US20060134343A1 - Thermal spraying powder, thermal spraying method, and method for forming thermal spray coating - Google Patents
Thermal spraying powder, thermal spraying method, and method for forming thermal spray coating Download PDFInfo
- Publication number
- US20060134343A1 US20060134343A1 US11/311,217 US31121705A US2006134343A1 US 20060134343 A1 US20060134343 A1 US 20060134343A1 US 31121705 A US31121705 A US 31121705A US 2006134343 A1 US2006134343 A1 US 2006134343A1
- Authority
- US
- United States
- Prior art keywords
- thermal spraying
- spraying powder
- thermal
- less
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
- C23C4/06—Metallic material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
- C23C4/12—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the method of spraying
Definitions
- the present invention relates to a thermal spraying powder, a thermal spraying method, and a method for forming a thermal spray coating.
- thermal spray coating is formed by spraying, to base material, thermal spraying material that has been heated to be softened or molten. Therefore, the surface of the thermal spray coating is inherently not smooth but rough. Thus, in a case where a surface is required to be smooth, the thermal spray coating is polished until a target surface roughness is achieved.
- the thermal spray coating having the above mentioned useful properties generally has a high hardness, polishing of the thermal spray coating is not easy in many cases.
- the thermal spray coating formed by spraying a cermet containing tungsten carbide and metal
- the thermal spray coating must be polished using diamond abrasive grain, which increases manufacturing costs. Therefore, there is a demand for a technique for forming the thermal spray coating having a small surface roughness, which omits or simplifies the polishing after thermal spraying.
- the thermal spray coating is inherently porous, and may include through holes that extend through the thermal spray coating from the base material to the surface of the thermal spray coating.
- the thermal spray coating is required to include no through holes depending on the use such as when the thermal spray coating is provided to prevent corrosion of the base material.
- the thermal spray coating is formed thick.
- the cost of the thermal spray coating is increased.
- the thickness of the thermal spray coating is desired to be as small as possible. Therefore, there is a demand for a technique for forming a thin thermal spray coating that includes no through holes.
- a method for closing the through holes by sealing has been proposed to prevent through holes.
- the costs are increased in this case also since the manufacturing process is increased.
- the thermal spray coating may be formed from a fine thermal spraying powder.
- fine thermal spraying powder When fine thermal spraying powder is sprayed, a dense thermal spray coating the surface roughness of which is small and that does not include through holes is obtained.
- supply of the thermal spraying powder from a powder feeder to a spray gun could become unstable. This is because as the thermal spraying powder becomes finer, the flowability of the thermal spraying powder is decreased. For example, when pulsation occurs while feeding the thermal spraying powder, the quality of the thermal spray coating is significantly decreased.
- the thermal spraying powder forms a bridge (powder bridging)
- the thermal spraying powder is not smoothly supplied to the spray gun, and the supply of the thermal spraying powder may be stopped in some cases.
- Japanese Laid-Open Patent Publication No. 2003-129212 discloses a technique for forming a thermal spray coating from a thermal spraying powder having 90% particle size D 90 of 20 ⁇ m or less.
- the thermal spraying powder of the above publication since the ratio of particles having a particle size of 1 ⁇ m or less in the thermal spraying powder is not specified, the thermal spraying powder could include a large amount of particles having a particle size of 1 ⁇ m or less. If the thermal spraying powder includes many particles having a particle size of 1 ⁇ m or less, in addition to decreasing the flowability of the thermal spraying powder, flocculation of the thermal spraying powder is likely to occur. If the thermal spraying powder that has been flocculated is mixed in the thermal spray coating, uniformity and density of the thermal spray coating may be decreased, through holes may be formed in the thermal spray coating, or the surface roughness of the thermal spray coating may be increased.
- thermal spraying powder that reliably forms a dense thermal spray coating with a low surface roughness. It is also an objective of the present invention to provide a thermal spraying method using the thermal spraying powder, and a method for forming a thermal spray coating using the thermal spraying powder.
- a thermal spraying powder in which 90% particle size D90 of the thermal spraying powder is 15 ⁇ m or less, and the ratio of the total volume of particles having a particle size of 1 ⁇ m or less to the total volume of all particles in the thermal spraying powder is 2% or less.
- the present invention also provides a thermal spraying method including spraying the above thermal spraying powder.
- the present invention provides a method for forming a thermal spray coating including spraying the above thermal spraying powder.
