TWI718436B - 容器用樹脂被膜金屬板 - Google Patents
容器用樹脂被膜金屬板 Download PDFInfo
- Publication number
- TWI718436B TWI718436B TW107139995A TW107139995A TWI718436B TW I718436 B TWI718436 B TW I718436B TW 107139995 A TW107139995 A TW 107139995A TW 107139995 A TW107139995 A TW 107139995A TW I718436 B TWI718436 B TW I718436B
- Authority
- TW
- Taiwan
- Prior art keywords
- resin coating
- coating layer
- less
- resin
- layer
- Prior art date
Abstract
本發明所涉及的容器用樹脂被膜金屬板,是在金屬板的雙面具備樹脂被膜層,其特徵為:在成型加工後位於容器的外面側的樹脂被膜層,是以融點在230℃以上254℃以下的範圍的聚酯樹脂作為主成分並且含有潤滑成分,潤滑成分的融點為80℃以上230℃以下,存在於樹脂被膜層的表面的潤滑成分的平均粒徑為17.0nm以下。
Description
本發明是有關於在金屬板的雙面具備樹脂被膜層的容器用樹脂被膜金屬板。
一般金屬容器大致分為兩片罐和三片罐。兩片罐是指藉由與罐底成為一體的罐體和蓋體的兩個部分所構成的金屬容器。另一方面,三片罐是指藉由罐身、上蓋、及底蓋的三個部分所構成的金屬容器。兩片罐因為在罐體不具焊接部所以外表美觀,但相反地則要求比一般更高的加工度。
以往,在作為金屬容器的素材使用的鍍鉻無錫鋼(TFS)及鋁等的金屬板,實施以提昇耐腐蝕性和耐候性為目的的塗裝。然而,實施此塗裝的技術在複雜的塗裝及燒上彩花的步驟須要大量的處理時間,而且還有排出大量的溶劑的問題。所以,為了解決這些問題,在金屬板表面具有熱可塑性薄膜的容器用樹脂被膜金屬板已被開發出來,現在,以飲料罐用素材為中心在工業上被廣泛運用。
另一方面,近年從降低材料成本及節省資源的觀點來看,使用於金屬容器的材料板厚的薄化正在發展中。在使用薄化的材料來製造相同形狀的罐體的情況下,因為加工度變高,所以特別是在位於樹脂被膜金屬板的金屬容器外面側的樹脂被膜層有產生斷裂或刮損的可能性。因此,為了製造高加工度的兩片罐的罐體,所以必須防止樹脂被膜層的斷裂或刮損的材料設計。
並且,為了在金屬容器外面側的樹脂被膜層提高設計性所以實施各種的印刷,但在印刷油墨和樹脂被膜層之間的親和性較小的情況下,無法確保印刷油墨的密合性,將有因印刷油墨的剝落而損害外觀的美觀度的可能性。因此,在金屬容器外面側的樹脂被膜層,必須有提高與印刷油墨的親和性的材料設計。
作為將容器用樹脂被膜金屬板作為素材來製造兩片罐體的技術,已提案有引伸加工法及DI加工法等的技術(參照專利文獻1、2、3)。另外,為了能進行提高印刷處理等的罐體的設計性的處理,尚提案有在成型加工後位於金屬容器的外面側的樹脂被膜層添加白色顏料的技術(參照專利文獻4,5)。並且,作為抑制製造高加工度的兩片罐時的樹脂被膜層的斷裂或刮損的技術,尚提案有在樹脂被膜層添加潤滑劑成分的技術(參照專利文獻6)。
