TW201817704A - 環氧(甲基)丙烯酸酯化合物及含有此化合物之硬化性組成物 - Google Patents
環氧(甲基)丙烯酸酯化合物及含有此化合物之硬化性組成物 Download PDFInfo
- Publication number
- TW201817704A TW201817704A TW106125226A TW106125226A TW201817704A TW 201817704 A TW201817704 A TW 201817704A TW 106125226 A TW106125226 A TW 106125226A TW 106125226 A TW106125226 A TW 106125226A TW 201817704 A TW201817704 A TW 201817704A
- Authority
- TW
- Taiwan
- Prior art keywords
- epoxy
- meth
- formula
- reaction
- acrylate
- Prior art date
Abstract
本發明係提供在導電圖型上,不易產生遷移之保護膜材料的環氧(甲基)丙烯酸酯化合物及含有此化合物之硬化性組成物。 本發明之環氧(甲基)丙烯酸酯化合物,其係以下通式(1)表示,雜質之鹵素原子的含量為100質量ppm以下。又,此環氧(甲基)丙烯酸酯化合物中,混合含有(甲基)丙烯醯基之單體或寡聚物之至少一種、及光聚合起始劑,成為導電圖型之保護膜形成用的硬化性組成物。(R1
~R5
之中之至少1個,具有下述式(2)表示之結構,剩餘的R1
~R5
各自獨立為氫原子、碳原子數為1~6之選自烷基及烷氧基所成群之任一。R6
表示氫原子或甲基)(*表示與構成式(1)中之R1
~R5
所連結之苯環之碳原子的連結部,R7
表示氫原子或甲基)。
Description
[0001] 本發明係有關環氧(甲基)丙烯酸酯化合物及含有此化合物之硬化性組成物。
[0002] 形成於基板上之導電圖型之厚度為非常薄的情形等,有時需要形成保護導電圖型用之絕緣性薄膜的技術。這種絕緣性薄膜的材料,例如下述專利文獻1中揭示環氧丙烯酸酯樹脂,下述專利文獻2中揭示在丙烯酸樹脂系黏結劑(聚合物、單體或寡聚物)中,加入沒食子酸或沒食子酸丙酯。 [先前技術文獻] [專利文獻] [0003] [專利文獻1]日本特開平7-48424號公報 [專利文獻2]日本特開2014-191894號公報
[發明所欲解決之課題] [0004] 但是上述專利文獻1所記載的環氧丙烯酸酯樹脂係由表氯醇之開環聚合所合成。又,丙烯酸酯化時,也使用三乙基苄基銨氯化物。因此,於環氧丙烯酸酯樹脂中,殘留氯分,導電圖型有容易產生遷移的問題。 [0005] 又,使用上述專利文獻2所記載之沒食子酸或沒食子酸丙酯之保護膜的情形,依據專利文獻2之發明人等,將含有經合成之奈米銀線的水分散體,塗佈於高透明PET薄膜之易接著面上,經乾燥後加壓處理所得之透明導電薄膜上,形成了保護層之導電層的信賴性試驗的結果,大多被認為在85℃、85%相對濕度條件下,放置500小時後,形成保護層之導電層之塗膜表面的薄片電阻上昇率為20%以上、未達30%的結果(參照表1),且成為導電圖型之劣化或外加電場時之遷移等疑慮的結果。 [0006] 本發明之目的係提供一種成為在導電圖型上不易產生遷移之保護膜材料的環氧(甲基)丙烯酸酯化合物及含有此化合物的硬化性組成物。 [用以解決課題之手段] [0007] 本發明包含以下的實施態樣。 [0008] [1]一種環氧(甲基)丙烯酸酯化合物,其係以下通式(1)表示,鹵素原子之含量為100質量ppm以下。(R1
~R5
之中之至少1個,具有下述式(2)表示之結構,剩餘的R1
~R5
各自獨立為氫原子、碳原子數為1~6之選自烷基及烷氧基所成群之任一。R6
表示氫原子或甲基)(*表示與式(1)中之R1
~R5
所連結之構成苯環之碳原子的連結部,R7
表示氫原子或甲基)。 [0009] [2]如[1]之環氧(甲基)丙烯酸酯化合物,其中前述環氧(甲基)丙烯酸酯化合物為式(3)或式(4)表示的化合物。(式中,R8
表示氫原子或甲基)(式中,R9
表示氫原子或甲基)。 [0010] [3]一種硬化性組成物,其係含有[1]或[2]之環氧(甲基)丙烯酸酯化合物、含有(甲基)丙烯醯基之單體及寡聚物之至少一種、及光聚合起始劑。 [發明效果] [0011] 依據本發明時,可提供一種成為在導電圖型上不易產生遷移之保護膜材料的環氧(甲基)丙烯酸酯化合物及含有此化合物的油墨(ink)組成物。
