TWI833054B - 用於介電應用的聚合物樹脂 - Google Patents
用於介電應用的聚合物樹脂 Download PDFInfo
- Publication number
- TWI833054B TWI833054B TW109144015A TW109144015A TWI833054B TW I833054 B TWI833054 B TW I833054B TW 109144015 A TW109144015 A TW 109144015A TW 109144015 A TW109144015 A TW 109144015A TW I833054 B TWI833054 B TW I833054B
- Authority
- TW
- Taiwan
- Prior art keywords
- group
- mol
- substituted
- polymer
- alkyl
- Prior art date
Abstract
提供了一種聚合物，其係來自混合物的共聚產物，該混合物包含：（a）10 mol%-50 mol%的至少一種可加成聚合的芳基環丁烯單體；（b）15 mol%-50 mol%的至少一種可加成聚合的二烯單體；以及（c）15 mol%-60 mol%的至少一種可加成聚合的芳香族乙烯基單體。該聚合物可以用於電子應用。
Description
本揭露關於聚合物樹脂組成物、製備此類樹脂之方法以及在製造電子器件中之用途。
聚合物樹脂被用於旋塗介電封裝、電路板、層壓板和其他電子應用中。該樹脂需要提供具有良好機械特性和良好黏附特性以及低介電特性的膜/塗層。特別地，希望具有高的拉伸強度、高的拉伸伸長率、與銅的良好黏附性、以及在高頻率下低的相對電容率（Dk）和損耗正切（Df）。另外，希望能夠在較低的溫度下固化樹脂而不需要過多的固化時間。
持續需要具有改進特性的介電樹脂組成物。
以下已經描述了許多方面和實施方式，並且該等方面和實施方式僅僅是示例性的而非限制性的。在閱讀本說明書之後，所屬領域的技術人員應瞭解，在不脫離本揭露的範圍的情況下，其他方面和實施方式係可能的。
如本說明書通篇所使用的，除非上下文另有明確指示，否則以下縮寫應具有以下含義：°C = 攝氏度；g = 克；nm = 奈米，µm = 微米；mm = 毫米；sec. = 秒；並且min. = 分鐘。除非另外指出，否則所有量係重量百分比（「wt.%」）並且所有比率係莫耳比。所有數值範圍皆為包含端值的，並且可以按任何順序組合，除了顯然此數值範圍被限制為加起來最高達100%的情況之外。除非另外指出，否則所有聚合物和低聚物的分子量均為以g/mol或道耳頓為單位的重量平均分子量（「Mw」），並且是使用凝膠滲透層析法與聚苯乙烯標準品進行比較而確定的。
除非上下文另有明確指示，否則冠詞「一」、「一個/種」和「該（the）」係指單數和複數。如本文使用的，術語「和/或」包括相關項中的一個或多個的任何和全部組合。
如本文使用的，R、Ra
、Rb
、R’、R’’和任何其他變數為通用命名並且可以與式中所定義的那些相同或不同。
如本文使用的，當應用於單體時，術語「可加成聚合的」旨在意指能夠藉由簡單連接基團而不共同產生其他產物而聚合的不飽和單體。
術語「相鄰」在其關於取代基時係指鍵合到用單鍵或多鍵連接在一起的碳上的基團。以下示出示例性相鄰R基團：
術語「烷氧基」旨在係指基團RO-，其中R係烷基。
術語「烷基」旨在意指衍生自脂肪族烴的基團並且包括直鏈、支鏈、或環狀基團。「衍生自」化合物的基團指示藉由除去一個或多個氫或氘形成的基團。在一些實施方式中，烷基具有1至20個碳原子。
術語「芳香族化合物」旨在意指包含至少一個具有4n+2非定域π電子的不飽和環狀基團的有機化合物。
術語「芳基」旨在意指衍生自具有一個或多個連接點的芳香族化合物的基團。該術語包括具有單環的基團以及具有可以藉由單鍵連接或稠合在一起的多個環的基團。碳環芳基在環結構中僅具有碳。雜芳基在環結構中具有至少一個雜原子。
術語「烷芳基」旨在意指具有一個或多個烷基取代基的芳基。
術語「芳氧基」旨在意指基團RO-，其中R係芳基。
當應用於組成物時，術語「可固化」旨在意指當暴露於輻射和/或熱或在使用條件下變得較硬且較難溶於溶劑中的材料。
術語「液體組成物」旨在意指材料溶解在其中以形成溶液的液體介質、材料分散在其中以形成分散體的液體介質、或材料懸浮在其中以形成懸浮液或乳液的液體介質。
術語「（甲基）丙烯酸酯」旨在意指為丙烯酸酯或甲基丙烯酸酯的基團。
術語「溶劑」旨在意指在室溫下為液體的有機化合物。該術語旨在涵蓋單一有機化合物或者兩種以上有機化合物的混合物。
在本說明書中，術語「膜」和「層」可互換使用。
所有範圍係包括端值的和可組合的。例如，術語「50 cPs至3000 cPs、或100 cPs以上的範圍」將包括50 cPs至100 cPs、50 cPs至3000 cPs和100 cPs至3000 cPs中的每一個。
在本說明書中，除非由使用上下文另外明確指明或相反指示，否則其中在本發明主題的實施方式被陳述或描述為包含（comprising）、包括（including）、含有（containing）、具有某些特徵或要素、由某些特徵或要素組成或由某些特徵或要素構成時，除了明確陳述或描述的那些之外的一個或多個特徵或要素也可存在於該實施方式中。所揭露的本發明主題的替代實施方式被描述為基本上由某些特徵或要素組成，其中將實質性改變操作原理或實施方式的區別特徵的實施方式特徵或要素在此不存在。所描述的本發明主題的另一個替代實施方式被描述為由某些特徵或要素組成，在該實施方式中或在其非實質變型中，僅存在所具體陳述或描述的特徵或要素。