[先前技術文獻]
[專利文獻]
專利文獻1 日本特開平2-303634號公報
專利文獻2 日本特開平4-91825號公報
專利文獻3 日本特開2004-148324號公報
專利文獻4 日本特開平8-169098號公報
專利文獻5 日本特開2004-130536號公報
專利文獻6 日本特開2017-30210號公報
[發明所欲解決之問題]
如上述般,為了抑制製造高加工度的兩片罐時的樹脂被膜層的斷裂或刮損,所以有藉由在樹脂被膜層添加潤滑劑成分的等的方法,確保樹脂被膜層表面的滑動性來提高加工性的必要。但是,潤滑劑成分的添加也有阻礙樹脂被膜層和印刷油墨的密合,且損害外觀的美觀度的原因的可能性。在有鑑於如此般的特性的情況下,就以往技術未能達成所要求的加工性及印墨密合性的兼顧,無法取得可兼顧抑制伴隨加工的樹脂被膜層的斷裂或刮損,以及印刷後的外觀的美觀度的容器用樹脂被膜金屬板。
此外,專利文獻6所記載的技術,藉由在樹脂被膜層添加潤滑劑成分並且控制樹脂被膜層的水接觸角,以謀求加工性及印墨密合性的兼顧。然而,在水接觸角為80°以上的疏水性表面,會有無法充分取得樹脂被膜層和印刷油墨的親和性的情況,可能在印刷後的內容物充填、蓋封罐、輸送等的諸步驟之間發生印刷油墨的剝落。
本發明是有鑑於上述課題所發明,其目的在於提供:可抑制伴隨加工的樹脂被膜層的斷裂或刮損及印刷後的印刷油墨的剝落的容器用樹脂被膜金屬板。
[解決問題之技術手段]
本發明的發明者們為了解決上述的課題所以致力於進行研究。其結果,本發明的發明者們得到以下的見解。換言之,在進行加工度較高的成型的情況下,為了抑制樹脂被膜層的斷裂或刮損,所以必須在樹脂被膜層中添加潤滑成分,降低樹脂被膜層表面的摩擦。然而,因為潤滑成分的添加有成為阻礙樹脂被膜層和印刷油墨的密合,損害外觀的美觀度的原因的可能性,所以控制添加的潤滑成分的種類及量是極為重要。
本發明的發明者們發現在樹脂被膜層表面的潤滑成分的分布狀態是表示樹脂被膜層和潤滑成分的親和性的指標,並發現藉著將其分散狀態成為特定的值以下,可抑制樹脂被膜層和印刷油墨的密合上的阻礙。通常,製罐步驟之印刷是在製罐加工緊接著進行的熱處理後實施的情況較多,有機潤滑成分在熱處理時濃化於樹脂被膜層表面,且阻礙樹脂被膜層和印刷油墨的密合。因此,提高樹脂被膜層和潤滑成分的親和性,且不易在熱處理時濃化於樹脂被膜層表面是非常重要。本發明是基於以上的見解進行,其要旨如下所述。
本發明所涉及的容器用樹脂被膜金屬板,是在金屬板的雙面具備樹脂被膜層,其特徵為:在成型加工後位於容器的外面側的前述樹脂被膜層,是以融點在230℃以上254℃以下的範圍的聚酯樹脂作為主成分並且含有潤滑成分,前述潤滑成分的融點為80℃以上230℃以下,存在於前述樹脂被膜層的表面的前述潤滑成分的平均粒徑為17.0nm以下。
此外,較理想為在成型加工後位於容器的外面側的前述樹脂被膜層所含有的前述潤滑成分,是在0.010質量%以上1.0質量%以下的範圍內。另外,較理想為在成型加工後位於容器的外面側的前述樹脂被膜層所含有的前述潤滑成分,是重量平均分子量2500以上且未達80000,酸價1.0mgKOH/g以上100mgKOH/g以下的酸改性聚烯烴或氧化聚烯烴。