[0013] 以下說明本實施發明之形態(以下稱實施形態)。又,本說明書中,(甲基)丙烯酸酯,表示丙烯酸酯或甲基丙烯酸酯,(甲基)丙烯酸表示丙烯酸或甲基丙烯酸,(甲基)丙烯醯基表示丙烯醯基或甲基丙烯醯基。 [0014] 環氧(甲基)丙烯酸酯化合物 實施形態之環氧(甲基)丙烯酸酯化合物,其特徵係具有在苯環上,經由碳原子、或碳原子及氧原子鍵結之複數的環氧基,與(甲基)丙烯酸之羧基進行鍵結的結構,鹵素原子之含量為100質量ppm以下。上述環氧基係經由碳原子、或碳原子及氧原子,複數鍵結於1個苯環上。 [0015] 上述環氧(甲基)丙烯酸酯化合物係以下的通式表示。 [0016](R1
~R5
之中之至少1個,具有下述式(2)表示之結構,剩餘的R1
~R5
各自獨立為氫原子、碳原子數為1~6之選自烷基及烷氧基所成群之任一。R6
表示氫原子或甲基。) [0017](*表示與式(1)中之R1
~R5
所連結之構成苯環之碳原子的連結部,R7
表示氫原子或甲基)。 [0018] 較佳之碳原子數為1~6的烷基及烷氧基,可列舉甲基、乙基、異丙基、t-丁基、甲氧基、乙氧基、異丙氧基、t-丁氧基等。上述環氧(甲基)丙烯酸酯化合物的具體例,可列舉以下結構的丁香酚型環氧(甲基)丙烯酸酯。 [0019](式中,R8
表示氫原子或甲基)。 [0020] 又,上述具體例,可列舉以下結構之2-烯丙基苯酚型環氧(甲基)丙烯酸酯。 [0021](式中,R9
表示氫原子或甲基)。 [0022] 又,本說明書中,丁香酚型、2-烯丙基苯酚型係分別表示合成對應之環氧化合物時之起始原料之具有羥基的化合物(醇或苯酚)。 [0023] 成為原料之在苯環上,具有經由碳原子、或碳原子及氧原子進行鍵結之環氧基的化合物,較佳為來自如上述之丁香酚或2-烯丙基苯酚的環氧化物。丁香酚、2-烯丙基苯酚均有市售,容易取得,此等在分子中含有1個與苯環鍵結之烯丙基,故再導入烯丙基時,以容易起火之鈀碳(Pd/C)作為觸媒使用時,可減少其使用量。藉由使用此等之環氧當量低的原料,可製造丙烯酸酯官能基濃度高的環氧(甲基)丙烯酸酯,可設計硬化塗膜之高交聯密度。又,因含有苯環,藉由與芳香環之π相互作用,與PET(聚對苯二甲酸乙二酯)、PEN(聚萘二甲酸乙二酯)、PI(聚醯亞胺)等含有芳香族環之基材的密著性變佳。 [0024] 上述丁香酚型環氧化物或2-烯丙基苯酚型環氧化物,較佳為將構成原料之丁香酚之烯丙醚或2-烯丙基苯酚之烯丙醚之烯丙基的碳-碳雙鍵,藉由過氧化氫進行了環氧化者,可得到不含鹵素的環氧化合物。 [0025] 丁香酚型環氧化物,可藉由例如以丁香酚之烯丙醚化合物作為原料使用之以下式(5)表示的反應來製造。 [0026][0027] 又,2-烯丙基苯酚型環氧化物,可藉由例如以2-烯丙基苯酚之烯丙醚化合物作為原料使用之以下式(6)表示的反應來製造。 [0028][0029] 過氧化氫源較佳為使用過氧化氫水溶液。過氧化氫水溶液之濃度無特別限制,一般而言,較佳為1~60質量%,更佳為5~50質量%,又更佳為10~40質量%。1質量%以上時,在工業上生產性的觀點、及分離時之能量成本的觀點較佳,60質量%以下時,在經濟性、安全性等的觀點較佳。 [0030] 過氧化氫之使用量,無特別限制,因反應進行,過氧化氫被消耗,故藉由繼續追加補充,將反應系內之濃度維持一定較佳。相對於原料之烯丙醚化合物之碳-碳雙鍵,過氧化氫之反應系內存在濃度保持為0.01~0.5莫耳當量,更佳為0.02~0.2莫耳當量,又更佳為0.05~0.1莫耳當量之範圍。過氧化氫之系內存在濃度,相對於原料之烯丙醚化合物之碳-碳雙鍵,為0.01莫耳當量以上時,生產性良好,為0.5莫耳當量以下時,在溶劑與水之混合組成中,可確保充分的安全性。反應初期,在反應系內一度投入多量的過氧化氫時,反應急遽進行,有危險的情形,故如後述,過氧化氫徐徐添加至反應系內為佳。反應終期之反應系內的過氧化氫濃度,無限制,相對於原料之烯丙醚化合物之碳-碳雙鍵時,過氧化氫之系內存在濃度可設為0.01莫耳當量以下。 [0031] 上述反應中,使用乙腈,在鹼共存下,使用過氧化氫進行烯丙基之環氧化。對於乙腈,過氧化氫產生作用,形成對氧化反應活性的過醯亞胺酸,過醯亞胺酸成為反應活性種,進行氧化反應。此方法可由中性至鹼性下進行反應。