WO2022191008A1 - 溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法 - Google Patents

溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法 Download PDF

Info

Publication number
WO2022191008A1
WO2022191008A1 PCT/JP2022/008964 JP2022008964W WO2022191008A1 WO 2022191008 A1 WO2022191008 A1 WO 2022191008A1 JP 2022008964 W JP2022008964 W JP 2022008964W WO 2022191008 A1 WO2022191008 A1 WO 2022191008A1
Authority
WO
WIPO (PCT)
Prior art keywords
steel sheet
hot
mass
dip galvanized
galvanized steel
Prior art date
Application number
PCT/JP2022/008964
Other languages
English (en)
French (fr)
Inventor
彬 川上
博雄 茂
広司 入江
崇之 前田
航 于
Original Assignee
株式会社神戸製鋼所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2022014412A external-priority patent/JP2022136976A/ja
Application filed by 株式会社神戸製鋼所 filed Critical 株式会社神戸製鋼所
Priority to CN202280017458.0A priority Critical patent/CN116917527A/zh
Priority to KR1020237031386A priority patent/KR20230145441A/ko
Priority to EP22766967.8A priority patent/EP4296386A1/en
Publication of WO2022191008A1 publication Critical patent/WO2022191008A1/ja

Abstract

本発明によると、高Ｓｉ含有であり、かつ、良好なめっき密着性を有する溶融亜鉛めっき鋼板の製造方法を提供することができる。本発明に係る溶融亜鉛めっき鋼板の製造方法は、Ｓｉ含有量が１．０質量％以上である鋼素材を熱間圧延して、５００℃～７００℃で巻き取る工程と、前記巻き取り後の鋼板の表面に、鋼板温度７５０℃以下の加熱温度で酸化処理を施し、それに続いて還元処理を施す工程と、前記還元処理後の鋼板に溶融亜鉛めっき処理を施し、前記鋼板の表面に亜鉛めっき層を形成する工程と、を含む。

Description

溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法
　本発明は、高Ｓｉ含有の高強度高加工性の溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法に関する。
　自動車業界では、ＣＯ２削減のための燃費向上および衝突安全性能の向上の観点から、自動車のボディー等の自動車用部材の軽量化および高強度化が要求されている。そのため、自動車のボディー等の自動車用部材には引張強度が９８０ＭＰａ以上の超高強度鋼板が適用されている。このような高強度鋼板の加工性を向上させるために、鋼板の化学組成に安価なＳｉを含有させる方法が知られている。鋼板の化学組成にＳｉを含有させることによって、鋼板の強度だけでなく、加工性も向上することができる。
　一般的に、Ｓｉ添加鋼を自動車用部材へ適用する場合、耐食性や溶接性確保の観点から、溶融亜鉛めっき鋼板（ＧＩ鋼板）および該溶融亜鉛めっき鋼板を合金化した合金化溶融亜鉛めっき鋼板（ＧＡ鋼板）が使用される。しかしながら、鋼板にＳｉが添加された溶融亜鉛めっき鋼板は、その製造過程においてＳｉ酸化物層が鋼板表面を覆うため、最終的に、不めっき、めっき密着性の低下、合金化処理における合金化ムラ等の問題を招きやすい。さらに、合金化溶融亜鉛めっき鋼板の加工時にめっきが剥離する等の問題も生じ得る。このようなＳｉ添加による問題を抑制するために、鋼素材にＳｉを含有する溶融亜鉛めっき鋼板は、酸化加熱帯および還元加熱帯を有する焼鈍炉を用いた酸化還元法を用いて製造されることが多い。酸化還元法によると、酸化加熱帯で生成した酸化鉄が還元焼鈍時において還元Ｆｅ層を生成するため、めっき時におけるめっき濡れ性を良好にすることができる。さらに、熱間圧延における巻き取り温度を高くすることによって、予めめっきに必要なＳｉＯ２等を含む内部酸化層を鋼板に形成する方法も用いられる。
　また、近年、溶融亜鉛めっき鋼板の強度および加工性のさらなる向上のために、鋼板のＳｉ含有量を１質量％以上まで増加させた溶融亜鉛めっき鋼板や内部酸化層を良好に形成させる方法について、様々な開発が進められている。
　具体的には、例えば、特許文献１には、質量％で、Ｃ：０．０５～０．２５％、Ｓｉ：０．３～２．５％、Ｍｎ：１．５～２．８％、Ｐ：０．０３％以下、Ｓ：０．０２％以下、Ａｌ：０．００５～０．５％、Ｎ：０．００６０％以下を含有し、残部Ｆｅおよび不可避的不純物からなる高強度鋼板の上に、Ｆｅを含有し、残部がＺｎおよび不可避的不純物からなる合金化溶融亜鉛めっき層を有する鋼板において、高強度鋼板とめっき層との界面から５μｍ以下の鋼板側の結晶粒界と結晶粒内にＳｉを含む酸化物が平均含有率０．６～１０質量％で存在し、めっき層中にＳｉを含む酸化物が平均含有率０．０５～１．５質量％で存在することを特徴とする外観が良好な高強度合金化溶融亜鉛めっき鋼板が記載されている。