- the thermal spraying powder of the preferred embodiment is a granulated and sintered powder of cermet.
- Particles of the thermal spraying powder are composed of tungsten carbide and at least one of cobalt, chromium, and nickel.
- the content of tungsten carbide, which is a ceramic component in the thermal spraying powder is greater than 92% by mass, in other words when the total content of cobalt, chromium, and nickel, which are metal components in the thermal spraying powder, is less than 8% by mass, the brittleness of the thermal spray coating formed of the thermal spraying powder is increased and there is a risk that the thermal spray coating does not have a high wear resistance. Therefore, the content of the ceramic component in the thermal spraying powder is preferably 92% by mass or less, and the content of the metal components in the thermal spraying powder is preferably 8% by mass or more.
- 90% particle size D 90 of the thermal spraying powder is greater than 15 ⁇ m (that is, when the ratio of the total volume of particles having a particle size of 15 ⁇ m or less to the total volume of all particles in the thermal spraying powder is less than 90%), it is difficult to form the thermal spray coating that is dense and has a small surface roughness from the thermal spraying powder since particles having a particle size of greater than 15 ⁇ m are included in the thermal spraying powder by a large amount. Therefore, the 90% particle size D 90 of the thermal spraying powder must be 15 ⁇ m or less (that is, the ratio of the total volume of particles having a particle size of 15 ⁇ m or less must be 90% or more).
- the 90% particle size D 90 of the thermal spraying powder is 15 ⁇ m or less, if it is greater than 13 ⁇ m (that is, if the ratio of the total volume of particles having a particle size of 13 ⁇ m or less to the total volume of all particles in the thermal spraying powder is less than 90%), the surface roughness and the density of the thermal spray coating formed of the thermal spraying powder are not significantly improved. Therefore, the 90% particle size D 90 of the thermal spraying powder is preferably 13 ⁇ m or less (the ratio of the total volume of particles having a particle size of 13 ⁇ m or less is preferably 90% or more).
- the 90% particle size D 90 of the thermal spraying powder is less than 5 ⁇ m (that is, when the ratio of the total volume of particles having a particle size of 5 ⁇ m or less to the total volume of all particles in the thermal spraying powder is greater than 90%), and more specifically less than 7 ⁇ m (that is, when the ratio of the total volume of particles having a particle size of 7 ⁇ m or less to the total volume of all particles in the thermal spraying powder is greater than 90%), the flowability of the thermal spraying powder is slightly decreased since particles having a particle size of 5 ⁇ m (or 7 ⁇ m) or less is included in the thermal spraying powder by a large amount.
- the 90% particle size D 90 of the thermal spraying powder is preferably 5 ⁇ m or more (the ratio of the total volume of particles having a particle size of 5 ⁇ m or less is preferably 90% or less), and the 90% particle size D 90 of the thermal spraying powder is more preferably 7 ⁇ m or more (the ratio of the total volume of particles having a particle size of 7 ⁇ m or less is more preferably 90% or less).
- the ratio of the total volume of particles having a particle size of 1 ⁇ m or less to the total volume of all particles in the thermal spraying powder is greater than 2% (that is, when 2% particle size D 2 of the thermal spraying powder is less than 1 ⁇ m)
- the flowability of the thermal spraying powder is significantly decreased since particles having a particle size of 1 ⁇ m or less is included in the thermal spraying powder by a large amount.
- supply of the thermal spraying powder from the powder feeder to the spray gun during spraying becomes unstable.
- flocculation of the thermal spraying powder may occur, thereby decreasing the uniformity and the density of the thermal spray coating, generating through holes in the thermal spray coating, or increasing the surface roughness of the thermal spray coating.
- the ratio of the total volume of particles having a particle size of 1 ⁇ m or less must be 2% or less (that is, the 2% particle size D 2 of the thermal spraying powder must be 1 ⁇ m or more).
- the ratio of the accumulated volume of particles having a particle size of 1 ⁇ m or less is 2% or less, if it is greater than 1.5% (that is, if 1.5% particle size D 1.5 of the thermal spraying powder is less than 1 ⁇ m)
- the stability of supplying the thermal spraying powder while spraying is not significantly improved. Therefore, the ratio of the total volume of particles having a particle size of 1 ⁇ m or less is preferably 1.5% or less (that is, the 1.5% particle size D 1.5 of the thermal spraying powder is preferably 1 ⁇ m or less).