因此,泛用性高,不使用特殊的試劑,故於成本上有利。 [0032] 乙腈在反應開始時之投入量係相對於原料之烯丙醚化合物的碳-碳雙鍵,腈基設為2.0~15莫耳當量的範圍為佳,更佳為3.0~10莫耳當量,又更佳為4.0~8.0莫耳當量。無法一概以原料之烯丙醚化合物的結構來決定,但是藉由相對於原料之烯丙醚化合物的碳-碳雙鍵,以乙腈的腈基成為2~15莫耳當量之範圍的量使用乙腈時,反應液容易變成均勻相,故較佳。又,乙腈之腈基的上述量為2莫耳當量以上時,收率良好,15莫耳當量以下時,過氧化氫之環氧化選擇率及成本良好。 [0033] 反應中,也可添加乙腈。乙腈之總使用量,相對於追添時之反應所使用之原料之烯丙醚化合物的總使用量之比例(乙腈/原料之烯丙醚化合物的碳-碳雙鍵(莫耳比))也為上述範圍,亦即較佳為2.0~15,更佳為3.0~10,又更佳為4.0~8.0。 [0034] 乙腈存在下,進行環氧化反應時,在反應液中,使供質子性溶劑共存,供質子性溶劑之存在下,使過氧化氫對於原料之烯丙醚化合物,產生作用為佳。供質子性溶劑係作為原料之烯丙醚化合物的溶劑產生機能。原料之烯丙醚化合物的黏度較高的情形時,供質子性溶劑也可作為對原料之烯丙醚化合物,提高過氧化氫之移動速度用的黏度稀釋劑產生機能。 [0035] 具體的供質子性溶劑,可列舉醇、胺、硫醇等。也可組合使用此等的供質子性溶劑。其中,醇特別是原料之烯丙醚化合物的親水性較低時,具有抑制原料之烯丙醚化合物及含有乙腈的有機相與含有過氧化氫之水相的分離,使反應液形成均勻相,提高反應速度的作用,故較佳。醇之中,較佳為碳原子數1~4之醇,更佳為碳原子數1~4之一級醇,又更佳為甲醇、乙醇、及1-丙醇。 [0036] 供質子性溶劑之使用量係相對於原料之烯丙醚化合物100質量份,較佳為10~1000質量份之範圍,更佳為80~800質量份之範圍,又更佳為100~500質量份之範圍。無法一概以原料之烯丙醚化合物的結構來決定,但是相對於原料之烯丙醚化合物100質量份,藉由以10~1000質量份之範圍使用供質子性溶劑,可使反應液容易變成均勻相,故較佳。又,相對於原料之烯丙醚化合物100質量份,供質子性溶劑之使用量為10質量份以上、1000質量份以下時,反應速度良好。 [0037] 供質子性溶劑之使用量係相對於乙腈100質量份,較佳為20~500質量份之範圍,更佳為25~400質量份之範圍,又更佳為33~300質量份之範圍。相對於疏水性更高、乙腈等對有機溶劑之溶解性高之原料的烯丙醚化合物,使增加乙腈的比率,亦即,相對於乙腈100質量份,使供質子性溶劑的量接近20質量份,進行反應為佳。 [0038] 含有原料之烯丙醚化合物之反應液的任意時點的pH,較佳為8~12的範圍,更佳為9~11,又更佳為9.5~11之範圍。pH為8以上時,反應速度良好,且可保持高生產性,12以下時,反應時可確保充分的安全性及收率。過氧化氫在高鹼環境下,活潑地產生分解,故反應初期的階段時,pH為9~10左右,在過氧化氫之添加同時,必要時,慢慢地將反應液之pH控制在10~11左右更佳。 [0039] 為了調整反應液的pH,使用鹼化合物,對於原料的烯丙醚化合物,在鹼化合物存在下,也可使過氧化氫產生作用。反應液之pH調整可用的鹼化合物,可列舉例如碳酸鉀、碳酸氫鉀、氫氧化鉀、氫氧化鈉、氫氧化銫等之無機鹼鹽、及甲醇鉀、乙醇鉀、甲醇鈉、乙醇鈉、氫氧化四甲基銨等之有機鹼鹽。在容易調整pH的觀點,較佳為碳酸鉀、碳酸氫鉀、氫氧化鉀、氫氧化鈉、甲醇鉀、乙醇鉀、甲醇鈉、及乙醇鈉。氫氧化鉀及氫氧化鈉,對水及醇的溶解性高,反應性也佳,故更佳。 [0040] 鹼化合物可溶解於水或供質子性溶劑的溶液來使用,且如前述溶解後使用為佳。供質子性溶劑較佳為醇,可列舉例如甲醇、乙醇、丙醇、丁醇等,使用與前述供質子性溶劑相同者為佳。反應液的pH隨著過氧化氫之添加避免低於9來追加鹼化合物溶液較佳。 [0041] 原料的烯丙醚化合物、過氧化氫、乙腈、供質子性溶劑及鹼化合物,對反應系的添加順序及態樣,無特別限制,考慮工業上安定地生產時,原料的烯丙醚化合物、乙腈及供質子性溶劑在最初投入於反應器中,儘量使反應溫度保持一定,且邊確認過氧化氫在反應被消耗,邊慢慢添加過氧化氫水溶液,可促進環氧化反應,反應生成物之分離及純化容易的觀點,較佳。採用這種方法時,即使在反應器內,過氧化氫異常分解,產生氧氣體,過氧化氫之蓄積量少,也可將壓力上昇抑制在最低。 [0042] 反應在均勻相(homogeneous phase)中進行。