　また、例えば、特許文献２には、めっき密着性、加工性および外観性に優れた高強度溶融亜鉛めっき鋼板の製造方法であって、質量％で、Ｃ：０．０５～０．３０％、Ｓｉ：０．１～２．０％、Ｍｎ：１．０～４．０％含むスラブを熱間圧延した後、特定の温度ＴＣでコイルに巻き取り、酸洗する熱間圧延工程と、熱間圧延工程で得られた熱延板に対して冷間圧延を施す冷間圧延工程と、冷間圧延工程で得られた冷延板に対して、特定の条件で焼鈍を施す焼鈍工程と、焼鈍工程後の焼鈍板に対して、０．１２～０．２２質量％のＡｌを含有した溶融亜鉛めっき浴で溶融亜鉛めっき処理を施す溶融亜鉛めっき処理工程と、を有する高強度溶融亜鉛めっき鋼板の製造方法が記載されている。
　さらに、例えば、特許文献３には、冷延鋼板であって、素材鋼片を、熱間圧延後、黒皮スケールを付着させたまま、実質的に還元が起きない雰囲気中にて６５０～９５０℃の温度範囲で熱処理を施して、鋼板の地鉄表層部に内部酸化層を形成させたのち、常法に従う酸洗、冷間圧延および再結晶焼鈍を施して得たことを特徴とする冷延鋼板が記載されている。
特開２００６－２３３３３３号公報 国際公開第２０１６／０３８８０１号 特開２０００－３０９８２４号公報
　本発明は、高Ｓｉ含有であり、かつ、良好なめっき密着性を有する溶融亜鉛めっき鋼板の製造方法を提供することを目的とする。
　本発明者らは、上記課題を解決すべく鋭意検討を行った結果、本発明に到達した。
　すなわち、本発明の第一の局面に係る溶融亜鉛めっき鋼板の製造方法は、Ｓｉ含有量が１．０質量％以上である鋼素材を熱間圧延して、５００℃～７００℃で巻き取る工程と、
　前記巻き取り後の鋼板の表面に、鋼板温度７５０℃以下の加熱温度で酸化処理を施し、それに続いて還元処理を施す工程と、
　前記還元処理後の鋼板に溶融亜鉛めっき処理を施し、前記鋼板の表面に亜鉛めっき層を形成する工程と、を含む。
　本発明の第二の局面に係る合金化溶融亜鉛めっき鋼板の製造方法は、前述の第一の局面に係る溶融亜鉛めっき鋼板の製造方法で得られる溶融亜鉛めっき鋼板に形成されている前記亜鉛めっき層を合金化する工程をさらに含む。
図１は、ファイアライト層が形成された場合における合金化溶融亜鉛めっき鋼板の概略図である。
　上述したように、特許文献１～特許文献３に記載の技術は、鋼板のＳｉ含有量を１質量％以上まで増加させた溶融亜鉛めっき鋼板等の製造方法や内部酸化層を良好に形成させる方法に関する技術である。
　しかしながら、９８０ＭＰａ以上の引張強度を有する高強度高加工性の溶融亜鉛めっき鋼板を得るために、Ｓｉ含有量を１質量％以上まで増加させた場合、従来の方法を適用しただけでは良好なめっき密着性を有する溶融亜鉛めっき鋼板を得ることは難しい。特に、鋼板のコイル幅方向センター（以下、単に「幅方向センター」とも言う）近傍と比べると、鋼板のコイル幅方向エッジ（以下、単に「幅方向エッジ」とも言う）近傍において、良好なめっき密着性を確保し難い。
　具体的には、高Ｓｉ添加鋼を用いる場合、熱間圧延における巻き取り後にコイルが冷却される際、鋼板の幅方向エッジ近傍ではコイルの冷却が急峻である。そのため、鋼板の幅方向エッジ近傍では、内部酸化層が成長し難く、層が薄く形成される。その一方で、鋼板の幅方向センター近傍では、内部酸化層が十分に成長し、層が厚く形成される。さらには、鋼板の幅方向エッジ近傍の内部酸化層では、酸洗で溶けにくい粒界酸化が薄くなっている。そのため、続く酸洗工程において、鋼板の幅方向センター近傍より、鋼板の幅方向エッジ近傍の内部酸化層が優先的に溶解し、鋼板の表面に粒内酸化しているＳｉＯ２が多く残存してしまう。その結果、鋼板の表面におけるＳｉＯ２は、後の酸化還元法における酸化処理の際、鋼板の表面が酸化して生成したＦｅＯと反応してしまい、焼鈍後において鋼板とめっきとの間に厚いファイアライト層（（ＦｅＯ）２・ＳｉＯ２層）を形成する。ファイアライト層が形成されると、それに続く工程であるめっき後において、めっき密着性が悪くなり、合金化後にめっきが剥離し易くなってしまう。図１に、ファイアライト層が形成された場合における合金化溶融亜鉛めっき鋼板の概略図を示す。図１において各符号は、合金化溶融亜鉛めっき鋼板１、鋼板２、ファイアライト層３およびめっき層４を表している。図１に示すように、合金化溶融亜鉛めっき鋼板１において、鋼板２の表面に形成されたファイアライト層３のために、めっき層４が鋼板２から剥離している。
　このような問題は、前述した特許文献に記載の技術を用いても解決することはできない。例えば、特許文献１に記載の鋼板の製造方法においても、幅方向エッジ近傍におけるコイルの急冷について考慮されていないため、内部酸化層の厚みを鋼板の幅方向に均一とすることは困難であり、鋼板の幅方向エッジ近傍の表面にＳｉＯ２が多く残存し易い。また、特許文献２に記載の製造方法についても、ＳｉおよびＭｎの含有量が多くなる程巻き取り温度を下げる必要があるため、幅方向エッジ近傍に所定の量の酸化物を生成させることが難しくなり、鋼板の表面にＳｉＯ２が残存し易いと考えられる。その結果、特許文献１および特許文献２に開示されている技術を用いても、ファイアライト層が形成するおそれがあり、鋼板の幅方向に均一な良好なめっき密着性を得ることは困難である。一方、特許文献３に記載の製造方法によると、熱処理の温度が高いため、表面を覆う還元Ｆｅ層を酸洗で除去することができなくなる。その結果、鋼板の汚染や鋼板の表面付近の脱炭が進行するため、所定の強度、例えば９８０ＭＰａもの引張強度を有する鋼板を得ることは難しくなる。
　そこで、本発明者らは、Ｓｉ含有量が多い鋼板を用いて、良好なめっき密着性を有する溶融亜鉛めっき鋼板を製造する方法について様々な研究を重ねた。そして、酸化処理の加熱の際のファイアライト層の形成を抑制することに着目し、本発明を完成した。具体的には、溶融亜鉛めっき鋼板の製造の際、酸化還元法における酸化処理の加熱温度を鋼板温度７５０℃以下に設定することによって、ファイアライト層の形成を抑制できることが分かった。その結果、鋼板の幅方向エッジ近傍でも良好なめっき密着性を有する高強度高加工性の溶融亜鉛めっき鋼板が得られることが分かった。このようにして得られる溶融亜鉛めっき鋼板およびめっき層が合金化された合金化溶融亜鉛めっき鋼板は、例えば９８０ＭＰａ以上の引張強度を有することができる。