- the particle size dispersion index of the thermal spraying powder is greater than 0.7, and more specifically greater than 0.67, the flowability of the thermal spraying powder is slightly decreased since the proportion of particles having a small particle size in the thermal spraying powder is increased.
- the particle size dispersion index of the thermal spraying powder is preferably 0.7 or less, and more preferably 0.67 or less.
- the value obtained by dividing the bulk density of the thermal spraying powder by the theoretical density of material forming the thermal spraying powder is preferably 0.15 or more, and more preferably 0.17 or more.
- a method for manufacturing the thermal spraying powder of the preferred embodiment that is, a method for manufacturing the granulated and sintered cermet powder composed of tungsten carbide and at least one of cobalt, chromium, and nickel will now be described.
- a metal powder consisting of at least one of cobalt, chromium, and nickel and tungsten carbide powder are mixed in a dispersion medium to prepare slurry.
- An appropriate binder may be added to the slurry.
- granulated powder is formed from the slurry using a roll granulator, a spray granulator, or a compression granulator.
- granulated powder is sintered, then crushed and classified to manufacture the granulated and sintered cermet powder composed of tungsten carbide and at least one of cobalt, chromium, and nickel.
- the sintering of the granulated powder may be performed either in vacuum or an inert gas atmosphere, and either an electric furnace or a gas furnace may be used.
- the thermal spraying powder of the preferred embodiment is used for forming the thermal spray coating through, for example, high-velocity flame spraying.
- the thermal spray coating formed of the thermal spraying powder of the preferred embodiment through high-velocity flame spraying has a sufficient wear resistance.
- a high-velocity flame spray gun that is capable of spraying the thermal spraying powder of this embodiment in a suitable manner includes high-output type high-velocity flame spray gun such as “JP-5000” manufactured by Praxair/TAFA and “Diamond jet (hybrid type)” manufactured by Sulzer Metco, and “ ⁇ -Gun” manufactured by WHITCO JAPAN Corporation.
- the preferred embodiment has the following advantages.
- the thermal spray coating that is dense and has a small surface roughness is formed using the thermal spraying powder of this embodiment.
- the thermal spray coating is reliably formed using the thermal spraying powder of this embodiment.
- the thermal spraying powder of this embodiment further reliably prevents the stability of supplying the thermal spraying powder while spraying from decreasing and the density of the thermal spray coating formed of the thermal spraying powder from decreasing.
- the thermal spraying powder of this embodiment suppresses problems caused by irregular sizes of particles in the thermal spraying powder.
- the granulated and sintered powder generally has sufficient flowability and less risk of contamination by impurities during a manufacturing process as compared to a fused and crushed powder and a sintered and crushed powder. Therefore, the thermal spraying powder of this embodiment consisting of the granulated and sintered powder has the same advantages.
- the particles in the thermal spraying powder of this embodiment consist of cermet. Therefore, the thermal spray coating having a sufficient wear resistance is formed using the thermal spraying powder of this embodiment.
- the preferred embodiment may be modified as follows.
- the particles in the thermal spraying powder may further include ceramics other than tungsten carbide such as chromium carbide instead of tungsten carbide or in addition to tungsten carbide.
- the particles in the thermal spraying powder may further include metal other than cobalt, chromium, and nickel instead of cobalt, chromium, and nickel or in addition to cobalt, chromium, and nickel.
- the thermal spraying powder may contain components other than the granulated and sintered powder of cermet composed of tungsten carbide and at least one of cobalt, chromium, and nickel.
- the content of the granulated and sintered powder in the thermal spraying powder is preferably 50% by mass or more, and more preferably 80% by mass or more.
- the thermal spraying powder may be a fused and crushed cermet powder or a sintered and crushed cermet powder instead of the granulated and sintered cermet powder.
- particles in the thermal spraying powder may or may not be composed of tungsten carbide and at least one of cobalt, chromium, and nickel.
- the fused and crushed powder is manufactured by melting a raw material powder and crushing and classifying the raw material powder after being cooled and solidified.
- the sintered and crushed powder is manufactured by sintering the raw material powder, and crushing and classifying the raw material powder.
- the thermal spraying powder of the preferred embodiment may be used for forming the thermal spray coating through a thermal spraying method other than the high-velocity flame spraying.
- examples 1 to 7 and comparative examples 1 to 4 granulated and sintered cermet powders containing 12% by weight of cobalt with the tungsten carbide as the main component were prepared as the thermal spraying powders.