另外,較理想為在成型加工後位於容器的外面側的前述樹脂被膜層,含有30質量%以下的範圍內的氧化鈦。
另外,較理想為在成型加工後位於容器的外面側的前述樹脂被膜層,具有由最表面層、中間層、及最下層所成的至少三層構造,前述最表面層及最下層的膜厚在1.0μm以上5.0μm以下的範圍內,前述中間層的膜厚在6.0μm以上30μm以下的範圍內,前述最表面層及最下層含有0.0質量%以上2.0質量%以下的範圍內的氧化鈦,前述中間層含有10質量%以上30質量%以下的範圍內的氧化鈦。
[發明效果]
依據本發明,可以提供:可抑制伴隨加工的樹脂被膜層的斷裂或刮損及印刷後的印刷油墨的剝落的容器用樹脂被膜金屬板。
以下,針對本發明的一個實施形態的容器用樹脂被膜金屬板進行說明。此外,以下只要沒有特別註明,則「%」是表示「質量%」。
第1(a)、(b)圖是表示本發明的一個實施形態的容器用樹脂被膜金屬板的構成的剖面圖。如第1(a)圖所示般,本發明的一個實施形態的容器用樹脂被膜金屬板1,具備:金屬板2;樹脂被膜層3,是形成於金屬板2的表面側;以及樹脂被膜層4,是形成於金屬板2的裏面側。樹脂被膜層3及樹脂被膜層4在成型加工後,分別位於金屬容器的外面側及內面側。
金屬板2是藉由馬口鐵及鍍鉻無錫鋼等的鋼板所形成。以馬口鐵而言,較理想為使用電鍍量為0.5g/m2
以上15g/m2
以下的範圍內。鍍鉻無錫鋼,較理想為在表面具有:金屬鉻層,是附著量在50mg/m2
以上200g/m2
以下的範圍內;以及鉻酸化物層,是金屬鉻層換算的附著量在3mg/m2
以上30g/m2
以下的範圍內。鋼板的種類若可以成型為目的形狀的話不特别限定,但較理想為以下所示的成分及製法。
(1)C(碳)量是使用在0.010%以上0.10%以下程度的範圍內的低碳鋼,以連續退火進行再結晶退火。
(2)C量是使用在0.010%以上0.10%以下程度的範圍內的低碳鋼,以連續退火進行再結晶退火及過時效時理。
(3)C量是使用在0.010%以上0.10%以下程度的範圍內的低碳鋼,以箱式退火進行再結晶退火。
(4)C量是使用在0.010%以上0.10%以下程度的範圍內的低碳鋼,在以連續退火或箱式退火進行再結晶退火後,進行二次冷軋(DR(Double Reduced)壓延)。
(5)使用將Nb、Ti等的固溶的C予以固定的元素添加於C量在大致0.003%以下程度的極低碳鋼的IF(Interstitial Free)鋼,以連續退火進行再結晶退火。
鋼板的機械特性是如果可以成型為目的形狀的話則不特別限定,但為了不損及加工性,而且保持充分的罐體強度,所以較理想為使用降伏點(YP)在220MPa以上580MPa以下程度的範圍者。另外,有關作為塑性異方性的指標的蘭克福特值(r值),較理想為0.8以上。並且,有關於r值的面內各向異性Δr,其絕對值較理想為0.7以下。
用來達成上述的特性的鋼的成分未特別限定,但含有例如Si,Mn,P,S,Al,N等的成分即可。較佳為Si含有量在0.001%以上0.1%以下的範圍內,Mn含有量在0.01%以上0.6%以下的範圍內,P含有量在0.002%以上0.05%以下的範圍內,S含有量在0.002%以上0.05%以下的範圍內,Al含有量在0.005%以上0.100%以下的範圍內,N含有量在0.0005%以上0.020%以下的範圍內。另外,也可以含有Ti、Nb、B、Cu、Ni、Cr、Mo、V等其他的成分,但從確保耐腐蝕性等的觀點來看,這些成分的含有量的總量較理想為0.02%以下。