除非另有定義，否則本文使用的所有技術和科學術語均具有與本揭露所屬領域普通技術人員所通常理解的相同含義。儘管與本文描述的那些方法和材料的類似者或等同者均可用於本揭露實施方式的實踐或檢驗，但以下描述了合適之方法和材料。此外，材料、方法和實例僅為說明性的並且不旨在係限制性的。
至於本文未描述的範圍，有關特定材料、加工行為和電路的許多細節均是常規的並且可以在光致抗蝕劑、有機發光二極體顯示器、光電檢測器、光伏電池、和半導體構件領域的教科書和其他來源中找到。
提供了包含來自混合物的共聚產物的聚合物，該混合物包含：基於共聚中存在的總單體計，（a）10 mol%-50 mol%的至少一種可加成聚合的芳基環丁烯單體；（b）15 mol%-50 mol%的至少一種可加成聚合的二烯單體；以及（c）15 mol%-60 mol%的至少一種可加成聚合的芳香族乙烯基單體。
該可加成聚合的芳基環丁烯單體係具有至少一個可加成聚合的取代基的芳基環丁烯。該取代基可以是乙烯基、烯丙基、或（甲基）丙烯酸酯基。基於共聚中存在的總單體，該單體可以以20 mol%-40 mol%的量存在。
在一些實施方式中，該芳基環丁烯單體具有式A-1或式A-2，如下所示：
其中：
K1
係選自由以下組成之群組的二價基團：烷基、芳基、碳環芳基、多環芳基、雜芳基、芳氧基、芳基烷基、羰基、酯、羧基、醚、硫酯、硫醚、三級胺、及它們的組合；
K2
係單鍵或選自由以下組成之群組的二價基團：烷基、芳基、碳環芳基、多環芳基、雜芳基、芳氧基、芳基烷基、羰基、酯、羧基、醚、硫酯、硫醚、三級胺、及它們的組合；
L1
係共價鍵或多價連接基團；
M係取代或未取代的二價芳香族基團、或者取代或未取代的二價雜芳香族基團；
R1
-R7
相同或者不同並且獨立地選自由以下組成之群組：氫、氘、烷基、烷氧基、取代或未取代的碳環芳基以及取代或未取代的雜芳基；並且
x和y相同或者不同並且是1至5的整數，其中當L1
係共價鍵時，y = 1。
在通式A-1中，K1
可以是未取代的不具有雜原子的C6-36
碳環芳基、或未取代的不具有雜原子的C6-18
碳環芳基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-36
碳環芳基、
或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-18
碳環芳基；或者未取代的C3-36
雜芳基、或未取代的C3-18
雜芳基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-36
雜芳基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-18
雜芳基；或者不具有環雜原子的未取代的C6-36
芳氧基、或不具有環雜原子的未取代C6-18
芳氧基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-36
雜芳氧基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-18
雜芳氧基；或者不具有雜原子的未取代的C6-36
芳基烷基、或不具有雜原子的未取代C6-18
芳基烷基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-36
雜芳基烷基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-18
雜芳基烷基。
在式A-1中，L1
係共價鍵；或者不具有環雜原子的多價C6-12
碳環芳基；或者係選自由苯基、聯苯基、和萘基組成之群組。
在式A-1中，M係不具有雜原子的未取代的C6-36
碳環芳基、或不具有雜原子的未取代的C6-18
碳環芳基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-36
碳環芳基、
或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-18
碳環芳基；或者未取代的C3-36
雜芳基、或未取代的C3-18
雜芳基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-36
雜芳基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-18
雜芳基。
在式A-1中，R5
係氫；或者C1-6
烷基、或C1-3
烷基；或者C1-6
烷氧基、或C1-3
烷氧基。
用於式A-1中的R5
的所有上述實施方式同樣適用於式A-1中的R6
和R7
；或者R5
= R6
= R7
= 氫。
在式A-1中，x係1、或2；y係1或2；或者x = y = 1。
在式A-2中，K2
係共價鍵；或者不具有雜原子的未取代的C6-36
碳環芳基或不具有雜原子的未取代的C6-18
碳環芳基；或者具有至少一個選自由烷基和烷氧基的取代基組成之群組的取代C6-36
碳環芳基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-18
碳環芳基；或者未取代的C3-36
雜芳基、或未取代的C3-18
雜芳基；或者具有至少一個選自由烷基和烷氧基的取代基組成之群組的取代C6-36
雜芳基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C6-18
雜芳基；或者不具有環雜原子的未取代的C6-36
芳氧基、或不具有環雜原子的未取代C6-18
芳氧基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-36
雜芳氧基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-18