藉由使反應液形成均勻相,可使原料的烯丙醚化合物與環氧化所必要的過氧化氫及乙腈,不需經由相間移動,以效率良好進行反應。因此,反應後的未反應物變少,可以高收率製造目的之環氧化物。使反應液形成均勻相用之各成分的量比,因原料之烯丙醚化合物的結構而改變,無法一概而論。但是如前述,可藉由將乙腈及/或供質子性溶劑變更為適當的量,來調整。 [0043] 如前述,反應液的任意時點的pH,較佳為8~12的範圍。為了調整反應液的pH,追加任意成分之鹼化合物的時期,無特別限制。可將所定量的鹼化合物在最初投入反應器中,此時也可在反應中追加或不追加。也可不將鹼化合物在最初投入反應器中,而僅在反應中追加。過氧化氫在高鹼環境下,活潑地產生分解,故反應初期的階段時,pH為9~10左右,在過氧化氫之添加同時,必要時,慢慢地將反應液之pH控制在10~11左右更佳。 [0044] 反應溫度較佳為0℃~60℃的範圍,更佳為10℃~50℃,又更佳為20℃~40℃。反應溫度為0℃以上時,反應良好進行,60℃以下時,可抑制乙腈及供質子性溶劑揮發或沸騰。 [0045] 反應時間係受反應溫度左右,無法一概決定,但是通常為2~100小時的範圍,較佳為4~80小時,更佳為6~60小時的範圍。 [0046] 反應終了後,回收含有反應生成物的有機層,藉由濃縮可得到反應粗生成物。反應液通常含有過氧化氫,故除去反應液中的水分後,回收含有反應生成物的有機層時,為了避免因過氧化氫之濃縮所致之爆發危険性,預先還原除去過氧化氫為佳。還原除去所使用之還原劑,可列舉亞硫酸鈉、硫代硫酸鈉等,但是不限定於此等的還原劑。又,回收含有反應生成物的有機層時,為了有效率地分離除去反應液中的水分與含有反應生成物的有機層,在反應液中,添加與水之相溶性低之適量的有機溶劑為佳。使用之有機溶劑例,可列舉甲苯、乙酸乙酯、二氯甲烷等,但是不限定於此等的有機溶劑。藉由此處理,除去殘存於反應液中的過氧化氫,同時可分離水層與含有有機溶劑的有機層。 [0047] 如上述,濃縮與水層分離後的有機層後,藉由蒸餾、色層分離、再結晶、昇華等的通常方法,可取出生成之原料之烯丙醚化合物的環氧化物。 [0048] 使如以上製造的丁香酚型環氧化物與(甲基)丙烯酸反應時,可製造(式(7))、實施形態之環氧(甲基)丙烯酸酯化合物的丁香酚型環氧(甲基)丙烯酸酯。 [0049](式中,R8
表示氫原子或甲基)。 [0050] 又,使上述2-烯丙基苯酚型環氧化物與(甲基)丙烯酸反應時,可製造(式(8))、實施形態之環氧(甲基)丙烯酸酯化合物的2-烯丙基苯酚型環氧(甲基)丙烯酸酯。 [0051](式中,R9
表示氫原子或甲基)。 [0052] (甲基)丙烯酸加成於環氧化物時,可以無溶劑反應,也可使用溶劑。前述溶劑為不阻礙反應的溶劑時,無特別限定,可列舉例如丙二醇單甲醚乙酸酯、二乙二醇單乙醚乙酸酯等之酯系溶劑。環氧化物與(甲基)丙烯酸之反應觸媒,可使用例如三苯基膦、三丁基膦等之膦系觸媒、二氮雜雙環十一碳烯等之三級胺系觸媒、乙基咪唑等之咪唑系觸媒。又,為了防止反應中之(甲基)丙烯醯基之聚合目的,可使用聚合抑制劑,例如對苯二酚、對苯二酚單甲醚、吩噻嗪、2,6-二-t-丁基-p-甲酚等。 [0053] 上述環氧化物與(甲基)丙烯酸之反應條件,反應溫度為20℃~180℃,較佳為50℃~150℃,更佳為60℃~130℃,反應時間為1~24小時,酸價成為5以下的時點作為終點。相對於環氧化物,(甲基)丙烯酸的添加量為相對於環氧化物的環氧基,較佳為1~2當量,更佳為1~1.5當量。即使不使用反應觸媒也可進行反應,但是使用反應觸媒的情形時,相對於(甲基)丙烯酸100質量份,使用0.1~2質量份為佳。使用聚合抑制劑的情形時,相對於(甲基)丙烯酸100質量份,較佳為使用0.01~1質量份。 [0054] 硬化性組成物 實施形態之硬化性組成物係除了上述環氧(甲基)丙烯酸酯化合物,包含光聚合起始劑、含有(甲基)丙烯醯基之單體或寡聚物之至少一種。光聚合起始劑,無特別限定,從對紫外線之反應性高的觀點,較佳為使用光自由基起始劑。