- example 8 fused and crushed cermet powder composed of tungsten carbide and cobalt was prepared as the thermal spraying powder.
- example 9 and comparative example 5 granulated and sintered cermet powders containing 10% by weight of cobalt and 4% by weight of chromium with tungsten carbide as the main component were prepared as the thermal spraying powders. Specifics of the thermal spraying powders of examples 1 to 9 and comparative examples 1 to 5 are as shown in Table 1.
- the column entitled “Ratio of particles having particle size of 1 ⁇ m or less” in Table 1 shows the ratio of the total volume of particles having a particle size of 1 ⁇ m or less to the total volume of all particles in the thermal spraying powder. The ratio was measured using a laser diffraction/scattering type of particle size distribution measuring instrument “LA-300” manufactured by HORIBA Ltd.
- the columns entitled “10% particle size D 10 ”, “50% particle size D 50 ”, and “90% particle size D 90 ” in Table 1 show the 10% particle size D 10 , the 50% particle size D 50 , and the 90% particle size D 90 of the thermal spraying powders measured using the laser diffraction/scattering type of particle size distribution measuring instrument “LA-300” manufactured by HORIBA Ltd.
- the 10% particle size D 10 of the thermal spraying powder is the size of the particle that is lastly summed up when the volume of particles in the thermal spraying powder is accumulated from particles of the smallest size in ascending order until the accumulated volume reaches 10% of the total volume of all the particles in the thermal spraying powder.
- the 50% particle size D 50 of the thermal spraying powder is the size of the particle that is lastly summed up when the volume of particles in the thermal spraying powder is accumulated from particles of the smallest size in ascending order until the accumulated volume reaches 50% of the total volume of all the particles in the thermal spraying powder.
- the 90% particle size D 90 of the thermal spraying powder is the size of the particle that is lastly summed up when the volume of particles in the thermal spraying powder is accumulated from particles of the smallest size in ascending order until the accumulated volume reaches 90% of the total volume of all the particles in the thermal spraying powder.
- D 90 represents the 90% particle size of the thermal spraying powder
- D 10 represents the 10% particle size of the thermal spraying powder.
- the column entitled “Bulk density/theoretical density” in Table 1 shows values obtained by dividing the bulk density of each thermal spraying powder measured using a bulk specific gravity measuring instrument (refer to JIS Z2504) by the theoretical density of material forming the thermal spraying powder.
- the thermal spray coatings having a thickness of 200 ⁇ m were formed by high-velocity flame spraying of the thermal spraying powders according to examples 1 to 4, 6 to 9, and comparative examples 1 to 5 under a first spraying condition shown in Table 2 and high-velocity flame spraying of the thermal spraying powder according to example 5 under a second spraying condition shown in Table 2. Then, depending on whether the thermal spray coatings were formed, the thermal spraying powders were evaluated according to a two rank scale: good (1) and poor (2). That is, when the thermal spray coating was formed, the thermal spraying powder was ranked good, and when the supply of the thermal spraying powder from the powder feeder to the spray gun was stopped and the thermal spray coating was not formed, the thermal spraying powder was ranked poor. The evaluation results are shown in the column entitled “Formation of coating” in Table 1.
- the surface roughnesses Ra of any 15 spots on each of the thermal spray coatings formed by high-velocity flame spraying of the thermal spraying powders according to examples 1 to 9 and comparative examples 1 to 5 were measured under a condition shown in Table 3. Based on the average value of the surface roughnesses Ra of the measured 15 spots, the thermal spraying powders were evaluated according to a three rank scale: excellent (1), good (2), and poor (3). That is, when the average value of the surface roughnesses Ra was less than 1.3 ⁇ m, the thermal spraying powder was ranked excellent, when it was 1.3 ⁇ m or more and less than 1.6 ⁇ m, the thermal spraying powder was ranked good, and when it was 1.6 ⁇ m or more, the thermal spraying powder was ranked poor.
- the evaluation results are shown in the column entitled “Surface roughness of thermal spray coating before polishing” in table 1.
- the thermal spraying powders were evaluated according to a three rank scale: excellent (1), good (2), and poor (3). That is, when the standard deviation of the surface roughness Ra was less than 0.3, the thermal spraying powder was ranked excellent, when it was 0.3 or more and less than 0.45, the thermal spraying powder was ranked good, and when it was 0.45 or more, the thermal spraying powder was ranked poor.