　すなわち、本発明によれば、高Ｓｉ含有であり、かつ、良好なめっき密着性を有する溶融亜鉛めっき鋼板の製造方法を提供することができる。
　以下、本発明の実施形態について、詳細に説明する。なお、本発明の範囲はここで説明する実施形態に限定されるものではなく、本発明の趣旨を損なわない範囲で種々の変更をすることができる。
　本明細書において、「内部酸化層」とは、熱間圧延および酸洗前の焼鈍（換言すると、「熱間圧延後かつ酸化還元法による焼鈍前の焼鈍」。以下同様。）の加熱時において鋼板内部に生成させることができる、ＳｉＯ２を含む内部酸化層（粒界酸化および粒内酸化の両方の酸化部分を含む）を意味する。さらに、内部酸化層は、溶融亜鉛めっき処理が施される鋼板の表層と、ＳｉＯ２等の酸化物を含有していない鋼板の内側の部分である鋼板素地部分との間に存在する。
　本明細書において、「（鋼板の）コイル幅方向エッジ」または「幅方向エッジ」とは、特定の位置を示していない限り、基本的に、コイル幅方向の両方のエッジ、すなわち板幅方向の両端を意図している。また、本明細書において、「（鋼板の）コイル幅方向エッジ近傍」または「幅方向エッジ近傍」とは、コイル幅方向エッジの位置の周辺箇所を意味する。コイル幅方向エッジから特定の位置を示す場合は、当該幅方向エッジ（換言すると、幅方向０ｍｍの位置）からの距離を併せて記す。
　本明細書において、「（鋼板の）コイル幅方向センター」または「幅方向センター」とは、鋼板の板幅方向の中央を意図している。また、本明細書において、「（鋼板の）コイル幅方向センター近傍」または「幅方向センター近傍」とは、コイル幅方向センターの位置の周辺箇所を意味する。
　本明細書において、「（鋼板の）圧延方向後端」とは、溶融亜鉛めっき用鋼板の圧延方向に対して平行な方向の後端の位置、すなわち最後端０ｍｍの位置を意図している。また、本明細書において、「（鋼板の）圧延方向後端近傍」とは、圧延方向後端の位置の周辺箇所を意味する。
　本明細書において、「（鋼板の）圧延方向前端」とは、溶融亜鉛めっき用鋼板の圧延方向に対して平行な方向の前端の位置、すなわち最前端０ｍｍの位置を意図している。また、本明細書において、「（鋼板の）圧延方向前端近傍」とは、圧延方向前端の位置の周辺箇所を意味する。
　１．溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
　本実施形態における溶融亜鉛めっき鋼板の製造方法は、Ｓｉ含有量が１．０質量％以上である鋼素材（鋼または鋼板）を熱間圧延して、５００℃～７００℃で巻き取る工程と、前記巻き取り後の鋼板の表面に、鋼板温度７５０℃以下の加熱温度で酸化処理を施し、それに続いて還元処理を施す工程と、前記還元処理後の鋼板に溶融亜鉛めっき処理を施し、前記鋼板の表面に亜鉛めっき層を形成する工程と、を含む。
　以下、各工程および各工程前後における任意の工程について、詳細に説明する。
　（圧延用の鋼素材の準備）
　まず、Ｓｉ含有量が１．０質量％以上である化学組成を有する圧延用のスラブ等の鋼素材を作製する。なお、鋼素材の化学組成は、後に詳細に述べる。スラブ等の鋼素材は既知の任意の方法により準備することができる。スラブの作製方法としては、例えば、後述する化学組成を有する鋼を溶製し、造塊または連続鋳造によって、スラブを作製する方法を挙げられる。必要に応じて、造塊または連続鋳造により得た鋳造材を分塊圧延してスラブを得てもよい。
　（熱間圧延）
　次いで、得られたスラブ等の鋼素材を用いて熱間圧延を行い、熱延鋼板を得る。
　熱間圧延は、既知の任意の条件による方法で行ってよいが、巻き取り温度を５００℃～７００℃にする。巻き取り温度を５００℃以上に設定することによって、内部酸化層を十分に成長させることができ、後の工程を経た後に、幅方向エッジ近傍の鋼板の表面にＳｉＯ２が露出および溶解し、ファイアライト層の形成に繋がってしまうおそれを防ぐことができる。巻き取り温度は、好ましくは５２０℃以上、より好ましくは５３０℃以上である。また、巻き取り温度を７００℃以下に設定することによって、熱延後の冷却で生成する還元鉄の量が増加してしまい、後の酸洗による除去が困難となることを避けることができる。巻き取り温度は、好ましくは６８０℃以下、より好ましく６６０℃以下である。
　熱間圧延時における他の条件については、特に限定されない。例えば、熱間圧延では、熱間圧延前のスラブを常法に従って１０００℃～１３００℃以下の温度で均熱保持し、仕上げ圧延温度を８００℃以上に設定し、その後コイル状の鋼板として巻き取ればよい。さらに、熱間圧延後の巻き取った熱延鋼板は、常温まで自然冷却してもよい。
　（焼鈍）
　さらに、巻き取り後の鋼板を、非還元性の雰囲気下において５４０℃～６２０℃の均熱保持温度で焼鈍すると好ましい。
　本明細書において、「非還元性の雰囲気下」とは、鋼板の表面が実質的に還元しないガス雰囲気下のことを意味する。限定されるわけではないが、例えば、Ｎ２‐１．０体積％未満Ｈ２、アルゴン、大気等のガス雰囲気下が好ましい。
　焼鈍時の均熱保持温度を５４０℃以上にすることによって、鋼板の幅方向エッジ近傍まで、内部酸化層を良好に成長させて残留させることができる。その結果、ムラなく合金化できる溶融亜鉛めっき鋼板を得ることができる。さらに、鋼板の幅方向センター近傍から幅方向エッジ近傍までだけでなく、鋼板の圧延方向前端近傍から圧延方向後端近傍まで、内部酸化層を良好に成長させて残留させるとより好ましい。その結果、鋼板の略全面においてムラなく略均一かつ確実に合金化できる溶融亜鉛めっき鋼板を得ることができる。なお、前述した熱間圧延時の巻き取りの際の加熱だけでは幅方向エッジ近傍まで十分に内部酸化層を成長させることは難しい。また、焼鈍時の均熱保持温度を６２０℃以下にすることによって、後の酸洗によるスケール除去が困難となってしまうことを避けることができる。焼鈍時の均熱保持温度は、より好ましくは５５０℃以上である。また、焼鈍時の均熱保持温度は、より好ましくは６１０℃以下である。