光自由基起始劑,可列舉例如苯乙酮、苯丙酮、二苯甲酮、呫噸醇(xanthol)、茀、苯甲醛、蒽醌、三苯基胺、咔唑、3-甲基苯乙酮、4-甲基苯乙酮、3-戊基苯乙酮、2,2-二乙氧基苯乙酮、4-甲氧基苯乙酮、3-溴苯乙酮、4-烯丙基苯乙酮、p-二乙醯基苯、3-甲氧基二苯甲酮、4-甲基二苯甲酮、4-氯二苯甲酮、4,4’-二甲氧基二苯甲酮、4-氯-4’-苄基二苯甲酮、3-氯呫噸酮、3,9-二氯呫噸酮、3-氯-8-壬基呫噸酮、苯偶姻、苯偶姻甲醚、苯偶姻丁醚、雙(4-二甲基胺基苯基)酮、苄基甲氧基縮醛、2-氯呫噸酮、2,2-二甲氧基-1,2-二苯基乙烷-1-酮(IRGACURE(註冊商標)651、BASF JAPAN製)、1-羥基-環己基-苯基-酮(IRGACURE(註冊商標)184、BASF JAPAN製)、2-羥基-2-甲基-1-苯基-丙烷-1-酮(DAROCUR(註冊商標)1173、BASF JAPAN製)、1-[4-(2-羥基乙氧基)-苯基]-2-羥基-2-甲基-1-丙烷-1-酮(IRGACURE(註冊商標)2959、BASF JAPAN製)、2-甲基-1-[4-(甲基硫基)苯基]-2-嗎啉基丙烷-1-酮(IRGACURE(註冊商標)907、BASF JAPAN製)、2-苄基-2-二甲基胺基-1-(4-嗎啉基苯基)-丁酮-1(IRGACURE(註冊商標)369、BASF JAPAN製)、2-(4-甲基苄基)-2-二甲基胺基-1-(4-嗎啉-4-基-苯基)-丁烷-1-酮(IRGACURE(註冊商標)379、BASF JAPAN製)、聯苯醯(Dibenzoyl)等。 [0055] 此等之中,較佳為α-羥基酮化合物(例如、苯偶姻、苯偶姻甲醚、苯偶姻丁醚、1-羥基-環己基-苯基-酮等)、苯基酮衍生物(例如、苯乙酮、苯丙酮、二苯甲酮、3-甲基苯乙酮、4-甲基苯乙酮、3-戊基苯乙酮、2,2-二乙氧基苯乙酮、4-甲氧基苯乙酮、3-溴苯乙酮、4-烯丙基苯乙酮、3-甲氧基二苯甲酮、4-甲基二苯甲酮、4-氯二苯甲酮、4,4’-二甲氧基二苯甲酮、4-氯-4’-苄基二苯甲酮、雙(4-二甲基胺基苯基)酮等)。 [0056] 藉由前述製造方法所得之上述各環氧(甲基)丙烯酸酯化合物係作為導電圖型之保護膜使用之環氧(甲基)丙烯酸酯組成物時,可抑制遷移之發生。上述組成物,可列舉在各環氧(甲基)丙烯酸酯化合物中,混合有含有(甲基)丙烯醯基之單體或寡聚物、光聚合起始劑者。此等之摻合比例係因組成物之保護膜形成方法而異,但是環氧(甲基)丙烯酸酯化合物可使用20~90質量份、含有(甲基)丙烯醯基之單體或寡聚物可使用10~80質量份、相對於環氧(甲基)丙烯酸酯化合物與含有(甲基)丙烯醯基之單體或寡聚物的總量100質量份,可使用光聚合起始劑1~5質量份。 [0057] 含有(甲基)丙烯醯基之單體或寡聚物,可列舉三羥甲基丙烷三丙烯酸酯、新戊二醇聚丙氧基二丙烯酸酯、新戊二醇二丙烯酸酯、三羥甲基丙烷聚乙氧基三丙烯酸酯、雙酚F聚乙氧基二丙烯酸酯、雙酚A聚乙氧基二丙烯酸酯、二季戊四醇聚己內酯(Hexanolide)六丙烯酸酯、三(羥基乙基)異三聚氰酸酯聚己內酯三丙烯酸酯、三環癸烷二羥甲基二丙烯酸酯、2-(2-丙烯醯氧基-1,1-二甲基)-5-乙基-5-丙烯醯氧基甲基-1,3-二噁烷、四溴雙酚A二乙氧基二丙烯酸酯、4,4-二巰基二苯基硫化物二甲基丙烯酸酯、聚四乙二醇二丙烯酸酯、1,9-壬二醇二丙烯酸酯、1,6-己烷二丙烯酸酯、二羥甲基三環癸烷二丙烯酸酯、二(三羥甲基)丙烷四丙烯酸酯、四羥甲基甲烷四丙烯酸酯、季戊四醇三丙烯酸酯、季戊四醇四丙烯酸酯、二季戊四醇單羥基五丙烯酸酯、二季戊四醇六丙烯酸酯、1,4-丁二醇二丙烯酸酯、聚乙二醇二丙烯酸酯、市售之寡酯(Oligoester)丙烯酸酯或芳香族系、脂肪族系等之胺基甲酸酯丙烯酸酯(寡聚物)等。 [0058] 又,上述組成物中也可含有溶劑。此溶劑可列舉合成前述環氧(甲基)丙烯酸酯化合物時可使用的溶劑。 [0059] 又,將製造階段作為原料使用的環氧化物,作為如上述之不含鹵素者時,製造的環氧(甲基)丙烯酸酯化合物中,可大幅減低作為雜質所含有的鹵素。因此,上述環氧(甲基)丙烯酸酯化合物,鹵素原子之含量可為100質量ppm以下,適合為50質量ppm以下。較佳為30質量ppm以下,更佳為15質量ppm以下。 [實施例] [0060] 以下具體地說明本發明之實施例。又,以下的實施例為容易理解本發明者,本發明不限制於此等的實施例者。 [0061] <酸價之測量方法> 本實施例中,酸價係藉由以下方法測量的值。 [0062] 100ml的三角燒瓶中,以精密天秤精秤試料約0.2g,此燒瓶中添加乙醇/甲苯=1/2(質量比)的混合溶劑10ml溶解。此外,此容器中添加1~3滴,作為指示藥劑的酚酞乙醇溶液,充分攪拌直到試料均勻為止。