- the evaluation results are shown in the column entitled “Variation of surface roughness” in Table 1.
- the surface roughnesses Ra of any 15 spots on each of the thermal spray coatings formed by high-velocity flame spraying of the thermal spraying powders according to examples 1 to 9 and comparative examples 1 to 5 were measured under the condition shown in Table 3 again after mirror polishing the thermal spray coatings. Based on the average value of the surface roughnesses Ra of the measured 15 spots, the thermal spraying powders were evaluated according to a three rank scale: excellent (1), good (2), and poor (3).
- the thermal spraying powder when the average value of the surface roughnesses Ra was less than 0.006 ⁇ m, the thermal spraying powder was ranked excellent, when it was 0.006 ⁇ m or more and less than 0.010 ⁇ m, the thermal spraying powder was ranked good, and when it was 0.010 ⁇ m or more, the thermal spraying powder was ranked poor.
- the evaluation results are shown in the column entitled “Surface roughness of thermal spray coating after polishing” in Table 1.
- the thermal spray coatings having a thickness of 50 ⁇ m formed on base materials by high-velocity flame spraying of the thermal spraying powders according to examples 1 to 9 and comparative examples 1 to 5 were subjected to a salt spray test (refer to JIS Z 2371). Thereafter, the base materials were visually checked to see whether red rust is generated. Based on generation of red rust after the salt spray test, the thermal spraying powders were evaluated according to a three rank scale: excellent (1), good (2), and poor (3).
- Base material SS400 steel plate
- Base material SS400 steel plate (7 cm ⁇ 5 cm ⁇ 2.3 mm, degreased (7 cm ⁇ 5 cm ⁇ 2.3 mm, degreased and surface roughened using an and surface roughened using an alumina grit #40) alumina grit #40)
- Spray gun “ ⁇ -Gun” manufactured Spray gun: “JP-5000” manu- by WHITCO JAPAN Corporation. factured by Praxair/TAFA Powder feeder: “AM-30” manu- Powder feeder: “AM-30” manu- factured by Technoserve Co. Ltd. factured by Technoserve Co. Ltd.
- Oxygen flow rate 1900 scfh
- Oxygen flow rate 1900 scfh Kerosene flow rate: 5.1 gph Kerosene flow rate: 5.1 gph Spraying distance: 250 mm Spraying distance: 380 mm Barrel length: 101.6 mm
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Plasma & Fusion (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Coating By Spraying Or Casting (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2004370262A JP4885445B2 (ja) | 2004-12-21 | 2004-12-21 | 溶射用粉末 |
JP2004-370262 | 2004-12-21 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20060134343A1 true US20060134343A1 (en) | 2006-06-22 |
Family
ID=36123340
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/311,217 Abandoned US20060134343A1 (en) | 2004-12-21 | 2005-12-19 | Thermal spraying powder, thermal spraying method, and method for forming thermal spray coating |
Country Status (5)
Country | Link |
---|---|
US (1) | US20060134343A1 (ja) |
EP (1) | EP1674589A2 (ja) |
JP (1) | JP4885445B2 (ja) |
KR (1) | KR101241244B1 (ja) |
CN (1) | CN1792469A (ja) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080226837A1 (en) * | 2006-10-02 | 2008-09-18 | Sulzer Metco Ag | Method for the manufacture of a coating having a columnar structure |
US20080245185A1 (en) * | 2006-09-12 | 2008-10-09 | Fujimi Incorporated | Thermal spray powder and thermal spray coating |
US20140241937A1 (en) * | 2011-07-25 | 2014-08-28 | Eckart Gmbh | Coating Method Using Special Powdered Coating Materials and Use of Such Coating Materials |