　焼鈍時の均熱保持時間は、特に限定されず、熱間圧延の条件（特に巻き取り温度）、本工程の均熱保持温度および後の工程の酸洗条件を考慮した上で、所望の内部酸化層を得るための好適な時間に制御すればよい。例えば、焼鈍時の均熱保持時間を３０時間以上確保することによって、所望の内部酸化層を有するめっき原板を得ることができる。焼鈍時の均熱保持時間の上限は、特に限定されないが、例えば、均熱保持時間が３０時間よりも過度に長い時間でなければ、生産性が低下することを防ぐことができる。
　（酸洗）
　次いで、焼鈍後の鋼板を酸洗すると好ましい。酸洗方法は特に限定されず、公知の任意の方法を適用すればよい。例えば、塩酸等を用いて浸漬させることにより、スケールを除去すればよい。
　酸洗は、鋼板に付着したスケールが除去される程度において調整しながら行うと好ましい。具体的には、例えば、スケールを除いた後の鋼板における酸洗減少量（すなわち、鋼板の面積当たりの重量減少量）が３１ｇ／ｍ２未満となるように酸洗することが好ましい。酸洗減少量を３１ｇ／ｍ２未満とすることによって、特に鋼板の幅方向エッジ近傍において鋼板の表面の内部酸化層中の素地鋼板結晶粒の一部が溶解し、剥離脱落して、ＳｉＯ２が鋼板の表面上に露出して分散してしまうことを防ぐことができる。それによって、めっき処理後におけるファイアライト層の形成を確実に抑制することができ、より優れためっき密着性を有する溶融亜鉛めっき鋼板を得ることができる。
　酸洗減少量は、酸洗液の種類（例えば塩酸液）、酸洗液の濃度、酸洗液の温度および酸洗時間を適切に制御することによって、前述の所望の酸洗減少量を達成することができる。例えば、塩酸濃度を、好ましくは３質量％以上、より好ましくは５質量％以上に設定すればよい。また、塩酸濃度は、例えば、好ましくは２０質量％以下、より好ましくは１５質量％以下に設定すればよい。さらに、例えば、酸洗液の温度は、好ましくは６０℃以上、より好ましくは７０℃以上に設定すればよい。また、酸洗液の温度は、好ましくは９０℃以下、より好ましくは８０℃以下に設定すればよい。酸洗時間は、例えば、酸洗減少量が３１ｇ／ｍ２未満になるように、酸洗液の濃度および温度に応じて、適宜調整すればよい。
　（冷間圧延）
　さらに、酸洗後の鋼板に冷間圧延を施してもよい。冷間圧延の方法は特に限定されず、公知の任意の方法を適用すればよい。例えば、所望する板厚にするために、冷間圧延の冷延率を１０％～７０％の範囲にすることができる。鋼板の板厚は、特に限定されない。
　（酸化処理および還元処理）
　次いで、得られた鋼板の表面に対して、酸化還元法による焼鈍を適用する。まず、鋼板の表面に酸化処理を施すことによって、鋼板の表面に酸化Ｆｅ層を形成する。さらに、還元性の雰囲気下で当該酸化Ｆｅ層に還元処理（本明細書において、「還元焼鈍処理」とも言う）を施して還元Ｆｅ層を形成する。この際、還元により酸化Ｆｅ層から供給される酸素は、鋼板内部におけるＳｉやＭｎを酸化させる。すなわち、このような酸化還元法による焼鈍を適用することによって、酸化Ｆｅ層がバリアー層となり、Ｓｉの酸化物を鋼板の内部に留めることができ、鋼板の表面近傍におけるＳｉの酸化を抑制することができる。その結果、溶融亜鉛めっきに対する濡れ性を良好とすることができ、最終的にめっき密着性についてもより良好とすることができる。
　酸化処理および還元処理は、公知の任意の単数または複数の設備を用いて実施すればよい。好ましくは、製造効率、コスト面および品質保持の観点から、連続溶融亜鉛めっきライン（ＣＧＬ：Ｃｏｎｔｉｎｕｏｕｓ　Ｇａｌｖａｎｉｚｉｎｇ　Ｌｉｎｅ）の設備が用いられる。連続溶融亜鉛めっきラインを用いることによって、酸化還元法による酸化処理および還元処理と、後述する溶融亜鉛めっき処理および合金化処理とを、一連の製造ラインで連続して行うことができる。さらに具体的には、酸化還元法による酸化処理および還元処理は、例えば、無酸化炉（ＮＯＦ：Ｎｏｎ　Ｏｘｙｇｅｎ　Ｆｕｒｎａｃｅ）型または直火炉（ＤＦＦ：Ｄｉｒｅｔ　Ｆｉｒｅｄ　Ｆｕｒｎａｃｅ）型の連続溶融亜鉛めっきラインにおける焼鈍炉を用いて行うとより好ましい。
　酸化処理は、例えばＮＯＦ型またはＤＦＦ型の焼鈍炉内の酸化加熱帯等において、鋼板の表面に、鋼板温度７５０℃以下の加熱温度で施される。鋼板温度を７５０℃以下にすることによって、特に鋼板の幅方向エッジ近傍表面におけるＳｉＯ２と酸化処理により生じるＦｅＯとの反応を抑制することができる。その結果、焼鈍後におけるファイアライト層の形成を防ぐことができ、良好なめっき密着性を有する溶融亜鉛めっき鋼板を得ることができる。
　本明細書において、酸化処理における加熱時の「鋼板温度」とは、酸化加熱帯において加熱制御される鋼板の最高到達板温を意味する。
　酸化処理における鋼板温度は、好ましくは７３０℃以下、より好ましくは７２０℃以下、さらに好ましくは７００℃以下である。酸化処理における鋼板温度の下限は、特に限定されず、鋼板の表面において後述するガス雰囲気下で酸化Ｆｅ層が形成される温度であればよい。例えば、酸化処理における鋼板温度は、好ましくは６５０℃以上、より好ましくは６７０℃以上である。
　酸化処理における昇温時間は、特に限定されず、過度に長すぎることで酸化処理によってファイアライト層が形成しないように調整すればよい。具体的には、酸化処理における昇温時間は、熱間圧延の条件（特に巻き取り温度）、酸洗前の焼鈍条件、酸洗条件および酸化処理における加熱時の鋼板温度を考慮した上で、適切に調整すればよい。例えば、酸化処理における昇温時間は、好ましくは１０秒以上、より好ましくは１５秒以上である。また、例えば、酸化処理における昇温時間は、好ましくは１２０秒以下、より好ましくは９０秒以下である。
　酸化処理は、特に限定されないが、例えば、Ｏ２、ＣＯ２、Ｎ２およびＨ２Ｏを含むガス雰囲気下において行うことができる。より詳細には、酸化処理は、例えばＮＯＦ型またはＤＦＦ型の焼鈍炉等において、コークス炉ガス（ＣＯＧ：Ｃｏｋｅｓ　Ｏｖｅｎ　Ｇａｓ）、液化石油ガス（ＬＰＧ：Ｌｉｑｕｅｆｉｅｄ　Ｐｅｔｒｏｌｅｕｍ　Ｇａｓ）等の燃焼ガス中で、未燃焼のＯ２濃度を制御したガス雰囲気下において行うことができる。Ｏ２濃度は１００ｐｐｍ～１７０００ｐｐｍの範囲で制御すると好ましい。Ｏ２濃度は、より好ましくは５００ｐｐｍ以上、さらに好ましくは２０００ｐｐｍ以上で制御される。また、Ｏ２濃度は、より好ましくは１５０００ｐｐｍ以下、さらに好ましくは１３０００ｐｐｍ以下で制御される。