雜芳氧基；或者不具有雜原子的未取代C6-36
芳基烷基、或不具有環雜原子的未取代C6-18
芳基烷基；或者具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-36
雜芳基烷基、或具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代C3-18
雜芳基烷基。
式A-1中的L1
、M、x和y同樣適用於式A-2中的L1
、M、x和y。用於式A-1中的R5
的所有上述實施方式同樣適用於式A-2中的R1
-R7
。
在一個實施方式中，該芳基環丁烯單體具有式A-1-a：
其中：
Ar係取代或未取代的碳環芳基、或者取代或未取代的雜芳基；
Q係共價鍵、O、S、或NRa
；
Ra
選自由以下組成之群組：氫、氘、取代或未取代的碳環芳基、以及取代或未取代的雜芳基；
R5
-R7
相同或者不同並且獨立地選自由以下組成之群組：氫、氘、烷基、烷氧基、取代或未取代的碳環芳基、以及取代或未取代的雜芳基；
R8
選自由以下組成之群組：烷基、烷氧基、取代或未取代的碳環芳基、以及取代或未取代的雜芳基；以及
a係0到4的整數。
在式A-1-a中，Ar係具有6-36個環碳的未取代的碳環芳基、或具有6-12個環碳的未取代的碳環芳基；或者具有6-36個環碳並且具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代碳環芳基、或具有6-12個環碳並且具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代碳環芳基；或者具有3-36個環碳的雜芳基、或具有3-12個環碳的雜芳基；或者具有6-36個環碳並且具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代雜芳基、或具有3-12個環碳並且具有至少一個選自由烷基和烷氧基組成之群組的取代基的取代雜芳基；或者選自由苯基、聯苯基、和萘基組成之群組。
在式A-1-a中，Q係共價鍵、或O、或S、或NH、或NCH3
。
在式A-1-a中，a係0；或者1；或者2；或者 ＞ 1；或者 ＞ 0並且至少一個R8
係C1-6
烷基、或C1-3
烷基；並且至少一個R8
係C1-6
烷氧基、或C1-3
烷氧基。
用於式A-1中的R5
的所有上述實施方式同樣適用於式A-1-a中的R5
-R7
。
在另一個實施方式中，該芳基環丁烯單體具有式A-2-a：
其中：
Ar係取代或未取代的碳環芳基或者取代或未取代的雜芳基；
Q係共價鍵、O、S、或NRa
；
Ra
選自由以下組成之群組：氫、氘、取代或未取代的碳環芳基、以及取代或未取代的雜芳基；
R1
-R7
相同或者不同並且獨立地選自由以下組成之群組：氫、氘、烷基、烷氧基、芳氧基、取代或未取代的碳環芳基、以及取代或未取代的雜芳基；
R8
選自由以下組成之群組：烷基、烷氧基、取代或未取代的碳環芳基、以及取代或未取代的雜芳基；以及
b係0到3的整數。
在式A-2-a中，b可以是0；或者1；或者2；或者 ＞ 1；或者 ＞ 0並且至少一個R8
係C1-6
烷基、或C1-3
烷基；並且至少一個R8
係C1-6
烷氧基、或C1-3
烷氧基。
用於式A-1-a中的Ar和Q的所有上述實施方式同樣適用於式A-2-a中的Ar和Q。用於式A-1中的R5
的所有上述實施方式同樣適用於式A-2-a中的R1
-R7
。
芳基環丁烯單體的實例可以包括但不限於1-(4-乙烯基苯氧基)-苯并環丁烯、1-(4-乙烯基甲氧基)-苯并環丁烯、1-(4-乙烯基苯基)-苯并環丁烯、1-(4-乙烯基羥基萘基)-苯并環丁烯、4-乙烯基-1-甲基-苯并環丁烯、4-乙烯基-1-甲氧基-苯并環丁烯和4-乙烯基-1-苯氧基-苯并環丁烯。
基於共聚中存在的總單體，該二烯單體可以以15 mol%-30 mol%、或20 mol%-25 mol%的量存在。在一個實施方式中，該二烯單體具有式B，如下所示：
其中：
R9
在每次出現時相同或不同並且選自由氫和甲基組成之群組；以及
R10
在每次出現時相同或不同並且選自由以下組成之群組：氫、C1-5
烷基、C1-5
烷氧基、C1-5
硫代烷基、以及C5-12
烯基。
在式B中，所有的R9
都可以是氫，或者三個R9
係氫並且一個R9
係甲基。兩個R10
相同；或者不同；或者至少一個R10
係氫；或者至少一個R10
係C1-3
烷基、或甲基；或者至少一個R10
係C1-3
烷氧基、或甲氧基；或者至少一個R10
係具有式-(CH2
)c
-CH=C(R11
)2
的烯基，其中c係1-5的整數並且R11
係氫或甲基。
二烯單體的實例可以包括但不限於丁二烯、異戊二烯、1,3-戊二烯、2,4-己二烯、環戊二烯、β-月桂烯、蘿艻萜、環辛二烯、菌綠烯、以及可聚合的萜烯。
基於共聚中存在的總單體，該芳香族乙烯基單體可以以40 mol%-60 mol%的量存在。在一個實施方式中，該芳香族乙烯基單體具有式C，如下所示：
其中：
R12
-R14
在每次出現時相同或不同並且選自由氫和C1-5
烷基組成之群組；以及
R15
在每次出現時相同或不同並且選自由氫和C1-5
烷基組成之群組，其中相鄰的R15
基團可以連接以形成稠合的6員芳族環。
在式C中，R12
可以是氫、或C1-3
烷基、或甲基。式C中的R12
可以同樣適用於式C中的R13
和R14
、或者R12
= R13
= R14
= 氫。
在式C中，所有的R15
都可以是氫；或者至少一個R15
係C1-3
烷基、或甲基；或者一個R15
係C1-3
烷基、或甲基；或者兩個R15
係C1-3
烷基、或甲基；或者兩個R15
連接在一起以形成稠合的6員芳環。