將此試料以0.1N氫氧化鉀-乙醇溶液滴定,指示藥劑之微紅色持續30秒時,作為中和的終點。由該結果使用下述計算式所得之值作為試料的酸價。 酸價(mgKOH/g)=〔B×f×5.611〕/S B:0.1N氫氧化鉀-乙醇溶液之使用量(ml) f:0.1N氫氧化鉀-乙醇溶液之參數(Factor) S:試料之採取量(g) [0063] <黏度之測量方法> 本實施例中,黏度係藉由以下方法測量的值。 使用Brookfield公司製B型黏度計DV-II+Pro,在25℃測量試料的黏度。又,黏度超過10000mPa・s的情形時,使用轉子(Rotor)編號52,而10000mPa・s以下的情形時,使用轉子編號40測量。 [0064] <環氧當量之測量法> 環氧當量之測量法係依據JIS K7236:2001測量。 [0065] [原料合成例1]基質(2-烯丙基苯酚烯丙醚)之合成 在3L三口圓底燒瓶中,投入將碳酸鉀(日本曹達股份公司製)567g(4.10mol)溶解於純水750g的溶液、及式(9)表示之2-烯丙基苯酚(東京化成工業股份公司製)500g(3.73mol),將反應器進行氮氣取代,加熱至85℃。氮氣流下,加入乙酸烯丙酯(昭和電工股份公司製)448g(4.47mol)、三苯基膦(北興化學股份公司製)9.77g(37.3mmol)、及50%含水5%-Pd/C-STD型(N.E.-chemcat股份公司製)3.17g(0.750mmol(作為Pd原子)),氮氣環境中,升溫至105℃,使反應4小時後,追加乙酸烯丙酯44.8g(0.447mol),繼續加熱12小時。反應終了後,將反應系冷卻至室溫後,添加純水使析出的鹽全部溶解為止,進行分液處理。分離有機層,餾除有機溶劑(70℃、50mmHg、2小時)。添加純水(500g)後,添加甲苯500g,保持80℃以上的溫度,確認未析出白色沉澱後,藉由過濾(使用1微米的薄膜過濾器(Advantec公司製KST-142-JA加壓(0.3MPa))回收Pd/C。以甲苯100g洗凈此濾渣(filter residue),同時分離水層。以50℃以上,使用純水500g,2次洗凈有機層,確認水層為中性。分離有機層後,減壓下、濃縮,得到以式(10)表示之2-烯丙基苯酚之烯丙醚化合物為主成分的淡黃色液體(669g、3.66mol、98.0%收率)。此淡黃色液體進行1
H-NMR測量的結果,確認含有以式(10)表示之化合物為主成分。屬於式(10)表示之化合物的測量數據如下述。 [0066]1
H-NMR{400MHz, CDCl3
, 27℃}, δ3.32(2H, dt, PhCH 2
CH=CH2
), δ4.54(2H, dt, PhOCH 2
CH=CH2
), δ5.01-5.09 (2H, m, PhCH2
CH=CH 2
), δ5.27(1H, dq, PhOCH2
CH= CH
H), δ5.42(1H, dq, PhOCH2
CH=CHH
), δ5.95(1H, m, PhCH2
CH
=CH2
), δ6.06(1H, m, PhOCH2
CH
=CH2
), δ6.92(m, 2H, aromatic), δ7.09(2H, m, aromatic)。 [0067][0068][0069] [原料合成例2] 基質(丁香酚烯丙醚)之合成 與原料合成例1同樣的條件下,將基質由2-烯丙基苯酚變更為丁香酚,實施反應。反應所使用之試劑的物質量、所得之目的物之烯丙醚體的物性數據如以下所示。 [0070] 在3L三口圓底燒瓶中,投入將碳酸鉀(日本曹達股份公司製)463g(3.35mol)溶解於純水750g的溶液、式(11)表示之丁香酚(東京化成工業股份公司製)500g(3.04mol),將反應器進行氮氣取代,加熱至85℃。氮氣流下,加入乙酸烯丙酯(昭和電工股份公司製)366g(3.65mol)、三苯基膦(北興化學股份公司製)8.00g(30.5mmol)、及50%含水5%-Pd/C-STD型(N.E.-chemcat股份公司製)2.59g(0.610mmol(作為Pd原子)),氮氣環境中,升溫至105℃,使反應4小時後,追加乙酸烯丙酯36.6g(0.365mol),繼續加熱12小時。反應終了後,將反應系冷卻至室溫後,添加純水使析出的鹽全部溶解為止,進行分液處理。分離有機層,餾除有機溶劑(70℃、50mmHg、2小時)。添加純水(500g)後,添加甲苯500g,保持80℃以上的溫度,確認未析出白色沉澱後,藉由過濾(使用1微米的薄膜過濾器(Advantec公司製KST-142-JA加壓(0.3MPa))回收Pd/C。