　還元焼鈍処理における鋼板の加熱温度（均熱保持温度）は、特に限定されず、酸化処理によって形成された酸化Ｆｅ層が還元Ｆｅ層になる温度で行われればよい。具体的には、好ましくはＡｃ３点以上の均熱保持温度で還元焼鈍を行うと好ましい。なお、Ａｃ３点は、下式（ｉ）により算出することができる（「レスリー鉄鋼材料学」（丸善株式会社発行、Ｗｉｌｌｉａｍ　Ｃ．　Ｌｅｓｌｉｅ著、ｐ２７３））。式（ｉ）中の［　］で囲まれた元素記号は、当該元素の含有量（質量％）を表す。
　Ａｃ３（℃）＝９１０－２０３×［Ｃ］１／２－１５．２×［Ｎｉ］＋４４．７×［Ｓｉ］＋１０４×［Ｖ］＋３１．５×［Ｍｏ］＋１３．１×［Ｗ］－｛３０×［Ｍｎ］＋１１×［Ｃｒ］＋２０×［Ｃｕ］－７００×［Ｐ］－４００×［Ａｌ］－１２０×［Ａｓ］－４００×［Ｔｉ］｝　…（ｉ）
　また、還元処理における加熱時間（均熱保持時間）は、特に限定されず、酸化処理により形成された酸化Ｆｅ層が還元Ｆｅ層になるように適切に調整すればよい。例えば、還元処理における加熱時間は、好ましくは３０秒以上、より好ましくは４５秒以上である。また、還元処理における加熱時間は、好ましくは６００秒以下、より好ましくは５００秒以下である。
　還元焼鈍処理は、例えばＮＯＦ型またはＤＦＦ型の焼鈍炉内の還元加熱帯等において、公知の任意の処理方法によって行うことができる。具体的には、主にＨ２ガスおよびＮ２等の不活性ガスを含む還元性の雰囲気下で、鋼板の表面を加熱することによって行うことができる。Ｈ２ガスおよびＮ２等の不活性ガスを含む混合ガスを用いる場合、例えばＨ２ガスを３体積％～２５体積％の割合において含み、Ｎ２等の不活性ガスを残部として含むことができる。
　（溶融亜鉛めっき処理）
　さらに、還元処理後の鋼板に溶融亜鉛めっき処理を施し、鋼板の表面に亜鉛めっき層を形成することによって、本実施形態における溶融亜鉛めっき鋼板を製造することができる。
　溶融亜鉛めっき処理の方法は特に限定されず、公知の任意の方法を適用すればよい。例えば、鋼板を亜鉛めっき浴に４００℃～５００℃程度の鋼板温度で浸漬させることによって、鋼板の表面に亜鉛めっき層を形成することができる。さらに、鋼板の亜鉛めっき浴への浸漬時間は、所望の亜鉛めっき付着量に応じて調整すればよい。
　（合金化処理）
　本実施形態に係る合金化溶融亜鉛めっき鋼板の製造方法では、前述の方法で得られた溶融亜鉛めっき鋼板に形成された亜鉛めっき層を合金化する工程をさらに含む。
　具体的には、溶融亜鉛めっき鋼板を所定の合金化温度で加熱することによって、鋼板に含まれるＦｅ原子が亜鉛めっき層に拡散し、亜鉛めっき層を合金化することができる。合金化方法は、特に限定されず、公知の任意の方法を適用することができる。合金化温度は、特に限定されないが、例えば、好ましくは４６０℃～６５０℃で設定することができる。合金化温度での加熱時間も、特に限定されないが、例えば、好ましくは１０秒～４０秒で設定することができる。さらに、合金化の加熱は、例えば大気雰囲気下とすることができる。
　２．鋼素材の化学組成
　本実施形態における溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法に使用される、鋼素材の化学組成は、Ｓｉ以外は特に限定されない。以下、鋼素材の化学組成の一例について説明する。
　［Ｓｉ：１質量％以上］
　Ｓｉは、安価な鋼の強化元素であり、かつ、鋼板の加工性に対して影響を与え難い。また、Ｓｉは、鋼板の加工性向上に有用な残留オーステナイトが分解して炭化物が生成することを抑制できる元素である。このような作用を有効に発揮させるため、Ｓｉ含有量は１．０質量％以上、好ましくは１．１質量％以上、さらに好ましくは１．２質量％以上である。Ｓｉ含有量の上限は、特に限定されないが、Ｓｉ含有量が多すぎると、Ｓｉによる固溶強化作用が顕著になって圧延負荷が増大してしまうおそれがあり、熱間圧延の際にＳｉスケールが発生して鋼板の表面欠陥が生じてしまう可能性がある。そのため、例えば、Ｓｉ含有量は、製造安定性の観点から、好ましくは３．０質量％以下、より好ましくは２．７質量％以下、さらに好ましくは２．５質量％以下である。
　［Ｍｎ：好ましくは１．５質量％以上３．０質量％以下］
　Ｍｎも、Ｓｉと同様に、安価な鋼の強化元素であり、鋼板の強度向上に有効である。Ｍｎは、Ｓｉと一緒に、さらに必要に応じてＣも一緒に鋼に添加することによって、最終的に９８０ＭＰａ以上の溶融亜鉛めっき鋼板の引張強度を確保するために特に有効な強化元素である。さらに、Ｍｎは、オーステナイトを安定化し、残留オーステナイトの生成による鋼板の加工性向上に寄与する元素である。このような作用を有効に発揮させるため、Ｍｎ含有量は、好ましくは１．５質量％以上、より好ましくは１．８質量％以上、さらに好ましくは２．０質量％以上である。しかしながら、Ｍｎ含有量が多すぎると、鋼板の延性が低下し、鋼板の加工性に悪影響を及ぼし、鋼板の溶接性が低下するおそれがある。このような観点から、Ｍｎ含有量は、好ましくは３．０質量％以下、より好ましくは２．８質量％以下、さらに好ましくは２．７質量％以下である。
　［Ｃ：好ましくは０．０８質量％以上０．３０質量％以下］
　Ｃは、鋼板の強度向上に有効な元素であり、Ｓｉと一緒に、さらに必要に応じてＭｎも一緒に鋼に添加することによって、最終的に９８０ＭＰａ以上の溶融亜鉛めっき鋼板の引張強度を確保するために特に有効な強化元素である。さらに、Ｃは、残留オーステナイトを確保して加工性を改善するために必要な元素である。このような作用を有効に発揮させるため、Ｃ含有量は、好ましくは０．０８質量％以上、より好ましくは０．１１質量％以上、さらに好ましくは０．１３質量％以上である。鋼板の強度の確保の観点からはＣ含有量が多い方が好ましいが、Ｃ含有量が多すぎると耐食性、スポット溶接性および加工性が劣化するおそれがある。そのため、Ｃ含有量は、好ましくは０．３０質量％以下、より好ましくは０．２５質量％以下、さらに好ましくは０．２０質量％以下である。
　［Ｐ：好ましくは０質量％超０．１質量％以下］