樹脂被膜層3是主成分為融點230℃以上254℃以下的聚酯樹脂。較佳為聚酯樹脂的融點在234℃以上252℃以下,更佳為聚酯樹脂的融點在238℃以上250℃以下的範圍。在聚酯樹脂的融點未達230℃的情況下,樹脂藉由在連續成型加工時施加的熱而軟化,且在樹脂被膜層3發生斷裂或刮損。另一方面,在聚酯樹脂的融點超過254℃的情況下,因聚酯樹脂的結晶性變高而導致樹脂的成型性劣化。
聚酯樹脂的原料,可使用各種的二羧酸成分及乙二醇成分。另外,在不損及耐熱性及加工性的範圍,可使複數的二羧酸成分、乙二醇成分進行共聚。作為二羧酸成分而言,可以例示如:對苯二甲酸、間苯二甲酸、萘二羧酸、聯苯二甲酸、二苯碸二羧酸、苯氧乙烷二羧酸、5-磺酸基間苯二甲酸鈉、鄰苯二甲酸等的芳香族二羧酸、草酸、琥珀酸、己二酸、癸二酸、二聚酸、馬來酸、富馬酸等的脂肪族二羧酸、環己烷二羧酸等的脂環族二羧酸、對羥基苯甲酸等的羥基羧酸等。作為乙二醇成分而言,可以例示如:乙烯二醇、丙二醇、丁二醇、戊二醇、己二醇、新戊二醇等的脂肪族乙二醇、環己烷二甲醇等的脂環族乙二醇、雙酚A、雙酚S等的芳香族乙二醇、二乙烯二醇等。
形成樹脂被膜層3的樹脂材料並非受該製法所限定。另外,也可以在聚酯的製造,視須要來添加發光增白材、抗氧化劑、熱穩定化材、紫外線吸收劑、抗靜電材等的添加物。在白色度的提昇上,發光增白材的添加較為有效。
樹脂被膜層3含有潤滑成分。在實施兩片罐的製造這類嚴峻加工時,從確保表面的滑動性的觀點來看,必須對於樹脂被膜層3添加潤滑成分。較佳為含有的有機潤滑成分是0.010%以上1.0%以下,更佳為0.020%以上0.90%以下,特佳為0.020%以上0.80%以下。潤滑成分的添加量未達0.010%的話,製罐加工時無法確保充分的滑動性,有發生樹脂被膜層3的刮損的可能性。另外,在潤滑成分的添加量超過1.0%的情況下,會有因樹脂被膜層3內的潤滑成分所占的比例提高而導致樹脂被膜層3產生軟化,且在製罐加工時發生刮損的可能性。
存在於樹脂被膜層3的表面的潤滑成分的平均粒徑為17.0nm以下。較佳為平均粒徑是15.0nm以下,更佳為13.0nm以下。在樹脂被膜層3表面分散的潤滑成分的平均粒徑是樹脂被膜層3和潤滑成分的親和性的指標,樹脂被膜層3和潤滑成分的親和性越大則分散的潤滑成分的平均粒徑越小。在樹脂被膜層3的表面分散的潤滑成分的平均粒徑超過17.0nm的情況下,由於樹脂被膜層3和潤滑成分的親和性較低,在製罐加工之後實施的加熱步驟中潤滑成分濃化於樹脂被膜層3表面而顯著阻礙印刷油墨的密合性,且在製罐加工後的內容物充填、蓋封罐、輸送等的諸步驟之間發生印刷油墨的剝落。
樹脂被膜層3所含有的潤滑成分的融點為80℃以上230℃以下。在使用融點未達80℃的潤滑成分的情況下,潤滑成分容易往樹脂被膜層3表面濃化,因潤滑成分往樹脂被膜層3表面的濃化,阻礙印刷油墨的密合。另一方面,在潤滑成分的融點超過230℃的情況下,無法在加工時取得充分的滑動性,在製罐加工時產生樹脂被膜層3的刮損或斷裂。添加的潤滑成分的融點較佳為90℃以上200℃以下,更佳為100℃以上180℃以下。