芳族乙烯基單體的實例可以包括但不限於苯乙烯、α-甲基苯乙烯、乙烯基甲苯、1-乙烯基萘和2-乙烯基萘。
該混合物可以進一步包含（d）3 mol%-10 mol%的可加成聚合的乙烯基取代的C3-12
雜環或乙烯基取代的C3-5
雜環單體。在一些實施方式中，該雜環單體可以進一步被一個或多個C1-6
烷基、C6-12
碳環芳基、或C3-12
雜芳基取代。基於共聚中存在的總單體，該雜環單體可以以4 mol%-7 mol%的量存在。該雜環單體選自由以下組成之群組：N-雜環、S-雜環、N,S-雜環、及它們的取代衍生物。
該N-雜環可以具有至少一個環氮。N-雜環的實例可以包括但不限於吡咯、吡啶、二𠯤、三𠯤、咪唑、苯并咪唑、以及喹啉酮。該S-雜環可以具有至少一個環硫。S-雜環的實例可以包括但不限於噻吩、苯并噻吩、以及二苯并噻吩。該N,S-雜環可以具有至少一個環氮和一個環硫。N,S-雜環的實例可以包括但不限於噻唑、噻二唑、以及噻二𠯤。
在一個實施方式中，該雜環單體具有式D，如下所示：
其中：
Z1
和Z2
相同或不同並且是N或CR15a
；以及
R12
-R14
和R15a
在每次出現時相同或不同並且選自由氫和C1-5
烷基組成之群組。
在式D中，Z1
= Z2
；或者Z1
≠ Z2
；或者Z1
係CH、或CR15a
、或N、或CH；或者Z2
係或CR15a
、或N。R12
係氫、或C1-3
烷基、或甲基。
用於式D中的R12
的所有上述實施方式同樣適用於式D中的R13
、R14
、以及R15a
；或者R12
= R13
= R14
= 氫。
該雜環單體的實例包括但不限於4-乙烯基吡啶、4-乙烯基-1,3-二𠯤、2-乙烯基-1,3,5-三𠯤、以及4-甲基-5-乙烯基-1,3-噻唑。此外，聚合中可以存在一種或多種另外的可加成聚合的單體。
聚合物可以藉由熱引發劑、光引發劑或其他光活性化合物的作用使上述可加成聚合的單體共聚而形成。
在一個實施方式中，共聚方法包括提供上述可加成聚合的單體和自由基引發劑在極性溶劑中的混合物；以及在5 h-50 h時間段內將該混合物加熱至50°C-150°C的溫度。在另一個實施方式中，共聚方法包括提供上述可加成聚合的單體在極性溶劑中的混合物；將混合物加熱至50°C-150°C的溫度以形成加熱的混合物，並在5 h-50 h的時間段內將自由基引發劑連續進料到加熱的混合物中。
極性溶劑可以是單一的有機化合物或化合物的混合物。極性溶劑係單體可混溶或可分散於其中的極性溶劑。基於反應混合物的總重量，該極性溶劑可以以10 wt.%-70 wt.%，或20 wt.%-50 wt.%的量存在。在一個實施方式中，該極性溶劑可以是非質子有機溶劑，例如（環）烷酮或環酯、或直鏈或支鏈酮和C1-8
酯。
自由基引發劑通常是偶氮化合物或有機過氧化物。在一個實施方式中，自由基引發劑係油溶性偶氮化合物。此類引發劑可以包括例如二甲基2,2'-偶氮雙(2-丙酸甲酯)和2,2’-偶氮雙(2,4-二甲基戊腈)。添加的總的引發劑可以是基於起始反應混合物的1 wt.%-5 wt.%。
在所希望的反應時間後，獲得所得的最終反應混合物，冷卻至室溫（20°C-25°C），並且根據需要進行處理。本揭露的聚合物可以按原樣使用或者可以藉由添加非溶劑（例如水或甲醇）以從溶液中沈澱聚合物並隨後除去有機溶劑來分離。
本揭露關於包含溶解或分散於一種或多種有機溶劑中的上述聚合物的液體組成物。使用任何已知的技術可以將該液體組成物沈積到基底上以形成膜並加熱以除去溶劑。在此之後，可以進行額外的加熱步驟以固化膜。在一些實施方式中，本揭露的液體組成物可以用於形成用於光刻、封裝、黏附、密封和塊電介質（bulk dielectric）應用的介電膜，諸如在旋塗塗層或緩衝層中。在基底上形成的介電膜可以直接使用或可以剝離下來並且在電子裝置中的不同基底上使用。
本領域中已知的任何基底可以用於本揭露。基底的實例可以包括但不限於矽、銅、銀、銦錫氧化物、二氧化矽、玻璃、氮化矽、鋁、金、聚醯亞胺以及環氧模製化合物。
合適的有機溶劑係聚合物在其中可溶的那些。尤其有用的有機溶劑係可用於製造或配製芳基環丁烯聚合物的任何溶劑。示例性有機溶劑包括但不限於極性質子和極性非質子溶劑，例如醇，諸如2-甲基-1-丁醇、4-甲基-2-戊醇和甲基異丁基甲醇；酯，諸如乳酸乙酯、丙二醇甲醚乙酸酯、2-羥基異丁酸甲酯、3-甲氧基丙酸甲酯、乙酸正丁酯以及乙酸3-甲氧基-1-丁酯；內酯，諸如γ-丁內酯；內醯胺，諸如N-甲基吡咯啶酮；醚，諸如丙二醇甲醚和二丙二醇二甲醚異構物，如PROGLYDETM
DMM（陶氏化學公司，米德蘭，密西根州（The Dow Chemical Company, Midland, MI））；酮，諸如2-丁酮、環戊酮、環己酮以及甲基環己酮；及它們的混合物。
合適的添加劑可以添加到本揭露的液體組成物中。該添加劑的實例可以包括但不限於一種或多種固化劑、交聯劑（例如與聚合物分離的交聯單體）、表面活性劑、無機填料、有機填料、增塑劑、黏合促進劑、金屬鈍化材料、以及任何前述的組合。合適的表面活性劑係熟悉該項技術者熟知的，並且較佳的是非離子型表面活性劑。此類表面活性劑可以以0至10 g/L、或0至5 g/L的量存在。
任何合適的無機填料都可視需要用於本發明的組成物中，並且是熟悉該項技術者眾所周知的。示例性的無機填料可以包括但不限於矽、碳化矽、氮化矽、氧化鋁、碳化鋁、氮化鋁、氧化鋯、及其混合物。無機填料可以是粉末、棒、球或任何其他合適形狀的形式。此類無機填料可以具有任何合適的尺寸。此類無機填料可以包含偶合劑，諸如以常規量的矽烷或鈦酸鹽。無機填料可以以基於組成物的總重量0至80 wt.%、或40 wt.%至80 wt.%的量作為固體使用。在一些實施方式中，不存在無機填料。