　Ｐは、不純物元素として不可避的に存在する元素である。Ｐ含有量が過剰になると、鋼板の溶接性を劣化させるおそれがある。そのため、Ｐ含有量は、好ましくは０．１質量％以下、より好ましくは０．０８質量％以下、さらに好ましくは０．０５質量％以下に抑制する。
　［Ｓ：好ましくは０質量％超０．０５質量％以下］
　Ｓは、不純物元素として不可避的に存在する元素である。通常、鋼は、不可避的に０．０００５質量％程度においてＳを含有している。Ｓ含有量が過剰になると、硫化物系介在物を形成し、腐食環境下で水素吸収を促し、鋼板の耐遅れ破壊性を劣化させ、鋼板の溶接性および加工性を劣化させるおそれがある。そのため、Ｓ含有量は、好ましくは０．０５質量％以下、より好ましくは０．０１質量％以下、さらに好ましくは０．００５質量％以下に抑制する。
　［Ａｌ：好ましくは０質量％超１．０質量％以下］
　Ａｌは、脱酸作用を有する元素である。このような作用を有効に発揮させるため、Ａｌ含有量は、好ましくは０質量％超、より好ましくは０．００５質量％以上、さらに好ましくは０．０２質量％以上である。Ａｌ含有量が過剰になると、アルミナ等の介在物が増加し、鋼板の加工性が劣化するおそれがある。そのため、Ａｌ含有量は、好ましくは１．０質量％以下、より好ましくは０．８質量％以下、さらに好ましくは０．５質量％以下である。
　［Ｃｒ：好ましくは０質量％超１．０質量％以下］
　Ｃｒは、鋼板の強度向上に有効な元素である。さらに、Ｃｒは、鋼板の耐食性を向上させる元素であり、鋼板の腐食による水素の発生を抑制する作用を有する。具体的には、Ｃｒは、酸化鉄（α－ＦｅＯＯＨ）の生成を促進させる作用を有する。酸化鉄は、大気中で生成する錆のなかでも熱力学的に安定であり、かつ保護性を有するといわれている。このような錆の生成を促進することによって、発生した水素が鋼板へ侵入することを抑制でき、過酷な腐食環境下、例えば、塩化物の存在下で鋼板を使用した場合でも水素による助長割れを十分に抑制できる。また、Ｃｒは、ＢおよびＴｉと同様に、鋼板の耐遅れ破壊性にも有効な元素であるため、鋼板の強度と伸び等の加工性に影響を与えない量において添加することができる。これらの作用を有効に発揮させるには、Ｃｒ含有量は、好ましくは０質量％超、より好ましくは０．００３質量％以上、さらに好ましくは０．０１質量％以上である。一方、Ｃｒ含有量が過剰になると、鋼板の伸び等の加工性が劣化するおそれがある。そのため、Ｃｒ含有量は、好ましくは１．０質量％以下、より好ましくは０．８質量％以下、さらに好ましくは０．６質量％以下である。
　［Ｃｕ：好ましくは０質量％超１．０質量％以下］
　Ｃｕも、Ｃｒと同様に、鋼板の強度向上に有効であり、かつ、鋼板の腐食による水素の発生を抑制する作用を有し、鋼板の耐食性を向上させる元素である。Ｃｕも、Ｃｒと同様に、酸化鉄の生成を促進させる作用を有する。これらの作用を有効に発揮させるには、Ｃｕ含有量は、好ましくは０質量％超、より好ましくは０．００３質量％以上、さらに好ましくは０．０５質量％以上である。また、鋼板の加工性の観点から、Ｃｕ含有量は、好ましくは１．０質量％以下、より好ましくは０．８質量％以下、さらに好ましくは０．５質量％以下である。
　［Ｎｉ：好ましくは０質量％超１．０質量％以下］
　Ｎｉも、ＣｒおよびＣｕと同様に、鋼板の強度向上に有効であり、かつ、鋼板の腐食による水素の発生を抑制する作用を有し、鋼板の耐食性を向上させる元素である。Ｎｉも、ＣｒおよびＣｕと同様に、酸化鉄の生成を促進させる作用を有する。これらの作用を有効に発揮させるには、Ｎｉ含有量は、好ましくは０質量％超、より好ましくは０．００３質量％以上、さらに好ましくは０．０５質量％以上である。また、鋼板の加工性の観点から、Ｎｉ含有量は、好ましくは１．０質量％以下、より好ましくは０．８質量％以下、さらに好ましくは０．５質量％以下である。
　［Ｔｉ：好ましくは０質量％超０．１５質量％以下］
　Ｔｉも、Ｃｒ、ＣｕおよびＮｉと同様に、鋼板の強度向上に有効であり、かつ、鋼板の腐食による水素の発生を抑制する作用を有し、鋼板の耐食性を向上させる元素である。Ｔｉも、Ｃｒ、ＣｕおよびＮｉと同様に、酸化鉄の生成を促進させる作用を有する。また、Ｔｉは、ＢおよびＣｒと同様に、鋼板の耐遅れ破壊性にも有効な元素であるため、鋼板の強度と伸び等の加工性に影響を与えない量において添加することができる。これらの作用を有効に発揮させるには、Ｔｉ含有量は、好ましくは０質量％超、より好ましくは０．００３質量％以上、さらに好ましくは０．０５質量％以上である。また、鋼板の加工性の観点から、Ｔｉ含有量は、好ましくは０．１５質量％以下、より好ましくは０．１２質量％以下、さらに好ましくは０．１０質量％以下である。
　［Ｎｂ：好ましくは０質量％超０．１５質量％以下］
　Ｎｂは、鋼板の強度向上に有効であり、かつ、焼入れ後のオーステナイト粒を微細化して鋼板の靭性の改善に作用する元素である。このような作用を有効に発揮させるには、Ｎｂ含有量は、好ましくは０質量％超、より好ましくは０．０３質量％以上、さらに好ましくは０．００５質量％以上である。一方、Ｎｂ含有量が過剰になると、炭化物、窒化物または炭窒化物を多量に生成し、鋼板の加工性または耐遅れ破壊性が劣化するおそれがある。そのため、Ｎｂ含有量は、好ましくは０．１５質量％以下、より好ましくは０．１２質量％以下、さらに好ましくは０．１０質量％以下である。
　［Ｖ：好ましくは０質量％超０．１５質量％以下］
　Ｖも、Ｎｂと同様に、鋼板の強度向上に有効であり、かつ、焼入れ後のオーステナイト粒を微細化して鋼板の靭性の改善に作用する元素である。このような作用を有効に発揮させるには、Ｖ含有量は、好ましくは０質量％超、より好ましくは０．０３質量％以上、さらに好ましくは０．００５質量％以上である。一方、Ｖ含有量が過剰になると、Ｎｂと同様に、炭化物、窒化物または炭窒化物を多量に生成し、鋼板の加工性または耐遅れ破壊性が劣化するおそれがある。そのため、Ｖ含有量は、好ましくは０．１５質量％以下、より好ましくは０．１２質量％以下、さらに好ましくは０．１０質量％以下である。
　［Ｂ：好ましくは０質量％超０．００５質量％以下］