US20150329954A1 (en) * | 2012-12-18 | 2015-11-19 | Commissariat à l'énergie atomique et aux énergies alternatives | Process for coating a substrate with an abradable ceramic material, and coating thus obtained |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4586823B2 (ja) * | 2007-06-21 | 2010-11-24 | トヨタ自動車株式会社 | 成膜方法、伝熱部材、パワーモジュール、車両用インバータ、及び車両 |
JP2011017079A (ja) * | 2009-06-10 | 2011-01-27 | Fujimi Inc | 溶射用粉末及び溶射皮膜の形成方法 |
US20120308776A1 (en) * | 2009-11-27 | 2012-12-06 | Seiji Kuroda | Cermet coating, spraying particles for forming same, method for forming cermet coating, and coated article |
KR102106486B1 (ko) | 2018-07-25 | 2020-05-07 | 안동대학교 산학협력단 | 내열성, 내마모성 및 내부식성이 우수한 용사분말, 이를 이용하여 용사피막을 형성하는 방법 및 용사피막이 형성된 그레이트바 |
JP6683902B1 (ja) * | 2018-08-27 | 2020-04-22 | トーカロ株式会社 | 溶射皮膜の形成方法 |
CN114226713B (zh) * | 2021-12-17 | 2023-07-25 | 武汉苏泊尔炊具有限公司 | 热喷涂粉末及其制备方法、烹饪器具 |
Citations (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4865252A (en) * | 1988-05-11 | 1989-09-12 | The Perkin-Elmer Corporation | High velocity powder thermal spray gun and method |
US4925626A (en) * | 1989-04-13 | 1990-05-15 | Vidhu Anand | Method for producing a Wc-Co-Cr alloy suitable for use as a hard non-corrosive coating |
US5075129A (en) * | 1989-11-27 | 1991-12-24 | Union Carbide Coatings Service Technology Corporation | Method of producing tungsten chromium carbide-nickel coatings having particles containing three times by weight more chromium than tungsten |
US5098748A (en) * | 1988-01-29 | 1992-03-24 | Mazda Motor Corporation | Method of producing a flame-spray-coated article and flame spraying powder |
US5419976A (en) * | 1993-12-08 | 1995-05-30 | Dulin; Bruce E. | Thermal spray powder of tungsten carbide and chromium carbide |
US5580833A (en) * | 1994-10-11 | 1996-12-03 | Industrial Technology Research Institute | High performance ceramic composites containing tungsten carbide reinforced chromium carbide matrix |
US5747163A (en) * | 1993-09-03 | 1998-05-05 | Douglas; Richard M. | Powder for use in thermal spraying |
US5763106A (en) * | 1996-01-19 | 1998-06-09 | Hino Motors, Ltd. | Composite powder and method for forming a self-lubricating composite coating and self-lubricating components formed thereby |
US5789077A (en) * | 1994-06-27 | 1998-08-04 | Ebara Corporation | Method of forming carbide-base composite coatings, the composite coatings formed by that method, and members having thermally sprayed chromium carbide coatings |
US5928976A (en) * | 1996-05-21 | 1999-07-27 | Tokyo Tungsten Co., Ltd. | Composite carbide powder used for cemented carbide and method of producing the same |
US6004372A (en) * | 1999-01-28 | 1999-12-21 | Praxair S.T. Technology, Inc. | Thermal spray coating for gates and seats |
US6354704B2 (en) * | 1998-03-18 | 2002-03-12 | Asahi Kogaku Kogyo Kabushiki Kaisha | Progressive power spectacle lens |
US6410470B1 (en) * | 2000-04-24 | 2002-06-25 | Saint-Gobain Industrial Ceramics, Inc. | Thermal spray powder process |
US6482534B2 (en) * | 2000-02-17 | 2002-11-19 | Fujimi Incorporated | Spray powder, thermal spraying process using it, and sprayed coating |
US6596397B2 (en) * | 2001-04-06 | 2003-07-22 | Shin-Etsu Chemical Co., Ltd. | Thermal spray particles and sprayed components |
US6641917B2 (en) * | 2001-01-25 | 2003-11-04 | Fujimi Incorporated | Spray powder and method for its production |
US20040016557A1 (en) * | 2002-07-24 | 2004-01-29 | Keshavan Madapusi K. | Coarse carbide substrate cutting elements and method of forming the same |
US6916534B2 (en) * | 2001-03-08 | 2005-07-12 | Shin-Etsu Chemical Co., Ltd. | Thermal spray spherical particles, and sprayed components |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2585540B2 (ja) * | 1986-07-15 | 1997-02-26 | バブコツク日立株式会社 | 溶射方法 |