以甲苯100g洗凈此濾渣,同時分離水層。以50℃以上,使用純水500g,2次洗凈有機層,確認水層為中性。分離有機層後,減壓下、濃縮,得到以式(12)表示之丁香酚之烯丙醚化合物為主成分的淡黃色液體(611g,2.99mol、98.5%收率)。 [0071][0072][0073] [合成例1]丁香酚型環氧化物之合成 將上述原料合成例2所得之丁香酚之烯丙醚化合物300g(1.47mol)、乙腈(純正化學股份公司製)707g(17.2mol)、甲醇(純正化學股份公司製)1240g(38.6mol)投入於5L三口燒瓶中,添加少量50質量%氫氧化鉀水溶液(和光純藥工業股份公司製),將反應液之pH調整為約10.5後,在內溫35℃下,將30質量%過氧化氫水溶液(三菱瓦斯化學股份公司製)1040g(9.18mol)以內溫不超過45℃,花費18小時滴下。又,添加過氧化氫水溶液時,pH會降低,故為了將pH維持9.0~11,也以另外方式滴下50質量%氫氧化鉀水溶液。反應後,添加10%亞硫酸鈉水溶液500g(將和光純藥工業股份公司製之亞硫酸鈉溶解於純水者)與甲苯750g,在室溫下攪拌30分鐘。分離水層後,以純水500g洗淨2次後,藉由餾除溶劑,可得到反應生成物(目的物)。所得之丁香酚型環氧化物(EUGG)的環氧當量為122g/eq。此生成物進行1
H-NMR測量的結果如圖1所示。藉此確認含有以式(13)表示之化合物為主成分者。 [0074][0075] [合成例2]2-烯丙基苯酚型環氧化物之合成 將上述原料合成例1所得之2-烯丙基苯酚之烯丙醚化合物300g(1.72mol)、乙腈(純正化學股份公司製)980g(23.9mol)、甲醇(純正化學股份公司製)330g(10.3mol)投入於5L三口燒瓶中,添加少量50質量%氫氧化鉀水溶液(和光純藥工業股份公司製),將反應液之pH調整為約10.5後,在內溫35℃下,將30質量%過氧化氫水溶液(三菱瓦斯化學股份公司製)1170g(10.3mol)以內溫不超過45℃,花費18小時滴下。又,添加過氧化氫水溶液時,pH會降低,故為了將pH維持9.0~11,也以另外方式滴下50質量%氫氧化鉀水溶液。反應後,添加10質量%亞硫酸鈉水溶液500g(將和光純藥工業股份公司製之亞硫酸鈉溶解於純水者)與甲苯750g,在室溫下攪拌30分鐘。分離水層後,將有機層(甲苯)以純水500g洗淨2次後,藉由餾除溶劑,可得到反應生成物(目的物)。所得之2-烯丙基苯酚型環氧化物(2APG)之環氧當量為112g/eq。此生成物進行1
H-NMR測量的結果如圖2所示。藉此確認含有以式(14)表示之化合物為主成分者。 [0076][0077] [合成例3]丁香酚型環氧化物之合成 依據Polym Int 2014;63:760-765合成EUGG。 [0078] [合成例4]2-烯丙基苯酚型環氧化物之合成 依據美國專利第2965607號公報合成2APG。 [0079] 實施例1 丁香酚型環氧丙烯酸酯(EUGG丙烯酸酯)之合成 將合成例1合成的丁香酚型環氧化物(EUGG)50.1g(考慮了環氧當量的環氧基:0.205mol)、吩噻嗪(和光純藥製)0.016g、三苯基膦(北興化學製)0.264g投入燒瓶中,在70℃下攪拌。將丙烯酸(昭和電工製)29.8g(0.414mol)慢慢滴下於其中。滴下後,升溫至120℃進行攪拌。適時取樣測量酸價。4小時後,成為酸價5以下,故作為反應終點。收量為72.5g,收率為93.0%,酸價為2.3,黏度為139000mPa・s。 [0080] 藉由1
H-NMR鑑定所得之化合物。圖3表示上述1
H-NMR光譜。圖3中,存在於圖1之3.2ppm及2.6ppm附近,來自環氧基的波峰消失,在5.9~6.4ppm附近,可重新確認來自丙烯醯基之波峰,故確認可得到式(15)表示之EUGG丙烯酸酯。 [0081][0082] 又,所得之EUGG丙烯酸酯之1