　Ｂは、鋼板の焼入れ性および溶接性の向上に有用な元素である。また、Ｂは、ＴｉおよびＣｒと同様に、鋼板の耐遅れ破壊性にも有効な元素であるため、鋼板の強度と伸び等の加工性に影響を与えない量において添加することができる。これらの作用を有効に発揮させるには、Ｂ含有量は、好ましくは０質量％超、より好ましくは０．０００２質量％以上、さらに好ましくは０．０００３質量％以上、特に好ましくは０．０００４質量％以上である。一方、Ｂ含有量が過剰になると、このような効果は飽和し、かつ、延性が低下して加工性が悪くなるおそれがある。そのため、Ｂ含有量は、好ましくは０．００５質量％以下、さらに好ましくは０．００４質量％以下、さらに好ましくは０．００３質量％以下である。
　［Ｎ：好ましくは０質量％超０．０１質量％以下］
　Ｎは、不純物元素として不可避的に存在する元素である。Ｎ含有量が過剰になると、窒化物を形成して鋼板の加工性が劣化するおそれがある。特に、焼入れ性の向上のために鋼板がＢを含有する場合、ＮはＢと結合してＢＮ析出物を形成し、Ｂの焼入れ性向上作用を阻害する。そのため、Ｎ含有量は、好ましくは０．０１質量％以下、より好ましくは０．００８質量％以下、さらに好ましくは０．００５質量％以下に抑制する。
　また、本実施形態における鋼素材の化学組成は、上記成分のほか、強度や十分な加工性を阻害しない範囲で、他の周知の任意成分をさらに含有することもできる。
　［残部］
　残部はＦｅおよび不可避不純物である。不可避不純物としては、原料、資材、製造設備等の状況によって持ち込まれる微量元素（例えば、Ａｓ、Ｓｂ、Ｓｎ等）の混入が許容される。なお、前述したようなＰ、ＳおよびＮは、通常含有量が少ないほど好ましいため、不可避不純物ともいえる。しかし、これらの元素は特定の範囲まで含有量を抑えることによって本発明がその効果を発揮することができるため、上記のように規定している。このため、本明細書において、残部を構成する「不可避不純物」は、その組成範囲が規定されている元素を除いた概念である。
　本実施形態における製造方法によると、Ｓｉ含有量が１質量％以上である高Ｓｉ含有の鋼素材を用いるために、高強度高加工性の溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板を安価に製造することができ、かつ、コイル幅方向においてめっき密着性を良好とすることができる。そのため、合金化溶融亜鉛めっき鋼板において、鋼板の幅方向エッジ近傍でもめっきが剥離することがない。より具体的には、製造される溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板は、９８０ＭＰａ以上の引張強度を有することができる。
　さらに、前述したように、連続溶融亜鉛めっきラインを用いて、酸化処理、還元処理、溶融亜鉛めっき処理および合金化処理を一連の製造ラインで連続して行うことによって、製品の品質を保持したまま安価に効率よくめっき密着性が良好な高強度高加工性の合金化溶融亜鉛めっき鋼板を製造することができる。
　以上、本発明の概要について説明したが、本発明の実施形態における溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法をまとめると下記の通りである。
　本発明の第一の局面に係る溶融亜鉛めっき鋼板の製造方法は、Ｓｉ含有量が１．０質量％以上である鋼素材を熱間圧延して、５００℃～７００℃で巻き取る工程と、
　前記巻き取り後の鋼板の表面に、鋼板温度７５０℃以下の加熱温度で酸化処理を施し、それに続いて還元処理を施す工程と、
　前記還元処理後の鋼板に溶融亜鉛めっき処理を施し、前記鋼板の表面に亜鉛めっき層を形成する工程と、を含む。
　前述の溶融亜鉛めっき鋼板の製造方法において、前記巻き取りと前記酸化処理との間に、非還元性の雰囲気下において５４０℃～６２０℃の均熱保持温度で鋼板を焼鈍する工程をさらに含むことが好ましい。
　本発明の第二の局面に係る合金化溶融亜鉛めっき鋼板の製造方法は、前述の第一の局面に係る溶融亜鉛めっき鋼板の製造方法で得られる溶融亜鉛めっき鋼板に形成されている前記亜鉛めっき層を合金化する工程をさらに含む。
　以下に、実施例により本発明をさらに具体的に説明するが、本発明は実施例により何ら限定されるものではない。
　（実施例１）
　実施例１では、本発明例の一つである溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板を製造し、製造した溶融亜鉛めっき鋼板におけるめっき密着性を評価した。
　［溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造］
　後の表１に示す鋼種Ａの化学組成の鋼材を転炉にて溶製した後、連続鋳造によりスラブを製造した。得られたスラブを、仕上げ圧延終了温度を９００℃として、板厚２．０ｍｍとなるまで熱間圧延し、後の表２に示すように６４０℃℃で巻き取り、得られた熱延鋼板を常温まで冷却した。その後、熱延鋼板を焼鈍炉に投入し、焼鈍を行った。焼鈍条件は、Ｎ２‐０．９体積％未満Ｈ２の非還元性の雰囲気下において、熱延鋼板を５８０℃まで約８．５時間で昇温し、５８０℃で３０時間均熱保持し、次いで２００℃以下まで約５時間かけて冷却した。その後、得られた焼鈍鋼板を、濃度８重量％である塩酸を用いて８５℃において４０秒間浸漬させることによって酸洗した。最後に、焼鈍鋼板が板厚２．０ｍｍから１．４ｍｍになるまで冷間圧延を行った。次いで、そのように製造した鋼板を用いて、ＮＯＦ型の焼鈍炉を有する連続溶融亜鉛めっきラインを適用して、酸化処理、還元処理、溶融亜鉛めっき処理および合金化処理を行った。酸化処理では、１７０００ｐｐｍ未満のＯ２とＣＯ２、Ｎ２およびＨ２Ｏとを含む燃焼排ガス雰囲気下において、４５秒の昇温時間で、７１６℃の鋼板温度になるように、鋼板を加熱した。
　ここで、「鋼板温度」とは、ＮＯＦ型（または後述する実施例２および実施例３ではＤＦＦ型）の焼鈍炉の酸化加熱帯において加熱制御される鋼板の最高到達板温を意味する。
　還元処理は、酸化後の鋼板を、Ｎ２‐Ｈ２のガス雰囲気下において、約８００℃（８００℃～９００℃）の均熱保持温度において約６０秒（５０秒～６０秒）にわたり加熱した。溶融亜鉛めっき処理は、還元後の鋼板を亜鉛めっき浴に４３０℃において浸漬させて、溶融亜鉛めっき層を形成した。このようにして溶融亜鉛めっき鋼板を得て、その後、合金化処理により合金化溶融亜鉛めっき鋼板を得た。
