TR201907448T4 - Soğuk haddelenmiş ve sıcak daldırma ile kaplanmış çelik sac, üretim yöntemi ve kullanımı. - Google Patents

Soğuk haddelenmiş ve sıcak daldırma ile kaplanmış çelik sac, üretim yöntemi ve kullanımı. Download PDF

Info

Publication number
TR201907448T4
TR201907448T4 TR2019/07448T TR201907448T TR201907448T4 TR 201907448 T4 TR201907448 T4 TR 201907448T4 TR 2019/07448 T TR2019/07448 T TR 2019/07448T TR 201907448 T TR201907448 T TR 201907448T TR 201907448 T4 TR201907448 T4 TR 201907448T4
Authority
TR
Turkey
Prior art keywords
steel sheet
production method
cold rolled
coated steel
hot dip
Prior art date
Application number
TR2019/07448T
Other languages
English (en)
Inventor
Fan Dongwei
Jo Jun Hyun
A Rotole John
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of TR201907448T4 publication Critical patent/TR201907448T4/tr

Abstract

Mevcut buluş, yüksek biçimlenebilirlik özelliklerine sahip olan ve yüksek mukavemet seviyeleri sergileyen ve öncelikli olarak motorlu araçlara yönelik takviye malzemeleri ve yapısal elemanlar şeklinde kullanılması amaçlanan, motorlu araçlarda kullanıma yönelik yüksek mukavemetli çok fazlı çelikler ile ilgilidir. Mevcut buluş, aynı zamanda, yüksek biçimlenebilirlik özelliğindeki çok fazlı çelik üretimi yöntemi ile ilgilidir.
TR2019/07448T 2014-06-06 2015-06-03 Soğuk haddelenmiş ve sıcak daldırma ile kaplanmış çelik sac, üretim yöntemi ve kullanımı. TR201907448T4 (tr)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2014/000991 WO2015185956A1 (en) 2014-06-06 2014-06-06 High strength multiphase galvanized steel sheet, production method and use

Publications (1)

Publication Number Publication Date
TR201907448T4 true TR201907448T4 (tr) 2019-06-21

Family

ID=51212883

Family Applications (1)

Application Number Title Priority Date Filing Date
TR2019/07448T TR201907448T4 (tr) 2014-06-06 2015-06-03 Soğuk haddelenmiş ve sıcak daldırma ile kaplanmış çelik sac, üretim yöntemi ve kullanımı.

Country Status (16)

Country Link
US (2) US10612107B2 (tr)
EP (1) EP3152336B1 (tr)
JP (1) JP6599902B2 (tr)
KR (1) KR102389648B1 (tr)
CN (1) CN106471147B (tr)
BR (1) BR112016027681B1 (tr)
CA (1) CA2951215C (tr)
ES (1) ES2729870T3 (tr)
HU (1) HUE044866T2 (tr)
MA (1) MA39954B1 (tr)
MX (1) MX2016016129A (tr)
PL (1) PL3152336T3 (tr)
RU (1) RU2675025C2 (tr)
TR (1) TR201907448T4 (tr)
UA (1) UA117865C2 (tr)
WO (2) WO2015185956A1 (tr)