JPH0347957A (ja) * | 1989-07-14 | 1991-02-28 | Nippon Steel Corp | 低鉄損一方向性珪素鋼板の製造方法 |
JPH0586452A (ja) * | 1991-09-27 | 1993-04-06 | Kobe Steel Ltd | 溶射用粉末材料 |
JP3203442B2 (ja) * | 1992-12-18 | 2001-08-27 | 太平洋セメント株式会社 | 複合溶射材料および溶射皮膜とその製造方法 |
JPH08311635A (ja) * | 1995-05-12 | 1996-11-26 | Sumitomo Metal Mining Co Ltd | 高速粉末式フレーム溶射用タングステンカーバイト系サーメット粉末 |
JPH1088311A (ja) * | 1996-09-17 | 1998-04-07 | Showa Denko Kk | タングステンカーバイド/コバルト溶射粉末及びその製造方法 |
JP3172488B2 (ja) * | 1998-03-10 | 2001-06-04 | トーカロ株式会社 | 耐摩耗性に優れる軟質非鉄金属部材および軟質非鉄金属部材の表面改質方法 |
JP3523216B2 (ja) * | 2001-04-06 | 2004-04-26 | 信越化学工業株式会社 | 溶射用希土類含有化合物粒子、これを溶射した溶射部材 |
JP3672833B2 (ja) | 2000-06-29 | 2005-07-20 | 信越化学工業株式会社 | 溶射粉及び溶射被膜 |
JP4044348B2 (ja) * | 2001-03-08 | 2008-02-06 | 信越化学工業株式会社 | 溶射用球状粒子および溶射部材 |
JP4273292B2 (ja) * | 2001-04-06 | 2009-06-03 | 信越化学工業株式会社 | 溶射用粒子、および該粒子を用いた溶射部材 |
JP4628578B2 (ja) * | 2001-04-12 | 2011-02-09 | トーカロ株式会社 | 低温溶射皮膜被覆部材およびその製造方法 |
JP2003129212A (ja) * | 2001-10-15 | 2003-05-08 | Fujimi Inc | 溶射方法 |
JP4354176B2 (ja) * | 2002-11-19 | 2009-10-28 | Jfeスチール株式会社 | Wcサーメット溶射ロールおよびその製造方法 |
-
2004
- 2004-12-21 JP JP2004370262A patent/JP4885445B2/ja active Active
-
2005
- 2005-12-14 KR KR1020050123259A patent/KR101241244B1/ko active IP Right Grant
- 2005-12-19 US US11/311,217 patent/US20060134343A1/en not_active Abandoned
- 2005-12-20 CN CNA2005101339593A patent/CN1792469A/zh active Pending
- 2005-12-20 EP EP05027976A patent/EP1674589A2/en not_active Withdrawn
Patent Citations (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5098748A (en) * | 1988-01-29 | 1992-03-24 | Mazda Motor Corporation | Method of producing a flame-spray-coated article and flame spraying powder |
US4865252A (en) * | 1988-05-11 | 1989-09-12 | The Perkin-Elmer Corporation | High velocity powder thermal spray gun and method |
US4925626A (en) * | 1989-04-13 | 1990-05-15 | Vidhu Anand | Method for producing a Wc-Co-Cr alloy suitable for use as a hard non-corrosive coating |
US5075129A (en) * | 1989-11-27 | 1991-12-24 | Union Carbide Coatings Service Technology Corporation | Method of producing tungsten chromium carbide-nickel coatings having particles containing three times by weight more chromium than tungsten |
US5747163A (en) * | 1993-09-03 | 1998-05-05 | Douglas; Richard M. | Powder for use in thermal spraying |
US5419976A (en) * | 1993-12-08 | 1995-05-30 | Dulin; Bruce E. | Thermal spray powder of tungsten carbide and chromium carbide |
US5789077A (en) * | 1994-06-27 | 1998-08-04 | Ebara Corporation | Method of forming carbide-base composite coatings, the composite coatings formed by that method, and members having thermally sprayed chromium carbide coatings |
US5580833A (en) * | 1994-10-11 | 1996-12-03 | Industrial Technology Research Institute | High performance ceramic composites containing tungsten carbide reinforced chromium carbide matrix |
US5763106A (en) * | 1996-01-19 | 1998-06-09 | Hino Motors, Ltd. | Composite powder and method for forming a self-lubricating composite coating and self-lubricating components formed thereby |
US5928976A (en) * | 1996-05-21 | 1999-07-27 | Tokyo Tungsten Co., Ltd. | Composite carbide powder used for cemented carbide and method of producing the same |
US6354704B2 (en) * | 1998-03-18 | 2002-03-12 | Asahi Kogaku Kogyo Kabushiki Kaisha | Progressive power spectacle lens |
US6004372A (en) * | 1999-01-28 | 1999-12-21 | Praxair S.T. Technology, Inc. | Thermal spray coating for gates and seats |