以作為添加於樹脂被膜層3的潤滑成分而言,從確保與樹脂被膜層3的主成分亦即聚酯樹脂的親和性的觀點來看,較佳為使用具有極性基的有機潤滑成分。作為具有極性基的有機潤滑成分而言,可以例示如:氧化聚乙烯等的聚烯烴氧化劑、乙烯丙烯酸共聚物、乙烯馬來酸酐共聚物等的酸改性聚烯烴等。與樹脂被膜層3的親和性是因有機潤滑成分的酸價等發生變化,但酸價越高,與樹脂被膜層3的親和性越高,在樹脂被膜層3表面的分散大小越小的傾向。
為了取得與樹脂被膜層3較高的親和性,所以控制樹脂被膜層3所含有的潤滑成分的酸價即可。潤滑成分的酸價是1.0mgKOH/g以上100mgKOH/g以下為佳,更佳為1.0mgKOH/g以上50mgKOH/g以下,特佳為2.0mgKOH/g以上45mgKOH/g以下。在樹脂被膜層3所含有的潤滑成分的酸價為未達1.0mgKOH/g的情況下,會有樹脂被膜層3及印刷油墨的親和性降低,且因為潤滑成分濃化在樹脂被膜層表面而阻礙印刷油墨的密合性的可能性。另外,在樹脂被膜層3所含有的潤滑成分的酸價超過100mgKOH/g的情況下,會有因樹脂被膜層3和潤滑成分的親和性變高而發生互溶,且在製罐加工時無法取得必須的摩擦係數降低效果,在製罐加工時發生刮損的可能性。
樹脂被膜層3所含有的潤滑成分,較理想為酸改性聚烯烴或氧化聚烯烴。這些潤滑成分正適合取得前述的性能,另外,因為在樹脂物性及成本面皆優秀,所以適合作為本發明的對象所要求的低成本化和高加工度的樹脂被膜金屬板用的潤滑成分。潤滑成分的重量平均分子量較佳為2500以上且未達80000。在潤滑成分的重量平均分子量未達2500的情況下,會有在樹脂被膜層3內的潤滑成分的可動性提高,潤滑成分濃化於樹脂被膜層3的表面,且阻礙印刷油墨的密合性的可能性。另一方面,在重量平均分子量為80000以上的情況下,會有在加工時無法取得充分的滑動性的可能性。潤滑成分的重量平均分子量,更佳為3000以上且未達75000,特佳為3500以上且未達70000。
樹脂被膜層3為了提高印刷後的設計性所以有被要求是白色的情況。在此情況下,也可以樹脂被膜層3含有30%以下的氧化鈦。氧化鈦的含有量,較佳為10%以上25%以下,更佳為12%以上20%以下。若氧化鈦含有量較少在加工後會有無法確保充分的白色度的可能性。另外,在氧化鈦含有量過多的情況下,會有在加工度較高的成型時,於金屬板2和樹脂被膜層3的密合性、以及樹脂被膜層3的加工性上發生問題的情況。
添加於樹脂被膜層3的氧化鈦雖未特別限定,但較佳為使用金紅石型氧化鈦的純度為90%以上的。在金紅石型氧化鈦的純度未達90%的情況下,在與樹脂材料的混合時氧化鈦的分散性不佳,樹脂被膜層3的品質變得不均一,有發生問題的可能性。
樹脂被膜層3也可以如第1(b)圖所示般,具有由最表面層3a、中間層3b、及最下層3c所成的至少三層構造。在此的情況下,最表面層3a及最下層3c的膜厚是1.0μm以上5.0μm以下為佳,更佳為1.5μm以上4.0μm以下,特佳為2.0μm以上3.0μm以下。而且中間層3b的膜厚是6.0μm以上30μm以下為佳,更佳為8.0μm以上25μm以下,特佳為10μm以上20μm以下。另外,較佳為最表面層3a及最下層3c含有0.0%以上2.0%以下的氧化鈦,中間層3b含有10%以上30%以下的氧化鈦。