Families Citing this family (40)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6131919B2 (ja) * 2014-07-07 2017-05-24 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
ES2674133T3 (es) * 2014-12-01 2018-06-27 Voestalpine Stahl Gmbh Procedimiento para el tratamiento térmico de un producto de manganeso-acero
JP6020605B2 (ja) * 2015-01-08 2016-11-02 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法
WO2016198906A1 (fr) 2015-06-10 2016-12-15 Arcelormittal Acier a haute résistance et procédé de fabrication
US20200165708A1 (en) * 2016-02-10 2020-05-28 Jfe Steel Corporation High-strength galvanized steel sheet and method of producing the same
MX2018011891A (es) * 2016-03-31 2019-01-10 Jfe Steel Corp Chapa de acero, chapa de acero revestida, metodo de produccion de chapa de acero laminada en caliente, metodo de produccion de chapa de acero dura laminada en frio, metodo de produccion de chapa de acero y metodo de produccion de chapa de acero revestida.
CN109072375B (zh) * 2016-03-31 2020-11-03 杰富意钢铁株式会社 薄钢板和镀覆钢板、以及热轧钢板的制造方法、冷轧全硬钢板的制造方法、薄钢板的制造方法和镀覆钢板的制造方法
CN105908089B (zh) * 2016-06-28 2019-11-22 宝山钢铁股份有限公司 一种热浸镀低密度钢及其制造方法
MX2019001147A (es) * 2016-08-10 2019-06-10 Jfe Steel Corp Lamina de acerro de alta resistencia y metodo para producir la misma.
CN109563593B (zh) * 2016-08-30 2020-11-27 杰富意钢铁株式会社 高强度钢板及其制造方法
WO2018062342A1 (ja) * 2016-09-30 2018-04-05 Ｊｆｅスチール株式会社 高強度めっき鋼板及びその製造方法
KR101889181B1 (ko) 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
CN107164624B (zh) * 2017-04-10 2020-02-21 首钢集团有限公司 一种控制含磷冷轧高强钢表面麻点缺陷的方法
CN107254572B (zh) * 2017-06-01 2019-07-02 首钢集团有限公司 一种冷轧硅锰双相钢表面麻点缺陷的控制方法
CN109207841B (zh) 2017-06-30 2021-06-15 宝山钢铁股份有限公司 一种低成本高成型性1180MPa级冷轧退火双相钢板及其制造方法
CN110832095B (zh) * 2017-08-09 2021-09-28 日本制铁株式会社 热轧钢板及其制造方法
DE102017123236A1 (de) * 2017-10-06 2019-04-11 Salzgitter Flachstahl Gmbh Höchstfester Mehrphasenstahl und Verfahren zur Herstellung eines Stahlbandes aus diesem Mehrphasenstahl
JP6443594B1 (ja) * 2017-10-20 2018-12-26 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
EP3653745A4 (en) * 2017-10-20 2020-07-15 JFE Steel Corporation HIGH-STRENGTH STEEL SHEET AND MANUFACTURING METHOD THEREOF
CN107761007A (zh) * 2017-10-23 2018-03-06 攀钢集团攀枝花钢铁研究院有限公司 低碳冷轧超高强双相钢及其制备方法
WO2019123953A1 (ja) * 2017-12-22 2019-06-27 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法及び連続溶融亜鉛めっき装置
JP7137492B2 (ja) * 2018-03-28 2022-09-14 株式会社神戸製鋼所 合金化溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板の製造方法
WO2020049344A1 (en) * 2018-09-07 2020-03-12 Arcelormittal Method for improving the formability of steel blanks
EP3904553B1 (en) * 2018-12-26 2023-12-13 JFE Steel Corporation High-strength hot-dip zinc-coated steel sheet
BE1026986B1 (fr) * 2019-01-23 2020-08-25 Drever Int S A Procédé et four pour le traitement thermique d’une bande d’acier de haute résistance comprenant une chambre d’homogénéisation en température
KR102508292B1 (ko) * 2019-01-29 2023-03-09 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
WO2021123887A1 (en) * 2019-12-19 2021-06-24 Arcelormittal High toughness hot rolled steel sheet and method of manufacturing the same
WO2021176249A1 (en) * 2020-03-02 2021-09-10 Arcelormittal High strength cold rolled and galvannealed steel sheet and manufacturing process thereof
CN111411295B (zh) * 2020-03-24 2021-06-15 首钢集团有限公司 一种多相钢构件及其制备方法、应用
CN113737108A (zh) * 2020-05-27 2021-12-03 宝山钢铁股份有限公司 一种耐延迟开裂的电镀锌超强双相钢及其制造方法
CN114107789B (zh) * 2020-08-31 2023-05-09 宝山钢铁股份有限公司 一种780MPa级高表面高性能稳定性超高扩孔钢及其制造方法
JP2023539649A (ja) * 2020-08-31 2023-09-15 宝山鋼鉄股▲分▼有限公司 高強度低炭素マルテンサイト高穴拡げ性鋼及びその製造方法
KR20230145441A (ko) * 2021-03-08 2023-10-17 가부시키가이샤 고베 세이코쇼 용융 아연 도금 강판의 제조 방법 및 합금화 용융 아연 도금 강판의 제조 방법
CN115181891B (zh) * 2021-04-02 2023-07-11 宝山钢铁股份有限公司 980MPa级别低碳低合金热镀锌双相钢及快速热处理热镀锌制造方法
CN113930599B (zh) * 2021-09-24 2023-06-13 首钢集团有限公司 一种改善镀锌hsla组织均匀性的制造方法
CN114231838A (zh) * 2021-11-17 2022-03-25 邯郸钢铁集团有限责任公司 低残余应力冷成型高强钢s700mc及其生产方法
CN114480986B (zh) * 2022-01-28 2023-03-24 本钢板材股份有限公司 一种热镀锌双相钢带钢及其生产工艺
CN114807755B (zh) * 2022-04-15 2024-03-26 马鞍山钢铁股份有限公司 一种具有良好涂层质量的高强韧性预涂覆钢板及其制备方法以及钢构件及其应用
EP4303516A1 (en) 2022-07-05 2024-01-10 John Cockerill S.A. Device for improving preoxidation in an annealing furnace
CN115584440A (zh) * 2022-10-19 2023-01-10 攀钢集团攀枝花钢铁研究院有限公司 一种具有不同屈强比的1180MPa级连退双相钢及其制备方法