H-NMR光譜的訊號如以下所示。 7.3ppm(s、1H)、6.9ppm(t、1H)、6.8ppm(s、1H)、6.4ppm(m、2H)、6.2ppm(m、2H)、5.9ppm(m、2H)、4.5ppm(q、H)、4.3ppm(m、2H)、4.1ppm(m、2H)、3.8ppm(s、3H)、2.9ppm(d、H)、2.8ppm(m、2H)。 [0083] 實施例2 2-烯丙基苯酚型環氧丙烯酸酯(2APG丙烯酸酯)之合成 將合成例2合成的2-烯丙基苯酚型環氧化物(2APG)50.0g(考慮環氧當量的環氧基:0.223mol)、吩噻嗪(和光純藥製)0.016g、三苯基膦(北興化學製)0.260g投入燒瓶中,在70℃下攪拌。將丙烯酸(昭和電工製)32.6g(0.452mol)慢慢滴下於其中。滴下後,升溫至120℃進行攪拌。適時取樣測量酸價。5小時後,成為酸價5以下,故作為反應終點。收量為73.0g,收率為93.4%,酸價為3.7,黏度為125000mPa・s。 [0084] 藉由1
H-NMR鑑定所得的化合物。圖4表示上述1
H-NMR光譜。圖4中,存在於圖2之3.2ppm及2.6ppm附近,來自環氧基的波峰消失,在5.9~6.5ppm附近,可重新確認來自丙烯醯基之波峰,故確認式(16)表示之2APG丙烯酸酯之合成。 [0085][0086] 又,所得之2APG丙烯酸酯之1
H-NMR光譜的訊號如以下所示。 7.5ppm(t、1H)、7.3ppm(s、1H)、7.2ppm(m、1H)、6.9ppm(dq、1H)、6.5ppm(q、2H)、6.2ppm(q、2H)、5.9ppm(t、2H)、4.4ppm(m、2H)4.1ppm(m、2H)、3.6ppm(m、H)、2.9ppm(m、1H)、2.8ppm(m、2H)。 [0087] 比較例1 除了使用同質量之合成例3合成的EUGG,取代合成例1合成的EUGG外,與實施例1同樣進行。 [0088] 比較例2 除了使用同質量之合成例4合成的2APG,取代合成例2合成的2APG,與實施例2同樣進行。 [0089] <全氯量測量> 依據JIS K-7243-3,測量實施例1~2及比較例1~2之環氧丙烯酸酯化合物的全氯量。結果如表1所示。 [0090][0091] 由表1可知,使用了合成例1~2之環氧丙烯酸酯化合物的實施例1~2,相較於使用了合成例3~4之環氧丙烯酸酯化合物的比較例1~2,更低氯量。 [0092] <信賴性試驗> 使用在實施例1~2及比較例1~2之環氧丙烯酸酯化合物各70質量份中,調配市售之多官能聚酯丙烯酸酯(東亞合成製M-7100)27質量份、作為光起始劑之IRGACURE(註冊商標)184(3質量份),並經均勻混合的各硬化性組成物,藉由塗佈棒印刷於ISO 9455-17所規定之梳形測量試驗片的梳形圖型上,厚度成為約5μm,使用小型UV照射裝置 QRU-2161-Z11-00(股份公司ORC製作所),製作藉由曝光約40mW/cm2
,使硬化的試驗片。 [0093] 將使用上述各硬化性組成物製作的試驗片各10個,於85℃、85RH%的恆溫恆濕槽內保管,外加電壓100V、經過1000小時後,電極間的絕緣阻抗成為初期電阻值(10之11次方等級)之1000分之一以下的試驗片,判定為產生了遷移,計算該試驗片數。結果如表2所示。表2中記載產生了遷移的試驗片數。 [0094][0095] 如表2所示,使用了實施例1~2之環氧丙烯酸酯化合物的環氧丙烯酸酯組成物,未確認遷移之發生。然而,使用了比較例1~2之環氧丙烯酸酯化合物的環氧丙烯酸酯組成物,以高的比例發生了遷移。此乃是各比較例之環氧丙烯酸酯化合物所含有之鹵素(氯)的比例,遠高於各實施例的緣故。
[0012] [圖1]以合成例1合成之丁香酚(eugenol)型環氧化物的1
H-NMR光譜。 [圖2]以合成例2合成之2-烯丙基苯酚型環氧化物的1
H-NMR光譜。 [圖3]實施例1之丁香酚型環氧丙烯酸酯的1
H-NMR光譜。 [圖4]實施例2之2-烯丙基苯酚型環氧丙烯酸酯的1
H-NMR光譜。
Claims (3)
- 一種環氧(甲基)丙烯酸酯化合物,其係以下通式(1)表示,鹵素原子之含量為100質量ppm以下,(R1 ~R5 之中之至少1個,具有下述式(2)表示之結構,剩餘的R1 ~R5 各自獨立為氫原子、碳原子數為1~6之選自烷基及烷氧基所成群之任一,R6 表示氫原子或甲基)(*表示與式(1)中之R1 ~R5 所連結之構成苯環之碳原子的連結部,R7 表示氫原子或甲基)。
- 如請求項1之環氧(甲基)丙烯酸酯化合物,其中前述環氧(甲基)丙烯酸酯化合物為式(3)或式(4)表示的化合物,(式中,R8 表示氫原子或甲基)(式中,R9 表示氫原子或甲基)。
- 一種硬化性組成物,其係含有請求項1或2之環氧(甲基)丙烯酸酯化合物、含有(甲基)丙烯醯基之單體及寡聚物之至少一種、及光聚合起始劑。