　［溶融亜鉛めっき鋼板のめっき密着性の評価］
　得られた合金化溶融亜鉛めっき鋼板のめっき密着性を評価した。具体的には、得られた合金化溶融亜鉛めっき鋼板を用いて、以下の条件にてクランクプレスでハット型成形部材を成形し、成形部材の側壁の摺動面のめっき剥離状況を目視にて判定した。なお、評価サンプルは、得られた合金化溶融亜鉛めっき鋼板の圧延方向後端近傍における、幅方向エッジから５０ｍｍ～１００ｍｍの位置を包含するように切り取った。具体的な評価基準についても以下に示す。実施例１の溶融亜鉛めっき鋼板のめっき密着性の評価結果は、鋼板の製造条件と共に、後の表２にまとめて示す。
（クランクプレスの条件）
　評価サンプルのサイズ：幅４０ｍｍ×長さ２５０ｍｍ
　ダイ幅：５２ｍｍ
　ダイ肩半径：２ｍｍ
　パンチ幅：４８ｍｍ
　パンチ肩半径：５ｍｍ
　ビード：有り
　ビード先端半径：２ｍｍ
　ビード高さ：３ｍｍ
　成形高さ：６０ｍｍ
　（めっき密着性の評価基準）
　〇：めっき層に明確な剥離は観察されない
　×：めっき層にフレーク状の浮き上がりが観察される
　（実施例２）
　実施例２では、後の表１に示す鋼種Ｃの化学組成の鋼材を用い、熱間圧延巻き取り温度を６６０℃とし、ＤＦＦ型の焼鈍炉を有する連続溶融亜鉛めっきラインを適用して、酸化処理、還元処理、溶融亜鉛めっき処理および合金化処理を行い、ＤＦＦ型の焼鈍炉内の酸化加熱帯の鋼板温度を６７１℃とし、還元処理の均熱保持温度を約９００℃（９００℃～９５０℃）とし、均熱保持時間を約３００秒（２４０秒～３６０秒）としたこと以外は、前述の実施例１と同じ方法で溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板を製造した。さらに、めっき密着性についても同様に評価した。実施例２の溶融亜鉛めっき鋼板のめっき密着性の評価結果についても、鋼板の製造条件と共に、後の表２にまとめて示す。
　（実施例３）
　実施例３では、後の表１に示す鋼種Ｄの化学組成の鋼材を用い、ＤＦＦ型の焼鈍炉内の酸化加熱帯の鋼板温度を６７９℃としたこと以外は、前述の実施例２と同じ方法で溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板を製造した。さらに、めっき密着性についても同様に評価した。実施例３の溶融亜鉛めっき鋼板のめっき密着性の評価結果についても、鋼板の製造条件と共に、後の表２にまとめて示す。
　（比較例１）
　比較例１では、後の表１に示す鋼種Ｂの化学組成の鋼材を用いて、熱間圧延巻き取り温度を５５０℃とし、ＮＯＦ型の焼鈍炉内の酸化加熱帯の鋼板温度を９０６℃としたこと以外は、前述の実施例１と同じ方法で溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板を製造した。さらに、めっき密着性についても同様に評価した。比較例１の溶融亜鉛めっき鋼板のめっき密着性の評価結果についても、鋼板の製造条件と共に、後の表２にまとめて示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　（考察）
　上記表２に示すように、溶融亜鉛めっきラインにおける加熱温度が７１６℃である実施例１、６７１℃である実施例２および６７９℃である実施例３の溶融亜鉛めっき鋼板は、優れためっき密着性を有していた。一方、比較例１の溶融亜鉛めっき鋼板は、酸洗前の焼鈍条件が実施例１、実施例２および実施例３と同じであっても、溶融亜鉛めっきラインにおける加熱温度が高く、本実施形態における規定の温度から外れるため、めっき密着性が劣っていた。これは、比較例１では酸化処理の加熱時の鋼板温度が高すぎたことにより、鋼板とめっきとの間に厚いファイアライト層が形成されたためと考えられる。
　本出願は、２０２１年３月８日に出願された日本国特許出願特願２０２１－０３６２２６号および２０２２年２月１日に出願された日本国特許出願特願２０２２－０１４４１２号を基礎とするものであり、その内容は、本願に含まれるものである。
　今回開示された実施形態および実施例は、全ての点で例示であって制限的なものではないと解されるべきである。本発明の範囲は、上述した説明ではなくて特許請求の範囲により示され、特許請求の範囲と均等の意味および範囲内での全ての変更が含まれることが意図される。
　本発明によれば、Ｓｉ含有量が多い場合であっても、良好なめっき密着性を有する溶融亜鉛めっき鋼板を製造することができる。そのため、例えば、自動車のボディー等の自動車用部材に好適に適用される９８０ＭＰａ以上の引張強度の高強度高加工性の溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板を効率的に製造することができる。
 

Claims (3)

  1. 　溶融亜鉛めっき鋼板の製造方法であって、
    　Ｓｉ含有量が１．０質量％以上である鋼素材を熱間圧延して、５００℃～７００℃で巻き取る工程と、
    　前記巻き取り後の鋼板の表面に、鋼板温度７５０℃以下の加熱温度で酸化処理を施し、それに続いて還元処理を施す工程と、
    　前記還元処理後の鋼板に溶融亜鉛めっき処理を施し、前記鋼板の表面に亜鉛めっき層を形成する工程と、を含む、溶融亜鉛めっき鋼板の製造方法。
  2. 　前記巻き取りと前記酸化処理との間に、非還元性の雰囲気下において５４０℃～６２０℃の均熱保持温度で鋼板を焼鈍する工程をさらに含む、請求項１に記載の溶融亜鉛めっき鋼板の製造方法。
  3. 　合金化溶融亜鉛めっき鋼板の製造方法であって、
    　請求項１または２に記載の溶融亜鉛めっき鋼板の製造方法で得られる溶融亜鉛めっき鋼板に形成されている前記亜鉛めっき層を合金化する工程をさらに含む、合金化溶融亜鉛めっき鋼板の製造方法。
PCT/JP2022/008964 2021-03-08 2022-03-02 溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法 WO2022191008A1 (ja)