因為在最表面層3a及最下層3c的膜厚是比1.0μm更小的情況下,會有無法充分確保樹脂被膜層3的光澤的可能性,以及發生樹脂被膜層3的斷裂或刮損的可能性,所以最表面層3a及最下層3c的膜厚是1.0μm以上為佳。另一方面,在最表面層3a及最下層3c的膜厚是比5.0μm更大的情況下,將產生為了確保白色度所以將中間層3b的膜厚加厚,或使中間層3b所含有的氧化鈦量增加的必要,從經濟性及加工性的觀點來看較為不妥。
[實施例]
使用厚度0.22mm的TFS(Tin Free Steel、金屬Cr層:120mg/m2
、Cr氧化物層:以金屬Cr換算10mg/m2
、調質度:T3CA)作為金屬板,以薄膜積層法(薄膜熱熔接法)來在金屬板的雙面被覆以下的表1~4所示的實施例1~31及比較例1~16的樹脂被膜層。被覆條件是如以下的表1所示。藉由將金屬板加熱,將以積層輥藉由雙軸拉伸法所製作的薄膜狀的樹脂被膜層熱壓接於金屬板,在熱壓接後經過1.5秒後進行水冷,製作金屬板的雙面以樹脂被膜層被覆的樣本。
針對所得到的容器用樹脂被膜金屬板,藉以下所示的方法來測定樹脂被膜層的融點以及在樹脂被膜層表面的潤滑成分的分散大小。
(1)樹脂被膜層的融點
使用示差掃描熱析裝置,以從室溫至290℃為止10℃/min.的升溫速度來將從容器用樹脂被膜金屬板剝離的樹脂被膜層升溫,將在200℃以上280℃以下的範圍的吸熱峰的峰溫度作為樹脂被膜層的融點。樹脂被膜層的剝離是藉著將容器用樹脂被膜金屬板在室溫浸漬於濃鹽酸(12mol/L):蒸餾水=1:1混合溶液中,並將金屬板予溶解來進行。
(2)在樹脂被膜層表面分散的潤滑成分的平均粒徑
使用化學力顯微鏡(CFM),在室溫進行5視野(視野面積:1μm×1μm)容器用樹脂被膜金屬板的樹脂被膜層表面的觀察,針對每個視野任意20個所觀察的潤滑成分的粒,由長徑及短徑的計測結果使用以下的式(1)算出粒徑,以其平均值(5視野×20點=100點的平均值)作為潤滑成分的平均粒徑。於觀察視野未觀察20點的潤滑成分的情況,則針對視野內的全部的粒進行計測,作為其平均值。此外,測定使用探針的先端部有疏水性處理的探針。另外,有關於在未達測量範圍10nm的大小發生分散的潤滑成分,在表1~4記載為「<10」。
(粒徑)={(長徑)×(短徑)}^(1/2)…(1)
針對上述實施例1~31及比較例1~16的容器用樹脂被膜金屬板,藉著以下所示的方法來評價加工性及印墨密合性。在表5表示加工性和印墨密合性的評價結果。如表5所示,在實施例1~31的容器用樹脂被膜金屬板,加工性及印墨密合性皆良好,在比較例1~16加工性及印墨密合性之中任一個的評價結果為不充分。
(1)加工性
將石蠟油塗布於實施例1~31及比較例1~16的容器用樹脂被膜金屬板後,將直徑123mm的圓板打孔,以沖杯機來引伸成型為內徑71mm、高度36mm的杯。接著,將所得到的杯裝入DI成型裝置,以打孔速度200mm/sec.、行程560mm來實施再引伸加工及3段階的引縮加工且總裁減率51%(各步驟的裁減率:23%、25%、25%)的加工,成型為內徑52mm、罐高度90mm的罐。針對成型後的罐,以目視觀察樹脂被膜層表面,依照以下的基準來評價加工性。