Family Cites Families (32)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3646538B2 (ja) * 1998-10-02 2005-05-11 Ｊｆｅスチール株式会社 加工性に優れた溶融亜鉛めっき高張力鋼板の製造方法
JP3882679B2 (ja) * 2002-05-23 2007-02-21 Ｊｆｅスチール株式会社 めっき外観の良好な深絞り性に優れた複合組織型高張力溶融亜鉛めっき冷延鋼板の製造方法
US6811624B2 (en) * 2002-11-26 2004-11-02 United States Steel Corporation Method for production of dual phase sheet steel
AU2003235443A1 (en) * 2003-05-27 2005-01-21 Nippon Steel Corporation High strength thin steel sheet excellent in resistance to delayed fracture after forming and method for preparation thereof, and automobile parts requiring strength manufactured from high strength thin steel sheet
US7883769B2 (en) 2003-06-18 2011-02-08 3M Innovative Properties Company Integrally foamed microstructured article
JP4486336B2 (ja) * 2003-09-30 2010-06-23 新日本製鐵株式会社 溶接性と延性に優れた高降伏比高強度冷延鋼板および高降伏比高強度溶融亜鉛めっき鋼板、並びに、高降伏比高強度合金化溶融亜鉛めっき鋼板とその製造方法
CA2747654C (en) * 2003-09-30 2015-04-21 Nippon Steel Corporation High yield ratio and high-strength thin steel sheet superior in weldability and ductility, high-yield ratio high-strength hot-dip galvanized thin steel sheet, high-yield ratio high-strength hot-dip galvannealed thin steel sheet, and methods of production of same
JP5162836B2 (ja) * 2006-03-01 2013-03-13 新日鐵住金株式会社 溶接部の耐水素脆性に優れる高強度冷延鋼板及びその製造方法
EP1897963A1 (fr) * 2006-09-06 2008-03-12 ARCELOR France Tole d'acier pour la fabrication de structures allegées et procédé de fabrication de cette tole
US9067260B2 (en) 2006-09-06 2015-06-30 Arcelormittal France Steel plate for producing light structures and method for producing said plate
JP5194878B2 (ja) * 2007-04-13 2013-05-08 Ｊｆｅスチール株式会社 加工性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
EP2009127A1 (en) * 2007-06-29 2008-12-31 ArcelorMittal France Process for manufacturing a galvanized or a galvannealed steel sheet by DFF regulation
ES2387040T3 (es) * 2007-08-15 2012-09-12 Thyssenkrupp Steel Europe Ag Acero de doble fase, producto plano de un acero de doble fase de este tipo y procedimiento para la fabricación de un producto plano
MX2010010116A (es) * 2008-03-27 2010-10-04 Nippon Steel Corp Chapa de acero galvanizado de alta resistencia, chapa galvanizada en baño caliente, aleada, de alta resistencia y chapa de acero laminada en frio de alta resistencia las cuales tienen propiedades superiores en moldeabilidad y soldabilidad, y metodo d
JP5251208B2 (ja) * 2008-03-28 2013-07-31 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP5504643B2 (ja) * 2008-08-19 2014-05-28 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP2010126757A (ja) * 2008-11-27 2010-06-10 Jfe Steel Corp 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5394709B2 (ja) * 2008-11-28 2014-01-22 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた超高強度鋼板
JP5564784B2 (ja) * 2008-12-05 2014-08-06 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板の製造方法
EP2415896B1 (en) * 2009-03-31 2016-11-16 JFE Steel Corporation Method for producing high-strength hot-dip galvanized steel plate
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
BRPI1010678A2 (pt) 2009-05-27 2016-03-15 Nippon Steel Corp chapade aço de alta resistência, chapa de aço banhada a quente e chapa de aço banhada a quente de liga que têm excelentes características de fadiga, alongamento e colisão, e método de fabricação para as ditas chapas de aço
ES2384135T3 (es) * 2009-08-25 2012-06-29 Thyssenkrupp Steel Europe Ag Procedimiento para fabricar un componente de acero provisto de un recubrimiento metálico de protección contra la corrosión y componente de acero
JP5771034B2 (ja) 2010-03-29 2015-08-26 株式会社神戸製鋼所 加工性に優れた超高強度鋼板、およびその製造方法
GB2493302A (en) * 2010-03-29 2013-01-30 Kobe Steel Ltd Ultra high strength steel plate having excellent workability, and protection method for same
JP5434960B2 (ja) * 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
KR20120075260A (ko) * 2010-12-28 2012-07-06 주식회사 포스코 도금밀착성이 우수한 용융도금강판 및 그 제조방법
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
DE102011051731B4 (de) * 2011-07-11 2013-01-24 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines durch Schmelztauchbeschichten mit einer metallischen Schutzschicht versehenen Stahlflachprodukts
PL2762590T3 (pl) * 2011-09-30 2019-05-31 Nippon Steel & Sumitomo Metal Corp Blacha stalowa ocynkowana i sposób jej wytwarzania
JP5569647B2 (ja) * 2011-09-30 2014-08-13 新日鐵住金株式会社 溶融亜鉛めっき鋼板及びその製造方法
EP2684975B1 (de) * 2012-07-10 2016-11-09 ThyssenKrupp Steel Europe AG Kaltgewalztes Stahlflachprodukt und Verfahren zu seiner Herstellung

