sheet, a polyimide sheet, a polyetherimide sheet, a polyaramide sheet, a polyetherketone sheet, a polyether-etherketone sheet, a polyphenylene sulfide sheet, a poly(4-methylpentene-1) sheet and the like.
• Polyethylene terephthalate and polyethylene naphthalate are preferred from the viewpoints of a heat resistance, a dimensional stability and an economical efficiency.
• a thickness of the substrate sheet is somewhat different depending on a material used, and it is usually 5 to 300 ⁇ m, preferably 10 to 100 ⁇ m. In the case of a polyethylene terephthalate sheet which is one of the preferred substrate sheets, the thickness is 10 to 50 ⁇ m.
• the pressure-sensitive adhesive can be applied on the release sheet or the substrate sheet by a gravure coating method, a bar coating method, a spray coating method, a spin coating method, a roll coating method, a die coating method, a knife coating method, an air knife coating method, a hot melt coating method, a curtain coating method and the like which are usually carried out.
• a thickness of the pressure-sensitive adhesive layer after drying which is formed on the release sheet or the substrate sheet is usually 1 to 50 ⁇ m, preferably 5 to 40 ⁇ m. Controlling a thickness of the pressure-sensitive adhesive layer to 1 ⁇ m or more makes it possible to secure an adhesive strength and a cohesion (holding power) which are required to the protective sheet for a coating layer, and controlling it to 50 ⁇ m or less avoids an increase in the cost and prevents the pressure-sensitive adhesive layer from protruding beyond the edges.
• the pressure-sensitive adhesive layer is formed on the release sheet or the substrate sheet to superpose both together, and then it is heated or irradiated with an energy beam as described above to cross-link the silicone resin component with the silicone rubber component, whereby it can be provided with a stable adhesive strength.
• the heating temperature in accelerating cross-linking by heating is usually 60 to 140° C., preferably 80 to 130° C. Heating at 60° C. or higher prevents the pressure-sensitive adhesive strength from being unsatisfactory due to insufficient cross-linking of the silicone resin component with the silicone rubber component, and heating at 140° C. or lower prevents thermal shrinkage from being brought about on the substrate sheet and prevents the pressure-sensitive adhesive deterioration and discoloration from taking place.
• An accelerating voltage of an electron beam in carrying out cross-linking by irradiating with an electron beam which is one of active energy beams is usually 130 to 300 kV, preferably 150 to 250 kV. Irradiation at an accelerating voltage of 130 kV or more makes it possible to prevent the adhesive strength from being unsatisfactory due to insufficient cross-linking of the silicone resin component with the silicone rubber component, and irradiation at an accelerating voltage of 300 kV or less makes it possible to prevent the pressure-sensitive adhesive layer and the substrate sheet from being deteriorated or discolored.
• the preferred range of the beam current is 1 to 100 mA.
• a dosage of the electron beam to be irradiated is preferably 1 to 70 Mrad, more preferably 2 to 20 Mrad. Irradiation at a dosage of 1 Mrad or more makes it possible to prevent the pressure-sensitive adhesive layer and the substrate sheet from being deteriorated or discolored and prevent the pressure-sensitive adhesiveness from being unsatisfactory due to insufficient cross-linking. Irradiation at a dosage of 70 Mrad or less makes it possible to prevent the cohesion from being reduced by deterioration or discoloration of the pressure-sensitive adhesive layer and prevent the substrate sheet from being deteriorated or shrunk.
• a dosage in the case of irradiating with a UV ray is suitably selected.
• a light quantity thereof is 100 to 500 mJ/cm 2
• an illuminance thereof is 10 to 500 mW/cm 2 .
• Heating and irradiation with an active energy beam are preferably carried out under nitrogen atmosphere in order to prevent the reaction from being disturbed by oxygen.
• the stable adhesive strength is provided by heating or irradiating with an active energy beam to cross-link the silicone resin component with the silicone rubber component.
• the substrate sheet is preferably subjected to corona discharge treatment and/or ozone treatment before the substrate sheet is superposed onto the surface of the pressure-sensitive adhesive layer applied on the release sheet or before applying the pressure-sensitive adhesive on the substrate sheet in order to strengthen a close adhesiveness between the pressure-sensitive adhesive layer and the substrate sheet from the viewpoint of preventing the “adhesive deposit” phenomenon that the pressure-sensitive adhesive layer is partially transferred onto the coating layer when stripping the protective sheet for a coating layer according to the present invention from coated surfaces of car bodies and parts of automobiles.
• release sheet Capable of being used as the release sheet are resin films of polyethylene terephthalate, polyethylene, polypropylene and the like which are coated with a releasing agent such as a fluorine-based resin, a silicone-based resin, a long chain alkyl group-containing carbamate and the like.
• a releasing agent such as a fluorine-based resin, a silicone-based resin, a long chain alkyl group-containing carbamate and the like.
• a thickness of the release sheet is somewhat different depending on the materials used, and it is usually 10 to 250 ⁇ m, preferably 20 to 200 ⁇ m.
• Used as the addition reaction type silicone-based adhesive was a solution prepared by diluting with 100 parts by mass of toluene, a solution containing 100 parts by mass of SD4585PSA (addition reaction type silicone containing a cross-linking agent) manufactured by Dow Corning Toray Co., Ltd. and 0.9 part by mass of SRX-212 manufactured by Dow Corning Toray Co., Ltd. which was a platinum-based curing catalyst.