評價「◎」:觀察不到刮損。
評價「○」:在離罐緣部2mm以內的高度發生微細刮損。無實用上的問題。
評價「△」:在超過罐緣部2mm且20mm以內的高度發生刮損。有實用上的問題。
評價「×」:在到達超過罐緣部20mm的高度發生刮損,或罐體破損。有實用上的問題。
(2)印墨密合性
實施例1~31及比較例1~16的容器用樹脂被膜金屬板藉由熱風乾燥爐進行熱處理在2分鐘成為樹脂被膜層的融點+8℃,且冷卻至室溫。之後,將聚酯系的印刷油墨(紅色)印刷於位在各樣本的容器外面側的樹脂被膜層,藉由熱風乾燥爐以180℃進行5分鐘的熱處理,且冷卻至室溫。將印刷有所得到的樣本的印墨的面,使用刮擦型塗膜硬度測試機在500g的荷重下,以10mm/min.的速度從印刷端部進行掃描,測定不發生印墨剝落的最大的鉛筆硬度,並依照以下的基準來評價印墨密合性。在罐體的輸送等的各步驟之間發生印刷油墨剝落的情況下,因從印刷端部剝落成為問題的情況較多,因而以將掃描從印刷端部開始的條件來實施評價。
評價「◎」:鉛筆硬度3H以上。
評價「○」:鉛筆硬度2H。無實用上的問題。
評價「△」:鉛筆硬度H。有實用上的問題。
評價「×」:鉛筆硬度為F以下。有實用上的問題。
依據本發明,可以提供:可抑制伴隨加工的樹脂被膜層的斷裂或刮損及印刷後的印刷油墨的剝落的容器用樹脂被膜金屬板。
1‧‧‧容器用樹脂被膜金屬板
2‧‧‧金屬板
3、4‧‧‧樹脂被膜層
3a‧‧‧最表面層
3b‧‧‧中間層
3c‧‧‧最下層
第1圖是表示本發明的一個實施形態的容器用樹脂被膜金屬板的構成的剖面圖。
1‧‧‧容器用樹脂被膜金屬板
2‧‧‧金屬板
3、4‧‧‧樹脂被膜層
3a‧‧‧最表面層
3b‧‧‧中間層
3c‧‧‧最下層
Claims (4)
- 一種容器用樹脂被膜金屬板,是在金屬板的雙面具備樹脂被膜層,其特徵為:在成型加工後位於容器的外面側的前述樹脂被膜層,是以融點在230℃以上254℃以下的範圍的聚酯樹脂作為主成分並且含有潤滑成分,前述潤滑成分的融點為80℃以上230℃以下,存在於前述樹脂被膜層的表面的前述潤滑成分的平均粒徑為17.0nm以下,在成型加工後位於容器的外面側的前述樹脂被膜層所含有的前述潤滑成分,是重量平均分子量2500以上且未達80000,酸價1.0mgKOH/g以上100mgKOH/g以下的酸改性聚烯烴或氧化聚烯烴。
- 如申請專利範圍第1項所述的容器用樹脂被膜金屬板,其中,在成型加工後位於容器的外面側的前述樹脂被膜層所含有的前述潤滑成分,是0.010質量%以上1.0質量%以下的範圍內。
- 如申請專利範圍第1或2項所述的容器用樹脂被膜金屬板,其中,在成型加工後位於容器的外面側的前述樹脂被膜層, 含有30質量%以下的範圍內的氧化鈦。
- 如申請專利範圍第3項所述的容器用樹脂被膜金屬板,其中,在成型加工後位於容器的外面側的前述樹脂被膜層,具有由最表面層、中間層、及最下層所成的至少三層構造,前述最表面層及最下層的膜厚在1.0μm以上5.0μm以下的範圍內,前述中間層的膜厚在6.0μm以上30μm以下的範圍內,前述最表面層及最下層含有0.0質量%以上2.0質量%以下的範圍內的氧化鈦,前述中間層含有10質量%以上30質量%以下的範圍內的氧化鈦。