Also Published As

Publication number Publication date
US20170137906A1 (en) 2017-05-18
JP6599902B2 (ja) 2019-10-30
EP3152336B1 (en) 2019-02-20
CA2951215C (en) 2023-08-01
KR20170015303A (ko) 2017-02-08
PL3152336T3 (pl) 2019-08-30
ES2729870T3 (es) 2019-11-06
US11047020B2 (en) 2021-06-29
JP2017520681A (ja) 2017-07-27
UA117865C2 (uk) 2018-10-10
CN106471147B (zh) 2018-07-10
EP3152336A1 (en) 2017-04-12
BR112016027681B1 (pt) 2021-04-27
MA39954B1 (fr) 2019-05-31
CN106471147A (zh) 2017-03-01
US10612107B2 (en) 2020-04-07
WO2015185975A1 (en) 2015-12-10
WO2015185956A1 (en) 2015-12-10
KR102389648B1 (ko) 2022-04-21
CA2951215A1 (en) 2015-12-10
HUE044866T2 (hu) 2019-11-28
RU2675025C2 (ru) 2018-12-14
US20190256942A1 (en) 2019-08-22
MX2016016129A (es) 2017-03-28
MA39954A (fr) 2017-04-12
RU2016147787A (ru) 2018-06-06
RU2016147787A3 (tr) 2018-10-26