該金屬鈍化材料可以是銅鈍化劑。合適的銅鈍化劑在本領域中是熟知的並且包括咪唑、苯并三唑、乙二胺或其鹽或酸酯、以及亞胺基二乙酸或其鹽。
任何合適的交聯劑可以視需要用於本發明的液體組成物中。合適的交聯劑可以與樹脂組成物中的官能基反應，該官能基包括熟悉該項技術者所選擇的烯烴和狄爾斯-阿德爾（Diels Alder）二烯烴。此類合適的交聯劑可以包括多官能硫醇、多官能疊氮化物、多官能氮丙啶和雙芳基環丁烯單體以及多官能親二烯體諸如（甲基）丙烯酸酯、馬來醯亞胺、烯丙基化合物、乙烯基矽烷化合物、或其他合適的親二烯體，前提係它們在用於固化組成物的條件下與本揭露的聚合物交聯。此類交聯劑的選擇係在熟悉該項技術者的能力範圍內的。基於組成物中可聚合單體的總重量，此類交聯劑典型地以0至30 wt.%、或0至15 wt.%的量使用。
各種固化劑可以用於本揭露的液體組成物中，其可以用於光刻中。合適的固化劑可以有助於含有雙苯并環丁烯的材料的固化，並且可以藉由熱或光來活化。示例性固化劑可以包括但不限於熱生成引發劑和光活性化合物（光生成引發劑）。此類固化劑的選擇在熟悉該項技術者的能力之內。較佳的熱生成引發劑係自由基引發劑，諸如但不限於偶氮二異丁腈、過氧化二苯甲醯、以及過氧化二異丙苯。較佳的光活性固化劑係從巴斯夫公司以Irgacure商標可獲得的自由基光引發劑、以及二偶氮萘醌（DNQ）化合物（包括DNQ化合物的磺酸酯）。合適的DNQ化合物係具有DNQ部分（如DNQ磺酸酯部分）的任何化合物，並且其在本發明的組成物中起到光活性化合物的作用，即，它們在暴露於合適的輻射時起到分解抑制劑的作用。合適的DNQ化合物揭露於美國專利號7,198,878和8,143,360中，其全部內容藉由引用併入本文。
基於聚合物固體的總重量，光活性化合物的量從0至30 wt.%變化。當存在時，基於聚合物固體的總重量，光活性化合物典型地以5 wt.%至30 wt.%、或5 wt.%至25 wt.%、或10 wt.%至25 wt.%的量使用。
任何合適的黏合促進劑可以用於本揭露的液體組成物並且此種黏合促進劑的選擇在熟悉該項技術者的能力之內係熟知的。較佳的黏合促進劑係含矽烷的材料或四烷基鈦酸酯、或含三烷氧基矽烷的材料。示例性黏合促進劑包括但不限於雙(三烷氧基矽基烷基)苯，諸如雙(三甲氧基矽基乙基)苯；胺基烷基三烷氧基矽烷，諸如胺基丙基三甲氧基矽烷、胺基丙基三乙氧基矽烷、以及苯基胺基丙基三乙氧基矽烷；和其他矽烷偶合劑，以及前述的混合物。黏合促進劑可以首先作為底漆層或作為添加劑施加到組成物中。特別合適的黏合促進劑包括AP 3000、AP 8000、和AP 9000C（麻塞諸塞州瑪律堡陶氏電子材料公司（Dow Electronic Materials, Marlborough, MA））。基於組成物的總重量，本揭露的液體組成物可以包含0至15 wt.%、或0.5 wt.%至10 wt.%、或1 wt.%至10 wt.%、或2 wt.%至10 wt.%的黏合促進劑。
本揭露的光刻液體組成物可以藉由以任何次序組合本揭露的一種或多種聚合物、任何有機溶劑、水或額外組分和作為固化劑的光活性化合物來製備。有機溶劑與上述那些相同。當本發明的組成物含有光活性化合物諸如重氮萘醌、鎓鹽或光引發劑時，較佳的是，首先將固化劑溶解於合適的有機溶劑或鹼水溶液中，然後與一種或多種本發明的聚合物和任何視需要的表面活性劑組合，並且然後與任何視需要的黏合促進劑組合。合適的光活性化合物的選擇係在本領域的普通技術水平內的。
在一些實施方式中，本揭露的液體組成物可以藉由任何合適之方法塗覆或沈積在基底上。基底與上述那些相同。用於塗布本發明組成物的合適方法可以包括但不限於旋塗、幕塗、噴塗、輥塗、浸塗、氣相沈積和層壓如真空層壓，等方法。在半導體製造工業中，旋塗係利用現有設備和製程的較佳之方法。在旋塗時，可隨著旋轉速度調節組成物的固體含量，以在其施加的表面上達到所希望的組成物厚度。
當本揭露的液體組成物不含黏合促進劑時，待塗覆有本發明組成物的基底的表面可以視需要首先與合適的黏合促進劑接觸或蒸汽處理。本領域中已知的各種氣相處理可以增加本揭露的聚合物與基底表面的黏附性，諸如電漿處理。在某些應用中，在用本發明的組成物塗覆表面之前，可以較佳的是使用黏合促進劑處理基底表面。黏合促進劑與上述那些相同。
典型地，將本揭露的液體組成物以400 rpm至4000 rpm的旋轉速度旋塗。分配在晶圓或基底上的本發明組成物的量取決於組成物中的總固體含量、所得層的希望厚度、以及熟悉該項技術者熟知的其他因素。當藉由旋塗將本發明組成物的膜或層流延時，許多（或全部）溶劑在膜沈積期間蒸發。較佳的是，在被佈置在表面上之後，將組成物加熱（軟烘烤）以除去任何剩餘的溶劑。儘管可以適當地使用其他溫度，但典型的烘烤溫度為90°C至120°C。除去殘餘溶劑的這種烘烤典型地進行大約一至兩分鐘，儘管可以適當使用更長或更短的時間。
典型地，本揭露的聚合物藉由加熱固化一段時間。合適的固化溫度範圍為140°C至300°C；或170°C至250°C。典型地，固化時間範圍係1分鐘至600分鐘、或30分鐘至240分鐘、或30分鐘至120分鐘。
在一個實施方式中，包含本文所述之聚合物的液體組成物可以旋轉流延到銅上。可以藉由狹縫式模頭塗布機或其他合適的設備流延該組成物，以形成微電子應用所期望的乾膜。流延膜可以在70°C-150°C或90°C-120°C的溫度下軟烘烤30秒至10分鐘以除去殘餘溶劑。然後可以使該軟烘烤膜經受150°C-250°C的固化條件30分鐘至4小時。