• the solution described above was applied on the surface of the substrate sheet described above by a knife coating method so that a thickness after drying was 30 ⁇ m and dried at 130° C. for 5 minutes, and then the substrate sheet was stuck together with a fluororesin-coated surface of the release sheet described above to prepare a protective sheet for a coating layer.
• Used as the addition reaction type silicone-based adhesive was a solution prepared by diluting with 100 parts by mass of toluene, a solution containing 100 parts by mass of SD4585PSA (an addition reaction type silicone containing a cross-linking agent) manufactured by Dow Corning Toray Co., Ltd., 10 parts by mass of SD4587LPSA (an addition reaction type silicone containing a cross-linking agent) manufactured by Dow Corning Toray Co., Ltd. and 1 part by mass of SRX-212 manufactured by Dow Corning Toray Co., Ltd. which was a platinum-based curing catalyst.
• the solution described above was applied on the surface of the substrate sheet described above by a knife coating method so that a thickness after drying was 30 ⁇ m and dried at 130° C. for 5 minutes, and then a layer side which was a pressure-sensitive adhesive layer was irradiated with an electron beam at an accelerating voltage of 200 kV, a beam current of 20 mA and a dosage of 5 Mrad under nitrogen atmosphere. Then, the substrate sheet was stuck together with a fluororesin-coated surface of the release sheet described above to prepare a protective sheet for a coating layer.
• a protective sheet for a coating layer was prepared in the same manner as in Example 1, except that a polyethylene terephthalate film “PET25T Q37 manufactured by Toray Industries, Inc.” having a thickness of 25 ⁇ m which contains a UV absorbent was used as a substrate sheet.
• a polyethylene film (trade name: PE Wadatoumei 50ASKAI4, manufactured by J-Film Corporation) having a thickness of 50 ⁇ m which contains an antistatic agent was used as a substrate sheet for the protective sheet, and a polyethylene terephthalate film (SP-PET3801, manufactured by Lintec Corporation) having a thickness of 38 ⁇ m which was coated with a silicone resin was used as a release sheet.
• Used as pressure-sensitive adhesive was a solution prepared by mixing 100 parts by mass of an acrylic-based pressure-sensitive adhesive obtained by diluting a butyl acrylate-acrylic acid copolymer (butyl acrylate/acrylic acid mole ratio: 10/1) having a weight average molecular weight of 600,000 to 30% by mass with ethyl acetate and 5 parts by mass of a 5% by mass ethyl acetate solution of 1,3-bis(N,N-diglycidylaminomethyl)cyclohexane as a cross-linking agent.
• a butyl acrylate-acrylic acid copolymer butyl acrylate/acrylic acid mole ratio: 10/1 having a weight average molecular weight of 600,000 to 30% by mass with ethyl acetate and 5 parts by mass of a 5% by mass ethyl acetate solution of 1,3-bis(N,N-diglycidylaminomethyl)cyclohexane as
• the above solution was applied on a silicone resin-coated surface of the release sheet described above by a knife coating method so that a thickness after drying was 20 ⁇ m and dried at 90° C. for 3 minutes, and then the release sheet was stuck together with the substrate sheet described above to prepare a protective sheet for comparison.
• a protective sheet for comparison was prepared in the same manner as in Comparative Example 1, except that used as a pressure-sensitive adhesive was a solution obtained by diluting a rubber base pressure-sensitive adhesive comprising a polyisobutylene having a viscosity average molecular weight of 800,000 to 30% by mass with toluene and that the cross-linking agent was not used.
• a double liquid type polyurethane-based top coating material for automobiles (prepared by mixing 100 parts by mass of Rock Multi Top Clear SF-150-5150 with 50 parts by mass of Rock Multi Top Clear S curing agent standard 150-5120 each manufactured by Rock Paint Co., Ltd.) was sprayed in a thickness of about 1 ⁇ m on a plate of a polyolefin base thermosetting elastomer on which an electrodepositing primer and an intermediate coating material were applied. It was dried at 60° C. for 10 minutes and left standing at room temperature for 30 minutes, and then the respective protective sheets obtained in the examples and the comparative examples which were cut into a tape shape were adhered on the coating layer. The sheets of a tape shape which were adhered on the coated surfaces with wrinkled parts were left standing at room temperature for 24 hours and then peeled, and the states of the coating layer were visually observed to evaluate the respective characteristics according to the following criteria.
• Step can be confirmed, and a vertical interval of stepping is 0.3 to 1 ⁇ m
• Step can be confirmed, and a vertical interval of stepping is 1 ⁇ m or more
• ⁇ Whitening can be confirmed but can not be confirmed after left standing outdoors for one week.
• X Whitening can be confirmed and can be still confirmed even after left standing outdoors for one week.
• Adhesive deposit can not be confirmed on the coated surface.
• Adhesive deposit can slightly be confirmed on the coated surface.
• Adhesive deposit can notably be confirmed on the coated surface.
• the protective sheet for a coating layer according to the present invention can be applied as well to a coating layer of a urethane-based coating material which is insufficiently cured, and in particular, it can suitably be used as a protective sheet for coated plastic-made parts such as bumpers and the like.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Wood Science & Technology (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Life Sciences & Earth Sciences (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Adhesive Tapes (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Laminated Bodies (AREA)
• Surface Treatment Of Glass (AREA)

Applications Claiming Priority (3)

Related Parent Applications (1)

Related Child Applications (1)

Publications (1)

Family

ID=38459057

Family Applications (2)

Family Applications After (1)

Country Status (8)

Families Citing this family (10)

Citations (2)

Family Cites Families (21)

• 2006
  • 2006-02-28 JP JP2006053907A patent/JP4953659B2/ja not_active Expired - Fee Related
• 2007
  • 2007-02-27 AU AU2007219431A patent/AU2007219431A1/en not_active Abandoned
  • 2007-02-27 CN CN2007800060104A patent/CN101384683B/zh not_active Expired - Fee Related
  • 2007-02-27 CA CA2643119A patent/CA2643119C/fr not_active Expired - Fee Related
  • 2007-02-27 WO PCT/JP2007/053637 patent/WO2007099952A1/fr active Application Filing
  • 2007-02-27 EP EP07737439A patent/EP1990391A4/fr not_active Withdrawn
  • 2007-02-27 US US12/280,992 patent/US20090068457A1/en not_active Abandoned
  • 2007-02-27 KR KR1020087020043A patent/KR101379134B1/ko not_active IP Right Cessation
• 2011
  • 2011-07-27 US US13/192,157 patent/US8574395B2/en not_active Expired - Fee Related

Patent Citations (3)

Also Published As

Similar Documents

Legal Events