Similar Documents

Publication Publication Date Title
TR201907448T4 (tr) Soğuk haddelenmiş ve sıcak daldırma ile kaplanmış çelik sac, üretim yöntemi ve kullanımı.
EP2738275A4 (en) HIGH-FIXED GALVANIZED STEEL PLATE AND HIGH-RESISTANCE STEEL PLATE WITH EXCELLENT FORMABILITY AND METHOD FOR THE PRODUCTION THEREOF
ZA201306547B (en) High-strength cold-rolled steel sheet with excellent local formability,and manufacturing method therefor
EP3050988A4 (en) High-strength steel sheet having excellent ductility and low-temperature toughness, and method for producing same
PL2700728T3 (pl) Blacha stalowa cienka walcowana na zimno o wysokiej wytrzymałości, wysoce jednorodnej rozciągliwości i doskonałej podatności na powiększanie otworu oraz sposób jej wytwarzania
ZA201408407B (en) Automotive chassis part made from high strength formable hot rolled steel sheet
EP3128026A4 (en) High-strength cold rolled steel sheet exhibiting excellent material-quality uniformity, and production method therefor
HUE054278T2 (hu) Eljárás javított szilárdsággal, hajlékonysággal és alakíthatósággal rendelkezõ nagy szilárdságú bevont acéllemez elõállítására
TR201900530T4 (tr) Geliştirilmiş mukavemet, süneklik ve şekillenebilirliğe sahip çelik sac üretim yöntemi.
TR201910618T4 (tr) Geliştirilmiş şekillendirilebilirliğe sahip yüksek mukavemetli çelik sac üretim yöntemi ve elde edilen sac.
EP2615191A4 (en) HIGH STRENGTH COLD ROLLED STEEL SHEET HAVING EXCELLENT STRETCH EDGE DEFORMABILITY PROPERTIES AND METHOD FOR MANUFACTURING THE SAME
EP3282032A4 (en) Steel sheet with excellent cold workability during forming, and process for producing same
KR20180084997A (ko) 고강도 용융 도금 열연 강판 및 그의 제조 방법
EP2821515A4 (en) SI-CONTAINING HIGH STRENGTH COLD-ROLLED STEEL PLATE, MANUFACTURING METHOD AND VEHICLE COMPONENT
EP3502300A4 (en) PROCESS FOR PRODUCING HALF-GALVANIZED HIGH-STRENGTH STEEL SHEET
EP3395992A4 (en) Super strength hot-rolled steel sheet excellent ductility and manufacturing therefor
EP2977481A4 (en) HIGH-WIRE HOT-ROLLED STEEL PLATE WITH A TENSILE STRENGTH OF 780 MPA OR MORE
MX2017012424A (es) Panel para vehiculo que comprende una hoja de acero revestida reforzada localmente.
WO2016093513A3 (ko) 성형성이 우수한 복합조직강판 및 이의 제조방법
EP2893050A4 (en) HIGH STRENGTH, LIGHTWEIGHT, FERRITIC WEIGHT STEEL SHEET WITH EXCELLENT RIGIDITY AND EXCELLENT DUCTILITY AND METHOD OF MANUFACTURING THE SAME
ZA201205762B (en) High-strength steel sheet having excellent bake hardenability and formability and method for manufacturing the same
ZA201205755B (en) Cold-rolled steel sheet having excellent formability and method for manufacturing the same
ZA201205756B (en) Cold-rolled steel sheet having excellent bending formability and method for manufacturing the same
EP3115482A4 (en) Cold-rolled steel sheet, manufacturing method therefor, and car part
TH1301003204B (th) แผ่นเหล็กกล้าความแข็งแรงสูง และแผ่นเหล็กกล้าชุบสังกะสีแบบจุ่มร้อนความแข็งแรงสูง ตลอดจนกรรมวิธีการผลิตนั้น