在一些實施方式中，本揭露的液體組成物的層也可以形成為乾膜並藉由層壓配置在基底的表面上。各種合適的層壓技術（包括真空層壓技術）可以使用並且對於熟悉該項技術者係熟知的。在形成乾膜時，首先使用狹縫式模頭塗布、凹版印刷或其他適當之方法將本發明的組成物佈置（例如塗覆）在合適的膜支撐片（例如聚酯片，較佳的聚對苯二甲酸乙二酯（PET）片，或聚醯亞胺片例如KAPTON™聚醯亞胺（杜邦公司（DuPont），德拉瓦州威明頓市）的前表面上。然後將組成物在合適的溫度（例如90°C至140°C）下軟烘適當的時間（例如1至30分鐘）以除去任何溶劑。然後在室溫（20°C-25°C）下將聚合物膜覆蓋片材（諸如聚乙烯）經輥層壓到乾燥的組成物上以在儲存和處理期間保護組成物。為了將乾燥的組成物佈置在基底上，首先將覆蓋片材移除。然後使用經輥層壓或真空層壓將載體片材上的乾燥組成物層壓到基底表面上。層壓溫度的範圍可以是20°C至120°C。然後移除（剝離）載體片材，將乾燥組成物留在該表面上。
所得的固化的膜具有良好的拉伸強度、拉伸伸長率、對期望的基底（例如銅）的良好的黏附性以及在高頻率下的低介電損耗。本文揭露的聚合物在不借助任何種類的無機填料的情況下即可獲得該等良好的特性。在高頻（10 GHz或28 GHz以下）下，介電膜可以具有小於3.0的Dk值和小於0.004的Df值。在一些實施方式中，在10 GHz的頻率下介電膜具有Dk ≤ 2.6和Df ≤ 0.004。在一些實施方式中，在28 GHz的頻率下介電膜具有Dk ≤ 2.6和Df ≤ 0.004。
本揭露還關於許多種電子裝置，該電子裝置包括在電子裝置基底上的至少一個本申請的介電膜的層。電子裝置基底可以是用於製造任何電子裝置的任何基底。示例性的電子裝置基底包括但不限於半導體晶圓、玻璃、藍寶石、矽酸鹽材料、氮化矽材料、碳化矽材料、顯示裝置基底、環氧模製化合物晶圓、電路板基底、以及熱穩定的聚合物。如本文使用的，術語「半導體晶圓」旨在涵蓋半導體基底、半導體裝置以及用於各種互連水平的各種封裝物，包括單晶圓晶圓、多晶圓晶圓、用於各種水平的封裝物、用於發光二極體（LED）的基底、或其他需要焊接連接的組件。半導體晶圓，諸如矽晶圓、砷化鎵晶圓、以及矽鍺晶圓，可以是圖案化或未圖案化的。如本文使用的，術語「半導體基底」包括具有一個或多個半導體層或結構的任何基底，該半導體層或結構包括半導體裝置的活性或可操作部分。術語「半導體基底」被定義為意指包含半導體材料的任何構造，諸如半導體裝置。半導體裝置係指半導體基底，在其上已經製造或正在製造至少一種微電子裝置。熱穩定的聚合物包括但不限於對用於將芳基環丁烯材料固化的溫度穩定的任何聚合物，例如聚醯亞胺，例如KAPTON™聚醯亞胺（杜邦公司，德拉瓦州威明頓市），液晶聚合物，例如VECSTAR™ LCP膜（可樂麗公司（Kuraray），日本東京）和雙馬來醯亞胺-三𠯤（BT）樹脂（三菱瓦斯化學株式會社（MGC），日本東京）。
實例
材料：
β-月桂烯（食品級）、20重量百分比的丁二烯甲苯溶液、4-甲基-5-乙烯基-1,3-噻唑和苯乙烯係從西格瑪奧德里奇公司（Sigma Aldrich）獲得的。Vazo 65和Vazo 601重氮引發劑購自和光化學公司（Wako Chemical）。乙烯基苯氧基BCB[1-(4-乙烯基苯氧基)苯并環丁烯]係根據美國專利申請號20190169327 A1製備的，其全部內容藉由引用併入本文。4-乙烯基吡啶購自西格瑪奧德里奇公司（Sigma Aldrich）並在使用前蒸餾。乙烯基甲苯異構物混合物得自玳爾科技公司（Deltech Corporation）。所有其他溶劑和化學品接收自陶氏化學公司（Dow Chemical Company）並且按原樣使用而不需要額外的純化。
測試方法
（1）介電特性：
使用在10-28 GHz工作的Keysight 85072A分裂圓柱體諧振器和Keysight N5224A PNA網路分析儀，採用IPC測試方法TM-6502.5.5.1測定自支撐膜的介電特性。膜的幾何形狀為使得基底延伸超過兩個圓柱形空腔部分的直徑。膜厚度為50 µm。
將自立式膜放置在分體圓柱諧振器的空腔中，並且使用網路分析儀測量TE011
諧振模式的諧振頻率和品質因子。使用由Keysight提供的軟體從TE011
諧振模式來計算膜的相對介電常數（Dk）和損耗正切（Df）。
（2）分子量測定程序：
將聚合物樣品製備為在四氫呋喃中的0.5 wt.%溶液並通過0.2微米Teflon過濾器過濾。流動相為四氫呋喃。柱係Waters Styragel HR5E 7.8 × 300 mm，柱批號0051370931。注射體積係100微升並且執行時間係27分鐘。相對於聚苯乙烯標準物報告分子量數據。
實例A
向100 ml的EasyMax™玻璃反應器中加入β-月桂烯（0.98 g）、1-(4-乙烯基苯氧基)苯并環丁烯（9.31 g）和苯乙烯（9.36 g）。然後將苯甲醚（6.67 g）加入反應器中。裝配反應器並在機械攪拌下混合直至均化。然後將內部反應器溫度升高至80°C，此時經過20小時以恒定速率加入V65（0.68 g）的苯甲醚（13.33 g）溶液。當加入完成時，將反應器在80°C下再保持2小時，然後將溫度降至室溫（20°C-25°C）。取樣用於GPC分析，並且將所得溶液通過5 μm孔徑Nylon™過濾器過濾到玻璃瓶中供使用。GPC Mn：27.4k，Mw：584.5k。
實例B
除了將2.019 g的β-月桂烯、9.578 g的1-(4-乙烯基苯氧基)苯并環丁烯、8.88 g的苯乙烯和6.21 g的均三甲苯添加到反應器中之外，使用與實例A中相同的程序。在反應溫度達到80°C下，加入0.7 g的V65在12.99 g的均三甲苯中的溶液。GPC數據：Mw 125.5k，Mn 20.3k。
實例1
除了將5.18 g的β-月桂烯、16.40 g的1-(4-乙烯基苯氧基)苯并環丁烯、13.95 g的苯乙烯和15.43 g的苯甲醚添加到反應器中之外，使用與實例A中相同的程序。加入1.20 g的V65和8.57 g的苯甲醚的引發劑進料。GPC Mn：11.8k，Mw：54.4k。
實例2
除了將5.52 g的β-月桂烯、12.40 g的1-(4-乙烯基苯氧基)苯并環丁烯、9.58 g的苯乙烯和6.88 g的環戊酮添加到反應器中之外，使用與實例A中相同的程序。經過18小時將0.91 g的V65和15.625 g環戊酮的引發劑進料加入反應混合物中。GPC Mn：7.9k，Mw：23.2k。
實例3
除了將8.37 g的β-月桂烯、13.11 g的1-(4-乙烯基苯氧基)苯并環丁烯、8.19 g的苯乙烯和5.29 g的環戊酮添加到反應器中之外，使用與實例A中相同的程序。加入0.97 g的V65和14.71 g的環戊酮的引發劑進料。GPC Mn：9.6k，Mw：29.1k。
藉由旋塗將以上形成的聚合物溶液沈積到直徑為200 mm的合適的Cu晶圓基底上，並在110°C下軟烘烤90秒。然後將聚合物膜在氮氣、小於100 ppm的氧氣下在200°C的BlueM烘箱中固化1小時。將所得基底切割成合適的尺寸並將膜在5%硫酸銨中水浴中提起、漂洗並乾燥以獲得用於測試的自支撐膜。
聚合物組成物在表1中給出，並且由聚合物組成物製備的膜的測試數據分別在如下所示的表2中列出。
[表 1
]. 聚合物組成物
(1) BCB：1-(4-乙烯基苯氧基)苯并環丁烯
[表 2
]. 膜測試數據
| 實例 | 單體mol% | ||
| 苯乙烯 | BCB(1) | β-月桂烯 | |
| A | 65 | 30 | 5 |
| B | 60 | 30 | 10 |
| 1 | 55 | 30 | 15 |
| 2 | 50 | 30 | 20 |
| 3 | 40 | 30 | 30 |
| 實例 | Dk 10GHz | Df 10GHz | Dk 28GHz | Df 28GHz |
| A | 2.71 | 0.0078 | 2.71 | 0.0068 |
| B | 2.65 | 0.0051 | 2.65 | 0.0056 |
| 1 | 2.60 | 0.0036 | 2.62 | 0.0039 |
| 2 | 2.54 | 0.0025 | 2.55 | 0.0028 |
| 3 | 2.6 | 0.0038 | 2.48 | 0.0035 |
結果表明，Df最初隨著二烯莫耳百分比的增加而降低。然而，當二烯莫耳百分比增加超過約25 mol%時，Df增加。類似地，Dk最初隨著二烯莫耳百分比的增加而降低。
實例4
使用與實例A中相同的程序，除了將15.52 g丁二烯甲苯溶液、19.14 g 1-(4-乙烯基苯氧基)苯并環丁烯、15.26 g乙烯基甲苯、1.51 g 4-乙烯基吡啶、0.99 g V601和10.0 g環己酮混合，然後在三個密封管之間分裝，然後放進反應器中的合適插入物中。將密封系統加熱至80°C並保持17小時，然後返回至25℃以供使用。GPC Mn：14.2k，Mw：40.9k。
實例5
除了將5.1 g的β-月桂烯、12.1 g的1-(4-乙烯基苯氧基)苯并環丁烯、9.53 g的乙烯基甲苯、1.01 g的4-乙烯基吡啶和11.79 g的苯甲醚添加到反應器中之外，使用與實例A中相同的程序。在80°C的反應溫度下加入0.41 g的V601。將反應保持15小時，然後經過12小時將0.41 g的V65和10.71 g苯甲醚的引發劑進料加入，隨後在80°C下再保持2小時，之後返回25°C。
實例6
除了將5.98 g的β-月桂烯、14.18 g的1-(4-乙烯基苯氧基)苯并環丁烯、11.19 g的乙烯基甲苯、1.33 g的4-甲基-5-乙烯基噻唑和6.21 g的環己酮添加到反應器中之外，使用與實例A中相同的程序。在反應溫度達到80 °C下，加入1.04 g的V65在12.86 g的環己酮中的溶液。GPC數據：Mw 32.1k，Mn 11.1k。
實例7
除了將6.33 g的β-月桂烯、12.01 g的1-(4-乙烯基苯氧基)苯并環丁烯、8.83 g的乙烯基甲苯、0.6 g的4-乙烯基吡啶和11.79 g的苯甲醚添加到反應器中之外，使用與實例A中相同的程序。在80°C的反應溫度下加入0.41 g的V601。反應保持15小時，然後經過12小時將0.41 g的V65和10.71 g苯甲醚的引發劑進料加入，隨後在80°C下再保持2小時，之後返回25°C。GPC數據：Mw 50.6k，Mn 10.6k。
實例8
除了將6.33 g的β-月桂烯、12.02 g的1-(4-乙烯基苯氧基)苯并環丁烯、8.42 g的乙烯基甲苯、1.0 g的4-乙烯基吡啶和11.79 g的苯甲醚添加到反應器中之外，使用與實例A中相同的程序。在80°C的反應溫度下加入0.41 g的V601。反應保持15小時，然後經過12小時將0.41 g的V65和10.71 g苯甲醚的引發劑進料加入，隨後在80°C下再保持2小時，之後返回25°C。
實例9
除了將11.76 g的β-月桂烯、13.95 g的1-(4-乙烯基苯氧基)苯并環丁烯、6.12 g的乙烯基甲苯、1.14 g的4-乙烯基吡啶和14.14 g的環己酮添加到反應器中之外，使用與實例A中相同的程序。在反應溫度達到80 °C下，加入1.02 g的V65在12.86 g的環己酮中的溶液。GPC數據：Mw 19.3k，Mn 4.4k。
實例10
除了將17.18 g的β-月桂烯、16.31 g的1-(4-乙烯基苯氧基)苯并環丁烯、4.29 g的乙烯基甲苯、1.33 g的4-乙烯基吡啶和9.75 g的環己酮添加到反應器中之外，使用與實例A中相同的程序。在反應溫度達到80°C下，加入1.19 g的V65在11.2 g的均三甲苯中的溶液。GPC數據：Mw 19.7k，Mn 6.7k。
如上所述，膜由上述形成的聚合物溶液製備。聚合物組成物在表3中給出，並且由聚合物組成物製備的膜的測試數據分別在下方的表4中列出。
[表 3
]. 聚合物組成物
(2) 乙烯基芳香族乙烯基甲苯異構物混合物。
(3) 二烯：丁二烯用於實例4且β-月桂烯用於所有其他實例。
(4) 乙烯基雜環：甲基-5-乙烯基噻唑用於實例6且4-乙烯基吡啶用於所有其他實例。
[表 4
]. 膜測試數據
ND = 未確定
| 實例 | 單體mol% | |||
| 乙烯基芳香族(2) | BCB | 二烯(3) | 乙烯基雜環(4) | |
| 4 | 45 | 30 | 20 | 5 |
| 5 | 45 | 30 | 20 | 5 |
| 6 | 45 | 30 | 20 | 5 |
| 7 | 42 | 30 | 25 | 3 |
| 8 | 40 | 30 | 25 | 5 |
| 9 | 25 | 30 | 40 | 5 |
| 10 | 15 | 30 | 50 | 5 |
| 實例 | Dk 10GHz | Df 10GHz | Dk 28GHz | Df 28GHz |
| 4 | 2.60 | 0.002 | 2.59 | 0.0023 |
| 5 | 2.43 | 0.002 | 2.44 | 0.0022 |
| 6 | ND | ND | 2.55 | 0.0028 |
| 7 | 2.36 | 0.002 | 2.41 | 0.0021 |
| 8 | 2.26 | 0.0021 | 2.32 | 0.0021 |
| 9 | 2.42 | 0.003 | 2.38 | 0.0032 |
| 10 | 2.52 | 0.0035 | 2.56 | 0.0039 |
結果表明，當二烯莫耳百分比增加超過約25 mol%時，Df增加。類似地，Dk最初隨著二烯莫耳百分比的增加而降低。然而，當二烯莫耳百分比增加超過約40 mol%時，Dk增加。
應注意的是，並不是所有的以上在一般性描述或實例中所描述的活動皆為必需的，一部分具體活動可能不是必需的，並且除了所描述的那些以外，還可進行一個或多個其他活動。此外，所列舉的活動的順序不必是它們實施的順序。
在前述說明書中，已參考具體實施方式描述了概念。然而，熟悉該項技術者理解，在不脫離如以下請求項中所規定的本揭露範圍的情況下可作出各種修改和改變。因此，應該在說明性的而非限制性的意義上看待本說明書和附圖，並且所有此類修改均旨在包括在本揭露的範圍內。
上面已經關於具體實施方式描述了益處、其他優點和問題的解決方案。然而，益處、優點、問題的解決方案、以及可能引起任何益處、優點、或解決方案出現或使其變得更明顯的一個或多個任何特徵不會被解釋為任何或所有請求項的關鍵的、必要的或基本的特徵。
要理解的是，為清楚起見，本文在單獨實施方式的上下文中所述之某些特徵還可以以組合形式在單個實施方式中提供。相反地，為了簡潔起見，在單個實施方式的背景下所述之各個特徵也可以單獨地或以任何子組合提供。本文指定的各個範圍內的數值的使用表述為近似值，就像該範圍內的最小值和最大值二者前面都有單詞「約」。以這種方式，可以使用高於和低於該範圍的輕微變化來實現與該等範圍內的值基本上相同的結果。而且，該等範圍的揭露旨在作為包括在最小與最大平均值之間的每個值的連續範圍，包括當一個值的一些分量與不同值的分量混合時可產生的分數值。此外，當揭露更寬和更窄的範圍時，在本揭露的期望內，使來自一個範圍的最小值與來自另一個範圍的最大值匹配，並且反之亦然。
無
無
Claims (16)
- 一種聚合物，其包含來自混合物的共聚產物，該混合物包含：(a)基於共聚中存在的總單體，30mol%-50mol%的至少一種可加成聚合的式A-1-a的芳基環丁烯單體
- 如請求項1所述之聚合物，其中該混合物包含(a)基於共聚中存在的總單體，20mol%-40mol%的芳基環丁烯單體。
- 如請求項1或2所述之聚合物，其中該混合物包含(b)基於共聚中存在的總單體，15mol%-30mol%的該二烯單體。
- 如請求項3所述之聚合物，其中該混合物包含(b)基於共聚中存在的總單體，20mol%-25mol%的該二烯單體。
- 如請求項1或2所述之聚合物，其中該二烯單體具有式B，
- 如請求項1或2所述之聚合物，其中該混合物包含(c)基於共聚中存在的總單體，40mol%-60mol%的該芳香族乙烯基單體。
- 如請求項1或2所述之聚合物，其中該芳香族乙烯基單體具有式C，
- 如請求項1所述之聚合物，其中該雜環單體選自由以下組成之群組：N-雜環、S-雜環、N,S-雜環、及它們的取代衍生物。
- 如請求項1所述之聚合物，其中該乙烯基取代的C3-12雜環單體選自由以下組成之群組：4-乙烯基吡啶、4-乙烯基-1,3-二、2-乙烯基-1,3,5-三
、以及4-甲基-5-乙烯基-1,3-噻唑。
- 一種液體組成物，其包含在溶劑中的如請求項1至9中任一項所述之聚合物。
- 如請求項10所述之液體組成物，其中該溶劑選自由以下組成之群組：環戊酮、環己酮、丙二醇單甲醚、丙二醇單甲醚乙酸酯、γ-丁內酯、3-甲氧基丙酸酯、二丙二醇二甲醚、3-甲氧基丁基乙酸酯、苯甲醚、均三甲苯、2-庚酮、傘花烯、2-丁酮、乳酸乙酯、乙酸戊酯、乙酸正丁酯、N-甲基-2-吡咯啶酮、N-丁基-2-吡咯啶酮。
- 一種介電膜，其藉由將如請求項10或11所述之液體組成物沈積到基底上並加熱所沈積的組成物製備。
- 如請求項12所述之介電膜，其中，該基底選自由以下組成之群組：銅、矽、氮化矽、鋁、金、銀、聚醯亞胺和環氧模製化合物。
- 如請求項12所述之介電膜，其中，該介電膜在10GHz下具有Dk2.6和Df
0.004。
- 如請求項12所述之介電膜，其中，該介電膜在28GHz下具有Dk2.6和Df
0.004。
- 一種電子器件，其具有至少一個包含如請求項12至15中任一項所述之介電膜的層。