US6482534B2 (en) * | 2000-02-17 | 2002-11-19 | Fujimi Incorporated | Spray powder, thermal spraying process using it, and sprayed coating |
US6410470B1 (en) * | 2000-04-24 | 2002-06-25 | Saint-Gobain Industrial Ceramics, Inc. | Thermal spray powder process |
US6641917B2 (en) * | 2001-01-25 | 2003-11-04 | Fujimi Incorporated | Spray powder and method for its production |
US6916534B2 (en) * | 2001-03-08 | 2005-07-12 | Shin-Etsu Chemical Co., Ltd. | Thermal spray spherical particles, and sprayed components |
US6596397B2 (en) * | 2001-04-06 | 2003-07-22 | Shin-Etsu Chemical Co., Ltd. | Thermal spray particles and sprayed components |
US20040016557A1 (en) * | 2002-07-24 | 2004-01-29 | Keshavan Madapusi K. | Coarse carbide substrate cutting elements and method of forming the same |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080245185A1 (en) * | 2006-09-12 | 2008-10-09 | Fujimi Incorporated | Thermal spray powder and thermal spray coating |
US8066795B2 (en) * | 2006-09-12 | 2011-11-29 | Fujimi Incorporated | Thermal spray powder and thermal spray coating |
US20080226837A1 (en) * | 2006-10-02 | 2008-09-18 | Sulzer Metco Ag | Method for the manufacture of a coating having a columnar structure |
US20140241937A1 (en) * | 2011-07-25 | 2014-08-28 | Eckart Gmbh | Coating Method Using Special Powdered Coating Materials and Use of Such Coating Materials |
US9580787B2 (en) * | 2011-07-25 | 2017-02-28 | Eckart Gmbh | Coating method using special powdered coating materials and use of such coating materials |
EP2737101B1 (de) * | 2011-07-25 | 2018-11-14 | Eckart GmbH | Beschichtungsverfahren nutzend spezielle pulverförmige beschichtungsmaterialien und verwendung derartiger beschichtungsmaterialien |
US20150329954A1 (en) * | 2012-12-18 | 2015-11-19 | Commissariat à l'énergie atomique et aux énergies alternatives | Process for coating a substrate with an abradable ceramic material, and coating thus obtained |
Also Published As
Publication number | Publication date |
---|---|
CN1792469A (zh) | 2006-06-28 |
JP2006176818A (ja) | 2006-07-06 |
KR20060071320A (ko) | 2006-06-26 |
JP4885445B2 (ja) | 2012-02-29 |
KR101241244B1 (ko) | 2013-03-14 |
EP1674589A2 (en) | 2006-06-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20060134343A1 (en) | Thermal spraying powder, thermal spraying method, and method for forming thermal spray coating | |
EP1485220B1 (en) | Corrosion resistant powder and coating | |
US6641917B2 (en) | Spray powder and method for its production | |
US8066795B2 (en) | Thermal spray powder and thermal spray coating | |
US7670406B2 (en) | Deposition system, method and materials for composite coatings | |
US7279221B2 (en) | Thermal spraying powder | |
CA2567089C (en) | Wear resistant alloy powders and coatings | |
KR20080087740A (ko) | 용사분말, 용사코팅 및 허스롤 | |
EP2505689A1 (en) | Cermet coating, spraying particles for forming same, method for forming cermet coating, and article with coating | |
US20120042807A1 (en) | Powder for thermal spraying and method for forming thermal-spray deposit | |
JP6683902B1 (ja) | 溶射皮膜の形成方法 | |
JP2013136814A (ja) | セラミック溶射皮膜及びその製造方法 | |
JP3917425B2 (ja) | 改良された溶射粉末の製造方法 | |
CN1174247A (zh) | 碳化钨基硬质合金喷焊(涂)粉及其生产工艺 | |
US4678511A (en) | Spray micropellets | |
JP3410025B2 (ja) | 炭化物サーメット溶射被覆部材およびその部材の製造方法 | |
KR20200136643A (ko) | 슬러리를 이용한 용사코팅 방법 및 이를 사용하여 제조된 코팅체 | |
JPH0261050A (ja) | 耐摩耗性被膜の形成方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: FUJIMI INCORPORATED, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KATO, NOBUAKI;OSAWA, SATORU;ITSUKAICHI, TSUYOSHI;REEL/FRAME:017169/0066 Effective date: 20051214 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |